CN113860270B - Cubic phase Cu 3 NbSe 4 Nano material and preparation method and application thereof - Google Patents

Cubic phase Cu 3 NbSe 4 Nano material and preparation method and application thereof Download PDF

Info

Publication number
CN113860270B
CN113860270B CN202111136519.9A CN202111136519A CN113860270B CN 113860270 B CN113860270 B CN 113860270B CN 202111136519 A CN202111136519 A CN 202111136519A CN 113860270 B CN113860270 B CN 113860270B
Authority
CN
China
Prior art keywords
nbse
nano material
preparation
cubic phase
reaction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202111136519.9A
Other languages
Chinese (zh)
Other versions
CN113860270A (en
Inventor
王文亮
冯文玲
赵玉彤
张文骞
刘梦雪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qufu Normal University
Original Assignee
Qufu Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qufu Normal University filed Critical Qufu Normal University
Priority to CN202111136519.9A priority Critical patent/CN113860270B/en
Publication of CN113860270A publication Critical patent/CN113860270A/en
Application granted granted Critical
Publication of CN113860270B publication Critical patent/CN113860270B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention belongs to Cu 3 NbSe 4 The technical field of preparation, in particular to cubic phase Cu 3 NbSe 4 A nano material and a preparation method and application thereof. The molecular formula of the nano material is Cu 3 NbSe 4 The crystal form is cubic phase, and the micro appearance of the nano material is a nano cubic structure. The method comprises the following steps: (1) Carrying out deoxidization and dehydration treatment on an organic solvent containing a soluble copper source, a niobium source and a selenium source, and then carrying out solvothermal reaction; (2) And separating out a solid product obtained by the solvothermal reaction to obtain the catalyst. The preparation process is simpler, the reaction condition is very mild, the energy consumption is obviously reduced, and the cost is low; more importantly, the cubic phase Cu with uniform appearance, controllable size, high crystallinity and good monodispersity is realized 3 NbSe 4 Preparation of nanomaterials, thus, cu prepared by the invention 3 NbSe 4 The micro-nano and integrated processing is easier to carry out in the application aspect.

Description

Cubic phase Cu 3 NbSe 4 Nano material and preparation method and application thereof
Technical Field
The invention belongs to Cu 3 NbSe 4 The technical field of preparation, in particular to cubic phase Cu 3 NbSe 4 A nano material and a preparation method and application thereof.
Background
The information in this background section is disclosed to enhance understanding of the general background of the invention and is not necessarily to be construed as an admission or any form of suggestion that this information forms part of the prior art already known to a person of ordinary skill in the art.
Solar energy has long been considered by researchers as the first choice alternative to fossil energy as a clean and sustainable energy source. The functional nano material with photoelectric characteristics can convert optical signals into electric signals, and has wide application prospects in the fields of solar cells, photodetectors, biosensors, field effect transistors and the like.
The development of novel efficient nano photoelectric conversion materials becomes a hotspot of current research. Cu (copper) 3 NbSe 4 The nano material has a proper optical band gap and good charge transmission characteristics, has strong absorption in a visible light range, and has potential application prospects in the field of photoelectric conversion. At present, research reports that Cu can be prepared by heating copper powder, niobium powder and selenium powder to 573K for 24 hours by using a solid-phase reaction method, then increasing the furnace temperature to 823K within 4 hours, keeping the temperature for 120 hours, and finally cooling to room temperature within 24 hours 3 NbSe 4 . However, the preparation method not only has long reaction time and high energy consumption, but also is the product Cu 3 NbSe 4 The shape of the copper alloy is not uniform, the size is not controllable, and the copper alloy is not beneficial to Cu 3 NbSe 4 Large-scale production and micro-nano application.
Disclosure of Invention
In order to solve the above problems, the present invention provides a cubic phase Cu 3 NbSe 4 A nano material and a preparation method and application thereof. Compared with the solid phase reaction method, the preparation process is simpler, the reaction condition is very mild, the energy consumption is obviously reduced, the cost is low, the method is environment-friendly, and more importantly, the cubic phase Cu with uniform appearance, controllable size and high crystallinity is realized 3 NbSe 4 And (4) preparing the nano material. In order to achieve the purpose, the invention discloses the following technical scheme:
in a first aspect of the present invention, there is provided Cu 3 NbSe 4 Nanomaterial of formula Cu 3 NbSe 4 The crystal form is cubic phase, and the microscopic appearance of the nano material is a nano-scale cubic structure. Relative to Cu prepared by solid-phase reaction method 3 NbSe 4 Material, cubic phase Cu of the invention 3 NbSe 4 The nano material not only has uniform appearance and controllable size, but also has good monodispersity and high crystallinity, so that the nano material is easier to carry out micro-nano and integrated processing in practical application.
