CN116730703A - Water-based solvent type permeable crystalline waterproof and anticorrosive material for concrete - Google Patents
Water-based solvent type permeable crystalline waterproof and anticorrosive material for concrete Download PDFInfo
- Publication number
- CN116730703A CN116730703A CN202310733251.XA CN202310733251A CN116730703A CN 116730703 A CN116730703 A CN 116730703A CN 202310733251 A CN202310733251 A CN 202310733251A CN 116730703 A CN116730703 A CN 116730703A
- Authority
- CN
- China
- Prior art keywords
- concrete
- water
- waterproof
- anticorrosive
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to the technical field of waterproof and anticorrosive materials, and provides a concrete water-based solvent type permeable crystallization waterproof and anticorrosive material, which comprises the following components in parts by weight: 8-12% of silicone, 20-30% of sodium silicate, 8-15% of silane, 2-4% of silica fume, 4-7% of magnesium fluosilicate, 2-4% of surfactant, 1-2% of propylene glycol, 0.1-0.5% of chelating and dispersing agent and 2-6% of protective agent; the material provided by the invention can quickly permeate into the concrete to form a hydrophobic net-shaped protective layer, so that the compressive strength of the concrete is increased, the corrosion resistance of the concrete is increased, the service life of the concrete is prolonged, silicate ions in the material are chemically reacted with calcium ions in the concrete along with the diffusion of surface water in the concrete to generate water-insoluble calcium silicate hydrate, the crystals are filled in concrete pores and are combined with the concrete to form a whole, the material has catalytic properties, once the material is subjected to the chemical reaction continuously, crystals are generated, and the waterproof effect of the material can be theoretically the same as the service life of a building.
Description
Technical Field
The invention belongs to the technical field of waterproof and anticorrosive materials, and particularly relates to a water-based solvent type permeable crystallization waterproof and anticorrosive material for concrete.
Background
The concrete refers to a general term of engineering composite materials which are formed by cementing aggregates into a whole by cementing materials, the term of concrete refers to cement which is used as cementing materials, sand and stone which are used as aggregates and water (which can contain additives and admixtures) are matched according to a certain proportion, and the cement concrete obtained by stirring is also called ordinary concrete, and is widely applied to civil engineering;
the existing building is a main body of a concrete structure, the concrete is easily influenced by multiple factors such as aggregate particle size, aggregate self activity, strength, impurities and additives in different areas, including stirring machinery, transportation time and the like, in the construction process, the existing building is also influenced by vibration time, parts and the like, structural compactness is caused, later environmental temperature control differences are likely to cause cracks, finally, soil property differences in all areas can influence the service life of the main body of the later structure, at present, sodium silicate and other potassium methyl silicate waterproofing agents have certain defects, firstly, the main body is sodium silicate potassium silicate permeable waterproofing agents have crack resistance to the concrete, the surface protection effect is lower, secondly, the surface hydrophobic potassium methyl silicate has short service life and is easy to volatilize, other waterproof protection layers are mostly film coating products, the film coating products are easily influenced by construction factors, constructors have uneven technical level, the thickness of a coating, the constructors can directly influence the structural waterproofing and the service life of the base layer.
Therefore, a concrete water-based solvent-type penetrating crystallization waterproof and anticorrosive material is proposed by the person skilled in the art to solve the problems proposed by the background art.
Disclosure of Invention
In order to solve the technical problems, the invention provides a water-based solvent type permeable crystalline waterproof and anticorrosive material for concrete, which solves the problems in the prior art.
