CN113520725A - 包含改性液体橡胶的热熔组合物和包含该组合物的吸收芯 - Google Patents
包含改性液体橡胶的热熔组合物和包含该组合物的吸收芯 Download PDFInfo
- Publication number
- CN113520725A CN113520725A CN202010318516.6A CN202010318516A CN113520725A CN 113520725 A CN113520725 A CN 113520725A CN 202010318516 A CN202010318516 A CN 202010318516A CN 113520725 A CN113520725 A CN 113520725A
- Authority
- CN
- China
- Prior art keywords
- hot melt
- absorbent article
- nonwoven
- disposable absorbent
- melt composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明包括一次性吸收制品,其中所要求的热熔组合物用于含有、固定和/或提供强度给吸收芯(即芯稳定化)。热熔组合物包含10重量%至60重量%的热塑性聚合物和3重量%至25重量%的改性液体橡胶。
Description
背景技术
热熔组合物通常用于将基底粘结在一起,以使这两个基底保持彼此固定的关系或者促进最终制品的完整性和功能性。在工业粘合剂领域,热熔组合物通常用于粘结在一起或促进各种制品的完整性和功能性,所述制品包括包含非织造基底的一次性吸收制品,例如成人失禁产品、一次性尿布、卫生巾、床垫、宠物垫、医用敷料等。
已有多种热熔组合物可用在一次性吸收制品的制造中。例如,在一次性尿布的制造中,热熔组合物用作构造粘合剂(例如,将底片粘结到非织造布和任选粘结到吸收垫)、用作弹性附件粘合剂(例如在例如腿部或腰部区域,将弹性材料粘结到底片)、用于芯稳定(例如,将热熔组合物施加于吸收芯(absorbent core)以增加芯的强度)和用作弹性材料以在一次性吸收制品中提供拉伸特性。
构造粘合剂(Construction adhesives)也已经常用于芯稳定。
然而,这些年来,对更薄的吸收芯的需求日益增加。在较薄的芯中,绒毛减少或被省掉并用超吸收性聚合物层代替。因此,芯稳定热熔体所需的性能提高,并且结构粘合剂通常不提供所需的性能。
需要一种替代性热熔组合物,所述组合物可牢固地粘结于吸收制品的芯中的超吸收性材料(super absorbent materials),尤其是当芯完全不含或基本不含绒毛时。
发明内容
一方面,本发明的特征在于一种包含吸收芯的一次性吸收制品,所述吸收芯包含超吸收性聚合物(super absorbent polymer)和热熔组合物(hot melt composition),
所述热熔组合物包含10重量%至60重量%的热塑性聚合物和3重量%至25重量%的改性液体橡胶,其中所述热熔组合物粘附于吸收芯内的超吸收性聚合物。在一个实施方案中,吸收芯基本不含绒毛,或甚至完全不含绒毛。
在另一个实施方案中,吸收芯还包含第一非织造布和第二非织造布,并且热熔组合物和超吸收性聚合物作为层存在于第一非织造布和第二非织造布之间。在一个实施方案中,第一非织造布和第二非织造布为具有7克/平方米至35克/平方米的基重的亲水性非织造布。在一个不同的实施方案中,吸收芯是复合芯。
在另一个实施方案中,一次性吸收制品还包含顶片和底片,并且其中吸收芯位于顶片和底片之间。
