CN1144552C - Glass desk-top with breaking proof protection and its making method - Google Patents
Glass desk-top with breaking proof protection and its making method Download PDFInfo
- Publication number
- CN1144552C CN1144552C CNB011090561A CN01109056A CN1144552C CN 1144552 C CN1144552 C CN 1144552C CN B011090561 A CNB011090561 A CN B011090561A CN 01109056 A CN01109056 A CN 01109056A CN 1144552 C CN1144552 C CN 1144552C
- Authority
- CN
- China
- Prior art keywords
- protective layer
- tempered glass
- layer
- glass layer
- partly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a glass table top with breaking proof protection and a making method thereof. The making method comprises that a tempered glass layer with a center hole is washed, dried and then is heated to 45 DEG to 65 DEG; an adhesive layer made of acrylic acid is added on the top surface of the tempered glass layer; a protective layer is stuck and attached on the tempered glass layer, and the redundant circumference of the protective layer is cut away to make the size of the protective layer equal to that of the tempered glass layer; a center hole is formed on the protective layer and is concentric with the center hole of the tempered glass layer. When the glass table top is used in outdoor places or gardens, even if the glass table top is smashed, the fragments can not become thin fragment blocks to fly apart all around but can be firmly stuck and attached on the protective layer so as to avoid persons being injured by the fragment blocks.
Description
The invention provides a kind of glass desk-top and manufacture method thereof with breaking proof protection; especially refer to a kind of be used in open air or the garden and have the glass desk-top of breaking proof protection; when the glass desk-top of the breaking proof protection in open air or the garden is unexpectedly broken or hit, can not be subjected to the injury of glass fragment the people on desk limit.Belong to daily apparatus.
At present, the outdoor desk used of general garden is a kind of outdoor furniture of popularizing very much.Usually the usefulness in the time of can being placed in user's preceding garden or the back garden as leisure or barbie.Cleaning, furnishings arrange or other reasons that the surface of this desk is glassware normally for convenience.This glass desk-top can be placed on the frame simply, general, in the centre of these glass desk-tops, a fixed central duck eye all can be arranged as the usefulness of laying parasol.
The shortcoming of the glass desk-top maximum of these outdoor uses is very easily broken.Though most this type of desktop all is by the tempered glass manufacturing,, if desktop by sharp object impact, glass desk-top falls on the ground or its surface by small stone to hit at a high speed, in a single day glass still can be destroyed in.Since around high pressure all concentrate to the central part of glass, so the central part of this class tempered glass most fragile part often.If have precipitate high wind to blow to the parasol at a center, very likely can move to whole glass desk-top underground and cause the glass desk-top fragmentation.
No matter these desktops by the tempered glass manufacturing by which kind of unexpected reason are broken, but the glass fragment after broken can make the particularly young children of people be subjected to very serious injury.Therefore, must seek a kind of diverse ways with it and solve the problems referred to above---prevent that the glass fragment that has been staved further is damaged again.
The present invention seeks to: a kind of glass desk-top and manufacture method thereof with breaking proof protection is provided, and wherein, when glass desk-top has been broken, but its fragment can brokenly not loose more more tiny fragments, but still is attached on the protective layer.Its protective layer sticks to securely and forms one behind the tempered glass in the hole of central authorities, and, thereby bubble again can be between protective layer and tempered glass institute's projection extend to the periphery of desktop again.Because the high pressure of periphery is all concentrated to the central part of glass, thus central duck eye full wafer tempered glass most fragile part often partly, so the present invention has the anti-periphery that breaks the protective layer performance of effect at this desktop.
The glass desk-top of this open air use is produced fast, and is with low cost, can produce in enormous quantities.
