CN114100594A - Cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material and preparation method thereof - Google Patents

Cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material and preparation method thereof Download PDF

Info

Publication number
CN114100594A
CN114100594A CN202111425631.4A CN202111425631A CN114100594A CN 114100594 A CN114100594 A CN 114100594A CN 202111425631 A CN202111425631 A CN 202111425631A CN 114100594 A CN114100594 A CN 114100594A
Authority
CN
China
Prior art keywords
cerium
zirconium
aluminum
catalytic material
composite catalytic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN202111425631.4A
Other languages
Chinese (zh)
Other versions
CN114100594B (en
Inventor
胡安明
孟祥光
齐悦
任昕
王斐
沈小艳
吕婧
陈黄琳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan University
Original Assignee
Sichuan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sichuan University filed Critical Sichuan University
Priority to CN202111425631.4A priority Critical patent/CN114100594B/en
Publication of CN114100594A publication Critical patent/CN114100594A/en
Application granted granted Critical
Publication of CN114100594B publication Critical patent/CN114100594B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, which consists of cerium-zirconium oxide nano particles and aluminum oxide micro particles, wherein the cerium-zirconium oxide nano particles are dispersedly loaded on the surface of the outer layer of the aluminum oxide micro particles to form a core-shell structure type composite catalytic material; the preparation method comprises the following steps: (1) preparing a micron-particle aluminum oxide material; (2) synthesizing cerium zirconium oxide nano material sol; (3) mixing the alumina micron particle material prepared in the step (1) with the cerium zirconium oxide nano material sol synthesized in the step (2) to generate slurry, and drying and roasting to obtain the granular cerium zirconium-aluminum based oxide micro-nano composite catalytic material; (4) coating the cerium zirconium-aluminum-based oxide micro-nano composite catalytic material obtained in the step (3) on a substrate after pulping, and drying and roasting to obtain a coated cerium zirconium-aluminum-based oxide micro-nano composite catalytic material; the supported noble metal is used for preparing the tail gas purifying catalyst of the fuel oil vehicle and other industrial catalysts.

Description

Cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material and preparation method thereof
Technical Field
The invention relates to a cerium-zirconium-aluminum-based oxide catalytic material and a preparation method thereof, in particular to a cerium-zirconium-aluminum-based oxide catalytic material prepared from a tail gas purification catalyst of a fuel vehicle and the like and other industrial catalysts and a preparation method thereof.
Background
The cerium-zirconium-aluminum-based oxide catalytic material is a catalytic material commonly used in a high-temperature resistant catalyst, for example, for manufacturing a three-way catalyst or a three-way catalyst (TWC) for purifying the tail gas of a gasoline vehicle, wherein alumina (Al)2O3) As a support material for the noble metal active component; cerium zirconium oxide (CeO)2-ZrO2CO-solvent) is used as both a carrier and an oxygen storage/release material, and oxygen is absorbed when the exhaust gas is rich in oxygen and released when the exhaust gas is poor in oxygen to maintain dynamic oxygen balance to enlarge the air/fuel ratio window, so that the reactions of removing CO and HC by oxidation and removing NOx by reduction can simultaneously occur, and thus the catalyst is considered as a key material of a three-way catalyst. A diesel exhaust purification oxidation catalyst (DOC), a fuel vehicle particulate filter catalyst (DPF, GPF), and the like are also used as the cerium-zirconium-aluminum-based oxide catalytic material. In addition, the noble metal supported catalyst such as petroleum cracking catalyst, hydrogenation catalyst, etc. can also be used as the cerium-zirconium-aluminum-based oxide catalytic material. The alumina used for the catalytic material has high thermal stability, and the specific surface area is 50-150 m mostly according to different roasting temperatures and time2The grain size is 1-25 mu m; the cerium-zirconium oxide has low thermal stability and a specific surface area of 20-70 m2The particle size of the particles is 1 to 25 μm. The type of the catalytic material composed of alumina and cerium zirconium oxide mainly includes three types of mixed type, miscible type and mixed leaching type.
The mixed cerium-zirconium-aluminum-based oxide catalytic material is prepared by mixing aluminum oxide and cerium-zirconium oxide microparticles, and is prepared by loading noble metals (Pt, Pd and Rh) or respectively loading noble metals and then mixing or coating the noble metals in layers, and is widely used for manufacturing three-way catalysts. For example, patent CN1032749(1989.05.10) discloses "rhodium-free three-way catalyst"; CN1413769(2003.04.30) discloses a three-way catalyst for automobile exhaust and a preparation method thereof; CN1824384(2006.08.30) discloses "high performance low noble metal three-way catalyst"; CN101161337(2008.04.16) discloses "a three-way catalyst and its preparation method"; CN101433846(2009.05.20) discloses a cerium-based composite oxide supported noble metal three-way catalyst and a preparation method thereof; CN102430403A (2012.05.02) discloses 'a low-precious metal content high-efficiency three-way catalyst and a preparation method thereof'; CN103143351A (2013.06.12) discloses "three-way catalyst"; CN104254387A (2014.12.31, priority date 2012.04.27) discloses "filter substrate containing three-way catalyst"; CN104334255A (2015.02.04, priority date 2012.06.06) discloses a "three-way catalyst system"; CN107206358A (2017.09.26, priority date 2015.02.06) discloses "three-way catalyst and its application in exhaust system"; CN107107037A (2017.08.29, priority date 2015.01.19) published "double-layer three-way catalyst with improved aging stability"; CN109153010A (2019.01.04, priority date 2016.05.25) discloses "a three-way catalyst for purifying exhaust gas of a gasoline engine"; CN111491731A (2020.08.04, priority date 2018.02.22) discloses a "three-way catalyst for exhaust gas purification" and the like. Wherein the cerium-zirconium oxide accounts for 30-60 wt% of the cerium-zirconium-aluminum-based oxide catalytic material.
