CN114934343A - Anti-static and anti-corrosion safety belt and preparation process thereof - Google Patents
Anti-static and anti-corrosion safety belt and preparation process thereof Download PDFInfo
- Publication number
- CN114934343A CN114934343A CN202210632286.XA CN202210632286A CN114934343A CN 114934343 A CN114934343 A CN 114934343A CN 202210632286 A CN202210632286 A CN 202210632286A CN 114934343 A CN114934343 A CN 114934343A
- Authority
- CN
- China
- Prior art keywords
- safety belt
- static
- antistatic
- drying
- putting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of safety belts, in particular to an anti-static and anti-corrosion safety belt and a preparation process thereof. The safety belt with the functions of static electricity prevention and corrosion prevention is characterized by comprising the following raw materials in parts by weight: 20-30% of carbon fiber, 15-25% of chinlon, 15-20% of polyester fiber, 4-9% of flame retardant, 5-10% of antioxidant, 5-10% of antistatic agent, 2-7% of wear-resisting agent and 5-12% of light stabilizer, wherein the sum of the proportions of the components is 100%. Compared with the prior art, the formula of the safety belt is added with the anti-static component, and the preparation process of the safety belt is correspondingly improved, so that the safety belt is not easy to corrode in a wet environment and is not easy to be influenced by static in a dry environment, and the use safety of the safety belt is improved.
Description
Technical Field
The invention relates to the technical field of safety belts, in particular to an anti-static and anti-corrosion safety belt and a preparation process thereof.
Background
When the worker works high above the ground, the worker needs to use a safety belt. The safety belt has a complex use environment, may be corroded due to a wet environment, may also generate static electricity due to a dry environment, and the static electricity may cause accidents such as fire and explosion, so that certain potential safety hazards exist.
Disclosure of Invention
The invention provides the anti-static and anti-corrosion safety belt and the preparation process thereof, aiming at overcoming the defects of the prior art, the anti-static component is added in the formula of the safety belt, the preparation process of the safety belt is correspondingly improved, the safety belt is ensured not to be easily corroded in a wet environment and not to be easily influenced by static in a dry environment, and the use safety of the safety belt is improved.
In order to achieve the purpose, the anti-static and anti-corrosion safety belt is designed and is characterized by comprising the following raw materials in parts by weight: 20-30% of carbon fiber, 15-25% of chinlon, 15-20% of polyester fiber, 4-9% of flame retardant, 5-10% of antioxidant, 5-10% of antistatic agent, 2-7% of wear-resisting agent and 5-12% of light stabilizer, wherein the sum of the proportions of the components is 100%.
The antistatic agent is one or more of stearyl trimethyl ammonium chloride and dilauryl dimethyl ammonium chloride.
The antioxidant is one or more of hindered phenol antioxidant or phosphite antioxidant.
The light stabilizer is one or more of 2- (3 ' -tert-butyl-2 ' -hydroxy-5 ' -methylphenyl) -5-chloro-benzotriazole or 2 ', 4 ' -di-tert-butylphenyl-3, 5-di-tert-butyl-4-hydroxybenzoate.
The flame retardant is one or more of ammonium polyphosphate or tricresyl phosphate.
The wear-resisting agent is selected from one or more of silicone powder or polytetrafluoroethylene.
A preparation process of an antistatic and anticorrosive safety belt comprises the following steps:
s1, preprocessing: weighing the raw materials, carrying out melt processing and blending forming on the raw materials to prepare a blended yarn with the count of 20S as a warp yarn and a blended yarn with the count of 41S as a weft yarn;
s2, warping: warping the warp yarn in the step S1 on warping equipment with the linear speed of the warp yarn being 300-500 m/min;
s2, weaving: putting the warped warp yarns into a weaving machine, putting the weft yarns into a weft feeding device of the weaving machine, and weaving by the weaving machine to obtain a woven safety belt;
s3, cleaning: cleaning the safety belt obtained in the step S2, and placing the safety belt in a dryer for drying, wherein the drying temperature is 75-85 ℃, and the drying time is set to be 1-2 hours;
s4, antiseptic treatment: the safety belt obtained in the step S4 is pressed and dipped in the anti-corrosion coating for 20 to 40 minutes, and is dried after being cleaned by clear water, wherein the drying temperature is 70 to 90 ℃, and the drying time is 2 to 8 minutes;
s5, staining: dyeing the safety belt obtained in the step S4 into a required color through a dyeing process;
s6, drying: putting the dyed safety belt into a dryer for drying;
s7, static electricity removal: and (4) putting the dried safety belt into a static eliminator to remove static on the surface of the safety belt.
Compared with the prior art, the anti-static component is added in the formula of the safety belt, and the preparation process of the safety belt is correspondingly improved, so that the safety belt is not easy to corrode in a wet environment and is not easy to be influenced by static in a dry environment, and the use safety of the safety belt is improved.
Detailed Description
The first embodiment is as follows:
the embodiment is an antistatic and anticorrosive safety belt, which comprises the following raw materials in parts by weight: 30% of carbon fiber, 15% of chinlon, 20% of polyester fiber, 6% of flame retardant, 10% of antioxidant, 10% of antistatic agent, 4% of wear-resisting agent and 5% of light stabilizer.
