CN116830335A - 具有改善的电解液粘度和cb值的锂离子电池和用电装置 - Google Patents
具有改善的电解液粘度和cb值的锂离子电池和用电装置 Download PDFInfo
- Publication number
- CN116830335A CN116830335A CN202280013146.2A CN202280013146A CN116830335A CN 116830335 A CN116830335 A CN 116830335A CN 202280013146 A CN202280013146 A CN 202280013146A CN 116830335 A CN116830335 A CN 116830335A
- Authority
- CN
- China
- Prior art keywords
- active material
- battery
- lithium
- positive electrode
- electrolyte
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种锂离子电池,其包含正极、负极和电解液,其中,根据GB/T10247‑2008测量,电解液在25℃下的粘度c为1‑6mPa.s;并且负极可嵌锂容量与正极可脱锂容量的比值CB为1.05‑1.5。锂离子电池具有大倍率的快充能力以及良好的循环性能。
Description
技术领域
本申请涉及锂电池技术领域,尤其涉及一种锂离子电池和用电装置。
背景技术
近年来,随着锂离子电池的应用范围越来越广泛,锂离子电池广泛应用于水力、火力、风力和太阳能电站等储能电源系统,以及电动工具、电动自行车、电动摩托车、电动汽车、军事装备、航空航天等多个领域。但是相比于传统的燃油驱动设备,里程焦虑、充电时间长等问题成为阻碍二次电池发展的主要问题,如何提高二次电池的快充能力是本领域技术人员的关注的焦点之一。
提高电池的快充能力是一个系统工程,其需要对电池的材料作出改变和升级。传统技术研究最多的是负极材料的改进,但同时还需要电解液、导电剂等材料的配合。因此,现有的具有快充能力的电池仍需要进一步改进。
发明内容
本申请是鉴于上述课题而进行的,其目的在于,提供一种具有改善的电解液粘度和CB值的锂离子电池,其包含特定粘度的电解液并具有特定范围的负极可嵌锂容量与正极可脱锂容量的比值CB,使得相应的电池具有大倍率的快充能力以及良好的循环性能。
为了达到上述目的,本申请提供一种锂离子电池和包含其的用电装置。
本申请的第一方面提供了一种锂离子电池,其包含正极、负极和电解液,其中,所述电解液在25℃下的粘度c为1-6mPa.s;并且负极可嵌锂容量与正极可脱锂容量的比值CB为1.05-1.5。
本申请的锂离子电池通过包含特定粘度的电解液并具有特定范围的负极可嵌锂容量与正极可脱锂容量的比值CB,使得锂离子的液相传输条件得到改善,并在负极提供更多的活性位点供锂离子嵌入,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述电池在35℃下自0%荷电状态到70%荷电状态的充电过程中存在大于等于4倍的单位时间内正极可脱锂容量的电流。由此,保证进一步改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述电池在35℃下自0%荷电状态到70%荷电状态的充电过程中的平均电流大于等于4倍的单位时间内正极可脱嵌容量。由此,保证进一步改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述负极包含集流体及附着在集流体至少一个表面上的负极活性材料层,其中所述活性材料层包括包含第一负极活性材料的第一活性材料层,以及附着在所述第一活性材料层远离所述集流体的表面上的包含第二负极活性材料的第二活性材料层。由此,可进一步在负极提供更多的活性位点供锂离子嵌入,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述第一负极活性材料的平均体积粒径Dv50大于第二负极活性材料的平均体积粒径Dv50。由此,可进一步在负极提供更多的活性位点供锂离子嵌入,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述第一负极活性材料层的压实密度大于第二负极活性材料层的压实密度。由此,可进一步在负极提供更多的活性位点供锂离子嵌入,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述负极活性材料层的厚度为30-150μm,孔隙率为20-60%,压实密度为1.2-1.9g/cm3。由此,可进一步在负极提供更多的活性位点供锂离子嵌入,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述电解液包含锂盐、溶剂和添加剂;其中所述锂盐包含主锂盐和副锂盐。由此,可进一步使得锂离子的液相传输条件得到改善,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述主锂盐与副锂盐不同,并且所述主锂盐或副锂盐各自独立地选自LiPF6、LiN(SO2F)2、LiBF4、LiN(CF3SO2)2、LiClO4、LiAsF6、LiB(C2O4)2、LiBF2C2O4、LiDFOP、LiPO2F2、LiFSO3、LiF中的至少一种。由此,可进一步使得锂离子的液相传输条件得到改善,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述主锂盐为六氟磷酸锂或LiFSI,其含量为8-20wt%,基于所述电解液的总重量计;所述副锂盐为二氟草酸硼酸锂、LiBF4、LiB(C2O4)2、二氟二草酸磷酸锂(LiDFOP)中的至少一种,其含量为0.001wt%-2wt%,基于所述电解液的总重量计。由此,可进一步使得锂离子的液相传输条件得到改善,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述溶剂包含环状酯和线性酯;所述环状酯的含量占溶剂质量的5-40%,所述线性酯的含量占溶剂质量的60-95%。