The mixed cerium-zirconium-aluminum-based oxide catalytic material is prepared by neutralizing and precipitating a mixed solution of cerium salt, zirconium salt and aluminum salt with alkali, washing, drying and roasting. For example, patent CN101094810(2007.12.26, priority 2004.12.30GB) discloses "a composite oxide for automotive catalysts and comprising alumina and zirconia and optionally ceria"; CN1695798(2005.11.16) discloses "cerium-zirconium-aluminum-based oxygen storage material and preparation method thereof"; CN101745375A (2010.06.23) discloses "cerium-zirconium-aluminum-based composite oxide material and its preparation method"; CN102824904A (2012.12.19) discloses an aluminum cerium zirconium composite oxide catalytic material and a preparation method thereof; CN103619468A (2014.03.05, priority 2011.07.01EP) discloses "ceria-zirconia-alumina composition with enhanced thermal stability"; CN104226295A (2014.12.24) discloses a cerium-zirconium-aluminum composite oxide, a gasoline car tail gas three-way catalyst and a preparation method thereof; CN109569566A (2019.04.05) discloses "cerium-zirconium-aluminum composite oxygen storage material and its preparation method"; CN110366445A (2019.10.22, priority 2016.12.23EP) discloses "anti-aging mixed oxides made of cerium, zirconium, aluminum and lanthanum for catalytic converters of motor vehicles"; CN110586145A (2019.12.20) discloses "a cerium-zirconium-aluminum composite material with high thermal stability, its preparation method and application". Wherein, the cerium zirconium oxide accounts for about 30 to 60 weight percent of the cerium zirconium aluminum-based oxide catalytic material.
The mixed-soaking type cerium-zirconium-aluminum-based oxide catalytic material is prepared by soaking alumina microparticles in a mixed solution of cerium salt and zirconium salt, and performing alkali neutralization precipitation, washing, drying and roasting, or directly drying and roasting. Wherein part of cerium and zirconium salt is immersed in the inner holes of the alumina particles, part of the salt is outside the particles, and is agglomerated into hydroxide after being neutralized by alkali, and the mixture of part of cerium zirconium oxide particles and alumina particles containing part of cerium zirconium oxide is obtained after roasting. If the alumina is impregnated by the concentrated cerium and zirconium salt solution, more cerium and zirconium salt enter the pores of the alumina particles, part of the salt is outside the particles and is agglomerated into particles when being concentrated to the saturation solubility in the drying process, and the mixture of part of cerium-zirconium oxide particles and alumina particles containing more cerium-zirconium oxide is still obtained after roasting. In addition, when cerium nitrate or zirconium nitrate is used, NOx generation after firing causes pollution. The mixed-leaching type catalytic material has poor performance and is not frequently used.
The common problem of the above mixed, miscible and mixed-impregnated cerium-zirconium-aluminum-based oxide catalytic materials is that if the amount of cerium-zirconium oxide is less than about 30 wt% (the amount of alumina is greater than about 70 wt%), the thermal resistance of the catalytic material is favorable and the oxygen storage/release function is not favorable, and it is difficult to effectively realize three-way catalysis; if the cerium zirconium oxide is used in an amount of more than about 30 wt% (the amount of alumina is less than about 70 wt%), it is advantageous for the oxygen storage/release effect of the catalytic material but disadvantageous for the heat resistance, resulting in insufficient durability of the catalyst, i.e., "fish and bear paw cannot be used concurrently". Meanwhile, the catalytic materials are all micron particles, most of cerium zirconium oxide is wrapped in the micron particles, the utilization rate is low when the catalyst is used, and the rapid oxygen storage/release effect is difficult to play. The prior art at home and abroad at present is difficult to solve the problems, and technical innovation is urgently needed.
Disclosure of Invention
The invention aims to make up for the defects of the prior art and provides a cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material and a preparation method thereof, which are used for solving the problems that fish and bear palms cannot be obtained simultaneously and the rapid oxygen storage/release is difficult.
In order to achieve the purpose, the invention adopts the following technical scheme.
A cerium zirconium-aluminum-based oxide micro-nano composite catalytic material is formed by nano self-assembly of cerium zirconium oxide nano particles and active alumina micro particles, wherein the cerium zirconium oxide nano particles are dispersed and loaded on the surface of the outer layer of the active alumina micro particles to form a core-shell structure type granular micro-nano composite catalytic material, and a coating-shaped micro-nano composite catalytic material coated on a substrate and marked as CeZrO @ Al2O3
The cerium-zirconium oxide nano particles are prepared from aqueous dispersion nano material sol, wherein the cerium-zirconium oxide is nano particle single crystals, the nano scale is 2-8 nm, the mass/volume percentage content in the sol is 1.0-20% (w/V), and the mass/volume percentage content is marked as CexZr1-xO2And x is 0.0 to 1.0. The activated alumina is gamma-Al2O3Rare earth oxide stabilized Al2O3One or more of the compositions are polycrystal particles with the granularity of 0.1-25 mu m; in the cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, the cerium-zirconium oxide accounts for 1.0-30 wt% of the composite catalytic material, and contains metal oxides, wherein the metal oxides comprise one or more of Ca, Sr, Ba, Sc, Y, La, Pr, Nd and Sm oxides as an auxiliary agent, and the cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material accounts for 0.0-20 wt% of the catalytic material.
The preparation method of the cerium zirconium-aluminum based oxide micro-nano composite catalytic material comprises the following steps.
(1) Preparation of micron-sized particulate alumina (Al)2O3) The micron scale is 0.1-25 μm, and the specific surface area is 50-200 m2The catalyst comprises 0.0-10 wt% of metal oxide auxiliary agent in mass percentage of oxide.
