CN117282644A - Lubricating coating based on natural wax molecule and siloxane polymer molecule composite, and preparation method and application thereof - Google Patents
Lubricating coating based on natural wax molecule and siloxane polymer molecule composite, and preparation method and application thereof Download PDFInfo
- Publication number
- CN117282644A CN117282644A CN202311141367.0A CN202311141367A CN117282644A CN 117282644 A CN117282644 A CN 117282644A CN 202311141367 A CN202311141367 A CN 202311141367A CN 117282644 A CN117282644 A CN 117282644A
- Authority
- CN
- China
- Prior art keywords
- coating
- wax
- layer
- molecules
- natural wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a lubricating coating based on the combination of natural wax molecules and siloxane polymer molecules, and a preparation method and application thereof. The preparation method realizes rapid polymerization by catalyzing siloxane molecules with trace acid on a smooth surface formed by natural wax, and comprises two steps: firstly, immersing a substrate into a melt of natural wax, and obtaining a coating layer with uniform thickness in a lifting and rotating mode, wherein a smooth and uniform wax layer is formed after the wax layer is completely solidified; and secondly, rapidly polycondensing dimethyl dimethoxy silane molecules in a solution to form a prepolymer solution by using a trace amount of sulfuric acid, and immersing the substrate coated with the wax layer into the prepolymer solution of dimethyl dimethoxy silane to enable siloxane molecules to be compounded with the wax layer to form a stable polysiloxane oligomer molecular layer. The prepared composite coating has excellent anti-fouling capability and has good application prospect in the field of underwater anti-fouling. The coating has low requirement on the substrate, good stability, and no toxicity and pollution to the environment.
Description
Technical Field
The invention belongs to the technical and application fields of biological materials, and particularly relates to a lubricating coating based on the combination of natural wax molecules and siloxane polymer molecules, and a preparation method and application thereof.
Background
Biofouling attached to the surfaces of underwater facilities such as ships, dykes and the like has a number of negative effects on the human environment, energy and economic development. Among the relevant biofouling control means, antifouling coating materials account for a large part.
At present, self-polishing type antifouling coating materials which do not contain organic tin still occupy the domestic and foreign coating markets. The paint is mainly characterized in that an antifouling agent filled in the paint is released through hydrolysis of base resin, toxic substances in the antifouling agent are utilized to kill fouling organisms, and fouling on the surface of equipment is removed through continuous removal of the base resin, so that a self-polishing effect is achieved. However, the release amount of toxic substances in the anti-fouling agent is not easy to control, and the long-term release of the toxic substances can inevitably pollute the water environment, and the ecological balance is destroyed in serious cases.
The low surface energy materials exhibit excellent properties in the areas of surface anti-fouling, self-cleaning and drag reduction. The fouling release type antifouling coating material with low surface energy makes it difficult for fouling organisms to form a firm adhesion layer on the surface of the material, thereby achieving the antifouling effect. The traditional organosilicon and organic fluorine materials for preparing the low-surface-energy fouling desorption type antifouling coating material are generally poor in combination performance with a substrate, and have high requirements on the substrate, so that the stability of the coating is not strong, and the static antifouling capability is not ideal.
The lubricated surface exhibits excellent slidability and anti-adhesion effects for a variety of substances, playing an important role in achieving fluid transport, self-cleaning and anti-fouling areas. The creation of a lubricated surface is related to the nepenthes predation principle inspired by nature, and in 2011, aizenberg group developed a technology (Slippery Porous Lubricant-filled Surfaces, SLIPS) of injecting a lubricated liquid into a porous surface, i.e. injecting a low surface energy liquid (such as silicone oil) into a material surface with interconnected pores, to prepare a liquid surface with an ultra-slip effect, so that fouling organisms are difficult to attach on the surface. However, in an underwater environment, the liquid lubricant tends to bleed out from the porous surface, resulting in a weaker stability of the coating, i.e. the long-term stability of the SLIPS system under water still faces a great challenge.
Studies have shown that grafting flexible molecules onto smooth surfaces is an effective strategy for preparing lubricated surfaces ("Liquid-like" strategy), in which the flexible molecules that provide lubrication are bound to relatively smooth surfaces by chemical bonding that renders the coating more stable than SLIPS surfaces. Currently, methods including vapor deposition, heat treatment, ultraviolet irradiation, and end-group functionalized complementary bonding are used to prepare Liquid-like surfaces. In these methods, flexible molecular polymers have a relatively stringent requirement on the substrate, and the substrate needs to be subjected to hydroxylation treatment or functionalization treatment of special reactive groups to form chemical bonds with the polymer, which not only increases the complexity and cost of coating preparation, but also makes such coatings difficult to mass-produce.
