CN1152505A - Spoke type light alloy wheel for motorcycle and production technology thereof - Google Patents
Spoke type light alloy wheel for motorcycle and production technology thereof Download PDFInfo
- Publication number
- CN1152505A CN1152505A CN 96117726 CN96117726A CN1152505A CN 1152505 A CN1152505 A CN 1152505A CN 96117726 CN96117726 CN 96117726 CN 96117726 A CN96117726 A CN 96117726A CN 1152505 A CN1152505 A CN 1152505A
- Authority
- CN
- China
- Prior art keywords
- wheel rim
- crude product
- water
- surplus
- wheel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The light alloy wheel is composed of aluminium alloy rim, tyre, hub and a group of steel spokes. The composition of aluminium alloy consists of 0.20-0.60% of copper, 0.45-0.90% of magnesium, 0.15-0.35% of manganese or chromium, 0.50-1.2% of silicon and the rest aluminium. Through the processes of shaping, sawing down coiled rim, welding, heat treatment, hole drilling, grinding and surface treating, the golden, blue, red, and bronze-coloured rims are made up. The invented wheel features good anti-corrosion property, strong dampening property, beautiful exterior decoration and moderate price.
Description
The invention belongs to a kind of bar type wheel, relate to a kind of spoke type light alloy wheel for motorcycle, be applicable to and improve existing motor bike bar type wheel.
The wheel of motor bike adapted can be divided into two kinds of integral type and spoke types from the assembling form.Existing spoke type bike wheel is installed in the tire on the wheel rim generally by the steel wheel rim, wheel hub, and one group of (being generally the 30-40 root) the steel spoke that is connected between wheel rim and the wheel hub is formed; Owing to adopt the steel wheel rim, its production and processing technology is complicated, is formed with environmental pollution in the production process, the rim surface easy-to-rust, and service life is short, and decorative appearance is poor, and body is heavier, and result of use is relatively poor.
The present invention's purpose is intended to overcome above-mentioned deficiency of the prior art, provides a kind of decorative appearance, corrosion to be better than the steel wheel rim greatly, simple spoke type light alloy wheel for motorcycle of production technology and production technology thereof.
Content of the present invention is: a kind of spoke type light alloy wheel for motorcycle, mainly by wheel rim (1), be installed in tire (2), the wheel hub (3) on the wheel rim (1), the one group of steel spoke (4) that is connected between wheel hub (3) and the wheel rim (1) is formed, its feature part is: the material of described wheel rim (1) is that aluminium is formed by (weight %) 0.20-0.60% copper, 0.45-0.90% magnesium, 0.15-0.35% manganese or chromium, 0.50-1.2% silicon, surplus; Promptly adopt the described LD of GB3190-82 " chemical analysis of aluminium and aluminum alloy converted products ", GBn222-84 " aluminium and aluminum alloy heat extrudate "
2Alloy material (seeing " material of construction application manual " the 3rd volume, China Standard Press, July in 1989 the 1st edition, 176-184 page or leaf).