Further, the Cu 3 NbSe 4 The nano material can show good dispersibility in a solvent, is in a monodisperse state and has good stability. Preparation of Cu by high temperature solid phase reaction 3 NbSe 4 The process of (2) is easy to generate sintering phenomenon, namely products are agglomerated together, and the dispersibility is poor.
Further, the Cu 3 NbSe 4 The size of the nano material is about 15 to 25 nm.
To this end, in a second aspect of the invention, a cubic phase Cu is provided 3 NbSe 4 The preparation method of the nano material comprises the following steps:
(1) Carrying out deoxidization and dehydration treatment on an organic solvent containing a soluble copper source, a niobium source and a selenium source, and then carrying out solvothermal reaction;
(2) And separating out a solid product obtained by the solvothermal reaction to obtain the catalyst.
Further, in the step (1), the ratio of Cu: nb: the molar ratio of Se is 3.
Further, in the step (1), the copper source is selected from one or more of cuprous chloride, cuprous bromide, cupric acetylacetonate, cupric chloride or cupric acetate.
Further, in the step (1), the niobium source is selected from one or two of niobium pentachloride and niobium oxalate.
Further, in the step (1), the selenium source is selected from one or more of diphenyl diselenide, selenium powder, dibenzyl diselenide or selenium dioxide.
Further, in the step (1), the organic solvent is selected from organic amines. Optionally, the organic amine is selected from one or more of oleylamine, hexadecylamine or octadecylamine. When the organic solvents are used as reaction media, the temperature required by the reaction can be met, and the organic solvents have the function of a surfactant, so that the morphology and the size of a product can be conveniently regulated and controlled.
Further, in the step (1), under an oxygen isolation condition (such as in a nitrogen or inert gas atmosphere), adding the copper source, the niobium source and the selenium source into a reaction medium, uniformly mixing, heating to 100 to 150 ℃, and reacting for 30 to 60min to dissolve the copper source, the niobium source and the selenium source and remove water, oxygen and low-boiling-point impurities in a reaction system.
Further, in the step (1), the temperature of the solvent is kept between 270 ℃ and 310 ℃, and the reaction time is controlled between 5 and 120min. The target product is difficult to obtain when the reaction temperature is too low, and the function of the surfactant is easily inactivated and volatilized when the temperature is too high.
Further, in the step (2), solid matters in the reaction liquid are separated in a centrifugal or filtering mode, and the centrifugal solid products are washed by a mixed liquid of absolute ethyl alcohol and chloroform to obtain the target products.
In a third aspect of the present invention, there is provided the cubic phase Cu 3 NbSe 4 The application of the nano material in the fields of photoelectricity, thermoelectricity and the like.
Compared with the prior art, the technical scheme of the invention has the following beneficial effects:
(1) Compared with the solid phase reaction method, the preparation process is simpler, the reaction condition is very mild, the energy consumption is obviously reduced, the cost is low, the method is environment-friendly, and more importantly, the cubic phase Cu with uniform appearance, controllable size, high crystallinity and good monodispersity is realized 3 NbSe 4 Preparation of nanomaterials, thus, cu prepared by the invention 3 NbSe 4 The micro-nano and integrated processing is easier to carry out in the application aspect. Because sintering phenomenon is easy to occur in the high-temperature solid-phase reaction process, namely products are agglomerated together, and the dispersibility is poor. The method is liquid phase preparation, reactants are dissolved in a solvent and then react in an ion or molecular form, and the reactants have the functions of a surfactant (such as crystal face selective adsorption and limitation of further growth of crystals) in the crystal nucleation and growth processes, so that the liquid phase reaction is obviously superior to the high-temperature solid phase reaction in the aspect of controlling the appearance and the size of a product.
