CN117813273A - 包含细填料和细粒化高炉矿渣粉的粘合剂组合物 - Google Patents
包含细填料和细粒化高炉矿渣粉的粘合剂组合物 Download PDFInfo
- Publication number
- CN117813273A CN117813273A CN202280031862.3A CN202280031862A CN117813273A CN 117813273 A CN117813273 A CN 117813273A CN 202280031862 A CN202280031862 A CN 202280031862A CN 117813273 A CN117813273 A CN 117813273A
- Authority
- CN
- China
- Prior art keywords
- mortars
- weight
- relative
- adhesive composition
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
上述目的的实现得益于一种粘合剂组合物,其包含:a.干重为1%至30%的至少一种石灰源;b.干重为5%至75%的粒化高炉矿渣粉;c.干重为20%至90%的至少一种填料;d.相对于组分a、b和c的总重量,干重为0.1%至5%的SO3 ‑;e.相对于组分a、b和c的总重量,干重为0.1%至1%的至少一种减水剂聚合物;f.相对于组分a、b和c的总重量,干重为0%至2%的至少一种不同于d的活化剂;所述粒化高炉矿渣粉是以下物质的颗粒混合物:‑相对于粒化高炉矿渣粉的总重量,10重量%至100重量%的d50大于或等于1μm且严格小于5μm的颗粒,‑相对于粒化高炉矿渣粉的总重量,0重量%至90重量%的d50大于或等于5μm且优选小于15μm的颗粒,所述填料是以下物质的颗粒混合物:‑相对于填料的总重量,10重量%至90重量%的d50大于或等于0.05μm且严格小于8μm的颗粒,和‑相对于填料的总重量,10重量%至90重量%的d50大于或等于8μm且严格小于200μm的颗粒。
Description
技术领域
本公开属于用于制备混凝土或工业砂浆的粘合剂组合物领域。本发明的技术领域涉及包含至少一种矿渣例如粒化高炉矿渣粉(Ground Granulated Blast furnace Slag,GGBS或矿渣)的水硬性矿物粘合剂,其用于能够凝固和硬化的组合物,例如砂浆或混凝土组合物。
更具体地,本发明涉及用于建筑工业的能够凝固和硬化的粘合剂和组合物,其包含至少一种作为水硬性粘合剂的矿渣(其一部分是超细的)和细石灰石填料。
本发明还涉及制备这些基于矿渣的粘合剂、这些能够凝固和硬化的干或湿组合物的方法。
由从这些组合物获得的凝固和硬化的产品制成的建筑应用也在本发明的领域中。
背景技术
由于大量二氧化碳的排放,硅酸盐水泥的生产对环境造成了强烈的负面影响。在窑内以非常高的温度(1450℃)煅烧原料、通过石灰石的脱二氧化碳的过程中,生产水泥本身就会产生CO2(方程式(1)):
CaCO3(s)→CaO(s)+CO2(g)(方程式(1))
此外,加热水泥窑所需的化石燃料燃烧时会释放二氧化碳。再加上研磨的额外排放量,每吨硅酸盐水泥几乎产生一吨CO2。总体而言,水泥行业约占全球二氧化碳排放量的7%至9%。
此外,特别由于其高碱度(pH高于13),处理硅酸盐水泥可能会导致健康问题(例如过敏)。此外,捏合过程中可能会释放六价铬(Cr(VI))等有害元素,如果接触到皮肤,其也会损害工人的健康。尽管水泥粉末中通常包含Cr(VI)还原剂(如硫酸亚铁),但其效率在时间上是有限的。建筑工人、特别是第三世界的建筑工人,不会经常检查与此类处理相关的最后期限。