在一个实施方案中,改性液体橡胶是羧化聚异戊二烯。在不同的实施方案中,改性液体橡胶具有每分子2至15个极性官能团。在另一个实施方案中,改性液体橡胶以4重量%至25重量%、5重量%至20重量%或甚至10重量%至20重量%存在。
在另一个实施方案中,热塑性聚合物是选自苯乙烯-异戊二烯-苯乙烯、苯乙烯-丁二烯-苯乙烯及其组合的苯乙烯嵌段共聚物。在不同的实施方案中,热塑性聚合物包括苯乙烯-异戊二烯-苯乙烯嵌段共聚物和苯乙烯-丁二烯-苯乙烯嵌段共聚物。在一个实施方案中,苯乙烯嵌段共聚物包括至少一种具有15重量%至75重量%的二嵌段含量的苯乙烯嵌段共聚物。
在一个实施方案中,热熔组合物另外包含40重量%至60重量%增粘剂,和5重量%至30重量%增塑剂。
在另一个实施方案中,热熔组合物包含10重量%至40重量%的热塑性聚合物,4重量%至25重量%的改性液体橡胶,40重量%至60重量%的烃增粘剂,和5重量%至30重量%的增塑剂。在一个实施方案中,热塑性聚合物是苯乙烯嵌段共聚物。
另一方面,本发明的特征在于一种吸收芯,其包含第一非织造布,第二非织造布,施加于第一非织造布的超吸收性聚合物层,施加于第二非织造布上的热熔组合物层,该热熔组合物层包含10重量%至60重量%的热塑性聚合物和3重量%至25重量%的改性液体橡胶,其中第一非织造布和第二非织造布以使得热熔组合物层面向超吸收性聚合物层的方式组合,并且吸收芯基本不含绒毛。
在一个实施方案中,吸收芯完全不含绒毛。在另一个实施方案中,第一非织造布和第二非织造布为SSS非织造布。
本发明的热熔组合物特别适用于芯稳定化。在芯稳定化中,通常为纤维化结构形式的热熔组合物用于将芯的吸收材料保持在适当位置。本发明的组合物是通用的,可用于粘附和稳定来自许多不同供应商的超吸收性聚合物。
其它特征和优点将由以下优选实施方案的描述和权利要求看出来。
术语
绒毛(Fluff)—纤维素纤维
基本不含绒毛—包含少于10重量%绒毛的吸收芯
完全不含绒毛—不含绒毛的吸收芯
具体实施方式
一次性吸收制品
本发明包括一次性吸收制品,其中所要求保护的热熔组合物用于粘附于、包含、固定和/或提供强度给吸收芯的元件(即芯稳定化)。
芯通常在一次性吸收制品内居中,并且通过附接措施(例如,热熔粘合剂)牢固地固定在顶片(例如,非织造布)和底片(例如,聚合物膜)之间。
本发明的热熔组合物可用于粘附、支撑和增强含有超吸水性聚合物(SAP)的芯,所述芯包括基本或完全不含绒毛的那些。
发明人发现,本发明的热熔组合物可成功地粘附于来自许多不同供应商的超吸收性聚合物。
该热熔组合物可用于将超吸收性聚合物和其它吸收材料在干燥(未膨胀状态)和润湿(溶胀状态)下都保持在适当位置。该热熔组合物也可用于使芯中的其它材料彼此粘附或粘附于超吸收层,例如非织造布、薄纱(tissues)等。
除了用于稳定吸收芯之外,该热熔组合物还可用于粘结一次性吸收制品内的各种基底,包括,例如膜(例如聚烯烃(例如聚乙烯和聚丙烯)膜)、多孔基底、纤维素基底、棉、丝、竹、片材(例如纸和纤维片材)、纸制品、织造和非织造纤维网、纤维(例如合成聚合物纤维和纤维素纤维)、弹性体和胶带背衬。
热熔组合物
热熔组合物包含热塑性聚合物和改性液体橡胶。所述热熔粘合剂组合物可另外包含增粘剂和增塑剂。
在一个实施方案中,热熔组合物包含10重量%至60重量%的热塑性聚合物和3重量%至25重量%的改性液体橡胶。
在第二实施方案中,热熔组合物包含10重量%至40重量%苯乙烯嵌段共聚物,4重量%至25重量%改性液体橡胶,30重量%至60重量%增粘剂,和5重量%至30重量%增塑剂。
在另一个实施方案中,热熔组合物包含10重量%至40重量%选自苯乙烯-丁二烯-苯乙烯(SBS)和苯乙烯-异戊二烯-苯乙烯(SIS)的苯乙烯嵌段共聚物和5重量%至20重量%改性液体橡胶。
