CN1186349A - Preparation of material for anode of solid lithium battery - Google Patents
Preparation of material for anode of solid lithium battery Download PDFInfo
- Publication number
- CN1186349A CN1186349A CN96118933A CN96118933A CN1186349A CN 1186349 A CN1186349 A CN 1186349A CN 96118933 A CN96118933 A CN 96118933A CN 96118933 A CN96118933 A CN 96118933A CN 1186349 A CN1186349 A CN 1186349A
- Authority
- CN
- China
- Prior art keywords
- polyaniline
- organic sulfur
- sulfur compound
- compound
- derivative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A process for preparing positive electrode of secondary lithium battery includes such technological steps as preparing compound solution of polyphenylamine derivative and organic sulfide in organic solvent of N-methylpyrrolidone, addition of conducting carbon black, and coating or brushing it on the surface of current collector such as copper, aluminium, platinum, or stainless steel. Obtained positive electrode has the advantage of high specific energy as the polyphenylamine derivative has better compatibility and stronger catalytic power to organic sulfide.
Description
The invention belongs to the preparation method of all solid lithium secondary battery positive electrode.
Along with the great attention of people to energy issue of world, society is to cheap, high specific energy, the demand of the chemical power source that discharges and recharges capable of circulation is more and more urgent, especially the high speed development of auto industry, the chemical power source that can be used for electric automobile has been played huge impetus, 1989, people such as the S.J.Visco of the U.S. can report with the positive electrode of organic sulfur compound as lithium battery in will " A Novel Classof Organosulfur Electrode for Energy Strorage " (J Electrochem.Soc.136 (661) 1989) and " Novel Solid Redox Polymerization Electrode " articles such as (J.Electrochem.Soc.138 (1891) 1991) in electrochemistry, obtain the great attention of various countries scholar and industrial quarters.Organic sulfur compound have high energy density (>900wh/kg), scope that can be in normal temperature~150 ℃ is used.Lithium/solid electrolyte/dimercaptothiodiazole the battery of laboratory assembling reaches 140Wh/kg 100 ℃ of energy densities.In battery charge and discharge process, the redox reaction of organic sulfur compound is conciliate collecting process with respect to polymerization, just the generation of S-S key and fracture process.
Although organic sulfur compound has high energy storage density, its redox reaction at normal temperatures is very slow, and this becomes the key factor that hinders this material use.Nineteen ninety-five Japan people such as N.Oyama at nature " Dimercapton-Polyaniline Composite Electrodes for Lithium Batteries with High EnergyDensity " (Nature, 373 (598) 1995) etc. reported compound in the article as positive electrode with polyaniline and organic sulfur compound, make the redox reaction speed and the invertibity of organic sulfur compound obtain significant raising, energy density reaches 185Ah/kg, at room temperature with 0.1mA/cm
2Current density can cycle charge-discharge 83 circles and capacity does not have marked change.Polyaniline has played electrochemical catalytic action therein, but and polyaniline itself also as one of positive active material of energy storage.
The preparation method who the purpose of this invention is to provide a kind of all solid lithium secondary battery positive electrode, promptly select polyaniline derivative and organic sulfur compound compound, the method of solution blending and physical mixed is united use, thereby improve the compatibility of catalyst and organic sulfur compound, polyaniline derivative and organic sulfur compound be compound near molecular level more than polyaniline and organic sulfur compound, thereby reach better catalytic effect.
The present invention is compound as electrochemical catalyst and positive active material and organic sulfur compound with polyaniline derivative, and concrete structure is as follows:
1). the derivative of polyaniline:
Wherein: R
1=-C
nH
2n+1(n=1~12) or-H
R
2=-H ,-Cl ,-OC
nH
2n+1Or-C
nH
2n+1(n=1~12)
X=0~12). organic sulfur compound:
(1) .2.5-dimercaptothiodiazole
(2) .2.2 '-dimercapto ether HSCH
2CH
2OCH
2CH
2SH
(4) .1.2-dithioglycol HSCH
2CH
2SH
(5) .2.2 '-dimercapto ethyl sulfide HSCH
2CH
2SCH
2CH
2SH
(6) .2-mercaptobenzothiazoler
With polyaniline derivative and organic sulfur compound, mol ratio is 1/0.5~1.2, under electromagnetic agitation, be dissolved in the organic solvent, organic solvent comprises oxolane, propene carbonate and N-methyl pyrrolidone, after adding the conductive carbon black of 0~15w%, continue to stir 4~12h, subsequently with mixture supersonic oscillations 2~12h, again mixture is handled 1~6h with colloid mill or in the oscillator that adds bead, the gained mixture evenly is applied to collection liquid surface with the method for printing or cast, collector comprises copper, aluminium, platinum or stainless steel volatilize whole solvents in air, dry in a vacuum again 12~48h.Obtain positive pole (2~20mg/cm
2) have good redox characteristic and a high energy storage density.