(2) The research shows that the Cu prepared by the embodiment of the invention 3 NbSe 4 Has strong absorption capacity in the visible light range and uses Cu 3 NbSe 4 The photoelectric detector constructed by nano materials has response speedThe advantages of high speed and stability are due to the following reasons: cu with high monodispersity and uniform appearance and size 3 NbSe 4 The nano material can not only carry out micro-nano processing film formation on a device substrate (taking a monocrystalline silicon substrate as an example) in a spin coating or drop coating mode, but also can be in close contact with the substrate to form good Cu 3 NbSe 4 a/Si heterojunction. Furthermore, since Cu 3 NbSe 4 The nano material has the advantages of high crystallinity and strong light absorption, so the nano material is prepared in Cu 3 NbSe 4 Under the action of a built-in electric field formed by the/Si heterojunction, the effective separation of photogenerated electrons and holes can be promoted, and the performance of the photoelectric detector is improved.
Drawings
The accompanying drawings, which are incorporated in and constitute a part of this specification, are included to provide a further understanding of the invention, and are incorporated in and constitute a part of this specification, illustrate exemplary embodiments of the invention and together with the description serve to explain the invention and not to limit the invention. Embodiments of the invention are described in detail below with reference to the attached drawing figures, wherein:
FIG. 1 shows an X-ray diffraction pattern (XRD) of a target product obtained in accordance with a first embodiment of the present invention.
FIG. 2 is a Transmission Electron Microscope (TEM) photograph of a target product obtained in the first example of the present invention.
FIG. 3 is a diagram showing the ultraviolet-visible (UV-vis) absorption spectrum of the objective product obtained in the first example of the present invention.
FIG. 4 is an I-t curve of a photodetector constructed by the target product obtained in the first embodiment of the present invention. .
FIG. 5 shows the X-ray diffraction pattern (XRD) of the object obtained by the second example of the present invention.
FIG. 6 is a Transmission Electron Microscope (TEM) photograph of a target product obtained by the third example of the present invention.
FIG. 7 is an X-ray diffraction pattern (XRD) of the object obtained in the fourth example of the present invention.
FIG. 8 is a Transmission Electron Microscope (TEM) photograph of a target product obtained in the fifth example of the present invention.
FIG. 9 shows the X-ray diffraction pattern (XRD) of the object obtained in the sixth example of the present invention.
DETAILED DESCRIPTION OF EMBODIMENT (S) OF INVENTION
The invention will be further illustrated with reference to the following specific examples. It should be understood that these examples are for illustrative purposes only and are not intended to limit the scope of the present invention. Experimental procedures without specific conditions noted in the following examples, generally according to conventional conditions or according to conditions recommended by the manufacturers.
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art. The reagents or starting materials used in the present invention can be purchased from conventional sources, and unless otherwise specified, the reagents or starting materials used in the present invention can be used in a conventional manner in the art or in accordance with the product specification.
In addition, any methods and materials similar or equivalent to those described herein can be used in the methods of the present invention. The preferred methods and materials described herein are exemplary only. The invention will now be further described with reference to the drawings and specific examples.
First embodiment
Cubic phase Cu 3 NbSe 4 The preparation of the nano material comprises the following steps:
(1) In a 100ml three-necked flask, 0.3mmol cuprous chloride, 0.1mmol niobium pentachloride, 0.4mmol diphenyl diselenide and 6.0ml oleylamine were added, respectively, to obtain a mixed solution.
(2) And (2) introducing nitrogen into the three-mouth bottle in the step (1), heating the mixed solution to 130 ℃ under the condition of magnetic stirring, and carrying out heat preservation reaction for 30min to remove water and low-boiling-point impurities in the reaction system.
(3) And continuously heating the mixed solution to 280 ℃, preserving the temperature, reacting for 30min, cooling to room temperature after the reaction is finished, and then washing and centrifuging the solid product for 3 times by using a mixed solution of absolute ethyl alcohol and chloroform with the volume ratio of 3.
Second embodiment
Cubic phase Cu 3 NbSe 4 Of nanometric materialsThe preparation method comprises the following steps:
(1) In a 100ml three-necked flask, 0.3mmol of cuprous bromide, 0.1mmol of niobium oxalate, 0.4mmol of diphenyldiselenide and 5.0g of octadecylamine were added, respectively, to obtain a mixed solution.
(2) And (2) introducing nitrogen into the three-mouth bottle in the step (1), heating the mixed solution to 130 ℃ under the condition of magnetic stirring, and carrying out heat preservation reaction for 60min to remove water and low-boiling-point impurities in the reaction system.
(3) And continuously heating the mixed solution to 280 ℃, preserving the temperature, reacting for 30min, cooling to room temperature after the reaction is finished, and then washing and centrifuging the solid product for 3 times by using a mixed solution of absolute ethyl alcohol and chloroform with the volume ratio of 3.
