CN117413102A - 多层柔性包装材料 - Google Patents
多层柔性包装材料 Download PDFInfo
- Publication number
- CN117413102A CN117413102A CN202280039549.4A CN202280039549A CN117413102A CN 117413102 A CN117413102 A CN 117413102A CN 202280039549 A CN202280039549 A CN 202280039549A CN 117413102 A CN117413102 A CN 117413102A
- Authority
- CN
- China
- Prior art keywords
- layer
- packaging material
- flexible packaging
- multilayer flexible
- material according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明整体涉及多层柔性包装材料的领域。具体地讲,本发明涉及用以包装干燥食物,优选甜食的多层柔性包装材料。本发明的包装材料是能够海洋降解的、可再循环利用的并且具有可接受的阻隔特性。
Description
技术领域
本发明整体涉及多层柔性包装材料的领域。具体地讲,本发明涉及一种多层柔性包装材料。本发明进一步涉及根据本发明的该多层柔性包装材料用以包装干燥食物的用途。
背景技术
塑料包装在经济和人们的日常生活中使用频繁。它具有多个优点,诸如其柔韧性和其轻重量。例如,此类重量减轻有助于节省燃料和减少运输过程中的CO2。它的阻隔性能由于对延长保质期有积极作用,因而有助于减少食物浪费。阻隔性能也有助于确保食品安全。
然而,根据欧盟委员会最近发布的《欧洲循环经济中的塑料战略(Europeanstrategy for plastics in a circular economy)》,欧洲每年产生约2580万吨塑料废物,其中此类废物中的不到30%被收集用于再循环利用,并且每年有15万至50万吨塑料废物进入海洋。
为确保减少塑料垃圾,工业和商业领域都做出了巨大努力。例如,一些超市用纸基袋代替塑料袋。然而,在食物包装中使用纸张来代替塑料并不是一项简单的任务。包装材料的改变不得损害消费者安全。包装必须起到保护食品的作用,但还必须足够坚固以在生产过程中由机器操纵,并且必须使得食物产品能够被有效地展示。
因此,需要具有改进的阻隔特性的纸质材料。特别地,需要不包括塑料层的具有改进的阻隔特性的纸质材料以允许在再循环利用期间更容易地分类和分离纸质材料。
在这方面,WO 2000/076862描述了一种用于包装应用的层压结构,该层压结构包括纸坯;和具有粘土颗粒的至少一个聚合物/纳米粘土复合层,该至少一个聚合物/纳米粘土复合层施加到所述纸坯,具有0.7纳米至9纳米的范围内的厚度。
然而,本领域需要甚至进一步改进纸基包装材料的阻隔性能。
特别地,对于旨在用于食物产品的包装,良好的阻隔特性对于维持所包装的食物的安全性和质量是必不可少的。典型地,这种阻隔性能包括气体透过性,例如O2、CO2和N2;蒸气透过性,例如水蒸气;液体透过性(例如水或油透过性);香气透过性;和光透过性。
此外,在这种再循环利用的背景下,消费者没有适当处理包装的问题,即乱扔垃圾。这种材料可能最终存在于自然环境中,特别成问题的是存在于海洋环境中。传统的甜食包装也很小,这增加了意外乱扔垃圾的可能性,并且所用的塑料材料可能需要数年才能降解。
因此,本发明寻求平衡阻隔性能、可回收性和海洋降解的问题。
不能将本说明书中对现有技术文献中的任何参照视为承认此类现有技术为众所周知的技术或形成本领域普遍常识的一部分。
发明内容