(2) Synthesizing aqueous dispersed cerium-zirconium oxide nano material sol, wherein the cerium-zirconium oxide is nano particle single crystal, the nano scale is 2-8 nm, the mass/volume percentage content in the sol is 1.0-20% (w/V), and the mass/volume percentage content is marked as CexZr1- xO2X is 0.0 to 1.0; wherein the metal oxide auxiliary agent is contained and accounts for 0.0-10 wt% of the mass of the oxide.
(3) And (3) mixing the alumina micron particle material prepared in the step (1) with the aqueous dispersion cerium-zirconium oxide nano material sol synthesized in the step (2) to generate slurry, drying and roasting to obtain the granular cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, wherein the cerium-zirconium oxide accounts for 1.0-30 wt% of the composite catalytic material.
(4) And (3) coating the slurry generated in the step (3) or the granular cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material on a substrate after pulping, drying and roasting to obtain the coated cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, wherein the substrate is a cordierite honeycomb ceramic substrate or an FeCrAl honeycomb metal substrate.
Wherein in the drying step (3), the temperature is raised from room temperature to 120 ℃ at the heating rate of 1-10 ℃/min and is kept constant for 1-3 h, the temperature is kept constant for 1-3 h at 500-600 ℃ in the roasting step, and then the temperature is lowered to room temperature; and (4) drying, namely heating the cerium zirconium-aluminum-based oxide micro-nano composite catalytic material from room temperature to 500 ℃ at a heating rate of 1-10 ℃/min, keeping the temperature of the roasting at 500-1000 ℃ for 1-24 h, and then cooling to room temperature, wherein the solid content of the slurry in terms of the total amount of metal oxides is 30-50 g/100ml, and the coating amount of the cerium zirconium-aluminum-based oxide micro-nano composite catalytic material on a substrate is 50-300 g/L.
According to the cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material and the preparation method thereof, the cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material is used for manufacturing tail gas purification catalysts of fuel vehicles and fuel general engines and other industrial catalysts by loading one or more of noble metals Pt, Pd, Rh, Au, Ir and Ru.
Compared with the prior art, the invention has the following beneficial effects.
In the cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, the dosage of the cerium-zirconium oxide is lower than 30 wt%, the dosage of the aluminum oxide is higher than 70 wt%, and the heat resistance of the aluminum oxide is greatly higher than that of the cerium-zirconium oxide, so that the heat resistance of the catalytic material can be greatly improved, and the durability of the catalyst is improved; on the other hand, as the cerium-zirconium oxide nano particles are dispersedly loaded on the surface of the outer layer of the alumina micro particles, the utilization rate is greatly improved, thereby improving the oxygen storage/release function and playing a role in rapidly storing/releasing oxygen. Therefore, the problem that fish and bear paw can not be obtained simultaneously is solved, and if the catalyst is used for purifying the tail gas of the gasoline car, the three-way catalysis can be effectively realized, and the durability of the catalyst is greatly improved.
Drawings
FIG. 1a) is a schematic diagram of a cerium zirconium-aluminum based oxide micro-nano composite catalytic material prepared by the invention; b) is a schematic diagram of a conventional mixed catalytic material of cerium zirconium-aluminum-based oxide. Wherein CeZrO is Ce, Zr and doped metal oxide, and AlO is Al and doped metal oxide.
Fig. 2a) is a photoelectron spectroscopy (XPS) graph and a surface atomic concentration of the micro-nano composite catalytic material prepared in example 4 according to the embodiment of the present invention; b) a photoelectron spectroscopy (XPS) graph and its surface atomic concentration of the conventional mixed catalytic material prepared for comparative example 4.
Fig. 3a) is a Temperature Programmed Reduction (TPR) diagram of the micro-nano composite catalytic material prepared in example 5 in the embodiment of the present invention, and b) is a Temperature Programmed Reduction (TPR) diagram of the conventional hybrid catalytic material prepared in comparative example 5.
Detailed Description
The cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material and the preparation method thereof are further described by the following specific embodiment in combination with the attached drawings.
A cerium zirconium-aluminum-based oxide micro-nano composite catalytic material is formed by nano self-assembly of cerium zirconium oxide nano particles and active alumina micro particles, wherein the cerium zirconium oxide nano particles are dispersed and loaded on the outer layer surface of the active alumina micro particles to form a core-shell structure type granular micro-nano composite catalytic material, and a coating-shaped micro-nano composite catalytic material coated on a substrate and marked as CeZrO @ Al2O3. Wherein the alumina is a porous material which can be prepared by self or obtained from commercial products, and the particle size D90 (the particle size range of more than 90 wt% by mass) is 0.1-25 μm, preferably 0.1-15 μm, and more preferably 0.5-10 μm; a specific surface area (BET method) of 50 to 200m2Per g, preferably 100-180 m after roasting at 600 ℃ for 5h2(ii)/g, more preferably 140 to 160m2/g。
The preparation of alumina is known to be well established, such as precipitation and peptization. The precipitation method comprises reacting aluminum salt (such as aluminum nitrate and aluminum trichloride) solution with alkaline solution (such as ammonia water and sodium hydroxide solution) to generate precipitate, filtering, washing, pulping, drying, and spraying to obtain alumina precursor powder; the peptization method is to add pseudo-boehmite (AlO (OH)) into acid (such as dilute nitric acid) to form colloid, then prepare slurry, and dry and spray the slurry to obtain alumina precursor powder. Drying the powder and roasting at about 500 ℃ to obtain gamma-Al2O3. In order to obtain gamma-Al with higher specific surface area2O3The addition of a certain amount of high polymer (such as polyethylene glycol and polyvinyl alcohol) in the spray slurry can play a role in pore-forming and increasing the specific surface area. gamma-Al2O3The specific surface area of the catalyst is rapidly reduced along with the rise of roasting or use temperature, in order to increase the thermal stability of the catalyst, one or more of alkaline earth or rare earth oxides such as Ca, Sr, Ba, Sc, Y, La, Pr, Nd and Sm oxides can be doped as an auxiliary agent, and the content of the auxiliary agent is 0.0-10 wt%; preferably oxides of higher atomic weight, more preferably Ba oxides and La oxides as doping aids, and in Al2O3The content of the aluminum oxide is 1-8 wt%, preferably 3-5 wt%, and the thermally stable aluminum oxide Al is obtained2O3The specific surface area can reach 140-160 m after roasting for 5 hours at 600 DEG C2(ii) in terms of/g. Further, gamma-Al2O3Or thermally stable Al2O3The particle size and the morphology of the particles are mainly related to the conditions of drying and spraying, and the required particle size and morphology are obtained by adjusting the spraying conditions.
