CN115353783A - 一种轻质、安全护卫的环保涂料 - Google Patents
一种轻质、安全护卫的环保涂料 Download PDFInfo
- Publication number
- CN115353783A CN115353783A CN202210881610.1A CN202210881610A CN115353783A CN 115353783 A CN115353783 A CN 115353783A CN 202210881610 A CN202210881610 A CN 202210881610A CN 115353783 A CN115353783 A CN 115353783A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- emulsion
- coating
- friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种轻质、安全护卫的环保涂料，本发明环保涂料涉及涂料组合物领域，其原料配方包括：纯净水、建筑助剂分散剂、建筑助剂、建筑乳、填料、羟乙基纤维素、流平助剂、防腐杀菌剂、防霉剂、缔合型增稠剂，本发明的涂料具有良好的耐水性、耐候性、耐久性，还具有良好的伸缩性，对涂层的微裂缝追随性强，本发明材料具有良好的拉伸强度和粘结强度，并具有较好的柔韧性，而其制备方法工艺简单，生产中无毒害产生，绿色环保，适于大规模工业化生产。
Description
技术领域
本发明涉及环保涂料，更具体地说，尤其涉及一种轻质、安全护卫的环保 涂料。
背景技术
涂料工业正在由高污染、高能耗、极度依赖于石油工业产品的传统品种逐 渐转向水性涂料、环境友好、多功能、资源节约型方向发展，中国《环境标志 产品技术要求水性涂料》、《室内用水性木器涂料》环境保护行业、化工行业 标准等的陆续出台，促进了水性涂料的发展，阻燃型水性功能涂料研发与应用 亦越来越广泛。
中国专利号CN103275575A公开了一种木质材料用聚丙烯酸乳液防火涂料， 它主要是由下列原料按照重量配比制成：110-120份聚丙烯酸乳液，36-40份闭 孔珍珠岩，20-24份醋酸丁酯，15-18份过氧化苯甲酰，10份硫酸钡，10份石 油醚，15份高岭土和8-10份三氧化二锑；该发明经工业试验证明，对木质材料 的表面进行涂饰处理，形成的聚丙烯酸乳液防火涂层具有粘结强度高、阻燃性 好的显著特点，并且在固化过程中无有机溶剂挥发、环保。但是，该发明涂料 以三氧化二锑为阻燃剂，不但存在分散不均匀的缺点，而且在涂料的使用中三 氧化二锑会不断游离至涂料表面导致阻燃性能不断降低。
发明内容
本发明针对上述缺点对现有技术进行改进，提供一种轻质、安全护卫的环 保涂料，技术方案如下：
一种轻质、安全护卫的环保涂料，所述的环保涂料的原料配方按质量百分 比的组分包括：
纯净水300份
建筑助剂分散剂1-2分
建筑助剂1-2份
建筑乳液350-400份
填料190-250份
羟乙基纤维素3-4份
流平助剂20-25份
防腐杀菌剂1-2份
防霉剂1-2份
缔合型增稠剂4-5份。
所述的乳液为丙烯酸乳液-弹性乳液。
所述填料由绒毛粉、轻质聚氨酯微球和水晶珠光粉组成，其分别按质量百 分比的组分为绒毛粉100-150份、轻质聚氨酯微球45-50份和水晶珠光粉45-50 份。
上述环保涂料的制备方法，所述的制备方法包括以下步骤：
步骤(1)：根据所述的环保涂料的各组分的质量百分比，将所述的建筑助剂分 散剂、羟乙基纤维素、水晶珠光粉和纯净水于室温下均匀混合，并研磨至40μm 以下；
步骤(2)：在300～500rpm的搅拌转速下，加入所述的有机硅消泡剂、乳液混 合均匀后反应；
步骤(3)：往反应后材料中加入绒毛粉、轻质聚氨酯微球和缔合型增稠剂助剂 添加调漆；
步骤(4)：过滤灌装；
步骤(5)：抽样检测；
步骤(6)：制袋装桶；
步骤(7)：清洁装置；
步骤(8)：成品出库。