本发明的目的是改进现有技术,特别是提供一种多层柔性包装材料,其提供改进的阻隔特性,并且可以再循环利用并能够在海洋条件下降解;并且提供此类多层柔性包装材料用以包装干燥食物产品的用途,或者至少为本领域中存在的包装解决方案提供有用的替代方案。
本发明人通过将以下物质应用于纸基包装材料而解决了上述问题:
聚合物层,所述聚合物层包含至少一种聚合物和任选的粘土阻隔材料,
阻隔层,所述阻隔层包含金属化材料、氧化铝或氧化硅或它们的混合物,和
密封层,
其中所述聚合物层包含至少一种选自以下的聚合物:丁烯二醇-乙烯醇共聚物(BVOH)、聚丁二酸丁二醇酯(PBS)、聚丁二酸丁二醇酯的共聚物、聚羟基链烷酸酯(PHA)、聚乳酸(PLA)及其混合物。
本发明提供水蒸气透过率(WVTR)和氧气透过率(OTR)测试结果,其满足包装干燥食品材料的要求,以及提供海洋降解和再循环利用的机会。重要的是,不需要聚乙烯(PE)或聚丙烯(PP)层来实现该目标。
因此,本发明的目的通过独立权利要求的主题实现。从属权利要求进一步拓展本发明的概念。
因此,本发明提供一种包括以下各项的多层柔性包装材料:纸层;铝层;纳米粘土阻隔涂层和密封层,该密封层施加到纳米粘土阻隔涂层的表面,表示多层柔性包装材料的内表面。
本发明还提供了根据本发明的多层柔性包装材料在包装干燥食物、优选甜食、优选巧克力产品和/或饼干或薄脆饼产品的用途。
如本说明书中所用,词语“包括”、“包含”和类似词语不应理解为具有排他性或穷举性的含义。换句话讲,它们旨在意指“包括,但不限于”。
本发明人已经表明,通过使用根据本发明的多层柔性包装材料,可获得在WVTR和OTR方面的可接受的结果。此外,如图所示,本发明在海洋降解方面提供了有利的特性。
附图说明
图1:参考材料纤维素、2020-31、2020-32和2020-33(从左至右)的视觉呈现
图2:培养8周后参考品纤维素滤纸的视觉呈现
图3:培养8周后测试品2020-31的视觉呈现
图4:培养8周后测试品2020-32的视觉呈现
图5:培养8周后测试品2020-33的视觉呈现
图6:实施例1-4的示意图
具体实施方式
本发明涉及一种从外表面到内表面包括以下层的多层柔性包装材料:
纸层,
聚合物层,所述聚合物层包含至少一种聚合物和任选的粘土阻隔材料,
阻隔层,所述阻隔层包含金属化材料、氧化铝或氧化硅或它们的混合物,和
密封层,
其中所述聚合物层包含至少一种选自以下的聚合物:丁烯二醇-乙烯醇共聚物(BVOH)、聚丁二酸丁二醇酯(PBS)、聚丁二酸丁二醇酯的共聚物、聚羟基链烷酸酯(PHA)、聚乳酸(PLA)及其混合物。
在高度优选的实施方案中,所述多层柔性阻隔材料没有聚烯烃层(诸如聚乙烯(PE)、聚对苯二甲酸乙二醇酯(PET)或聚丙烯(PP)层)。在优选的实施方案中,术语“不含”是指0重量%。
出于本发明的目的,如果包装材料是一种能够弯曲而不断裂的材料,则其应被视为柔性的。进一步地,例如,此种柔性材料可以是可被手弯曲而不断裂的材料。通常,根据本发明的多层柔性包装材料可具有140g/m2或更小的基重。
本发明的包装材料是纸基的。本领域的技术人员将能够例如基于待包装的产品、预期的保质期以及纸材料是否要用作初级、次级或三级包装来选择适当的纸层。
本发明包括含有金属化材料、氧化铝或氧化硅或它们的混合物的阻隔层。
可以通过物理气相沉积将金属化层施加到多层柔性包装材料。例如,可以通过真空沉积工艺来施加金属化层。真空沉积工艺的示例描述于《固体薄膜》(Thin SolidFilms),第666卷,2018年11月30日,第6页至14页中。真空沉积是一种蒸发过程,其中金属从固相变换到气相,然后回到固相,从而逐渐增加膜厚度。通过真空沉积产生的涂层具有以下优点:良好的耐磨性、冲击强度和温度强度,以及在复杂表面上沉积的能力。在优选的实施方案中,金属化工艺沉积铝。