热熔组合物的粘度可为在160℃不大于20,000cP,在160℃不大于10,000cP,在160℃在约500cP与20,000cP之间,或甚至在160℃在约500cP与10,000cP之间。
热塑性聚合物
热熔组合物包含热塑性聚合物。该热熔粘合剂组合物可包含多于一种热塑性聚合物。热塑性聚合物可以选自乙烯均聚物、乙烯共聚物、丙烯均聚物、丙烯共聚物、苯乙烯嵌段共聚物、它们的官能化形式(例如,羟基改性或马来酸酐改性形式),以及它们的共混物。
热塑性聚合物可以使用各种催化剂制备,包括例如单位点催化剂(例如茂金属催化剂(例如茂金属催化的乙烯α-烯烃共聚物)、限制几何构型催化剂(例如使用限制几何构型催化剂由乙烯和α-烯烃共聚单体制备且具有不大于2.5的多分散指数并具有长链支化的均匀线性或基本线性乙烯α-烯烃互聚物))、多位点催化剂(multiple single sitecatalysts)、齐格勒-纳塔催化剂以及它们的组合。
热塑性聚合物可包含官能团(即,被官能化的),包括例如羟基、羧酸基团、酸酐基团(例如,马来酸酐)、以及它们的组合。
热熔粘合剂组合物可包含10重量%至70重量%、10重量%至60重量%、10重量%至50重量%、10重量%至40重量%、或甚至10重量%至30重量%的热塑性聚合物。
聚合物可以是密度不大于0.90克/立方厘米(g/cm3)或甚至不大于0.88g/cm3的乙烯α-烯烃共聚物。α-烯烃单体具有至少三个碳原子,或甚至3至20个碳原子,其合适的实例包括丙烯、异丁烯、丁烯、戊烯、己烯、庚烯、辛烯、壬烯、癸烯、十二碳烯、4-甲基-1-戊烯、3-甲基-1-戊烯、3,5,5-三甲基-1-己烯、5-乙基-1-壬烯、及其组合。合适的乙烯共聚物的具体实例包括乙烯-丙烯、乙烯-丁烯、乙烯-己烯、乙烯-辛烯以及它们的组合。
有用的乙烯α-烯烃共聚物可以各种商品名购得,包括例如来自DowDuPontChemical Company(Midland,Michigan)的商品名AFFINITY系列,包括例如AFFINITY GA1875、AFFINITY GA 1900和AFFINITY GA 1950乙烯-辛烯弹性体,AFFINITY GA 1000R马来酸酐改性的乙烯-辛烯共聚物(其也被制造商称为互聚物),AFFINITY乙烯-丙烯共聚物,和来自Dow Chemical Company(Midland,Michigan)的商品名ENGAGE系列,包括ENGAGE 8200、ENGAGE 8401和ENGAGE 8402乙烯-辛烯共聚物。
聚合物可以是基于丙烯的聚合物。基于丙烯的聚合物可以选自丙烯α烯烃共聚物和丙烯均聚物。丙烯-α-烯烃共聚物衍生自丙烯和至少一种不同于丙烯的α-烯烃共聚单体(例如C2共聚单体和C4-C20α-烯烃共聚单体,以及它们的组合)。有用的α-烯烃共聚单体包括例如具有至少两个碳原子、至少四个碳原子、四个碳原子至八个碳原子的α-烯烃单体以及它们的组合。合适类别的α-烯烃共聚单体的实例包括单-α烯烃(即,一个不饱和双键)和更高级的α烯烃(例如,二烯(例如,1,9-癸二烯))。合适的α-烯烃单体包括例如乙烯、丁烯、戊烯、己烯、庚烯、辛烯、壬烯、癸烯、十二碳烯、4-甲基-1-戊烯,3-甲基-1-戊烯、3,5,5-三甲基-1-己烯、5-乙基-1-壬烯,以及它们的组合。合适的丙烯-α-烯烃共聚物的具体实例包括丙烯-乙烯、丙烯-丁烯、丙烯-己烯、丙烯-辛烯以及它们的组合。
有用的丙烯-α-烯烃共聚物包括例如共聚物、三元共聚物和更高级聚合物、至少两种不同的丙烯-α-烯烃共聚物的混合物,以及它们的组合。有用的丙烯-α-烯烃共聚物还包括例如改性的、未改性的、接枝的和未接枝的丙烯-α-烯烃共聚物、单模态(uni-modal)丙烯-α-烯烃聚合物、多模态丙烯-α-烯烃共聚物以及它们的组合。术语"多模态(multi-modal)"是指聚合物具有通过尺寸排阻色谱法(SEC)测定的多模态分子量分布(重均分子量(Mw)/数均分子量(Mn))。
