CN1161281C - Adsorbing straw material for treating effluent containing heavy metal ions and its prpen - Google Patents
Adsorbing straw material for treating effluent containing heavy metal ions and its prpen Download PDFInfo
- Publication number
- CN1161281C CN1161281C CNB00130187XA CN00130187A CN1161281C CN 1161281 C CN1161281 C CN 1161281C CN B00130187X A CNB00130187X A CN B00130187XA CN 00130187 A CN00130187 A CN 00130187A CN 1161281 C CN1161281 C CN 1161281C
- Authority
- CN
- China
- Prior art keywords
- stalk
- steam
- heavy metal
- steam puffed
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a straw adsorbing material for treating effluent containing heavy metal ions, which is made of steam exploding straws treated by steam explosion, as well as steam exploding straws soaked and modified by ZnCl2 solution or FeCl3 solution. Each kilo of the steam exploding straws comprises 4 to 8g of ZnCl2 or 6 to 10g of FeCl3. The preparation method of the straw adsorbing material comprises: the straw material is treated by the steam explosion; the steam exploding straws after being treated by the steam explosion can also be modified by soaking the steam exploding straws in the ZnCl2 solution or the FeCl3 solution. The straw adsorbing material has the advantages of large specific surface area, strong adsorbing capability, abundant raw material, low price, simple preparation method and easy operation, and largely reduces the cost of treating effluent containing heavy metal ions.
Description
Invention field
The invention belongs to environment-friendly novel Products Development and Application Areas, relate to the sorbing material and the preparation method that are used to handle effluent containing heavy metal ions, particularly a kind of stalk sorbing material and preparation method who is used to handle effluent containing heavy metal ions.
Background technology
At present, the method of utilizing absorption principle that effluent containing heavy metal ions and high concentrated organic wastewater are handled is comparatively general, is a kind of sorbent material commonly used such as gac in handling effluent containing heavy metal ions, but the Activated Carbon Production cost is higher, can cause that cost for wastewater treatment is huge to be increased, domestic enterprise's waste water treatment expense often substantially exceeds domestic environmental fines expense, and domestic enterprise generally is difficult to bear, and feasible application with this method of activated carbon treatment effluent containing heavy metal ions is very limited.Though, use Testa arachidis hypogaeae [Shukla SR was also arranged in recent years, Sakhardane, V D, J.Appl.Polym.Sci. (polymer application science), 1991,41:829-835], corn cob [Odozi T O, Agriculture Wastes (agricultural wastes), 1985,12:13-21], modified wood [Wang Gehui, Song Zhanqian, chemistry of forest product and industry, 1999,19 (3): 79-87] relevant report that etc. is used for the processing of heavy metal wastewater thereby as sorbent material, but make aforesaid method unsatisfactory because of its processing process is complicated eventually, thereby be difficult to promote.
Summary of the invention
The object of the invention is: overcome the cost height that the sorbing material that is used to handle effluent containing heavy metal ions in the prior art exists, shortcomings such as processed complex, and provide a kind of stalk sorbing material and preparation method who is used to handle effluent containing heavy metal ions, promptly select cheap stalk for use, it is carried out steam explosion and modification processing, gas explosion is handled stalk material fibre space is enlarged rapidly, than more significant vesicular structure is arranged before the explosion, modification is handled the adsorptivity of gas explosion stalk material is greatly improved, and stalk is abundant, cheap, its preparation method is simple, easy to operate, be used for handling effluent containing heavy metal ions technology, can reduce the effluent containing heavy metal ions processing cost significantly, in actual application, have special advantages.
