CN113280419A - Method for regulating and controlling room temperature by using heat storage material - Google Patents
Method for regulating and controlling room temperature by using heat storage material Download PDFInfo
- Publication number
- CN113280419A CN113280419A CN202110640720.4A CN202110640720A CN113280419A CN 113280419 A CN113280419 A CN 113280419A CN 202110640720 A CN202110640720 A CN 202110640720A CN 113280419 A CN113280419 A CN 113280419A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat conduction
- heat storage
- phase
- phase change
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for regulating and controlling room temperature by using a heat storage material, which is characterized in that a phase-change heat storage plate is laid in a room, the phase-change material packaged in the phase-change heat storage plate absorbs heat in the daytime to realize liquefaction heat storage, and then is solidified at night to release heat to realize temperature regulation and control in the room. The invention has the advantages of higher heat storage and release efficiency of the heat storage and release material, capability of more efficiently and reliably realizing room temperature regulation and control, more contribution to energy conservation and the like.
Description
Technical Field
The invention relates to the technical field of building walls, in particular to a method for regulating and controlling room temperature by using a heat storage material.
Background
With the improvement of living standard of people, the design of a temperature regulation and control system is considered in the design and manufacture of the modern buildings so as to improve the comfort of rooms of the buildings. The common building temperature regulation is usually realized by installing an air conditioning system, and higher cost is required.
In order to control temperature and reduce cost, people consider arranging a phase-change material in a building board, wherein the phase-change material can be liquefied and absorb heat at high temperature in the day to reduce indoor air conditioning load, and then release heat at low temperature at night to heat the interior of a room; therefore, the heat storage and release adjustment can be realized by means of the phase-change material, the air conditioner load is greatly reduced, and the indoor environment comfort level of a room is improved. For example, CN107227807A discloses a phase change energy storage building thermal insulation structure, CN107419819A discloses an energy storage building wall structure containing double layers of phase change material plates, and the like.
However, in the existing building board materials which rely on the phase-change material to realize the heat storage and release functions, the phase-change material in the board and the outdoor environment outside the board realize heat transfer through the board material, so that the defects of limited heat transfer efficiency and low heat storage and release efficiency of the phase-change material exist, the heat storage and release effect is reduced, the load of an indoor air-conditioning heating system is increased, and the energy is not saved.
Disclosure of Invention
Aiming at the defects of the prior art, the technical problems to be solved by the invention are as follows: how to provide a method for regulating and controlling the room temperature by using a heat storage material, which has higher heat storage and release efficiency, can improve the heat storage and release effect and the room temperature control and regulation effect and is more beneficial to saving energy.
In order to solve the technical problems, the invention adopts the following technical scheme:
a method for regulating and controlling room temperature by using heat storage materials is characterized in that a phase change heat storage plate is laid in a room, the phase change materials packaged in the phase change heat storage plate absorb heat in the daytime to realize liquefaction heat storage, and then the phase change materials are solidified and released heat at night to realize temperature regulation and control in the room.
Like this, realize the inside and outside heat conduction of panel through metal heat conduction frame for be provided with the heat conduction effect of metal heat conduction frame region in the building panel body in everywhere position and obtain very big improvement, improved between the building panel outside and inside and the heat transfer effect between the region everywhere inside, and then improved the holistic heat efficiency that holds of building panel, improved panel to room control by temperature change regulation effect, more be favorable to the energy saving.
The method for regulating and controlling the room temperature by using the heat storage material is realized by the following phase change heat storage plate, wherein the phase change heat storage plate comprises a building plate body, a plurality of phase change material particles are packaged in the building plate body, and a metal heat conduction frame is embedded in the building plate body.
Therefore, when the phase change heat storage plate is used, the heat storage and release functions can be realized by the phase change material particles packaged in the phase change heat storage plate, and the temperature control adjustment in a room is realized. The metal heat conduction frame is additionally arranged, so that the heat transfer efficiency inside and outside the plate can be greatly improved, and the energy is saved.
Furthermore, the metal heat conduction frame comprises a plurality of layers of horizontal net racks arranged at intervals up and down, and vertical net racks arranged in a criss-cross mode are arranged among the horizontal net racks of each layer, so that the metal heat conduction frame integrally forms a three-dimensional net rack structure.
Therefore, the heat conduction efficiency of all parts in the plate can be better improved, and the preparation of the metal heat conduction frame is convenient.
Further, the metal heat conduction frame is arranged along the whole space area of the building plate body.
Therefore, the heat conduction efficiency of all parts in the plate can be better improved. Specifically, the metal heat conduction frame can be consistent in length and width dimensions and plate dimensions, and the thickness dimension is 1-5mm lower than that of the plate. This ensures the best heat conduction while leaving room for the outer surface to be provided with the steel mesh sheet and the graphite powder material coating.
Furthermore, phase change material particles inside the building board body are attached to the metal heat conduction frame.
In this way, heat conduction between the phase change material and the exterior of the building panel may be better achieved through the metal heat conducting frame.
Further, the metal heat conduction frame is made of ferromagnetic metal materials.
Therefore, the magnetic phase-change material particles can be conveniently adopted to be attracted to the surface of the metal heat conduction frame in the preparation process, and heat conduction is better realized through the metal heat conduction frame.