由此,进一步改善电解液的粘度,可使得锂离子的液相传输条件得到改善,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述环状酯为碳酸亚乙酯、碳酸亚丙基酯或其组合;所述线性酯包含碳酸二甲酯。由此,进一步改善电解液的粘度,可使得锂离子的液相传输条件得到改善,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述线性酯选自碳酸二乙酯、碳酸甲乙酯、甲酸甲酯、乙酸甲酯、乙酸乙酯、乙酸丁酯、丙酸甲酯、丁酸甲酯、丁酸乙酯、丁酸丙酯、丁酸丁酯、乙酸异丙酯、乙酸异戊酯和其组合。由此,进一步改善电解液的粘度,可使得锂离子的液相传输条件得到改善,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,在所述电解液中,锂盐摩尔浓度b(mol/L)、溶剂中线性酯占溶剂质量的百分比a%与电解液在25℃下的粘度c满足以下关系式:
2≤c+2*a%≤8;
2≤c+b≤8。由此,进一步改善电解液的粘度,可使得锂离子的液相传输条件得到改善,从而改善所述电池的大倍率快充能力和循环性能。
在任意实施方式中,所述正极包含集流体及附着在集流体至少一个表面上的包含正极活性材料的正极活性材料层,所述正极活性材料包含式LiNixCoyQzM1-x-y-zO2的三元材料,其中Q为Mn或Al,M包含Co、Ni、Mn、Mg、Cu、Zn、Al、Sn、B、Ga、Cr、Sr、V和Ti中至少一种,0≤x<1,0≤y≤1,0≤z≤1,x+y+z≤1。由此,进一步改善所述电池的大倍率快充能力和循环性能。
本申请的第二方面提供一种用电装置,包括选自本申请的第一方面的二次电池。
本申请的二次电池通过包含特定粘度的电解液并具有特定范围的负极可嵌锂容量与正极可脱锂容量的比值CB,改善锂离子的液相传输条件,使得锂离子快速迁移至负极,并在负极提供更多的活性位点供锂离子嵌入,从而改善所述电池的大倍率快充能力和循环性能。
附图说明
图1是本申请一实施方式的二次电池的示意图。
图2是图1所示的本申请一实施方式的二次电池的分解图。
图3是本申请一实施方式的二次电池用作电源的用电装置的示意图。
附图标记说明:
5、二次电池;51、壳体;52、电极组件;53、盖板;6、用电装置。
具体实施方式
以下,适当地参照附图详细说明具体公开了本申请的锂离子电池和用电装置的实施方式。但是会有省略不必要的详细说明的情况。例如,有省略对已众所周知的事项的详细说明、实际相同结构的重复说明的情况。这是为了避免以下的说明不必要地变得冗长,便于本领域技术人员的理解。此外,附图及以下说明是为了本领域技术人员充分理解本申请而提供的,并不旨在限定权利要求书所记载的主题。
本申请所公开的“范围”以下限和上限的形式来限定,给定范围是通过选定一个下限和一个上限进行限定的,选定的下限和上限限定了特别范围的边界。这种方式进行限定的范围可以是包括端值或不包括端值的,并且可以进行任意地组合,即任何下限可以与任何上限组合形成一个范围。例如,如果针对特定参数列出了60-120和80-110的范围,理解为60-110和80-120的范围也是预料到的。此外,如果列出的最小范围值1和2,和如果列出了最大范围值3,4和5,则下面的范围可全部预料到:1-3、1-4、1-5、2-3、2-4和2-5。在本申请中,除非有其他说明,数值范围“a-b”表示a到b之间的任意实数组合的缩略表示,其中a和b都是实数。例如数值范围“0-5”表示本文中已经全部列出了“0-5”之间的全部实数,“0-5”只是这些数值组合的缩略表示。另外,当表述某个参数为≥2的整数,则相当于公开了该参数为例如整数2、3、4、5、6、7、8、9、10、11、12等。
如果没有特别的说明,本申请的所有实施方式以及可选实施方式可以相互组合形成新的技术方案。
如果没有特别的说明,本申请的所有技术特征以及可选技术特征可以相互组合形成新的技术方案。
如果没有特别的说明,本申请的所有步骤可以顺序进行,也可以随机进行,优选是顺序进行的。例如,所述方法包括步骤(a)和(b),表示所述方法可包括顺序进行的步骤(a)和(b),也可以包括顺序进行的步骤(b)和(a)。例如,所述提到所述方法还可包括步骤(c),表示步骤(c)可以任意顺序加入到所述方法,例如,所述方法可以包括步骤(a)、(b)和(c),也可包括步骤(a)、(c)和(b),也可以包括步骤(c)、(a)和(b)等。
如果没有特别的说明,本申请所提到的“包括”和“包含”表示开放式,也可以是封闭式。例如,所述“包括”和“包含”可以表示还可以包括或包含没有列出的其他组分,也可以仅包括或包含列出的组分。
如果没有特别的说明,在本申请中,术语“或”是包括性的。举例来说,短语“A或B”表示“A,B,或A和B两者”。更具体地,以下任一条件均满足条件“A或B”:A为真(或存在)并且B为假(或不存在);A为假(或不存在)而B为真(或存在);或A和B都为真(或存在)。
目前,相比于传统的燃油驱动设备,里程焦虑、充电时间长等问题成为阻碍二次电池发展的主要问题,如何提高二次电池的快充能力是本领域技术人员的关注的焦点之一。提高电池的快充能力是一个系统工程,其需要对电池的材料作出改变和升级。传统技术研究最多的是负极材料的改进,但同时还需要电解液、导电剂等材料的配合。因此,现有的具有快充能力的电池仍需要进一步改进。发明人研究发现本申请第一方面的锂离子电池包含特定粘度的电解液并具有特定范围的负极可嵌锂容量与正极可脱锂容量的比值CB,使得其具有大倍率的快充能力以及良好的循环性能。
锂离子电池
在一些实施方式中,本申请提供一种锂离子电池,其包含正极、负极和电解液,其中,所述电解液在25℃下的粘度c为1-6mPa.s,优选2-5mPa.s,进一步可选为3.5-4mPa.s,根据GB/T10247-2008测量;并且负极可嵌锂容量与正极可脱锂容量的比值CB为1.05-1.5,可选为1.1-1.3,进一步可选为1.1-1.2。