Embodiment of the present invention are as follows:
The stalk sorbing material that is used to handle effluent containing heavy metal ions provided by the invention is characterized in that: this stalk sorbing material is a kind of steam puffed stalk of handling through steam explosion;
In order further to improve the adsorptive power of steam puffed stalk, the stalk sorbing material that is used to handle effluent containing heavy metal ions of the present invention, for a kind of through ZnCl
2Solution or FeCl
3The steam puffed stalk that the solution soaking modification was handled contains the ZnCl of 4-8g in the per kilogram steam puffed stalk
2Or the FeCl of 6-10g
3
The preparation method who is used to handle the stalk sorbing material of effluent containing heavy metal ions provided by the invention, it is characterized in that, comprise that the stalk material is carried out steam explosion to be handled: will be packed in the steam-explosion jar equipment by rough lumber to the long stalk of 20-30mm, operating pressure 1.2-1.7Mpa in the steam-explosion jar equipment, dimension was pressed 5-10 minute, instant decompression discharges, and just makes steam puffed stalk, stalk sorbing material promptly of the present invention;
The preparation method who is used to handle the stalk sorbing material of effluent containing heavy metal ions provided by the invention is characterized in that, comprises that also above-mentioned steam puffed stalk is carried out modification to be handled, and its modification is handled and comprised the steps:
1) in concentration the ZnCl of 4-8g/l with steam puffed stalk
2Solution or concentration are the FeCl of 6-10g/l
3Steep in the solution, make the ZnCl that contains 4-8g in the per kilogram steam puffed stalk
2Or the FeCl of 6-10g
3
2) filter above-mentioned soak solution, the steam puffed stalk seasoning after the filtration is crushed to the 20-80 order, promptly makes the ZnCl that contains that is used to handle effluent containing heavy metal ions of the present invention
2Or FeCl
3The stalk sorbing material.
Stalk sorbing material that is used for handling effluent containing heavy metal ions provided by the invention and preparation method thereof has following advantage: overcome shortcomings such as cost height that sorbing material that prior art is used to handle effluent containing heavy metal ions exists, processed complex; Stalk sorbing material of the present invention is selected cheap stalk for use, be a kind of stalk material through gas explosion and modification processing, gas explosion is handled its fibre space is enlarged rapidly, specific surface area increases, than more significant vesicular structure is arranged before the explosion, modification is handled the adsorptivity of gas explosion stalk material is greatly improved, and because stalk is abundant, its preparation method is simple, easy to operate, be used for handling effluent containing heavy metal ions technology, can reduce processing cost significantly, in actual application, have special advantages.
Embodiment
Below in conjunction with embodiment the present invention is further specified.
Embodiment 1: prepare stalk sorbing material of the present invention with the method for the invention provides, and handle sexavalent chrome heavy metal ion in heavy metal wastewater thereby with this stalk sorbing material:
1. prepare stalk sorbing material of the present invention: will be by rough lumber to the long 80kg stalk of the 25mm 1M that packs into
3In the steam-explosion jar, operating pressure 1.5Mpa in the steam-explosion jar, dimension was pressed 10 minutes, opened baiting valve, and instant decompression discharges, and just makes steam puffed stalk, i.e. the stalk sorbing material of present embodiment;
The stalk sorbing material that uses present embodiment to prepare is handled the sexavalent chrome heavy metal ion in the heavy metal wastewater thereby:
Adopt Static Adsorption and dynamic adsorption dual mode to handle:
1) Static Adsorption: with the 0.5g granularity is that the stalk sorbing material that 30 purpose present embodiments prepare mixes with 50ml waste water water sample, places shaking table vibration absorption, shakes speed and is 150rpm.Adsorption temp is 20 ℃, and wherein the waste water water sample adopts different pH values, different concentration of heavy metal ion, and different adsorption times, its adsorption effect is: chromic removal efficient is 84.3%.
2) dynamic adsorption: with the 3g granularity is that the stalk sorbing material of 30 purpose present embodiments preparations is filled in the packed column that external diameter is 3.6cm, and is 4.5 with different in flow rate with pH, and concentration is the K of 0.5g/l
2Cr
2O
7Solution slowly injects post, and calculates its saturated extent of adsorption: 2.07mg/g.