The currently reported method has more problems that firstly, the thickness of the flexible molecular layer playing a key sliding function is in the nanometer level and is generally lower than 100 nanometers, and in practical application, such as ship surface, the roughness of the flexible molecular layer is generally in the micrometer level, so that the flexible molecular layer prepared by the existing method cannot fully cover the surface of a real object, the sliding property of the flexible molecular layer is greatly reduced, and the flexible molecular layer is easily damaged and has very low tolerance due to the excessively high surface roughness. Second, the flexible molecular layer is capable of bonding to the surface of the object if the surface of the object is required to contain a necessary functional group, such as a hydroxyl group. While surfaces of things, such as marine surfaces, typically contain corrosion protection layers, such as paints, the corrosion protection layer surface is an inert layer and contains little reactive functionality. How to effectively graft flexible molecules onto the surface of an object is a challenging task.
Disclosure of Invention
The invention aims to overcome the defects in the prior art and provide a lubricating coating based on the combination of natural wax molecules and siloxane polymer molecules, a preparation method and application thereof, and a substance which is easy to form a film and can fully cover the surface of a substrate is introduced, so that a flat surface layer is formed on the surface of an object, the roughness of the object is reduced, and the new surface contains abundant hydroxyl functional groups.
In order to achieve the above purpose, the present invention adopts the following technical scheme:
the first object of the invention is to provide a method for preparing a lubricating coating based on the composition of natural wax molecules and siloxane polymer molecules, comprising the following specific steps:
s1, immersing a substrate into a melt of natural wax, and obtaining a coating layer with uniform thickness in a lifting and rotating mode, wherein a smooth and uniform wax layer is formed after the wax layer is completely solidified;
s2, mixing siloxane monomer molecules with isopropanol, adding concentrated sulfuric acid, and rapidly polycondensing to form a prepolymer solution;
s3, immersing the substrate coated with the wax layer into a prepolymer solution of siloxane monomer molecules to enable the siloxane molecules to be compounded with the wax layer, and forming a stable polysiloxane oligomer molecular layer.
Further, the natural wax at least completely covers the substrate after being melted, and the thickness of the natural wax layer covered on the surface of the substrate is 0.1-100 mu m.
Further, the volume ratio of the siloxane monomer molecules to the isopropyl alcohol is 1: (4-5), the volume ratio of the siloxane monomer molecules to the concentrated sulfuric acid is 2mL: (100-120) mu L.
Further, the natural wax includes palm wax or beeswax.
Further, the siloxane monomer molecule comprises dimethyldimethoxy silane.
Further, in step S1, the preparation process of the melt of the natural wax includes weighing the natural wax in a beaker, heating the beaker in a water bath at 80-85 ℃, continuously heating and homogenizing the solid natural wax for 20-60 min after the solid natural wax is completely converted into liquid, and keeping Wen Daiyong in the water bath after bubbles in the melt are completely discharged.
In step S1, the curing time is 2-6 hours.
The second purpose of the invention is to prepare the lubricating coating by adopting the preparation method.
Further, the drop sliding angle of the lubricating coating is: sliding angle under 10. Mu.L drop<40 0 。
The second purpose of the invention is to apply the lubricating coating prepared by the preparation method to the preparation of underwater antifouling products.
Compared with the prior art, the invention has the beneficial effects that:
(1) The invention provides a preparation method of a lubricating coating based on the combination of natural wax molecules and siloxane polymer molecules, which realizes the rapid polymerization of siloxane molecules by micro acid catalysis on the smooth surface formed by natural wax, and comprises the following two steps: firstly, immersing a substrate into a melt of natural wax, and obtaining a coating layer with uniform thickness in a lifting and rotating mode, wherein a smooth and uniform wax layer is formed after the wax layer is completely solidified; and secondly, rapidly polycondensing dimethyl dimethoxy silane molecules in a solution to form a prepolymer solution by using a trace amount of sulfuric acid, immersing the substrate coated with the wax layer into the dimethyl dimethoxy silane prepolymer solution to enable siloxane molecules to be compounded with the wax layer, and forming a stable polysiloxane oligomer molecular layer (DMS). Thus preparing the composite coating, and showing excellent anti-fouling capability.