与现有技术相比，本发明的有益效果为：本发明的涂料具有良好的耐水性、 耐候性、耐久性，还具有良好的伸缩性，对涂层的微裂缝追随性强，材料具有 良好的拉伸强度和粘结强度，并具有较好的柔韧性，而其制备方法工艺简单， 生产中无毒害产生，绿色环保，适于大规模工业化生产。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述 的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明的实 施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实 施例，都属于本发明的保护范围。
下面将对本发明实施例作进一步地详细描述，详细如下：
一种轻质、安全护卫的环保涂料，所述的环保涂料的原料配方按质量百分 比的组分包括：
纯净水300份
建筑助剂分散剂1-2分
建筑助剂1-2份
建筑乳液350-400份
填料190-250份
羟乙基纤维素3-4份
流平助剂20-25份
防腐杀菌剂1-2份
防霉剂1-2份
缔合型增稠剂4-5份。
所述的乳液为丙烯酸乳液-弹性乳液。
所述填料由绒毛粉、轻质聚氨酯微球和水晶珠光粉组成，其分别按质量百 分比的组分为绒毛粉100-150份、轻质聚氨酯微球45-50份和水晶珠光粉45-50 份。
实施例一：
环保涂料的原料配方(wt％)见下表1
其制备方法包括以下步骤：
步骤(1)：根据所述的环保涂料的各组分的质量百分比，将所述的建筑助 剂分散剂、羟乙基纤维素、水晶珠光粉和纯净水于室温下均匀混合，并研磨至 40μm以下；
步骤(2)：在300～500rpm的搅拌转速下，加入所述的有机硅消泡剂、乳 液混合均匀后反应；
步骤(3)：往反应后材料中加入绒毛粉、轻质聚氨酯微球和缔合型增稠剂 助剂添加调漆；
步骤(4)：过滤灌装；
步骤(5)：抽样检测；
步骤(6)：制袋装桶；
步骤(7)：清洁装置；
步骤(8)：成品出库。
实施例二：
环保涂料的原料配方(wt％)见下表2
其制备方法包括以下步骤：
步骤(1)：根据所述的环保涂料的各组分的质量百分比，将所述的建筑助 剂分散剂、羟乙基纤维素、水晶珠光粉和纯净水于室温下均匀混合，并研磨至 40μm以下；
步骤(2)：在300～500rpm的搅拌转速下，加入所述的有机硅消泡剂、乳 液混合均匀后反应；
步骤(3)：往反应后材料中加入绒毛粉、轻质聚氨酯微球和缔合型增稠剂 助剂添加调漆；
步骤(4)：过滤灌装；
步骤(5)：抽样检测；
步骤(6)：制袋装桶；
步骤(7)：清洁装置；
步骤(8)：成品出库。
本发明的涂料具有良好的耐水性、耐候性、耐久性，本发明还涂料具有良 好的伸缩性，对涂层的微裂缝追随性强，本发明材料具有良好的拉伸强度和粘 结强度，并具有较好的柔韧性，而其制备方法工艺简单，生产中无毒害产生， 绿色环保，适于大规模工业化生产。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言， 可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变 化、修改、替换和变形，本发明的范围由所附权利要求及其等同物限定。
Claims (4)
1.一种轻质、安全护卫的环保涂料，其特征在于，所述的环保涂料的原料配方按质量百分比的组分包括：
纯净水300份
建筑助剂分散剂1-2分
建筑助剂1-2份
建筑乳液350-400份
填料190-250份
羟乙基纤维素3-4份
流平助剂20-25份
防腐杀菌剂1-2份
防霉剂1-2份
缔合型增稠剂4-5份。
2.根据权利要求1所述的一种具有高强耐擦洗、仿皮革的环保涂料，其特征在于，所述的乳液为丙烯酸乳液-弹性乳液。
3.根据权利要求1所述的一种具有高强耐擦洗、仿皮革的环保涂料，其特征在于，所述填料由绒毛粉、轻质聚氨酯微球和水晶珠光粉组成，其分别按质量百分比的组分为绒毛粉100-150份、轻质聚氨酯微球45-50份和水晶珠光粉45-50份。
4.一种根据权利要求1所述的环保涂料的制备方法，其特征在于，所述的制备方法包括以下步骤：
步骤(1)：根据所述的环保涂料的各组分的质量百分比，将所述的建筑助剂分散剂、羟乙基纤维素、水晶珠光粉和纯净水于室温下均匀混合，并研磨至40μm以下；
步骤(2)：在300～500rpm的搅拌转速下，加入所述的有机硅消泡剂、乳液混合均匀后反应；
步骤(3)：往反应后材料中加入绒毛粉、轻质聚氨酯微球和缔合型增稠剂助剂添加调漆；
步骤(4)：过滤灌装；
步骤(5)：抽样检测；
步骤(6)：制袋装桶；
步骤(7)：清洁装置；
步骤(8)：成品出库。