A kind of glass desk-top of the present invention with breaking proof protection, it is characterized in that: this glass desk-top includes:
The tempered glass layer of one reservation shape and size; One by vinyl chlorination thing (PolyvinylChloride) or by the protective layer of plastics (Polyester) systems, its thickness approximately is 0.3 to 0.8 millimeter and has the identical shaped and size of tempered glass; Reach one by the made adhesion coating of acrylic acid (Acrylic); its thickness is preferably between 0.1 to 0.2 millimeter; and flatly place on the surface of tempered glass and under this protective layer, so, be combined into one with tempered glass with by vinyl chlorination thing or the protective layer that is made of plastics.
And concrete detailed saying, this glass desk-top with breaking proof protection comprises a tempered glass layer, a protective layer and an adhesion coating, and this tempered glass layer has the shape and a central hole of reserving in advance; This protective layer is by vinyl chlorination thing or plastics are made has 0.3 millimeter to 0.8 millimeter thickness and with this tempered glass layer identical width is arranged, this tempered glass layer normally has figured plate glass and uneven top surface is arranged, and there is the style of special decoration on this surface; This protective layer is intactly to be attached on the top surface of this tempered glass layer that central hole is arranged, wherein, the centre duck eye has the diameter identical with this central authorities hole and forms a centre hole with one heart with the central hole of this tempered glass layer among this protective layer, this adhesion coating is applied to the bottom of top surface He this protective layer of this tempered glass layer fifty-fifty, so, this protective layer and this tempered glass layer constipation integrator; And; those pulling force that are trapped among this protective layer peripheral portions increase to an edge protection; promptly should central authorities the periphery of duck eye circle trail from this tempered glass layer, guarantee that this peripheral portions round this central authorities' duck eye and protective layer entreats duck eye among attaching this tempered glass layer securely.
A kind of manufacture method with glass desk-top of breaking proof protection of the present invention has following steps:
(a) with neutral water, its pH value is 7 (neutrality), removes to clean a tempered glass laminar surface that is provided with a central hole, and greasy dirt etc. is removed;
(b) the broken glass layer of the reinforcement that will clean dries up;
(c) with full wafer tempered glass layer with 45 ℃ to the 65 ℃ processing of heating;
(d) apply fifty-fifty by the made adherent coating of acrylic acid and arrange in this temperature on 45 ℃ to 65 ℃ tempered glass laminar surface, thereby constitute an adhesion coating at the tempered glass laminar surface;
(e) be that 0.3 to 0.8 millimeter width protective layer bigger than this tempered glass layer is fitted in this temperature and remains on the tempered glass layer between 45 ℃ to 65 ℃ with a slice thickness, be combined into one up to this protective layer and this tempered glass layer, wherein, this protective layer is provided with a center partly in the position, central hole of this tempered glass layer;
(f) peripheral portions that this protective layer is had more cuts into measure-alike with tempered glass;
(g) center of this protective layer partly pressed down to increase to the central hole of tempered glass layer direction be attached at the peripheral portions in the central hole on this tempered glass layer, thus guarantee this center partly among this tempered glass layer the hole, centre stretch and attach.
(h) grind the top top in this tempered glass layer central authorities hole, partly form a concentric hole with the central hole of this guarantor's tempered glass layer up to the center of this protective layer.
Wherein, more comprise one in program (a) numerous tempered glass layers that reservation shape is arranged are provided.
Wherein, this program (a) more comprises one with the conglobate glassy layer of a sheet of glass-cutting and special decorative pattern is being arranged on the top and the tempered glass layer is heated between 500 ℃ to 550 ℃ and adding cold with 0 ℃ to-40 ℃ and constitute this tempered glass layer at least at once.