Steam puffed stalk is handled the underlying condition conclusion of hexavalent chromium wastewater:
The quick-fried processing of vapour has increased the specific surface area of stalk, has significantly improved the internal space of stalk, makes it have more micropore, has increased its adsorptive power, its adsorptive power with see Table 1 without the contrast of the quick-fried processing stalk of vapour material:
The quick-fried processing of table 1. vapour is to the influence of stalk specific surface area
Material | Specific surface area (cm 2/g) | Methylene blue decolorizing ability ml methylene blue/g material | Iodine sorption value mg iodine/g material |
The stalk material | 3.31 | 2 | 42.6 |
The steam puffed stalk material | 4.09 | 6 | 62.4 |
Steam puffed stalk is 0.5 to the optimal adsorption condition of Cr (VI) for water sample pH value, when concentration of heavy metal ion is 2.208g/l, and absorption 30min, Cr (VI) removes efficient can reach 84.30%;
Adsorption process accords with Freundlich isothermal adsorption formula, equation is lgx/m=0.34481gc-3.02g, shows that steam puffed stalk belongs to monolayer adsorption to the absorption of Cr (VI), and more or less freely;
When water sample concentration is 0.5g/l, pH is 4.5, and when crossing post with the speed of 4.3ml/min, the dynamic saturated extent of adsorption of steam puffed stalk is 2.07mg/g.
Embodiment 2: prepare stalk sorbing material of the present invention with the method for the invention provides, and handle ferric iron heavy metal ion in heavy metal wastewater thereby with this stalk sorbing material:
Prepare stalk sorbing material of the present invention: will be by rough lumber to the long 80kg stalk of the 30mm 1M that packs into
3In the steam-explosion jar, operating pressure 1.7Mpa in the steam-explosion jar, dimension was pressed 5 minutes, opened baiting valve, and instant decompression discharges, and just makes steam puffed stalk, i.e. the stalk sorbing material of present embodiment;
2. experimental implementation mode
Adopt Static Adsorption and two kinds of operating method of dynamic adsorption:
Static Adsorption: with the 1g granularity is that 45 purpose steam puffed stalks mix with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different heavy metal ion are dense, adsorbs the different time, and its adsorption effect is that iron ion removal efficient is 71.63%;
Dynamic adsorption: the 3g steam puffed stalk is filled in the packed column that external diameter is 3.6cm, and is 2 with different in flow rate with pH, concentration is that the ferric sulphate ammonium solution of 0.42g/l slowly injects post, and to calculate its saturated extent of adsorption be 6.57mg/g.
3. steam puffed stalk is handled the conclusion of Fe (III) waste water (present embodiment):
(1) steam puffed stalk is 2 to the optimal adsorption condition of Cr (VI) for water sample pH value, when concentration of heavy metal ion is 0.42g/l, and absorption 210min, Cr (VI) removes efficient can reach 71.63%;
(2) adsorption process accords with Freundlich isothermal adsorption formula, equation is lgx/m=1.9581gc-0.4828, shows that steam puffed stalk belongs to monolayer adsorption to the absorption of Cr (VI), and more or less freely;
(3) when water sample concentration be 0.42g/l, pH is 2.0, when crossing post with the speed of 6.7ml/min, the dynamic saturated extent of adsorption of steam puffed stalk is 6.57mg/g.
Embodiment 3: prepare stalk sorbing material of the present invention with the method for the invention provides, and handle sexavalent chrome heavy metal ion in heavy metal wastewater thereby with this stalk sorbing material:
Prepare stalk sorbing material of the present invention: its processing step is:
1) the quick-fried processing stalk of vapour material: will be by rough lumber to the long 80kg stalk of the 20mm 1M that packs into
3In the steam-explosion jar, operating pressure 1.2Mpa in the steam-explosion jar, dimension was pressed 10 minutes, opened baiting valve, and instant decompression discharges and promptly makes steam puffed stalk;
2) above-mentioned steam puffed stalk is handled in modification, manufactures the stalk sorbing material-steam puffed stalk zinc of present embodiment:
Above-mentioned steam puffed stalk is dipped in the ZnCl of 5g/l, 4g/l and 8g/l respectively
2In the solution, fully soak (present embodiment soaks 24h), use 5g/l ZnCl
2During solution soaking, 1g steam puffed stalk material is dipped in 10ml ZnCl
2In the solution; Use 4g/l ZnCl
2During solution soaking, 1g steam puffed stalk material is dipped in 12ml ZnCl
2In the solution; Use 8g/l ZnCl
2During solution soaking, 1g steam puffed stalk material is dipped in 15ml ZnCl
2In the solution;
3) filter above-mentioned mixed solution respectively, the stalk material after the filtration is crushed to it 30 orders afterwards through seasoning, promptly gets the stalk sorbing material-steam puffed stalk zinc of present embodiment;
Present embodiment concentration is the ZnCl of 5g/l
2Solution soaking and the steam puffed stalk zinc for preparing, ZnCl in every gram steam puffed stalk zinc
2Content be 0.05 the gram;
With concentration is the ZnCl of 4g/l
2Solution soaking and the steam puffed stalk zinc for preparing, ZnCl in every gram steam puffed stalk zinc
2Content be 0.048 the gram;
With concentration is the ZnCl of 8g/l
2Solution soaking and the steam puffed stalk zinc for preparing, ZnCl in every gram steam puffed stalk zinc
2Content be 0.12 the gram.
