CN114525028B - Adjustable polymer-based porous electromagnetic shielding material, and preparation method and application thereof - Google Patents
Adjustable polymer-based porous electromagnetic shielding material, and preparation method and application thereof Download PDFInfo
- Publication number
- CN114525028B CN114525028B CN202111129010.1A CN202111129010A CN114525028B CN 114525028 B CN114525028 B CN 114525028B CN 202111129010 A CN202111129010 A CN 202111129010A CN 114525028 B CN114525028 B CN 114525028B
- Authority
- CN
- China
- Prior art keywords
- electromagnetic shielding
- polymer
- based porous
- solution
- shielding material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an adjustable polymer-based porous electromagnetic shielding material, and a preparation method and application thereof, and belongs to the technical field of shielding materials 4 Solution and FeCl 3 The solution is stirred evenly, then the temperature is raised for reaction, then alkali liquor is dripped for adjustment to be alkaline, and EG/Fe is obtained after washing and drying 3 O 4 A composite material; finally EG/Fe 3 O 4 The composite material is sequentially added with deionized water, triethanolamine, a foam stabilizer and polyether polyol and uniformly mixed, then stannous octoate is added for uniform dispersion, the mixture is added with toluene diisocyanate and stirred, then poured into a mold for applying pressure, and finally the mold is dried to obtain the polymer-based porous electromagnetic shielding material. The preparation method disclosed by the invention is simple to operate, raw materials are easy to obtain, and the prepared shielding material has the characteristics of light weight, high elasticity and adjustable aperture, and is expected to be applied to the fields of flexible electronics and stealth materials.
Description
Technical Field
The invention relates to the technical field of electromagnetic shielding materials, in particular to an adjustable polymer-based porous electromagnetic shielding material, and a preparation method and application thereof.
Background
With the continuous development and progress of scientific technology, more and more electronic devices gradually come into the field of vision of people. However, the use of electronic products inevitably causes electromagnetic interference, and these electromagnetic interference signals cause great trouble to the normal operation of electronic components, so that electromagnetic shielding and microwave absorption technologies are attracting more and more attention.
The polymer-based porous material has the advantages of light weight and high elasticity, the cellular structure can provide a plurality of reflection interfaces in the transmission process of electromagnetic waves, so that the electromagnetic waves are lost after being reflected and absorbed for many times, the electromagnetic shielding performance is favorably improved, the pore size of the porous material is an important factor influencing the electromagnetic shielding performance, the efficient shielding of the material on the electromagnetic waves in a specific frequency band can be realized by adjusting the pore size of the porous material, and the polymer-based porous material has important significance for the development of the electromagnetic shielding material.
The electromagnetic shielding material has the loss of electromagnetic waves mainly represented by dielectric loss and magnetic loss, however, although the pore structure of the polymer porous material has a good effect on multiple reflection and absorption of electromagnetic waves, most polymers do not have conductivity, and the application of the polymer porous material in the electromagnetic shielding material is severely limited.
Therefore, it is an urgent need to solve the problems of the art to provide a tunable polymer-based porous electromagnetic shielding material, and a preparation method and application thereof.
Disclosure of Invention
In view of the above, the invention provides an adjustable polymer-based porous electromagnetic shielding material, and a preparation method and application thereof, the preparation method disclosed by the invention is simple to operate, raw materials are easy to obtain, and the shielding material prepared by the method provided by the invention has the characteristics of light weight, high elasticity and adjustable pore diameter, can realize shielding of electromagnetic waves in different frequency bands, and is expected to play an important role in the fields of flexible electronics and stealth materials.