Wherein, this handling procedure (e) more comprises follow procedure (e-1) will be by the made adhesion coating of acrylic acid (Acrylic), and its thickness preferably is situated between in 0.1 to 0.2 millimeter, places fifty-fifty on the surface of tempered glass layer; (e-2) provide a volume continuous protective layer, it is that relatively this tempered glass layer is big for 0.3 millimeter to 0.8 millimeter its width that this protective layer has thickness; (e-3) end and the numerous tempered glass layer a slices that will roll up continuous protective layer followed on the roller that alternately is placed on pair of parallel of a slice; wherein, the continuous protective layer of this volume is to be attached to the top of this tempered glass layer to the thin layer with viscosity in overlapping mode.This pair roller post is arranged as the continuous protective layer of this volume is still kept the usefulness of 45 degree Celsius to the Celsius 65 tempered glass layers 11 of spending to the top pressurization to this; (e-4) will roll up continuous protective layer and be cut into the polylith protective layer according to the quantity of this tempered glass layer.
Wherein, this pair roller is a pair of rubber system roller.
Wherein, in (e-3) program, a pressure plare; before putting this corresponding roller into, should be placed on the top of this protective layer earlier, wherein; this pressure plare not monoenergetic is protected this protective layer, and can also become the pressure transfer of snare average pressure and protective layer is attached on this tempered glass layer.
Wherein, this pressure plare is the bedding and padding by rubber material or the made softness of foamed material.
Wherein, the bottom of the protective layer that this volume is continuous is providing one by the made adhesion coating of acrylic acid (Acrylic), is used as and guarantees that this protective layer can easily adhere on this tempered glass layer.
Wherein, in program (g), the pressure head of a circle is arranged, on the end partly of the center of this protective layer in order to dexterously this center is partly depressed to the central hole of this tempered glass layer.The inside pressure of this pressure head increases the pulling force of the peripheral portions of this protective layer, the inside pressure of this pressure head again a step this protective layer peripheral portions is entreated toward this tempered glass layer among the hole above limit portion stretching, extension and adhering to.
Wherein, in program (g), the pressure head of a circle is arranged on the central part one end of this protective layer, in order to dexterously this center is partly depressed to the central hole of this tempered glass layer.The inside pressure of this pressure head increases the pulling force of the peripheral portions of this protective layer, the inside pressure of this pressure head again a step this protective layer peripheral portions is entreated toward this tempered glass layer among the hole above limit portion stretching, extension and adhering to.
Wherein, in program (g), the pressure head of a circle is arranged on the central part one end of this protective layer, in order to dexterously this center is partly depressed to the central hole of this tempered glass layer.The inside pressure of this pressure head increases the pulling force of the peripheral portions of this protective layer, the inside pressure of this pressure head again a step this protective layer peripheral portions is entreated toward this tempered glass layer among the hole above limit portion stretching, extension and adhering to.
Wherein, in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing, person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separates with this protective layer and forms a centre hole with one heart with this tempered glass layer.
Wherein, in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing, person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separates with this protective layer and forms a centre hole with one heart with this tempered glass layer.
Wherein, in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing, person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separates with this protective layer and forms a centre hole with one heart with this tempered glass layer.
Wherein, in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing, person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separates with this protective layer and forms a centre hole with one heart with this tempered glass layer.
Wherein, in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing, person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separate with this protective layer and also forms a centre hole with one heart.
Wherein, in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing, person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separate with this protective layer and also forms a centre hole with one heart.
Wherein, the top surface of this tempered glass layer is had the neutral water of pH value to clean
The present invention has following accompanying drawing:
Fig. 1 is the cutaway view that a garden combines with the glass desk-top and the embodiment of the invention.
Fig. 2 is the manufacturing process table of the embodiment of the invention.
Fig. 3 is the perspective view of expressing its cutting process of the present invention.
Fig. 4 be the embodiment according to the present invention express its protective layer how ideally with this tempered glass laminating sectional view together.
Fig. 5 is a flow chart of producing this central, circular duck eye method according to the present invention's embodiment.
Now lift preferred embodiment and conjunction with figs. is described as follows:
Please be illustrated in figures 1 and 2, the glass desk-top 10 that garden of the present invention is used comprises a tempered glass layer 11, one protective layer 12 and an adhesion coating 13.This tempered glass has reservation shape, thickness, width and is provided with a hole 121 in central authorities.This protective layer 12 is made by vinyl chlorination thing or plastics, and its thickness has 0.3 millimeter to 0.8 millimeter also with this tempered glass layer 11 identical width to be arranged.