Third embodiment
Cubic phase Cu 3 NbSe 4 The preparation of the nano material comprises the following steps:
(1) In a 100ml three-necked flask, 0.3mmol of cuprous chloride, 0.1mmol of niobium pentachloride, 0.4mmol of diphenyl diselenide and 4.5g of hexadecylamine were added, respectively, to obtain a mixed solution.
(2) And (2) introducing nitrogen into the three-mouth bottle in the step (1), heating the mixed solution to 100 ℃ under the condition of magnetic stirring, and carrying out heat preservation reaction for 60min to remove water and low-boiling-point impurities in the reaction system.
(3) And continuously heating the mixed solution to 270 ℃, preserving the temperature, reacting for 120min, cooling to room temperature after the reaction is finished, and then washing and centrifuging the solid product for 3 times by using a mixed solution of absolute ethyl alcohol and chloroform with the volume ratio of 3.
Fourth embodiment
Cubic phase Cu 3 NbSe 4 The preparation of the nano material comprises the following steps:
(1) In a 100ml three-necked flask, 0.3mmol of acetylacetone copper, 0.1mmol of niobium pentachloride, 0.4mmol of dibenzyl diselenide and 6.0ml of oleylamine were added, respectively, to obtain a mixed solution.
(2) And (2) introducing nitrogen into the three-mouth bottle in the step (1), heating the mixed solution to 120 ℃ under the condition of magnetic stirring, and carrying out heat preservation reaction for 45min to remove water and low-boiling-point impurities in the reaction system.
(3) And continuously heating the mixed solution to 310 ℃, preserving the temperature, reacting for 5min, cooling to room temperature after the reaction is finished, and then washing and centrifuging the solid product for 3 times by using a mixed solution of absolute ethyl alcohol and chloroform with the volume ratio of 3.
Fifth embodiment
Cubic phase Cu 3 NbSe 4 The preparation of the nano material comprises the following steps:
(1) In a 100ml three-necked flask, 0.3mmol of cuprous chloride, 0.1mmol of niobium pentachloride, 0.4mmol of diphenyl diselenide and 5.0g of octadecylamine were added, respectively, to obtain a mixed solution.
(2) And (2) introducing nitrogen into the three-mouth bottle in the step (1), heating the mixed solution to 150 ℃ under the condition of magnetic stirring, and carrying out heat preservation reaction for 20min to remove water and low-boiling-point impurities in the reaction system.
(3) And continuously heating the mixed solution to 280 ℃, preserving the temperature, reacting for 30min, cooling to room temperature after the reaction is finished, and then washing and centrifuging the solid product for 3 times by using a mixed solution of absolute ethyl alcohol and chloroform with the volume ratio of 3.
Sixth embodiment
Cubic phase Cu 3 NbSe 4 The preparation of the nano material comprises the following steps:
(1) In a 100ml three-necked flask, 0.3mmol of copper chloride, 0.1mmol of niobium pentachloride, 0.4mmol of selenium powder and 6.0ml of oleylamine are respectively added to obtain a mixed solution.
(2) And (2) introducing nitrogen into the three-mouth bottle in the step (1), heating the mixed solution to 100 ℃ under the condition of magnetic stirring, and carrying out heat preservation reaction for 60min to remove water and low-boiling-point impurities in the reaction system.
(3) And continuously heating the mixed solution to 300 ℃, preserving the temperature, reacting for 30min, cooling to room temperature after the reaction is finished, and then washing and centrifuging the solid product for 3 times by using a mixed solution of absolute ethyl alcohol and chloroform with the volume ratio of 3.
Seventh embodiment
Cubic phase Cu 3 NbSe 4 The preparation of the nano material comprises the following steps:
(1) In a 100ml three-necked flask, 0.3mmol of copper acetate, 0.1mmol of niobium pentachloride, 0.4mmol of selenium dioxide and 6.0ml of oleylamine were added, respectively, to obtain a mixed solution.
(2) And (2) introducing nitrogen into the three-mouth bottle in the step (1), heating the mixed solution to 140 ℃ under the condition of magnetic stirring, and carrying out heat preservation reaction for 30min to remove water and low-boiling-point impurities in the reaction system.
(3) And continuously heating the mixed solution to 290 ℃, preserving the temperature, reacting for 60min, cooling to room temperature after the reaction is finished, and then washing and centrifuging the solid product for 3 times by using a mixed solution of absolute ethyl alcohol and chloroform with the volume ratio of 3.