(2) The present invention utilizes the complexing ability of natural waxes with silicone polymers to produce a composite coating on a relatively rough and inert substrate surface. The coating has obvious influence on the surface energy and wettability of the surface of the material, and the antifouling capacity of the surface of the substrate is greatly improved. The micro-nano structure of the coating endows the surface of the material with good hydrophobic property; the low surface energy and the lubricating effect enable the coating to have good antifouling capacity; has excellent anti-adhesion effect on inorganic nano particles, proteins, marine microalgae and other pollutants. Experiments on underwater hanging plates show that the coating can reduce the adhesion of sludge, algae and other pollutants in water to a certain extent in a static water area environment. And the raw material natural wax has the characteristics of easy availability, green and non-toxicity, low price, reproducibility, good film forming capability and the like, so that the preparation method of the coating is simple, the requirement on a substrate is low, the stability is good, the environment is non-toxic and pollution-free, and the coating is a coating material with development prospect in the field of underwater pollution prevention.
(3) Because of the relatively low surface energy and stable composite effect of the two raw material molecules, the coating has low surface energy and excellent lubricity, and pollutant molecules are not easy to adhere to the surface of the coating, so that the coating has good anti-adhesion effect on the surfaces of various pollutants. The main materials of the composite coating are natural waxes (such as carnauba wax CW and beeswax BW and waxes with active hydroxyl or hydroxy fatty acid esters in other components) and siloxane monomer molecules. The natural wax has excellent film forming property, and the natural wax melted into liquid has good flowing effect and can rapidly form a film on the surface of a substrate; siloxane monomer molecules (such as dimethyl dimethoxy silane) are polymerized into siloxane oligomer under the catalysis of trace sulfuric acid, and silane chains have good flexibility and are easy to form a lubricating surface. The natural wax cooperates with the siloxane low polymer molecules with lubricating effect through active groups to form a stable composite coating.
Drawings
FIGS. 1a and 1b are graphs comparing the wiener structure and roughness of a DMS@CW coating layer and a DMS@BW coating layer;
FIG. 2 is a graph showing the surface energy, wettability and sliding properties of the surfaces of the substrates before and after the modification of the ship plate substrate by the DMS@CW coating and the DMS@BW coating, respectively;
FIG. 3 is a graph of the stability of the bonding of the DMS@CW coating to the substrate;
FIG. 4 is a graph of the anti-fouling effect of a DMS@CW coating on proteins;
FIG. 5 is a graph of the antifouling effect of a DMS@CW coating on marine microalgae;
FIG. 6 is a graph of the anti-fouling effect of a DMS@CW coating on nanoparticles;
FIG. 7 is a graph of the underwater antifouling effect of DMS@CW coating.
Detailed Description
In order to make the objects, technical solutions and advantages of the present invention more apparent, the following detailed description of the specific embodiments of the present invention will be given with reference to the accompanying drawings. The examples are not to be construed as limiting the specific techniques or conditions described in the literature in this field or as per the specifications of the product. The reagents or apparatus used were conventional products commercially available without the manufacturer's attention.
In practice, the natural wax is melted to cover the substrate at least completely, and the natural wax layer on the surface of the substrate may have a thickness of 0.1 μm to 100 μm.
Contact angle and sliding angle measurements in this example: testing wettability of the surface of the coating by adopting a contact angle/interfacial tension measuring instrument; the test liquid is water and n-hexadecane; for contact angle testing, the liquid volumes were all 10.0 μl, and the contact angles were measured 5 times at different locations for each sample, and averaged; for the slip angle test, the liquid volumes were all 10.0 μl, and the slip angles were measured 5 times at different locations for each sample, and averaged.
Example 1
(1) Pretreatment of a material substrate:
placing the substrate in an ultrasonic cleaning instrument, cleaning for 10min by deionized water, drying by nitrogen, cleaning for 10min by absolute ethyl alcohol, and drying by nitrogen for later use.
(2) Preparation of palm wax melt:
30.0g of flaky carnauba wax is weighed into a 100ml beaker, placed into a water bath kettle at 85 ℃ for heating, heated and homogenized for 30min after all the solid carnauba wax is converted into liquid, and Wen Daiyong is kept in the water bath kettle after bubbles in the liquid are completely discharged.
