CN113192662B - 一种用于提高太阳能电池用导电浆料附着力的有机载体 - Google Patents
一种用于提高太阳能电池用导电浆料附着力的有机载体 Download PDFInfo
- Publication number
- CN113192662B CN113192662B CN202110316818.4A CN202110316818A CN113192662B CN 113192662 B CN113192662 B CN 113192662B CN 202110316818 A CN202110316818 A CN 202110316818A CN 113192662 B CN113192662 B CN 113192662B
- Authority
- CN
- China
- Prior art keywords
- resin
- conductive paste
- organic vehicle
- solar cell
- improving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于电子材料技术领域，公开了一种用于提高太阳能电池用导电浆料附着力的有机载体包括高附着力的树脂体系、分散剂体系、有机溶剂、触变剂和增稠剂，其中高附着力的树脂体系是弹性体树脂、玻璃化温度≥130℃的树脂和相容性树脂的混合物，本发明采用的高玻璃化温度≥130℃的树脂在整个太阳能电池用导电浆料体系中可以有效的提升栅线耐高温特性及高温下硬度，在有机载体中添加弹性树脂可以提升栅线柔韧性及塑型，本申请还添加了相容性树脂提升整体浆料相容性并改善浆料对基材的附着力。本申请的分散剂体系是脂肪酸类添加剂、润湿剂和润滑剂的混合物，本发明的有机载体还提调整导电浆料的高宽比，提高了电池效率。
Description
技术领域
本发明涉及电子材料技术领域，尤其涉及一种用于提高太阳能电池用导电浆料附着力的有机载体。
背景技术
晶硅太阳能电池用导电浆料主要包括正电极银浆、背电极银浆和背电极铝浆。导电浆料主要有金属填料、无机粘结剂、有机载体组成。作为关键材料，有机载体是由树脂、分散剂、增稠剂、触变剂、溶剂等组成，协调导电浆料多组分相容性，使固体形态的导电相、粘结相和其他固体微粒混合物分散成具有流体特性的浆料，保障长期储存性，可控制浆料的流变特性，以便于刷印到基板上，形成所需图形。因此，有机载体的选择必须满足以下要求：
（1）对基体和金属微粒具有良好的浸润性，保证金属微粒在有机粘合剂中得到充分良好的分散，并在基体上形成连续的金属覆盖层；
（2）溶剂在常温下不易挥发，这是保证稳定生产的关键。因为若在浸涂过程中溶剂大量挥发，必使浆料的黏度增大，功能金属相消耗量增大，严重时浸涂后浆料表面出现针孔、尖头等缺陷；
（3）有机粘合剂的粘度要适中，制成的浆料应具有良好的流平性和触变性，浸涂后，界面平直，不流挂，无尖头；
（4）浆料干燥后，对基体有良好的附着性能，保证在多次通过硅橡胶孔板时不易磨损脱落；
（5）烧渗时树脂能完全分解，挥发，不留灰分，保证浸涂层的连续性和良好的可焊性。
晶硅光伏电池金属化丝网印刷生产线，主要设备包括上料机、丝网印刷机、烘干炉、硅片暂存机、硅片翻转机、烘干炉、测试分检机等。其中，丝网印刷和烘干烧结为最主要的工序。丝网印刷通常包括两道印制背银工序和一道印制正银工序，其功用是通过采用丝网印刷的方式将预定的图形印刷在硅片上，从而在电池背面上形成正负两个电极以实现电池工作时能产生的电流导出的目的。烘干过程是为了将有机树脂粘合剂燃烧掉，剩下几乎是纯粹的、由于玻璃质作用而密合在硅片上的银电极，并且使晶体硅原子以一定的比例融入熔融的银电极材料中去，从而形成上下电极的欧姆接触，提高电池片的开路电压和填充因子两个关键参数，使其具有电阻特性，以提高电池片的转换效率。整个过程中电池片运输是通过皮带运输移动，二次正反印刷则是通过翻转机实现。
随着丝网印刷效率的提升，印刷速度从过去的100 mm/s到500mm/s，伴随印刷速度的提高，皮带传输速率加快，产线电池片与皮带间的摩擦加剧。另外，电池片翻转速度也会加快，也会带来震动摩擦。伴随印刷速度提升，通常会提升烘干温度，高温烘干会影响机载体对硅片基材的附着力。目前，产线大约有60%采用分步印刷，其中不少采用四道分步印刷，代表着一道、二道栅线经历更多次的高温烘干、皮带摩擦，加剧栅线掉粉现象如图3所示出现的局部掉粉断栅现象。综上，以上丝网印刷工艺的调整对浆料印刷性和对基材附着性提出了更高的要求。
发明内容
为了解决上述问题，本发明通过优化设计树脂体系和分散剂体系的搭配及配比，实现了栅线对硅片表面优异的附着力，有效改善了电池片印刷后烘干掉粉的问题，同时缓解了印刷边缘毛刺不平整的现象，还有效改善导电浆料长期储存稳定性，本发明的具体发明内容如下：