The antistatic agent is stearyl trimethyl ammonium chloride. The antioxidant is phosphite ester antioxidant. The light stabilizer is 2- (3 '-tert-butyl-2' -hydroxy-5 '-methylphenyl) -5-chloro-benzotriazole or 2'. The flame retardant is ammonium polyphosphate. The wear-resisting agent is polytetrafluoroethylene.
The preparation process comprises the following steps:
s1, preprocessing: weighing the raw materials, carrying out melt processing and blending forming on the raw materials to prepare a blended yarn with the count of 20S as a warp yarn and a blended yarn with the count of 41S as a weft yarn;
s2, warping: warping the warp yarn in the step S1 on warping equipment with the linear speed of the warp yarn being 300-500 m/min;
s2, weaving: putting the warped warp yarns into a weaving machine, putting the weft yarns into a weft feeding device of the weaving machine, and weaving by the weaving machine to obtain a woven safety belt;
s3, cleaning: cleaning the safety belt obtained in the step S2, and placing the safety belt in a dryer for drying, wherein the drying temperature is 75-85 ℃, and the drying time is set to be 1-2 hours;
s4, antiseptic treatment: the safety belt obtained in the step S4 is pressed and dipped in the anti-corrosion coating for 20 to 40 minutes, and is dried after being cleaned by clear water, wherein the drying temperature is 70 to 90 ℃, and the drying time is 2 to 8 minutes;
s5, staining: dyeing the safety belt obtained in the step S4 into a required color through a dyeing process;
s6, drying: putting the dyed safety belt into a dryer for drying;
s7, static electricity removal: and (4) putting the dried safety belt into a static eliminator to remove static electricity on the surface of the safety belt.
The invention also adds the anti-static component in the formula of the safety belt, correspondingly improves the preparation process of the safety belt, ensures that the safety belt is not easy to corrode in a wet environment and is not easy to be influenced by static in a dry environment, and improves the use safety of the safety belt.
Claims (7)
1. The safety belt with the functions of static electricity prevention and corrosion prevention is characterized by comprising the following raw materials in parts by weight: 20-30% of carbon fiber, 15-25% of chinlon, 15-20% of polyester fiber, 4-9% of flame retardant, 5-10% of antioxidant, 5-10% of antistatic agent, 2-7% of wear-resisting agent and 5-12% of light stabilizer, wherein the sum of the proportions of the components is 100%.
2. The safety belt with antistatic and anticorrosion functions as claimed in claim 1, wherein: the antistatic agent is one or more of stearyl trimethyl ammonium chloride and dilauryl dimethyl ammonium chloride.
3. The safety belt with antistatic and anticorrosion functions as claimed in claim 1, wherein: the antioxidant is one or more of hindered phenol antioxidant or phosphite antioxidant.
4. The safety belt with the functions of static electricity prevention and corrosion prevention according to claim 1, wherein: the light stabilizer is one or more of 2- (3 ' -tert-butyl-2 ' -hydroxy-5 ' -methylphenyl) -5-chloro-benzotriazole or 2 ', 4 ' -di-tert-butylphenyl-3, 5-di-tert-butyl-4-hydroxybenzoate.
5. The safety belt with antistatic and anticorrosion functions as claimed in claim 1, wherein: the flame retardant is one or more of ammonium polyphosphate or tricresyl phosphate.
6. The safety belt with antistatic and anticorrosion functions as claimed in claim 1, wherein: the wear-resistant agent is selected from one or more of silicone powder or polytetrafluoroethylene.
7. A process for preparing the antistatic and anticorrosive safety belt according to any one of claims 1 to 6, characterized in that: the method comprises the following steps:
s1, preprocessing: weighing the raw materials, carrying out melt processing and blending forming on the raw materials to prepare a blended yarn with the count of 20S as a warp yarn and a blended yarn with the count of 41S as a weft yarn;
s2, warping: warping the warp yarns in the step S1 on warping equipment with the linear speed of the warp yarns being 300-500 m/min;
s2, weaving: putting the warped warp yarns into a weaving machine, putting the weft yarns into a weft feeding device of the weaving machine, and weaving by the weaving machine to obtain a woven safety belt;
s3, cleaning: cleaning the safety belt obtained in the step S2, and placing the safety belt in a dryer for drying, wherein the drying temperature is 75-85 ℃, and the drying time is set to be 1-2 hours;
s4, antiseptic treatment: the safety belt obtained in the step S4 is pressed and dipped in the anti-corrosion coating for 20 to 40 minutes, and is dried after being cleaned by clear water, wherein the drying temperature is 70 to 90 ℃, and the drying time is 2 to 8 minutes;
s5, staining: dyeing the safety belt obtained in the step S4 into a required color through a dyeing process;
s6, drying: putting the dyed safety belt into a dryer for drying;
s7, static electricity removal: and (4) putting the dried safety belt into a static eliminator to remove static on the surface of the safety belt.