The raw material of the cerium-zirconium oxide nano-particles is aqueous dispersion nano-material sol, wherein the cerium-zirconium oxide is nano-particle single crystals with the nano-scale of 2-8 nm, the mass percentage of the cerium-zirconium oxide single crystals in the sol is 1.0-20 wt%, and the cerium-zirconium oxide single crystals are marked as CexZr1-xO2X is 0.0 to 1.0; the cerium zirconium oxide composite material contains metal oxides, one or more of Ca, Sr, Ba, Sc, Y, La, Pr, Nd and Sm oxides are used as auxiliaries, and the mass percentage of the metal oxides in the cerium zirconium oxide composite material is 0.0-10 wt%.
The synthesis process of cerium-zirconium oxide water dispersed nanometer material sol is further improved with the method of the invention patent CN 104591275B, and includes the following steps: (1) carrying out precipitation reaction on an inorganic salt aqueous solution of Ce and Zr and an inorganic alkali aqueous solution to prepare a Ce-Zr mixed hydroxide precipitate; (2) heating and refluxing the Ce-Zr mixed hydroxide precipitate to prepare a Ce-Zr hydroxide eutectic; (3) filtering and washing the Ce-Zr hydroxide eutectic to prepare Ce-Zr hydroxide hydrogel; (4) mixing the Ce-Zr hydroxide hydrogel with aqueous solution of organic alcohols, organic acids and high polymers to prepare Ce-Zr oxide synthetic slurry; (5) heating the Ce-Zr oxide synthetic slurry and carrying out one-step hydro-thermal synthesis to obtain aqueous medium dispersion cerium-zirconium oxide nano material sol, wherein the mass percentage of the cerium-zirconium oxide is 8-12 wt%; (6) and further evaporating and concentrating the sol, or diluting with water to obtain the cerium zirconium oxide with the mass percentage of 1.0-20 wt% in the sol.
To a specified composition CexZr1-xO2(x is 0.0 to 1.0) synthesis of nanomaterial by preparing and mixing aqueous solution of inorganic salts of Ce and Zr, and diluting with water until the total concentration of Ce and Zr ions is 0.2 to 2.0 mol.L-1Preferably 0.5 to 1.0 mol.L-1. Preparing aqueous solution of inorganic alkali, and making precipitation reaction according to the amount of Ce salt and Zr saltThe pH value of the end point is 7-8; the volume of the inorganic alkali aqueous solution is equivalent to that of the inorganic salt aqueous solution of Ce and Zr, and the amount concentration of the substance is 0.5-2.5 mol.L-1Preferably 1.0 to 2.0 mol.L-1
And carrying out precipitation reaction on the inorganic alkali aqueous solution and the inorganic salt aqueous solution of Ce and Zr under stirring, wherein positive single titration, reverse single titration or parallel flow titration can be adopted, and the titration end point pH is 7-10, preferably the pH is 7-8. And carrying out precipitation reaction to obtain a suspension of the Ce-Zr mixed hydroxide precipitate. Before the precipitation reaction, a certain volume of hydrogen peroxide is added into the aqueous solution of the inorganic salts of Ce and Zr or the aqueous solution of inorganic bases, the amount of the added hydrogen peroxide is 0.5-2.0 times, preferably 0.6-1.0 times of that of the cerium, and the precipitate is brown yellow.
In order to dope in the aqueous medium dispersion cerium zirconium oxide nano material, the selected water-soluble inorganic salt doped with metal is added into the inorganic salt aqueous solution of Ce and Zr to prepare a mixed aqueous solution, and then precipitation reaction is carried out. The doped metal comprises one or more of Ca, Sr, Ba, Sc, Y, La, Pr, Nd and Sm, preferably one or more of Sc, Y, La, Pr, Nd and Sm, and the mass percentage of the oxide of the doped metal in the total oxide is 0.0-10 wt%.
And heating and stirring the Ce-Zr mixed hydroxide precipitate or the M-doped mixed hydroxide precipitate turbid liquid obtained by the precipitation reaction at 60 ℃, adding water-soluble organic alcohol to mix with the Ce and Zr mixed hydroxide precipitate turbid liquid, then carrying out heating reflux treatment under stirring, wherein the heating reflux temperature is 90-105 ℃, carrying out reflux treatment for 1-8 h, preferably 2-5 h, and then cooling to room temperature to obtain the Ce-Zr hydroxide co-solution turbid liquid. The volume of the added organic alcohol accounts for 0-30% of the total volume of the mixed solution, and the amount of the added organic alcohol enables the boiling point temperature during reflux not to exceed 105 ℃.
Stirring and dispersing the Ce-Zr hydroxide codissolved suspension, then filtering, wherein the filtering mode can be suction filtration or filter pressing to remove inorganic impurities in the suspension, washing with pure water to be neutral, and the pH value of the filtrate is 6.9-7.2. After the last filtration, a Ce-Zr hydroxide hydrogel was obtained and maintained at a defined water content depending on the composition of Ce and Zr.
