CN113372880A - 一种防冻保湿扬尘抑制剂及其制备方法 - Google Patents
一种防冻保湿扬尘抑制剂及其制备方法 Download PDFInfo
- Publication number
- CN113372880A CN113372880A CN202110575197.1A CN202110575197A CN113372880A CN 113372880 A CN113372880 A CN 113372880A CN 202110575197 A CN202110575197 A CN 202110575197A CN 113372880 A CN113372880 A CN 113372880A
- Authority
- CN
- China
- Prior art keywords
- percent
- dust
- water
- inhibitor
- freezing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及环保领域，为了解决抑尘剂喷洒后容易结冰导致路面打滑的问题，公开了一种防冻保湿扬尘抑制剂及其制备方法，所述一种防冻保湿扬尘抑制剂，包括以下组分：高分子基材、抗冻剂、吸湿剂、分散剂、渗透剂、水。本发明制备的扬尘抑制剂通过喷洒作业过程渗透剂能够携带各组分浸入路面表层，高分子基材充分吸水膨胀能够在路面上形成一层透气保湿的高分子膜，能够在低温条件下保持不结冰状态。本发明所述的一种防冻保湿扬尘抑制剂中的吸水因子能够吸附潮湿空气中的水蒸气，能够起到持续保湿5‑7天左右；透气保湿的高分子膜能够抑制粉尘离开地面，从而达到抑尘的目的。
Description
技术领域
本发明涉及环保技术领域，尤其涉及一种防冻保湿扬尘抑制剂及其制备方法。
背景技术
空气污染是目前环保领域亟需解决的问题，而城市的主要大气污染物为可吸入颗粒，路面车辆行驶等会带起扬尘，特别是在冬季，干旱寒冷的北方地区因可吸入颗粒物造成的空气污染尤其严重。目前，解决粉尘颗粒问题有效方法之一是喷洒抑尘剂，但是在北方地区在冬季气候条件下，普通的抑尘剂喷洒后容易结冰导致路面打滑，给安全带来了一定的隐患。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种防冻保湿扬尘抑制剂及其制备方法。
为了实现上述目的，本发明采用了如下技术方案：
一种防冻保湿扬尘抑制剂，包括以下重量比的组分：高分子基材6％-15％、抗冻剂30％-50％、吸湿剂3％-13％、分散剂4％-10％、渗透剂0.3％-0.8％，水补至100％。
优选的，所述高分子基材包括羟乙基纤维素、羧甲基纤维素钠、聚丙烯酸钠、聚丙烯酸、聚乙烯吡咯烷酮K30、聚乙烯吡咯烷酮K60、聚乙烯吡咯烷酮K90、聚乙烯醇等其中的一种或者几种的混合物。
优选的，所述抗冻剂包括氯化钙、乙酸钠、氯化镁、亚硝酸钠、氯化钠中的一种或多种的混合物。
优选的，所述吸湿剂包括甘油、山梨糖醇、吡咯烷酮羧酸、动物胶、透明质酸钠中的一种或多种的混合物。
优选的，分散剂包括十二烷基硫酸钠、三聚磷酸钠、聚丙烯酰胺中的一种或多种的混合物。
优选的，渗透剂包括脂肪醇聚氧乙烯醚(AEO-9)、聚氧乙烯辛基苯酚醚(OP-10)种的一种或多种的混合物。
上述防冻保湿扬尘抑制剂的制备方法，包括以下步骤：
按重量百分比称取以下组分：高分子基材6％-15％、抗冻剂30％-50％、吸湿剂3％-13％、分散剂4％-10％、渗透剂0.3％-0.8％，水补至100％；
将高分子基材和分散剂加入水中，加热到30-60℃，搅拌混合均匀；
将渗透剂、抗冻剂、吸湿剂、分散剂依次加入搅拌均匀，得到扬尘抑制剂。