合适的市售丙烯-α-烯烃共聚物可以各种商品名获得,包括例如ExxonMobilChemical Company(Houston,Texas)的商品名VISTAMAXX系列,包括VISTAMAXX 6202丙烯-乙烯共聚物、VISTAMAXX 8880丙烯-乙烯共聚物和VISTAMAXX 8380丙烯-乙烯共聚物。合适的丙烯均聚物可以各种商品名商购,包括例如L-MODU S400 S410、S600和S901,来自Idemitsu Kosan Co.,Ltd.(日本)的丙烯均聚物。
在优选的实施方案中,聚合物可以是苯乙烯嵌段共聚物。苯乙烯嵌段共聚物具有至少一个包含苯乙烯的A嵌段和至少一个包含例如弹性体共轭二烯(例如氢化和未氢化的共轭二烯)、倍半萜(例如氢化和未氢化的倍半萜)以及它们的组合的B嵌段。A嵌段和B嵌段以任意结合方式彼此结合,使得所得共聚物显示各种结构,包括例如无规、直链、支化、辐射状(radial)、星形、梳形、递变以及它们的组合。嵌段共聚物可呈现任意形式,包括例如线性A-B嵌段、线性A-B-A嵌段、线性A-(B-A)n-B多嵌段和辐射状(A-B)n-Y嵌段,其中Y是多价化合物且n是至少3的整数,四嵌段共聚物,例如A-B-A-B,和具有A-B-A-B-A结构的五嵌段共聚物。粘合剂组合物可以包含至少两种不同嵌段共聚物的共混物。
合适的苯乙烯A嵌段包括,例如,苯乙烯、α-甲基苯乙烯、邻甲基苯乙烯、间甲基苯乙烯、对甲基苯乙烯、对叔丁基苯乙烯、2,4-二甲基苯乙烯、2,4,6-三甲基苯乙烯,以及它们的组合。
合适的嵌段弹性体共轭二烯B嵌段包括,例如丁二烯(例如聚丁二烯)、异戊二烯(例如聚异戊二烯)、2,3-二甲基-1,3-丁二烯、1,3-戊二烯、1,3-己二烯以及它们的组合,和它们的氢化形式,包括例如乙烯、丙烯、丁烯以及它们的组合。合适的B嵌段倍半萜包括,例如,β法呢烯。苯乙烯嵌段共聚物可具有不饱和中间嵌段,或者中间嵌段可为饱和的,即氢化的。
有用的苯乙烯嵌段共聚物包括,例如,苯乙烯-丁二烯(SB)、苯乙烯-丁二烯-苯乙烯(SBS)、苯乙烯-异戊二烯嵌段(SI)、苯乙烯-异戊二烯-苯乙烯(SIS)、苯乙烯-乙烯-丁烯-苯乙烯(SEBS)、苯乙烯-乙烯-丙烯-苯乙烯(SEPS)、苯乙烯-异丁烯-苯乙烯以及它们的组合。特别有用的嵌段共聚物包括苯乙烯-丁二烯-苯乙烯、苯乙烯-异戊二烯-苯乙烯以及它们的组合。
热熔组合物可以包含多于一种苯乙烯嵌段共聚物。在一个优选的实施方案中,热熔组合物包含苯乙烯-丁二烯-苯乙烯和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的共混物。在另一实施方案中,嵌段共聚物中的至少一种具有15重量%至75重量%,或甚至20重量%至60重量%的二嵌段含量。
苯乙烯嵌段共聚物的苯乙烯含量可为至少10重量%、至少12重量%、不大于50重量%、不大于40重量%、不大于35重量%、10重量%至50重量%、12重量%至45重量%、或甚至12重量%至35重量%。
苯乙烯嵌段共聚物的熔体流动速率ASTM D1238(230℃,2.16kg)可为0.5至300、10至300、或甚至15至250。
有用的嵌段共聚物可以商品名KRATON D系列购自Kraton Corporation(Houston,Texas);以商品名VECTOR系列购自Taiwan Synthetic Rubber Corporation(TSRC)(台北市,中国台湾),包括VECTOR4211和DPX-660苯乙烯-异戊二烯-苯乙烯嵌段共聚物;以商品名GLOBALPRENE系列购自LCY Grit Corp(中国台湾),包括GLOBALPRENE 5516D和以商品名KIBITON系列购自Chi Mei Corp.(中国台湾),包括KIBITON TPE PB-5502。
