CN115260982B - Self-healing silicone sealant and preparation method thereof - Google Patents
Self-healing silicone sealant and preparation method thereof Download PDFInfo
- Publication number
- CN115260982B CN115260982B CN202211124445.1A CN202211124445A CN115260982B CN 115260982 B CN115260982 B CN 115260982B CN 202211124445 A CN202211124445 A CN 202211124445A CN 115260982 B CN115260982 B CN 115260982B
- Authority
- CN
- China
- Prior art keywords
- self
- healing
- silicone sealant
- groups
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a self-healing silicone sealant and a preparation method thereof, wherein the raw materials of the self-healing silicone sealant comprise a self-healing agent and metal salt; the self-healing agent is obtained by reacting hydrogen-containing silane and an amide olefine acid compound under the action of a catalyst; the structural formula of the hydrogen-containing silane is HSi (R 1 )(OR 2 ) 2 Wherein R is 1 Selected from: c (C) 1 ‑C 6 Alkoxy, C 1 ‑C 6 Alkyl, R 2 Selected from: c (C) 1 ‑C 6 An alkyl group; the structural formula of the amide alkenoic acid compound is H 2 NCOCH＝CH(CH 2 ) m COOH, wherein m is selected from: 0. 1, 2, 3, 4; the metal salt consists of ferric salt and zinc salt. The self-healing silicone sealant has good self-healing effect and excellent mechanical property.
Description
Technical Field
The invention relates to the field of sealants, in particular to a self-healing silicone sealant and a preparation method thereof.
Background
The condensed silicone rubber has good flexibility, high and low temperature resistance and weather resistance, can be spontaneously crosslinked to form an elastomer at normal temperature, is simple in construction operation, and is widely applied to the field of building joint sealing. In the use process of the sealant, the problems of damage, defect or bubble and the like of the sealant are easily caused due to improper or error manual construction operation, so that the mechanical property of the sealant is reduced, and even the sealant is invalid when serious. In particular to structural sealant for curtain walls, which plays a role of bonding curtain wall glass and an aluminum alloy frame, once the bonding strength of the sealant is greatly reduced, the weight of the curtain wall glass cannot be born, and the glass can fall down from high altitude, so that the life safety of people is seriously endangered.
The self-healing material is capable of realizing self-healing after being damaged and recovering the performance of the material. Currently, most self-healing materials are achieved by physical or chemical action that introduces dynamic bonds. Common dynamic bonds include dynamic non-covalent bonds and dynamic covalent bonds. Dynamic non-covalent bonds refer to a relatively weak reversible interaction between molecules, such as hydrogen bonding, ionic bonding, coordination bonding, pi-pi stacking, and the like.
After the silicone sealant is cured, an irreversible covalent cross-linking bond of Si-O-Si exists in the system, and the silicone sealant does not have the capability of repairing damage. When the sealant is used for building joint filling, damage or bubbles existing in the colloid cannot be found in time due to the limitation of the use environment, and the colloid performance is easy to be reduced.
The inventors of the present invention have found in the previous studies that synthesizing a hydrogen-containing silane and an amidic acid compound under the catalysis of chloroplatinic acid as a self-healing agent can achieve a self-healing property of a condensation type silicone sealant of about 60 to 70%. Further research shows that the self-healing agent is added with metal ions (such as Fe 3+ ，Al 3+ ，Cu 2+ Etc.), the self-healing capability and/or mechanical properties of the silicone sealant can be further improved, wherein Fe 3+ The effect is most remarkable, and the self-healing performance of the silicone sealant can reach about 75-82%.
Disclosure of Invention
The invention aims to further improve the self-healing performance of a condensation type silicone sealant.
In order to achieve the above purpose, the invention comprises the following technical scheme.
The self-healing silicone sealant comprises a self-healing agent and metal salt;
the self-healing agent is obtained by reacting hydrogen-containing silane and an amide olefine acid compound under the action of a catalyst;
the structural formula of the hydrogen-containing silane is HSi (R 1 )(OR 2 ) 2 Wherein R is 1 Selected from: c (C) 1 -C 6 Alkoxy, C 1 -C 6 Alkyl, R 2 Selected from: c (C) 1 -C 6 An alkyl group;
the structural formula of the amide alkenoic acid compound is H 2 NCOCH＝CH(CH 2 ) m COOH, wherein m is selected from: 0. 1 part(s),2、3、4；
The metal salt consists of ferric salt and zinc salt.