本发明的目的在于提供一种用于提高太阳能电池用导电浆料附着力的有机载体，其技术点在于：以所述用于提高太阳能电池用导电浆料附着力的有机载体重量为100%计，包括1.5-8.5wt%的高附着力的树脂体系、1-5wt%的分散剂体系、84.5-90wt%的有机溶剂、1-4wt%的触变剂和1-4wt%的增稠剂；
以所述高附着力的树脂体系重量为100%计，所述高附着力的树脂体系脂是0-30wt%的弹性体树脂、15-30wt%的玻璃化温度≥130℃的树脂和10-60wt%的相容性树脂的混合物；
以所述分散剂体系重量为100%计，所述分散剂体系是10-40wt%的脂肪酸类添加剂、10-30wt%的润湿剂和30-60wt%的润滑剂的混合物。
在发明的有的实施例中，本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体配方体系中的弹性体树脂为1,2-聚丁二烯均聚物、端羟基聚丁二烯、马来酸酐化聚丁二烯树脂和苯乙烯-丁二烯共聚物中的至少一种。
在发明的有的实施例中，本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体配方体系中的述玻璃化温度≥130℃的树脂为双马来酰亚胺树脂、酚醛树脂、松香改性酚醛树脂和苯并噁嗪树脂中的至少一种。
在发明的有的实施例中，本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体配方体系中的相容性树脂为丙烯酸树脂、丙烯酸-马来酸酐共聚物、苯乙烯-马来酸酐共聚物和长链烷基丙烯酸酯共聚物中的至少一种。
在发明的有的实施例中，本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体配方体系中的脂肪酸类添加剂为饱和脂肪酸及其衍生改性物和不饱和脂肪酸及其衍生改性物中的至少一种。
在发明的有的实施例中，本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体配方体系中的述润湿剂为饱和脂肪醇接枝物及其磷酸酯化衍生物和不饱和脂肪醇的接枝物及其磷酸酯化衍生物中的至少一种。
在发明的有的实施例中，本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体配方体系中的润滑剂为二聚酸及其胺化衍生物或者三聚酸及其胺化衍生物中的至少一种。
在发明的有的实施例中，本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体配方体系中的有机溶剂为二乙二醇丁醚、松油醇、丁基卡比醇、邻苯二甲酸二丁酯和二乙二醇丁醚醋酸酯以任意比例互溶得到。
在发明的有的实施例中，本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体配方体系中的触变剂为改性聚酰胺蜡、聚烯烃蜡、改性氢化蓖麻油和氢化蓖麻油中的至少一种。
在发明的有的实施例中，本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体配方体系中的述增稠剂为乙基纤维素和聚酰胺纤维中的至少一种。
与现有技术相比，本发明的有效效果为：
本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体包括高附着力的树脂体系、分散剂体系、有机溶剂、触变剂和增稠剂，其中高附着力的树脂体系是弹性体树脂、玻璃化温度≥130℃的树脂和相容性树脂的混合物，本发明采用的玻璃化温度≥130℃的树脂在整个太阳能电池用导电浆料体系中可以有效的提升栅线耐高温特性及高温下硬度，但是随着高玻璃化温度≥130℃的树脂的加入会带来浆料脆性较大的问题，因此在有机载体中添加弹性树脂可以提升栅线柔韧性及塑型，本申请还添加了相容性树脂提升整体浆料相容性并改善浆料对基材的附着力。本申请的分散剂体系是脂肪酸类添加剂、润湿剂和润滑剂的混合物。基于本发明的有机载体的配方体系，将其应用于导电浆料中实现了栅线对硅片表面优异的附着力，有效改善了电池片印刷后烘干掉粉的问题，同时缓解了印刷边缘毛刺不平整的现象，还有效改善导电浆料长期储存稳定性，本发明的有机载体还提调整导电浆料的高宽比，提高了电池效率。
附图说明
图1为添加实施例1制备的有机载的导电浆料的轮廓图；
图2为添加对比例1制备的有机载的导电浆料的轮廓图；
图3为现有四道印刷产线中出现的印刷出现掉粉情况的示意图。
具体实施方式
本发明的一种用于提高太阳能电池用导电浆料附着力的有机载体包括：