目前对新型粘合剂的研究大多旨在用对环境影响较小的粘合剂替代各种应用中的水泥。一种途径是使用无需昂贵处理的资源,例如来自其他行业的副产品(对某一行业而言是废物,但对其他行业而言是主要资源)。高炉矿渣就是实例,其是钢铁工业的副产品。通过将该产品研磨成细粉(GGBS),即可获得一种胶结材料,其可部分替代水泥使用,也可通过添加一些化学活化剂单独使用。
值得注意的是,使用GGBS不仅环保,而且在用于配制砂浆和混凝土时还具有多种增强的特性,例如高抗硫酸盐侵蚀性、低渗透性、在化学侵蚀性环境中的良好抗性、低水化热(大体积结构所需的)、总体上优异的耐久性、重金属或放射性核素固定化的可能性等。
在此背景下,本发明旨在通过实现以下目的中的至少一个来解决上述问题和/或需求中的至少一个:
-O1-提供一种基于矿渣的粘合剂或包含所述基于矿渣的粘合剂的砂浆或混凝土组合物,其是基于普通硅酸盐水泥(Ordinary Portland Cement,OPC)的组合物的有吸引力的替代品。
-O2-提供一种环境友好的基于矿渣的粘合剂或包含所述基于矿渣的粘合剂的砂浆或混凝土组合物。
-O3-提供一种基于矿渣的粘合剂或包含所述基于矿渣的粘合剂的砂浆或混凝土组合物,其在健康和安全问题方面比基于OPC的组合物更可接受。
-O4-提供一种基于矿渣的粘合剂或包含所述基于矿渣的粘合剂的砂浆或混凝土组合物,其产生具有通过多种方式(如振动压实、喷涂、抹平、浇铸等)制造的适当能力的干砂浆、干和半干预制混凝土以及湿砂浆和混凝土制剂。
-O5-提供一种基于矿渣的粘合剂或包含所述基于矿渣的粘合剂的砂浆或混凝土组合物,其产生具有适当的流变特性的湿制剂,即在所述湿制剂使用者所需的通常凝固时间(例如几分钟至几小时)内稳定的流变性(良好的和易性)。
-O6-提供一种基于矿渣的粘合剂或包含所述基于矿渣的粘合剂的砂浆或混凝土组合物,其产生具有所需机械特性、特别是可接受的早期强度(例如24小时)的硬化材料。
-O7-提供一种基于矿渣的粘合剂或包含所述基于矿渣的粘合剂的砂浆或混凝土组合物,其产生具有所需耐久性的硬化材料。
-O8-提供一种基于矿渣的粘合剂或包含所述基于GGBS的粘合剂的砂浆或混凝土组合物,其产生具有通常所需的凝固时间(例如,几分钟至几个小时)的硬化材料。
-O9-提供一种制备基于矿渣的粘合剂或包含所述基于矿渣的粘合剂的砂浆或混凝土组合物的简单且廉价的方法,其符合目的-O1-至-O9-中的至少一个。
-O10-提供一种制备湿形式的基于矿渣的粘合剂或包含所述基于矿渣的粘合剂的砂浆或混凝土组合物的简单且廉价的方法。
-O11-提供用于建筑工业的硬化产品,其包含矿渣作为至少部分的粘合剂。
发明内容
上述目的的实现得益于一种粘合剂组合物,其包含:
a.干重为1%至30%的至少一种石灰源;
b.干重为5%至75%的粒化高炉矿渣粉(ground granulated blast furnaceslag);
c.干重为20%至90%的至少一种填料;
d.相对于组分a、b和c的总重量,干重为0.1%至5%的SO3 -;
e.相对于组分a、b和c的总重量,干重为0.1%至1%的至少一种减水剂聚合物;
f.相对于组分a、b和c的总重量,干重为0%至2%的至少一种不同于d的活化剂;
所述粒化高炉矿渣粉是以下物质的颗粒混合物:
-相对于粒化高炉矿渣粉的总重量,10重量%至100重量%的d50大于或等于1μm且严格小于5μm的颗粒,
-相对于粒化高炉矿渣粉的总重量,0重量%至90重量%的d50大于或等于5μm且优选小于15μm的颗粒,
所述填料是以下物质的颗粒混合物:
-相对于填料的总重量,10重量%至90重量%的d50大于或等于0.05μm且严格小于8μm的颗粒,和
-相对于填料的总重量,10重量%至90重量%的d50大于或等于8μm且严格小于200μm的颗粒。