In order to achieve the purpose, the invention adopts the following technical scheme:
a preparation method of an adjustable polymer-based porous electromagnetic shielding material specifically comprises the following steps:
(1) Adding the expanded graphite into the mixed solvent, uniformly stirring, and then adding FeSO 4 Solution and FeCl 3 Uniformly stirring the solution to obtain a mixed solution;
(2) Heating the mixed solution for reaction, then dropwise adding alkali liquor to adjust the mixed solution to be alkaline, and washing and drying the mixed solution to obtain EG/Fe 3 O 4 A composite material;
(3) To the above EG/Fe 3 O 4 The composite material is sequentially added with deionized water, triethanolamine, a foam stabilizer and polyether polyol and uniformly mixed, then stannous octoate is added for uniform dispersion, the mixture is added with toluene diisocyanate and stirred, then poured into a mold for applying pressure, and finally the mold is dried to obtain the polymer-based porous electromagnetic shielding material.
The beneficial effects of the preferred technical scheme are as follows: the preparation method disclosed by the invention firstly prepares Fe 3 O 4 The nano particles are loaded on expandable graphite to obtain EG/Fe 3 O 4 Composite material, EG/Fe 3 O 4 The composite material is filled into the polymer-based porous material to obtain the adjustable polymer-based porous electromagnetic shielding material. The porous material with the average diameter of the pores between 50 and 500 mu m is obtained by adjusting the proportion of the raw materials and the preparation process, and the porous material respectively shows good electromagnetic shielding effect in different frequency bands of electromagnetic waves; the diameter of the porous polymer cell is regulated to realize the shielding of electromagnetic waves in a specific frequency band.
Preferably, the mixed solvent in the step (1) is prepared from water and absolute ethyl alcohol according to the ratio of 7:2 in a volume ratio;
FeSO 4 solution and FeCl 3 The concentration of the solution is 0.5mol/L respectively;
the expanded graphite, the mixed solvent, and the FeSO 4 Solution and said FeCl 3 The mixing mass ratio of the solution is 1: (20 to 35): 10:10;
the stirring speed is 200-300 r/min; the time is 20-40 min.
The beneficial effects of the preferred technical scheme are as follows: the invention adopts an in-situ polymerization method to polymerize Fe 3 O 4 The nano particles are loaded on the expanded graphite, so that the expanded graphite with good conductivity and the magnetic Fe 3 O 4 The nano particles are combined to obtain the composite material, so that the electromagnetic shielding performance of the filler is further improved.
Preferably, in the step (2), the temperature is increased to 45-60 ℃, the reaction time is 2-4 h, the alkali liquor is ammonia water, and the pH value is 11 after adjustment;
the washing times are 3-5 times;
the drying temperature is 60-80 ℃.
Preferably, the foam stabilizer in the step (3) is one or any combination of a silicone stabilizer and a silicone polyether copolymer stabilizer;
the EG/Fe 3 O 4 The mass ratio of the composite material, the deionized water, the triethanolamine, the foam stabilizer, the polyether polyol, the stannous octoate and the toluene diisocyanate is (5-20): (6-15): 0.5: (2-4): 100:0.5: (60-80).
The beneficial effects of the preferred technical scheme are as follows: the invention uses EG/Fe 3 O 4 The composite filler is filled in the polyurethane porous material, so that the polyurethane porous material is endowed with good electric conductivity and magnetism, and the electromagnetic shielding performance of the porous material is enhanced.
Preferably, the drying temperature in the step (3) is 80-90 ℃, and the drying time is 10-20 min.
Preferably, the rotating speed of the stirring in the step (3) is 2000r/min; the applied pressure is 10-100N;
the beneficial effects of the preferred technical scheme are as follows: according to the invention, isocyanate and water are fully reacted by high-speed stirring to generate carbon dioxide gas to obtain the porous material, and the average pore size of the porous material is regulated and controlled by applying different pressures in the chemical foaming process, so that the porous material plays an important role in absorption and reflection attenuation of electromagnetic waves in different frequency bands.
The invention also provides an adjustable polymer-based porous electromagnetic shielding material, which is prepared by adopting the method.