The experimental implementation mode
Static Adsorption and two kinds of operating method of dynamic adsorption are adopted in this experiment:
Static Adsorption: with the 0.5g granularity is that 30 orders are through 5g/l ZnCl
2The steam puffed stalk zinc of solution soaking mixes with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different concentration of heavy metal ion adsorb the different time, and its optimal adsorption effect is that hexavalent chromium removal efficient is 86.76%.
With the 0.5g granularity is that 30 orders are through 4g/l ZnCl
2The steam puffed stalk zinc of solution soaking mixes with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different concentration of heavy metal ion adsorb the different time, and its optimal adsorption effect is that hexavalent chromium removal efficient is 85.28%.
With the 0.5g granularity is that 30 orders are through 8g/l ZnCl
2The steam puffed stalk zinc of solution soaking mixes with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different concentration of heavy metal ion adsorb the different time, and its adsorption effect is that hexavalent chromium removal efficient is 86.84%.
Dynamic adsorption: with 3g through 5gl ZnCl
2The steam puffed stalk zinc that solution soaking was handled is filled in the packed column that external diameter is 3.6cm, and is 6.0 with different in flow rate with pH, and concentration is the K of 1ug/ml
2Cr
2O
7Solution slowly injects post, and to calculate its saturated extent of adsorption be 5.15mg/g.
With 3g through 4g/l ZnCl
2The steam puffed stalk zinc that solution soaking was handled is filled in the packed column that external diameter is 3.6cm, and is 6.0 with different in flow rate with pH, and concentration is the K of 1ug/ml
2Cr
2O
7Solution slowly injects post, and to calculate its saturated extent of adsorption be 4.96mg/g.
With 3g through 8g/l ZnCl
2The steam puffed stalk zinc that solution soaking was handled is filled in the packed column that external diameter is 3.6cm, and is 6.0 with different in flow rate with pH, and concentration is the K of 1ug/ml
2Cr
2O
7Solution slowly injects post, and to calculate its saturated extent of adsorption be 5.23mg/g.
Steam puffed stalk zinc is handled the underlying condition conclusion of hexavalent chromium wastewater:
(1). steam puffed stalk zinc is 1.0 to the optimal adsorption condition of Cr (VI) for water sample pH value, when concentration of heavy metal ion is 0.125ug/ml, absorption 4h, the removal efficient of Cr (VI) can reach 86.84%.
(2). adsorption process accords with Langmuir isothermal adsorption formula, equation is Ce/q=0.6847Ce+1.617, relation conefficient is r=0.9992, shows that steam puffed stalk zinc belongs to monolayer adsorption to the absorption of Cr (VI)
(3). when water sample concentration is 1ug/ml, pH is 6.0, and when crossing post with the speed of 21.82ml/min, the dynamic saturated extent of adsorption of steam puffed stalk zinc is 5.23mg/g.