Further, the metal heat conduction frame is made of steel wire mesh sheets.
Therefore, the cost is low, the preparation is facilitated, the heat conductivity is good, the surface strength and the overall strength of the plate can be better improved, and the plate is prevented from cracking. When the metal heat conduction frame is prepared, the horizontal net rack of the single layer can be cut out by adopting the steel wire mesh sheet independently, then the vertical net rack arranged in a vertically and horizontally staggered manner is welded above the horizontal net rack, and then the horizontal net racks with the multiple layers of the vertical net racks are overlapped and welded into a whole to obtain the three-dimensional net rack structure. Thus, the manufacture is convenient, fast and reliable.
Further, the building board body is a gypsum board.
Therefore, gypsum is used as a gel material, so that the phase change material particles are conveniently packaged, the production and the manufacture of the plate are facilitated, and the cost of the plate can be reduced while the plate is ensured to have enough hardness. Meanwhile, gypsum is used as a gel material, in the production and preparation process of the board, a large amount of heat is released in the hydration process of the gypsum material which is hydrated from anhydrous calcium sulfate to generate calcium sulfate dihydrate, the phase-change material particles are liquefied by heat absorption, and the board is not completely solidified at the moment, so that the non-wettability between the phase-change material and the gypsum material and the attraction performance between the phase-change material and the metal heat conduction frame can be utilized, and the adhering state of the phase-change material and the metal heat conduction frame from the original point contact is converted into the adhering state of surface contact. After the plate is finally solidified and formed, the phase-change material and the metal heat conduction frame are attached and compact, so that the heat conduction effect from the metal heat conduction frame to the phase-change material is greatly improved.
Furthermore, the surface of at least one side of the building board body is an inner decorative surface, a layer of metal mesh cloth is laid on the surface of the metal heat conduction frame where the inner decorative surface is located, and the metal mesh cloth is embedded and fixed in the gel material of the building board body.
Therefore, when the building board is used, the interior surface is positioned on the inner side of a room, and the existence of the metal mesh cloth can further greatly improve the conduction efficiency from heat in the room to the metal heat conduction frame; meanwhile, the metal mesh cloth can also improve the surface hardness of the building board and improve the surface quality.
Furthermore, the outer surface of the metal mesh cloth is also provided with a layer of graphite powder material coating.
The graphite powder coating can better conduct heat, improve the surface radiation absorption rate of the building board, improve the surface compactness of the building board and improve the surface decoration effect of the board.
Furthermore, a decorative layer is arranged on the surface of the graphite powder material coating.
The decorative layer can better improve the appearance of the plate and improve the decoration of the plate. The decorative layer can be a sprayed glaze layer or a pattern layer.
Further, the phase change material particles are a solid mixture containing 75-80 parts (optimally 78 parts) of paraffin, 13-17 parts (optimally 15 parts) of high-density polyethylene, 1.3-3 parts (optimally 2.2 parts) of silicon dioxide and 4-5.5 parts (optimally 4.8 parts) of carbon material in parts by mass.
The phase-change material particles are prepared by adopting the raw materials in the proportion, wherein paraffin occupies an absolute majority proportion as a phase-change material main body, the phase-change effect is ensured, high-density polyethylene and silicon dioxide are used as supporting materials, the material strength and the applied plate strength can be better improved, granulation can be better realized, the carbon material is kept in a graphite state, the self heat conductivity of the phase-change material particles can be better improved, the equivalent heat conductivity coefficient of the prepared product can be larger than 0.73W/(m ℃), and the latent heat of phase change can be larger than 112kJ/kg, so that the use requirement is greatly met. Therefore, the phase change particle material with the composition ratio has the characteristics of excellent heat storage and release effect and excellent heat transfer effect, the phase change temperature region is just in the range of the suitable temperature of a human body about 27 ℃, and meanwhile, the phase change material of the raw material has good non-wetting property with gypsum used as a gel material in a liquefied state, the working stability of the phase change material is ensured, and the like.
Further, the particle size of the phase-change material particles is 8-10mm
The phase-change material particles with the particle size are convenient to granulate during production and preparation, are convenient to mix with gel materials when used for building boards, and meanwhile, in the manufacturing process of the building boards, the smaller particle size is more convenient to enable the material particles to attract and draw close to a metal heat conduction frame in the building boards through vibration.
Furthermore, the phase change material particles also contain 3-15 parts by mass (or 3-15% by mass) of magnetic powder material.
Therefore, the prepared phase-change material particles contain certain magnetism, so that when the phase-change material particles are applied to the phase-change heat storage plate, the phase-change material particles can be better attracted and attached to the metal heat conduction frame in the preparation process of the plate, and the heat conduction effect from the phase-change material particles to the metal heat conduction frame is improved.
Further, the phase change material particles are prepared from the following raw materials in parts by mass, wherein the raw materials for preparing the phase change material particles comprise 75-80 parts (optimally 78 parts) of paraffin, 13-17 parts (optimally 15 parts) of high-density polyethylene, 0.5-1.5 parts (optimally 1 part) of diatomite, 0.8-1.5 parts (optimally 1.2 parts) of silica powder, 4-5.5 parts (optimally 4.8 parts) of graphite and 3-15 parts (optimally 8 parts) of magnetic powder.