This tempered glass layer 11 normally is used as figuratum glass and uneven top surface 112 is arranged, and there is the style of special decoration on this surface.This protective layer 12 is intactly to be attached on the top surface 112 of this tempered glass layer 11 that central hole 121 is arranged.Wherein, among this protective layer 12 hole 121, centre have the diameter identical 111 with this central authorities' duck eye and dexterously with the central hole 111 of this tempered glass layer 11 in line.This adhesion coating has thickness Jie to accord with between 0.1 millimeter to 0.2 millimeter; this adhesion coating is made by acrylic acid bur or identical material; this adhesion coating is by the bottom 122 of the average top surface that is applied to this tempered glass layer 12 112 and this protective layer 12; so, this protective layer 12 and tempered glass layer 11 constipation integrator.And; those pulling force increases that are trapped among these protective layer 12 peripheral portions 123 become an edge protection 124; promptly should trail from this tempered glass layer by central authorities hole 121 round peripheries; this part is the part of full wafer tempered glass most fragile; because the high pressure of periphery is all concentrated to the middle body of glass, and guarantee that this peripheral portions 123 round this central authorities hole 121 and protective layer 12 connects securely and pasting hole 111 among this tempered glass layer 11.
According to Fig. 1 to Fig. 5,, above-mentionedly can finish according to follow procedure relevant outdoor desktop structure 10 for a large amount of productions:
(a) provide numerous tempered glass layers 11, each piece tempered glass and this mesopore 111 all have predetermined shape and width.This program (a) further comprises again cuts conglobate glassy layer with a sheet of glass plate and is heated to 500 degree Celsius at least in the style that special decoration is arranged on the top 112 with this tempered glass layer 11 between 550 degree Celsius, and at once adds cold this mesopore 111 that makes with zero centigrade to 40 degrees below zero Celsius and can be cut out.
(b) be that the water cleaning of 7 (promptly neutral) is clean with the ph value fully to the top 112 of each piece tempered glass layer 11 of major general, and possible greasy dirt is removed.
(c) the tempered glass layer 11 that all is cleaned up is dried up.
(d) full wafer tempered glass layer 11 is heated between 45 ℃ to 65 ℃.
(e) protective layer 12 its width that this sheet thickness is about 0.3 to 0.8 millimeter be relatively this tempered glass layer 11 be placed on greatly this temperature remain on 45 ℃ to 65 ℃ between tempered glass layer 11 on; form one up to this protective layer 12 and this tempered glass layer 11; wherein, this protective layer 12 has a circular part 120 in centre on the mesopore 111 of this tempered glass layer 12.
According to shown in Figure 2, this program (e) further comprises follow procedure again:
(e-1) will place its temperature of each sheet to be situated between fifty-fifty and accord with on the surface of this tempered glass layer 11 between 45 degree Celsius and 65 degree Celsius and on this protective layer 112 by the made adhesion coating of acrylic acid (Acrylic).
(e-2) provide a volume continuous protective layer 12, it is 0.3 millimeter to 0.8 millimeter that this protective layer has thickness, and its width relatively this tempered glass layer 11 is big.
(e-3) will roll up an end of continuous protective layer 12 and the rubber roll that alternately is placed on pair of parallel 21 that numerous tempered glass layer 11 a slices are followed a slice; on 22, wherein the continuous protective layer 12 of this volume is to depend in overlapping mode to be arranged on the top of this tempered glass layer 11 to the thin layer 13 with viscosity.This is arranged as the continuous protective layer 12 of this volume is still kept the usefulness of tempered glass layer 11 111 pressurizations to the top of 45 ℃ to 65 ℃ to this rubber roll 21,22.
(e-4) as shown in Figure 3, this volume is continuous protective layer 12 quantity according to this tempered glass layer are cut into polylith protective layer 12.