The inventive method is simple, can prepare the anode composite of polyaniline derivative and organic sulfur compound under the situation that does not need complex industrial equipment and operational means; The use polyaniline derivative can be better more compound mutually with organic sulfur compound than polyaniline, and reach the interaction of nearly molecular level; The polyaniline derivative that uses part nitrogen to replace has the alkalescence stronger than polyaniline, and organic sulfur compound is had better catalytic action, can obtain than using the higher positive pole of polyaniline catalysis specific energy; Methods such as casting, printing and spraying can be used, and, the positive electrode of all thickness can be obtained by selecting different concentration.
Embodiment provided by the invention is as follows:
Embodiment 1:
N-methyl polyaniline (x=0.79) 0.3g, 2.5-dimercaptothiodiazole 0.37g, mol ratio is 1/0.84, adds successively under condition of stirring in the 5ml N-methyl pyrrolidone, makes mixed solution, adds 0.06g (9.0w%) conductive carbon black, stirs 12h.Said mixture is passed through sonic oscillation 4h again, use milling treatment of colloid 1h again, be applied to the Copper Foil collection liquid surface, in air, use infrared oven dry, and vacuumize 48h.In cyclic voltammetry curve, oxidation peak current and reduction peak current are bigger, oxidation peak and reduction peak spacing 30mv, embody good invertibity and high electro-chemical activity, by oxidation peak or reduction calculated by peak area, N-methyl polyaniline (x=0.79) is 5 times of N-methyl polyaniline (x=0.79) with the specific capacity of 2.5-dimercaptothiodiazole compound, and makes catalyst with polyaniline, and the specific capacity of polyaniline and 2.5-dimercaptothiodiazole compound is 1.9 times of polyaniline.
Embodiment 2;
N-methyl polyaniline (x=0.36) 0.3g, 2.5-dimercaptothiodiazole 0.39g, mol ratio is 1/0.84, under stirring state, add successively in the 5ml N-methyl pyrrolidone, make mixed solution, add 0.06g (8.7w%) conductive carbon black, processing procedure is identical with embodiment 1.In cyclic voltammetry curve, oxidation peak and reduction peak spacing 40mv embody good invertibity and high electro-chemical activity, and by oxidation peak or reduction calculated by peak area, the compound specific capacity is 4.6 times of N-methyl polyaniline (x=0.36).
Embodiment 3:
N-methyl polyaniline (x=0.79) 0.3g, trithiocyanuric acid 0.44g, mol ratio is 1/0.84, under condition of stirring, add in the 5mlN-methyl pyrrolidone successively, make mixed solution, add 0.07g (9.5w%) conductive carbon black, processing procedure is identical with embodiment 1.In cyclic voltammetry curve, oxidation peak and reduction peak spacing 200mv embody good invertibity and high electro-chemical activity, and by oxidation peak or reduction calculated by peak area, the compound specific capacity is 3.2 times of N-methyl polyaniline (x=0.79).
Embodiment 4:
N-methyl polyaniline (x=0.79) 0.3g, poly-2.2 '-dimercapto ether 0.37g, mol ratio is 1/0.92, conductive carbon black 0.06g (8.9w%), add in the 5ml N-methyl pyrrolidone, grind 1h so that evenly in mortar, sonic oscillation is handled 12h, use milling treatment of colloid 6h again, be applied to platinum electrode surface.Infrared oven dry in the air, dry in a vacuum 48h is in cyclic voltammetry curve, oxidation peak and reduction peak spacing 240mv, embody good invertibity, by oxidation peak or reduction calculated by peak area, the compound specific capacity is 1.8 times of N-methyl polyaniline (x=0.79).
Embodiment 5:
N-methyl polyaniline (x=0.79) 0.3g, to diphenyl disulfide phenol 0.38g, mol ratio is 1/0.90, conductive carbon black 0.07g (10w%) adds in the 5ml oxolane, and mixture adds the 6h that vibrates in the bottle that bead is housed, handle 4h with sonic oscillation again, be applied to platinum electrode surface.Oxolane is removed in the normal temperature volatilization in the air, dry 24h in the vacuum in cyclic voltammetry curve, embodies good invertibity and high electro-chemical activity, by oxidation peak or reduction calculated by peak area, the compound specific capacity is 2.5 times of N-methyl polyaniline (x=0.79).