Composition, structural characterization and performance testing
FIG. 1 shows the X-ray diffraction pattern of the object obtained in the first example. As can be seen from the figure: all diffraction peaks are good indexes of Cu 3 NbSe 4 (JCPDS Card No. 81-2492) and no impurity peak, indicating that the target product prepared by the method of the embodiment is cubic phase Cu 3 NbSe 4 And (4) crystals. Likewise, the results of fig. 5, 7 and 9 also show that the target products prepared by the second, fourth and sixth examples have similar results to fig. 1.
FIG. 2 is a Transmission Electron Microscope (TEM) photograph of the objective product obtained in the first example, showing that Cu was prepared by the method 3 NbSe 4 The shape is uniform, the size is controllable, and the shape is concretely a nano cube with the size of 15-25 nm. Similarly, the results of fig. 6 and 8 also show that the target products prepared by the third and fifth examples have similar results to those of fig. 2.
FIG. 3 is an ultraviolet-visible (UV-vis) absorption spectrum of the product obtained in the first example, demonstrating cubic phase Cu 3 NbSe 4 The nano material has stronger absorption in the visible light range, which shows that the Cu prepared by the method 3 NbSe 4 The nano material can be used as a photoelectric conversion material to be applied to the research field of photoelectric equipment.
FIG. 4 is an I-t curve of a photodetector constructed by the product obtained in the first embodiment. In this experiment, the target product obtained in the first example and the graphene electrode were formed on a single crystal silicon wafer by a spin coating process to form Cu 3 NbSe 4 A photodetector of the/Si heterostructure type. As shown in fig. 4: the light intensity is 60mW/cm at the wavelength of 520nm 2 And the condition of applying 0.5V bias voltage shows that the photoelectric detector has good responsiveness and stability.
Although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that changes may be made in the embodiments and/or equivalents thereof without departing from the spirit and scope of the invention. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the protection scope of the present invention.

Claims (5)

1. Cubic phase Cu 3 NbSe 4 The preparation method of the nano material is characterized in that the molecular formula of the nano material is Cu 3 NbSe 4 The crystal form is cubic phase; the micro appearance of the nano material is a nano-scale cube; the preparation method comprises the following steps:
(1) Deoxidizing and dehydrating an organic solvent containing a soluble copper source, a niobium source and a selenium source, mixing a reaction medium containing the copper source, the niobium source and the selenium source uniformly under an oxygen-isolated condition, and then heating to 100 to 150 ℃ for reaction for 30 to 60min; then carrying out solvothermal reaction;
the organic solvent is selected from one or more of oleylamine, hexadecylamine or octadecylamine;
cu in the organic solvent: nb: the molar ratio of Se is 3;
the temperature of the solvothermal reaction is kept between 270 and 310 ℃, and the reaction time is controlled between 5 and 120min;
wherein: the copper source is selected from one or more of cuprous chloride, cuprous bromide, copper acetylacetonate, cupric chloride or cupric acetate; the niobium source is selected from one or two of niobium pentachloride and niobium oxalate; in the step (1), the selenium source is selected from one or more of diphenyl diselenide, selenium powder, dibenzyl diselenide or selenium dioxide;
(2) And separating out a solid product obtained by the solvothermal reaction to obtain the catalyst.
2. Cubic phase Cu as claimed in claim 1 3 NbSe 4 The preparation method of the nano material is characterized in that the Cu 3 NbSe 4 The nano material is in a monodisperse state.
3. Cubic phase Cu as claimed in claim 1 3 NbSe 4 The preparation method of the nano material is characterized in that the Cu 3 NbSe 4 The size of the nano material is 15 to 25 nm.
4. Cubic phase Cu as claimed in claim 1 3 NbSe 4 The preparation method of the nano material is characterized in that in the step (2), solid matters in the reaction liquid are separated in a centrifugal or filtering mode, and the centrifugal solid products are washed by mixed liquid of absolute ethyl alcohol and chloroform to obtain target products.
5. Cubic phase Cu produced by the production method according to any one of claims 1 to 4 3 NbSe 4 The application of the nano material in the photovoltaic, thermoelectric or photoelectric field.
CN202111136519.9A 2021-09-27 2021-09-27 Cubic phase Cu 3 NbSe 4 Nano material and preparation method and application thereof Active CN113860270B (en)