CN117720314A - 一种可净化水质砂浆及其制备方法 - Google Patents
一种可净化水质砂浆及其制备方法 Download PDFInfo
- Publication number
- CN117720314A CN117720314A CN202311702958.0A CN202311702958A CN117720314A CN 117720314 A CN117720314 A CN 117720314A CN 202311702958 A CN202311702958 A CN 202311702958A CN 117720314 A CN117720314 A CN 117720314A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- mortar
- activated carbon
- purifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种可净化水质砂浆由以下按重量份计算的成分组成：普通硅酸盐水泥100～350份，多层状结构骨料600～800份，填料20～30份，活性炭5～20份，粉状明矾3～10份，植物抗菌剂1～10份；添加剂0.5～3份。宙石、麦饭石、珊瑚石、沸石是很多层状结构组成，能水池的污物和化学物质进行吸收与分解。活性炭在砂浆吸附水中的细微混着物、有机化合物、微生物残渣等有害物质，从而降低水质的硬度。粉状明矾属可对水质中细小杂质进行聚合吸附；结合植物抗菌剂起到除臭、杀菌、抗微生物滋生等作用。以多层状骨料、活性炭、明矾、植物抗菌剂等为可净化水质材料按一定比例组成的砂浆，可以改善建筑蓄水工程的水质。
Description
技术领域：
本发明涉及建筑材料领域，具体涉及一种可净化水质砂浆及其制备方法。
技术背景：
随着居民的生活水平越来越高，人们对建筑材料的要求越来越高。在建筑蓄水领域如蓄水池，游泳池，水产养殖鱼虾等场地对水质要求较高的场景。这些场所蓄水中长久之后会慢慢滋生一些生物细菌和细微浑浊物，或轻或重受到污染。而在场地建设使用的普通砂浆，诸如水泥、集料及外加剂水所含的一些碱性物质,也会对水质HP值产生一定的影响。现有砂浆行业内因过量添加各种化学外加剂，导致在建筑施工用料过程中会具有刺激性的物质，最主要的原因是化学外加剂溶于水后的所本身具有的。为了改善建筑蓄水部位慢慢滋生一些生物细菌和细微浑浊物的污染现象及普通砂浆应用对水质的一些影响；提高蓄水池的水质量、水产养殖场景的水质量。在建筑蓄水领域急需一种可以改善及净化水质的建筑砂浆。
发明内容：
为了解决这一类似问题，本发明目的在于提供一种可净化水质的建筑砂浆及其制备方法，改善蓄水建筑施工中普通砂浆泛出的碱盐、碳酸钙无机化合物及水池长期滋生的微生物细菌、细微浑浊物的污染现象，提高环境中水的质量。经过本研究发明，以多层状结构骨料、活性炭、明矾、植物抗菌剂等可净化水质材料按一定比例组成的砂浆；可以改善建筑蓄水工程的水质质量。这种非常出色的连续多孔结构骨料，在用作水质净化是能够大量吸附水质的有害物质。能对砂浆及水池的污物和化学物质进行吸收与分解。活性碳在砂浆中增强水泥的耐湿性和减轻潮气侵袭的风险；同时通过活性炭吸附水中的细微混着物、有机化合物、微生物残渣等有害物质，从而提高水的质量。活性炭可以降低水池的水质的硬度，含有活性炭水泥砂浆可以吸收大部分的碳酸钙；降低水质含有的铁、锰、镉等有害物质的含量，从而改善水环境。宙石、麦饭石、珊瑚石、沸石等提高除污效果的同时能降低水质中COD、BOD等有害化合物的含量。粉状明矾属可对水质中细小杂质进行聚合吸附；在砂浆中结合植物抗菌剂起到除臭、杀菌、抗微生物滋生等作用。如上所诉蓄水池的水流经过可净化水质砂浆接触范围内既能形成净化的效果，减少对传统水处理设备的依赖。
具体实施方法
一种可净化水质砂浆及其制备方法。具体如下：一种可净化水质砂浆由以下按重量份计算的成分组成：普通硅酸盐水泥100～350份，骨料600～800份，填料20～30份，活性炭5～20份，粉状明矾3～10份，植物抗菌剂1～10；添加剂0.5～3份。
一种净化水质砂浆其特征在于水泥属于市面上销售的325或425普通硅酸盐水泥；骨料是以宙石、麦饭石、珊瑚石、沸石为机制砂，属于粒径小于4mm以下的连续级配砂；是经离心式制砂机粉碎形成粒径小于4.7mm以下的连续级配砂组成。填料属于200～300目的粉煤灰、硅灰粉、矿粉等填料；活性炭属于100目以下的果壳活性炭、煤质活性炭和木质活性炭等；粉状明矾属于150目以下白色粉末状，所诉粉状明矾是硫酸钾与硫酸铝的复盐，可对水质中细小杂质进行聚合吸附；植物抗菌剂属于从蔷薇、石竹、紫萝兰、茉莉等植物叶颈提取的精油调制成的粉末状，其具有天然的防腐特质，同时还有着杀菌、抗微生物滋生等特性。添加剂属于砂浆类的高效塑化剂。