Adding water-soluble organic alcohol, organic acid and high polymer into the Ce-Zr hydroxide hydrogel, stirring at the constant temperature of room temperature to 60 ℃ for 2-5 h, mixing and dispersing to prepare Ce-Zr oxide synthetic slurry. Wherein the amount of the added organic alcohol does not exceed the mass of the Ce-Zr oxide, and preferably does not exceed 40 percent of the mass of the Ce-Zr oxide; the amount of the added high polymer is not more than the mass of the Ce-Zr oxide, and preferably not more than 30 percent of the mass of the Ce-Zr oxide; the amount of the organic acid added is not more than the amount of the Ce-Zr oxide, preferably not more than 70% of the amount of the Ce-Zr oxide. The Ce-Zr oxide nanoparticles are effectively dispersed through the synergistic effect of organic alcohols, organic acids and high polymers, so that the expected synthetic effect is obtained.
The Ce-Zr mixed hydroxide precipitate, the Ce-Zr hydroxide eutectic, the Ce-Zr hydroxide hydrogel and the Ce-Zr oxide synthetic slurry prepared by the steps are precursors, the preparation of each precursor influences the synthetic result, and the desired synthetic effect is obtained through the synergistic effect of the preparation steps.
And heating and stirring the Ce-Zr oxide synthetic slurry, wherein the heating temperature is room temperature to 80 ℃, keeping the temperature for 1-5 hours, preferably 40-60 ℃, keeping the temperature for 2-4 hours, and stirring to fully mix the synthetic slurry.
A hydrothermal synthesis mode is to put the heated and mixed Ce-Zr oxide synthesis slurry into a hydrothermal kettle, heat the slurry to 120-220 ℃ and keep the temperature for 2-12 h, preferably 140-180 ℃ for 2-8 h, so as to obtain the aqueous medium dispersion cerium-zirconium oxide nano material. A hydrothermal synthesis mode is that the Ce-Zr oxide synthesis slurry is placed into a hydrothermal kettle, the temperature is raised to 120-200 ℃ at the heating rate of 0.2-2 ℃/min, the temperature is kept for 2-10 hours, preferably, the temperature is raised to 140-180 ℃ at the heating rate of 0.5-1.0 ℃/min, and the temperature is kept for 2-6 hours, so that the aqueous medium dispersion cerium-zirconium oxide nano material is obtained.
The Ce-Zr mixed hydroxide precipitate, the Ce-Zr hydroxide eutectic, the Ce-Zr hydroxide hydrogel and the Ce-Zr oxide synthetic slurry obtained by the steps are all precursors, the preparation of each precursor influences the synthetic result, and the ideal synthetic effect is achieved through the synergistic effect of the preparation steps and the coupling effect with the hydrothermal synthesis step.
According to the above embodiment, aqueous medium-dispersed Ce is obtainedxZr1-xO2Nanomaterial of which Ce isxZr1-xO2The mass (w/g) of the nano material is 8-12% (w/V) of the volume (V/ml) of the nano material sol; preferably, the Ce can be evaporated and concentrated at a proper temperature, for example, 60-90 ℃ by heating, or concentrated by vacuumizing, and the Ce is concentrated in the process of concentrationxZr1-xO2The nano particles do not generate coagulation until the nano material sol becomes gel, CexZr1-xO2The mass percentage of the (B) can reach more than 20 percent (w/V); preferably, it can be diluted with pure water, for example, with deionized water in an arbitrary ratio, and Ce is present during the dilutionxZr1-xO2The nanoparticles do not generate coagulation, CexZr1-xO2The mass percentage of (b) can be less than 1% (w/V) or less.
In order to prepare the granular cerium zirconium-aluminum-based oxide micro-nano composite catalytic material, the prepared alumina micro-granular material is mixed with the synthesized aqueous dispersion cerium zirconium oxide nano material sol to generate slurry, and the slurry is dried and roasted to obtain the granular cerium zirconium-aluminum-based oxide micro-nano composite catalytic material. According to Ce in the solxZr1-xO2Mass percentage of and CexZr1-xO2The catalyst is prepared and mixed to generate slurry, wherein the catalyst accounts for 1.0-30 wt% of the mass of the catalyst; adding alumina into sol under stirring, or adding sol into alumina under stirring, or simultaneously adding alumina and sol under stirring to obtain paste-like slurry; heating, frying and drying the slurry, wherein the heating temperature is 30-90 ℃, preferably 40-80 ℃, more preferably 45-60 ℃, and slow frying is favorable for uniformly dispersing the nano particles on the surfaces of the micron carrier particles; then drying in an oven at 90-150 deg.C for 1-5 hours, preferably at 100-130 deg.C for 2-EAnd 3 hours, sieving, heating to 500-.
In order to prepare the coated cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, the prepared aluminum oxide micro-particle material and the synthesized aqueous dispersed cerium-zirconium oxide nano material sol are mixed to generate slurry, or the granular cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material is added into water to generate slurry in an emulsifying, shearing or ball-milling mode, wherein the solid content of the slurry in terms of the total amount of metal oxides is 20-60 g/100ml, preferably 30-50 g/100 ml; coating the cordierite honeycomb ceramic matrix or FeCrAl honeycomb metal matrix with the slurry, wherein the coating amount of the cerium-zirconium-aluminum-based oxide on the matrix is controlled to be 50-300 g/L, preferably 100-200 g/L by manual coating, mechanical coating or automatic coating; heating the coated substrate from room temperature to 500 ℃ at a heating rate of 1-10 ℃/min for drying, then heating to 500-1000 ℃ and keeping the temperature for roasting for 1-24 h, wherein the specific drying, roasting temperature and time are determined according to specific application; then cooling to room temperature to obtain the coated cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material.
According to the cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material and the preparation method thereof, the cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material is used for manufacturing tail gas purification catalysts of fuel vehicles and fuel general engines and other industrial catalysts by loading one or more of noble metals Pt, Pd, Rh, Au, Ir and Ru.