改性液体橡胶
热熔组合物包含改性液体橡胶(modified liquid rubber)。液体是指橡胶在室温(例如21℃)下为液体。
改性液体橡胶可以包含各种不同的骨架,包括聚异戊二烯、聚丁二烯、苯乙烯-丁二烯共聚物等,它们是以不同的方式聚合的,例如均聚物、共聚物(例如无规共聚物)、嵌段共聚物以及它们的组合。液体橡胶可以是氢化的。
改性是指液体橡胶已由极性官能团改性。极性官能团可以包括羟基、羧基、酸酐基团等。
改性的量可以变化。在一些实施方案中,每分子有2至15个极性官能团。据认为,这种改性改进了对吸收芯中的极性材料如超吸收体(superabsorbent)的粘附。
有用的改性液体橡胶包括羧化聚异戊二烯,其可以LIR商品名购自KurraryCompany,Ltd.(Osaka,日本),包括LIR-403和LIR-410;以及羧化聚丁二烯,其可以RICON商品名购自Cray Valley(Exton,Pennsylvania),包括RICON 130MA8。
改性液体橡胶以2重量%至30重量%、3重量%至25重量%、4重量%至25重量%、5重量%至20重量%、或甚至10重量%至20重量%存在于组合物中。
增塑剂
热熔组合物可以包含增塑剂。增塑剂的类型没有特别限制。
可用的增塑剂包括例如聚丁烯、聚异丁烯、聚烯烃共聚物(例如丙烯-乙烯共聚物)、低聚α烯烃、油(例如环烷石油基的油、石蜡油、矿物油、动物油、植物油、合成油、油的衍生物、未改性的液体橡胶(例如聚异戊二烯、聚丁二烯等)、脂肪酸的甘油酯、以及它们的组合)、以及它们的组合。
有用的增塑剂可以各种商品名购得,包括例如来自Calumet Specialty ProductsPartners,LP(Indianapolis,Indiana)的CALSOL 5550环烷油和来自HRPC(福建,中国)的KN-4010环烷油。
热熔组合物可包含至少5重量%、至少10重量%、5重量%至30重量%、或甚至5重量%至25重量%的增塑剂。
增粘剂
热熔组合物包含增粘剂。增粘剂的类型没有特别限制。
增粘剂在室温下可以是流体或固体。合适的增粘剂类型包括例如芳族、脂族和脂环族烃树脂、混合的芳族和脂族改性烃树脂、芳族改性脂族烃树脂以及它们的氢化形式;萜、改性萜以及它们的氢化形式;天然松香、改性松香、松香酯以及它们的氢化形式;低分子量聚乳酸;以及它们的组合。有用的天然和改性松香的实例包括脂松香、木松香、妥尔油松香(tall oil rosin)、蒸馏松香(distilled rosin)、氢化松香、二聚松香和聚合松香。有用的松香酯的实例包括例如浅色木松香的甘油酯、氢化松香的甘油酯、聚合松香的甘油酯,天然和改性松香的季戊四醇酯,包括浅色木松香的季戊四醇酯、氢化松香的季戊四醇酯、妥尔油松香的季戊四醇酯和松香的酚改性季戊四醇酯。
增粘剂也可以是改性的,即,用极性材料(如羟基、羧基、酸酐基团等)官能化的。
有用的增粘剂可以各种商品名购得,包括例如Exxon Mobil Chemical Company(Houston,Texas)的商品名ESCOREZ系列的烃增粘树脂,包括ESCOREZ 5400、ESCOREZ 5415、ESCOREZ 5600,和Luhua Chemical(中国)的商品名LUHOREZ系列的烃增粘树脂,包括LUHOREZ HD 1100。
热熔组合物可以包含10重量%至70重量%、15重量%至65重量%、30重量%至60重量%或甚至40重量%至60重量%的增粘剂。
附加组分