在本发明中,二氧化硅膜的沉积方法不受限制。二氧化硅膜可以通过不同的方法制备,例如溶胶-凝胶、液相沉积、溅射、化学气相沉积(CVD)、热氧化、等离子体增强化学气相沉积(PECVD)、大气压等离子体沉积和物理气相沉积(PVD)。PVD是最成熟的真空沉积技术之一。其包括真空蒸镀、离子镀和溅射沉积。这些技术允许更好地控制膜厚度并确保沉积的膜具有良好的粘附性能。
在本发明中,氧化铝膜的沉积方法不受限制。在一个实施方案中,可以通过真空沉积来沉积氧化铝层。
本领域的技术人员可例如取决于预期的保质期、所包装的产品和包装材料的总厚度来适当地调整阻隔层的厚度。在根据本发明的多层柔性包装材料中,阻隔层可具有例如在20nm至500nm、30nm至400nm或50nm至200nm的范围内的厚度。
阻隔层的光密度范围可优选地在1.4至3.8的范围内,这与30纳米至200纳米的厚度相关。
纳米粘土阻隔涂层是本领域的技术人员已知的。例如。纳米粘土阻隔涂层可以是PVOH-聚丙烯酸-纳米粘土阻隔涂层。此类PVOH-聚丙烯酸-纳米粘土阻隔件的示例可从专业供应商商购获得。此外,本领域的技术人员将能够配制此类PVOH-聚丙烯酸-纳米粘土阻隔件。到2023年纸和纸板中的可持续阻隔涂层,最新技术报告,史密瑟斯信息有限公司(Smithers information Ltd.),2018年,第134页至142页,总结了最新技术。通常,此类PVOH-聚丙烯酸-纳米粘土阻隔件可例如通过官能化纳米粘土的表面以允许足够的排斥力从而允许形成曲折路径来制造。纳米粘土可选自由铝硅酸盐组成的群组,诸如例如蒙脱石(MMT)纳米粘土。
对于一些应用,如果纳米粘土阻隔涂层具有包含聚氨酯的组合物,则可为优选的。聚氨酯可用于部分或完全替换PVOH-聚丙烯基质。聚氨酯具有例如赋予极其良好的耐化学品性、耐溶剂性和耐久性的优点。如此,例如,纳米粘土阻隔涂层组合物可包含1重量%至10重量%之间的聚氨酯、2重量%至6重量%之间的聚氨酯或3重量%至5重量%之间的聚氨酯。
对于一些应用,如果纳米粘土分散在聚偏二氯乙烯聚合物基质中,则可为优选的。在这种情况下,PVDC基质中的固有疏水性和空间位阻作用进一步改善WVTR阻隔特性。
在优选的实施方案中,纳米粘土分散在丁烯二醇-乙烯醇共聚物(BVOH)、聚丁二酸丁二醇酯(PBS)、聚丁二酸丁二醇酯的共聚物、聚羟基链烷酸酯(PHA)、聚乳酸(PLA)及其混合物的基体中。
在上述实施方案中,纳米粘土材料以聚合物层的0.5重量%至10.0重量%、1.0重量%至8.0重量%或1.25重量%至5.0重量%的量存在于聚合物层中。
在一个实施方案中,聚合物层的剩余部分是丁烯二醇-乙烯醇共聚物(BVOH)、聚丁二酸丁二醇酯(PBS)、聚丁二酸丁二醇酯的共聚物、聚羟基链烷酸酯(PHA)、聚乳酸(PLA)及其混合物。
在一个优选的实施方案中,聚合物层包含含有分散在丁烯二醇-乙烯醇共聚物(BVOH)、聚丁二酸丁二醇酯(PBS)、聚丁二酸丁二醇酯的共聚物、聚羟基链烷酸酯(PHA)、聚乳酸(PLA)及其混合物的基体中的纳米粘土的部分以及含有丁烯二醇-乙烯醇共聚物(BVOH)、聚丁二酸丁二醇酯(PBS)、聚丁二酸丁二醇酯的共聚物、聚羟基链烷酸酯(PHA)、聚乳酸(PLA)及其混合物的第二部分。
在一个优选的实施方案中,含纳米粘土的部分与第二部分之间的重量比为0.1∶1.0至1.0∶0.1,优选0.25∶1.0至1.0∶0.25,并且更优选0.5∶1.0至1.0∶0.5。例如1.0:1.0。
在高度优选的实施方案中,聚合物层包含分散在丁烯二醇-乙烯醇共聚物(BVOH)基体中的纳米粘土的混合物的第一部分以及BVOH的第二部分。
在优选的实施方案中,聚合物层包含BVOH和纳米粘土混合物,并且BVOH的第二部分是层。