Content of the present invention also comprises a kind of production technology of spoke type light alloy wheel for motorcycle, mainly by the wheel rim production technology, tire (2) production technology, wheel hub (3) production technology, spoke (4) production technology, each detail assembly becomes wheel technology to form, described wheel rim (1) production technology is checked by the section bar blank, the blaze note, carve anti-slop serrations, moulding, sawed-off, welding (argon arc welding), the roughening thorn, grind, T6 quenches, the school circle is flat, punching, T4 handles, grind, surface treatment, check, packing, the warehouse-in operation constitutes, and its feature part is that described surface treatment procedure is made up of the following step:
A, mechanical buffing are about to wheel rim (1) crude product and handle through mechanical buffing;
B, degreaser electrolytic: wheel rim (1) crude product after step a handles being placed to contain 7-15 (g/l, back with) trisodium phosphate, 8-15 natrium carbonate, 0.3 interfacial agent, surplus be in the aqueous system of water, is that 60-70 ℃, electric current are 3-4A/dm in temperature
2Soak 3-5min under the condition;
C, taking-up are with cleaning washing 2 times;
D, pickling: wheel rim (1) crude product after handling through step c is placed the aqueous system that contains 100-250g/l sulfuric acid, soaking and washing 3-6min;
E, taking-up are cleaned with clean water;
F, chemical polish: wheel rim (1) crude product after handling through step e is placed in the solution that contains 77% (weight %, the back together) phosphoric acid, 15% sulfuric acid, 6% nitric acid, 0.5% Roman vitriol, 0.4% boric acid, under 100-105 ℃ of temperature, soaked 1-3 minute;
G, taking-up are cleaned with clean water;
H, anodization: wheel rim (1) crude product after step g is handled is placed the aqueous system that contains 150-250g/l sulfuric acid, is that 15-25 ℃, electric current are 1-1.5A/dm in temperature
2, voltage is under the 12-20V condition, handles 40-60min;
I, taking-up are cleaned with clean water;
J, painted: adopt the painted or electrolytic coloring mode of organic matter, make wheel rim (1) crude product surface become golden yellow, blueness, redness or bronze-colored;
K, painted after, clean with clean water;
L, hot water sealing: wheel rim (1) crude product is placed pure water more than or equal to 90 ℃, under the PH=5.5-6.5 condition, soak 20min at least;
M, use hot water washing;
N, oven dry;
O, with wheel rim (1) crude product top finishing finish varnish;
P, oven dry promptly make wheel rim (1) product.
In the content of the present invention, described employing organic matter coloring mode makes wheel rim (1) crude product surface become golden yellow, be will wheel rim (1) crude product after step I is handled to place to contain 0.5 (g/l, afterwards together) alizarin yellow, 0.3 sodium alizarinsulfonate, surplus are in the solution of water, in temperature is under 75 ℃ of-85 ℃ of conditions, soaks 1-3min; Or place contain the 0.5g/l reactive brilliant orange, surplus is the solution of water, under 70-80 ℃ of temperature, soaks 5-15min; Or place and contain that the 0.035g/l cubozols is golden yellow, 0.1 cubozols is orange, surplus is in the solution of water, under room temperature, PH=4.5-5 condition, soaks 1-3min;
In the content of the present invention, described employing organic matter coloring mode makes wheel rim (1) crude product surface become blueness, be wheel rim (1) crude product after handling through step I is placed contain the 3.5g/l direct fast blue, surplus is the solution of water, soaks 15-20mim under room temperature; Or place contain 5g/l patience anthraquinone blue, surplus is the solution of water, soaks down 5-20min at 50-60 ℃; Or place contain the 2-5g/l direct light turquoise blue, surplus is the solution of water, under 60-70 ℃, PH=4.5-5 condition, soaks 1-5min; Or place contain the 5g/l reactive brilliant bule, surplus is the solution of water, under room temperature, PH=4.5-5.5 condition, soaks 1-5min; Or to place 2-5g/l acid blue, surplus be the solution of water, 70-80 ℃ soak down 2-15min,
In the content of the present invention, described employing electrolytic coloring mode makes wheel rim (1) crude product surface become blueness, be wheel rim (1) crude product after handling through step I is placed contain the 2g/l potassium ferricyanide, surplus is the solution of water, under 13V voltage, soaks 1min.
In the content of the present invention, described employing electrolytic coloring mode makes wheel rim (1) crude product surface become redness, is wheel rim (1) crude product after handling through step I to be placed to contain 7g/l sulfuric acid, 20g/l Roman vitriol, surplus be the solution of water, under 13V voltage, soaks 1min.
In the content of the present invention, described employing electrolytic coloring mode makes wheel rim (1) crude product surface become golden yellow, be will wheel rim (1) crude product after step I is handled to place that to contain 5g/l sulfuric acid, 0.15g/l silver sulfate, surplus be the solution of water, under 8V voltage, soak 3min; Or place that to contain 7g/l sulfuric acid, 1.5g/l mineral chameleon, surplus be the solution of water, under 13V voltage, soak 2min; Or place that to contain 7g/l sulfuric acid, 1.5g/l sodium selenate, surplus be the solution of water, under 13V voltage, soak 10min; Or place that to contain 7g/l sulfuric acid, 1.5g/l llurate, surplus be the solution of water, under 13V voltage, soak 10min.