In some embodiments, the self-healing silicone sealant comprises the following raw materials in parts by weight:
in some of these embodiments, R 1 Selected from: -OCH 3 、-OCH 2 CH 3 、-CH 3 、-CH 2 CH 3 ，R 2 is-CH 3 or-CH 2 CH 3 。
In some embodiments, m is 0 or 1.
In some of these embodiments, the mass ratio of the hydrogen-containing silane to the amideoic acid compound is 1:0.7-1.3.
In some of these embodiments, the hydrogen-containing silane is HSi (OCH) 3 ) 3 The amide alkenoic acid compound is H 2 NCOCH＝CHCOOH；
Preferably, HSi (OCH) 3 ) 3 And H 2 Ncoch=chcooh at a mass ratio of 1:0.8-1.
In some of these embodiments, the hydrogen-containing silane is HSi (OCH) 2 CH 3 ) 3 The amide alkenoic acid compound is H 2 NCOCH＝CHCH 2 COOH；
Preferably, HSi (OCH) 2 CH 3 ) 3 And H 2 NCOCH＝CHCH 2 The mass ratio of COOH is 1:0.7-0.9.
In some of these embodiments, the hydrogen-containing silane is HSi (CH 3 )(OCH 3 ) 2 The amide alkenoic acid compound is H 2 NCOCH＝CHCH 2 COOH；
Preferably, HSi (CH 3 )(OCH 3 ) 2 And H 2 NCOCH＝CHCH 2 The mass ratio of COOH is 1:1.1-1.3.
In some of these embodimentsThe hydrogen-containing silane is HSi (CH) 2 CH 3 )(OCH 2 CH 3 ) 2 The amide alkenoic acid compound is H 2 NCOCH＝CHCOOH；
Preferably, HSi (CH 2 CH 3 )(OCH 2 CH 3 ) 2 And H 2 Ncoch=chcooh at a mass ratio of 1:0.7-0.9.
In some of these embodiments, the catalyst is chloroplatinic acid.
In some of these embodiments, the mass ratio of the hydrogen-containing silane to the catalyst is 1:0.002% -0.008%.
In some of these embodiments, the method of preparing the self-healing agent comprises the steps of: adding the hydrogen-containing silane, the amide olefine acid compound and the catalyst into an organic solvent, heating to 60-90 ℃, reacting for 60-210 min, then heating to 70-100 ℃ and continuously reacting for 4-7 hours, finally heating the temperature in a reaction kettle to 110-130 ℃ and vacuumizing to remove the solvent, thus obtaining the self-healing agent.
In some embodiments, the organic solvent is selected from at least one of toluene, xylene, and petroleum ether.
In some of these embodiments, the mass ratio of the hydrogen-containing silane to the organic solvent is 1:0.6-2.
In some embodiments, the time for vacuumizing and removing the solvent is 100 min-210min, and the vacuum degree is-0.090 MPa to-0.099 MPa.
In some of these embodiments, the metal salt consists of ferric chloride and zinc chloride.
In some of these embodiments, the metal salt consists of a mass ratio of 1:0.2-3 of ferric chloride and zinc chloride.
In some of these embodiments, the metal salt consists of a mass ratio of 1:0.8-1.2 of ferric chloride and zinc chloride.
In some of these embodiments, the metal salt consists of a mass ratio of 1:0.3-0.5 of ferric chloride and zinc chloride.
In some of these embodiments, the alpha, omega-dihydroxy polydimethylsiloxane has a viscosity of from 5 Pa.s to 100 Pa.s at 25 ℃.
In some of these embodiments, the simethicone has a viscosity of 0.2 Pa-s to 0.5 Pa-s at 25 ℃.
In some embodiments, the inorganic filler is selected from at least one of nano-activated calcium carbonate, heavy calcium carbonate, silica fume, and diatomaceous earth.
In some of these embodiments, the cross-linking agent is selected from at least one of methyltrimethoxysilane, propyltrimethoxysilane, octyltrimethoxysilane, and phenyltrimethoxysilane.
In some of these embodiments, the coupling agent is selected from at least one of gamma-aminopropyl trialkoxysilane, N- (beta-aminoethyl) -gamma-aminopropyl trialkoxysilane, gamma-glycidoxypropyl trialkoxysilane, gamma-mercaptopropyl trimethoxysilane, and 3-isocyanatopropyl trialkoxysilane.