在优选的实施方案中,第一部分与第二部分的比率为0.25∶1.0至1.0∶0.25。在一个优选的实施方案中,聚合物层具有1g/m2至20g/m2范围内的克重(即,两部分的总克重)。
在本发明中,从阻隔特性的观点来看,发现在聚合物层中利用BVOH的实施方案是最优选的。
密封剂的性质不受特别限制,然而,在优选的实施方案中,密封剂包括选自聚酯(例如PHA、PBS、PBSA等)、玻璃纸、聚乙烯醇和衍生物(例如BVOH、PVOH等)及其混合物的材料。
在优选的实施方案中,密封层包含至少一种选自聚羟基链烷酸酯(PHA)、聚丁二酸丁二醇酯(PBS)、聚丁二酸丁二醇酯的共聚物及其混合物的材料。
在本发明中,当使用术语“聚丁二酸丁二醇酯的共聚物”时,这涵盖本领域中用于包装的已知共聚物,最优选为聚(丁二酸-己二酸丁二酯)(PBSA)。
在优选的实施方案中,纸层的克重为40g/m2至130g/m2,优选50g/m2至100g/m2,并且更优选60g/m2至100g/m2或55g/m2至90g/m2。
在优选的实施方案中,聚合物层的克重在1g/m2至20g/m2,优选2g/m2至15g/m2,并且更优选3g/m2至10g/m2的范围内。
在优选的实施方案中,密封层的克重在1g/m2至30g/m2,优选2g/m2至25g/m2,并且更优选5g/m2至15g/m2的范围内。
在一个优选的实施方案中,包装的总克重在42.5g/m2至150g/m2,优选50g/m2至125g/m2,并且更优选60g/m2至100g/m2的范围内。
在优选的实施方案中,纸层的克重为60g/m2至100g/m2。
聚合物层的克重在3g/m2至10g/m2的范围内。
阻隔层包含金属化材料,并且
所述密封层的克重在5g/m2至15g/m2的范围内。
本发明的多层柔性包装材料可以是用于食物产品的包装材料。例如,它可以是初级包装材料、二级包装材料或三级包装材料。如果多层柔性包装材料是用于食物产品的包装材料,则用于食物产品的初级包装材料可以是与实际食物产品直接接触的用于食物产品的包装材料。食物产品用二级包装材料可以是有助于将包含在初级包装中的一种或多种食物产品固定的食物产品用包装材料。当在单一容器中向消费者提供多种食物产品时,通常使用二级包装材料。食物产品用三级包装材料可以是有助于在运输期间将包含在初级包装和/或初级和次级包装中的一种或多种食物产品固定的食物产品用包装材料。
在一个优选的实施方案中,包装是用于食物产品、优选甜食食物产品、优选巧克力产品和/或饼干或薄脆饼产品的初级包装。
对于本发明的一些应用,如果纸层是无孔的,则可为优选的。如果纸层具有多孔表面,则可添加覆盖多孔纸表面的附加表面层以使其为不透气的。此类附加表面层可包含淀粉、颜料-淀粉或颜料-乳胶制剂或由淀粉、颜料-淀粉或颜料-乳胶制剂组成。纸材料的孔隙体积与总体积之比称为纸材料的孔隙率。出于本发明的目的,如果葛尔莱(Gurley)渗透率小于20ml/min(Tappi T547),如果其具有小于40%,例如小于30%或小于20%的孔隙率,则纸层应被视为无孔的。因此,在本发明的一个实施方案中,纸层是无孔纸层。
如果纸层具有低表面粗糙度,则也可为优选的。例如,纸层可具有小于100ml/min的本特生(Bendtsen)粗糙度。本特生粗糙度可根据ISO 8791-2:2013确定,因此以引用方式并入本文。
包装材料的阻隔特性是本领域的技术人员众所周知的。如果包装材料是用于食物产品的包装材料,则例如此类良好的阻隔特性对于维持所包装的食物的安全性和质量是必不可少的。典型地,这种阻隔性能包括气体透过性,例如O2、CO2和N2;蒸气透过性,例如水蒸气;液体透过性(例如水或油透过性);香气透过性;和光透过性。
在将铝层和/或纳米粘土阻隔件施加到纸层之前,底漆可用于更好地连接涂层与纸层。底漆通常具有允许涂层牢固地附着到其的化学性质,而底漆又牢固地附着到纸层。