本申请的锂离子电池通过包含特定粘度的电解液并具有特定范围的负极可嵌锂容量与正极可脱锂容量的比值CB,能够实现正负极较好较快的浸润回吸,使得锂离子的液相传输条件得到改善,并在负极提供更多的活性位点供锂离子嵌入,从而改善所述电池的大倍率快充能力和循环性能。
在本申请中,所述术语“正极可脱锂容量”意指在电池中,正极材料实际的可脱锂容量。其测试方法如下:在PRS340/11-119-11布劳恩手套箱中拆解电池,取正极极片,组装成正极-锂片的CR2430型号半扣式电池,采用的正极极片面积为a mm2,其中电解液采用1MLiPF6于EC/EMC/DEC=3/5/2中的溶液;然后将组装好的半扣式电池静置3h,测试在25℃下进行,采用0.1C先在电压区间2.5-eV下进行充电(Charge)脱锂,其中e为电芯设计的使用上限电压,再采用0.05C放电(Discharge)嵌锂至2.5V,循环2次,取第二次循环的放电扣电容量记为Y mAh,实际电池设计的正极极片长为b mm,宽为c mm,正极活性材料涂覆于正极集流体的面数d,则正极脱锂容量=Y/a*b*c*d。
在一些实施方式中,所述正极可脱锂容量为2000-300000mAh,可选为3000-150000mAh,进一步可选为3000-5000mAh。
在本申请中,所述术语“负极可嵌锂容量”意指在电池中,负极材料实际的可嵌锂容量。其测试方法为:在PRS340/11-119-11布劳恩手套箱中拆解电池,取负极极片,组装成负极-锂片的CR2430型号半扣式电池,采用的负极极片面积为f mm2,其中电解液采用1MLiPF6于EC/EMC/DEC=3/5/2中的溶液;然后将组装好的半扣式电池静置3h,测试在25℃下进行,采用0.1C先在电压区间2V-0V下进行放电(Discharge)嵌锂,再采用0.05C充电(Discharge)脱锂至2V,循环2次,取第二次循环的放电扣电容量记为ZmAh,实际电池设计的负极极片长为h mm,宽为i mm,负极活性材料涂覆于负极集流体的面数d,则负极可嵌锂容量=Z/f*h*i*d。
在一些实施方式中,所述负极可嵌锂容量为2100-315000mAh,可选为3000-100000mAh,进一步可选为3500-4500mAh。
在一些实施方式中,所述电池在35℃下自0%荷电状态(SOC)到70%荷电状态的充电过程(0-70%SOC)中存在大于等于4倍的单位时间内正极可脱嵌容量的电流,可选地所述电流大于等于5倍的单位时间内正极可脱嵌容量,进一步可选地为4倍至6.5倍的单位时间内正极可脱嵌容量。由此,保证进一步改善所述电池的大倍率快充能力和循环性能。在该实施方式中,所述电流为瞬时电流。
在本申请中,“单位时间内正极可脱锂容量”是指正极在单位时间(1h)内的脱锂量;在此过程中产生的平均电流作为本申请中电流量化的基准。由此,可将正极可脱锂容量与电流关联起来。
在一些实施方式中,在35℃下自0%荷电状态到70%荷电状态的充电过程中通常可采用恒流直充的方式,例如以4倍的单位时间内正极可脱嵌容量的电流从0%荷电状态充电至70%荷电状态;也可以采用分步充电方式,例如0-10%SOC采用A倍的单位时间内正极可脱嵌容量的电流,10-20%SOC采用B倍的单位时间内正极可脱嵌容量的电流,20-30%SOC采用C倍的单位时间内正极可脱嵌容量的电流,30-40%SOC采用D倍的单位时间内正极可脱嵌容量的电流,40-50%SOC采用E倍的单位时间内正极可脱嵌容量的电流,50-60%SOC采用F倍的单位时间内正极可脱嵌容量的电流,60-70%SOC采用G倍的单位时间内正极可脱嵌容量的电流等,其中A、B、C、D、E、F至少一个不为4。本领域技术人员可以理解,在分步充电方式中,分步的SOC以及电流大小可根据需要进行调整。
对于已经封装的电池,采用正极脱锂容量检测方法测试得出正极可脱锂容量;采用如上测充电模式对电池进行充电2个循环,然后拆解取正极极片,采用正极可脱锂容量检测方法测试得出此时正极的脱锂容量Z,如果Z/X≥40%,则认为符合满足4倍的单位时间内正极可脱嵌容量的充电倍率。
在一些实施方式中,所述电池在35℃自0%荷电状态到70%荷电状态的充电过程(0-70%SOC)中的平均电流大于等于4倍的单位时间内正极可脱嵌容量。由此,保证进一步改善所述电池的大倍率快充能力和循环性能。
在一个实施方式中,所述0-70%SOC的平均电流的测试方法为:采用恒流直充的方式的话,平均电流即为充电电流;采用如上所述的分步充电方式的话,平均电流为(A+B+C+D+E+F+G)/7。
在一些实施方式中,所述负极包含集流体及附着在集流体至少一个表面上的负极活性材料层,其中所述活性材料层包括包含第一负极活性材料的第一活性材料层,以及附着在所述第一活性材料层远离所述集流体的表面上的包含第二负极活性材料的第二活性材料层。
在一些实施方式中,所述第一负极活性材料的平均体积粒径Dv50大于第二负极活性材料的平均体积粒径Dv50。
在一些实施方式中,所述第一负极活性材料的平均体积粒径Dv50为10-20μm,第二负极活性材料的平均体积粒径Dv50为9-19μm,根据粒度分布激光衍射法(具体参照GB/T19077.1-2009)测量。
在一些实施方式中,所述第一负极活性材料层的压实密度大于第二负极活性材料层的压实密度。
在一些实施方式中,所述第一负极活性材料层的压实密度为1.3-2g/cm3,第二负极活性材料层的压实密度为1.2-1.9g/cm3,根据分别通过标准天平称量负极材料层质量、通过直尺测量负极极片涂布面积,然后可计算负极材料层单位面积质量,即涂布面密度CW(mg/cm2)。然后通过扫描电镜法离子抛光断面形貌分析(具体参照JY/T010-1996)测量负极材料层厚度(至少测量5处,取平均值),根据涂膜的压实密度=负极极片涂布面密度CW(mg/cm2)/负极材料层厚度(cm),计算得出负极材料层压实密度PD(单位mg/cm3),再换算成g/cm3。
在一些实施方式中,所述第一负极活性材料层的厚度为10-120μm,第二负极活性材料层的厚度为10-120μm,根据扫描电镜法离子抛光断面形貌分析(参照JY/T010-1996)(至少测量5处,取平均值)测量。
在一些实施方式中,所述负极活性材料层的厚度为30-150μm,孔隙率为20-60%,可选为25-40%,进一步可选为27-33%;压实密度为1.2-1.9g/cm3,可选为1.3-1.8g/cm3。
