CN116835999A - 一种混凝土微生物养护剂 - Google Patents
一种混凝土微生物养护剂 Download PDFInfo
- Publication number
- CN116835999A CN116835999A CN202310699663.6A CN202310699663A CN116835999A CN 116835999 A CN116835999 A CN 116835999A CN 202310699663 A CN202310699663 A CN 202310699663A CN 116835999 A CN116835999 A CN 116835999A
- Authority
- CN
- China
- Prior art keywords
- parts
- concrete
- curing agent
- microorganism
- bacteria
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种混凝土微生物养护剂，属于混凝土技术领域，具体涉及一种混凝土微生物养护剂，所述混凝土微生物养护剂包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；所述微生物菌株包括硝化细菌、解磷菌、乳酸菌、酵母菌、益生菌；所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质；所述营养物质包括磷元素、氮元素、钾元素。本发明采用微生物养护剂，在施工和使用的过程中不会对环境造成较大的污染，能够有效的保护生态环境，保护施工人员和周围环境，起到环保的作用效果。
Description
技术领域
本发明属于混凝土技术领域，尤其涉及一种混凝土微生物养护剂。
背景技术
混凝土在施工过程中容易受到外界环境的影响，如温度、湿度、风化等，这些因素会导致混凝土表面的龟裂、开裂和脱落等问题。混凝土在使用过程中还会受到各种外力的作用，如水、气体和化学物质等，这些因素会导致混凝土内部结构的损伤和腐蚀，从而降低混凝土的强度和耐久性。
但目前普遍采用化学养护剂可能会在施工和使用过程中对环境造成一定的污染，甚至会对生态环境造成不可逆的损害，化学养护剂可能含有一些有毒成分，对施工人员和周围环境造成一定的危害，如果不当使用可能会对人体健康造成损害。
发明内容
基于背景技术存在的技术问题，本发明提出了一种混凝土微生物养护剂。
本发明提出的一种混凝土微生物养护剂，所述混凝土微生物养护剂包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；
所述微生物菌株包括硝化细菌、解磷菌、乳酸菌、酵母菌、益生菌；
所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质；
所述营养物质包括磷元素、氮元素、钾元素。
优选地，所述益生菌为枯草芽孢杆菌。
优选地，所述酵母菌为发酵酵母菌。
优选地，所述解磷菌为磷酸盐溶解菌、硅酸盐细菌中一种或者两种组合而成。
优选地，所述乳酸菌为乳杆菌、链球菌、片球菌中一种或者多种组合而成。
优选地，所述氮元素占总重量的1～5%，所述磷元素占总重量的0.5～2%，所述钾元素占总重量的0.5～2%。
优选地，当微生物菌株为益生菌的时候，其中益生菌为100份，所述基质中还包括
氨基酸混合物，所述氨基酸混合物包括谷氨酸、精氨酸、天门冬氨酸、缬氨酸，其中氨基酸混
合物为250份、葡萄糖为500份，所述辅助剂为50份磷酸二氢钾、5份、0.5份
、0.5份、0.5份、0.5份、0.5份。
优选地，当微生物菌种为酵母菌的时候，其中酵母菌为100份，所述辅助剂为500份酵母份、250份酪蛋白酸水解物、50份酵母精氨酸、25份碳酸氢钠，其中所述基质中的蛋白胨为250份。
优选地，当微生物菌种为解磷菌的时候，其中解磷菌为100份，所述辅助剂为硝酸铵50份、硫酸镁25份、磷酸二氢钾10份、氯化钙5份、硅酸钠2.5份。
与现有技术相比，本发明的有益效果是：
1、制备的微生物养护剂在混凝土脱模后喷涂，28d混凝土碳化深度降低20%～30%，养护效果明显，微生物养护剂具有更好的环保性、安全性、长效性、适用范围广和经济性等优势，具有较高的应用前景和推广价值。