(f) as shown in Figure 3, wipe out the peripheral portions of unnecessary protective layer 12 up to the shape of this protective layer 12 identical with the shape of this tempered glass layer 11.
(g) as Fig. 2, shown in Figure 3, first central duck eye 121 of each block protection layer 12 dexterously with the central duck eye 112 of this tempered glass layer 11 and paste and constitute outdoor glass desktop 10.According to the present invention, this program (g) further comprises follow procedure again:
(g-1) center of this protective layer 12 partly 120 is depressed increasing the peripheral portions that this is attached near the protective layer 12 of the mesopore 111 the tempered glass layer 11 to the direction of the mesopore 111 of tempered glass layer 11, thereby guarantee that this peripheral portions hole 111 among this tempered glass layer 11 stretches and depending on.(g-2) the top limit portion in hole 111 among this tempered glass layer 11 being ground up to the center of this protective layer 12 partly 120 separates also with the centre hole 121 of this protective layer 12 and the mesopore 111 of this tempered glass layer 11 couples together dexterously.
This g program as shown in Figure 5, is the centre hole 121 that a specially designed program constitutes the present invention.Be noted that this center 120 is not directly to be cut out by this protective layer 12 and form centre hole 121 partly.If this is because this center partly 120 is directly cut out by protective layer 12, so, just the face limit portion on this centre hole 111 that is attached to that the periphery of this centre hole 121 will can not be fit to.So further polish process may need the peripheral portions cutting of this centre hole 121 is removed again.And directly this this center part 120 can cause the peripheral portions that some bubbles and the limit portion that can make this centre hole elongate this glass desk-top through be everlasting this tempered glass layer 11 and protective layer 12 by cutting out in this protective layer 12.
According to the present invention, need not make any cutting by this centre hole 121.Wherein, program (g-1) as shown in Figure 5, has the pressure head 21 of a circle on the one end, in order to dexterously this center partly 120 is depressed to the central hole of this tempered glass layer 11.The inside pressure of this pressure head 21 increases the pulling force of the peripheral portions 123 of this protective layer 12.And, because the lower surface 122 of this protective layer 12 may also provide an adhesion coating, the inside pressure of this pressure head 21 again a step protective layer 12 peripheral portions 123 toward top limit portion's stretching, extension of these this mesopores 111 of tempered glass layer with depending on.
Then; in (g-2) program; there is the polishing wheel that is rotating to be used as this centre hole 111 upper strata limit portion of polishing; in the person, just relatively with this center partly 120 peripheral thickness reduce up to this protective layer 12 be the center partly 120 separate with this protective layer 12 and form a centre hole 121 also dexterously with this tempered glass layer 11 among hole 111 connect together.With this program (g) see through to press by and grind the method that constitutes this centre hole 121, can be at one time, eliminate completely at the uneven stickup pulling force on the protective layer 12 and go to prevent those to break bubbles between glass layer 11 and this protective layer 12 in this reinforcements.
Perhaps, because this protective layer 12 is thin films, and most tempered glass layer 11 of manufacturing outdoor glass desktop that is used as is all from the teeth outwards with motif, as shown in Figure 4.Guarantee that if desired this protective layer 12 is to be affixed under the average pulling force on this tempered glass layer 11 completely, should (e-3) program can be revised as the roller 21 of using a correspondence ", 22 " replace this to rubber roll.But; one pressure plare 30; for example a hard card plate or is with the bedding and padding system of foamed material or the made softness of rubber material and about 2 millimeters thickness is arranged; before putting this corresponding roller into 21 "; 21 ", should be placed on the top of this protective layer 12 earlier, wherein; this pressure plare 30 is single can only protect this protective layer 12, and can also be being applied in this pressure head 21 more greatly ", 22 " pressure transfer become average pressure so that protective layer is attached on this tempered glass layer 11.