Therefore, the silicon dioxide raw material in the phase-change material particles is obtained by adding the diatomite and the silica powder, so that the framework strength of the paraffin phase-change material, the uniform dispersibility of the mixed material and the flame retardant property of the material can be better improved. The carbon material in the phase change particulate material is obtained from graphite. Therefore, the method is not only beneficial to the increase of the self heat-conducting property of the phase-change material particles, but also can utilize the porous characteristic of the graphite to load other materials in the preparation process to complete mixing, thereby improving the material mixing effect.
Further, when the phase-change material particles are prepared, the graphite material and the magnetic powder material are separately mixed, and then the rest materials are mixed and granulated.
Therefore, the graphite and the magnetic powder are mixed firstly, so that the magnetic powder material can be loaded in the pores of the graphite, and then the rest materials are mixed, so that the magnetic powder can be uniformly distributed when the materials are mixed, the quality can be balanced, and the phenomenon that the materials are layered when being granulated in a molten state due to the fact that the magnetic powder has high specific gravity and the graphite has low specific gravity is avoided. The quality of the phase-change material particles obtained by granulation is ensured.
Further, the phase change material particles are prepared by the following preparation method: a, obtaining the following raw materials in parts by mass: 75-80 parts of powdered paraffin (optimally 78 parts), 13-17 parts of powdered high-density polyethylene (optimally 15 parts), 0.5-1.5 parts of diatomite (optimally 1 part), 0.8-1.5 parts of silica powder (optimally 1.2 parts), 4-5.5 parts of expandable graphite powder (optimally 4.8 parts) and 3-15 parts of magnetic powder material (optimally 7 parts); b, heating expandable graphite powder to expand the expandable graphite powder, adding the magnetic powder material while keeping the expanded state, and uniformly stirring to complete the loading of the graphite on the magnetic powder material; c, adding paraffin wax and continuing stirring, and adding the rest raw materials and continuing stirring uniformly in the process that the temperature of the graphite falls back and is gradually reduced; d, pouring the mixture obtained in the step c in a still flowing state into a granulator for granulation.
Like this, adopt expanded graphite powder heating earlier and make its inflation, the volume increase, then add the stirring of magnetic powder material, can make magnetic powder material enter into graphite hole depths well, accomplish the load to the magnetic powder material. Then adding powdered paraffin, and utilizing the temperature of the expanded graphite to quickly melt the paraffin and enter the graphite pores to block the magnetic powder material; with the decrease of the graphite temperature, the graphite volume is gradually reduced and recovered to the normal volume proportion, the redundant part of paraffin is extruded from the graphite pores to form a fluid mixture with the main volume proportion occupied by the paraffin, and then the rest raw materials are added to be well stirred in the fluid paraffin and then granulated. Therefore, the method can better complete the loading of the magnetic powder material and the fusion with the paraffin material by utilizing the characteristics of the expanded graphite, greatly improve the uniformity of material distribution and ensure the granulation quality.
Further, in step b, expandable graphite is treated in a muffle furnace (RIMG 0114) at 800 ℃ for 30 seconds to complete expansion heating.
Therefore, the graphite expanding device has the advantages of convenience, rapidness and simplicity in operation, and the graphite can be expanded to hundreds of times, so that the magnetic powder material can be conveniently loaded and fused with the paraffin material. Of course, other heating devices may be used to heat the substrate.
And d, granulating by using a double-screw extrusion granulator.
The double-screw extrusion type granulator is mature existing equipment, has a heating function, can ensure that materials are granulated in a melt blending state at about 130-140 ℃, better meets the characteristic requirements of phase-change material particles on granulation, and has a stirring function during granulation, so that the materials are better uniformly mixed.
The invention also discloses a preparation method of the phase change heat storage plate, which comprises the following steps: 1) firstly, preparing a ferromagnetic metal heat conduction frame (preferably the metal heat conduction frame) with a three-dimensional grid structure, and flatly laying the metal heat conduction frame in a cavity of a plate forming mold; 2) adding the gel material into phase-change material particles (preferably the phase-change material particles) containing magnetic powder components and corresponding water, mixing and stirring uniformly to form a fluid mixture, pouring the fluid mixture into a mold cavity, and leveling; 3) installing a vibrator on the plate forming mold, vibrating the plate forming mold in the process of pouring the fluid mixture into the mold cavity, and keeping vibrating for a period of time after pouring is finished; 4) and removing the mold after the gel material is solidified and formed.
Therefore, in the preparation process of the phase change heat storage plate, the phase change material particles can be tightly attracted to the metal heat conduction frame by adopting a vibration mode during pouring depending on the attraction performance between the ferromagnetic metal heat conduction frame and the phase change material particles containing magnetic powder components. The phase change heat storage plate finally obtained can better realize the mutual heat conduction of phase change material particles at each position in the plate and the heat conduction between the inner part and the outer surface of the plate by means of the metal heat conduction frame, and greatly improves the heat conduction performance of the plate.