本发明还涉及一种干混凝土组合物或干工业砂浆组合物,特别是瓷砖粘合剂、涂料、组装砂浆、修补砂浆、泥灰、技术砂浆和用于地板覆盖物的砂浆,其包含至少一种骨料和上述的粘合剂组合物。
本发明还涉及一种湿混凝土组合物或湿工业砂浆组合物,特别是瓷砖粘合剂、涂料、组装砂浆、修补砂浆、泥灰、技术砂浆和用于地板覆盖物的砂浆,其包含至少一种骨料、上述的粘合剂组合物和水。
此外,本发明涉及一种由上述的湿混凝土组合物或湿工业砂浆组合物获得的硬化的混凝土组合物或硬化的工业砂浆组合物。
此外,本发明涉及一种用于制备如上所述的湿混凝土组合物或湿工业砂浆组合物的方法,其包括将水、至少一种骨料和如上所述的粘合剂组合物混合的步骤,该粘合剂组合物在混合步骤之前或在混合步骤期间原位由单独和/或以预混物形式获得的粘合剂组合物的至少一些不同的组分制备。
本发明涉及一种如上所述的粘合剂组合物用于改善湿混凝土组合物或湿工业砂浆组合物(特别是瓷砖粘合剂、涂料、组装砂浆、修补砂浆、泥灰、技术砂浆和用于地板覆盖物的砂浆)的新鲜状态流变性的用途。
定义
根据本文的术语,必须考虑以下非限制性定义:
“矿渣”是指在矿石熔炼或精炼过程中从金属中分离出的石质副产品物质。
“GGBS”或“GGBFS”:粒化高炉矿渣粉(Ground Granulated Blast Furnace Slag),其等同于高炉矿渣、粒化高炉矿渣(Granulated Blast Furnace Slag,GBFS)、高炉水碎矿渣粉和高炉矿渣细骨料。
“水泥”被理解为是指用于制造砂浆或混凝土的粉末状物质。其是一种矿物粘合剂,可能不含任何有机化合物。其是指任何普通水泥,包括矿渣硅酸盐混合水泥和基于碱激发的水泥。
“粘合剂”是指“水硬性粘合剂”,指任何通过仅加水即可硬化的材料,如GGBS和水泥。
“砂浆”是指由粘合剂、骨料(例如沙子)以及其他组分(例如掺合料)组成的材料。
“混凝土”是指由粘合剂、骨料(例如沙子和砾石)以及其他组分(例如掺合料)组成的材料。
“d50”给出了材料颗粒的粒度分布的中值粒径(对于胶结材料通常以微米为单位)。这意味着50%的颗粒尺寸小于指定数目,50%的颗粒尺寸大于给定数目。d50的测量通过激光衍射分析(也称为激光衍射光谱法)、使用例如由MALVERN公司商业化的“Mastersizer2000”激光衍射分析仪、以湿法进行。
具体实施方式
粘合剂组合物
根据本发明的粘合剂组合物包含:
a.干重为1%至30%的至少一种石灰源;
b.干重为5%至75%的粒化高炉矿渣粉;
c.干重为20%至90%的至少一种填料;
d.相对于组分a、b和c的总重量,干重为0.1%至5%的SO3 -;
e.相对于组分a、b和c的总重量,干重为0.1%至1%的至少一种减水剂聚合物;
f.相对于组分a、b和c的总重量,干重为0%至2%的至少一种不同于d的活化剂;
所述粒化高炉矿渣粉是以下物质的颗粒混合物:
-相对于粒化高炉矿渣粉的总重量,10重量%至100重量%的d50大于或等于1μm且严格小于5μm的颗粒,
-相对于粒化高炉矿渣粉的总重量,0重量%至90重量%的d50大于或等于5μm且优选地小于15μm的颗粒,
所述填料是以下物质的颗粒混合物:
-相对于填料的总重量,10重量%至90重量%的d50大于或等于0.05μm且严格小于8μm的颗粒,和
-相对于填料的总重量,10重量%至90重量%的d50大于或等于8μm且严格小于200μm的颗粒。
组分a
根据本发明的粘合剂组合物包含干重为1%至30%、优选3%至25%、更优选5%至20%的组分a,其为石灰源。
优选地,石灰源是硅酸盐水泥或石灰,例如水硬性石灰、氢氧化钙、熟石灰、生石灰和石灰浆。