2、采用微生物养护剂，在施工和使用的过程中不会对环境造成较大的污染，能够有效的保护生态环境，保护施工人员和周围环境，起到环保的作用效果。
具体实施方式
本技术发明人通过对混凝土养护剂进行大量研究，创新的提出了微生物养护剂，以克服现有技术所存在的问题。
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。下列实施例中未注明具体条件的实验方法，通常按照国家标准测定。若没有相应的国家标准，则按照通用的国际标准、常规条件、或按照制造厂商所建议的条件进行。
除非另有定义或说明，本文中所使用的所有专业与科学用语与本领域技术熟练人员所熟悉的意义相同。此外任何与所记载内容相似或均等的方法及材料皆可应用于本发明方法中。
实施例
一种混凝土微生物养护剂，包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；所述营养物质包括磷元素、氮元素、钾元素，所述氮元素占总重量的1～5%，所述磷元素占总重量的0.5～2%，所述钾元素占总重量的0.5～2%。
所述微生物菌株选用益生菌，益生菌可以产生有机酸和酶等物质，从而促进混凝土的硬化和强度提高，益生菌为枯草芽孢杆菌；所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质，所述基质中还包括氨基酸混合物；
当益枯草芽孢杆菌为100份的时候，所述氨基酸混合物包括谷氨酸、精氨酸、天门
冬氨酸、缬氨酸，其中氨基酸混合物为250份、葡萄糖为500份，其中糖水为50000份的2%浓度
糖水；所述辅助剂为50份磷酸二氢钾、5份、0.5份、0.5份、0.5份、0.5份、0.5份。
制备的微生物养护剂在混凝土脱模后喷涂，28d混凝土碳化深度降低20%～30%，养护效果明显。
实施例
一种混凝土微生物养护剂，包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；所述营养物质包括磷元素、氮元素、钾元素，所述氮元素占总重量的1～5%，所述磷元素占总重量的0.5～2%，所述钾元素占总重量的0.5～2%。
所述微生物菌株选用酵母菌，该酵母菌为发酵酵母菌，酵母菌可以利用混凝土中的糖类和蛋白质等有机物，产生二氧化碳和酒精等有机物，从而促进混凝土的硬化和强度提高；所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质；
当酵母菌为100份的时候，葡萄糖为1000份，其中糖水为50000份的2%浓度糖水，所述辅助剂为500份酵母份、250份酪蛋白酸水解物、50份酵母精氨酸、25份碳酸氢钠，其中所述基质中的蛋白胨为250份。
制备的微生物养护剂在混凝土脱模后喷涂，28d混凝土碳化深度降低20%～30%，养护效果明显。
实施例
一种混凝土微生物养护剂，包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；所述营养物质包括磷元素、氮元素、钾元素，所述氮元素占总重量的1～5%，所述磷元素占总重量的0.5～2%，所述钾元素占总重量的0.5～2%。
所述微生物菌株选用解磷菌，解磷菌为磷酸盐溶解菌；所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质；
当磷酸盐溶解菌为100份的时候，所述辅助剂为硝酸铵50份、硫酸镁25份、磷酸二氢钾10份、氯化钙5份、硅酸钠2.5份。
制备的微生物养护剂在混凝土脱模后喷涂，28d混凝土碳化深度降低20%～30%，养护效果明显。
实施例
一种混凝土微生物养护剂，包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；所述营养物质包括磷元素、氮元素、钾元素，所述氮元素占总重量的1～5%，所述磷元素占总重量的0.5～2%，所述钾元素占总重量的0.5～2%。
所述微生物菌株选用解磷菌，解磷菌为硅酸盐细菌；所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质；
当磷酸盐溶解菌为100份的时候，所述辅助剂为硝酸铵50份、硫酸镁25份、磷酸二氢钾10份、氯化钙5份、硅酸钠2.5份。
制备的微生物养护剂在混凝土脱模后喷涂，28d混凝土碳化深度降低20%～30%，养护效果明显。
实施例