(3) Preparing a DMS prepolymer solution:
2.0mL of a dimethyldimethoxysilane solution was taken and mixed with 10.0mL of isopropanol, 100. Mu.L of concentrated sulfuric acid was added, and the mixture was stirred at room temperature on a magnetic stirrer at 4500rpm for 10 minutes. The prepolymer solution is ready-to-use.
(4) Preparation of DMS@CW composite coating
The surface of the ship plate substrate (2 cm multiplied by 2 cm) is coated and modified by a dip coating method, the pretreated ship plate is immersed into palm wax melt, and the ship plate is vertically lifted and rotated after being preheated until a uniform palm wax coating layer is formed. Taking out and naturally solidifying for 3 hours at room temperature. Immersing the solidified palm wax coated substrate into DMS prepolymer solution, directly taking out after 30s, and placing at room temperature, and forming a siloxane oligomer molecular composite layer after the solvent on the surface of the wax layer naturally volatilizes.
Example 2
(1) Pretreatment of a material substrate:
placing the substrate in an ultrasonic cleaning instrument, cleaning for 10min by deionized water, drying by nitrogen, cleaning for 10min by absolute ethyl alcohol, and drying by nitrogen for later use.
(2) Preparation of palm wax melt:
30.0g of flaky carnauba wax is weighed into a 100ml beaker, placed into a water bath kettle at 85 ℃ for heating, heated and homogenized for 30min after all the solid carnauba wax is converted into liquid, and Wen Daiyong is kept in the water bath kettle after bubbles in the liquid are completely discharged.
(3) Preparing a DMS prepolymer solution:
2.0mL of a dimethyldimethoxysilane solution was taken and mixed with 10.0mL of isopropanol, 100. Mu.L of concentrated sulfuric acid was added, and the mixture was stirred at room temperature on a magnetic stirrer at 4500rpm for 10 minutes. The prepolymer solution is ready-to-use.
(4) Preparation of DMS@CW composite coating
The surface of the ship plate substrate (2 cm multiplied by 2 cm) is coated and modified by a dip coating method, the pretreated ship plate is immersed into palm wax melt, and the ship plate is vertically lifted and rotated after being preheated until a uniform palm wax coating layer is formed. Taking out and naturally solidifying for 3 hours at room temperature. Immersing the solidified palm wax coated substrate into DMS prepolymer solution, directly taking out after 1min, and placing at room temperature, and forming a siloxane oligomer molecular composite layer after the solvent on the surface of the wax layer naturally volatilizes.
Example 3
(1) Pretreatment of a material substrate:
placing the substrate in an ultrasonic cleaning instrument, cleaning for 10min by deionized water, drying by nitrogen, cleaning for 10min by absolute ethyl alcohol, and drying by nitrogen for later use.
(2) Preparation of palm wax melt:
30.0g of flaky carnauba wax is weighed into a 100ml beaker, placed into a water bath kettle at 85 ℃ for heating, heated and homogenized for 30min after all the solid carnauba wax is converted into liquid, and Wen Daiyong is kept in the water bath kettle after bubbles in the liquid are completely discharged.
(3) Preparing a DMS prepolymer solution:
2.0mL of a dimethyldimethoxysilane solution was taken and mixed with 10.0mL of isopropanol, 120. Mu.L of concentrated sulfuric acid was added, and the mixture was stirred at room temperature on a magnetic stirrer at 4500rpm for 20 minutes. The prepolymer solution is ready-to-use.
(4) Preparation of DMS@CW composite coating
The surface of the ship plate substrate (2 cm multiplied by 2 cm) is coated and modified by a dip coating method, the pretreated ship plate is immersed into palm wax melt, and the ship plate is vertically lifted and rotated after being preheated until a uniform palm wax coating layer is formed. Taking out and naturally solidifying for 3 hours at room temperature. Immersing the solidified palm wax coated substrate into DMS prepolymer solution, directly taking out after 1min, and placing at room temperature, and forming a siloxane oligomer molecular composite layer after the solvent on the surface of the wax layer naturally volatilizes.
Example 4
(1) Pretreatment of a material substrate:
placing the substrate in an ultrasonic cleaning instrument, cleaning for 10min by deionized water, drying by nitrogen, cleaning for 10min by absolute ethyl alcohol, and drying by nitrogen for later use.