The beneficial effects of the preferred technical scheme are as follows: the invention passes magnetic Fe 3 O 4 In-situ growth of nano particles on the surface of conductive expanded graphite to obtain EG/Fe 3 O 4 Compounding the filler and introducing the filler into the polymer to obtain the polymer-based conductive electromagnetic shielding material. Wherein the large surface area and the loose void structure of the expanded graphite are utilized as Fe 3 O 4 The in-situ growth of the nano particles creates conditions, and the nano particles have stronger interaction, thereby providing a good foundation for the preparation of the conductive polymer; the expanded graphite has good conductivity, and is beneficial to the dielectric loss of electromagnetic waves; fe 3 O 4 The nano particles have excellent magnetism and can promote the magnetic loss of electromagnetic waves; the combination of the conductive expanded graphite and the magnetic Fe3O4 nano particles improves the impedance matching characteristic, so that more electromagnetic waves enter the material to be lost, and the electromagnetic shielding performance of the material is improved; fe 3 O 4 The particles are supported on the expanded graphite to form an interface contact resistance on the surface thereof, thereby forming a capacitor-like structure to promote absorption loss of electromagnetic waves, and having a positive effect on electromagnetic shielding.
The invention further provides an application of the adjustable polymer-based porous electromagnetic shielding material in flexible electronic or stealth materials.
Compared with the prior art, the invention discloses and provides the adjustable polymer-based porous electromagnetic shielding material and the preparation method and application thereof.
(1) The invention utilizes the large surface area and the loose void structure of the expanded graphite as Fe 3 O 4 The in-situ growth of the nano particles creates conditions and the nano particles are stored between the conditionsThe strong interaction provides a good foundation for the preparation of the conductive polymer;
(2) In addition, the expanded graphite has good conductivity, and is beneficial to the dielectric loss of electromagnetic waves; fe 3 O 4 The nanoparticles have excellent magnetic properties, promote magnetic loss of electromagnetic waves, and are Fe 3 O 4 The nano particles have simple preparation process and low cost, and are ideal fillers for preparing electromagnetic shielding materials;
(3) Conductive expanded graphite and magnetic Fe 3 O 4 The combination of the nano particles improves the impedance matching characteristic, so that more electromagnetic waves enter the material to be lost, and the electromagnetic shielding performance of the material is improved; fe 3 O 4 The particles are supported on the expanded graphite to form an interface contact resistance on the surface thereof, thereby forming a capacitor-like structure to promote absorption loss of electromagnetic waves, and having a positive effect on electromagnetic shielding.
(4) The invention realizes the high-efficiency shielding of electromagnetic waves in different frequency bands by regulating and controlling the diameter of the foam polymer foam pores;
(5) The polyurethane foam as a three-dimensional network structure provides an effective place for multiple reflection and absorption of electromagnetic waves;
(6) According to the invention, by regulating and controlling the diameter of the polyurethane foam hole, electromagnetic waves are lost when being transmitted to the shielding material, so that the electromagnetic waves are prevented from directly penetrating through the shielding material, and the electromagnetic shielding effect is achieved. The polyurethane foam with the large cell diameter has a good shielding effect on low-frequency-band electromagnetic waves, the polyurethane foam with the small cell diameter has a good shielding effect on high-frequency-band electromagnetic waves, and the polyurethane foam achieves the shielding efficiency of being larger than 20dB in the electromagnetic wave range of 500 MHz-12 GHz by adjusting the cell diameter of the polyurethane foam.
Drawings
FIG. 1 is an SEM photograph of the polymer-based porous electromagnetic shielding materials prepared in examples 1-6;
FIG. 2 shows EG/Fe prepared in examples 1 to 6 3 O 4 SEM pictures of the composite filler.