The water-based solvent type permeable crystallization waterproof and anticorrosive material for the concrete comprises the following components in parts by weight: 8-12% of silicone, 20-30% of sodium silicate, 8-15% of silane, 2-4% of silica fume, 4-7% of magnesium fluosilicate, 2-4% of surfactant, 1-2% of propylene glycol, 0.1-0.5% of chelating and dispersing agent, 2-6% of protective agent, 0.5-0.8% of defoaming agent, 0.02-0.05% of early strength agent, 0.3-0.8% of antiseptic bactericide and the balance of water, wherein the protective agent is wetting dispersing agent;
the preparation method of the water-based solvent type osmotic crystallization waterproof and anticorrosive material for concrete comprises the following steps:
s1, adding water into a reaction kettle;
s2, sequentially adding a defoaming agent, an antiseptic bactericide, an early strength agent, 2% -4% of a surfactant, and stirring to prepare a mixed solution by chelating each dispersing agent, silica fume, propylene glycol, a wetting dispersing agent, magnesium fluosilicate, silicone and silane;
s3, adding sodium silicate into the mixed solution, and fully mixing and stirring in a reaction kettle;
s4, filtering and canning the stirred material.
Preferably, the silicone is siloxane, and the silicone has the advantages of excellent water resistance, moisture resistance, seepage resistance, ageing resistance, pollution resistance and the like, and prevents moisture from penetrating into a substrate, so that exfoliation caused by freeze thawing and weathering is reduced, the service life of the substrate is prolonged, and meanwhile, a layer of insoluble waterproof high polymer compound with a thickness of a few molecules can be formed on the surface and the inside of a structure by the material.
Preferably, the sodium silicate is a sodium silicate solution with the mass fraction of 40-45, and the sodium silicate solution has the function of being capable of generating chemical reaction with free calcium ions in the concrete to generate insoluble crystals and filling cracks and gaps in the concrete, so that the compactness and the waterproofness of the concrete are improved.
Preferably, the silane is 90% isobutyl triethoxysilane, which has a small molecular structure and can penetrate through the cementitious surface, penetrate into the interior of the concrete to chemically react with air exposed in the acid-alkali environment and water molecules of the substrate to form a permanent firm high-environmental protection waterproof layer, so that corrosion, loosening, stripping and mildewing of the concrete and the internal steel bar structure caused by corrosion of the substrate due to water seepage, sunlight, acid rain and acid-alkali environment can be effectively prevented, and the service life of the concrete is prolonged.
Preferably, the magnesium fluosilicate is magnesium fluosilicate solution, has the function of inhibiting concrete from being cracked, has a certain cracking resistance, and can be used as an antifreeze for concrete surface treatment.
The surfactant is sodium dodecyl sulfonate, and has the main effects of reducing the surface tension of an interface and promoting the permeation of materials.
Preferably, the propylene glycol is industrial-grade propylene glycol, so that the permeability and freezing resistance of the material can be effectively improved.
Preferably, the early strength agent is triethanolamine, so that the early concrete strength and the impermeability can be improved.
Preferably, the water is deionized water, and the resistivity of the ionized water is more than or equal to 10MΩ. cm.
Compared with the prior art, the invention has the following beneficial effects:
1. the invention provides a permeable crystallization type concrete solvent waterproof material capable of efficiently protecting a concrete surface layer, which comprises the following steps that firstly, the material has a very small molecular structure, can rapidly permeate into the concrete, a protective network is formed in the permeated range, a first hydrophobic net-shaped protective layer is formed, the compressive strength of the concrete can be effectively increased, the corrosion resistance of the concrete is increased, the service life of the concrete is effectively prolonged, and secondly, silicate ions in the material react with calcium ions in the concrete along with the diffusion of surface water in the concrete to generate water-insoluble calcium silicate hydrate, crystals are filled in concrete pores and are combined with the concrete to form a whole, so that the material has catalytic characteristics, once meeting water, chemical reaction can be continuously generated, and the waterproof effect of the material can be theoretically the same as the service life of a building.
Drawings
FIG. 1 is a flow chart of the material fabrication of the present invention;
FIG. 2 is a diagram of the inspection standard of the present invention;
FIG. 3 is a graph showing the detection results of the present invention.