Further, the gel material adopted in the step 2) is mainly anhydrous gypsum powder, and is added according to the following mass portion ratio, 65-75 parts (optimally 70 parts) of phase change material particles and 25-30 parts (optimally 27 parts) of anhydrous gypsum powder.
Thus, hydration reaction of the anhydrous gypsum is utilized, and crystal water is combined to generate calcium sulfate dihydrate to realize solidification, so that the prepared board is the gypsum board. The gypsum board can reduce the cost and ensure that the board has enough hardness. Meanwhile, a large amount of heat can be released in the hydration process of the gypsum material, the heat enables phase-change material particles to absorb heat to be liquefied, and the board is not completely solidified at the moment, so that the non-wetting property between the phase-change material and the gypsum material and the suction performance between the phase-change material and the metal heat conduction frame can be utilized, and the phase-change material and the metal heat conduction frame are in a contact state from the original point contact state to a surface contact state. After the plate is finally solidified and formed, the phase-change material and the metal heat conduction frame are attached and compact, so that the heat conduction effect from the metal heat conduction frame to the phase-change material is greatly improved.
Further, graphite powder is added into the gel material according to the proportion of 1-5 parts by mass (optimally 3 parts by mass).
Therefore, the added graphite powder can improve the heat-conducting property and the emissivity of the gel material and improve the flame retardant property of the gel material.
Further, in the step 2), after the fluid mixture is poured into the die cavity, the fluid mixture is leveled to just submerge the metal heat conduction frame, a layer of metal mesh cloth is laid on the metal heat conduction frame, and the metal mesh cloth is solidified and formed into a whole by means of gel materials.
Therefore, the arranged metal mesh cloth can better improve the heat transfer effect of the surface and the interior of the plate and can well strengthen the surface hardness and the quality of the plate.
Further, in the step 3), after the fluid mixture is poured into the mold cavity and leveled, the temperature inside the mold cavity is controlled during vibration, so that the temperature inside the fluid mixture is higher than the phase transition temperature of the phase change material particles, and vibration and temperature maintenance are stopped after lasting for 10-100 seconds.
Therefore, when the plate is not solidified, the internal phase-change material particles absorb heat and liquefy, and the adhesion performance between the phase-change material particles and the metal heat conduction frame is utilized, so that the phase-change material and the metal heat conduction frame are in a state of being adhered to each other by original point contact and are converted into a state of being adhered to each other by surface contact. After the plate is finally solidified and formed, the phase-change material and the metal heat conduction frame are attached and compact, so that the heat conduction effect from the metal heat conduction frame to the phase-change material is greatly improved.
And further, in the step 3), controlling and maintaining the temperature inside the die cavity of the die by means of an electric heating module arranged on the die. Thus, control is conveniently achieved.
Further, the method also comprises a step 5) of brushing or spraying a graphite powder coating on the upper surface of the building board body obtained by the step 4) of removing the formwork.
Therefore, the graphite powder coating can better conduct heat, improve the surface radiation absorption rate of the building board, improve the surface compactness of the building board and improve the surface decoration effect of the board.
Furthermore, a decorative layer is arranged on the surface of the graphite powder material coating.
The decorative layer can better improve the appearance of the plate and improve the decoration of the plate. The decorative layer can be a sprayed glaze layer or a pattern layer.
In conclusion, the invention has the advantages of higher heat storage and release efficiency of the heat storage and release material, capability of realizing room temperature regulation more efficiently and reliably, more contribution to energy conservation and the like.
Drawings
Fig. 1 is a schematic structural view of a phase change thermal storage plate according to the present invention.
Detailed Description
The present invention will be described in further detail with reference to specific embodiments.
In the specific implementation:
a method for regulating and controlling room temperature by using heat storage materials is characterized in that a phase change heat storage plate is laid in a room, the phase change materials packaged in the phase change heat storage plate absorb heat in the daytime to realize liquefaction heat storage, then solidification heat release is carried out at night to realize temperature regulation and control in the room, and heat conduction is realized through a metal heat conduction frame in the phase change heat storage plate in the heat storage and release process.
Like this, realize the inside and outside heat conduction of panel through metal heat conduction frame for be provided with the heat conduction effect of metal heat conduction frame region in the building panel body in everywhere position and obtain very big improvement, improved between the building panel outside and inside and the heat transfer effect between the region everywhere inside, and then improved the holistic heat efficiency that holds of building panel, improved panel to room control by temperature change regulation effect, more be favorable to the energy saving.
The method for regulating and controlling the room temperature by using the heat storage material is realized by the phase change heat storage plate shown in fig. 1, the phase change heat storage plate comprises a building plate body 1, a plurality of phase change material particles 2 are packaged in the building plate body, and a metal heat conduction frame 3 is further embedded in the building plate body.
Like this, when this building panel used, can rely on the phase change material granule of encapsulation in it to realize holding heat release function, realized the inside control by temperature change regulation in room. The metal heat conduction frame is additionally arranged, so that the heat conduction effect of all positions in the metal heat conduction frame region arranged in the building board body is greatly improved, the heat transfer effect between the outside and the inside of the building board and between all regions in the inside is improved, the integral heat storage and release efficiency of the building board is further improved, the temperature control and adjustment effect of the board on a room is improved, and the energy saving is facilitated.