Embodiment 4: prepare stalk sorbing material of the present invention with the method for the invention provides, and handle sexavalent chrome heavy metal ion in heavy metal wastewater thereby with this stalk sorbing material:
Prepare stalk sorbing material of the present invention: its processing step is:
1) the quick-fried processing stalk of vapour material: will be by rough lumber to the long 80kg stalk of the 20mm 1M that packs into
3In the steam-explosion jar, operating pressure 1.2Mpa in the steam-explosion jar, dimension was pressed 10 minutes, opened baiting valve, and instant decompression discharges and promptly makes steam puffed stalk;
2) above-mentioned steam puffed stalk is handled in modification, manufactures the stalk sorbing material-steam puffed stalk zinc of present embodiment:
Above-mentioned steam puffed stalk material is dipped in the ZnCl of 5g/l, 4g/l, 8g/l respectively
2In the solution, fully soak (present embodiment soaks 24h), use 5g/l ZnCl
2During solution soaking, 1g steam puffed stalk material is dipped in 10mlZnCl
2In the solution; Use 4g/l ZnCl
2During solution soaking, 1g steam puffed stalk material is dipped in 12mlZnCl
2In the solution; Use 8g/l ZnCl
2During solution soaking, 1g steam puffed stalk material is dipped in 15mlZnCl
2In the solution;
3) filter above-mentioned mixed solution respectively, the stalk material after the filtration is crushed to it 80 orders afterwards through seasoning, promptly gets the stalk sorbing material-steam puffed stalk zinc of present embodiment;
Present embodiment concentration is the ZnCl of 5g/l
2Solution soaking and the steam puffed stalk zinc for preparing, ZnCl in every gram steam puffed stalk zinc
2Content be 0.05 the gram;
With concentration is the ZnCl of 4g/l
2Solution soaking and the steam puffed stalk zinc for preparing, ZnCl in every gram steam puffed stalk zinc
2Content be 0.048 the gram;
With concentration is the ZnCl of 8g/l
2Solution soaking and the steam puffed stalk zinc for preparing, ZnCl in every gram steam puffed stalk zinc
2Content be 0.12 the gram.
The experimental implementation mode
Static Adsorption and two kinds of operating method of dynamic adsorption are adopted in this experiment:
Static Adsorption: with the 0.5g granularity is that 80 orders are through 5g/l ZnCl
2The steam puffed stalk zinc of solution soaking mixes with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different concentration of heavy metal ion adsorb the different time, and its optimal adsorption effect is that hexavalent chromium removal efficient is 86.75%.
With the 0.5g granularity is that 80 orders are through 4g/l ZnCl
2The steam puffed stalk zinc of solution soaking mixes with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different concentration of heavy metal ion adsorb the different time, and its adsorption effect is that hexavalent chromium removal efficient is 86.23%.
With the 0.5g granularity is that 80 orders are through 8g/l ZnCl
2The steam puffed stalk zinc of solution soaking mixes with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different concentration of heavy metal ion adsorb the different time, and its optimal adsorption effect is that hexavalent chromium removal efficient is 86.84%.
Dynamic adsorption: with the 3gg0 order through 5g/l ZnCl
2The steam puffed stalk zinc that solution soaking is crossed is filled in the packed column that external diameter is 3.6cm, and is 6.0 with different in flow rate with pH, and concentration is the K of 1ug/ml
2Cr
2O
7Solution slowly injects post, and to calculate its saturated extent of adsorption be 5.15mg/g.
With the 3g80 order through 4g/l ZnCl
2The steam puffed stalk zinc that solution soaking is crossed is filled in the packed column that external diameter is 3.6cm, and is 6.0 with different in flow rate with pH, and concentration is the K of 1ug/ml
2Cr
2O
7Solution slowly injects post, and to calculate its saturated extent of adsorption be 5.06mg/g;
With the 3g80 order through 8g/l ZnCl
2The steam puffed stalk zinc that solution soaking is crossed is filled in the packed column that external diameter is 3.6cm, and is 6.0 with different in flow rate with pH, and concentration is the K of 1ug/ml
2Cr
2O
7Solution slowly injects post, and to calculate its saturated extent of adsorption be 5.23mg/g;
Steam puffed stalk zinc is handled the underlying condition conclusion of hexavalent chromium wastewater:
(1) steam puffed stalk zinc is 1.0 to the optimal adsorption condition of Cr (VI) for water sample pH value, when concentration of heavy metal ion is 0.125ug/ml, and absorption 4h, the removal efficient of Cr (VI) can reach 86.84%.