Detailed Description
Embodiments of the present invention are described in further detail below with reference to the accompanying drawings and examples. The following examples are illustrative of the invention but are not intended to limit the scope of the invention.
As shown in fig. 1:
embodiment one: the invention provides a concrete water-based solvent type penetrating crystallization waterproof and anticorrosive material, which comprises the following components in parts by weight: 8-12% of silicone, 20-30% of sodium silicate, 8-15% of silane, 2-4% of silica fume, 4-7% of magnesium fluosilicate, 2-4% of surfactant, 1-2% of propylene glycol, 0.1-0.5% of chelating and dispersing agent, 2-6% of protective agent, 0.5-0.8% of defoamer, 0.02-0.05% of early strength agent, 0.3-0.8% of antiseptic and bactericide, and the balance of water;
the preparation method of the water-based solvent type osmotic crystallization waterproof and anticorrosive material for concrete comprises the following steps:
s1, adding water into a reaction kettle;
s2, sequentially adding a defoaming agent, an antiseptic bactericide, an early strength agent, 2% -4% of a surfactant, and stirring to prepare a mixed solution by chelating each dispersing agent, silica fume, propylene glycol, a wetting dispersing agent, magnesium fluosilicate, silicone and silane;
s3, adding sodium silicate into the mixed solution, and fully mixing and stirring in a reaction kettle;
s4, filtering and canning the stirred material.
Furthermore, the silicone is siloxane, and has the advantages of excellent water resistance, moisture resistance, seepage resistance, ageing resistance, pollution resistance and the like, and moisture penetration into a substrate is avoided.
Further, the sodium silicate is a sodium silicate solution with the mass fraction of 40-45, and the sodium silicate solution is used for generating chemical reaction with free calcium ions in the concrete to generate insoluble crystals so as to fill cracks and gaps in the concrete.
Furthermore, the silane is 90% isobutyl triethoxysilane, has a small molecular structure and can penetrate through the cementitious surface, penetrate into the concrete, and chemically react with air exposed in the acid-base environment and water molecules of the substrate to form a permanent, firm and high-environmental-protection waterproof layer.
Furthermore, the magnesium fluosilicate is magnesium fluosilicate solution, has the function of inhibiting concrete from being cracked, has a certain anti-cracking function, and can be used as an antifreeze for concrete surface treatment.
Furthermore, the propylene glycol is industrial-grade propylene glycol, so that the permeability and freezing resistance of the material can be effectively improved.
Furthermore, the early strength agent adopts triethanolamine, so that the early concrete strength and the impermeability can be improved.
Further, the water is deionized water, and the resistivity of the ionized water is more than or equal to 10MΩ. cm.
From the above, when the anticorrosive material is prepared, water is firstly added into a reaction kettle, the weight portion of the water is 19.35%, then defoaming agent 0.5%, antiseptic bactericide 0.3%, early strength agent 0.02%, surfactant 2%, chelating dispersing agents 0.1%, silica fume 2%, propylene glycol 1%, wetting dispersing agent 2%, magnesium fluosilicate 4%, silicone 20% and silane 8% are added into the water, and stirring is carried out to prepare a mixed solution, wherein the defoaming agent is used for eliminating foam in the stirring process of the material, the antiseptic bactericide has the effect of ensuring the storage life of the material, and the early strength and the impermeability can be effectively improved by adopting triethanolamine as the early strength agent.
Furthermore, the surfactant can obviously reduce the water absorption capacity of the substrate, has certain hydrophobic, hydrophobic and waterproof properties, can enable the surface of the coating to be smoother, reduces the water absorption and cracking properties of the coating, and the chelating and dispersing agent has adsorption complexing effect on metal ions, so that the water quality can be obviously softened in the material.