The metal heat conduction frame 3 comprises a plurality of layers of horizontal net racks arranged at intervals from top to bottom, and vertical net racks arranged in a criss-cross mode are arranged among the horizontal net racks of each layer, so that the metal heat conduction frame integrally forms a three-dimensional net rack structure.
Therefore, the heat conduction efficiency of all parts in the plate can be better improved, and the preparation of the metal heat conduction frame is convenient.
Wherein the metal heat conducting frame 3 is arranged along the whole space area of the building board body.
Therefore, the heat conduction efficiency of all parts in the plate can be better improved. Specifically, the metal heat conduction frame can be consistent in length and width dimensions and plate dimensions, and the thickness dimension is 1-5mm lower than that of the plate. This ensures the best heat conduction while leaving room for the outer surface to be provided with the steel mesh sheet and the graphite powder material coating.
Wherein, phase change material granule 2 and the metal heat conduction frame 3 of the inside building panel body 1 are pasted and are set up mutually.
In this way, heat conduction between the phase change material and the exterior of the building panel may be better achieved through the metal heat conducting frame.
Wherein, the metal heat conduction frame 3 is made of ferromagnetic metal material.
Therefore, the magnetic phase-change material particles can be conveniently adopted to be attracted to the surface of the metal heat conduction frame in the preparation process, and heat conduction is better realized through the metal heat conduction frame.
Wherein, the metal heat conduction frame 3 is made of a steel wire mesh sheet.
Therefore, the cost is low, the preparation is facilitated, the heat conductivity is good, the surface strength and the overall strength of the plate can be better improved, and the plate is prevented from cracking. When the metal heat conduction frame is prepared, the horizontal net rack of the single layer can be cut out by adopting the steel wire mesh sheet independently, then the vertical net rack arranged in a vertically and horizontally staggered manner is welded above the horizontal net rack, and then the horizontal net racks with the multiple layers of the vertical net racks are overlapped and welded into a whole to obtain the three-dimensional net rack structure. Thus, the manufacture is convenient, fast and reliable.
Wherein the building board body 1 is a gypsum board.
Therefore, gypsum is used as a gel material, so that the phase change material particles are conveniently packaged, the production and the manufacture of the plate are facilitated, and the cost of the plate can be reduced while the plate is ensured to have enough hardness. Meanwhile, gypsum is used as a gel material, in the production and preparation process of the board, a large amount of heat is released in the hydration process of the gypsum material which is hydrated from anhydrous calcium sulfate to generate calcium sulfate dihydrate, the phase-change material particles are liquefied by heat absorption, and the board is not completely solidified at the moment, so that the non-wettability between the phase-change material and the gypsum material and the attraction performance between the phase-change material and the metal heat conduction frame can be utilized, and the adhering state of the phase-change material and the metal heat conduction frame from the original point contact is converted into the adhering state of surface contact. After the plate is finally solidified and formed, the phase-change material and the metal heat conduction frame are attached and compact, so that the heat conduction effect from the metal heat conduction frame to the phase-change material is greatly improved.
Wherein, building board body 1 has one side surface at least and is interior trim, and the metal heat conduction frame surface that interior trim was located has still laid one deck metal screen cloth 4, and metal screen cloth 4 gomphosis is fixed in the gel material of building board body.
Therefore, when the building board is used, the interior surface is positioned on the inner side of a room, and the existence of the metal mesh cloth can further greatly improve the conduction efficiency from heat in the room to the metal heat conduction frame; meanwhile, the metal mesh cloth can also improve the surface hardness of the building board and improve the surface quality.
Wherein, the outer surface of the metal mesh 4 is also provided with a layer of graphite powder material coating 5.
The graphite powder coating can better conduct heat, and the radiation absorptivity of the surface of the building board is improved, so that the radiation absorptivity of the graphite powder coating on the surface of the near infrared and far infrared section materials is more than 90%, and the emissivity is more than 92%; but also can improve the surface compactness of the building board and improve the surface decoration effect of the board.
Wherein, the surface of the graphite powder material coating 5 is also provided with a decorative layer 6.
The decorative layer can better improve the appearance of the plate and improve the decoration of the plate. The decorative layer can be a sprayed glaze layer or a pattern layer.
In the present embodiment, the phase change material particles are a solid mixture containing 75 to 80 parts by mass of paraffin (most preferably 78 parts), 13 to 17 parts by mass of high density polyethylene (most preferably 15 parts), 1.3 to 3 parts by mass of silica (most preferably 2.2 parts), and 4 to 5.5 parts by mass of a carbon material (most preferably 4.8 parts).
The phase-change material particles are prepared by adopting the raw materials in the proportion, wherein paraffin occupies an absolute majority proportion as a phase-change material main body, the phase-change effect is ensured, high-density polyethylene and silicon dioxide are used as supporting materials, the material strength and the applied plate strength can be better improved, granulation can be better realized, the carbon material is kept in a graphite state, the self heat conductivity of the phase-change material particles can be better improved, the equivalent heat conductivity coefficient of the prepared phase-change material particles can be larger than 0.73W/(m ℃), the phase-change latent heat can be larger than 112kJ/kg, and the use requirement is greatly met. Therefore, the phase change particle material with the composition ratio has the characteristics of excellent heat storage and release effect and excellent heat transfer effect, the phase change temperature region is just in the range of the suitable temperature of a human body about 27 ℃, and meanwhile, the phase change material of the raw material has good non-wetting property with gypsum used as a gel material in a liquefied state, the working stability of the phase change material is ensured, and the like.