在石灰源是硅酸盐水泥的情况下,有利的是,其至少一部分是d50小于或等于8μm、优选小于或等于3.5μm的超细水泥。该实施方式是有利的,因为与其他实施方式相比,其能够获得增加的抗压强度。
组分b
根据本发明的粘合剂组合物包含干重为5%至75%、优选10%至65%、更优选15%至50%、甚至更优选20%和40%的组分b,其为粒化高炉矿渣粉(GGBS)。
根据本发明,至少一部分粒化高炉矿渣粉是超细的,即由d50大于或等于1μm且严格小于5μm的颗粒制成。
在一些实施方式中,所述粒化高炉矿渣粉是以下物质的颗粒混合物:
-相对于粒化高炉矿渣粉的总重量,20重量%至90重量%、优选30重量%至80重量%、更优选40重量%至65重量%的d50大于或等于1μm且严格小于5μm的颗粒,
-相对于粒化高炉矿渣粉的总重量,0重量%至90重量%、优选20重量%至70重量%、更优选35重量%至60重量%的d50大于或等于5μm且优选小于15μm的颗粒。
组分c
根据本发明的粘合剂组合物包含干重为20%至90%、优选30%至80%、更优选40%至70%、甚至更优选50%至60%的组分c,其为填料。
填料是一种细颗粒状的惰性无机材料。换言之,填料在水的存在下无法与石灰或水泥反应而产生水合物。
优选地,填料是石灰石填料,更优选地,填料是源自石坑的天然材料,例如方解石及其多晶型物,如文石或球霰石,以及白云石或沉淀碳酸钙及其混合物。
根据本发明,填料是以下物质的颗粒混合物:
-相对于填料的总重量,10重量%至90重量%的d50大于或等于0.05μm且严格小于8μm的颗粒,和
-相对于填料的总重量,10重量%至90重量%的d50大于或等于8μm且严格小于200μm的颗粒。
这种填料分隔,与GGBS分隔组合,能够获得降低根据本发明的粘合剂组合物和混凝土或工业砂浆的粘度并增加其抗压强度的技术效果。
在一些实施方式中,填料是以下物质的颗粒混合物:
-相对于填料的总重量,20重量%至80重量%、优选25重量%至50重量%、更优选30重量%至40重量%的d50大于或等于0.05μm且严格小于8μm的颗粒,和
-相对于填料的总重量,20重量%至80重量%,优选30重量%至70重量%,更优选40重量%至65重量%的d50大于或等于8μm且严格小于200μm的颗粒。
组分d
根据本发明,粘合剂组合物还包含相对于组分a、b和c的总重量,干重为0.1%至5%的SO3 -。
SO3 -的含量根据组分a、b和c的分配来确定。换言之,SO3 -的干重百分比通过考虑组分a、b和c的含量之和代表100%的干重来确定。
优选地,SO3 -来自硫酸钠、硫酸钾、硫酸钙、硫酸酐、再生石膏或其混合物。
组分e
根据本发明,粘合剂组合物还包含相对于组分a、b和c的总重量,干重为0.1%至1%的至少一种减水剂聚合物。
减水剂聚合物的含量根据组分a、b和c的分配来确定。换言之,减水剂聚合物的干重百分比通过考虑组分a、b和c的含量之和代表100%的干重来确定。
优选地,减水剂聚合物选自由以下组成的组:木质素磺酸盐聚合物、三聚氰胺磺酸盐聚合物、萘磺酸盐聚合物、聚羧酸醚聚合物、聚氧乙烯膦酸酯、乙烯基共聚物及其混合物。
组分f
根据本发明,粘合剂组合物还包含相对于组分a、b和c的总重量,干重为0%至2%的至少一种不同于d的活化剂。
不同于d的活化剂的含量根据组分a、b和c的分配来确定。换言之,活化剂的干重百分比通过考虑组分a、b和c的含量之和代表100%的干重来确定。
优选地,不同于d的活化剂是碱金属盐,优选氯化钠、氯化钾、氯化锂、碳酸钠、碳酸钾、碳酸锂、硝酸钙、硝酸钠、硝酸钾、硝酸锂、亚硝酸钠、亚硝酸钾,亚硝酸锂、亚硝酸钙、硫氰酸钠、硫氰酸钾、硫氰酸锂、链烷醇胺例如三乙醇胺(TEA)、三异丙醇胺(TIPA)、二乙醇胺(DEA)或其混合物,优选硝酸钙。
任选的其他组分
粘合剂组合物有利地富含一种或多种其他组分,这些组分是优选地选自以下列表的成分,特别是功能添加剂:
·保水剂
保水剂具有在凝固之前保留混合水的特性。水被保留在湿制剂浆料中,从而提高其粘合力。在某种程度上,载体对水的吸收较少。
保水剂优选地选自包含以下的组:改性纤维素、改性瓜尔豆胶、改性纤维素醚和/或瓜尔豆胶醚以及其混合物,更优选地选自由以下组成的组:甲基纤维素、甲基羟丙基纤维素、甲基羟乙基纤维素及其混合物。
·流变剂
可能的流变剂(也称为“增稠剂”)优选地选自包含以下、更优选地由以下组成的组:淀粉醚、纤维素醚和/或树胶(例如Welan瓜尔豆胶黄原胶、琥珀酰聚糖)、改性多糖(优选改性淀粉醚)、聚乙烯醇、聚丙烯酰胺、海泡石及其混合物。
·除泡剂/消泡剂
可能的除泡剂优选地选自包含以下、更优选地由以下组成的组:聚醚多元醇及其混合物。
·杀生物剂
可能的杀生物剂优选地选自包含以下、更优选地由以下组成的组:矿物氧化物如氧化锌及其混合物。
·颜料
可能的颜料优选地选自包含以下、更优选地由以下组成的组:TiO2、氧化铁及其混合物。
·阻燃剂
阻燃剂(或防燃剂)使得可以提高组合物的耐火性和/或降低组合物的火焰蔓延速度。
·加气剂(Air-entraining agent)
加气剂(表面活性剂)有利地选自包含以下、更优选地由以下组成的组:天然树脂、硫酸化或磺化的化合物、合成洗涤剂、有机脂肪酸及其混合物,优选地选自包含以下、更优选地由以下组成的组:木质素磺酸盐、脂肪酸的碱性皂及其混合物,并且更优选地选自包含以下、更优选地由以下组成的组:烯烃磺酸盐、十二烷基硫酸钠及其混合物。
·缓凝剂
缓凝剂有利地选自包含以下、更优选地由以下组成的组:酒石酸及其盐:钠盐或钾盐;柠檬酸及其盐:钠盐(柠檬酸三钠)及其混合物。
此外,其他组分可以是:
·增塑剂
·纤维
·分散粉末
·润湿剂
·聚合树脂
·络合剂
·基于多元醇的干燥减缩剂。
粘合剂组合物中这些任选的其他组分的总含量优选地为粘合剂组合物总重量的0.001重量%至10重量%。
干混凝土组合物或干工业砂浆组合物
本发明还涉及干混凝土组合物或干工业砂浆组合物,特别是瓷砖粘合剂、涂料、组装砂浆、修补砂浆、泥灰、技术砂浆和用于地板覆盖物的砂浆,其包含至少一种骨料和上述的粘合剂组合物。干混凝土或工业砂浆组合物最终可以含有其他掺合料和添加剂。
根据本发明,“干”混凝土组合物或“干”工业砂浆组合物是指呈粉末形式且准备与水混合的组合物。换言之,本发明的干混凝土组合物或干工业砂浆组合物可以含有一些水分,但其基本上包含旨在在其应用前与水混合的固体组分。
骨料包括建筑中使用的一大类颗粒材料,包括沙子、砾石、碎石、矿渣(非粒状)、再生混凝土和土工合成骨料。它们起到强化作用,增加整体复合材料的强度。
有利地,所述干混凝土组合物或干工业砂浆组合物除骨料之外还可以包含一种或多种成分,特别是功能性掺合料、添加剂和纤维,其可以与上述在粘合剂组合物的详细描述中定义的其他任选组分相同。
干混凝土组合物或干工业砂浆组合物中这些任选的其他组分的总含量优选地为粘合剂组合物总重量的0.1重量%至10重量%。
湿混凝土组合物或湿工业砂浆组合物
本发明还涉及一种湿混凝土组合物或湿工业砂浆组合物,特别是瓷砖粘合剂、涂料、组装砂浆、修补砂浆、泥灰(renders)、技术砂浆和用于地板覆盖物的砂浆,其包含至少一种骨料、上述粘合剂组合物和水。
在一个具体的实施方式中,湿砂浆组合物是所谓的“即用型”砂浆。“即用型”砂浆用于在建筑工地上组装砖块或砌块。它们是通过在搅拌站直接将组合物的所有元素(粘合剂、骨料和其他组分)与水混合而获得的。它们包含缓凝剂,允许运输和延迟使用长达数天,同时保持其流变和硬化特性。
用于制备湿混凝土组合物或湿砂浆组合物的方法