热熔组合物任选包含附加组分,包括例如稳定剂、抗氧化剂、附加聚合物(例如基于丁烯的烯烃聚合物等)、粘附促进剂、涂料、抗粘添加剂、紫外光稳定剂、腐蚀抑制剂、着色剂(例如颜料和染料)、填料、表面活性剂、湿度指示剂、以及它们的组合。
有用的抗氧化剂包括,例如,季戊四醇四[3,(3,5-二叔丁基-4-羟基苯基)丙酸酯]、2,2'-亚甲基双(4-甲基-6-叔丁基苯酚),亚磷酸酯,包括例如亚磷酸三(对壬基苯基)酯(TNPP),以及4,4'-二亚苯基二亚膦酸双(2,4-二叔丁基苯基)酯,3,3'-硫代二丙酸二硬脂基酯(DSTDP),以及它们的组合。有用的抗氧化剂可以各种商品名购得,包括例如商品名IRGANOX系列,包括例如IRGANOX 1010、IRGANOX 565和IRGANOX 1076受阻酚类抗氧化剂和IRGAFOS 168亚磷酸酯抗氧化剂,所有这些均可购自BASF Corporation(Florham Park,NewJersey),以及ETHYL 702 4,4'-亚甲基双(2,6-二叔丁基苯酚)。当存在时,组合物优选包含约0.1重量%至约2重量%的抗氧化剂。
吸收芯
吸收芯包含芯和任选的芯包裹物(core wrap)。吸收芯可于装配线中在线(即,在一次性吸收制品中)制造。或者,芯可以离线制造,然后卷起(rolled up)或结彩(festooned)以在以后的日期或不同的场所使用。
芯可以在设计、形状和所用材料方面变化。它可以成形为类似于长矩形或类似于狗骨头。它可以是一个连续的形状,或者可以被分成由例如顶片和底片形成的多通道。
芯可以是复合芯(composite core)。复合芯是基本不含绒毛的或甚至完全不含绒毛的。复合芯包含多于一个SAP层,所述SAP层与非织造布或薄纱层以及热熔组合物交替。复合芯可包含与热熔组合物和非织造布或薄纱交替的1-5,或甚至2-4个单独的SAP层。
非织造布可以是高膨松(high loft)或相对蓬松(relatively fluffy)的非织造布,例如SSS非织造布。SSS非织造布包含三层纺粘(spun bond)非织造布,它特别柔软,可改进芯的柔软性。非织造布可包含聚丙烯纤维,并且优选是亲水性的以改善进入芯的吸收。
非织造布可具有相对高的基重(basis weight)。非织造布可具有5克/平方米(gsm)至40gsm、7gsm至30gsm或甚至10gsm至25gsm的基重。
可将热熔组合物施加到第一基底(例如第一非织造布)上,将超吸收性聚合物施加到第二基底(例如第二非织造布)上,然后以使得超吸收性聚合物和热熔组合物彼此面对的方式将基底配对,形成吸收芯的层。
或者,可将热熔组合物施加到第一基底(例如第一非织造布)上,在与第二基底(例如第二非织造布)配对之前将超吸收性聚合物直接施加到热熔组合物之上。
或者,可将超吸收体(superabsorbent)涂敷到第一基底(例如第一非织造布)上,在与第二基底(例如第二非织造布)配对之前将热熔组合物直接施加到超吸收体之上。
第二基底可任选地含有在将这两个基底放在一起之前施加的热熔组合物和超吸收性聚合物。可将这两个基底以使得涂覆侧彼此面对的方式配对。
热熔组合物可作为纤维化网以层的形式施加。所述网可通过如下方式获得:螺旋喷涂、无规喷涂(例如SIGNATURE喷涂,使用购自Nordson Corporation(Westlake,Ohio)的SIGNATURE喷嘴),以及Ω模式喷涂,使用购自ITW Dynatec(Hendersonville,TN)的OMEGA喷嘴。或者,热熔组合物可以作为涂层存在(例如,全缝(full slot)、图案缝(pattern slot)等)。
吸收芯的附加层可由超吸收性聚合物、热熔组合物和基底(例如,非织造布、薄纱等)的附加层形成。附加层的顺序和数量没有特别限制。