(2) Preparation of beeswax melt:
15.0g of massive beeswax is weighed into a 100ml beaker, placed into a water bath kettle at 75 ℃ for heating, heated and homogenized for 30min after the beeswax is completely converted into liquid, and the bubbles in the melt are completely discharged and then kept in the water bath kettle for Wen Daiyong.
(3) Preparing a DMS prepolymer solution:
2.0mL of a dimethyldimethoxysilane solution was taken and mixed with 10.0mL of isopropanol, 100. Mu.L of concentrated sulfuric acid was added, and the mixture was stirred at room temperature on a magnetic stirrer at 4500rpm for 20 minutes. The prepolymer solution is ready-to-use.
(4) Preparation of DMS@BW composite coating
The surface of the ship plate substrate (2 cm multiplied by 2 cm) is coated and modified by a dip coating method, the pretreated ship plate is immersed into beeswax melt, and the ship plate is vertically lifted and rotated after being preheated until a uniform palm wax coating layer is formed. Taking out and naturally solidifying for 3 hours at room temperature. Immersing the cured beeswax-coated substrate into DMS prepolymer solution, directly taking out after 1min, and placing at room temperature, and forming the siloxane oligomer molecular composite layer after the solvent on the surface of the wax layer naturally volatilizes.
In order to better explore the detergency performance of the lubricating coating provided by the invention, the applicant conducted the following studies:
(1) Micro-nano structure and roughness graph comparison research
As shown in FIGS. 1a and 1b, the DMS@CW is prepared in example 1 and the DMS@BW is prepared in example 4.
The microscopic morphology of the DMS@CW coating layer is in a nano-scale fold shape, and the fold distribution is relatively uniform and dense. The average roughness of the coating was 0.99 μm (Ra), the mean square roughness (Rq) was 1.35 μm, and a smooth surface with a certain glossiness was formed in a macroscopic state with a thickness of 93.3. Mu.m.
The surface of the DMS@BW coating layer is provided with a plurality of uneven block-shaped protrusions, and the continuous block-shaped protrusions and the intermediate ravines form a corrugated-like structure. The bump-like projections had a diameter of about 10 μm to 25. Mu.m, the average roughness of the coating layer was 1.04 μm (Ra), and the mean square roughness (Rq) was 1.27. Mu.m. A smooth and flat surface is formed in a macroscopic state.
The average roughness of the base substrate was 1.31 μm (Ra), and the mean square roughness (Rq) was 1.6. Mu.m. Both coatings reduce the surface roughness of the substrate compared to the original substrate, allowing it to form a smoother surface.
(2) And (5) researching the surface energy, wettability and slidability of the surfaces of the substrates before and after the substrates of the ship plates are modified.
As shown in FIG. 2, the DMS@CW is prepared in example 2 and the DMS@BW is prepared in example 4.
As can be seen from FIG. 2, the uncoated boat deck substrate has a relatively high surface energy (36.09 mJ/m 2 ) The droplets are in a viscous state at their surface. The surface energy of the ship plate substrate coated with the natural wax layer is greatly reduced, wherein the surface energy of the substrate coated with the palm wax layer is 21.08mJ/m 2 The surface energy of the substrate coated with beeswax is 18.18mJ/m 2 . The surface energy of the coating layer is not changed substantially after the wax layer is compounded with the siloxane polymer molecules (change value 2.00+ -1 mJ/m) 2 ) The molecular layer of siloxane polymer gives the coating an excellent lubricating effect, wherein the Sliding Angle (SA) of the droplet on the DMS@CW coating is 18.16 DEG and the Sliding Angle (SA) on the DMS@CW coating is 18.37 deg.
(3) Stability study of the bonding of DMS@CW coatings to substrates
The test was carried out using the dms@cw coating prepared in example 3.
The coatings were subjected to substrate adhesion testing using ASTM standards. Firstly, drawing a grid shape on the surface of a coating by using a blade, then adhering a 3M adhesive tape to a grid scratch, applying pressure by using tweezers to remove gaps between the adhesive tape and the coating, tearing off the 3M adhesive tape with horizontal upward force along two sides of the adhesive tape after staying for 1min, and observing whether the grid area and the scratch edge fall off under a scanning electron microscope.
