CN114605825A - 一种感光防静电复合材料及其制备方法 - Google Patents
一种感光防静电复合材料及其制备方法 Download PDFInfo
- Publication number
- CN114605825A CN114605825A CN202210370709.5A CN202210370709A CN114605825A CN 114605825 A CN114605825 A CN 114605825A CN 202210370709 A CN202210370709 A CN 202210370709A CN 114605825 A CN114605825 A CN 114605825A
- Authority
- CN
- China
- Prior art keywords
- photosensitive
- composite material
- antistatic
- resin
- antistatic composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种感光防静电复合材料，由以下重量比的原料组成：二烯丙级双酚A改性双马来酰亚胺树脂：导电硫酸钡：氧化钕：纳米填料=10:1.25:1.25:1。与现有技术相比，本发明用二烯丙级双酚A改性双马来酰亚胺树脂为基体树脂生产出来的感光防静电复合材料既能对光敏感起到感光作用可以被电路焊接设备所识别，又能起到防静电的作用，达到焊接工艺对防护材料防静电的要求，完全满足现在焊机技术的使用工艺，且产品性能稳定，使用次数较高，达到30000次以上。产品的成本较低，达到了良好的经济效益。
Description
技术领域
本发明涉及领域，特别是一种感光防静电复合材料及其制备方法。
背景技术
感光防静电复合材料是近年来根据电子治具焊接行业发展衍生出来的一种新的复合材料，该材料最大的特性是能够被目前最先进的感光波峰焊焊接设备所识别，且具有良好的综合性能。
传统的防静电材料主要主要依靠炭黑起到防静电的作用，故表面统一为黑色表面，随着波峰焊接技术的发展，为了加快波峰焊接的速率，现在的进口设备统一改为对光敏感的焊接设备，该类设备的好处有以下两个方面，1：焊接设备速度快，2：焊接精度高。随之而来的问题也就产生了，传统的黑色防静电复合材料不能反射光，不对光敏感，光敏焊接设备感受不到，故其不工作。
另外，随着电子制造行业焊接技术的发展，目前电路板焊接技术对焊接托盘（托盘由感光复合材料制作而成）的要求越来越高，现在的焊接技术要求除了要求制作托盘的材料要起到感光作用、能够防静电以外，还要求托盘的重复使用次数要达到30000次以上。目前市场上销售的感光复合材料没有一款能够重复使用30000次，经实验对比发现，不能重复使用30000次以上的主要原因是复合材料的基体树脂耐温不够，随着使用次数的增加材料的性能衰减较快；这就造成感光复合材料的使用量加大，成本增高。
发明内容
本发明的目的是要解决现有技术中存在的不足，提供一种感光防静电复合材料及其制备方法。
为达到上述目的，本发明是按照以下技术方案实施的：
本发明的第一个目的是要提供一种感光防静电复合材料，由以下重量比的原料组成：二烯丙级双酚A改性双马来酰亚胺树脂：导电硫酸钡：氧化钕：纳米填料=10:1.25:1.25:1。
进一步地，所述纳米填料为纳米为氧化硅与纳米氧化钕。
本发明的第二个目的是要提供一种感光防静电复合材料的制备方法，包括以下步骤：
S1、按重量比10:1.25:1.25:1取二烯丙级双酚A改性双马来酰亚胺树脂、导电硫酸钡、氧化钕、纳米填料混合，搅拌均匀得复合树脂胶料；
S2、取复合树脂胶料，经玻璃纤维浸胶形成层压感光板预浸布；
S3、将层压感光板预浸布继续在270℃条件下压制成感光防静电复合材料。
与现有技术相比，本发明用二烯丙级双酚A改性双马来酰亚胺树脂为基体树脂生产出来的感光防静电复合材料既能对光敏感起到感光作用，又能起到防静电的作用，防静电指数达到105-109，达到焊接工艺对防护材料的要求，完全满足现在焊机技术的使用工艺，且产品性能稳定，使用次数较高，达到30000次以上，产品的成本较低，达到了良好的经济效益。
具体实施方式
为使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步的详细说明。此处所描述的具体实施例仅用于解释本发明，并不用于限定发明。
实施例1
称取二烯丙级双酚A改性双马来酰亚胺树脂10kg、导电硫酸钡1.25kg、氧化钕1.25kg、纳米填料1kg混合，搅拌均匀得复合树脂胶料；
然后取复合树脂胶料，经玻璃纤维浸胶形成层压感光板板预浸布；
最后将层压导磁板预浸布继续在190℃条件下压制成感光防静电复合材料。
对比例1
与实施例1不同在于使用环氧树脂为基体树脂，其余同实施例1。
经检测，以环氧树脂为基体树脂做出的感光复合材料的玻璃化温度为270摄氏度。
实施例1感光防静电复合材料是通过在二烯丙级双酚A改性双马来酰亚胺树脂中加入一定比例的导电硫酸钡和氧化钕使复合材料的的颜色即能对光敏感起到感光作用，又能使合成石起到防静电的作用。本实施例的感光防静电复合材料经实际检测，其具体的技术指标如表1所示。
表1
| 颜色 | 棕色 |
| 防静电指数 | 10<sup>5</sup>-10<sup>9</sup> |
| 光敏度 | 良好 |
| 燃烧性（级） | HB 40 |
| 密度/比重 g/cm<sup>3</sup> | 2.0 |
| 工作温度 ℃ | 300 |
| 抗弯强度23℃（常温） Mpa | 410 |
| 抗压强度23℃（常温） Mpa | 600 |
| 横向的导热 W/M.K | 0.27 |
| 线膨胀系数 10<sup>-6</sup>/K | 10 |
| 吸水率 % | <0.2 |
由表1可以看出，本发明制备的感光防静电复合材料能够满足现在焊接技术的工艺要求，因此以二烯丙级双酚A改性双马来酰亚胺树脂为基体树脂做出的感光复合材料可以重复使用30000次以上，可达到40000次。
本发明的技术方案不限于上述具体实施例的限制，凡是根据本发明的技术方案做出的技术变形，均落入本发明的保护范围之内。
Claims (3)
1.一种感光防静电复合材料，其特征在于，由以下重量比的原料组成：二烯丙级双酚A改性双马来酰亚胺树脂：导电硫酸钡：氧化钕：纳米填料=10:1.25:1.25:1。
2.根据权利要求1所述的感光防静电复合材料，其特征在于：所述纳米填料为纳米二氧化硅与纳米氧化钕。
3.一种如权利要求1所述的感光防静电复合材料的制备方法，其特征在于，包括以下步骤：
S1、按重量比10:1.25:1.25:1取二烯丙级双酚A改性双马来酰亚胺树脂、导电硫酸钡、氧化钕、纳米填料混合，搅拌均匀得复合树脂胶料；
S2、取复合树脂胶料，经玻璃纤维浸胶形成层压感光板预浸布；
S3、将层压感光板预浸布继续在270℃条件下压制成感光防静电复合材料。