(2) adsorption process meets Lamgmuir isothermal adsorption formula, and equation is Ce/q=0.6847Ce+1.617, and relation conefficient is r=0.9992, shows that steam puffed stalk zinc belongs to monolayer adsorption to the absorption of Cr (VI)
When water sample concentration is 1ug/ml, pH is 6.0, and when crossing post with the speed of 21.82ml/min, the dynamic saturated extent of adsorption of steam puffed stalk zinc is 5.23mg/g.
Embodiment 5: prepare stalk sorbing material of the present invention with the method for the invention provides, and handle sexavalent chrome heavy metal ion in heavy metal wastewater thereby with this stalk sorbing material:
Prepare stalk sorbing material of the present invention: its processing step is:
1. the quick-fried processing stalk of vapour material:
The stalk 80kg that rough lumber is grown to the about 25mm 1M that packs into
3In the steam-explosion jar, feed steam, treat in the drain tank to close the charging valve behind the freezing air, boost to 1.5Mpa, dimension is pressed 10min, opens baiting valve, and instant decompression discharges and promptly gets steam puffed stalk;
2. above-mentioned steam puffed stalk is handled in modification, manufactures the stalk sorbing material-steam puffed stalk iron of present embodiment:
Above-mentioned steam puffed stalk material is dipped in the FeCl of 6g/l, 8g/l, 10g/l respectively
3In the solution, fully soak (present embodiment soaks 24h), use 6g/l FeCl
3During solution soaking, 1g steam puffed stalk material is dipped in 10mlFeCl
3In the solution; Use 8g/l FeCl
3During solution soaking, 1g steam puffed stalk material is dipped in 12mlFeCl
3In the solution; Use 10g/l FeCl
3During solution soaking, 1g steam puffed stalk material is dipped in 15mlFeCl
3In the solution;
4) filter above-mentioned mixed solution respectively, the steam puffed stalk after the filtration is crushed to it 20 orders afterwards through seasoning, promptly gets the stalk sorbing material-steam puffed stalk iron of present embodiment;
Present embodiment concentration is the FeCl of 6g/l
3Solution soaking and the steam puffed stalk iron for preparing, FeCl in every gram steam puffed stalk iron
3Content be 0.06 the gram;
With concentration is the FeCl of 8g/l
3Solution soaking and the steam puffed stalk iron for preparing, FeCl in every gram steam puffed stalk iron
3Content be 0.096 the gram;
With concentration is the FeCl of 10g/l
3Solution soaking and the steam puffed stalk iron for preparing, FeCl in every gram steam puffed stalk iron
3Content be 0.15 the gram.
The experimental implementation mode
Static Adsorption and two kinds of operating method of dynamic adsorption are adopted in this experiment:
Static Adsorption: with the 0.5g granularity is that 20 orders are through 6g/l FeCl
3The steam puffed stalk zinc of solution soaking mixes with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different concentration of heavy metal ion adsorb the different time, and its optimal adsorption effect is that hexavalent chromium removal efficient is 88.68%.
With the 0.5g granularity is that 20 orders are through 8g/l FeCl
3The steam puffed stalk zinc of solution soaking mixes with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different concentration of heavy metal ion adsorb the different time, and its optimal adsorption effect is that hexavalent chromium removal efficient is 88.75%.
With the 0.5g granularity is that 20 orders are through 10g/l FeCl
3The steam puffed stalk zinc of solution soaking mixes with the 50ml water sample, places shaking table vibration absorption, shakes speed and is 150rpm, and adsorption temp is 20 ℃.Wherein water sample adopts different pH values, and different concentration of heavy metal ion adsorb the different time, and its adsorption effect is that hexavalent chromium removal efficient is 88.85%.