在一些实施方式中,所述电解液包含锂盐、溶剂和添加剂;其中所述锂盐包含主锂盐和副锂盐。
在一些实施方式中,所述主锂盐与副锂盐不同,并且所述主锂盐或副锂盐各自独立地选自LiPF6、LiN(SO2F)2(LiFSI)、LiBF4、LiN(CF3SO2)2(LiTFSI)、LiClO4、LiAsF6、LiB(C2O4)2(LiBOB)、LiBF2C2O4(LiDFOB)、二氟二草酸磷酸锂(LiDFOP)、LiPO2F2、LiFSO3、LiF中的至少一种。所述主锂盐与副锂盐区别在于其含量不同。
在一些优选的实施方式中,所述主锂盐为六氟磷酸锂或LiFSI或其二者混合物,其含量为8-20wt%,可选为10-15wt%,基于所述电解液的总重量计;所述副锂盐为二氟草酸硼酸锂LiBF2C2O4(LiDFOB)、LiBF4、LiB(C2O4)2(LiBOB)、二氟二草酸磷酸锂(LiDFOP)中的至少一种,可选为LiDFOB或LiDFOP,其含量为0.001wt%-2wt%,例如1-2wt%,可选为0.8-1.5wt%,基于所述电解液的总重量计。
在一些优选的实施方式中,电解液中锂盐的摩尔浓度b为0.6-1.5mol/L,可选为0.8-1.2mol/L。
在一些实施方式中,所述溶剂包含环状酯和线性酯;所述环状酯的含量占溶剂质量的5-40%,可选为25-35%,所述线性酯的含量占溶剂质量的60-95%,可选地为65-80%。
在一些实施方式中,所述环状酯为碳酸亚乙酯(EC)、碳酸亚丙基酯(PC)或其组合;所述线性酯包含碳酸二甲酯(DMC)。
在一些实施方式中,所述线性酯除了DMC,还可包含选自以下组分的至少一种:碳酸二乙酯(DEC)、碳酸甲乙酯(EMC)、甲酸甲酯、乙酸甲酯(MA)、乙酸乙酯(EA)、乙酸丁酯、乙腈(SN)、丙酸甲酯、丙酸乙酯(EP)、丁酸甲酯、丁酸乙酯、丁酸丙酯、丁酸丁酯、乙酸异丙酯、乙酸异戊酯和其组合;可选为碳酸二乙酯DEC、乙酸乙酯EA、乙酸甲酯MA、乙腈SN、丙酸乙酯EP和组合。
在一个优选的实施方式中,所述环状酯为碳酸亚乙酯(EC),所述线性酯包含碳酸二甲酯(DMC)和碳酸甲乙酯(EMC)。
在一些实施方式中,在所述电解液中,锂盐摩尔浓度b(mol/L)、溶剂中线性酯占溶剂质量的百分比a%与电解液在25℃下的粘度c满足以下关系式:
2≤c+2*a%≤8,可选为3≤c+2*a%≤7;
2≤c+b≤8,可选为3≤c+b≤7。
在一些实施方式中,所述正极包含集流体及附着在集流体至少一个表面上的包含正极活性材料的正极活性材料层,所述正极活性材料包含式LiNixCoyQzM1-x-y-zO2的三元材料,其中Q为Mn或Al,M包含Co、Ni、Mn、Mg、Cu、Zn、Al、Sn、B、Ga、Cr、Sr、V和Ti中至少一种,0≤x<1,可选为0.5≤x<1;0≤y≤1,0≤z≤1,x+y+z≤1。
以下适当参照附图对本申请的锂离子电池和用电装置进行说明。
通常情况下,锂离子电池包括正极、负极、电解质和隔离膜。在电池充放电过程中,活性锂离子在正极和负极之间往返嵌入和脱出。电解质在正极和负极之间起到传导离子的作用。隔离膜设置在正极和负极之间,主要起到防止正负极短路的作用,同时可以使锂离子通过。
正极
所述正极包括正极集流体以及设置在正极集流体至少一个表面的正极膜层,所述正极膜层包括正极活性材料。所述正极活性材料包含式LiNixCoyQzM1-x-y-zO2的三元材料,其中Q为Mn或Al,M包含Co、Ni、Mn、Mg、Cu、Zn、Al、Sn、B、Ga、Cr、Sr、V和Ti中至少一种,0≤x<1,可选为0.5≤x<1;0≤y≤1,0≤z≤1,x+y+z≤1。
作为示例,正极集流体具有在其自身厚度方向相对的两个表面,正极膜层设置在正极集流体相对的两个表面的其中任意一者或两者上。
在一些实施方式中,所述正极集流体可采用金属箔片或复合集流体。例如,作为金属箔片,可采用铝箔。复合集流体可包括高分子材料基层和形成于高分子材料基层至少一个表面上的金属层。复合集流体可通过将金属材料形成在高分子材料基材上而形成。其中,金属材料包括但不限于铝、铝合金、镍、镍合金、钛、钛合金、银及银合金等。高分子材料基材(如聚丙烯(PP)、聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸丁二醇酯(PBT)、聚苯乙烯(PS)、聚乙烯(PE)等的基材)
在一些实施方式中,所述正极活性材料可为锂镍钴氧化物、锂镍钴锰氧化物(LiNi1/3Co1/3Mn1/3O2(也可以简称为NCM333)、LiNi0.5Co0.2Mn0.3O2(也可以简称为NCM523)、LiNi0.5Co0.25Mn0.25O2(也可以简称为NCM211)、LiNi0.6Co0.2Mn0.2O2(也可以简称为NCM622)、LiNi0.65Co0.07Mn0.28O2、LiNi0.8Co0.1Mn0.1O2(也可以简称为NCM811))、锂镍钴铝氧化物(如LiNi0.85Co0.15Al0.05O2)、LiNi1/3Co1/3Al1/3O2或其改性化合物中的至少一种,优选为NCM622。但本申请并不限定于这些材料,还可以使用其他可被用作电池正极活性材料的传统材料。这些正极活性材料可以仅单独使用一种,也可以将两种以上组合使用。
在一些实施方式中,所述正极活性材料还可包含本领域公知的用于电池的其他正极活性材料。作为示例,其他正极活性材料可包括以下材料中的至少一种:橄榄石结构的含锂磷酸盐、锂钴氧化物(如LiCoO2)、锂镍氧化物(如LiNiO2)、锂锰氧化物(如LiMnO2、LiMn2O4)、锂锰钴氧化物、锂镍锰氧化物及其改性化合物等中的至少一种。橄榄石结构的含锂磷酸盐的示例可包括但不限于磷酸铁锂(如LiFePO4(也可以简称为LFP))、磷酸铁锂与碳的复合材料、磷酸锰锂(如LiMnPO4)、磷酸锰锂与碳的复合材料、磷酸锰铁锂、磷酸锰铁锂与碳的复合材料中的至少一种。
在一些实施方式中,所述正极活性材料在正极膜层中的重量比为80-100重量%,基于正极膜层的总重量计。