本发明还涉及一种用于制备上述湿混凝土组合物或湿工业砂浆组合物的方法,该方法包括将至少一种骨料和上述的粘合剂组合物与水混合的步骤,该粘合剂组合物在混合步骤之前或在混合步骤期间原位由单独和/或以预混物形式获得的粘合剂组合物的至少一些不同的组分制备。
换言之,湿混凝土组合物或湿工业砂浆组合物可以通过两种不同的方法制备。
在第一种方法中,制备粘合剂组合物,然后将其与至少一种骨料混合。此后将干混凝土组合物或干砂浆组合物与水混合。
在第二种方法中,通过在水中混合粘合剂组合物的各组分和骨料来制备湿混凝土组合物或湿工业砂浆组合物。
根据本公开,术语“混合”必须被理解为任何形式的混合。
在一个优选的实施方式中,在与骨料混合之前将一部分粘合剂组合物和至少一部分水混合在一起。
在一个优选的实施方式中,以水与粘合剂组合物的比例为0.1至0.5、有利地为0.15至0.45、更有利地为0.2至0.4来实施该方法。
硬化的混凝土组合物或硬化的工业砂浆组合物
本发明还涉及由上述湿混凝土组合物或湿工业砂浆组合物获得的硬化的混凝土组合物或硬化的工业砂浆组合物。
粘合剂组合物的用途
本发明还涉及上述粘合剂组合物用于改善湿混凝土组合物或湿工业砂浆组合物(特别是瓷砖粘合剂、涂料、组装砂浆、修补砂浆、泥灰、技术砂浆和用于地板覆盖物的砂浆)的新鲜状态流变性的用途。
有利地,对于根据本发明的用途,浆料新鲜状态的屈服应力为0帕(Pa)至200Pa、有利地为5Pa至100Pa、并且更有利地为10Pa至50Pa。
有利地,对于根据本发明的用途,浆料新鲜状态的粘度为0Pa.s至5帕秒(Pa.s)、有利地为0.1Pa.s至3Pa.s、并且更有利地为0.25Pa.s至1.5Pa.s。
本发明还涉及上述粘合剂组合物用于制备预制混凝土或预拌混凝土的用途。
实施例
实施例1:填料颗粒与GGBS颗粒粒度分布的协同效应
根据标准NF EN 196-1,按照混合方案和试样尺寸制备四种砂浆。根据标准NF EN196-1确定这些砂浆的抗压强度。组成和抗压强度列于下表1中。
表1
从表1可以看出,含有标准石灰石填料和标准GGBS(CE1)的砂浆的抗压强度低于包含超细石灰石填料(CE2)或超细GGBS(CE3)的砂浆。超细石灰石填料和超细GGBS(E1)的复合砂浆的抗压强度大于CE2和CE3的砂浆,表明超细石灰石填料和超细GGBS的组合具有协同效应。
实施例2:超细GGBS的量的影响
根据标准NF EN 196-1,按照混合方案和试样尺寸制备另一种砂浆。根据标准NFEN 196-1确定该砂浆的抗压强度。组成和抗压强度列于下表2中,其中再现了实施例E1。
表2
从表2可以看出,包含较多超细GGBS的砂浆E2的抗压强度大于砂浆E1的抗压强度。
实施例3:超细水泥的效果
根据标准NF EN 196-1制备另外五种砂浆。根据标准NF EN 196-1确定这些砂浆24小时后的抗压强度。组成和抗压强度列于下表3中,其中再现了实施例E1。
表3
从表3中可以看出,尽管用超细硅酸盐水泥(E3)替代约13重量%的标准硅酸盐水泥时微不足道的降低,但可以得出结论,根据本发明的砂浆的抗压强度随着用超细硅酸盐水泥代替标准硅酸盐水泥的比例的增加而增加。
Claims (15)
1.一种粘合剂组合物,所述粘合剂组合物包含:
a.干重为1%至30%的至少一种石灰源;
b.干重为5%至75%的粒化高炉矿渣粉;
c.干重为20%至90%的至少一种填料;
d.相对于所述组分a、b和c的总重量,干重为0.1%至5%的SO3 -;
e.相对于所述组分a、b和c的总重量,干重为0.1%至1%的至少一种减水剂聚合物;
f.相对于所述组分a、b和c的总重量,干重为0%至2%的至少一种不同于d的活化剂;
所述粒化高炉矿渣粉是以下物质的颗粒混合物:
-相对于所述粒化高炉矿渣粉的总重量,10重量%至100重量%的d50大于或等于1μm且严格小于5μm的颗粒,