Furthermore, silica fume contains a large amount of amorphous spherical particles SiO2, the particles are extremely fine and have high activity, and the reinforcing effect is shown in the following way when the silica fume is doped into cement concrete: evenly distributed in the hydration product, has good micro-filling effect, and compacts the concrete; the method is particularly beneficial to the early and middle strength development of the concrete, reduces free Ca (OH) 2 in the concrete, reduces the size of original flaky crystals, improves the dispersity in the concrete and obviously improves the interface structure in the concrete. These characteristics result in a significant increase in the strength and durability of the concrete.
Further the surfactant is sodium dodecyl sulfonate, and the main function is to reduce the surface tension of the interface. Promoting material penetration. Can also play a certain role in dispersing to prevent the agglomeration of sodium silicate colloid particles.
Furthermore, the propylene glycol is industrial propylene glycol, so that the permeability and freezing resistance of the material can be effectively improved, the wetting dispersant mainly acts to reduce the surface tension of an interface and promote the material permeation, in addition, in the preparation process, the material can also have a good dispersing effect to prevent material molecules from agglomerating, and the magnesium fluosilicate adopts magnesium fluosilicate solution, so that the magnesium fluosilicate solution acts to inhibit concrete from cracking, plays a certain anti-cracking role and can be used as an antifreeze for concrete surface treatment.
Furthermore, the silicone is siloxane, and the silicone has the advantages of excellent water resistance, moisture resistance, seepage resistance, ageing resistance, pollution resistance and the like, and prevents moisture from penetrating the substrate, so that the peeling caused by freeze thawing and weathering is reduced, the service life of the substrate is prolonged, and the material can be used for generating a layer of insoluble waterproof high polymer compound with a thickness of a few molecules on the surface and in the structure.
Furthermore, the silane is 90% isobutyl triethoxysilane, has a small molecular structure and can penetrate through the cementitious surface, and the silane is permeated into the concrete to chemically react with air exposed in the acid-alkali environment and water molecules of the substrate to form a permanent firm high-environment-friendly waterproof layer, so that corrosion, loosening, stripping and mildew of the concrete and the internal reinforcing steel structure caused by corrosion of the substrate due to water seepage, sunlight, acid rain and acid-alkali environment can be effectively prevented, and the service life of the concrete is prolonged.
Further, adding sodium silicate into the mixed solution, and stirring again in a reaction kettle, wherein the sodium silicate is 40-45 mass percent sodium silicate solution, and the sodium silicate is used for generating chemical reaction with free calcium ions in the concrete to generate insoluble crystals and filling cracks and gaps in the concrete, so that the compactness and the water resistance of the concrete are improved.
Further, the stirred material was filtered and canned.
Through the operation, the invention provides the permeable crystallization type concrete solvent waterproof material capable of efficiently protecting the concrete surface layer, firstly, the material has a small molecular structure, can rapidly permeate into the concrete, a protective network is formed in the permeated range, a first hydrophobic net-shaped protective layer is formed, the compressive strength of the concrete can be effectively increased, the corrosion resistance of the concrete is increased, the service life of the concrete is effectively prolonged, silicate ions in the material react with calcium ions in the concrete along with the diffusion of surface water in the concrete, calcium silicate hydrate which is insoluble in water is generated, crystals are filled in concrete pores and are combined with the concrete to form a whole, the material has catalytic characteristics, once the crystals are generated continuously, and the waterproof effect of the material can be theoretically the same as the service life of a building.
Embodiment two: the embodiment is different from the first embodiment, the water-based solvent-based penetrating crystalline waterproof and anti-corrosion material prepared by the invention is sprayed in a concrete test block with the thickness of 100 multiplied by 150 multiplied by 100mm, and the main performances of the water-based solvent-based penetrating crystalline waterproof and anti-corrosion material are tested according to JC/T474-2008 (mortar concrete waterproof agent) and JC/T1018-2020 (water-based inorganic waterproof agent) and GB 1845-2012 (cement-based penetrating crystalline waterproof material), as shown in fig. 2 and 3, the freezing resistance, alkali resistance, heat resistance and compressive strength of the water-based penetrating crystalline waterproof and anti-corrosion material prepared by the invention are improved, the service life of the water-based penetrating crystalline waterproof and anti-corrosion material is prolonged, the material penetrating height can reach 33mm, and the waterproof and anti-corrosion effect is obvious.