Detailed Description
The technical solutions in the embodiments of the present invention are clearly and completely described below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The embodiment of the invention discloses a preparation method of an adjustable polymer-based porous electromagnetic shielding material, which specifically comprises the following steps:
(1) Adding the expanded graphite into the mixed solvent, uniformly stirring, and then adding FeSO 4 Solution and FeCl 3 Uniformly stirring the solution to obtain a mixed solution;
wherein the mixed solvent is prepared from water and absolute ethyl alcohol according to the weight ratio of 7:2 by volume ratio; feSO 4 Solution and FeCl 3 The concentration of the solution is 0.5mol/L;
expanded graphite, mixed solvent and FeSO 4 Solution and FeCl 3 The mass ratio of the solution is 1: (20 to 35): 10:10;
the stirring speed is 200-300 r/min; the time is 20-40 min;
(2) Heating the mixed solution to 45-60 ℃, reacting for 2-4 h, then dropwise adding ammonia water to adjust the pH value to 11 alkalinity, washing for 3-5 times, and drying at 60-80 ℃ to obtain EG/Fe 3 O 4 A composite material;
(3) To the above EG/Fe 3 O 4 Sequentially adding deionized water, triethanolamine, a foam stabilizer and polyether polyol into the composite material, uniformly mixing, then adding stannous octoate, uniformly dispersing, adding toluene diisocyanate, stirring, pouring into a mold, applying pressure, finally placing the mold into a vacuum oven, and drying at 80-90 ℃ for 10-20 min to obtain the polymer-based porous electromagnetic shielding material;
the foam stabilizer is one or any combination of a silicone stabilizer and a silicone polyether copolymer stabilizer;
wherein, EG/Fe 3 O 4 Composite material, deionized water,The mass ratio of the triethanolamine to the foam stabilizer to the polyether polyol to the stannous octoate to the toluene diisocyanate is (5-20): (6-15): 0.5: (2-4): 100:0.5: (60-80); the stirring speed is 2000r/min; the applied pressure is 10-100N.
Example 1
The embodiment 1 of the invention discloses a preparation method of an adjustable polymer-based porous electromagnetic shielding material, which specifically comprises the following steps:
(1) 2g of expanded graphite was added to 30mL of a mixed solvent composed of water and absolute ethanol in a ratio of 7:2, and then 10mL of FeSO with a concentration of 0.5mol/L is added thereto 4 Solution and 10mL FeCl with concentration of 0.5mol/L 3 Solution, guaranteed Fe 3+ With Fe 2+ In a molar ratio of 1:1, uniformly stirring, heating to 50 ℃, reacting for 3 hours, then dropwise adding ammonia water until the pH value is 11, washing and drying to obtain EG/Fe 3 O 4 A composite material;
(2) To 10g of EG/Fe 3 O 4 6g of deionized water, 0.4g of triethanolamine, 3g of foam stabilizer and 50g of polyether polyol are sequentially added into the composite material and uniformly mixed, then 0.4g of stannous octoate is added for uniform dispersion, then 30g of toluene diisocyanate is added, the mixture is stirred at the rotating speed of 2000r/min and poured into a mold to apply the pressure of 10N, and then the mold is placed into a vacuum oven to be dried for 10min at the temperature of 85 ℃ to obtain the polymer-based porous electromagnetic shielding material.
Example 2
The embodiment 2 of the invention discloses a preparation method of an adjustable polymer-based porous electromagnetic shielding material, which specifically comprises the following steps:
(1) 2g of expanded graphite was added to 30mL of a mixed solvent composed of water and absolute ethanol in a ratio of 7:2, and then 10mL of FeSO with a concentration of 0.5mol/L is added thereto 4 Solution and 10mL FeCl with concentration of 0.5mol/L 3 Solution, guaranteed Fe 3+ With Fe 2+ In a molar ratio of 1:1, uniformly stirring, heating to 50 ℃, reacting for 3 hours, then dropwise adding ammonia water until the pH value is 11, washing and drying to obtain EG/Fe 3 O 4 A composite material;
(2) To 10g of EG/Fe 3 O 4 4g of deionized water, 0.4g of triethanolamine, 3g of foam stabilizer and 50g of polyether polyol are sequentially added into the composite material and uniformly mixed, then 0.4g of stannous octoate is added for uniform dispersion, then 30g of toluene diisocyanate is added, the mixture is stirred at the rotating speed of 2000r/min and poured into a mould to apply the pressure of 10N, and then the mould is placed into a vacuum oven to be dried for 10min at the temperature of 85 ℃ to obtain the polymer-based porous electromagnetic shielding material.