1.5-8.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是0-30wt%的弹性体树脂（1,2-聚丁二烯均聚物、端羟基聚丁二烯、马来酸酐化聚丁二烯树脂和苯乙烯-丁二烯共聚物中的至少一种）、15-30wt%的玻璃化温度≥130℃的树脂（双马来酰亚胺树脂、酚醛树脂、松香改性酚醛树脂和苯并噁嗪树脂中的至少一种）和30-60wt%的相容性树脂（丙烯酸树脂、马来酸酐共聚物为丙烯酸-马来酸酐共聚物、苯乙烯-马来酸酐共聚物和长链烷基丙烯酸酯共聚物中的至少一种）的混合物，其中弹性体树脂的添加可以有效改善导电浆料的高宽比增加导电性能，玻璃化温度≥130℃的树脂使得导电浆料在250℃、320℃和380℃温度下表现优异，减少掉粉情况的产生，相容性树脂的添加可以增加导电浆料的平整度。
1-5wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是10-40wt%的脂肪酸类添加剂（饱和脂肪酸及其衍生改性物和不饱和脂肪酸及其衍生改性物中的至少一种）、10-30wt%的润湿剂（饱和脂肪醇接枝物及其磷酸酯化衍生物和不饱和脂肪醇的接枝物及其磷酸酯化衍生物中的至少一种）和30-60wt%的润滑剂（二聚酸及其胺化衍生物或者三聚酸及其胺化衍生物中的至少一种）的混合物，该分散剂体系的应用在增加导电浆料触变指数的同时，还能有效保证导电浆料的储存稳定性。
84.5-90wt%有机溶剂，有机溶剂为二乙二醇丁醚、松油醇、丁基卡比醇、邻苯二甲酸二丁酯和二乙二醇丁醚醋酸酯以任意比例互溶得到。
1-4wt%的触变剂，触变剂为改性聚酰胺蜡、聚烯烃蜡、改性氢化蓖麻油和氢化蓖麻油中的至少一种，这些触变剂使得有机载体中的高附着力的树脂体系在静止时有较高的稠度，在外力作用下又变成低稠度流体的物质，将其作为浆料的有机载体使用时，具有较好的印刷特性和塑形性。
1-4wt%的增稠剂，增稠剂为乙基纤维素和聚酰胺纤维中的至少一种，增稠剂用于调节有机载体的稠度，乙基纤维素增稠剂分子的疏水主链与周围水分子通过氢键缔合，提高了聚合物本身的流体体积，减少了颗粒自由活动的空间，从而提高了本发明的有机载体的黏度。
本发明将高附着力的树脂体系、分散剂体系、有机溶剂、触变剂和增稠剂混合后40-60℃、400-600rmp转速下混合搅拌均匀，即得本发明的用于提高太阳能电池用导电浆料附着力的有机载体。
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
实施例1
本实施例的一种用于提高太阳能电池用导电浆料附着力的有机载体包括：
7wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%的端羟基聚丁二烯、20wt%的酚醛树脂和40wt%的为丙烯酸-马来酸酐共聚物的混合物。
5wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是30wt%的饱和脂肪酸（硬脂酸）、20wt%的不饱和脂肪醇的磷酸酯化衍生物（油醇聚醚-2 磷酸酯）和50wt%二聚酸的混合物。
54wt%有机溶剂，有机溶剂为二乙二醇丁醚、松油醇、丁基卡比醇、邻苯二甲酸二丁酯和二乙二醇丁醚醋酸酯以任意比例互溶得到。
2wt%的氢化蓖麻油。
2wt%的乙基纤维素。
本发明将高附着力的树脂体系、分散剂体系、有机溶剂、触变剂和增稠混合后40-60℃、400-600rmp转速下混合搅拌均匀，即得本发明的用于提高太阳能电池用导电浆料附着力的有机载体。
实施例2
本实施例的一种用于提高太阳能电池用导电浆料附着力的有机载体包括：
7wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%苯乙烯-丁二烯共聚物、30wt%的双马来酰亚胺树脂和50wt%的长链烷基丙烯酸酯共聚物的混合物。
1wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是40wt%的不饱和脂肪酸（油酸的乙醇胺改性衍生物）、20wt%的不饱和脂肪醇的磷酸酯化衍生物（三油醇磷酸酯）和40wt%三聚酸的混合物。
88wt%有机溶剂，有机溶剂为二乙二醇丁醚、松油醇、丁基卡比醇、邻苯二甲酸二丁酯和二乙二醇丁醚醋酸酯以任意比例互溶得到。
2wt%的改性氢化蓖麻油。
2wt%的乙基纤维素。
本发明将高附着力的树脂体系、分散剂体系、有机溶剂、触变剂和增稠混合后40-60℃、400-600rmp转速下混合搅拌均匀，即得本发明的用于提高太阳能电池用导电浆料附着力的有机载体。
实施例3
本实施例的一种用于提高太阳能电池用导电浆料附着力的有机载体包括：