在一些实施方式中,正极膜层还可选地包括粘结剂。作为示例,所述粘结剂可以包括聚偏氟乙烯(PVDF)、聚四氟乙烯(PTFE)、偏氟乙烯-四氟乙烯-丙烯三元共聚物、偏氟乙烯-六氟丙烯-四氟乙烯三元共聚物、四氟乙烯-六氟丙烯共聚物及含氟丙烯酸酯树脂中的至少一种。所述粘结剂在正极膜层中的重量比为0-20重量%,基于正极膜层的总重量计。
在一些实施方式中,正极膜层还可选地包括导电剂。作为示例,所述导电剂可以包括超导碳、炭黑(例如乙炔黑、科琴黑)、碳点、碳纳米管、石墨烯及碳纳米纤维中的至少一种。所述导电剂在正极膜层中的重量比为0-20重量%,基于正极膜层的总重量计。
在一些实施方式中,可以通过以下方式制备正极极片:将上述用于制备正极极片的组分,例如正极活性材料、导电剂、粘结剂和任意其他的组分分散于溶剂(例如N-甲基吡咯烷酮)中,形成正极浆料,其中所述正极浆料固含量为40-80wt%,室温下的粘度调整到5000-25000mPa·s,将正极浆料涂覆在正极集流体的表面,烘干后经过冷轧机冷压后形成正极极片;正极粉末涂布单位面密度为12-26mg/cm2,正极极片压实密度为2.0-3.6g/cm3,可选为2.3-3.5g/cm3。所述压实密度的计算公式为
压实密度=涂布面密度/(挤压后极片厚度-集流体厚度)。
负极
所述负极包括负极集流体以及设置在负极集流体至少一个表面上的负极膜层(也称为负极活性材料层),所述负极膜层包括负极活性材料。所述负极本申请如上所述的关于负极的技术特征。
作为示例,负极集流体具有在其自身厚度方向相对的两个表面,负极膜层设置在负极集流体相对的两个表面中的任意一者或两者上。
在一些实施方式中,所述负极集流体可采用金属箔片或复合集流体。例如,作为金属箔片,可以采用铜箔。复合集流体可包括高分子材料基层和形成于高分子材料基材至少一个表面上的金属层。复合集流体可通过将金属材料形成在高分子材料基材上而形成。其中,金属材料包括但不限于铜、铜合金、镍、镍合金、钛、钛合金、银及银合金等,高分子材料基材包括但不限于聚丙烯(PP)、聚对苯二甲酸乙二醇酯(PET)、聚对苯二甲酸丁二醇酯(PBT)、聚苯乙烯(PS)、聚乙烯(PE)等基材。
在一些实施方式中,负极活性材料可采用本领域公知的用于电池的负极活性材料。作为示例,负极活性材料可包括以下材料中的至少一种:人造石墨、天然石墨、软炭、硬炭、硅基材料、锡基材料和钛酸锂等。所述硅基材料可选自单质硅、硅氧化合物、硅碳复合物、硅氮复合物以及硅合金中的至少一种。所述锡基材料可选自单质锡、锡氧化合物以及锡合金中的至少一种。但本申请并不限定于这些材料,还可以使用其他可被用作电池负极活性材料的传统材料。这些负极活性材料可以仅单独使用一种,也可以将两种以上组合使用。
在一些实施方式中,所述负极活性材料包含天然石墨、人造石墨、中间相微碳球(简称为MCMB)、硬碳、软碳、硅、硅-碳复合物、硅氧复合物、Li-Sn合金、Li-Sn-O合金、Sn、SnO、SnO2、尖晶石结构的锂化TiO2-Li4Ti5O12、Li-Al合金中的一种或几种。
在一些实施方式中,所述负极包含集流体及附着在集流体至少一个表面上的负极活性材料层,其中所述活性材料层包括包含第一负极活性材料的第一活性材料层,以及附着在所述第一活性材料层远离所述集流体的表面上的包含第二负极活性材料的第二活性材料层。
在一些实施方式中,所述第一负极活性材料为天然石墨、人造石墨、中间相微碳球(简称为MCMB)、硬碳、软碳、硅、硅-碳复合物、硅氧复合物、Li-Sn合金、Li-Sn-O合金、Sn、SnO、SnO2、尖晶石结构的锂化TiO2-Li4Ti5O12、Li-Al合金中的至少一种;所述第二负极活性材料为天然石墨、人造石墨、中间相微碳球(简称为MCMB)、硬碳、软碳、硅、硅-碳复合物、硅氧复合物、Li-Sn合金、Li-Sn-O合金、Sn、SnO、SnO2、尖晶石结构的锂化TiO2-Li4Ti5O12、Li-Al合金中的至少一种。
在一些实施方式中,如果负极活性材料包括两种及两种以上的混合物质,那么负极活性材料的平均体积粒径是指所述混合物质的平均体积粒径。
在一些实施方式中,负极活性材料包含硅。所述硅含量占负极活性材料层重量的1-25%,分布于活性材料层的至少一层中。
在一些实施方式中,在所述第一活性材料层中硅含量(以SiO2计)为0-25%,基于所述第一活性材料层的重量计;在所述第二活性材料层中硅含量(以SiO2计)为0-25%,基于第二活性材料层的重量计。
在一些实施方式中,所述负极活性材料在负极膜层中的重量比为70-100重量%,基于负极膜层的总重量计。
在一些实施方式中,负极膜层还可选地包括粘结剂。所述粘结剂可选自丁苯橡胶(SBR)、聚丙烯酸(PAA)、聚丙烯酸钠(PAAS)、聚丙烯酰胺(PAM)、聚乙烯醇(PVA)、海藻酸钠(SA)、聚甲基丙烯酸(PMAA)及羧甲基壳聚糖(CMCS)中的至少一种。所述粘结剂在负极膜层中的重量比为0-30重量%,基于负极膜层的总重量计。
在一些实施方式中,负极膜层还可选地包括导电剂。导电剂可选自超导碳、炭黑(例如乙炔黑、科琴黑)、碳点、碳纳米管、石墨烯及碳纳米纤维中的至少一种。所述导电剂在负极膜层中的重量比为0-20重量%,基于负极膜层的总重量计。
在一些实施方式中,负极膜层还可选地包括其他助剂,例如增稠剂(如羧甲基纤维素钠(CMC-Na))等。所述其他助剂在负极膜层中的重量比为0-15重量%,基于负极膜层的总重量计。
在一些实施方式中,可以通过以下方式制备负极极片:将上述用于制备负极极片的组分,例如负极活性材料、导电剂、粘结剂和任意其他组分分散于溶剂(例如去离子水)中,形成负极浆料,其中所述负极浆料固含量为30-70wt%,室温下的粘度调整到2000-10000mPa·s;将所得到的负极浆料涂覆在负极集流体上,经过干燥工序,冷压例如对辊,得到负极极片。负极粉末涂布单位面密度为6-16mg/cm2,负极极片压实密度1.2-2.0g/m3。
负极活性材料层的孔隙率可通过气体置换法得到,孔隙率P=(V1-V2)/V1×100%,V1表示负极膜片的表观体积,V2表示负极膜片的真实体积。
单位面积负极中负极活性物质的质量的可使用标准天平称量得到。
负极活性材料层的厚度可采用万分尺测量得到,例如可使用型号为Mitutoyo293-100、精度为0.1μm的万分尺测量得到。需要说明的是,本发明所述的负极活性材料层厚度是指经冷压压实后并用于组装电池的负极极片中的负极活性材料层的厚度。
