CN117924963A - 含有花青素的植物的花和/或含有叶绿素的植物的叶在制备耐高温色素中的应用 - Google Patents
含有花青素的植物的花和/或含有叶绿素的植物的叶在制备耐高温色素中的应用 Download PDFInfo
- Publication number
- CN117924963A CN117924963A CN202311731685.2A CN202311731685A CN117924963A CN 117924963 A CN117924963 A CN 117924963A CN 202311731685 A CN202311731685 A CN 202311731685A CN 117924963 A CN117924963 A CN 117924963A
- Authority
- CN
- China
- Prior art keywords
- pigment
- resistant
- anthocyanin
- chlorophyll
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供含有花青素的植物的花和/或含有叶绿素的植物的叶在制备耐高温色素中的应用，所述耐高温色素采用含有花青素的植物的花、含有叶绿素的植物的叶制备。本发明提供一种耐高温色素，其原料为天然植物，且可采用植物废弃物，成本低，并且提取剂乙醇对生物体和环境友好，制备的耐高温色素无毒无害、绿色环保、均匀性和稳定性好。且耐高温色素用于绘画颜料，在高温天气下变色不明显，方便保存。
Description
技术领域
本发明涉及生物质材料领域，特别是涉及含有花青素的植物的花和/或含有叶绿素的植物的叶在制备耐高温色素中的应用。
背景技术
木材是一种重要的可再生资源，广泛应用于建筑领域、家具制作、船舶制造、包装材料、艺术品制作，还可作为生物质能源，用于取暖、发电等。随着新材料的种类日益增多，各行各业对材料的需求不断增加，木材作为一种有着漫长使用史的材料，也需要不断开拓新的应用，增加经济价值。
发明内容
鉴于以上所述现有技术的缺点，本发明的目的在于提供含有花青素的植物的花和/或含有叶绿素的植物的叶在制备耐高温色素中的应用，用于解决现有技术中绘画颜料不利于人体健康且高温天气下容易变色的技术问题。
为实现上述目的及其他相关目的，本发明是通过以下技术方案获得的。
本发明提供含有花青素的植物的花和/或含有叶绿素的植物的叶在制备耐高温色素中的应用。
优选地，所述含有花青素的植物为蔷薇科。更优选为玫瑰花。
优选地，所述含有叶绿素的植物选自桑科、木犀科和杨柳科中的一种或多种。更优选地，所述含有叶绿素的植物选自菩提树、丁香树和杨树中的一种或多种。
优选地，所述耐高温色素是指色素耐60℃老化1h。
更优选地，所述色素60℃下老化1h，Lab色度与初始相比差异均小于0.5。
优选地，采用乙醇和/或水作为提取剂提取含有花青素的植物的花和/或含有叶绿素的植物的叶，固液分离处理，蒸干处理。
更优选地，含有花青素的植物的花和/或含有叶绿素的植物的叶在提取前，还进行洗涤处理。
进一步优选地，采用乙醇作为提取剂提取含有叶绿素的植物的叶。
进一步优选地，采用水作为提取剂提取含有花青素的植物的花。
更优选地，提取时，液固比为5～15mL/g。进一步优选为10mL/g。
更优选地，含有叶绿素的植物的叶的提取温度为5～40℃。
更优选地，含有花青素的植物的花的提取温度为5～60℃。
更优选地，所述分离处理包括离心，离心转速为3000-8000r/min。离心的作用为去除大分子杂质。
进一步优选地，离心时间为5min～10min。
更优选地，所述分离处理还包括过滤。
本发明还提供一种提高绘画颜料耐高温性能的方法，为采用含花青素的植物的花和/或含有叶绿素的植物的叶的耐高温色素作为所述绘画颜料的色素来源。
优选地，所述含有花青素的植物为蔷薇科。
优选地，所述含有叶绿素的植物选自桑科、木犀科和杨柳科中的一种或多种。
优选地，所述耐高温色素是指色素耐60℃老化1h。
更优选地，所述色素60℃下老化1h，Lab色度与初始相比差异均小于0.5。