Dynamic adsorption: with 3g through 6g/l FeCl
3The steam puffed stalk zinc that solution soaking was handled is filled in the packed column that external diameter is 3.6cm, and is 6.0 with different in flow rate with pH, and concentration is the K of 1ug/ml
2Cr
2O
7Solution slowly injects post, and to calculate its saturated extent of adsorption be 5.18mg/g.
With 3g through 8g/l FeCl
3The steam puffed stalk zinc that solution soaking was handled is filled in the packed column that external diameter is 3.6cm, and is 6.0 with different in flow rate with pH, and concentration is the K of 1ug/ml
2Cr
2O
7Solution slowly injects post, and to calculate its saturated extent of adsorption be 5.21mg/g.
With 3g through 10g/1 FeCl
3The steam puffed stalk zinc that solution soaking was handled is filled in the packed column that external diameter is 3.6cm, and is 6.0 with different in flow rate with pH, and concentration is the K of 1ug/ml
2Cr
2O
7Solution slowly injects post, and to calculate its saturated extent of adsorption be 5.23mg/g.
Steam puffed stalk iron is handled the underlying condition conclusion of hexavalent chromium wastewater
(1). steam puffed stalk iron is 3.0 to the optimal adsorption condition of Cr (VI) for water sample pH value, when concentration of heavy metal ion is 0.125ug/ml, absorption 4h, the removal efficient of Cr (VI) can reach 88.85%.
(2). adsorption process accords with Langmuir isothermal adsorption formula, equation is Ce/q=0.6838Ce+1.621, relation conefficient is r=0.9992, shows that steam puffed stalk iron belongs to monolayer adsorption to the absorption of Cr (VI)
(3). when water sample concentration is 1ug/ml, pH is 6.0, and when crossing post with the speed of 21.82ml/min, the dynamic saturated extent of adsorption of steam puffed stalk iron is 5.24mg/g.
(4). under identical adsorption conditions, steam puffed stalk, steam puffed stalk zinc, steam puffed stalk iron see Table 2 to the adsorption effect of Cr (VI).
The different sorbent materials of table 2. are to the adsorption effect of Cr (VI)
Water sample pH value | Adsorption time (h) | Adsorption temp (℃) | Cr (VI) removes efficient (%) | |
The steam puffed stalk sorbent material | 3 | 4 | 20 | 21.47 |
Steam puffed stalk zinc sorbent material | 3 | 4 | 20 | 86.17 |
The steam puffed stalk iron adsorbent | 3 | 4 | 20 | 88.85 |
Claims (3)
1, a kind of stalk sorbing material that is used to handle effluent containing heavy metal ions is characterized in that: this stalk sorbing material is a kind of through the steam explosion processing with through ZnCl
2Solution or FeCl
3The steam puffed stalk that the solution soaking modification was handled.
2, by the described stalk sorbing material that is used to handle effluent containing heavy metal ions of claim 1, it is characterized in that, contain the ZnCl of 4-8g in the per kilogram steam puffed stalk
2Or the FeCl of 6-10g
3
3, a kind of preparation method who is used to handle the stalk sorbing material of effluent containing heavy metal ions is characterized in that, comprises the steps:
1) the stalk material being carried out steam explosion handles: will be packed in the steam-explosion jar equipment by rough lumber to the long stalk of 20-30mm, and the operating pressure 1.2---1.7Mpa in the steam-explosion jar equipment, dimension was pressed 5--10 minute, and instant decompression discharges, and makes steam puffed stalk;
2) steam puffed stalk of handling through steam explosion is carried out modification and handle, its modification treatment step is:
A) in concentration the ZnCl of 4-8g/l with steam puffed stalk
2Solution or concentration are the FeCl of 6-10g/l
3Fully soak in the solution, make the ZnCl that contains 4-8g in the per kilogram steam puffed stalk
2Or the FeCl of 6-10g
3
B) filter above-mentioned soak solution, the steam puffed stalk seasoning after the filtration is crushed to the 20-80 order, promptly makes the ZnCl that contains that the present invention is used to handle effluent containing heavy metal ions
2Or FeCl
3The stalk sorbing material.