Wherein the particle size of the phase-change material particles is 8-10mm
The phase-change material particles with the particle size are convenient to granulate during production and preparation, are convenient to mix with gel materials when used for building boards, and meanwhile, in the manufacturing process of the building boards, the smaller particle size is more convenient to enable the material particles to attract and draw close to a metal heat conduction frame in the building boards through vibration.
Wherein, the phase-change material particles also contain 3-15 parts by mass (or 3-15% by mass) of magnetic powder material.
Therefore, the prepared phase-change material particles contain certain magnetism, so that when the phase-change material particles are applied to the phase-change heat storage plate, the phase-change material particles can be better attracted and attached to the metal heat conduction frame in the preparation process of the plate, and the heat conduction effect from the phase-change material particles to the metal heat conduction frame is improved.
The phase-change material particles are prepared from the following raw materials in parts by mass, wherein the raw materials for preparing the phase-change material particles comprise 75-80 parts (optimally 78 parts) of paraffin, 13-17 parts (optimally 15 parts) of high-density polyethylene, 0.5-1.5 parts (optimally 1 part) of diatomite, 0.8-1.5 parts (optimally 1.2 parts) of silica powder, 4-5.5 parts (optimally 4.8 parts) of graphite and 3-15 parts (optimally 8 parts) of magnetic powder.
Therefore, the silicon dioxide raw material in the phase-change material particles is obtained by adding the diatomite and the silica powder, so that the framework strength of the paraffin phase-change material, the uniform dispersibility of the mixed material and the flame retardant property of the material can be better improved. The carbon material in the phase change particulate material is obtained from graphite. Therefore, the method is not only beneficial to the increase of the self heat-conducting property of the phase-change material particles, but also can utilize the porous characteristic of the graphite to load other materials in the preparation process to complete mixing, thereby improving the material mixing effect.
When the phase-change material particles are prepared, the graphite material and the magnetic powder material are independently mixed, and then the rest materials are mixed and granulated.
Therefore, the graphite and the magnetic powder are mixed firstly, so that the magnetic powder material can be loaded in the pores of the graphite, and then the rest materials are mixed, so that the magnetic powder can be uniformly distributed when the materials are mixed, the quality can be balanced, and the phenomenon that the materials are layered when being granulated in a molten state due to the fact that the magnetic powder has high specific gravity and the graphite has low specific gravity is avoided. The quality of the phase-change material particles obtained by granulation is ensured.
Specifically, the phase change material particles are prepared by the following preparation method: a, obtaining the following raw materials in parts by mass: 75-80 parts of powdered paraffin (optimally 78 parts), 13-17 parts of powdered high-density polyethylene (optimally 15 parts), 0.5-1.5 parts of diatomite (optimally 1 part), 0.8-1.5 parts of silica powder (optimally 1.2 parts), 4-5.5 parts of expandable graphite powder (optimally 4.8 parts) and 3-15 parts of magnetic powder material (optimally 7 parts); b, heating expandable graphite powder to expand the expandable graphite powder, adding the magnetic powder material while keeping the expanded state, and uniformly stirring to complete the loading of the graphite on the magnetic powder material; c, adding paraffin wax and continuing stirring, and adding the rest raw materials and continuing stirring uniformly in the process that the temperature of the graphite falls back and is gradually reduced; d, pouring the mixture obtained in the step c in a still flowing state into a granulator for granulation.
Like this, adopt expanded graphite powder heating earlier and make its inflation, the volume increase, then add the stirring of magnetic powder material, can make magnetic powder material enter into graphite hole depths well, accomplish the load to the magnetic powder material. Then adding powdered paraffin, and utilizing the temperature of the expanded graphite to quickly melt the paraffin and enter the graphite pores to block the magnetic powder material; with the decrease of the graphite temperature, the graphite volume is gradually reduced and recovered to the normal volume proportion, the redundant part of paraffin is extruded from the graphite pores to form a fluid mixture with the main volume proportion occupied by the paraffin, and then the rest raw materials are added to be well stirred in the fluid paraffin and then granulated. Therefore, the method can better complete the loading of the magnetic powder material and the fusion with the paraffin material by utilizing the characteristics of the expanded graphite, greatly improve the uniformity of material distribution and ensure the granulation quality.
Wherein, the expandable graphite is treated in a muffle furnace (RIMG 0114) at 800 ℃ for 30 seconds in the step b, and the expansion heating is completed.
Therefore, the method has the advantages of convenience, rapidness and simplicity in operation, and the graphite can be expanded to the size of 500 times of that of 300 times, so that the magnetic powder material can be conveniently loaded and fused with the paraffin material. Of course, other heating devices may be used to heat the substrate.
And d, granulating by using a double-screw extrusion granulator.