Example 3
The embodiment 3 of the invention discloses a preparation method of an adjustable polymer-based porous electromagnetic shielding material, which specifically comprises the following steps:
(1) 2g of expanded graphite was added to 30mL of a mixed solvent composed of water and absolute ethanol in a ratio of 7:2, and then 10mL of FeSO with a concentration of 0.5mol/L is added thereto 4 Solution and 10mL FeCl with concentration of 0.5mol/L 3 Solution, guaranteed Fe 3+ With Fe 2+ In a molar ratio of 1:1, uniformly stirring, heating to 50 ℃, reacting for 3 hours, then dropwise adding ammonia water until the pH value is 11, washing and drying to obtain EG/Fe 3 O 4 A composite material;
(2) To 10g of EG/Fe 3 O 4 Adding 3g of deionized water, 0.4g of triethanolamine, 3g of a foam stabilizer and 50g of polyether polyol into the composite material in sequence, uniformly mixing, adding 0.4g of stannous octoate, uniformly dispersing, adding 30g of toluene diisocyanate, stirring at the rotating speed of 2000r/min, pouring into a mold, applying the pressure of 10N, and then placing in a vacuum oven to dry for 10min at the temperature of 85 ℃ to obtain the polymer-based porous electromagnetic shielding material.
Example 4
The embodiment 4 of the invention discloses a preparation method of an adjustable polymer-based porous electromagnetic shielding material, which specifically comprises the following steps:
(1) 2g of expanded graphite was added to 30mL of a mixed solvent composed of water and absolute ethanol in a ratio of 7:2, and then 10mL of FeSO with a concentration of 0.5mol/L is added thereto 4 Solution and 10mL FeCl with concentration of 0.5mol/L 3 Solution, guaranteed Fe 3+ With Fe 2+ In a molar ratio of 1:1, uniformly stirring, heating to 50 ℃, reacting for 3 hours, then dropwise adding ammonia water until the pH value is 11, washing and drying to obtain EG/Fe 3 O 4 A composite material;
(2) To 10g of EG/Fe 3 O 4 2g of deionized water, 0.4g of triethanolamine, 3g of foam stabilizer and 50g of polyether polyol are sequentially added into the composite material and uniformly mixed, then 0.4g of stannous octoate is added for uniform dispersion, then 30g of toluene diisocyanate is added, the mixture is stirred at the rotating speed of 2000r/min and poured into a mold to apply the pressure of 10N, and then the mold is placed into a vacuum oven to be dried for 10min at the temperature of 85 ℃ to obtain the polymer-based porous electromagnetic shielding material.
Example 5
The embodiment 5 of the invention discloses a preparation method of an adjustable polymer-based porous electromagnetic shielding material, which specifically comprises the following steps:
(1) 2g of expanded graphite was added to 30mL of a mixed solvent composed of water and absolute ethanol in a ratio of 7:2, and then 10mL of FeSO with a concentration of 0.5mol/L is added thereto 4 Solution and 10mL FeCl with concentration of 0.5mol/L 3 Solution, guaranteed Fe 3+ With Fe 2+ In a molar ratio of 1:1, uniformly stirring, heating to 50 ℃, reacting for 3 hours, then dropwise adding ammonia water until the pH value is 11, washing and drying to obtain EG/Fe 3 O 4 A composite material;
(2) To 10g of EG/Fe 3 O 4 2g of deionized water, 0.4g of triethanolamine, 3g of foam stabilizer and 50g of polyether polyol are sequentially added into the composite material and uniformly mixed, then 0.4g of stannous octoate is added for uniform dispersion, then 30g of toluene diisocyanate is added, the mixture is stirred at the rotating speed of 2000r/min and poured into a mold for applying the pressure of 20N, and then the mixture is placed into a vacuum oven to be dried for 10min at the temperature of 85 ℃ to obtain the polymer-based porous electromagnetic shielding material.