As can be seen from FIG. 3, the grid area and the scratch edge of the coating are not fallen off when observed under a scanning electron microscope, which shows that the coating has good adhesion capability with the steel plate substrate and good bonding stability with the substrate.
(4) Investigation of the antifouling Effect of DMS@CW coating on proteins
The test was carried out using the dms@cw coating prepared in example 1.
Using FITC-labeled bovine serum albumin and human LgG protein as adhesion proteins, the proteins were dissolved in PBS buffer at ph=0.4 at a concentration of 1mg/mL. A region on the coating was marked with a knife blade, the prepared protein buffer was dropped into the test region, left at room temperature in the dark for 4h, and then washed out with PBS buffer. The adhesion of the proteins in the region was observed and recorded with a two-photon confocal microscope.
As can be seen from fig. 4, the two proteins fluoresce very strongly on the boat deck base, covering almost the entire area. And the protein adhesion amount on the surface of the DMS@CW coating is small, and only weak fluorescence is observed under a microscope. The fluorescence intensity in the region was quantified, and the fluorescence intensity of the control group was set to 100.00%, which was referred to as an adhesion rate of 100.00%. The bovine serum albumin attachment rate of the dms@cw coating was 37.70% and the human LgG protein attachment rate was only 0.16%. This shows that the DMS@CW coating can obviously reduce the protein adhesion rate and has good protein adhesion resistance.
(5) Research on antifouling effect of DMS@CW coating on marine microalgae
Experiments were performed using dms@cw prepared in example 1 and dms@bw prepared in example 4.
The algae type is Phaeophyta tsaoko, the body size is about several micrometers, the initial concentration of algae is about 104/mL, the algae is co-cultured with the sample on the 7 th day of breeding, the culture temperature is 20-28 ℃, the illumination time is 8-16 h each day, and the algae is shaken in the morning and evening.
As can be seen from FIG. 5a, the algae on the ship plate (Blank) is adhered to a serious extent, and the algae adhered to the ship plate in 15day is spread over almost the whole surface. The attachment amount of the flat algae is continuously increased from 15 days to 30 days. The pictures show that the density and thickness of the attached flat algae are increased, and the surface of the ship plate is seriously polluted by algae. The algae attachment amount of the DMS@CW coating is relatively low, the attachment amount of the flat algae is low within 15 days, and the attachment density is low. The attachment density and thickness of the flat algae on the surface of the coating are almost unchanged from 15 days to 30 days. The DMS@BW coating is slightly polluted by the flat algae within 15 days, and the attachment amount of the flat algae is gradually increased from 15 days to 30 days.
As can be seen from fig. 5b, when the attachment area of the flat algae is quantitatively treated and the attachment area of the flat algae in the control group is set to be 100.00%, the attachment area of the flat algae in the 15 th day of the dms@cw coating is 27.08%, and the attachment area of the flat algae in the 30 th day of the flat algae is 43.06%, which indicates that the algae attachment speed of the coating in the static seawater environment is slow, and the coating has good static algae resistance. The algae attachment area of the DMS@BW coating layer at 15day is 73.26%, and the algae attachment area at 30day is almost 100%.
(6) Study of antifouling effect of DMS@CW coating on nanoparticles
The test was carried out using the dms@cw coating prepared in example 3.
Titanium dioxide (TiO) with a diameter of 100nm was used 2 ) Nanoparticle test 2g of nano TiO 2 Fully dispersing in 20mL of ultrapure water to obtain nano TiO with the concentration of 2g/mL 2 A suspension. Square areas with a length and width of 0.5cm x 0.5cm were selected on the surface of the prepared coating and marked with a knife scribe. Sucking 20 mu L of prepared nano TiO by a pipette 2 The suspension liquid is dripped in a square test area, after the suspension liquid stays for 1min, the liquid is sucked from the edge of the area by using filter paper, the operation is repeated for 10 times, and then the sample is dried by using nitrogen. Observing and recording TiO in the test area under a scanning electron microscope 2 Adhesion of nanoparticles.
As can be seen from FIG. 6, a large amount of nano TiO exists on the surface of the ship plate substrate 2 Particle residue, except surface-stacked nano-TiO 2 Besides particles, a large amount of nano TiO is hidden in the defect structure and the concave part of the surface 2 And (3) particles. While on the relatively smooth surface of the DMS@CW coating, there are few nano TiO 2 The particles remain. Nano TiO in the opposite region 2 Quantifying the particle coverage area, and quantifying the nano TiO of the ship plate of the control group 2 The particle coverage was set at 100.00%. Nano TiO on surface of DMS@CW coating 2 The particle coverage area is only 1.88%, which shows that the coating has good anti-adhesion effect on inorganic nano particles.