优选的，搅拌速率为500-1500r/min，搅拌时间为15-50min。
上述防冻保湿扬尘抑制剂的使用方法，温度为-10℃时，按体积比1：10加水使用；温度为-12℃时，按体积比1：8加水使用；温度为-15℃时，按体积比1：6加水使用；温度为-20℃时，按体积比1：4加水使用。
本发明的有益效果为：
本发明所述的一种防冻保湿扬尘抑制剂通过喷洒作业过程渗透剂能够携带各组分浸入路面表层，高分子基材充分吸水膨胀能够在路面上形成一层透气保湿的高分子膜，能够在低温条件下保持不结冰状态。本发明所述的一种防冻保湿扬尘抑制剂中的吸水因子能够吸附潮湿空气中的水蒸气，能够起到持续保湿5-7天左右；透气保湿的高分子膜能够抑制粉尘离开地面，从而达到抑尘的目的。本发明所述的扬尘抑制剂实现了在低温条件下洒水抑尘的操作，合理使用能够避免在气温较低情况下作业产生的路面湿滑的现象，不会影响寒冷天气条件下市民的正常生活。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
实施例1
按表中重量百分比称取各组分：
| 名称 | 含量 |
| 聚乙烯吡咯烷酮K30 | 5.0％ |
| 透明质酸钠 | 1.0％ |
| 山梨糖醇 | 2.0％ |
| 氯化钙 | 15.0％ |
| 乙酸钠 | 21.5％ |
| AEO-9 | 0.6％ |
| 十二烷基硫酸钠 | 6.0％ |
| 水 | 48.9％ |
在釜中加水，将十二烷基硫酸钠加入水中，加入聚乙烯吡咯烷酮K30，加热到40℃，以1500r/min的搅拌速率快速搅拌50min，搅拌混合均匀；将其他组分按AEO-9、氯化钙、乙酸钠、山梨糖醇、透明质酸钠依次加入，以500r/min的搅拌速率搅拌15min搅拌均匀。
实施例2
按表中重量百分比称取各组分：
| 名称 | 含量 |
| 羧甲基纤维素钠 | 3.0％ |
| 聚乙烯吡咯烷酮K90 | 3.5％ |
| 甘油 | 1.0％ |
| 山梨糖醇 | 2.0％ |
| 氯化镁 | 25.0％ |
| 亚硝酸钠 | 15.0％ |
| OP-10 | 0.5％ |
| 十二烷基硫酸钠 | 5.0％ |
| 水 | 45.0％ |
在釜中加水，将十二烷基硫酸钠加入水中，加入羧甲基纤维素钠、聚乙烯吡咯烷酮K90，加热到50℃，快速搅拌混合均匀。将其他组分按OP-10、氯化镁、亚硝酸钠、甘油、山梨糖醇依次加入搅拌均匀。
实施例3
按表中重量百分比称取各组分：
在釜中加水，将三聚磷酸钠加入水中，加入聚乙烯吡咯烷酮K30、羟乙基纤维素，加热到40℃，快速搅拌混合均匀。将其他组分按OP-10、乙酸钠、氯化钠、山梨糖醇、动物胶依次加入搅拌均匀。
实施例4
按表中重量百分比称取各组分：
| 名称 | 含量 |
| 羟乙基纤维素 | 7.5％ |
| 聚乙烯吡咯烷酮K30 | 2.5％ |
| 透明质酸钠钠 | 5.0％ |
| 山梨糖醇 | 5.0％ |
| 乙酸钠 | 15.0％ |
| 亚硝酸钠 | 20.0％ |
| 聚氧乙烯辛基苯酚醚(OP-10) | 0.5％ |
| 聚丙烯酰胺 | 5.0％ |
| 水 | 39.5％ |
在釜中加水，将聚丙烯酰胺加入水中，加入羟乙基纤维素、聚乙烯吡咯烷酮K30，加热到40℃，快速搅拌混合均匀。将其他组分按OP-10、乙酸钠、亚硝酸钠、山梨糖醇、透明质酸钠依次加入搅拌均匀。
实施例5
按表中重量百分比称取各组分：
在釜中加相应量水，将十二烷基硫酸钠加入水中，加入羟乙基纤维素、羧甲基纤维素钠，加热到30℃，快速搅拌混合均匀。将其他组分按AEO-9、氯化钙、乙酸钠、甘油、山梨糖醇依次加入搅拌均匀。
实施例6
按表中重量百分比称取各组分：
| 名称 | 含量 |