In some of these embodiments, the catalyst is selected from at least one of tetraisopropyl titanate, tetrabutyl titanate, diisopropyl di (ethylacetoacetate) titanate, dibutoxybis (ethylacetoacetate) titanate, and diisobutyl di (ethylacetoacetate) titanate.
In some embodiments, the self-healing silicone sealant comprises the following raw materials in parts by weight:
the viscosity of the alpha, omega-dihydroxy polydimethylsiloxane is 50 Pa.s-90 Pa.s at 25 ℃;
the viscosity of the simethicone at 25 ℃ is 0.2 Pa.s-0.4 Pa.s;
the inorganic filler is nano active calcium carbonate;
the cross-linking agent is methyltrimethoxysilane;
the coupling agent is gamma-aminopropyl trialkoxy silane and/or gamma-mercaptopropyl trimethoxy silane.
In some embodiments, the self-healing silicone sealant comprises the following raw materials in parts by weight:
the hydrogen-containing silane is HSi (OCH) 2 CH 3 ) 3 The amide alkenoic acid compound is H 2 NCOCH＝CHCH 2 COOH, the HSi (OCH) 2 CH 3 ) 3 And H 2 NCOCH＝CHCH 2 The mass ratio of COOH is 1:0.7 to 0.9;
the viscosity of the alpha, omega-dihydroxy polydimethylsiloxane is 70 Pa.s-90 Pa.s at 25 ℃;
the viscosity of the simethicone at 25 ℃ is 0.3 Pa.s-0.4 Pa.s;
the inorganic filler is nano active calcium carbonate;
the cross-linking agent is methyltrimethoxysilane;
the coupling agent is gamma-mercaptopropyl trimethoxy silane.
The invention also provides a preparation method of the self-healing silicone sealant, which comprises the following technical scheme.
The preparation method of the self-healing silicone sealant comprises the following steps:
dehydrating and blending the alpha, omega-dihydroxyl polysiloxane, the dimethyl silicone oil and the inorganic filler for 60-180 minutes under the conditions that the temperature is 80-150 ℃ and the vacuum degree is minus 0.06MPa to minus 0.099MPa, and cooling to obtain a base material; and (3) putting the base material into a stirrer, adding the cross-linking agent, the coupling agent, the self-healing agent, the metal salt and the catalyst, and mixing and reacting for 40-120 min under the condition that the vacuum degree is minus 0.06MPa to minus 0.099MPa and the stirring speed is 50-800 rpm, thus obtaining the self-healing silicone sealant.
In the previous researches, the inventor prepares a novel self-healing agent through the reaction of specific hydrogen-containing silane and amide olefine acid compounds under the action of a catalyst, and the self-healing agent is prepared into the condensation type silicone sealant, so that the condensation type silicone sealant is successfully endowed with good self-healing performance, and the mechanical property of the silicone sealant is improved.
The inventor further researches that the multi-crosslinking network can be constructed by further adding ferric salt and zinc salt on the basis of adding the self-healing agent into the silicone sealant, the ferric salt, the zinc salt and the self-healing agent have a synergistic effect, and the self-healing capacity and the mechanical property of the obtained silicone sealant can be further improved. When the obtained silicone sealant is used for building joint filling and sealing, good bonding strength can be provided, and meanwhile, the damage of the sealant caused by air bubbles and artificial construction can be repaired, so that the risk of rubber material failure is reduced.
Detailed Description
The technical scheme of the invention is further described by the following specific examples. It will be apparent to those skilled in the art that the examples are merely to aid in understanding the invention and are not to be construed as a specific limitation thereof.
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. The terminology used in the description of the invention herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention.
The terms "comprising" and "having" and any variations thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, apparatus, article, or device that comprises a list of steps is not limited to the elements or modules listed but may alternatively include additional steps not listed or inherent to such process, method, article, or device.
In the present invention, the term "plurality" means two or more. "and/or", describes an association relationship of an association object, and indicates that there may be three relationships, for example, a and/or B, and may indicate: a exists alone, A and B exist together, and B exists alone. The character "/" generally indicates that the context-dependent object is an "or" relationship.
The viscosity in the invention refers to the viscosity under the test condition of 25 ℃.