本发明还提供一种耐高温绘画颜料，包含耐高温色素及辅料，所述耐高温色素提取自含花青素的植物的花、和/或含有叶绿素的植物的叶的色素。
优选地，所述含有花青素的植物为蔷薇科。
优选地，所述含有叶绿素的植物选自桑科、木犀科和杨柳科中的一种或多种。
优选地，所述耐高温色素是指色素耐60℃老化1h。
更优选地，所述色素60℃下老化1h，Lab色度与初始相比差异均小于0.5。
优选地，所述辅料为乙醇和/或水。
优选地，所述耐高温色素在耐高温绘画颜料中的质量百分数为0.1～15％。如可以为0.1％、0.112％、0.2％、0.237％、0.5％、0.628％、1.0％、3.0％、5.0％、7.0％、9.0％、11.0％、11.11％。
本发明提供含有花青素的植物的花和/或含有叶绿素的植物的叶在制备耐高温色素中的应用，其原料为天然植物，且可采用植物废弃物，成本低，并且提取剂乙醇对生物体和环境友好，制备的耐高温色素无毒无害、绿色环保、均匀性和稳定性好。且耐高温色素用于绘画颜料，在高温天气下变色不明显，方便保存。
具体实施方式
以下由特定的具体实施例说明本发明的实施方式，熟悉此技术的人士可由本说明书所揭露的内容轻易地了解本发明的其他优点及功效。
在进一步描述本发明具体实施方式之前，应理解，本发明的保护范围不局限于下述特定的具体实施方案；还应当理解，本发明实施例中使用的术语是为了描述特定的具体实施方案，而不是为了限制本发明的保护范围。下列实施例中未注明具体条件的试验方法，通常按照常规条件，或者按照各制造商所建议的条件。
当实施例给出数值范围时，应理解，除非本发明另有说明，每个数值范围的两个端点以及两个端点之间任何一个数值均可选用。除非另外定义，本发明中使用的所有技术和科学术语与本技术领域技术人员通常理解的意义相同。除实施例中使用的具体方法、设备、材料外，根据本技术领域的技术人员对现有技术的掌握及本发明的记载，还可以使用与本发明实施例中所述的方法、设备、材料相似或等同的现有技术的任何方法、设备和材料来实现本发明。
本申请申请人提供一种新型耐高温色素，其从特定的天然植物中提取出天然色素成分，可用于木材染料、树叶染料和绘画颜料，其属于天然色素，具有环保特性，而且耐高温色素本身在高温条件下具有稳定性，不容易变色；将其作为绘画颜料绘于纸张上，形成的画作也经得起高温，不容易变化。
实施例1
本实施例提供一种具体的耐高温色素，制备方法如下：
取菩提树叶若干片，用去离子水将其表面冲洗干净，并洗涤至中性，将叶片剪碎，加入无水乙醇至液面完全浸没叶片表面，室温25℃下静置，当叶片变黄后，过滤，并将滤液离心处理，离心转速为8000r/min，离心时间为10min，取上清液，在40℃温度下蒸干，获得耐高温色素。
本实施例还提供一种具体的耐高温绘画颜料，制备方法如下：将0.05g耐高温色素中加入7.91g无水乙醇，完全溶解，获得耐高温绘画颜料。耐高温绘画颜料中耐高温色素的质量百分数为0.628％。
实施例2
本实施例提供一种具体的耐高温色素，制备方法与实施例1相同。
本实施例还提供一种具体的耐高温绘画颜料，制备方法与实施例1基本相同，不同之处仅在于：耐高温绘画颜料中无水乙醇的质量为0.4g。耐高温绘画颜料中耐高温色素的质量百分数为11.11％。
实施例3
本实施例提供一种具体的耐高温色素，制备方法与实施例1相同。
本实施例还提供一种具体的耐高温绘画颜料，制备方法与实施例1基本相同，不同之处仅在于：耐高温绘画颜料中无水乙醇的质量为21.05g。耐高温绘画颜料中耐高温色素的质量百分数为0.237％。
实施例4
本实施例提供一种具体的耐高温色素，制备方法与实施例1相同。
本实施例还提供一种具体的耐高温绘画颜料，制备方法与实施例1基本相同，不同之处仅在于：耐高温绘画颜料中无水乙醇的质量为44.5g。耐高温绘画颜料中耐高温色素的质量百分数为0.112％。
实施例5
本实施例提供一种具体的耐高温色素，制备方法与实施例1基本相同，不同之处仅在于：离心转速为5000r/min。
本实施例还提供一种具体的耐高温绘画颜料，制备方法与实施例1相同。
实施例6