In the content of the present invention, described employing electrolytic coloring mode makes wheel rim (1) crude product surface become bronze-colored, be will wheel rim (1) crude product after step I is handled to place that to contain 25g/l boric acid, 40g/l nickelous sulfate, surplus be the solution of water, under 13V voltage, PH=4-4.5 condition, soak 5min; Or place that to contain 25g/l boric acid, 20g/l nickelous sulfate, 15g/l ammonium sulphate, surplus be the solution of water, under 20V voltage, soak 2min.
The present invention has following characteristics:
(1) spoke adopts the steel spoke in the wheel of the present invention, wheel rim adopts the moulding aluminium, make through PROCESS FOR TREATMENT such as volume circle, welding, heat treatment, punching, grinding, surface treatments, become the on all four wheel rim of steel wheel rim in assembly properties specification and the existing bar type wheel, and weight is about 65% of steel wheel rim, intensity and rigidity reach steel wheel rim level, and anti-corrosive properties is better than the steel wheel rim greatly, and production technology is simple than the steel wheel rim;
(2) wheel compatibility of the present invention the strong advantage of anti-corrosive properties vibration damping good and the spoke wheel wheel of integral type aluminium wheel, decorative appearance is good, the wheel rim color can be produced shades of colours such as golden yellow, blueness, look red be, bronze-colored according to market demand, production technology is simpler, make the existing practicality of motorcycle rim, have ornamentally again, also have protective effect, effectively prolong the service life of wheel rim attached to the color layers of rim surface;
(3) the present invention is widely applicable, can be used for all sizes such as 1.20 * 17,1.40 * 17,1.40 * 18,1.60 * 18,50 types that can assemble or change the outfit, 60 types, 70 types, 80 types, 90 types, 100 types, the former assembling bar type wheel of 125 types; The productive costs of wheel of the present invention is higher by 18% than steel wheel rim wheel, than whole aluminium wheel low 31%, price quality ratio is between whole aluminium wheel and spoke type steel wheel, easily promote, market is big, about 2,000 ten thousand of existing national motor bike recoverable amount, wherein the bar type wheel of steel wheel rim is no less than 1,500 ten thousand, if 1% motor bike adopts wheel of the present invention, then annual requirement is 300,000, by 10% profit, year can make a profit about 1,800,000 yuan.
Fig. 1 is a car wheel structure scheme drawing of the present invention;
Fig. 2 is wheel rim 1 structural representation among Fig. 1;
Fig. 3 is the section structure scheme drawing of Fig. 2.
Among the figure: 1-wheel rim, 2-tire, 3-wheel hub, 4-spoke, 5-bar mother.
Be embodiments of the invention below: referring to each accompanying drawing.
Embodiment 1:
A kind of spoke type light alloy wheel for motorcycle, mainly by wheel rim 1, be installed in one group of steel spoke 4 that tire 2 on the wheel rim 1, wheel hub 3, bar mother 5 by spoke 4 be connected between wheel hub 3 and the wheel rim 1 and form same prior art; The material of described wheel rim 1 is that aluminium is formed by (weight %) 0.2% bronze medal, 0.45% magnesium, 0.15% manganese or chromium, 0.50% silicon, surplus; Promptly adopt the described LD of GB3190-82 " chemical analysis of aluminium and aluminum alloy converted products ", GBn222-84 " aluminium and aluminum alloy heat extrudate "
2Alloy material (seeing " material of construction application manual ", the 3rd volume, China Standard Press, July in 1989 the 1st edition, 176-184 page or leaf).