Example 6
The embodiment 6 of the invention discloses a preparation method of an adjustable polymer-based porous electromagnetic shielding material, which specifically comprises the following steps:
(1) 2g of expanded graphite is added into 30mL of mixed solventWater and absolute ethanol as given in 7:2, and then 10mL of FeSO with a concentration of 0.5mol/L is added thereto 4 Solution and 10mL FeCl with concentration of 0.5mol/L 3 Solution, guaranteed Fe 3+ With Fe 2+ In a molar ratio of 1:1, uniformly stirring, heating to 50 ℃, reacting for 3 hours, then dropwise adding ammonia water until the pH value is 11, washing and drying to obtain EG/Fe 3 O 4 A composite material;
(2) To 10g of EG/Fe 3 O 4 2g of deionized water, 0.4g of triethanolamine, 3g of foam stabilizer and 50g of polyether polyol are sequentially added into the composite material and uniformly mixed, then 0.4g of stannous octoate is added for uniform dispersion, then 30g of toluene diisocyanate is added, the mixture is stirred at the rotating speed of 2000r/min and poured into a mold to apply the pressure of 50N, and then the mold is placed into a vacuum oven to be dried for 10min at the temperature of 85 ℃ to obtain the polymer-based porous electromagnetic shielding material.
Comparative example 1
The invention discloses a preparation method of a polymer-based porous electromagnetic shielding material, which comprises the following steps:
(1) Sequentially adding 6g of deionized water, 0.4g of triethanolamine, 3g of foam stabilizer and 50g of polyether polyol into a beaker, and uniformly mixing;
(2) And adding 0.4g of stannous octoate into the obtained mixed solution, uniformly dispersing, then adding 30g of toluene diisocyanate, stirring at the rotating speed of 2000r/min, pouring into a mould, applying the pressure of 10N, and then placing the mould into a vacuum oven to dry for 10min at the temperature of 85 ℃ to obtain the polymer-based porous electromagnetic shielding material.
Effect verification
1. The average cell diameters of the polymer-based porous electromagnetic shielding composites prepared in examples 1 to 6 were counted and calculated as shown in table 1.
2. Preparing EG/Fe in step (1) of examples 1-6 by adopting Zeiss scanning electron microscope SIGMA300 3 O 4 The composite material was characterized and the SEM image is shown in FIG. 1.
3. The polymer-based porous electromagnetic shielding composite materials prepared in examples 1 to 6 were characterized by a zeiss scanning electron microscope SIGMA300, and the obtained SEM image is shown in fig. 2.
4. The electromagnetic shielding performance of the polymer-based porous composite materials obtained in examples 1 to 6 and comparative example 1 was tested using a vector network analyzer CEYEAR3672A-S, and the results are shown in table 1.
TABLE 1 average cell diameter and shielding effectiveness of the porous materials obtained in the examples
As can be seen from Table 1, the polymer-based porous electromagnetic shielding composite material prepared in example 1 has an excellent shielding effect on electromagnetic waves of 500MHz to 1GHz, and the electromagnetic shielding effectiveness reaches 35dB; the polymer-based porous electromagnetic shielding composite material prepared in the embodiment 2 has a good shielding effect on electromagnetic waves of 1 GHz-3 GHz, and the average electromagnetic shielding effectiveness is 31dB; the polymer-based porous electromagnetic shielding composite material prepared in the embodiment 3 has a good shielding effect on electromagnetic waves of 3 GHz-6 GHz, and the average electromagnetic shielding effectiveness is 28dB; the polymer-based porous electromagnetic shielding composite material prepared in the embodiment 4 has a good shielding effect on electromagnetic waves of 6 GHz-8 GHz, and the average electromagnetic shielding effectiveness is 26dB; the polymer-based porous electromagnetic shielding composite material prepared in the embodiment 5 has a good shielding effect on electromagnetic waves of 8 GHz-10 GHz, and the average electromagnetic shielding effectiveness is 24dB; the polymer-based porous electromagnetic shielding composite material prepared in example 6 has a good shielding effect on electromagnetic waves of 10 GHz-12 GHz, and the average electromagnetic shielding effectiveness is 21dB.