(7) Underwater antifouling effect research of DMS@CW coating
The test was carried out using the dms@cw coating prepared in example 2.
A self-made simulated hanging plate device is adopted to vertically hang a sample with the size of 3.0cm multiplied by 3.0cm at a position with the depth of about 30cm to 50cm from the water surface. The underwater hanging plate time is 3-4 months and 7-8 months each year, namely the vigorous period of aquatic organisms such as algae and snails, and the water temperature is about 15-25 ℃. After 30 days, the sample was removed and the contamination level of the sample was recorded after rinsing the surface contamination of the sample with pure water gently.
As can be seen from fig. 7, the macroscopic image shows that the pollution of the substrate surface of the ship board is serious within 30day, and the whole paint surface is almost completely covered by sludge, algae and the like in water. The pollution condition of the DMS@CW coating at the 30day is lighter, and the original appearance of the coating is not completely covered by pollutants. The microscopic morphology comparison shows that the pollutant attached to the surface of the ship plate reaches a certain thickness, almost completely covers the original morphology of the ship plate, the pollutant on the surface of the DMS@CW coating is sparsely covered, and only part of the area is adhered by the pollutant. And the DMS@CW coating is not foamed and falls off in one month of underwater soaking, which shows that the DMS@CW coating reduces the adhesion of pollutants on the surface of a ship board in a still water environment and has a certain application potential in underwater antifouling application.
The above is not relevant and is applicable to the prior art.
Although specific embodiments of the invention have been described in detail by way of example, it will be appreciated by those skilled in the art that the foregoing examples are provided for illustration only and are not intended to limit the scope of the invention, and that various modifications or additions and substitutions are possible to the described specific embodiments without departing from the scope of the invention as defined in the accompanying claims. It should be understood by those skilled in the art that any modification, equivalent substitution, improvement, etc. made to the above embodiments according to the technical substance of the present invention should be included in the scope of protection of the present invention.
Claims (10)
1. A method for preparing a lubricating coating based on the composition of natural wax molecules and silicone polymer molecules, comprising the following specific steps:
s1, immersing a substrate into a melt of natural wax, and obtaining a coating layer with uniform thickness in a lifting and rotating mode, wherein a smooth and uniform wax layer is formed after the wax layer is completely solidified;
s2, mixing siloxane monomer molecules with isopropanol, adding concentrated sulfuric acid, and rapidly polycondensing to form a prepolymer solution;
s3, immersing the substrate coated with the wax layer into a prepolymer solution of siloxane monomer molecules to enable the siloxane molecules to be compounded with the wax layer, and forming a stable polysiloxane oligomer molecular layer.
2. The method according to claim 1, wherein the natural wax is melted to cover the substrate at least completely, and the natural wax layer on the surface of the substrate has a thickness of 0.1 μm to 100 μm.
3. The method of claim 2, wherein the volume ratio of the siloxane monomer molecules to the isopropyl alcohol is 1: (4-5), the volume ratio of the siloxane monomer molecules to the concentrated sulfuric acid is 2mL: (100-120) mu L.
4. The method of claim 1, wherein the natural wax comprises palm wax or beeswax.
5. The method of preparation of claim 1, wherein the siloxane monomer molecule comprises dimethyldimethoxysilane.
6. The preparation method of the natural wax according to claim 1, wherein in the step S1, the preparation process of the melt of the natural wax is that the natural wax is weighed in a beaker, and is heated in a water bath kettle at 80-85 ℃, and after the natural wax in solid state is completely converted into liquid, the natural wax is continuously heated and homogenized for 20-60 min, so that bubbles in the melt are completely discharged and then kept in the water bath kettle for Wen Daiyong.
7. The method of claim 6, wherein the curing time in step S1 is 2 to 6 hours.
8. A lubricating coating produced by the production method according to any one of claims 1 to 7.
9. The lubricious coating of claim 8 wherein the droplet slip angle of the lubricious coating is: sliding angle under 10. Mu.L drop<40 0 。
10. Use of a lubricating coating as claimed in claim 8 or 9 in the manufacture of an underwater antifouling product.