Embodiment 6:
N-methyl polyaniline (x=0.79) 0.3g, 2.2 '-dimercapto ethyl sulfide 0.37g, mol ratio is 1/0.84, the conductive carbon black ratio is identical with embodiment 1, add in the 5ml propene carbonate, the careful 1h that grinds adds bead again and is waving the 2h that vibrates on the oscillator in mortar, sonic oscillation is handled 4h, is applied on the platinum electrode.The normal temperature volatilization removes and sends out carbon elimination acid propylene ester in the air, dry 24h in the vacuum in cyclic voltammetry curve, embodies good invertibity and high electro-chemical activity, by oxidation peak or reduction calculated by peak area, the compound specific capacity is 3.3 times of N-methyl polyaniline (x=0.79).
Embodiment 7:
N-methyl polyaniline (x=0.79), 2-mercaptobenzothiazole, conductive carbon black ratio are identical with embodiment 1, add in the 5ml propene carbonate, and processing procedure is identical with embodiment 6.In cyclic voltammetry curve, embody good invertibity and high electro-chemical activity, by oxidation peak or reduction calculated by peak area, the compound specific capacity is 2 times of N-methyl polyaniline (x=0.79).
Embodiment 8:
N-butyl polyaniline (x=0.70) 0.3g, 1.2-dithioglycol 0.2g, mol ratio is 1/0,92,0.05g (10w%) conductive carbon black adds in the 2ml N-methyl pyrrolidone, the careful 1h that grinds in mortar, said mixture is applied to platinum electrode surface through sonic oscillation 8h.Infrared oven dry in the air, dry in a vacuum 48h is in cyclic voltammetry curve, oxidation peak and reduction peak spacing 40mv, embody good invertibity, by oxidation peak or reduction calculated by peak area, the compound specific capacity is 1.8 times of N-butyl polyaniline (x=0.79).
Embodiment 9:
Adjacent methyl polyaniline 0.3g, 2.5-dimercaptothiodiazole 0.38g, mol ratio is 1/0,90,0.08g (11.8w%) conductive carbon black adds in the 2ml N-methyl pyrrolidone, processing procedure is identical with embodiment 8, in cyclic voltammetry curve, and oxidation peak and reduction peak spacing 200mv, embody good invertibity, by oxidation peak or the reduction calculated by peak area, the compound specific capacity is adjacent methyl polyaniline, 1.5 times.
Embodiment 10:
O-methoxy polyaniline 0.3g, trithiocyanuric acid 0.28g, mol ratio is 1/0,70,0.07 (12w%) conductive carbon black adds in the 2mlN-methyl pyrrolidone, processing procedure is identical with embodiment 8, in cyclic voltammetry curve, oxidation peak and reduction peak spacing 200mv embody good invertibity, by oxidation peak or reduction calculated by peak area, the compound specific capacity is 1.2 times of O-methoxy polyaniline.
Embodiment 11:
N-methyl polyaniline (x=0.79) 0.3g, 2.5-dimercaptothiodiazole 0.48g, mol ratio is 1/1.1, add in the 5mlN-methyl pyrrolidone, processing procedure is identical with embodiment 1, in cyclic voltammetry curve, oxidation peak and reduction peak spacing 40mv, embody good invertibity and high electro-chemical activity, by oxidation peak or reduction calculated by peak area, the compound specific capacity is 2.3 times of N-methyl polyaniline (x=0.79).
Claims (1)
1. the preparation method of a novel all solid lithium secondary battery positive electrode, select polyaniline derivative and organic sulfur compound compound, the method of solution blending and physical mixed is united use, thereby improve the compatibility of catalyst and organic sulfur compound, polyaniline derivative and organic sulfur compound be compound near molecular level more than polyaniline and organic sulfur compound, thereby reach better catalytic effect, concrete structure is as follows:
R
1=-C
nH
2n+1(n=1~12) or-H
R
2=-H ,-Cl ,-OC
nH
2n+1Or-C
nH
2n+1(n=1~12)
X=0~1 organic sulfur compound:
(2) 2.2 '-dimercapto ether HSCH
2CH
2OCH
2CH
2SH
(3) trithiocyanuric acid
(4) 1.2-dithioglycol HSCH
2CH
2SH
(5) 2.2 '-dimercapto ethyl sulfide HSCH
2CH
2SCH
2CH
2SH
(6) 2-mercaptobenzothiazole
(7) to diphenyl disulfide phenol
With polyaniline derivative and organic sulfur compound, mol ratio is 1/0.5~1.2, under electromagnetic agitation, be dissolved in the organic solvent, organic solvent comprises oxolane, propene carbonate, the N-methyl pyrrolidone, after adding the conductive carbon black of 0~15w%, continue to stir 4~12h, subsequently with mixture supersonic oscillations 2~12h, again mixture is handled 1~6h with colloid mill or in the oscillator that adds bead, the gained mixture evenly is applied to collection liquid surface with the method for printing or cast, collector comprises copper, aluminium, platinum or stainless steel volatilize whole solvents in air, dry in a vacuum again 12~48h.