While embodiments of the present invention have been shown and described above for purposes of illustration and description, it will be understood that the above embodiments are illustrative and not to be construed as limiting the invention, and that variations, modifications, alternatives, and variations may be made to the above embodiments by one of ordinary skill in the art within the scope of the invention.
Claims (9)
1. A concrete water-based solvent type penetrating crystallization waterproof and anticorrosive material is characterized in that: the coating comprises the following components in parts by weight: 8-12% of silicone, 20-30% of sodium silicate, 8-15% of silane, 2-4% of silica fume, 4-7% of magnesium fluosilicate, 2-4% of surfactant, 1-2% of propylene glycol, 0.1-0.5% of chelating and dispersing agent, 2-6% of protective agent, 0.5-0.8% of defoamer, 0.02-0.05% of early strength agent, 0.3-0.8% of antiseptic and bactericide, and the balance of water;
the preparation method of the water-based solvent type osmotic crystallization waterproof and anticorrosive material for concrete comprises the following steps:
s1, adding water into a reaction kettle;
s2, sequentially adding a defoaming agent, an antiseptic bactericide, an early strength agent, 2% -4% of a surfactant, and stirring to prepare a mixed solution by chelating each dispersing agent, silica fume, propylene glycol, a wetting dispersing agent, magnesium fluosilicate, silicone and silane;
s3, adding sodium silicate into the mixed solution, and fully mixing and stirring in a reaction kettle;
s4, filtering and canning the stirred material.
2. The aqueous solvent-based permeable crystalline waterproof and anticorrosive concrete material according to claim 1, wherein: the silicone is siloxane, and has the advantages of excellent water resistance, moisture resistance, seepage resistance, ageing resistance, pollution resistance and the like, and moisture permeation into a substrate is reduced as much as possible.
3. The aqueous solvent-based permeable crystalline waterproof and anticorrosive concrete material according to claim 1, wherein: the sodium silicate is a sodium silicate solution with the mass fraction of 40-45, and the sodium silicate solution is used for generating chemical reaction with free calcium ions in concrete to generate insoluble crystals and filling cracks and gaps in the concrete.
4. The aqueous solvent-based permeable crystalline waterproof and anticorrosive concrete material according to claim 1, wherein: the silane is 90% isobutyl triethoxysilane, has a small molecular structure and can penetrate through the cementitious surface, penetrate into the concrete, and chemically react with air exposed in the acid-base environment and water molecules of the substrate to form a permanent firm high-environmental protection waterproof layer.
5. The aqueous solvent-based permeable crystalline waterproof and anticorrosive concrete material according to claim 1, wherein: the magnesium fluosilicate is magnesium fluosilicate solution, has the function of inhibiting concrete from being cracked, has a certain anti-cracking function, and can be used as an antifreeze for concrete surface treatment.
6. A concrete aqueous solvent type penetrating crystallization waterproof and anticorrosive material according to claim 1, wherein: the surfactant is sodium dodecyl sulfonate, and has the main effects of reducing the surface tension of an interface and promoting the permeation of materials.
7. The aqueous solvent-based permeable crystalline waterproof and anticorrosive concrete material according to claim 1, wherein: the propylene glycol is industrial-grade propylene glycol, and can effectively increase the permeability and freezing resistance of the material.
8. The aqueous solvent-based permeable crystalline waterproof and anticorrosive concrete material according to claim 1, wherein: the early strength agent adopts triethanolamine, and can improve the strength and impermeability of early concrete.
9. The aqueous solvent-based permeable crystalline waterproof and anticorrosive concrete material according to claim 1, wherein: the water is deionized water, and the resistivity of the ionized water is more than or equal to 10MΩ & cm.