下面将结合本发明的实施案例，对本发明中的技术方案进行清楚、完整的描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。需要说明另外，各个实施例之间的技术方案可以相互结合，但是必须是以本领域普通技术人员能够实现为基础，当技术方案的结合出现相互矛盾或无法实现时应当认为这种技术方案的结合不存在，也不在本发明要求的保护范围之内。以下结合具体实施例对本发明的技术方案作进一步详细说明，应当理解以下实施例仅仅用以解释本发明，并不用于限定本发明。
实施例1，一种可净化水质砂浆及其制备方法，包括以下步骤：普通硅酸盐水泥280份，骨料机制砂700份，填料20份，活性炭6份，粉状明矾3份，植物抗菌剂2份，添加剂0.6份。先将称量好的普通硅酸盐水泥、骨料机制砂、填料各组分倒入搅拌机预混30秒；再将称量好的活性炭、粉状明矾、植物抗菌剂、添加剂添加入搅拌机混合120秒；混合均匀后打包所得可净化水质砂浆。
其中所诉水泥为425普通硅酸盐水泥；砂子属于粒径0.15～3mm的宙石、麦饭石、珊瑚石、沸石为机制砂；填料为200目的粉煤灰、硅灰粉、矿粉等；所诉活性炭为100目以下的果壳活性炭、煤质活性炭和木质活性炭等均可，不影响最终效果；所诉粉状明矾是硫酸钾与硫酸铝的复盐，可对细小杂质进行聚合吸附；植物抗菌剂属于从植物叶颈提取的精油调制成的粉末状，其具有天然的防腐特质，同时还有着抗菌、抗微生物的特性；添加剂属于抹灰砂浆类的高效塑化剂，主要为松香树脂类与烷基苯磺酸盐类，由于其拥有着良好的引气性与分散性能，其在砂浆之中使之表现出优异的和易性与保水性。该砂浆用水量为砂浆总量占比的14％时，其物理性能的28d抗压强度为41mpa,抗折强度为6.5mpa。
实施例2，一种可净化水质砂浆及其制备方法，包括以下步骤：普通硅酸盐水泥230份，骨料740份，填料20份，活性炭10份，粉状明矾6份，植物抗菌剂4份，添加剂1.2份。先将称量好的普通硅酸盐水泥、骨料机制砂、填料各组分倒入搅拌机预混30秒；再将称量好的活性碳、粉状明矾、植物抗菌剂、添加剂添加入搅拌机混合120秒；混合均匀后打包所得可净化水质砂浆。该砂浆用水量为砂浆总量占比的14％时，其物理性能的28d抗压强度为38.5mpa,抗折强度为6.3mpa。
实施例3，一种可净化水质砂浆及其制备方法，包括以下步骤：普通硅酸盐水泥180份，骨料760份，填料15份，活性炭12份，粉状明矾8份,植物抗菌剂8份，添加剂2份。先将称量好的普通硅酸盐水泥、骨料机制砂、填料各组分倒入搅拌机预混30秒；再将称量好的活性炭、粉状明矾、植物抗菌剂、添加剂添加入搅拌机混合120秒；混合均匀后打包所得可净化水质砂浆。该砂浆用水量为砂浆总量占比的14％时，其物理性能的28d抗压强度为34.6mpa,抗折强度为5.9mpa。
实施例4，一种可净化水质砂浆及其制备方法，包括以下步骤：普通硅酸盐水泥130份，骨料680份，填料10份，活性炭20份，粉状明矾10份,植物抗菌剂10份，添加剂2.6份。先将称量好的普通硅酸盐水泥、骨料机制砂、填料各组分倒入搅拌机预混30秒；再将称量好的活性碳、粉状明矾、植物抗菌剂、添加剂添加入搅拌机混合120秒；混合均匀后打包所得可净化水质砂浆。该砂浆用水量为砂浆总量占比的14％时，其物理性能的28d抗压强度为28.3mpa,抗折强度为5.2mpa。
对比列5，一种普通砂浆的组分:普通硅酸盐水泥200份，河砂780份，粉煤灰20份，添加剂3份。所述的普通砂浆没有添加净水材料，该砂浆用水量为砂浆总量占比的14％时，其物理性能的28d抗压强度为27.3mpa,抗折强度为4.8mpa。
将以上实施例1、2、3、4的可净化水质砂浆，与对比列5普通砂浆分别制作出5个1立方米的蓄水池，注入相同的水，经过30天净化。经过水质检测仪器检测得到被净化后水质的的检测结果。如下表所示：
由以上实施案例检测结果可知本发明所提供的一种可净化水质砂浆及其制备方法，以宙石、麦饭石、珊瑚石、沸石等多层状结构骨料、活性炭、明矾、植物抗菌剂等可净化水质材料按一定比例组成的砂浆，随着可净化水质材料比例的逐步增加，水质的各项指标逐步被净化降低。创造了砂浆在蓄水建筑领域具有净化水质的功能。
以上所述仅为本发明的为实施例，并非因此限制本发明的专利范围，凡是在本发明的发明构思下，利用本发明说明书所做的等效结构变换，或直接/间接运用在其他相关的技术领域均包括在本发明的专利保护范围内。
Claims (5)
1.一种可净化水质砂浆由以下按重量份计算的成分组成：普通硅酸盐水泥100～350份，多层状结构骨料600～800份，填料20～30份，活性炭5～20份，粉状明矾3～10份，植物抗菌剂1～10；添加剂0.5～3份。
2.根据权利要求1所诉的一种可净化水质砂浆其特征在骨料是以多层状结构的宙石、麦饭石、珊瑚石、沸石为机制砂；属于粒径小于4.7mm以下的连续级配砂。
3.根据权利要求1所诉的一种可净化水质砂浆其特征在于活性碳属于100目以下的果壳活性炭、煤质活性炭和木质活性炭等组成。
4.根据权利要求1所诉的一种可净化水质砂浆其特征在于粉状明矾属于150目以下白色粉末状，所诉粉状明矾是硫酸钾与硫酸铝的复盐。
5.根据权利要求1所诉的一种可净化水质砂浆其特征在植物抗菌剂属于从蔷薇、石竹、紫萝兰、茉莉等植物叶颈提取的精油调制成的粉末状，其细度在100～200目。