The production technology of this spoke type light alloy wheel for motorcycle, mainly by wheel rim 1 production technology, tire 2 production technologies, wheel hub 3 production technologies, spoke 4 production technologies that contain bar mother 5, each detail assembly becomes wheel technology to form, described wheel rim 1 production technology is checked by the section bar blank, the blaze note, carve anti-slop serrations, moulding, sawed-off, welding (argon arc welding), the roughening thorn, grind with grinder, carrying out T6 with well formula hardening furnace quenches, the school circle is flat, punching, T4 heat treatment, grind, surface treatment, check, packing, the warehouse-in operation constitutes, and described surface treatment procedure is made up of the following step:
A, mechanical buffing are about to wheel rim 1 crude product and handle through mechanical buffing;
B, degreaser electrolytic: wheel rim 1 crude product after step a handles placed containing 7 (g/l, back with) trisodium phosphate, 8 natrium carbonates, 0.3 interfacial agent, surplus is in the aqueous system of water, is that 60-70 ℃, electric current are 3-4A/dm in temperature
2Soak 3-5min under the condition;
C, taking-up are with cleaning washing 2 times;
D, pickling: wheel rim 1 crude product after handling through step c is placed the aqueous system that contains 100-250g/l sulfuric acid, soaking and washing 3-6min;
E, taking-up are cleaned with clean water;
F, chemical polish: wheel rim 1 crude product after handling through step e is placed in the solution that contains 77% (weight %, the back together) phosphoric acid, 15% sulfuric acid, 6% nitric acid, 0.5% Roman vitriol, 0.4% boric acid, under 100-105 ℃ of temperature, soaked 1-3 minute;
G takes out, and cleans with clean water;
H, anodization: wheel rim 1 crude product after step g is handled is placed the aqueous system that contains 150-250g/l sulfuric acid, is that 15-25 ℃, electric current are 1-1.5A/dm in temperature
2, voltage is under the 12-20V condition, handles 40-60min;
I, taking-up are cleaned with clean water;
J, painted: adopt the organic matter coloring mode, make wheel rim 1 crude product surface become golden yellow, that is: wheel rim 1 crude product is placed that to contain 0.5g/l alizarin yellow, 0.3g/l sodium alizarinsulfonate, surplus be the solution of water, under 75 ℃ of-85 ℃ of temperature, soak 1-3min;
K, painted after, take out and to clean with clean water;
L, hot water sealing: wheel rim 1 crude product is placed pure water more than or equal to 90 ℃, under the PH=5.5-6.5 condition, soak 20min at least;
M, use hot water washing;
N, oven dry;
O, with wheel rim 1 crude product top finishing finish varnish;
P, oven dry promptly make product.
Embodiment 2:
A kind of spoke type light alloy wheel for motorcycle, main by wheel rim 1, be installed in tire 2, the wheel hub 3 on the wheel rim 1, the one group of steel spoke 4 that is connected between wheel hub 3 and the wheel rim 1 is formed same prior art; Described wheel rim 1 material is that aluminium is formed by (weight %) 0.60% bronze medal, 0.90% magnesium, 0.35% manganese or chromium, 1.2% silicon, surplus; Promptly adopt the described LD of GB3190-82 " chemical analysis of aluminium and aluminum alloy converted products ", GBn222-84 " aluminium and aluminum alloy heat extrudate "
2Alloy material (seeing " material of construction application manual " the 3rd volume, China Standard Press, July in 1989 the 1st edition, 176-184 page or leaf).