Example 1
32 parts of HSi (OCH) 3 ) 3 Added into a reaction kettle filled with 30 parts of toluene and stirred to obtain a mixed solution. 30 parts of H 2 NCOCH=CHCOOH and 0.0010 part of chloroplatinic acid are added into the mixed solution, the temperature is raised to 65 ℃, the reaction is carried out for 180min, and the temperature is continuously raised to 75 ℃ for continuous reaction for 6 hours; finally, the temperature in the reaction kettle is increased to 110 ℃, and the reaction kettle is vacuumized to-0.090 MPa to remove the solvent for 180min, so as to obtain the self-healing agent.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with 50 Pa.s viscosity, 30 parts of simethicone with 0.3 Pa.s viscosity and 120 parts of nano active calcium carbonate for 90 minutes at the temperature of 110 ℃ and under the vacuum degree of-0.095 MPa, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 5 parts of methyltrimethoxysilane, 1 part of gamma-aminopropyl triethoxysilane, 7 parts of self-made self-healing agent, 1 part of ferric chloride, 1 part of zinc chloride and 4 parts of diisobutyl di (acetoacetate) titanate, and mixing and reacting for 90 minutes under the vacuum degree of-0.095 MPa and the stirring speed of 300rpm to obtain the self-healing silicone sealant.
Example 2
64 parts of HSi (OCH) 2 CH 3 ) 3 Added into a reaction kettle filled with 60 parts of dimethylbenzene and stirred to obtain a mixed solution. 50 parts of H 2 NCOCH＝CHCH 2 Adding COOH and 0.0020 part of chloroplatinic acid into the mixed solution, heating to 90 ℃, reacting for 60min, and continuously heating to 100 ℃ for reacting for 4 hours; finally, the temperature in the reaction kettle is increased to 130 ℃ and vacuumized to-0.099 MPa to remove the solvent for 100min, thus obtaining the self-healing agent.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with 100 Pa.s viscosity, 50 parts of simethicone with 0.2 Pa.s viscosity and 90 parts of heavy calcium carbonate for 60 minutes at the temperature of 150 ℃ and the vacuum degree of-0.099 MPa, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 7 parts of propyltrimethoxysilane, 3 parts of N- (beta-aminoethyl) -gamma-aminopropyl triethoxysilane, 10 parts of self-made self-healing agent, 3 parts of ferric chloride, 2 parts of zinc chloride and 6 parts of diisopropyl di (acetoacetate) titanate, and mixing and reacting for 120min under the vacuum degree of-0.099 MPa and the stirring speed of 50rpm to obtain the self-healing silicone sealant.
Example 3
25 parts of HSi (CH) 3 )(OCH 3 ) 2 Adding the mixture into a reaction kettle filled with 50 parts of petroleum ether, and stirring to obtain a mixed solution. 30 parts of H 2 NCOCH＝CHCH 2 Adding COOH and 0.0015 part of chloroplatinic acid into the mixed solution, heating to 80 ℃, reacting for 100min, and continuously heating to 90 ℃ for reacting for 5 hours; finally, the temperature in the reaction kettle is increased to 120 ℃ and vacuumized to-0.095 MPa to remove the solvent for 120min, thus obtaining the self-healing agent.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with the viscosity of 5 Pa.s, 3 parts of simethicone with the viscosity of 0.5 Pa.s and 180 parts of silicon micropowder at the temperature of 80 ℃ and under the vacuum degree of-0.06 MPa for 180 minutes, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 3 parts of octyl trimethoxy silane, 2 parts of gamma-glycidoxypropyl trimethoxy silane, 5 parts of self-made self-healing agent, 2 parts of ferric chloride, 3 parts of zinc chloride and 3 parts of dibutoxy bis (ethyl acetoacetate) titanate, and mixing and reacting for 40min under the vacuum degree of-0.06 MPa and the stirring speed of 800rpm to obtain the self-healing silicone sealant.