用于本发明的目的的底漆可选自:丙烯酸共聚物、聚酯、聚羟基链烷酸酯、天然和化学改性的淀粉、木聚糖和化学改性的木聚糖、聚偏二氯乙烯、聚乙烯醇、乙基乙烯醇、醋酸乙烯酯、乙烯基醋酸乙酯、硝酸纤维素、聚烯烃、硅烷、聚氨酯或它们的组合。
用于本发明的目的的一种或多种底漆可包含纳米粘土。将纳米粘土添加到至少一种底漆具有以下优点:所得多层柔性包装材料的阻隔特性得以改善。因此,在根据本发明的多层柔性包装材料中,例如,施加到纸层的内表面的底漆可包含纳米粘土。这导致增强的阻隔特性。
适当的底漆是本领域的技术人员已知的并且可相应地选择。待施加在纸层与铝层之间的底漆可以是例如聚氨酯。另选地,可使用聚氨酯接合层。待施加在纸层与纳米粘土阻隔涂层之间的底漆也可以是聚氨酯。
例如,为了确保铝层很好地防止磨损,其可使用保护层来保护。适当的保护层是本领域的技术人员众所周知的,并且可选自:丙烯酸共聚物、聚酯、聚羟基链烷酸酯、天然和化学改性的淀粉、木聚糖和化学改性的木聚糖、聚偏二氯乙烯、聚乙烯醇、乙基乙烯醇、醋酸乙烯酯、乙烯基醋酸乙酯、硝酸纤维素、聚烯烃、硅烷、聚氨酯或它们的组合。使用此类保护层具有以下优点:铝层稳定并且保护良好而免受不利影响,从而维持其完整性并且因此其对本发明的多层柔性包装材料的阻隔特性的积极影响。
根据本发明的多层柔性包装材料包括密封层。
使用密封层,例如使用聚合物分散体来涂覆诸如纸包装材料的纸材料以例如改善纸材料的阻隔特性在本领域中是众所周知的。示例例如描述于T.,SavolainenA.V.(1997)Barrier dispersion coating of paper and board.见:Brander J.,ThornI.(编著)Surface Application of Paper Chemicals.Springer,Dordrecht.coated,paper materials。
对于消费者信息和设计目的,可将油墨层施加到纸层上。此外,如果存在施加在纸层与油墨层之间的底漆,则此处可为优选的。适当的底漆是本领域的技术人员已知的,并且可以例如是聚氨酯底漆。
为了将高质量的饰面添加到根据本发明的多层柔性包装材料的外表面,可将套印清漆(OPV)施加到油墨层的表面。OPV是本领域的技术人员众所周知的,并且可例如根据本发明的包装材料的预期目的来选择。例如,OPV可选自由以下项组成的组:常规胶印凸版清漆、丙烯酸清漆、UV清漆和可由水或溶剂基聚合物制剂表示的凹版清漆。
因此,本发明的多层柔性包装材料还可包括:底漆,该底漆施加到纸层;油墨层,该油墨层施加到纸层上的底漆;和套印清漆层,该套印清漆层施加到油墨层。
如上文所讨论,发明人惊奇地发现,当铝层和PVOH-聚丙烯酸-纳米粘土阻隔涂层均位于包装材料的面向所包装的产品的内侧上时,实现了相当令人满意的阻隔特性。这允许仅油墨层,任选地与底漆和/或OVP一起,位于包装材料的外表面上。因此,很好地保护了铝层和PVOH-聚丙烯酸-纳米粘土阻隔涂层而例如在运输、处理和消费者接触期间免受任何外部影响,使得其完整性得以良好地保护,并且本发明的多层柔性包装材料的阻隔特性更容易维持。
根据本发明的多层柔性包装材料可具有适合于包装材料的任何厚度。本领域的技术人员将能够确定适当的厚度。然而,特别地,特别是如果包装材料旨在用于包装食物产品,则包装材料应尽可能薄,同时仍确保食物产品的安全性和保质期。例如,根据本发明的多层柔性包装材料可具有在30μm至150μm、40μm至120μm或50μm至100μm的范围内的总厚度。
本领域的技术人员可适当地选择根据本发明的多层柔性包装材料的单独组分的克重或厚度。
在本发明的优选实施方案中,根据本发明的多层柔性包装材料可以是可回收利用的。例如,其可使用纸张和纸箱料流回收利用。在再循环利用期间,铝层将与包装的剩余部分分离。本发明的主题实现了省略诸如PE或PP层的聚烯烃层的事实提高了本发明的包装材料在再循环利用期间的可分类性。通常,在散浆机中再循环利用期间,将铝与包装材料的剩余部分分离。因此,根据本发明的多层柔性包装材料可作为纸张和/或纸箱再循环利用。