电解液
电解液在正极极片和负极极片之间起到传导离子的作用。
所述电解液包含本申请如上所述的技术特征。
在一些实施方式中,所述电解液包含锂盐、溶剂和添加剂;其中所述锂盐包含主锂盐和副锂盐。
在一些实施方式中,所述主锂盐与副锂盐不同,并且所述主锂盐或副锂盐各自独立地选自六氟磷酸锂(LiPF6)、双氟磺酰亚胺锂(LiN(SO2F)2,LiFSI)、四氟硼酸锂(LiBF4)、双三氟甲磺酰亚胺锂(LiTFSI)、高氯酸锂(LiClO4)、六氟砷酸锂(LiAsF6)、三氟甲磺酸锂(LiTFS)、二草酸硼酸锂(LiB(C2O4)2,LiBOB)、二氟草酸硼酸锂(LiBF2C2O4,LiDFOB)、二氟磷酸锂(LiPO2F2)、二氟二草酸磷酸锂(LiDFOP)、LiPO2F2、LiFSO3、LiF及四氟草酸磷酸锂(LiTFOP)中的一种或几种。
在一些实施方式中,所述主锂盐与副锂盐不同,并且所述主锂盐或副锂盐各自独立地选自LiPF6、LiN(SO2F)2(LiFSI)、LiBF4、LiN(CF3SO2)2(LiTFSI)、LiClO4、LiAsF6、LiB(C2O4)2(LiBOB)、LiBF2C2O4(LiDFOB)、二氟二草酸磷酸锂(LiDFOP)、LiPO2F2、LiFSO3、LiF中的至少一种。所述主锂盐与副锂盐区别在于其含量不同。
在一些优选的实施方式中,所述主锂盐为六氟磷酸锂或LiFSI,其含量为8-20wt%,基于所述电解液的总重量计;所述副锂盐为二氟草酸硼酸锂LiBF2C2O4(LiDFOB)、LiBF4、LiB(C2O4)2(LiBOB)、二氟二草酸磷酸锂(LiDFOP)中的至少一种,可选为LiDFOB或LiDFOP,其含量为0.001wt%-2wt%,基于所述电解液的总重量计。
在一些优选的实施方式中,电解液中锂盐的摩尔浓度b为0.8-1.2mol/L。
在一些实施方式中,所述溶剂包含环状酯和线性酯;所述环状酯的含量占溶剂质量的5-40%,所述线性酯的含量占溶剂质量的60-95%。
在一些实施方式中,所述环状酯为碳酸亚乙酯(EC)、碳酸亚丙基酯(PC)或其组合;所述线性酯包含碳酸二甲酯(DMC)。
在一些实施方式中,所述线性酯除了DMC,还可包含选自以下组分的至少一种:碳酸二乙酯(DEC)、碳酸甲乙酯(EMC)、甲酸甲酯、乙酸甲酯(MA)、乙酸乙酯(EA)、乙酸丁酯、乙腈(SN)、丙酸甲酯、丙酸乙酯(EP)、丁酸甲酯、丁酸乙酯、丁酸丙酯、丁酸丁酯、乙酸异丙酯、乙酸异戊酯和其组合;可选为碳酸二乙酯DEC、乙酸乙酯EA、乙酸甲酯MA、乙腈SN、丙酸乙酯EP和组合。
在一个优选的实施方式中,所述环状酯为碳酸亚乙酯(EC),所述线性酯包含碳酸二甲酯(DMC)和碳酸甲乙酯(EMC)。
在一些实施方式中,所述添加剂包含碳酸酯(例如碳酸氟代亚乙酯FEC)、硫酸酯(例如硫酸乙烯酯DTD)和磺酸酯(例如1,3-丙烷磺酸内酯PS)。所述碳酸酯包括碳酸氟代亚乙酯(FEC)、碳酸亚乙烯酯(VC)、碳酸1,2-二氟亚乙酯、碳酸1,1-二氟亚乙酯、碳酸1,1,2-三氟亚乙酯、碳酸1,1,2,2-四氟亚乙酯、碳酸1-氟-2-甲基亚乙酯、碳酸1-氟-1-甲基亚乙酯、碳酸1,2-二氟-1-甲基亚乙酯、碳酸1,1,2-三氟-2-甲基亚乙酯或碳酸三氟甲基亚乙酯中的至少一种。所述硫酸酯包括硫酸乙烯酯(DTD)、硫酸二乙酯(DES)、硫酸二甲酯(DMS)和4,4-双(1,3,2-二氧杂硫杂环戊烷)-2,2,2,2-四氧化物中的至少一种。所述磺酸酯包括1,3-丙烷磺酸内酯(1,3-PS)、丙烯磺酸内酯(PES)、3-氟-1,3-丙磺酸内酯(FPS)、甲烷二磺酸乙烯酯(MMDS)中的至少一种。
在一些优选的实施方式中,所述添加剂包含碳酸氟代亚乙酯(FEC)、硫酸乙烯酯(DTD)和1,3-丙烷磺酸内酯(1,3-PS)。
在一些优选的实施方式中,所述添加剂含量占电解液总质量的质量百分含量为0-7%。
在一些实施方式中,所述电解液还可选地包括其他添加剂。例如其他添加剂可以包括负极成膜添加剂、正极成膜添加剂,还可以包括能够改善电池某些性能的添加剂,例如改善电池过充性能的添加剂、改善电池高温或低温性能的添加剂等。
隔离膜
在一些实施方式中,二次电池中还包括隔离膜。本申请对隔离膜的种类没有特别的限制,可以选用任意公知的具有良好的化学稳定性和机械稳定性的多孔结构隔离膜。
在一些实施方式中,隔离膜的材质可选自玻璃纤维、无纺布、聚乙烯、聚丙烯及聚偏二氟乙烯中的至少一种。隔离膜可以是单层薄膜,也可以是多层复合薄膜,没有特别限制。在隔离膜为多层复合薄膜时,各层的材料可以相同或不同,没有特别限制。
在一些实施方式中,所述隔离膜的厚度为4-40μm,可选为12-20μm。
在一些实施方式中,正极极片、负极极片和隔离膜可通过卷绕工艺或叠片工艺制成电极组件。
在一些实施方式中,二次电池可包括外包装。该外包装可用于封装上述电极组件及电解质。
在一些实施方式中,二次电池的外包装可以是硬壳,例如硬塑料壳、铝壳、钢壳等。二次电池的外包装也可以是软包,例如袋式软包。软包的材质可以是塑料,作为塑料,可列举出聚丙烯、聚对苯二甲酸丁二醇酯以及聚丁二酸丁二醇酯等。
本申请对二次电池的形状没有特别的限制,其可以是圆柱形、方形或其他任意的形状。例如,图1是作为一个示例的方形结构的二次电池5。
在一些实施方式中,参照图2,外包装可包括壳体51和盖板53。其中,壳体51可包括底板和连接于底板上的侧板,底板和侧板围合形成容纳腔。壳体51具有与容纳腔连通的开口,盖板53能够盖设于所述开口,以封闭所述容纳腔。正极极片、负极极片和隔离膜可经卷绕工艺或叠片工艺形成电极组件52。电极组件52封装于所述容纳腔内。电解液浸润于电极组件52中。二次电池5所含电极组件52的数量可以为一个或多个,本领域技术人员可根据具体实际需求进行选择。
在一些实施方式中,二次电池可以组装成电池模块,电池模块所含二次电池的数量可以为一个或多个,具体数量本领域技术人员可根据电池模块的应用和容量进行选择。
在电池模块中,多个二次电池5可以是沿电池模块的长度方向依次排列设置。当然,也可以按照其他任意的方式进行排布。进一步可以通过紧固件将该多个二次电池5进行固定。