Example 4
64 parts of HSi (CH) 2 CH 3 )(OCH 2 CH 3 ) 2 Added into a reaction kettle containing 40 parts of toluene and stirred to obtain a mixed solution. 50 parts of H 2 NCOCH=CHCOOH and 0.0018 parts of chloroplatinic acid are added into the mixed solution, the temperature is raised to 75 ℃, the reaction is carried out for 130min, and the temperature is continuously raised to 85 ℃ for continuous reaction for 5.5 hours; finally, the temperature in the reaction kettle is increased to 125 ℃ and vacuumized to-0.099 MPa to remove the solvent for 110min, thus obtaining the self-healing agent.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with the viscosity of 20 Pa.s, 20 parts of simethicone with the viscosity of 0.4 Pa.s and 130 parts of diatomite at the temperature of 100 ℃ under the condition that the vacuum degree is minus 0.09MPa for 120 minutes, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 4 parts of phenyl trimethoxy silane, 1.5 parts of 3-isocyanatopropyl trimethoxy silane, 8 parts of self-made self-healing agent, 1 part of ferric chloride, 3 parts of zinc chloride and 5 parts of tetraisopropyl titanate, and mixing and reacting for 60 minutes under the conditions of vacuum degree of-0.08 MPa and stirring speed of 500rpm to obtain the self-healing silicone sealant.
Example 5
29 parts of HSi (OCH) 2 CH 3 ) 3 Added into a reaction kettle containing 35 parts of toluene and stirred to obtain a mixed solution. 23 parts of H 2 NCOCH＝CHCH 2 Adding COOH and 0.0013 part of chloroplatinic acid into the mixed solution, heating to 85 ℃, reacting for 80min, and continuously heating to 95 ℃ for reacting for 4.5 hours; finally, the temperature in the reaction kettle is increased to 115 ℃ and vacuumized to-0.095 MPa to remove the solvent for 150min, thus obtaining the self-healing agent.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with the viscosity of 80 Pa.s, 30 parts of simethicone with the viscosity of 0.35 Pa.s and 100 parts of nano active calcium carbonate for 80 minutes at the temperature of 120 ℃ under the condition that the vacuum degree is-0.08 MPa, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 6 parts of methyltrimethoxysilane, 2 parts of gamma-mercaptopropyl trimethoxysilane, 9 parts of self-made self-healing agent, 3 parts of ferric chloride, 1 part of zinc chloride and 4 parts of tetrabutyl titanate, and mixing and reacting for 110min at the vacuum degree of-0.085 MPa and the stirring speed of 200rpm to obtain the self-healing silicone sealant.
Example 6
This example differs from example 1 in that no zinc chloride and no iron chloride were added.
32 parts of HSi (OCH) 3 ) 3 Added into a reaction kettle filled with 30 parts of toluene and stirred to obtain a mixed solution. 30 parts of H 2 NCOCH=CHCOOH and 0.0010 part of chloroplatinic acid are added into the mixed solution, the temperature is raised to 65 ℃, the reaction is carried out for 180min, and the temperature is continuously raised to 75 ℃ for continuous reaction for 6 hours; finally, the temperature in the reaction kettle is increased to 110 ℃, and the reaction kettle is vacuumized to-0.090 MPa to remove the solvent for 180min, so as to obtain the self-healing agent.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with 50 Pa.s viscosity, 30 parts of simethicone with 0.3 Pa.s viscosity and 120 parts of nano active calcium carbonate for 90 minutes at the temperature of 110 ℃ and under the vacuum degree of-0.095 MPa, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 5 parts of methyltrimethoxysilane, 1 part of gamma-aminopropyl triethoxysilane, 7 parts of self-made self-healing agent and 4 parts of diisobutyl di (acetoacetate) titanate, and mixing and reacting for 90min at the stirring speed of 300rpm under the vacuum degree of-0.095 MPa to obtain the self-healing silicone sealant.
Example 7
This example differs from example 1 in that no zinc chloride was added and the amount of ferric chloride was 2 parts.
32 parts of HSi (OCH) 3 ) 3 Added into a reaction kettle filled with 30 parts of toluene and stirred to obtain a mixed solution. 30 parts of H 2 NCOCH=CHCOOH and 0.0010 part of chloroplatinic acid are added into the mixed solution, the temperature is raised to 65 ℃, the reaction is carried out for 180min, and the temperature is continuously raised to 75 ℃ for continuous reaction for 6 hours; finally, the temperature in the reaction kettle is increased to 110 ℃, and the reaction kettle is vacuumized to-0.090 MPa to remove the solvent for 180min, so as to obtain the self-healing agent.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with 50 Pa.s viscosity, 30 parts of simethicone with 0.3 Pa.s viscosity and 120 parts of nano active calcium carbonate for 90 minutes at the temperature of 110 ℃ and under the vacuum degree of-0.095 MPa, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 5 parts of methyltrimethoxysilane, 1 part of gamma-aminopropyl triethoxysilane, 7 parts of self-made self-healing agent, 2 parts of ferric chloride and 4 parts of diisobutyl di (acetoacetate) titanate, and mixing and reacting for 90min at the stirring speed of 300rpm under the vacuum degree of-0.095 MPa to obtain the self-healing silicone sealant.