8.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是30wt%的1,2-聚丁二烯均聚物、30wt%的苯并噁嗪树脂和40wt%的丙烯酸-马来酸酐共聚物的混合物。
2wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是40wt%的饱和脂肪酸（月硅酸的乙醇胺改性衍生物）、30wt%不饱和脂肪醇的磷酸酯化衍生物（三油醇磷酸酯）和30wt%的三聚酸的二乙醇胺酰胺化改性物的混合物。
84.5wt%有机溶剂，有机溶剂为二乙二醇丁醚、松油醇、丁基卡比醇、邻苯二甲酸二丁酯和二乙二醇丁醚醋酸酯以任意比例互溶得到。
2wt%的改性聚酰胺蜡。
3wt%的聚酰胺纤维。
本发明将高附着力的树脂体系、分散剂体系、有机溶剂、触变剂和增稠混合后40-60℃、400-600rmp转速下混合搅拌均匀，即得本发明的用于提高太阳能电池用导电浆料附着力的有机载体。
实施例4
本实施例的一种用于提高太阳能电池用导电浆料附着力的有机载体包括：
8.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%的马来酸酐化聚丁二烯树脂、30wt%的松香改性酚醛树脂和50wt%的丙烯酸-马来酸酐共聚物的混合物。
1.5wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是25wt%的不饱和脂肪酸的衍生改性物（油酸的乙醇胺改性衍生物）、20wt%不饱和脂肪醇的磷酸酯化衍生物（三油醇磷酸酯）和55wt%的三聚酸。
87wt%有机溶剂，有机溶剂为二乙二醇丁醚、松油醇、丁基卡比醇、邻苯二甲酸二丁酯和二乙二醇丁醚醋酸酯以任意比例互溶得到。
1.5wt%的聚烯烃蜡。
1wt%的乙基纤维素和0.5wt%的聚酰胺纤维的混合物。
本发明将高附着力的树脂体系、分散剂体系、有机溶剂、触变剂和增稠混合后40-60℃、400-600rmp转速下混合搅拌均匀，即得本发明的用于提高太阳能电池用导电浆料附着力的有机载体。
实施例5
本实施例的一种用于提高太阳能电池用导电浆料附着力的有机载体包括：
3.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%的1,2-聚丁二烯均聚物、30wt%的双马来酰亚胺树脂和50wt%的和长链烷基丙烯酸酯共聚物的混合物。
3.5wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是30wt%的饱和脂肪酸（硬脂酸）、20wt%的不饱和脂肪醇的磷酸酯化衍生物（油醇聚醚-2 磷酸酯）和50wt%二聚酸的混合物。
87wt%有机溶剂，有机溶剂为二乙二醇丁醚、松油醇、丁基卡比醇、邻苯二甲酸二丁酯和二乙二醇丁醚醋酸酯以任意比例互溶得到。
3wt%的氢化蓖麻油。
2wt%的聚酰胺纤维和1wt%的聚酰胺纤维的混合。
本发明将高附着力的树脂体系、分散剂体系、有机溶剂、触变剂和增稠混合后40-60℃、400-600rmp转速下混合搅拌均匀，即得本发明的用于提高太阳能电池用导电浆料附着力的有机载体。
对比例1
本对比例中用“5wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是60wt%的饱和脂肪酸（硬脂酸）和40wt%的不饱和脂肪醇的磷酸酯化衍生物（油醇聚醚-2 磷酸酯）的混合物。”替换实施例1中的“5wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是30wt%的饱和脂肪酸（硬脂酸）、20wt%的不饱和脂肪醇的磷酸酯化衍生物（油醇聚醚-2 磷酸酯）和50wt%二聚酸的混合物。”，其余操作同实施例1，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例2
将对比例1中的“硬脂酸”换成“月桂酸”，其余其余操作同对比例1，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例3
将对比例1中的“饱和脂肪酸（硬脂酸）”换成“不饱和脂肪酸（油酸）”，其余其余操作同对比例1，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例4
本对比例中用“5wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是66wt%的不饱和脂肪酸（油酸的乙醇胺改性衍生物）和34wt%的不饱和脂肪醇的磷酸酯化衍生物（三油醇磷酸酯）酸的混合物。”替换实施例2中的“55wt%的分散剂体系，以分散剂体系重量为100%计，分散剂体系是40wt%的不饱和脂肪酸（油酸的乙醇胺改性衍生物）、20wt%的不饱和脂肪醇的磷酸酯化衍生物（三油醇磷酸酯）和40wt%三聚酸的混合物。”，其余操作同实施例2，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例5