One embodiment is a three-way catalyst for purifying the tail gas of a gasoline vehicle, which loads noble metals Pt, Pd and Rh. Taking a granular cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, respectively soaking Pt, Pd and Rh salts easily, drying, and roasting at a constant temperature of about 500 ℃ for 1-3 h to obtain catalysts respectively loaded with Pt, Pd and Rh; then, the Pd catalyst is slurried and coated on a cordierite honeycomb ceramic substrate, and a first layer of coated catalyst is obtained after drying, constant temperature of 500 ℃ and roasting for 2-3 hours; and then mixing, pulping and coating the Pt and Rh catalyst on the first layer of coated catalyst, drying, and roasting at the constant temperature of 550-600 ℃ for 2-3 h to obtain the ternary catalyst, wherein the use amounts of the Pt, Pd and Rh and the coating amount of each catalyst are determined according to specific application. The three-way catalyst prepared by the method can effectively play a role in quickly storing/releasing oxygen and greatly improve the durability of the catalyst. The method can also be used for manufacturing tail gas purification catalysts of motorcycles, diesel vehicles, gas vehicles and fuel oil general engines, and the selection of the noble metal is determined according to specific application.
One embodiment is used for a space rocket propellant catalyst, and the noble metal Ir is loaded on the space rocket propellant catalyst. Taking a granular cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, easily dipping Ir salt, drying, and roasting at a constant temperature of about 500 ℃ for 1-3 h to obtain an Ir-loaded catalyst; and then the Ir catalyst is coated on the millimeter particle carrier in a slurrying way, and the coated catalyst is obtained after drying and roasting, so that the use amount of Ir can be greatly saved, and the cost is saved.
The noble metal supported catalyst is used in the fields of petrochemical industry, natural gas chemical industry, synthesis gas chemical industry, biomass chemical industry, pharmaceutical chemical industry and the like, zirconium-aluminum-based oxide micro-nano composite catalytic materials can be used, and the noble metal is selected according to specific application.
Specific examples the following examples are further illustrative of, but not limiting to, embodiments of the present invention, and any substitutions beyond those examples are intended to be within the scope of the embodiments of the present invention.
The performance detection of the cerium-zirconium-aluminum-based oxide catalytic material mainly comprises four types, namely detection of specific surface area, oxygen storage amount, surface performance and reduction performance.
The specific surface area reflects the capability of the catalytic material to disperse the noble metal, and the higher the specific surface area of the material is, the better the effect of dispersing the noble metal is under the condition of a specified temperature and a specified roasting time. By low temperature N2Testing the specific surface area by an adsorption method (BET method), sieving a sample by a 40-60-mesh sieve, weighing 0.2g of the sample, placing the sample in a testing tube, pretreating at 300 ℃ for 3 hours, and then loading the sample into a nitrogen adsorption instrument for testing.
The oxygen storage amount reflects the oxygen storage/release capacity of the cerium-zirconium-aluminum-based oxide catalytic material. Taking 0.200g of sample, placing in a quartz tube (tube length 820mm, inner diameter 10), heating to 500 deg.C, keeping constant temperature, and introducing oxygen gas (containing O) of reaction gas21.0V%, the remainder being N2) With reducing gas (containing CO 2.0V%, the remainder being N)2) To be provided with300ml min-1Alternately flowing through the reaction tube at a flow rate, separating reducing gas by gas chromatograph at intervals of 3.0min, converting into methane, and detecting CO by FID2The amount of (c); the reaction gas is continuously and alternately circulated for three times to obtain the testing average value so as to obtain the measured CO2The amount of oxygen storage is calculated.
The surface performance comprises surface appearance and surface element concentration, the surface appearance of the coated catalytic material can be observed by a Scanning Electron Microscope (SEM), the surface element concentration is tested by photoelectron spectroscopy (XPS), and the higher the surface cerium concentration is, the better the rapid oxygen storage/release performance is.
Reduction performance reflects Ce in cerium-zirconium-aluminum-based oxide catalytic material+4Reduction to Ce+3The performance of the alloy is shown in the specification, the reduction temperature is low, the low-temperature reduction performance is good, and a Temperature Programmed Reduction (TPR) method is adopted for testing.
Example 1
Preparing alumina by peptization method, wherein BaO and La are doped2O3The content of the oxide accounts for 2 wt% and 3 wt% respectively, and the specific surface area is 152m after roasting for 5h at 600 DEG C2·g-1The particle size D90 is 0.1-16 μm and is marked as Al2O3
Synthesis of aqueous dispersed Ce0.6Zr0.4O2The nanometer material sol has a nanometer particle size of 5.2nm, Ce0.6Zr0.4O2Is 10.0% (w/V) in mass/volume percentage, wherein Y is doped2O3、La2O3The contents are 0.2% (w/V) and 0.3% (w/V), respectively, and the metal oxide is designated CeZrO.
Mixing 50ml of sol and 12.25g of alumina with stirring2O3Preparing slurry, wherein the solid content of the metal oxide is about 33% (w/V), heating, frying and drying the slurry at 60 ℃, then placing the slurry in a drying oven for drying at 120 ℃ for 3 hours, sieving to obtain a 40-60 mesh sample, heating the sample to 600 ℃ at room temperature for roasting for 5 hours, and heating to 1000 ℃ at room temperature for roasting for 5 hours to obtain the granular cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, wherein CeZrO and Al are2O3Is 30-70, the specific surface area and oxygen storage amount are shown in Table I.
Example 2
The preparation method is the same as example 1, 50ml of sol and 21.00g of alumina are taken, and the solid content of the metal oxide in the prepared slurry is about 47 percent (w/V); CeZrO and Al are obtained2O3The mass ratio of (2) is 20-80, and the measured specific surface area and oxygen storage amount are listed in the table I.