The double-screw extrusion type granulator is mature existing equipment, has a heating function, can ensure that materials are granulated in a melt blending state at about 130-140 ℃, better meets the characteristic requirements of phase-change material particles on granulation, and has a stirring function during granulation, so that the materials are better uniformly mixed.
The phase-change material prepared by the method has the equivalent heat conductivity coefficient of more than 0.73W/(m ℃), and the latent heat of phase change can be more than 112kJ/kg, so that the use requirement of the building phase-change heat storage plate can be well met.
In this embodiment, the phase change heat storage plate is prepared by the following preparation method, including the following steps: 1) firstly, preparing a ferromagnetic metal heat conduction frame (namely the metal heat conduction frame) with a three-dimensional grid structure, and flatly laying the metal heat conduction frame in a cavity of a plate forming mold; 2) adding the gel material into phase-change material particles (namely the phase-change material particles) containing magnetic powder components and corresponding water, mixing and stirring uniformly to form a fluid mixture, pouring the fluid mixture into a mold cavity, and leveling; 3) installing a vibrator on the plate forming mold, vibrating the plate forming mold in the process of pouring the fluid mixture into the mold cavity, and keeping vibrating for a period of time after pouring is finished; 4) and removing the mold after the gel material is solidified and formed.
Therefore, in the preparation process of the phase change heat storage plate, the phase change material particles can be tightly attracted to the metal heat conduction frame by adopting a vibration mode during pouring depending on the attraction performance between the ferromagnetic metal heat conduction frame and the phase change material particles containing magnetic powder components. The phase change heat storage plate finally obtained can better realize the mutual heat conduction of phase change material particles at each position in the plate and the heat conduction between the inner part and the outer surface of the plate by means of the metal heat conduction frame, and greatly improves the heat conduction performance of the plate.
Wherein, the gel material adopted in the step 2) is mainly anhydrous gypsum powder, and is added according to the following mass portion ratio, 65-75 parts (optimally 70 parts) of phase change material particles and 25-30 parts (optimally 27 parts) of anhydrous gypsum powder.
Thus, hydration reaction of the anhydrous gypsum is utilized, and crystal water is combined to generate calcium sulfate dihydrate to realize solidification, so that the prepared board is the gypsum board. The gypsum board can reduce the cost and ensure that the board has enough hardness. Meanwhile, a large amount of heat can be released in the hydration process of the gypsum material, the heat enables phase-change material particles to absorb heat to be liquefied, and the board is not completely solidified at the moment, so that the non-wetting property between the phase-change material and the gypsum material and the suction performance between the phase-change material and the metal heat conduction frame can be utilized, and the phase-change material and the metal heat conduction frame are in a contact state from the original point contact state to a surface contact state. After the plate is finally solidified and formed, the phase-change material and the metal heat conduction frame are attached and compact, so that the heat conduction effect from the metal heat conduction frame to the phase-change material is greatly improved.
Wherein, graphite powder with the proportion of 1-5 parts by mass (optimally 3 parts) is also added into the gel material.
Therefore, the added graphite powder can improve the heat-conducting property and the emissivity of the gel material and improve the flame retardant property of the gel material.
And 2) after the fluid mixture is poured into a mold cavity, leveling the fluid mixture until the fluid mixture just submerges the metal heat conduction frame, laying a layer of metal mesh cloth above the metal heat conduction frame, and solidifying and forming the metal mesh cloth into a whole by means of a gel material.
Therefore, the arranged metal mesh cloth can better improve the heat transfer effect of the surface and the interior of the plate and can well strengthen the surface hardness and the quality of the plate.
And 3) after the fluid mixture is poured into the mold cavity and leveled, controlling the internal temperature of the mold cavity in the vibration process, so that the internal temperature of the fluid mixture is higher than the phase change temperature of the phase change material particles, and stopping vibration and temperature maintenance after the internal temperature of the fluid mixture is kept for 10-100 seconds.
Therefore, when the plate is not solidified, the internal phase-change material particles absorb heat and liquefy, and the adhesion performance between the phase-change material particles and the metal heat conduction frame is utilized, so that the phase-change material and the metal heat conduction frame are in a state of being adhered to each other by original point contact and are converted into a state of being adhered to each other by surface contact. After the plate is finally solidified and formed, the phase-change material and the metal heat conduction frame are attached and compact, so that the heat conduction effect from the metal heat conduction frame to the phase-change material is greatly improved.
And 3) controlling and maintaining the temperature inside the die cavity in the step by virtue of an electric heating module arranged on the die. Thus, control is conveniently achieved.
Wherein, the method also comprises the step 5), and a layer of graphite powder coating is brushed or sprayed on the upper surface of the building board body obtained by the step 4) of removing the form.
Therefore, the graphite powder coating can better conduct heat, improve the surface radiation absorption rate of the building board, improve the surface compactness of the building board and improve the surface decoration effect of the board.
Wherein, a decorative layer is arranged on the surface of the graphite powder material coating.
The decorative layer can better improve the appearance of the plate and improve the decoration of the plate. The decorative layer can be a sprayed glaze layer or a pattern layer.
The equivalent heat conductivity coefficient of the plate finally obtained through tests can reach 2W/(m ℃), the latent heat of phase change can reach 112kJ/kg, and the requirement of the building phase change heat storage plate can be well met.
