CN1132226A - 远红外线放射性内外墙涂料 - Google Patents
远红外线放射性内外墙涂料 Download PDFInfo
- Publication number
- CN1132226A CN1132226A CN 95110136 CN95110136A CN1132226A CN 1132226 A CN1132226 A CN 1132226A CN 95110136 CN95110136 CN 95110136 CN 95110136 A CN95110136 A CN 95110136A CN 1132226 A CN1132226 A CN 1132226A
- Authority
- CN
- China
- Prior art keywords
- aqua
- water
- far infrared
- organosilicon
- calcium chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
远红外线放射性内外墙涂料,由粉剂和水剂构成,粉剂由白水泥30%、硅石粉30%、太白粉15%、贝粉15%、氧化锌5%配制成。外墙水剂由一定比例的氯化钙、水、消泡剂、EVA和有机硅配制成;内墙水剂由一定比例的PVA、水、氯化钙、消泡剂和有机硅配制成。使用时将粉剂和水剂按1∶1混合均匀后,即可使用。本涂料防水性能好,耐高温,且在阳光照射下能辐射远红外线,作为内墙涂料有益于人身体健康。
Description
本发明属于一种在阳光照射下,可发射远红外线的涂料。
目前,已生产的内外墙涂料种类较多,但有些涂料防水性能差,有的不耐高温,还有的涂料在高温潮湿的情况下易发霉。
本发明的目的,是提供一种防水性能好,耐高温,不发霉,且在阳光照射下能辐射远红外线的内外墙涂料。
远红外线放射性内外墙涂料由水剂和粉剂两种组份组成。粉剂由白水泥30%、硅石粉(硅酸钙粒度400目)30%、太白粉15%,贝粉15%、氧化锌5%配制而成。
外墙水剂,由氯化钙5~10%、水80~55%、消泡剂5%、EVA(乙稀乙酸共聚物)5~15%、有机硅5~10%配制而成;内墙水剂由PVA(聚乙稀醇酸)7~15%、水78~55%、氯化钙5~10%、消泡剂5~10%配制而成。
使用时将水剂和粉剂按1∶1(重量比)混合均匀后,便可使用。并可用聚苯乙稀80%和甲苯20%的混合剂,作光面处理。
远红外线放射性内外墙涂料的生产工艺:
1、粉剂:将自水泥、硅石粉、太白粉、贝粉和氧化锌,按上述比例混合后,再用粉碎机进一步粉碎,包装后,即为成品。
2、外墙水剂:将EVA、水、氯化钙、消泡剂、有机硅,按上述比例混合后,加温至60~80℃,同时搅拌,再经过滤后,包装即为成品。
3、内墙水剂的制造方法与外墙水剂的制造方法相同。
实施例:粉剂由白水泥30%、硅石粉30%、太白粉15%、贝粉15%、氧化锌5%配制成;外墙水剂,由EVA10%、水77%、氯化钙7%、消泡剂3%、有机硅3%配制成;内墙水剂由PVA5%、水80%、氯化钙10%、消泡剂2%、有机硅3%配制成。
远红外线放射性内外墙涂料具有下述优点:
1、防水性能好。使用本发明的涂料可在表面形成防水涂膜。
2、强度高、稳定性好,耐高温。本涂料在500℃高温下,不变质、不龟裂、不产生任何有害气体,防火效果好。
3、耐磨性好。涂膜表面与水泥面有同样强度的耐磨性能。
4、具有良好的防霉性能。涂膜在高温潮湿下不发霉,可以用水洗刷迅速除去油污。
5、本涂料由于在阳光照射下,能辐射远红外线,当用于内墙涂料时,辐射的远红外线能渗透到人体一定深度,能促进人体新陈代谢,使人体组织更加活性化,起到保健作用。
Claims (2)
1、远红外线放射性内外墙涂料,由粉剂和水剂组成,其特征在于所述的粉剂由白水泥30%、硅石粉30%、太白粉15%、氧化锌5%配制成;所述的水剂包括外墙水剂和内墙水剂,外墙水剂由氯化钙5~10%、水80~55%、消泡剂5~10%、EVA5~15%、有机硅5~10配制成;内墙水剂由PVA7~15%、水78~55%、有机硅5~10%、氯化钙5~10%、消泡剂5~10%配制成。
2、根据权利要求1所述的远红外线放射性内外墙涂料,其特征在于所述的外墙水剂由EVA10%、水78%氯化钙7%、消泡剂3%、有机硅3%配制成;所述的内墙水剂由PVA5%、水80%、氯化钙10%、消泡剂2%、有机硅3%配制成。