芯包含能够吸收通过顶片接收的体液和固体的吸收材料。尽管本发明的芯主要包含SAP作为吸收材料,但吸收芯可含有有限量的其它吸收材料,包括天然纤维素纤维(即绒毛)、木浆、棉、合成纤维、非织造布、薄纱、泡沫或任何其它吸收材料。
如上所述,本发明的芯主要包含SAP作为吸收材料。SAP是合意的,因为它可以吸收和保留相对于其自身质量而言非常大量的液体。聚丙烯酸钠是常用的超吸水性聚合物。然而,其它材料也可用作超吸收性聚合物,包括例如聚丙烯酰胺共聚物、乙烯马来酸酐共聚物、交联的羧甲基纤维素、聚乙烯醇共聚物、交联的聚环氧乙烷以及聚丙烯腈的淀粉接枝共聚物。SAP可以进一步包括生物基材料。
吸收芯可基本不含绒毛,或甚至完全不含绒毛。在完全不含绒毛的芯中,吸收芯包含热熔组合物、超吸收性聚合物和任选的非织造布和/或薄纱层。
芯包裹物可为包裹芯以将芯的组分保持在适当位置的任何材料。芯包裹物通常包裹芯的两个较长侧面,使端部开放。芯包裹物可选自非织造布和薄纱。
吸收芯可用于各种一次性吸收制品中,包括例如一次性尿布、成人失禁产品、卫生巾、医用敷料(例如伤口护理产品)、绷带、手术垫、宠物训练垫(例如宠物垫)和肉包装产品。
现在将通过以下非限制性实施例描述本发明。除非另有说明,实施例中所述的所有份数、比率、百分比和量均以重量计。
实施例
测试程序
除非另有说明,实施例中和整个说明书中使用的测试程序包括以下程序。
热熔组合物制备
在Sigma叶片式混合器中以1千克(kg)批量制备热熔样品。使用约150℃的加热油温度。首先加入聚合物、油、一部分增粘剂和添加剂,共混直至顺滑,然后加入剩余的增粘剂,共混直至顺滑,然后加入液体橡胶和增塑剂。使混合物混合直至均匀,然后倾倒。每个样品用约1.5-2小时制备。
粘度测试方法
粘度是根据标题为"Standard Test Method for Apparent Viscosity ofAdhesives and Coating Materials"的ASTM D-3236-15(May,2015),使用RVDV2型Brookfield Thermosel粘度计和27号锭子测定。结果以厘泊(cP)报告。
动态剥离强度
热熔组合物在160℃的温度下施涂,使用2英寸宽的SIGNATURE(即无规喷涂)模式,4克/平方米(gsm)的增重(或涂布重量),以及在施涂后0.39秒时为5.25牛顿/厘米(3磅/线性英寸)的辊隙压力(nip pressure)。将粘合剂施加到标准亲水性非织造布上,然后层压到标准纺粘非织造布上。
样品如表中所示进行老化。在INSTRON试验机上以25.4厘米(10英寸)/分钟的速度将样品拉开。所报告的值是5次粘结的平均值。
湿剥离强度
样品如上所述在动态剥离强度试验中制备,然后将它们浸入水中,拉出,并将过量水吸干。然后如表中所示将它们老化。
热稳定性
将100克粘合剂装入玻璃罐中,然后用一片铝箔覆盖。然后在设定为180℃的烘箱中老化72小时后,目测评价样品。
SAP粘合试验
将热熔组合物在140-155℃施涂到第一非织造布上,使用5cm宽的SIGNATURE模式以及4克/平方米(gsm)至7gsm的热熔组合物增重。将SAP颗粒施加到热熔组合物上以涂覆该热熔组合物。然后将具有SAP的热熔组合物翻转并将SAP面朝下放置在第二非织造布上以形成层合物。第一和第二非织造布均为15gsm的SSS(3层)亲水性非织造布。
然后将层合物切成10cm长。每10cm长的层合物包含0.7至0.8克SAP。
然后将尺寸为10cm×5cm且中空的金属矩形放置在层合物的顶部上,这样金属矩形形成围绕整个SAP粘合区域的周界。
然后将21-24克染成蓝色的水缓慢地倾倒在层合物的顶部。
一旦水被倾倒并且已完全吸收到SAP中(几分钟),就将第一非织造布从第二非织造布上拉开,并且按照以下指标评价保留在第一非织造布上的SAP的量:
粘结的—粘结区域中的SAP全部留在原位
基本粘结的—粘结区域中的超过75%的SAP留在原位
部分粘结的—粘结区域中的约25%至75%的SAP留在原位
基本未粘结的—粘结区域的大于75%SAP未留在原位
未粘结的—粘结区域中的SAP都未留在原位
表1—实施例中使用的材料
表2—实施例
FLC5720是可从HB Fuller Company获得的基于SBC的热熔构造粘合剂。
它不含改性液体橡胶。
其它实施方案在权利要求书内。
Claims (20)
1.一次性吸收制品,其包含吸收芯,
所述吸收芯包含超吸收性聚合物和热熔组合物;
所述热熔组合物包含:
10重量%至60重量%的热塑性聚合物,和
3重量%至25重量%的改性液体橡胶,
其中所述热熔组合物粘附于所述吸收芯内的所述超吸收性聚合物。
2.根据权利要求1所述的一次性吸收制品,其中吸收芯基本不含绒毛。
3.根据权利要求1或2所述的一次性吸收制品,其中吸收芯完全不含绒毛。
4.根据权利要求1至3任一项所述的一次性吸收制品,其中所述吸收芯还包含第一非织造布和第二非织造布,所述热熔组合物和所述超吸收性聚合物作为所述第一非织造布和所述第二非织造布之间的层存在。
5.根据权利要求4所述的一次性吸收制品,其中所述第一非织造布和所述第二非织造布为具有7克/平方米至35克/平方米的基重的亲水性非织造布。
6.根据权利要求1至5任一项所述的一次性吸收制品,其中所述吸收芯为复合芯。
7.根据权利要求1至6任一项所述的一次性吸收制品,其还包含顶片和底片,其中所述吸收芯位于所述顶片和所述底片之间。
8.根据权利要求1至7任一项所述的一次性吸收制品,其中所述改性液体橡胶为羧化聚异戊二烯。
9.根据权利要求1至8任一项所述的一次性吸收制品,其中所述改性液体橡胶具有每分子2至15个极性官能团。
10.根据权利要求1至9任一项所述的一次性吸收制品,其中所述改性液体橡胶以4重量%至25重量%存在。
11.根据权利要求1至10任一项所述的一次性吸收制品,其中所述改性液体橡胶以5重量%至20重量%存在。
12.根据权利要求1至11任一项所述的一次性吸收制品,其中所述改性液体橡胶以10重量%至20重量%存在。
13.根据权利要求1至12任一项所述的一次性吸收制品,其中所述热塑性聚合物为苯乙烯嵌段共聚物,其选自苯乙烯-异戊二烯-苯乙烯、苯乙烯-丁二烯-苯乙烯以及它们的组合。
14.根据权利要求1至12任一项所述的一次性吸收制品,其中所述热塑性聚合物包含苯乙烯-异戊二烯-苯乙烯嵌段共聚物和苯乙烯-丁二烯-苯乙烯嵌段共聚物。
15.根据权利要求13或14所述的一次性吸收制品,其中所述苯乙烯嵌段共聚物包含至少一种具有15重量%至75重量%的二嵌段含量的苯乙烯嵌段共聚物。
16.根据权利要求1至15任一项所述的一次性吸收制品,其中所述热熔组合物还包含:
40重量%至60重量%的增粘剂,和
5重量%至30重量%的增塑剂。
17.根据权利要求1至16任一项所述的一次性吸收制品,其中所述热熔组合物包含:
10重量%至40重量%的热塑性聚合物,
4重量%至25重量%的改性液体橡胶,
40重量%至60重量%的烃增粘剂,和
5重量%至30重量%的增塑剂。
18.根据权利要求1至17任一项所述的一次性吸收制品,其中所述热塑性聚合物为苯乙烯嵌段共聚物。
19.吸收芯,其包含:
a.第一非织造布,
b.第二非织造布,
c.施加到所述第一非织造布上的超吸收性聚合物层,
d.施加到第二非织造布上的热熔组合物层,其包含:
i.10重量%至60重量%的热塑性聚合物,和
ii.3重量%至25重量%的改性液体橡胶,
其中第一非织造布和第二非织造布以使得热熔组合物层面向超吸收性聚合物层的方式组合,并且吸收芯基本不含绒毛。
20.根据权利要求19所述的吸收芯,其中所述吸收芯完全不含绒毛。