可选地,电池模块还可以包括具有容纳空间的外壳,多个二次电池5容纳于该容纳空间。
在一些实施方式中,上述电池模块还可以组装成电池包,电池包所含电池模块的数量可以为一个或多个,具体数量本领域技术人员可根据电池包的应用和容量进行选择。
在电池包中可以包括电池箱和设置于电池箱中的多个电池模块。电池箱包括上箱体和下箱体,上箱体能够盖设于下箱体,并形成用于容纳电池模块的封闭空间。多个电池模块可以按照任意的方式排布于电池箱中。
另外,本申请还提供一种用电装置,所述用电装置包括本申请提供的二次电池、电池模块、或电池包中的至少一种。所述二次电池、电池模块、或电池包可以用作所述用电装置的电源,也可以用作所述用电装置的能量存储单元。所述用电装置可以包括移动设备(例如手机、笔记本电脑等)、电动车辆(例如纯电动车、混合动力电动车、插电式混合动力电动车、电动自行车、电动踏板车、电动高尔夫球车、电动卡车等)、电气列车、船舶及卫星、储能系统等,但不限于此。
作为所述用电装置,可以根据其使用需求来选择二次电池、电池模块或电池包。
图3是作为一个示例的用电装置。该用电装置为纯电动车、混合动力电动车、或插电式混合动力电动车等。为了满足该用电装置对二次电池的高功率和高能量密度的需求,可以采用电池包或电池模块。
作为另一个示例的装置可以是手机、平板电脑、笔记本电脑等。该装置通常要求轻薄化,可以采用二次电池作为电源。
实施例
为了使本申请所解决的技术问题、技术方案及有益效果更加清楚,以下将结合实施例和附图对本申请进行进一步详细说明。显然,所描述的实施例仅仅是本申请一部分实施例,而不是全部的实施例。以下对至少一个示例性实施例的描述实际上仅仅是说明性的,决不作为对本申请及其应用的任何限制。基于本申请中的实施例,本领域普通技术人员在没有付出创造性劳动前提下所获得的所有其他实施例都属于本申请保护的范围。
实施例中未注明具体技术或条件的,按照本领域内的文献所描述的技术或条件或者按照产品说明书进行。所用试剂或仪器未注明生产厂商者,均为可以通过市购获得的常规产品。
一、实施例
实施例1
1、电解液的制备:
电解液的制备在含水量<10ppm的氩气气氛手套箱中进行,首先将碳酸亚乙酯(EC)、碳酸甲乙酯(EMC)和碳酸二乙酯(DEC)按照3:5:2的质量比例进行混合,然后加入1mol/L的主锂盐LiPF6,占电解液整体的1wt%的副锂盐LiBF4+LiDFOB,占电解液整体的4wt%的添加剂FEC+DTD+1,3-PS,混合均匀,获得电解液。电解液的粘度为3.8mPa.s。
2、正极极片的制备:
将正极活性材料三元材料LiNi0.65Co0.07Mn0.28O2、粘结剂聚偏氟乙烯、导电剂乙炔黑按照重量比98:1:1的比例进行混合溶于溶剂N-甲基吡咯烷酮(NMP)中制成正极浆料,然后将浆料涂布在集流体铝箔上,干燥后进行冷压、切边、裁片、分条等,制成尺寸为87*665mm的正极极片,备用。
3、负极极片的制备:
将负极活性材料石墨、SiO2、粘结剂丁苯橡胶和分散剂羧甲基纤维素钠按重量比96.5:1.5:1:1的比例溶于去离子水中,形成第一负极浆料。采用6um铜箔作为负极集流体,先将第一层负极浆料涂覆于负极集流体上,涂布重量为4.25mg/cm2,形成第一活性材料层。待第一活性材料层干燥后再涂覆第二负极浆料,将负极活性材料石墨、SiO2、粘结剂丁苯橡胶和分散剂羧甲基纤维素钠按重量比96.5:1.5:1:1的比例溶于去离子水中,形成第二负极浆料;第二活性材料层涂覆重量为4.25mg/cm2,形成第二活性材料层。
再先后经过干燥、冷压、裁切得到复合负极极片,冷压后,涂覆于铜箔一个表面上的复合活性材料层厚度为51um,活性材料层压实密度为1.65g/cm3。制成尺寸为93*691mm的负极极片,备用
4、隔离膜
隔离膜基材为8μm厚的聚乙烯(PE),在隔离膜基材的两侧各涂覆2μm氧化铝陶瓷层,最后在涂布了陶瓷层的两侧各涂覆2.5mg的粘结剂聚偏二氟乙烯(PVDF),烘干。
5、组装成电池:
将上述的正极极片、隔离膜、负极极片按顺序卷绕或叠好,使隔离膜处于正负极极片中间,得到裸电芯,将裸电芯置于外包装中,将9.3g的上述制备的电解液注入到干燥后的电芯中,经过静置、化成、整形等工序,获得容量为3100mAh的锂离子二次电池。
实施例2-26和对比例1-3的制备步骤与实施例1类似,但是改变电解液或负极的材料或组成,参见表1。
参数测试
负极活性材料层的孔隙率P%测试
负极活性材料层的孔隙率P%可以如下进行测量:利用小分子直径的惰性气体如氦气或氮气,通过置换法精确测量得到待测样品的真实体积,并且结合玻尔定律(PV=nRT)得到待测样品的孔隙率。孔隙率P=(V11-V12)/V11×100%,其中V11表示负极活性材料层的表观体积,V12表示负极活性材料层的真实体积。
电解液的粘度测试
在一定温度下,转子在样品中以恒定转速持续旋转时受到的剪切力使弹簧产生扭矩,扭矩与粘度成正比,由此得到粘度值。
具体地,采用博勒飞(DV-2TLV)粘度计对成品电解液的粘度进行测试。控制环境温度为25℃,环境湿度<80%,取30mL的电解液,将其恒温在25℃的水浴锅中至少30min,将转子装入样品杯,加入样品至离杯口约0.3cm处,启动连接着的粘度计,选择70RPM的转速进行测试,采集10个数据点,求取多点平均值。
表1各实施例和对比例的相关参数
二、电池性能测试
1、正极可脱锂容量
在PRS340/11-119-11布劳恩手套箱中拆解电池,取正极极片,组装成正极-锂片的CR2430型号半扣式电池,采用的正极极片面积为a mm2,其中电解液采用1M LiPF6于EC/EMC/DEC=3/5/2中的溶液;然后将组装好的半扣式电池静置3h,测试在25℃下进行,采用0.1C先在电压区间2.5-eV下进行充电(Charge)脱锂,其中e为电芯设计的使用上限电压,再采用0.05C放电(Discharge)嵌锂至2.5V,循环2次,取第二次循环的放电扣电容量记为YmAh,实际电池设计的正极膜片长为b mm,宽为c mm,正极活性材料涂覆于正极集流体的面数d,则正极脱锂容量为X=Y/a*b*c*d。
2、负极可嵌锂容量