Example 8
This example differs from example 1 in that no ferric chloride was added and zinc chloride was used in an amount of 2 parts.
32 parts of HSi (OCH) 3 ) 3 Added into a reaction kettle filled with 30 parts of toluene and stirred to obtain a mixed solution. 30 parts of H 2 NCOCH=CHCOOH and 0.0010 part of chloroplatinic acid are added into the mixed solution, the temperature is raised to 65 ℃, the reaction is carried out for 180min, and the temperature is continuously raised to 75 ℃ for continuous reaction for 6 hours; finally, the temperature in the reaction kettle is increased to 110 ℃, and the reaction kettle is vacuumized to-0.090 MPa to remove the solvent for 180min, so as to obtain the self-healing agent.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with 50 Pa.s viscosity, 30 parts of simethicone with 0.3 Pa.s viscosity and 120 parts of nano active calcium carbonate for 90 minutes at the temperature of 110 ℃ and under the vacuum degree of-0.095 MPa, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 5 parts of methyltrimethoxysilane, 1 part of gamma-aminopropyl triethoxysilane, 7 parts of self-made self-healing agent, 2 parts of zinc chloride and 4 parts of diisobutyl di (acetoacetate) titanate, and mixing and reacting for 90min at the stirring speed of 300rpm under the vacuum degree of-0.095 MPa to obtain the self-healing silicone sealant.
Comparative example 1
This comparative example differs from example 1 in that no self-healing agent, ferric chloride and zinc chloride were added.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with 50 Pa.s viscosity, 30 parts of simethicone with 0.3 Pa.s viscosity and 120 parts of nano active calcium carbonate for 90 minutes at the temperature of 110 ℃ and under the vacuum degree of-0.095 MPa, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 5 parts of methyltrimethoxysilane, 1 part of gamma-aminopropyl triethoxysilane and 4 parts of diisobutyl di (acetoacetate) titanate, and mixing and reacting for 90 minutes at the stirring speed of 300rpm under the vacuum degree of-0.095 MPa to obtain the self-healing silicone sealant.
Comparative example 2
This comparative example differs from example 1 in that no self-healing agent was added.
Dehydrating and blending 100 parts of alpha, omega-dihydroxypolydimethylsiloxane with 50 Pa.s viscosity, 30 parts of simethicone with 0.3 Pa.s viscosity and 120 parts of nano active calcium carbonate for 90 minutes at the temperature of 110 ℃ and under the vacuum degree of-0.095 MPa, and cooling to obtain a base material; and (3) putting the base material into a planetary mixer, adding 5 parts of methyltrimethoxysilane, 1 part of gamma-aminopropyl triethoxysilane, 1 part of ferric chloride, 1 part of zinc chloride and 4 parts of diisobutyl di (acetoacetate) titanate, and mixing and reacting for 90min at a vacuum degree of-0.095 MPa and a stirring speed of 300rpm to obtain the self-healing silicone sealant.
The silicone sealants prepared in examples 1 to 8 and comparative examples 1 to 2 were subjected to the performance test shown in table 1, and the performance test method of the samples in table 1 was as follows:
1. the tensile bond strength and the elongation at break are detected according to GB/T13477 "determination of the tensile bond of the 8 th part of the building sealing material";
2. self-healing test: and (3) re-splicing the fracture parts of the samples subjected to the tensile adhesion test, and re-carrying out the tensile adhesion test after standing for 3 days at normal temperature.