The production technology of this spoke type light alloy wheel for motorcycle, mainly by: wheel rim 1 production technology, tire 2 production technologies, wheel hub 3 production technologies, spoke 4 production technologies, each detail assembly become wheel technology to form, described wheel rim 1 production technology by section bar blank check, blaze note, carve that anti-slop serrations, moulding, sawed-off, welding (argon arc welding), roughening thorn, grinding, T6 quench, the school circle is flat, punching, T4 heat treatment, grinding, surface treatment, check, packing, warehouse-in operation constitute; Described surface treatment procedure is made up of the following step:
A, mechanical buffing are about to wheel rim 1 crude product and handle through mechanical buffing;
B, degreaser electrolytic: wheel rim 1 crude product after step a handles placed containing 15 (g/l, back with) trisodium phosphate, 15 natrium carbonates, 0.3 interfacial agent, surplus is in the aqueous system of water, is that 60-70 ℃, electric current are 3-4A/dm in temperature
2Soak 3-5min under the condition;
C, taking-up are cleaned 2 times with clean water;
D, pickling: wheel rim 1 crude product after handling through step c is placed the aqueous system that contains 100-250g/l sulfuric acid, soaking and washing 3-6min;
E, taking-up are cleaned with clean water;
F, chemical polish: wheel rim 1 crude product after handling through step e is placed in the solution that contains 77% (weight %, the back together) phosphoric acid, 15% sulfuric acid, 6% nitric acid, 0.5% Roman vitriol, 0.4% boric acid, under 100-105 ℃ of temperature, soaked 1-3 minute;
G takes out, and cleans with clean water;
H, anodization: wheel rim 1 crude product after step g is handled is placed the aqueous system that contains 150-250g/l sulfuric acid, is that 15-25 ℃, electric current are 1-1.5A/dm in temperature
2, voltage is under the 12-20V condition, handles 40-60min;
I, taking-up are cleaned with clean water;
J, painted: adopt the electrolytic coloring mode, make wheel rim 1 crude product surface become blueness; That is: wheel rim 1 crude product is placed contain the 2g/l potassium ferricyanide, surplus is the solution of water, under 13V voltage, soaks 1min;
K, painted after, take out and to clean with clean water;
L, hot water sealing: wheel rim 1 crude product is placed pure water more than or equal to 90 ℃, under the PH=5.5-6.5 condition, soak 20min at least;
M, use hot water washing;
N, oven dry;
O, with wheel rim 1 crude product top finishing finish varnish;
P, oven dry promptly obtain product.
Embodiment 3:
A kind of spoke type light alloy wheel for motorcycle, main by wheel rim 1, be installed in tire 2, the wheel hub 3 on the wheel rim 1, the one group of steel spoke 4 that is connected between wheel hub 3 and the wheel rim 1 is formed same prior art; The material of described wheel rim 1 is that aluminium is formed by (weight %) 0.40% bronze medal, 0.60% magnesium, 0.25% manganese or chromium, 0.80% silicon, surplus; Promptly adopt the described LD of GB3190-82 " chemical analysis of aluminium and aluminum alloy converted products ", GBn222-84 " aluminium and aluminum alloy heat extrudate "
2Alloy material (seeing " material of construction application manual ", the 3rd volume, China Standard Press, July in 1989 the 1st edition, 176-184 page or leaf).
The production technology of this spoke type light alloy wheel for motorcycle, mainly by: wheel rim 1 production technology, tire 2 production technologies, wheel hub 3 production technologies, spoke 4 production technologies, each detail assembly become wheel technology to form, described wheel rim 1 production technology by section bar blank check, blaze note, carve that anti-slop serrations, moulding, sawed-off, welding (argon arc welding), roughening thorn, grinding, T6 quench, the school circle is flat, punching, T4 heat treatment, grinding, surface treatment, check, packing, warehouse-in operation constitute; Described surface treatment procedure is made up of the following step:
A, mechanical buffing are about to wheel rim 1 crude product and handle through mechanical buffing;
B, degreaser electrolytic: wheel rim 1 crude product after step a handles placed containing 10 (g/l, back with) trisodium phosphate, 12 natrium carbonates, 0.3 interfacial agent, surplus is in the aqueous system of water, is that 60-70 ℃, electric current are 3-4A/dm in temperature
2Soak 3-5min under the condition;
C, taking-up are with cleaning washing 2 times;
D, pickling: wheel rim 1 crude product after handling through step c is placed the aqueous system that contains 100-250g/l sulfuric acid, soaking and washing 3-6min;
E, taking-up are cleaned with clean water;
F, chemical polish: wheel rim 1 crude product after handling through step e is placed in the solution that contains 77% (weight %, the back together) phosphoric acid, 15% sulfuric acid, 6% nitric acid, 0.5% Roman vitriol, 0.4% boric acid, under 100-105 ℃ of temperature, soaked 1-3 minute;
G, taking-up are cleaned with clean water;
H, anodization: wheel rim 1 crude product after step g is handled is placed the aqueous system that contains 150-250g/l sulfuric acid, is that 15-25 ℃, electric current are 1-1.5A/dm in temperature
2, voltage is under the 12-20V condition, handles 40-60min;
I, taking-up are cleaned with clean water;
J, painted: adopt the electrolytic coloring mode, make wheel rim 1 crude product surface become redness; That is: wheel rim 1 crude product is placed to contain 7g/l sulfuric acid, 20g/l Roman vitriol, surplus be the solution of water, under 13V voltage, soak 1min;
K, painted after, clean with clean water;
L, hot water sealing: wheel rim 1 crude product is placed pure water more than or equal to 90 ℃, under the PH=5.5-6.5 condition, soak 20min at least;
M, use hot water washing;
N, oven dry;
O, with wheel rim 1 crude product top finishing finish varnish;
P, oven dry promptly get product.