Example 3
The preparation method is the same as that of the example 1, 50ml of sol and 47.25g of alumina are taken, 43ml of deionized water is added into the sol for dilution and then slurried with the alumina, and the solid content of metal oxide is about 50 percent (w/V); CeZrO and Al are obtained2O3The mass ratio of (2) is 10-90, and the measured specific surface area and oxygen storage amount are listed in the table I.
Comparative example 1
The alumina was prepared as in example 1. Conventional micron-particle oxygen storage material Ce0.6Zr0.4O2The preparation of (1) is carried out by coprecipitation, mixing solution of Ce and Zr salt (adding right amount of H)2O2) Carrying out concurrent flow titration with alkali liquor (ammonia solution) to generate precipitate, filtering, washing to be neutral, adding a high polymer pore-forming agent, pulping, drying and spraying to obtain precursor powder; drying the powder, decomposing the high polymer, and roasting at 600 ℃ for 5h to obtain micron particle Ce0.6Zr0.4O2In which Y is doped2O3、La2O3Is Ce0.6Zr0.4O2In an amount of 2 wt% and 3 wt%, respectively, and a specific surface area of 74.6m2·g-1Oxygen storage amount is 205 mu mol O2·g-1The particle size D90 is 0.1-14 μm; the metal oxide is designated CeZrO.
Taking Al2O312.5g and CeZrO12.5g, adding deionized water, stirring to obtain slurry with the solid content of metal oxide being about 50% (w/V), heating, stir-frying and drying the slurry at 60 ℃, then placing the slurry in a drying oven for drying at 120 ℃ for 3 hours, sieving to obtain a 40-60 mesh sample, heating the sample to 600 ℃ at room temperature for roasting for 5 hours, and heating to 1000 ℃ at room temperature for roasting for 5 hours to obtain the granular cerium-zirconium-aluminum-based oxide micron mixed catalytic material, wherein the granular cerium-zirconium-aluminum-based oxide micron mixed catalytic material is prepared by the steps ofMedium CeZrO and Al2O3The mass ratio of (2) is 50-50, and the measured specific surface area and oxygen storage amount are listed in the table I.
Comparative example 2
The preparation method is the same as that of comparative example 1, wherein CeZrO is mixed with Al2O3The mass ratio of (2) is 40-60, and the measured specific surface area and oxygen storage amount are shown in the table I.
Comparative example 3
The preparation method is the same as that of comparative example 1, wherein CeZrO is mixed with Al2O3The mass ratio of (2) is 30-70, and the measured specific surface area and oxygen storage amount are listed in the table I.
Watch 1
Figure BDA0003378282970000081
The result shows that after roasting at 600 ℃ for 5 hours, the specific surface area of example 1 is higher than 27.1 percent compared with comparative example 1, and the oxygen storage capacity is higher than 32.7 percent; after roasting for 5 hours at 1000 ℃, the specific surface area of the example 1 is 32.3% higher than that of the comparative example 1, and the oxygen storage amount is higher than 35.1%, so that the thermal stability and the oxygen storage performance of the micro-nano composite catalytic material are greatly higher than those of the micro-micron mixed catalytic material.
Example 4
Synthesis of aqueous dispersed Ce0.6Zr0.4O2Nanomaterial colloids wherein Ce is0.6Zr0.4O2The mass/volume percentage content of (A) is 8.8% (w/V), La2O3The content was 0.44% (w/V). 50ml of sol was taken and commercially available commercial alumina (containing Al)2O395 wt% of the rest La and Pr), 26.2g of the rest La and Pr, and the mass ratio of the metal oxide to the alumina in the sol body is 15 | 85; adding 20ml of deionized water into the sol for dilution, and mixing the sol with alumina for pulping, wherein the solid content of metal oxide is about 40% (w/V); coating the slurry on a 400-pore cordierite honeycomb ceramic substrate with the coating amount of about 120g/L, heating the coated substrate from room temperature to 600 ℃ at the heating rate of 3 ℃/min, and roasting at the constant temperature for 2h to obtain the coated cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material, wherein CeO2The content was 9.7 wt%. Taking a 4 x 4mm piece of the coated substrate, and performing photoelectron spectroscopy(XPS) analysis, see FIG. 2a), the surface Ce mass concentration is 20.46%.
Comparative example 4
Taking a commercially available oxygen storage material (containing CeO)2 33wt%、ZrO262 wt% of the balance La and Nd, 15.0g of commercial alumina (containing Al)2O395 wt% and the rest La and Pr)15.0g, the mass ratio is 50 | 50, deionized water is added for mixing and pulping, and the solid content of the metal oxide is about 40% (w/V); coating the slurry on a 400-pore cordierite honeycomb ceramic substrate with the coating amount of about 120g/L, and roasting the coated substrate at the constant temperature of 3 ℃/min from room temperature to 600 ℃ for 2h to obtain the coated cerium-zirconium-aluminum-based oxide micron mixed catalytic material, wherein CeO2The content was 16.5 wt%. A4X 4mm piece of the coated substrate was analyzed by photoelectron spectroscopy (XPS), and the surface Ce concentration was 15.67% by mass as shown in FIG. 2 b).
Micro-nano composite catalytic material CeO2The content is 41.2 percent lower than that of the mixed catalytic material, and the mass concentration of Ce on the surface is higher than 31.4 percent, which indicates that the micro-nano composite catalytic material forms a core-shell structure type CeZrO @ Al2O3,Al2O3The content and the mass concentration of Ce on the surface are greatly improved, so that the oxygen storage capacity, the rapid oxygen storage/release function and the thermal stability of the material are greatly improved or enhanced.
Example 5
The granular cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material roasted for 5 hours at the temperature of 600 ℃ in the example 1 is taken and subjected to a Temperature Programmed Reduction (TPR) test, the result is shown in the attached figure 3a), the initial reduction temperature is lower, the reduction peak temperature is 573 ℃, and the peak type is narrower, so that the low-temperature reduction performance is better, and the rapid oxygen storage/release effect is facilitated.