| 可溶性淀粉 | 3.5％ |
| 高吸水性树脂 | 3.0％ |
| 甘油 | 1.0％ |
| 山梨糖醇 | 2.0％ |
| 氯化钙 | 15.0％ |
| 氯化钠 | 20.0％ |
| 十二烷基苯磺酸钠 | 8.6％ |
| 水 | 46.9％ |
在釜中加相应量水，将十二烷基硫酸钠加入水中，加入可溶性淀粉、高吸水性树脂，加热到40℃，快速搅拌混合均匀。将其他组分按甘油、山梨糖醇、氯化钙、氯化钠依次加入搅拌均匀。
实施例7
按表中重量百分比称取各组分：
| 名称 | 含量 |
| 高吸水性树脂 | 3.5％ |
| 羟乙基纤维素 | 3.0％ |
| 甘油 | 1.0％ |
| 山梨糖醇 | 2.0％ |
| 氯化钙 | 15.0％ |
| 亚硝酸钠 | 20.0％ |
| 十二烷基硫酸钠 | 8.6％ |
| 水 | 46.9％ |
在釜中加相应量水，将十二烷基硫酸钠加入水中，加入高吸水性树脂、羟乙基纤维素，加热到40℃，快速搅拌混合均匀。将其他组分按甘油、山梨糖醇、氯化钙、亚硝酸钠依次加入搅拌均匀。
冰点、抑尘效率、腐蚀性、沥青路面横向力系数SFC是评价防冻保湿扬尘抑制剂的因素，对本发明实施例1-7制备所得的防冻保湿扬尘抑制剂(按体积比1：10加水使用)的以上性能进行测试，具体结果如表1所示：
表1各实施例(按体积比1：10稀释)的性能
由表1可得,实施例4综合性能最好。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (8)
1.一种防冻保湿扬尘抑制剂，其特征在于，包括以下重量比的组分：高分子基材6%-15%、抗冻剂30%-50%、吸湿剂3%-13%、分散剂4%-10%、渗透剂0.3%-0.8%，水补至100%。
2.根据权利要求1所述的一种防冻保湿扬尘抑制剂，其特征在于，所述高分子基材包括羟乙基纤维素、羧甲基纤维素钠、聚丙烯酸钠、聚丙烯酸、聚乙烯吡咯烷酮K30、聚乙烯吡咯烷酮K60、聚乙烯吡咯烷酮K90、聚乙烯醇等其中的一种或者几种的混合物。
3.根据权利要求1所述的一种防冻保湿扬尘抑制剂，其特征在于，所述抗冻剂包括氯化钙、乙酸钠、氯化镁、亚硝酸钠、氯化钠中的一种或多种的混合物。
4.根据权利要求1所述的一种防冻保湿扬尘抑制剂，其特征在于，所述吸湿剂包括甘油、山梨糖醇、吡咯烷酮羧酸、动物胶、透明质酸钠中的一种或多种的混合物；分散剂包括十二烷基硫酸钠、三聚磷酸钠、聚丙烯酰胺中的一种或多种的混合物；渗透剂包括脂肪醇聚氧乙烯醚(AEO-9)、聚氧乙烯辛基苯酚醚(OP-10)种的一种或多种的混合物。
5.根据权利要求1所述的一种防冻保湿扬尘抑制剂，其特征在于，包括以下重量比的组分：高分子基材10%、抗冻剂35%、吸湿剂10%、分散剂5%、渗透剂0.5%，水39.5%。
6.如上述权利要求1-5任一所述的一种防冻保湿扬尘抑制剂的制备方法，其特征在于，包括以下步骤：
按重量百分比称取以下组分：高分子基材6%-15%、抗冻剂30%-50%、吸湿剂3%-13%、分散剂4%-10%、渗透剂0.3%-0.8%，水补至100%；
将高分子基材和分散剂加入水中，加热到30-60℃，搅拌混合均匀；
将渗透剂、抗冻剂、吸湿剂、分散剂依次加入搅拌均匀，得到扬尘抑制剂。
7.根据权利要求6所述的一种防冻保湿扬尘抑制剂的制备方法，其特征在于，搅拌速率为500-1500r/min，搅拌时间为15-50min。
8.如上述权利要求1-5任一所述的一种防冻保湿扬尘抑制剂的使用方法，其特征在于，温度为-10℃时，按体积比1：10加水使用；温度为-12℃时，按体积比1：8加水使用；温度为-15℃时，按体积比1：6加水使用；温度为-20℃时，按体积比1：4加水使用。