-相对于所述粒化高炉矿渣粉的总重量,0重量%至90重量%的d50大于或等于5μm且优选小于15μm的颗粒,
所述填料是以下物质的颗粒混合物:
-相对于所述填料的总重量,10重量%至90重量%的d50大于或等于0.05μm且严格小于8μm的颗粒,和
-相对于所述填料的总重量,10重量%至90重量%的d50大于或等于8μm且严格小于200μm的颗粒,
d50的测量通过激光衍射分析,也称为激光衍射光谱法、使用例如由MALVERN公司商业化的“Mastersizer 2000”激光衍射分析仪、以湿法进行。
2.根据权利要求1所述的粘合剂组合物,其中所述石灰源是硅酸盐水泥或石灰,例如水硬石灰、氢氧化钙、熟石灰、生石灰和石灰浆。
3.根据前述权利要求中任一项所述的粘合剂组合物,其中所述石灰源是硅酸盐水泥,其至少一部分是d50小于或等于8μm、优选小于或等于3.5μm的超细水泥,
d50的测量通过激光衍射分析,也称为激光衍射光谱法、使用例如由MALVERN公司商业化的“Mastersizer 2000”激光衍射分析仪、以湿法进行。
4.根据前述权利要求中任一项所述的粘合剂组合物,其中所述填料是源自石坑的天然材料,例如方解石及其多晶型物,如文石或球霰石,以及白云石或沉淀碳酸钙及它们的混合物。
5.根据前述权利要求中任一项所述的粘合剂组合物,其中所述SO3 -来自硫酸钠、硫酸钾、硫酸钙、硫酸酐、再生石膏或它们的混合物。
6.根据前述权利要求中任一项所述的粘合剂组合物,其中所述减水剂聚合物选自由以下组成的组:木质素磺酸盐聚合物、三聚氰胺磺酸盐聚合物、萘磺酸盐聚合物、聚羧酸醚聚合物、聚氧乙烯膦酸酯、乙烯基共聚物及它们的混合物。
7.根据前述权利要求中任一项所述的粘合剂组合物,其中所述不同于d的活化剂是碱金属盐,优选氯化钠、氯化钾、氯化锂、碳酸钠、碳酸钾、碳酸锂、硝酸钙、硝酸钠、硝酸钾、硝酸锂、亚硝酸钠、亚硝酸钾、亚硝酸锂、亚硝酸钙、硫氰酸钠、硫氰酸钾、硫氰酸锂、链烷醇胺如三乙醇胺(TEA)、三异丙醇胺(TIPA)、二乙醇胺(DEA)或它们的混合物,优选硝酸钙。
8.一种干混凝土组合物或干工业砂浆组合物,特别是瓷砖粘合剂、涂料、组装砂浆、修补砂浆、泥灰、技术砂浆和用于地板覆盖物的砂浆,其包含至少一种骨料和根据权利要求1至7中任一项所述的粘合剂组合物。
9.一种湿混凝土组合物或湿工业砂浆组合物,特别是瓷砖粘合剂、涂料、组装砂浆、修补砂浆、泥灰、技术砂浆和用于地板覆盖物的砂浆,其包含至少一种骨料、根据权利要求1至7中任一项所述的粘合剂组合物和水。
10.一种由根据权利要求9所述的湿混凝土组合物或湿工业砂浆组合物获得的硬化的混凝土组合物或硬化的工业砂浆组合物。
11.一种用于制备根据权利要求9所述的湿混凝土组合物或湿工业砂浆组合物的方法,包括将水、至少一种骨料和根据权利要求1至7中任一项所述的粘合剂组合物混合的步骤,所述粘合剂组合物在所述混合步骤之前或在所述混合步骤期间原位由单独和/或以预混物形式获得的所述粘合剂组合物的至少一些不同的组分制备。
12.根据权利要求11所述的方法,其中水与粘合剂组合物的比例为0.1至0.5、有利地为0.15至0.45、并且更有利地为0.2至0.4。
13.根据权利要求1至7中任一项所述的粘合剂组合物用于制备预制混凝土或预拌混凝土或者用于改善湿混凝土组合物或湿工业砂浆组合物,特别是瓷砖粘合剂、涂料、组装砂浆、修补砂浆、泥灰、技术砂浆和用于地板覆盖物的砂浆的新鲜状态流变性的用途。
14.根据权利要求13所述的粘合剂组合物的用途,其中浆料的新鲜状态屈服应力为0帕至200帕、有利地为5帕至100帕、更有利地为10帕至50帕。
15.根据权利要求13所述的粘合剂组合物的用途,其中浆料的新鲜状态粘度为0帕秒至5帕秒、有利地为0.1帕秒至3帕秒、更有利地为0.25帕秒至1.5帕秒。