Comparative example 5
The granular cerium-zirconium-aluminum-based oxide micron mixed catalytic material roasted for 5 hours at the temperature of 600 ℃ in the comparative example 1 is taken for carrying out a Temperature Programmed Reduction (TPR) test, the result is shown in the attached figure 3b), the initial reduction temperature is higher, the reduction peak temperature is 622 ℃, the peak type is wider, and the low-temperature reduction performance is poor.
All test data of the present invention is not compared to any published patent, paper data or other literature data. Because the same index is tested, different testing methods are used in different laboratories, or the testing method is the same and the testing condition is different, or the testing condition is the same and the sample processing condition is different, the testing results are greatly different; even in the same laboratory, the same sample is tested by the same test method and test conditions, and the operation of different personnel can cause great errors.
The preparation method of the invention is easy to be industrially scaled up, and the process changes made in the process of scaling up do not constitute substantial innovation, thus still falling within the scope of protection of the claims of the invention.

Claims (10)

1. The cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material is characterized by being formed by nano self-assembly of cerium-zirconium oxide nano particles and active alumina micro particles, wherein the cerium-zirconium oxide nano particles are dispersed and loaded on the surface of the outer layer of the active alumina micro particles to form a granular micro-nano composite catalytic material with a core-shell structure and a coating-shaped micro-nano composite catalytic material coated on a substrate, and the coating-shaped micro-nano composite catalytic material is marked as CeZrO @ Al2O3
2. The cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material as claimed in claim 1, wherein the cerium-zirconium oxide nanoparticles are prepared from aqueous dispersed nanomaterial sol, wherein the cerium-zirconium oxide nanoparticles are single crystals of nanoparticles with a nanoscale of 2-8 nm, and the mass/volume percentage of the cerium-zirconium oxide nanoparticles in the sol is 1.0-20%, and the cerium-zirconium-aluminum-based oxide nanoparticles are marked as CexZr1-xO2,x=0.0~1.0。
3. The cerium zirconium-aluminum based oxide micro-nano composite catalytic material as claimed in claim 1, wherein the active alumina is γ -Al2O3Rare earth oxide stabilized Al2O3One or more of the above components are polycrystalline particles with a particle size of 0.1-25 μm.
4. The cerium zirconium-aluminum based oxide micro-nano composite catalytic material as claimed in claim 1, wherein the cerium zirconium oxide accounts for 1.0-30 wt% of the composite catalytic material.
5. The cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material of claim 1, wherein the cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material contains metal oxides, and the metal oxides comprise one or more of oxides of Ca, Sr, Ba, Sc, Y, La, Pr, Nd and Sm as an auxiliary agent, and the mass percentage of the metal oxides in the catalytic material is 0.0-20 wt%.
6. A preparation method of a cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material is characterized by comprising the following steps:
(1) preparation of micron-sized particulate alumina (Al)2O3) The activated alumina has a micron size of 0.1-25 μm and a specific surface area of 50-200 m2The additive comprises the auxiliary agent of claim 5, and accounts for 0.0-10 wt% of the oxide;
(2) synthesizing aqueous dispersed cerium-zirconium oxide nano material sol, wherein the cerium-zirconium oxide is nano particle single crystal, the nano scale is 2-8 nm, the mass/volume percentage content in the sol is 1.0-20%, and the cerium-zirconium oxide nano material sol is marked as CexZr1-xO2X is 0.0 to 1.0, wherein the mass percentage of the auxiliary agent in the formula 5 is 0.0 to 10 wt% of the oxide;
(3) mixing the alumina micron particle material prepared in the step (1) with the aqueous dispersion cerium-zirconium oxide nano material sol synthesized in the step (2) to generate slurry, and drying and roasting the slurry to obtain the granular cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material;
(4) and (3) coating the slurry generated in the step (3) or the granular cerium-zirconium-aluminum-based oxide micro/nano composite catalytic material on a substrate after pulping, drying and roasting to obtain the coated cerium-zirconium-aluminum-based oxide micro/nano composite catalytic material, wherein the substrate is a cordierite honeycomb ceramic substrate or an FeCrAl honeycomb metal substrate.
7. The preparation method of the cerium zirconium-aluminum based oxide micro-nano composite catalytic material as claimed in claim 6, wherein the drying in the step (3) is performed by heating from room temperature to 120 ℃ at a heating rate of 1-10 ℃/min for 1-3 h, and the baking is performed by heating from 500-600 ℃ for 1-3 h, and then cooling to room temperature.
8. The preparation method of the cerium zirconium-aluminum based oxide micro-nano composite catalytic material as claimed in claim 6, wherein the drying in the step (4) is performed by heating from room temperature to 500 ℃ at a heating rate of 1-10 ℃/min, and the roasting is performed by keeping the temperature at 500-1000 ℃ for 1-24 h, and then cooling to room temperature.
9. The preparation method of the cerium zirconium-aluminum based oxide micro-nano composite catalytic material as claimed in claim 6, wherein the slurry in the step (4) has a solid content of 30-50 g/100ml based on the total amount of metal oxides, and the coating amount of the cerium zirconium-aluminum based oxide micro-nano composite catalytic material on the substrate is 50-300 g/L.
10. The cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material and the preparation method thereof as claimed in any one of claims 1 to 8, wherein the cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material is used for manufacturing tail gas purification catalysts of fuel vehicles and fuel general engines and other industrial catalysts by loading one or more of noble metals of Pt, Pd, Rh, Au, Ir and Ru.
CN202111425631.4A 2021-11-26 2021-11-26 Cerium-zirconium-aluminum-based oxide micro-nano composite catalytic material and preparation method thereof Active CN114100594B (en)