In conclusion, the invention has the advantages of higher heat storage and release efficiency of the heat storage and release material, capability of realizing room temperature regulation more efficiently and reliably, more contribution to energy conservation and the like.
Claims (10)
1. A method for regulating and controlling room temperature by using heat storage materials is characterized in that a phase change heat storage plate is laid in a room, the phase change materials packaged in the phase change heat storage plate absorb heat in the daytime to realize liquefaction heat storage, and then the phase change materials are solidified and released heat at night to realize temperature regulation and control in the room.
2. The method for regulating and controlling the temperature of a room using a heat storage material according to claim 1, which is implemented by a phase change heat storage plate comprising a building plate body, wherein a plurality of phase change material particles are encapsulated inside the building plate body, and a metal heat conduction frame is embedded in the building plate body.
3. The method for regulating and controlling the temperature of a room using a heat storage material according to claim 2, wherein the metal heat conduction frame comprises a plurality of layers of horizontal net frames arranged at intervals up and down, and vertical net frames arranged in a criss-cross manner are provided between the horizontal net frames of each layer, so that the metal heat conduction frame as a whole forms a three-dimensional net frame structure;
the metal heat conduction frame is arranged along the whole space area of the building plate body;
phase change material particles inside the building board body are attached to the metal heat conduction frame;
the metal heat conduction frame is made of ferromagnetic metal material.
4. The method for regulating room temperature using a thermal storage material according to claim 2, wherein the building panel body is a gypsum board; the building board body at least has one side surface as an interior surface, a layer of metal mesh cloth is further laid on the surface of the metal heat conduction frame where the interior surface is located, and the metal mesh cloth is embedded and fixed in the gel material of the building board body.
5. The method for regulating and controlling room temperature using heat storage material of claim 4, wherein the metal mesh cloth is further provided with a graphite powder coating on the outer surface; the surface of the graphite powder material coating is also provided with a decorative layer.
6. The method for regulating room temperature using a heat storage material according to claim 2, wherein the phase change material particles further contain a magnetic powder material in an amount of 3 to 15% by mass.
7. The method for regulating room temperature using a heat storage material according to claim 2, wherein the phase change material particles are prepared using raw materials comprising, by mass, 75 to 80 parts of paraffin, 13 to 17 parts of high density polyethylene, 0.5 to 1.5 parts of diatomaceous earth, 0.8 to 1.5 parts of silica powder, 4 to 5.5 parts of graphite, and 3 to 15 parts of magnetic powder.
8. The method for controlling room temperature using a heat storage material according to claim 7, wherein the phase change material particles are prepared by a method comprising: a, obtaining the following raw materials in parts by mass: 75-80 parts of powdered paraffin, 13-17 parts of powdered high-density polyethylene, 0.5-1.5 parts of diatomite, 0.8-1.5 parts of silica powder, 4-5.5 parts of expandable graphite powder and 3-15 parts of magnetic powder material; b, heating expandable graphite powder to expand the expandable graphite powder, adding the magnetic powder material while keeping the expanded state, and uniformly stirring to complete the loading of the graphite on the magnetic powder material; c, adding paraffin wax and continuing stirring, and adding the rest raw materials and continuing stirring uniformly in the process that the temperature of the graphite falls back and is gradually reduced; d, pouring the mixture obtained in the step c in a still flowing state into a granulator for granulation.
9. The method for regulating room temperature using a heat storage material according to claim 2, wherein the phase-change heat storage sheet is prepared according to the following method comprising the steps of: 1) firstly, preparing a ferromagnetic metal heat conduction frame of a three-dimensional grid structure, and flatly laying the metal heat conduction frame in a cavity of a plate forming die; 2) adding the gel material into phase-change material particles containing magnetic powder and corresponding water, mixing and stirring uniformly to form a fluid mixture, pouring the fluid mixture into a mold cavity, and leveling; 3) installing a vibrator on the plate forming mold, vibrating the plate forming mold in the process of pouring the fluid mixture into the mold cavity, and keeping vibrating for a period of time after pouring is finished; 4) and removing the mold after the gel material is solidified and formed.
10. The method for regulating and controlling the temperature of a room using a heat storage material according to claim 9, wherein the gel material used in the step 2) is mainly anhydrous gypsum powder, and is added in the following ratio by mass, 65 to 75 parts of phase change material particles and 25 to 30 parts of anhydrous gypsum powder; graphite powder with the mass part ratio of 1-5 parts is also added into the gel material;
2) in the step, after the fluid mixture is poured into a mold cavity, leveling the fluid mixture until the fluid mixture just submerges the metal heat conduction frame, laying a layer of metal mesh cloth above the metal heat conduction frame, and solidifying and forming the metal mesh cloth into a whole by means of a gel material;
3) in the step, after the fluid mixture is poured into a mold cavity and is leveled, controlling the internal temperature of the mold cavity in the vibration process, so that the internal temperature of the fluid mixture is higher than the phase change temperature of the phase change material particles and stops vibration and temperature maintenance after lasting for 10-100 seconds;
and 5) coating or spraying a graphite powder coating on the upper surface of the building plate body obtained by the form removal in the step 4).