As shown in table 1, comparative examples 1 and 2 did not add self-made self-healing agent, silicone sealants did not have self-healing properties, and samples exhibiting fracture splice did not have substantially tensile bond strength. In examples 1-8, when 5-10 parts of self-made self-healing agent is added into silicone sealant, the samples after fracture splicing recover part of the tensile bonding strength; also, the tensile bond strength at 28 days of standard condition curing was significantly higher than that of comparative examples 1 and 2. The self-healing agent prepared by the invention can endow the silicone sealant with good self-healing effect, and can obviously improve the mechanical property of the silicone sealant. The self-healing agent prepared by the method can participate in the crosslinking reaction of the silicone sealant, and the structure contains amide groups, so that when the fracture of a silicone sealant sample is spliced, soft silicone rubber molecular chains generate chain segment movement, and the amide groups on the molecular chains form dynamic crosslinking bonds through the hydrogen bonding effect, so that the self-healing of the silicone sealant is realized; and the self-healing agent can play a role of a cross-linking agent, and after a cross-linked network is formed, amide groups among molecular chains can form dynamic cross-linking bonds through hydrogen bonding, so that the interaction among the molecular chains can be further enhanced, and the mechanical property of the silicone sealant is improved.
As can be seen from comparison of examples 1 and examples 6-8, the mechanical properties and self-healing properties of the silicone sealant can be further improved by adding the metal salt based on the self-made self-healing agent, because the metal ions can form dynamic coordination bonds with carboxyl groups in the self-made self-healing agent, thereby further enhancing the interaction between molecular chains. And compared with the method that only self-made self-healing agent and one metal salt are added, the method has the advantages that two metal salts of ferric salt and zinc salt are added to be matched with each other on the basis of adding the self-made self-healing agent, so that the mechanical property and the self-healing property of the silicone sealant can be further improved, and the ferric salt and the zinc salt can be used for synergistically improving the mechanical property and the self-healing property of the silicone sealant.
TABLE 1
The technical features of the above-described embodiments may be arbitrarily combined, and all possible combinations of the technical features in the above-described embodiments are not described for brevity of description, however, as long as there is no contradiction between the combinations of the technical features, they should be considered as the scope of the description.
The above examples illustrate only a few embodiments of the invention, which are described in detail and are not to be construed as limiting the scope of the invention. It should be noted that it will be apparent to those skilled in the art that several variations and modifications can be made without departing from the spirit of the invention, which are all within the scope of the invention. Accordingly, the scope of protection of the present invention is to be determined by the appended claims.
Claims (16)
1. The self-healing silicone sealant is characterized by comprising a self-healing agent and metal salt;
the self-healing agent is obtained by reacting hydrogen-containing silane and an amide olefine acid compound under the action of a catalyst;
the hydrogen-containingThe silane has the structural formula HSi (R 1 )(OR 2 ) 2 Wherein R is 1 Selected from: c (C) 1 -C 6 Alkoxy, C 1 -C 6 Alkyl, R 2 Selected from: c (C) 1 -C 6 An alkyl group;
the structural formula of the amide alkenoic acid compound is H 2 NCOCH＝CH(CH 2 ) m COOH, wherein m is selected from: 0. 1, 2, 3, 4;
the metal salt consists of ferric salt and zinc salt;
the mass ratio of the hydrogen-containing silane to the amide acrylic compound is 1:0.7-1.3;
the preparation method of the self-healing agent comprises the following steps: adding the hydrogen-containing silane, the amide olefine acid compound and the catalyst into an organic solvent, heating to 60-90 ℃, reacting for 60-210 min, then heating to 70-100 ℃ and continuously reacting for 4-7 hours, finally heating the temperature in a reaction kettle to 110-130 ℃ and vacuumizing to remove the solvent, thus obtaining the self-healing agent.
2. The self-healing silicone sealant according to claim 1, wherein the raw materials comprise, in parts by weight:
3. the self-healing silicone sealant according to claim 1, wherein R 1 Selected from: -OCH 3 、-OCH 2 CH 3 、-CH 3 、-CH 2 CH 3 ，R 2 is-CH 3 or-CH 2 CH 3 The method comprises the steps of carrying out a first treatment on the surface of the And/or the number of the groups of groups,
m is 0 or 1.
4. A self-healing silicone sealant according to claim 3, wherein the hydrogen-containing silane is HSi (OCH) 3 ) 3 The amide olefine acid compoundThe substance is H 2 Ncoch=chcooh; and/or the number of the groups of groups,
the hydrogen-containing silane is HSi (OCH) 2 CH 3 ) 3 The amide alkenoic acid compound is H 2 NCOCH＝CHCH 2 COOH。
5. A self-healing silicone sealant according to claim 3, wherein the hydrogen-containing silane is HSi (OCH) 3 ) 3 The amide alkenoic acid compound is H 2 NCOCH＝CHCOOH，HSi(OCH 3 ) 3 And H 2 Ncoch=chcooh at a mass ratio of 1:0.8 to 1.