The invention is not restricted to the foregoing description, content of the present invention is described all can be implemented.
Claims (8)
1, a kind of spoke type light alloy wheel for motorcycle, mainly by wheel rim (1), be installed in tire (2), the wheel hub (3) on the wheel rim (1), the one group of steel spoke (4) that is connected between wheel hub (3) and the wheel rim (1) is formed, it is characterized in that: the material of described wheel rim (1) is that aluminium is formed by (weight %) 0.20-0.6% copper, 0.45-0.90% magnesium, 0.15-0.35% manganese or chromium, 0.50-1.2% silicon, surplus.
2, a kind of production technology of spoke type light alloy wheel for motorcycle, mainly by: wheel rim (1) production technology, tire (2) production technology, wheel hub (3) production technology, spoke (4) production technology, each detail assembly become wheel technology to form, described wheel rim (1) production technology by section bar blank check, blaze note, carve that anti-slop serrations, moulding, sawed-off, welding, roughening thorn, grinding, T6 quench, the school circle is flat, punching, T4 heat treatment, grinding, surface treatment, check, packing, warehouse-in operation constitute, and it is characterized in that described surface treatment procedure is made up of the following step:
A, mechanical buffing are about to wheel rim (1) crude product and handle through mechanical buffing;
B, degreaser electrolytic: wheel rim (1) crude product after step a handles being placed to contain 7-15 (g/l, back with) trisodium phosphate, 8-15 natrium carbonate, 0.3 interfacial agent, surplus be in the aqueous system of water, is that 60-70 ℃, electric current are 3-4A/dm in temperature
2Soak 3-5min under the condition;
C, taking-up are with cleaning washing 2 times;
D, pickling: wheel rim (1) crude product after handling through step c is placed the aqueous system that contains 100-250g/l sulfuric acid, soaking and washing 3-6min;
E, taking-up are cleaned with clean water;
F, chemical polish: wheel rim (1) crude product after handling through step e is placed in the solution that contains 77% (weight %, the back together) phosphoric acid, 15% sulfuric acid, 6% nitric acid, 0.5% Roman vitriol, 0.4% boric acid, under 100-105 ℃ of temperature, soaked 1-3 minute;
G, taking-up are cleaned with clean water;
H, anodization: wheel rim (1) crude product after step g is handled is placed the aqueous system that contains 150-250g/l sulfuric acid, is that 15-25 ℃, electric current are 1-1.5A/dm in temperature
2, voltage is under the 12-20V condition, handles 40-60min;
I, taking-up are cleaned with clean water;
J, painted: adopt the painted or electrolytic coloring mode of organic matter, make wheel rim (1) crude product surface become golden yellow, blueness, redness or bronze-colored;
K, painted after, clean with clean water;
L, hot water sealing: wheel rim (1) crude product is placed pure water more than or equal to 90 ℃, under the PH=5.5-6.5 condition, soak 20min at least;
M, use hot water washing;
N, oven dry;
O, with wheel rim (1) crude product top finishing finish varnish;
P, oven dry promptly make product.