The embodiments in the present description are described in a progressive manner, each embodiment focuses on differences from other embodiments, and the same and similar parts among the embodiments are referred to each other. The device disclosed in the embodiment corresponds to the method disclosed in the embodiment, so that the description is simple, and the relevant points can be referred to the description of the method part.
The previous description of the disclosed embodiments is provided to enable any person skilled in the art to make or use the present invention. Various modifications to these embodiments will be readily apparent to those skilled in the art, and the generic principles defined herein may be applied to other embodiments without departing from the spirit or scope of the invention. Thus, the present invention is not intended to be limited to the embodiments shown herein but is to be accorded the widest scope consistent with the principles and novel features disclosed herein.
Claims (7)
1. The preparation method of the adjustable polymer-based porous electromagnetic shielding material is characterized by comprising the following steps:
(1) Adding the expanded graphite into the mixed solvent, uniformly stirring, and then adding FeSO 4 Solution and FeCl 3 Uniformly stirring the solution to obtain a mixed solution;
(2) Heating the mixed solution for reaction, then dropwise adding alkali liquor to adjust the mixed solution to be alkaline, and washing and drying the mixed solution to obtain EG/Fe 3 O 4 A composite material;
(3) To the above EG/Fe 3 O 4 Sequentially adding deionized water, triethanolamine, a foam stabilizer and polyether polyol into the composite material, uniformly mixing, then adding stannous octoate, uniformly dispersing, adding toluene diisocyanate, stirring, pouring into a mold, applying pressure, and finally drying the mold to obtain the polymer-based porous electromagnetic shielding material;
the foam stabilizer is one or any combination of a silicone stabilizer and a silicone polyether copolymer stabilizer;
the EG/Fe 3 O 4 The mass ratio of the composite material, the deionized water, the triethanolamine, the foam stabilizer, the polyether polyol, the stannous octoate and the toluene diisocyanate is (5-20): (6-15): 0.5: (2-4): 100:0.5: (60-80); the rotating speed of the stirring is 2000r/min; the applied pressure is 10-100N; by adjusting the raw material proportion and the preparation process, the porous material with the average diameter of the cells between 50 and 500 mu m is obtained, and the porous material respectively shows good electromagnetic shielding effect in different frequency bands of electromagnetic waves.
2. The method for preparing the tunable polymer-based porous electromagnetic shielding material according to claim 1, wherein the mixed solvent in step (1) is prepared from water and absolute ethyl alcohol according to a ratio of 7:2 in a volume ratio;
FeSO 4 solution and FeCl 3 The concentration of the solution is 0.5mol/L respectively;
the expanded graphite, the mixed solvent, and the FeSO 4 Solution and the FeCl 3 The mixing mass ratio of the solution is 1: (20 to 35): 10:10;
the stirring speed is 200-300 r/min; the time is 20-40 min.
3. The method for preparing the adjustable polymer-based porous electromagnetic shielding material according to any one of claims 1 to 2, wherein the temperature is raised to 45 to 60 ℃ in the step (2), the reaction time is 2 to 4 hours, the alkali solution is ammonia water, and the adjusted pH value is 11;
the washing times are 3-5 times;
the drying temperature is 60-80 ℃.
4. The method for preparing adjustable polymer-based porous electromagnetic shielding material according to claim 3, wherein the EG/Fe 3 O 4 Fe in composite material 3 O 4 The particle diameter of the particles is 10 to 20nm.
5. The method for preparing the adjustable polymer-based porous electromagnetic shielding material according to claim 1, wherein the drying temperature in the step (3) is 80-90 ℃ and the drying time is 10-20 min.
6. An adjustable polymer-based porous electromagnetic shielding material prepared by the method of any one of claims 1 to 5.
7. Use of the tunable polymer-based porous electromagnetic shielding material according to claim 6 in flexible electronic or stealth materials.