本实施例提供一种具体的耐高温色素，制备方法与实施例1基本相同，不同之处仅在于：离心转速为3000r/min。
本实施例还提供一种具体的耐高温绘画颜料，制备方法与实施例1相同。
实施例7
本实施例提供一种具体的耐高温色素，制备方法如下：
取若干玫瑰花瓣，用去离子水将其表面冲洗干净，并洗涤至中性，放入去离子水至液面完全浸没花瓣，室温25℃下静置，当玫瑰花瓣的颜色全部退去时，过滤，滤液离心处理，离心转速为8000r/min，离心时间为10min，取上清液，在40℃温度下蒸干，获得耐高温色素。
本实施例提供一种具体的耐高温绘画颜料，制备方法如下：
将0.05g天然色素中加入7.91g水，混合均匀，获得耐高温绘画颜料。耐高温绘画颜料中耐高温色素的质量百分数为0.628％。
实施例8
本实施例提供一种具体的耐高温色素，制备方法与实施例7基本相同，不同之处仅在于：提取时，静置温度为60℃。
实施例9
本实施例提供一种具体的耐高温色素，制备方法与实施例7基本相同，不同之处仅在于：提取时，静置温度为40℃。
对比例1
将0.125g丙烯颜料(含量40％，ARTSIR艺先生无甲醛丙烯画颜料(黄绿)，购入厂家：河北青竹画材科技有限公司)中加入7.835g去离子水，完全溶解，获得丙烯颜料液。
对比例2
将0.125g丙烯颜料(含量40％，ARTSIR艺先生无甲醛丙烯画颜料(紫色)，购入厂家：河北青竹画材科技有限公司)中加入7.835g去离子水，完全溶解，获得丙烯颜料液。
对实施例1、7制备的耐高温绘画颜料和对比例1、2制备的丙烯颜料液，进行色度测试。测试方法如下：
分别将实施例1、11制备的耐高温绘画颜料和对比例1、2制备的丙烯颜料液用毛笔在纸上画一条线，待完全干透后，使用色度计(厂家为NIPPON DENSHOKU，型号为ND120)对其颜色数值进行测试，记录材色数据；然后将纸放入鼓风干燥箱中60℃高温处理1小时，拿出恢复室温25℃后，再使用色度计测试其颜色数据。对比两次实验的材色数据，数据差异越大，说明其变色越明显。
表1
说明：其中L*表示亮度，a*表示红绿，b*表示黄蓝
上述实施例仅例示性说明本发明的原理及其功效，而非用于限制本发明。任何熟悉此技术的人士皆可在不违背本发明的精神及范畴下，对上述实施例进行修饰或改变。因此，举凡所属技术领域中具有通常知识者在未脱离本发明所揭示的精神与技术思想下所完成的一切等效修饰或改变，仍应由本发明的权利要求所涵盖。
Claims (10)
1.含有花青素的植物的花和/或含有叶绿素的植物的叶在制备耐高温色素中的应用。
2.根据权利要求1所述的应用，其特征在于，所述含有花青素的植物为蔷薇科；
和/或，所述含有叶绿素的植物选自桑科、木犀科和杨柳科中的一种或多种；
和/或，所述耐高温色素是指色素耐60℃老化1h。
3.根据权利要求2所述的应用，其特征在于，所述色素60℃下老化1h，Lab色度与初始相比差异均小于0.5。
4.一种提高绘画颜料耐高温性能的方法，为采用含花青素的植物的花和/或含有叶绿素的植物的叶的耐高温色素作为所述绘画颜料的色素来源。
5.根据权利要求4所述的方法，其特征在于，所述含有花青素的植物选自蔷薇科；
和/或，所述含有叶绿素的植物选自桑科、木犀科和杨柳科中的一种或多种；
和/或，所述耐高温色素是指色素耐60℃老化1h。
6.根据权利要求5所述的方法，其特征在于，所述色素60℃下老化1h，Lab色度与初始相比差异均小于0.5。
7.一种耐高温绘画颜料，其特征在于，包含耐高温色素及辅料，所述耐高温色素提取自含花青素的植物的花和/或含有叶绿素的植物的叶的色素。
8.根据权利要求7所述的耐高温绘画颜料，其特征在于，所述含有花青素的植物为蔷薇科；
和/或，所述含有叶绿素的植物选自桑科、木犀科和杨柳科中的一种或多种；
和/或，所述耐高温色素是指色素耐60℃老化1h。
9.根据权利要求8所述的耐高温绘画颜料，其特征在于，所述色素60℃下老化1h，Lab色度与初始相比差异均小于0.5。
10.根据权利要求8所述的耐高温绘画颜料，其特征在于，所述辅料为乙醇和/或水；
和/或，所述耐高温色素在耐高温绘画颜料中的质量百分数为0.1～15％。