3, press the production technology of the described spoke type light alloy wheel for motorcycle of claim 2, it is characterized in that: described employing organic matter coloring mode makes wheel rim (1) crude product surface become golden yellow, be will wheel rim (1) crude product after step I is handled to place to contain 0.5 (g/l, alizarin yellow, 0.3 sodium alizarinsulfonate afterwards together), surplus is in the solution of water, in temperature is under 75 ℃ of-85 ℃ of conditions, soaks 1-3min; Or place contain the 0.5g/l reactive brilliant orange, surplus is the solution of water, under 70-80 ℃ of temperature, soaks 5-15min; Or place and contain that the 0.035g/l cubozols is golden yellow, 0.1 cubozols is orange, surplus is in the solution of water, under room temperature, PH=4.5-5 condition, soaks 1-3min.
4, press the production technology of the described spoke type light alloy wheel for motorcycle of claim 2, it is characterized in that: described employing organic matter coloring mode makes wheel rim (1) crude product surface become blueness, be will wheel rim (1) crude product after step I is handled place contain the 3.5g/l direct fast blue, surplus is the solution of water, soaks 15-20min under room temperature; Or place contain 5g/l patience anthraquinone blue, surplus is the solution of water, under 50-60 ℃, invade the bubble 5-20min; Or place contain the 2-5g/l direct light turquoise blue, surplus is the solution of water, under 60-70 ℃, PH=4.5-5 condition, soaks 1-5min; Or place contain the 5g/l reactive brilliant bule, surplus is the solution of water, under room temperature, PH=4.5-5.5 condition, soaks 1-5min; Or to place 2-5g/l acid blue, surplus be the solution of water, soaks 2-15min down at 70-80 ℃.
5, press the production technology of the described spoke type light alloy wheel for motorcycle of claim 2, it is characterized in that: described employing electrolytic coloring mode makes wheel rim (1) crude product surface become blueness, be will wheel rim (1) crude product after step I is handled place contain the 2g/l potassium ferricyanide, surplus is the solution of water, under 13V voltage, soak 1min.
6, press the production technology of the described spoke type light alloy wheel for motorcycle of claim 2, it is characterized in that: described employing electrolytic coloring mode makes wheel rim (1) crude product surface become redness, be will wheel rim (1) crude product after step I is handled to place that to contain 7g/l sulfuric acid, 20g/l Roman vitriol, surplus be the solution of water, under 13V voltage, soak 1min.
7, press the production technology of the described spoke type light alloy wheel for motorcycle of claim 2, it is characterized in that: described employing electrolytic coloring mode makes wheel rim (1) crude product surface become golden yellow, be will wheel rim (1) crude product after step I is handled to place that to contain 5g/l sulfuric acid, 0.15g/l silver sulfate, surplus be the solution of water, under 8V voltage, soak 3min; Or place that to contain 7g/l sulfuric acid, 1.5g/l mineral chameleon, surplus be the solution of water, under 13V voltage, soak 2min; Or place that to contain 7g/l sulfuric acid, 1.5g/l sodium selenate, surplus be the solution of water, under 13V voltage, soak 10min; Or place that to contain 7g/l sulfuric acid, 1.5g/l llurate, surplus be the solution of water, under 13V voltage, soak 10min.
8, press the production technology of the described spoke type light alloy wheel for motorcycle of claim 2, it is characterized in that: described employing electrolytic coloring mode makes wheel rim (1) crude product surface become bronze-colored, be will wheel rim (1) crude product after step I is handled to place that to contain 25g/l boric acid, 40g/l nickelous sulfate, surplus be the solution of water, under 13V voltage, PH=4-4.5 condition, soak 5min; Or place that to contain 25g/l boric acid, 20g/l nickelous sulfate, 15g/l ammonium sulphate, surplus be the solution of water, under 20V voltage, soak 2min.