本发明的主题的一个优点是,尽管优选地省略了诸如PE或PP层的聚烯烃层,但实现了极佳的阻隔特性。
根据本发明的多层柔性包装材料可具有在0.1g/m2d至50g/m2d(38℃,90%RH)范围内的WVTR阻隔率。
这些极佳的阻隔特性允许根据本发明的多层柔性包装材料可用于包装干燥食物产品。出于本发明的目的,根据国际食品法典委员会,术语“食物”应意指旨在供人类食用的任何物质,无论是经加工的、半加工的还是原始的,并且包括饮料、口香糖和已在“食物”的制造、制备或处理中使用的任何物质,但不包括化妆品或烟草或仅用作药物的物质。
值得注意的是,极佳的阻隔特性允许根据本发明的多层柔性包装材料可用于包装干燥食物产品。干燥食物产品包括粉末和颗粒,例如待在奶或水中复原的粉末和颗粒。例如,干燥食物产品可具有5%或更少的水含量。
因此,根据本发明的多层柔性包装材料可用于包装干燥食物。本发明的主题还扩展到根据本发明的多层柔性包装材料用以包装干燥食物的用途。
本领域的技术人员将理解,他们可自由地合并本文所公开的本发明的所有特征。特别地,针对本发明的产品所描述的特征可以与针对本发明的方法所描述的特征相组合,反之亦然。另外,可组合针对本发明的不同实施方案所描述的特征。
尽管以举例的方式对本发明进行了描述,但应当理解,在不脱离权利要求书中所定义的本发明范围的前提下,可作出变型和修改。
此外,对于具体的特征如果存在已知的等同物,则应如同在本说明书中明确提到的那样来并入此类等同物。参见附图和非限制性实施例后,本发明的另外的优点和特征将变得显而易见。
实施例:
实施例1-4
使用金属化工艺(真空沉积-铝)、用于聚合物层的分散涂覆和用于密封层的挤出涂覆来制备以下组合物。
实施例5
制备本发明的下列组合物用于海洋降解测试:
2020-31:OPV/油墨/纸/PHA/金属化/PVOH
2020-32:OPV/油墨/纸/BVOH/金属化/PVOH
2020-33:OPV/油墨/纸/PHA/AlOx/PVOH
崩解测试执行两次。在启动时,每个反应器加入2片2cm×2cm。每4周,将反应器的内容物在2.0mm筛上过筛,并目视监测参考材料和测试材料的崩解。
图1给出了在启动时参考材料和测试品的视觉呈现。图2至5给出了在30℃±2℃下培养8周后,在参考品和测试品的重复品中检索到的碎片的视觉呈现。
培养8周后,参考品纤维素滤纸的崩解没有太大进展,除了边缘有一些降解(图2)。
测试品2020-31的崩解发生了显著变化,在2.0mm的筛网上只留下了几个部分,并且只有一小部分顶层仍然可见(图3)。
测试项目2020-32继续降解,并且大多数碎片已经通过2.0mm筛(图4)。
测试品2020-33中4周后的压痕仍在继续,可见总体碎片(图5)。
实施例6
将实施例1和3在23℃和85%RH下以g/m2/天计的WVTR与81gsm市售单面涂布的光泽纸进行比较,所述纸在反面具有阻隔(氧气、水蒸气、油脂、矿物油和香气)涂层。
样品 | 折叠的 | 平坦的 |
实施例1 | 5.1±0.4 | 2.1 |
实施例3 | 4.0±0.2 | 0.7 |
参考 | 20.7±3.9 | 0.16±0.03 |
实施例7
在自动包装线上使用来自实施例3的纸以每分钟30和80巴的速率包装单指标准KitKat(巧克力包裹的薄脆饼产品)。棒的包装没有任何问题,没有观察到质量缺陷。将包装在200N下在100-110度之间密封0.5秒。
使用Abiss Leak系统在六个样品棒上进行EXOS测试。标准小于16ml/min。样品提供3.2-4.2ml/min的范围,平均为3.6ml/min。