According to above-mentioned explanation; when this outdoor glass desktop 10 is broken and when becoming fragment, the top surface of the glass fragment that each piece is broken still can other be attached on this protective layer 12 and prevented that those destroyed glass fragments from falling or degree of being subjected to further destroys.In other words, the invention provides one very effective method go to solve general common glass breakage problem.And a large amount of fast and cheap methods that provide of producing are provided this outdoor glass desktop fabrication schedule.
Claims (19)
1, a kind of manufacture method with glass desk-top of breaking proof protection, it is characterized in that: it has following program:
(a) the tempered glass layer end face that is provided with a central hole cleaned up;
(b) the tempered glass layer that this is cleaned up dries up;
(c) this tempered glass layer is heated to 45 ℃ to 65 ℃;
(d) apply fifty-fifty thin layer by the made viscosity of acrylic acid in this temperature on the surface of the tempered glass layer between 45 ℃ and 65 ℃, thereby constitute an adhesion coating.
(e) be that 0.3 to 0.8 millimeter width protective layer big than this tempered glass layer fits in this temperature and remains on the tempered glass layer between 45 ℃ to 65 ℃ with a slice thickness; be combined into one up to this protective layer and this tempered glass layer; wherein, this protective layer also is provided with a center partly in centre on respect to the central hole of tempered glass layer.
(f) the peripheral portions well cutting that this protective layer is had more measure-alike up to this tempered glass layer;
(g) center of this protective layer is partly pressed down the peripheral portions that is attached at the central hole of this tempered glass layer with increase to the direction in the central hole of tempered glass layer, thereby guarantee that this center partly stretches and attaching to the central hole of this tempered glass layer.
(h) grind the top top of this tempered glass layer centre hole, partly separate up to the center of this protective layer and form a centre hole with one heart with this tempered glass layer with the central hole of this protective layer.
2, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 1 is characterized in that: wherein, this program (a) more comprises one provides numerous tempered glass layers that reservation shape is arranged.
3, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 2; it is characterized in that: wherein, this program (a) more comprises one with the conglobate glassy layer of a sheet of glass-cutting and special decorative pattern is being arranged on the top and the tempered glass layer is heated between 500 ℃ to 550 ℃ and adding cold with 0 ℃ to-40 ℃ and constitute this tempered glass layer at least at once.
4, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 2, it is characterized in that: wherein, this program (e) more comprises follow procedure (e-1) will be by the made adhesion coating of acrylic acid (Acrylic), its thickness preferably is situated between in 0.1 to 0.2 millimeter, places fifty-fifty on the surface of tempered glass layer; (e-2) provide a volume continuous protective layer, it is that relatively this tempered glass layer is big for 0.3 millimeter to 0.8 millimeter its width that this protective layer has thickness; (e-3) end and the numerous tempered glass layer a slices that will roll up continuous protective layer followed on the roller that alternately is placed on pair of parallel of a slice, wherein, the continuous protective layer of this volume is to be attached to the top of this tempered glass layer to the thin layer with viscosity in overlapping mode; This pair roller post is arranged as the continuous protective layer of this volume is still kept the usefulness of 45 degree Celsius to the Celsius 65 tempered glass layers of spending to the top pressurization to this; (e-4) will roll up continuous protective layer and be cut into the polylith protective layer according to the quantity of this tempered glass layer.
5, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 4, it is characterized in that: wherein, this pair roller is a pair of rubber system roller.
6, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 4; it is characterized in that: wherein; in (e-3) program; one pressure plare; before putting this corresponding roller into, should be placed on the top of this protective layer earlier, wherein; this pressure plare not only can be protected this protective layer, and can also become the pressure transfer of snare average pressure and protective layer is attached on this tempered glass layer.
7, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 1, it is characterized in that: wherein, this pressure plare is the bedding and padding by rubber material or the made softness of foamed material.
8, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 1; it is characterized in that: wherein; the bottom of the protective layer that this volume is continuous is providing one by the made adhesion coating of acrylic acid (Acrylic), is used as to guarantee that this protective layer can easily adhere on this tempered glass layer.
9, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 1, it is characterized in that: wherein, in program (g), the pressure head that one circle is arranged on the end partly of the center of this protective layer is in order to partly to depress this center dexterously to the central hole of this tempered glass layer; The inside pressure of this pressure head increases the pulling force of the peripheral portions of this protective layer, the inside pressure of this pressure head again a step this protective layer peripheral portions is entreated toward this tempered glass layer among the hole above limit portion stretching, extension and adhering to.
10, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 4, it is characterized in that: wherein, in program (g), the pressure head that one circle is arranged on the central part one end of this protective layer is in order to partly to depress this center dexterously to the central hole of this tempered glass layer; The inside pressure of this pressure head increases the pulling force of the peripheral portions of this protective layer, the inside pressure of this pressure head again a step this protective layer peripheral portions is entreated toward this tempered glass layer among the hole above limit portion stretching, extension and adhering to.
11, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 7; it is characterized in that: wherein; in program (g); the pressure head that one circle is arranged on the central part one end of this protective layer; in order to dexterously this center is partly depressed to the central hole of this tempered glass layer; the inside pressure of this pressure head increases the pulling force of the peripheral portions of this protective layer, the inside pressure of this pressure head again a step this protective layer peripheral portions is entreated toward this tempered glass layer among the hole above limit portion stretching, extension and adhering to.
12, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 1; it is characterized in that: wherein; in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing; person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separates with this protective layer and forms a centre hole with one heart with this tempered glass layer.
13, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 4; it is characterized in that: wherein; in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing; person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separates with this protective layer and forms a centre hole with one heart with this tempered glass layer.
14, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 7; it is characterized in that: wherein; in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing; person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separates with this protective layer and forms a centre hole with one heart with this tempered glass layer.
15, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 9; it is characterized in that: wherein; in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing; person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separates with this protective layer and forms a centre hole with one heart with this tempered glass layer.
16, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 1; it is characterized in that: wherein; in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing; person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separate with this protective layer and also forms a centre hole with one heart.
17, a kind of manufacture method with glass desk-top of breaking proof protection according to claim 11; it is characterized in that: wherein; in program (h); there is the polishing wheel that is rotating to be used as this centre hole upper strata limit portion of polishing; person in this way, just relatively this center peripheral thickness partly being reduced up to this protective layer is that the center partly separate with this protective layer and also forms a centre hole with one heart.
18, according to claim 1 or 4 or 7 or 9 to 17 described a kind of manufacture methods with glass desk-top of breaking proof protection, it is characterized in that: wherein, the top surface of this tempered glass layer is had the neutral water of pH value to clean
19, a kind of glass desk-top with breaking proof protection is characterized in that: this glass desk-top with breaking proof protection comprises a tempered glass layer, a protective layer and an adhesion coating, and this tempered glass layer has the shape and a central hole of reserving in advance; This protective layer is by vinyl chlorination thing or plastics are made has 0.3 millimeter to 0.8 millimeter thickness and with this tempered glass layer identical width is arranged, this tempered glass layer normally has figured plate glass and uneven top surface is arranged, and there is the style of special decoration on this surface; This protective layer is intactly to be attached on the top surface of this tempered glass layer that central hole is arranged, wherein, the centre duck eye has the diameter identical with this central authorities hole and forms a centre hole with one heart with the central hole of this tempered glass layer among this protective layer, this adhesion coating is applied to the bottom of top surface He this protective layer of this tempered glass layer fifty-fifty, so, this protective layer and this tempered glass layer constipation integrator; And; those pulling force that are trapped among this protective layer peripheral portions increase to an edge protection; promptly should central authorities the periphery of duck eye circle trail from this tempered glass layer, guarantee that this peripheral portions round this central authorities' duck eye and protective layer entreats duck eye among attaching this tempered glass layer securely.