在PRS340/11-119-11布劳恩手套箱中拆解电池,取负极极片,组装成负极-锂片的CR2430型号半扣式电池,采用的负极极片面积为f mm2,其中电解液采用1M LiPF6于EC/EMC/DEC=3/5/2中的溶液;然后将组装好的半扣式电池静置3h,测试在25℃下进行,采用0.1C先在电压区间2V-0V下进行放电(Discharge)嵌锂,再采用0.05C充电(Discharge)脱锂至2V,循环2次,取第二次循环的放电扣电容量记为ZmAh,实际电池设计的负极膜片长为hmm,宽为i mm,负极活性材料涂覆于负极集流体的面数d,则负极可嵌锂容量=Z/f*h*i*d。
3、充电能力测试
倍率性能测试(充电至70%SOC的测试):调节测试温度至35℃,对锂离子电池进行xC倍率(x为0.5、0.8、1、1.2、1.5、2、2.5、3)下的充电,然后在1C下放电,充电倍率依次增高,以阳极电位0V为充电截止条件,模拟获得0-10%SOC、10-20%SOC、20-30%SOC、30-40%SOC、40-50%SOC、50-60%SOC、60-70%SOC区间内能够实现的最大充电倍率,从而计算出0~70%SOC所需的充电时间(min)。
4、循环性能测试
在25℃下,将二次电池以1C恒流充电至4.3V,继续恒压充电至电流为0.05C,此时二次电池为满充状态,记录此时的充电容量,即为第1圈充电容量;将二次电池静置5min后,以1C恒流放电至2.8V,此为一个循环充放电过程,记录此时的放电容量,即为第1圈放电容量。将二次电池按照上述方法进行循环充放电测试,记录每圈循环后的放电容量。二次电池45℃循环600圈容量保持率(%)=600圈循环后的放电容量/第1圈放电容量×100%。
三、各实施例、对比例测试结果
按照上述方法分别制备各实施例和对比例的电池,并测量各项性能参数,结果见下表2。
表2各实施例和对比例的电池性能
通过上述实施例和对比例可得知,本申请的锂离子电池在电解液粘度在1-6mPa.s范围内,CB值为1.1-1.5的情况下,甚至负极活性材料的孔隙率在25-40%的范围内的情况下,其具有良好的快充能力以及容量保持率,例如0-80%SOC所需的充电时间可缩短至6分钟,循环600圈后容量保持率仍保持在95%以上(参见实施例12)。
需要说明的是,本申请不限定于上述实施方式。上述实施方式仅为示例,在本申请的技术方案范围内具有与技术思想实质相同的构成、发挥相同作用效果的实施方式均包含在本申请的技术范围内。此外,在不脱离本申请主旨的范围内,对实施方式施加本领域技术人员能够想到的各种变形、将实施方式中的一部分构成要素加以组合而构筑的其它方式也包含在本申请的范围内。
Claims (16)
1.一种锂离子电池,其包含正极、负极和电解液,其中,所述电解液在25℃下的粘度c为1-6mPa.s;并且负极可嵌锂容量与正极可脱锂容量的比值CB为1.05-1.5。
2.根据权利要求1所述的电池,其特征在于,所述电池在35℃下自0%荷电状态到70%荷电状态的充电过程中存在大于等于4倍的单位时间内正极可脱嵌容量的电流。
3.根据权利要求1或2所述的电池,其特征在于,所述电池在35℃下自0%荷电状态到70%荷电状态的充电过程中的平均电流大于等于4倍的单位时间内正极可脱嵌容量。
4.根据权利要求1-3中任一项所述的电池,其特征在于,所述负极包含集流体及附着在集流体至少一个表面上的负极活性材料层,其中所述活性材料层包括包含第一负极活性材料的第一活性材料层,以及附着在所述第一活性材料层远离所述集流体的表面上的包含第二负极活性材料的第二活性材料层。
5.根据权利要求4所述的电池,其特征在于,所述第一负极活性材料的平均体积粒径Dv50大于第二负极活性材料的平均体积粒径Dv50。
6.根据权利要求4或5所述的电池,其特征在于,所述第一负极活性材料层的压实密度大于第二负极活性材料层的压实密度。
7.根据权利要求4-6中任一项所述的电池,其特征在于,所述负极活性材料层的厚度为30-150μm,孔隙率为20-60%,压实密度为1.2-1.9g/cm3。
8.根据权利要求1-7中任一项所述的电池,其特征在于,所述电解液包含锂盐、溶剂和添加剂;其中所述锂盐包含主锂盐和副锂盐。
9.根据权利要求8所述的电池,其特征在于,所述主锂盐与副锂盐不同,并且所述主锂盐或副锂盐各自独立地选自LiPF6、LiN(SO2F)2、LiBF4、LiN(CF3SO2)2、LiClO4、LiAsF6、LiB(C2O4)2、LiBF2C2O4、LiDFOP、LiPO2F2、LiFSO3、LiF中的至少一种。
10.根据权利要求8或9所述的电池,其特征在于,所述主锂盐为六氟磷酸锂或LiFSI,其含量为8-20wt%,基于所述电解液的总重量计;所述副锂盐为二氟草酸硼酸锂、LiBF4、LiB(C2O4)2、二氟二草酸磷酸锂(LiDFOP)中的至少一种,其含量为0.001wt%-2wt%,基于所述电解液的总重量计。
11.根据权利要求8-10中任一项所述的电池,其特征在于,所述溶剂包含环状酯和线性酯;所述环状酯的含量占溶剂质量的5-40%,所述线性酯的含量占溶剂质量的60-95%。
12.根据权利要求11所述的电池,其特征在于,所述环状酯为碳酸亚乙酯、碳酸亚丙基酯或其组合;所述线性酯包含碳酸二甲酯。
13.根据权利要求12所述的电池,其特征在于,所述线性酯选自碳酸二乙酯、碳酸甲乙酯、甲酸甲酯、乙酸甲酯、乙酸乙酯、乙酸丁酯、丙酸甲酯、丁酸甲酯、丁酸乙酯、丁酸丙酯、丁酸丁酯、乙酸异丙酯、乙酸异戊酯和其组合。
14.根据权利要求8-13中任一项所述的电池,其特征在于,在所述电解液中,锂盐摩尔浓度b(mol/L)、溶剂中线性酯占溶剂质量的百分比a%与电解液在25℃下的粘度c满足以下关系式:
2≤c+2*a%≤8;
2≤c+b≤8。
15.根据权利要求1-14中任一项所述的电池,其特征在于,所述正极包含集流体及附着在集流体至少一个表面上的包含正极活性材料的正极活性材料层,所述正极活性材料包含式LiNixCoyQzM1-x-y-zO2的三元材料,其中Q为Mn或Al,M包含Co、Ni、Mn、Mg、Cu、Zn、Al、Sn、B、Ga、Cr、Sr、V和Ti中至少一种,0≤x<1,0≤y≤1,0≤z≤1,x+y+z≤1。
16.一种用电装置,其特征在于,包括选自权利要求1-15中任一项所述的二次电池。