使用食品安全润滑剂对纸张内部进行油脂测试,在油脂测试后没有观察到油脂渗透/阻隔件破裂。
实施例8
对实施例1的纸重复实施例7。在30和80巴每分钟下运行,没有观察到质量缺陷。在两个测试中获得2.0和3.1的EXOS值,并且在油脂测试后没有观察到油脂渗透/阻隔件破裂。
实施例9
在包裹四指产品的实施例1-4上,用25℃/50%RH持续6小时和40℃/50%RH持续6小时的2个循环时间进行了额外的耐油脂性测试。所有实施例提供的结果至少表明6个月的保质期,其中实施例1、3和4提供0.3%的面积下油脂沾污。实施例3在两个单独的试验中提供了0.0%的面积。
实施例10-13
使用金属化工艺(真空沉积-铝)、用于聚合物层的分散涂覆和用于密封层的挤出涂覆来制备以下组合物。
用10nm金层涂覆材料,并使用显微镜以100x和1000x的倍数进行评估。
评估材料的孔,并且发现在涂覆后没有针孔。
发现实施例10和12具有含有较低水平的可见颗粒的更均匀的涂层。这支持了BVOH涂层在本发明内提供最有效的阻隔特性的发现。
可回收性由ProPakma公司使用纤维产率来评估并且发现具有可接受的可回收性水平。
评估90%RH 38℃和65%RH 22℃下的相对WVTR,并发现实施例10和12优于实施例11和14。
Claims (15)
1.多层柔性包装材料,所述多层柔性包装材料从外表面到内表面包括以下层:
纸层,
聚合物层,所述聚合物层包含至少一种聚合物和任选的粘土阻隔材料,
阻隔层,所述阻隔层包含金属化材料、氧化铝或氧化硅或它们的混合物,和
密封层,
其中所述聚合物层包含至少一种选自以下的聚合物:丁烯二醇-乙烯醇共聚物(BVOH)、聚丁二酸丁二醇酯(PBS)、聚丁二酸丁二醇酯的共聚物、聚羟基链烷酸酯(PHA)、聚乳酸(PLA)及其混合物。
2.根据权利要求1所述的多层柔性包装材料,其中将油墨施加到所述纸层的外表面。
3.根据权利要求1和2所述的多层柔性包装材料,其中所述聚合物层包含聚丁二酸丁二醇酯(PBS)或聚丁二酸丁二醇酯的共聚物与聚羟基链烷酸酯的混合物。
4.根据权利要求1和2所述的多层柔性包装材料,其中所述聚合物层包含丁烯二醇-乙烯醇共聚物(BVOH)和粘土。
5.根据前述权利要求中的任一项所述的多层柔性包装材料,其中所述纸层的克重为40g/m2至130g/m2。
6.根据前述权利要求中的任一项所述的多层柔性包装材料,其中所述聚合物层的克重在1g/m2至20g/m2的范围内。
7.根据前述权利要求中的任一项所述的多层柔性包装材料,其中所述密封层的克重在1g/m2至30g/m2的范围内。
8.根据前述权利要求中的任一项所述的多层柔性包装材料,其中所述包装的总克重在42.5g/m2至150g/m2的范围内。
9.根据前述权利要求中的一项所述的多层柔性包装材料,其中所述阻隔层的厚度在20nm至500nm的范围内。
10.根据前述权利要求中的一项所述的多层柔性包装材料,其中所述包装材料的总厚度在30μm至150μm的范围内。
11.根据前述权利要求中的一项所述的多层柔性包装材料,其中
所述纸层的克重为60g/m2至100g/m2,
所述聚合物层的克重在3g/m2至10g/m2的范围内,
所述阻隔层包含金属化材料,并且
所述密封层的克重在5g/m2至15g/m2的范围内。
12.根据前述权利要求中的一项所述的多层柔性包装材料,其中所述材料包括铝金属化层,并且所述聚合物层包含BVOH和纳米粘土混合物并且还包括BVOH层。
13.根据前述权利要求中的任一项所述的多层柔性包装材料用于包装干燥食物的用途。
14.干燥食物产品,所述干燥食物产品包装在根据前述权利要求中的任一项所述的多层柔性包装材料中。
15.根据权利要求13所述的用途或根据权利要求14所述的经包装的干燥食物产品,其中所述干燥食物产品是甜食产品,优选地是包含巧克力和/或薄脆饼的产品。