6. A self-healing silicone sealant according to claim 3, wherein the hydrogen-containing silane is HSi (OCH) 2 CH 3 ) 3 The amide alkenoic acid compound is H 2 NCOCH＝CHCH 2 COOH，HSi(OCH 2 CH 3 ) 3 And H 2 NCOCH＝CHCH 2 The mass ratio of COOH is 1:0.7 to 0.9.
7. The self-healing silicone sealant according to claim 1, wherein the catalyst is chloroplatinic acid.
8. The self-healing silicone sealant according to claim 7, wherein the mass ratio of the hydrogen-containing silane to the catalyst is 1:0.002% -0.008%.
9. The self-healing silicone sealant according to any one of claims 1 to 8, wherein the organic solvent is selected from at least one of toluene, xylene, and petroleum ether.
10. The self-healing silicone sealant according to any one of claims 1 to 8, wherein the mass ratio of the hydrogen-containing silane to the organic solvent is 1:0.6-2.
11. The self-healing silicone sealant according to any one of claims 1 to 8, wherein the time for evacuating and removing the solvent is 100min to 210min, and the degree of vacuum is-0.090 MPa to-0.099 MPa.
12. The self-healing silicone sealant according to any one of claims 1 to 8, wherein the metal salt consists of ferric chloride and zinc chloride.
13. The self-healing silicone sealant according to claim 12, wherein the metal salt consists of the following components in mass ratio of 1:0.2-3 of ferric chloride and zinc chloride.
14. A self-healing silicone sealant according to claim 2, wherein the α, ω -dihydroxy polydimethylsiloxane has a viscosity of 5 Pa-s to 100 Pa-s at 25 ℃; and/or the number of the groups of groups,
the viscosity of the simethicone at 25 ℃ is 0.2 Pa.s-0.5 Pa.s; and/or the number of the groups of groups,
the inorganic filler is at least one selected from nano active calcium carbonate, heavy calcium carbonate, silicon micropowder and diatomite; and/or the number of the groups of groups,
the cross-linking agent is at least one selected from methyltrimethoxysilane, propyltrimethoxysilane, octyltrimethoxysilane and phenyltrimethoxysilane; and/or the number of the groups of groups,
the coupling agent is at least one of gamma-aminopropyl trialkoxysilane, N- (beta-aminoethyl) -gamma-aminopropyl trialkoxysilane, gamma-glycidol ether oxypropyl trialkoxysilane, gamma-mercaptopropyl trimethoxysilane and 3-isocyanatopropyl trialkoxysilane; and/or the number of the groups of groups,
the catalyst is at least one of tetraisopropyl titanate, tetrabutyl titanate, diisopropyl di (ethyl acetoacetate) titanate, dibutoxybis (ethyl acetoacetate) titanate and diisobutyl di (ethyl acetoacetate) titanate.
15. The self-healing silicone sealant according to claim 1, wherein the raw materials comprise, in parts by weight:
the viscosity of the alpha, omega-dihydroxy polydimethylsiloxane is 50 Pa.s-90 Pa.s at 25 ℃;
the viscosity of the simethicone at 25 ℃ is 0.2 Pa.s-0.4 Pa.s;
the inorganic filler is nano active calcium carbonate;
the cross-linking agent is methyltrimethoxysilane;
the coupling agent is gamma-aminopropyl trialkoxy silane and/or gamma-mercaptopropyl trimethoxy silane.
16. A method for preparing the self-healing silicone sealant according to claim 2 or 15, comprising the steps of:
dehydrating and blending the alpha, omega-dihydroxyl polysiloxane, the dimethyl silicone oil and the inorganic filler for 60-180 minutes under the conditions that the temperature is 80-150 ℃ and the vacuum degree is minus 0.06MPa to minus 0.099MPa, and cooling to obtain a base material; and (3) putting the base material into a stirrer, adding the cross-linking agent, the coupling agent, the self-healing agent, the metal salt and the catalyst, and mixing and reacting for 40-120 min under the condition that the vacuum degree is minus 0.06MPa to minus 0.099MPa and the stirring speed is 50-800 rpm, thus obtaining the self-healing silicone sealant.