CN114799094B - Treatment method for steel infiltration between continuous casting tundish plates - Google Patents
Treatment method for steel infiltration between continuous casting tundish plates Download PDFInfo
- Publication number
- CN114799094B CN114799094B CN202210443654.6A CN202210443654A CN114799094B CN 114799094 B CN114799094 B CN 114799094B CN 202210443654 A CN202210443654 A CN 202210443654A CN 114799094 B CN114799094 B CN 114799094B
- Authority
- CN
- China
- Prior art keywords
- tundish
- steel
- flow
- continuous casting
- accident
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to the field of steelmaking continuous casting, and relates to a treatment method for steel infiltration between continuous casting tundish plates.
Description
Technical Field
The invention belongs to the field of steelmaking continuous casting, and relates to a treatment method for steel infiltration between continuous casting tundish plates.
Background
The continuous casting tundish is subjected to inter-plate steel infiltration in the casting process, if improper treatment is carried out, production interruption occurs, fire, equipment damage and casualties can occur in serious cases, and great loss is caused to the production and operation of a steel mill, but no standard or standard treatment flow and method are found in China at present.
Disclosure of Invention
In view of the above, the present invention aims to provide a method for treating inter-tundish steel infiltration, which is used for normalizing the inter-tundish steel infiltration treatment process.
In order to achieve the above purpose, the present invention provides the following technical solutions: a method for treating steel infiltration between continuous casting tundish plates, which uses a tool blind plate and a plugging cone, comprises the following steps:
s1, when steel seepage occurs between tundish plates, firstly, the ladle pouring operation should be stopped immediately;
s2, judging whether the steel flow is out of control or not: the flow is smaller, large-area decompression diffusion or splashing does not occur, and the non-control can be judged; the flow is large, large-area diffusion and splashing occur, and direct burn risks can be generated for close-range operators, and the operators can be regarded as out of control;
s21, uncontrolled handling of steel flow: the method has the advantages that other flows can be blinded without burn risk, the steel seepage flow is not treated, and the tundish car is started to be above the accident slag basin in an accident running control mode;
s22, steel loss control treatment: the steel seepage flow blind plate is arranged on the slideway, the flow is blocked by using the blocking cone, if 2 blocking cones are used, the flow is still not blocked, other flows can be firstly blocked under the condition of no burn risk, and then the tundish car is started to be arranged above the accident slag basin in an accident running control mode;
s3, once the tundish reaches the upper part of the accident slag basin, immediately throwing the emergency chill into the tundish from the corresponding or nearby flow holes above the tundish cover, and rapidly cooling and blocking the flow;
optionally, the emergency chill is a green block or other cooling material.
Alternatively, the molten steel flowing into the accident slag pot must be covered with tundish covering slag to protect the tundish car.
Optionally, the volume of the accident slag basin is larger than that of the molten steel in the tundish, so that the molten steel is ensured not to overflow.
The invention has the beneficial effects that: the treatment method for the steel infiltration between the continuous casting tundish plates standardizes the treatment flow and the treatment method for the steel infiltration between the continuous casting tundish plates, prevents the expansion of production safety accidents and ensures stable and smooth production.
Additional advantages, objects, and features of the invention will be set forth in part in the description which follows and in part will become apparent to those having ordinary skill in the art upon examination of the following or may be learned from practice of the invention. The objects and other advantages of the invention may be realized and obtained by means of the instrumentalities and combinations particularly pointed out in the specification.
Detailed Description
Other advantages and effects of the present invention will become apparent to those skilled in the art from the following disclosure, which describes the embodiments of the present invention with reference to specific examples. The invention may be practiced or carried out in other embodiments that depart from the specific details, and the details of the present description may be modified or varied from the spirit and scope of the present invention. The following embodiments are merely illustrative of the basic concepts of the present invention, and the following embodiments and features of the embodiments may be combined with each other without conflict.
DETAILED DESCRIPTION OF EMBODIMENT (S) OF INVENTION
A method for treating steel infiltration between continuous casting tundish plates, which uses a tool blind plate and a plugging cone, comprises the following steps:
s1, when steel seepage occurs between tundish plates, firstly, the ladle pouring operation should be stopped immediately;
s2, judging whether the steel flow is out of control or not: the flow is smaller, large-area decompression diffusion or splashing does not occur, and the non-control can be judged; the flow is large, large-area diffusion and splashing occur, and direct burn risks can be generated for close-range operators, and the operators can be regarded as out of control;
s21, uncontrolled handling of steel flow: the method has the advantages that other flows can be blinded without burn risk, the steel seepage flow is not treated, and the tundish car is started to be above the accident slag basin in an accident running control mode;
s22, steel loss control treatment: the steel seepage flow blind plate is arranged on the slideway, the flow is blocked by using the blocking cone, if 2 blocking cones are used, the flow is still not blocked, other flows can be firstly blocked under the condition of no burn risk, and then the tundish car is started to be arranged above the accident slag basin in an accident running control mode;
s3, once the tundish reaches the upper part of the accident slag basin, immediately throwing an emergency chill (cooling material such as pig iron block and the like) into the tundish from a corresponding or nearby flow hole above the tundish cover, and rapidly cooling and blocking the flow;
in this embodiment, the molten steel flowing into the accident slag pot must be covered with tundish covering slag to protect the tundish car.
In the embodiment, the volume of the accident slag basin is larger than that of the molten steel in the tundish, so that the molten steel is ensured not to overflow.
Finally, it is noted that the above embodiments are only for illustrating the technical solution of the present invention and not for limiting the same, and although the present invention has been described in detail with reference to the preferred embodiments, it should be understood by those skilled in the art that modifications and equivalents may be made thereto without departing from the spirit and scope of the present invention, which is intended to be covered by the claims of the present invention.
Claims (4)
1. A method for treating steel infiltration between continuous casting tundish plates, which uses a tool blind plate and a plugging cone, is characterized by comprising the following steps:
s1, when steel seepage occurs between tundish plates, firstly, the ladle pouring operation should be stopped immediately;
s2, judging whether the steel flow is out of control or not: the flow is smaller, large-area decompression diffusion or splashing does not occur, and the non-control can be judged; the flow is large, large-area diffusion and splashing occur, and direct burn risks can be generated for close-range operators, and the operators can be regarded as out of control;
s21, uncontrolled handling of steel flow: the method has the advantages that other flows can be blinded without burn risk, the steel seepage flow is not treated, and the tundish car is started to be above the accident slag basin in an accident running control mode;
s22, steel loss control treatment: the steel seepage flow blind plate is arranged on the slideway, the flow is blocked by using the blocking cone, if 2 blocking cones are used, the flow is still not blocked, other flows can be firstly blocked under the condition of no burn risk, and then the tundish car is started to be arranged above the accident slag basin in an accident running control mode;
s3, once the tundish reaches the upper part of the accident slag basin, immediately throwing the emergency chill into the tundish from the corresponding or nearby flow holes above the tundish cover, and rapidly cooling and blocking the flow.
2. The method for treating steel infiltration between continuous casting tundish plates according to claim 1, characterized by: the emergency chill is a green block or other cooling material.
3. The method for treating steel infiltration between continuous casting tundish plates according to claim 1, characterized by: molten steel flowing into the accident slag pot must be covered with tundish covering slag to protect the tundish car.
4. The method for treating steel infiltration between continuous casting tundish plates according to claim 1, characterized by: the volume of the accident slag basin is larger than that of the molten steel in the tundish, so that the molten steel is ensured not to overflow.