一种混凝土微生物养护剂，包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；所述营养物质包括磷元素、氮元素、钾元素，所述氮元素占总重量的1～5%，所述磷元素占总重量的0.5～2%，所述钾元素占总重量的0.5～2%。
所述微生物菌株选用解磷菌，解磷菌为硅酸盐细菌、硅酸盐细菌混合菌种；所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质；
当磷酸盐溶解菌为100份的时候，所述辅助剂为硝酸铵50份、硫酸镁25份、磷酸二氢钾10份、氯化钙5份、硅酸钠2.5份。
制备的微生物养护剂在混凝土脱模后喷涂，28d混凝土碳化深度降低20%～30%，养护效果明显。
实施例
一种混凝土微生物养护剂，包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；所述营养物质包括磷元素、氮元素、钾元素，所述氮元素占总重量的1～5%，所述磷元素占总重量的0.5～2%，所述钾元素占总重量的0.5～2%。
所述微生物菌株包括硝化细菌，硝化细菌可以将混凝士中的氨氮转化为硝酸盐，从而促进混凝士的硬化和强度提高，所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质。
制备的微生物养护剂在混凝土脱模后喷涂，28d混凝土碳化深度降低20%～30%，养护效果明显。
实施例
一种混凝土微生物养护剂，包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；所述营养物质包括磷元素、氮元素、钾元素，所述氮元素占总重量的1～5%，所述磷元素占总重量的0.5～2%，所述钾元素占总重量的0.5～2%。
所述微生物菌株包括乳酸菌，所述乳酸菌为乳杆菌、链球菌、片球菌中一种或者多种组合而成，乳酸菌可以发酵混凝土中的糖类，产生乳酸和醋酸等有机物从而促进混凝士的硬化和强度提高，所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质。
制备的微生物养护剂在混凝土脱模后喷涂，28d混凝土碳化深度降低20%～30%，养护效果明显。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (9)
1.一种混凝土微生物养护剂，其特征在于，所述混凝土微生物养护剂包括由微生物菌株、基质20%～50%、营养物质2%～9%、微量元素0.1%～0.5%和不超过1%的辅助剂；
所述微生物菌株包括硝化细菌、解磷菌、乳酸菌、酵母菌、益生菌；
所述基质包括糖水、葡萄糖、果糖、明胶、蛋白胨，所述基质为液态基质；
所述营养物质包括磷元素、氮元素、钾元素。
2.根据权利要求1所述的一种混凝土微生物养护剂，其特征在于，所述益生菌为枯草芽孢杆菌。
3.根据权利要求1所述的一种混凝土微生物养护剂，其特征在于，所述酵母菌为发酵酵母菌。
4.根据权利要求1所述的一种混凝土微生物养护剂，其特征在于，所述解磷菌为磷酸盐溶解菌、硅酸盐细菌中一种或者两种组合而成。
5.根据权利要求1所述的一种混凝土微生物养护剂，其特征在于，所述乳酸菌为乳杆菌、链球菌、片球菌中一种或者多种组合而成。
6.根据权利要求1所述的一种混凝土微生物养护剂，其特征在于，所述氮元素占总重量的1～5%，所述磷元素占总重量的0.5～2%，所述钾元素占总重量的0.5～2%。
7.根据权利要求2所述的一种混凝土微生物养护剂，其特征在于，当微生物菌株为益生
菌的时候，其中益生菌为100份，所述基质中还包括氨基酸混合物，所述氨基酸混合物包括
谷氨酸、精氨酸、天门冬氨酸、缬氨酸，其中氨基酸混合物为250份、葡萄糖为500份，所述辅
助剂为50份磷酸二氢钾、5份、0.5份、0.5份、0.5份、
0.5份、0.5份。
8.根据权利要求3所述的一种混凝土微生物养护剂，其特征在于，当微生物菌种为酵母菌的时候，其中酵母菌为100份，所述辅助剂为500份酵母份、250份酪蛋白酸水解物、50份酵母精氨酸、25份碳酸氢钠，其中所述基质中的蛋白胨为250份。
9.根据权利要求4所述的一种混凝土微生物养护剂，其特征在于，当微生物菌种为解磷菌的时候，其中解磷菌为100份，所述辅助剂为硝酸铵50份、硫酸镁25份、磷酸二氢钾10份、氯化钙5份、硅酸钠2.5份。