将对比例4中的“不饱和脂肪酸（油酸的乙醇胺改性衍生物）”换成“饱和脂肪酸（硬脂酸的二乙醇胺改性衍生物）”，其余其余操作同对比例4，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例6
本对比例中用“7wt%的高附着力的树脂体系，以高附着力的树脂体系脂重量为100%计，高附着力的树脂体系是30wt%苯乙烯-丁二烯共聚物和70%的长链烷基丙烯酸酯共聚物的混合物。”替换实施例2中的“7wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%苯乙烯-丁二烯共聚物、30wt%的双马来酰亚胺树脂和50%的长链烷基丙烯酸酯共聚物的混合物。”，其余操作同实施例2，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例7
本对比例中用“7wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是40wt%的双马来酰亚胺树脂和60%的长链烷基丙烯酸酯共聚物的混合物。”替换实施例2中的“7wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%苯乙烯-丁二烯共聚物、30wt%的双马来酰亚胺树脂和50%的长链烷基丙烯酸酯共聚物的混合物。”，其余操作同实施例2，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例8
本对比例中用“8.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是40wt%的马来酸酐化聚丁二烯树脂和60wt%的松香改性酚醛树脂的混合物。”替换实施例4中的“8.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%的马来酸酐化聚丁二烯树脂、30wt%的松香改性酚醛树脂脂和50%的丙烯酸-马来酸酐共聚物的混合物。”，其余操作同实施例4，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例9
本对比例中用“8.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是30wt%的马来酸酐化聚丁二烯树脂、50wt%的松香改性酚醛树脂和20%的丙烯酸-马来酸酐共聚物的混合物。”替换实施例4中的“8.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%的马来酸酐化聚丁二烯树脂、30wt%的松香改性酚醛树脂和50%的丙烯酸-马来酸酐共聚物的混合物。”，其余操作同实施例4，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例10
本对比例中用“8.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是10wt%的马来酸酐化聚丁二烯树脂、20wt%的松香改性酚醛树脂和70wt%的丙烯酸-马来酸酐共聚物的混合物。”替换实施例4中的“8.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%的马来酸酐化聚丁二烯树脂、30wt%的松香改性酚醛树脂和50%的丙烯酸-马来酸酐共聚物的混合物。”，其余操作同实施例4，制备得到本对比例的用于提高导电浆料附着力的有机载。
对比例11
本对比例中用“3.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系脂是40wt%的松香改性酚醛树脂和60wt%的和长链烷基丙烯酸酯共聚物的混合物。”替换实施例5中的“3.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%的1,2-聚丁二烯均聚物、30wt%的松香改性酚醛树脂和50wt%的和长链烷基丙烯酸酯共聚物的混合物。”，其余操作同实施例5，制备得到本对比例的用于提高导电浆料附着力的有机载。
实施例12
本对比例中用“3.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是5wt%的1,2-聚丁二烯均聚物、35wt%的松香改性酚醛树脂和60wt%的和长链烷基丙烯酸酯共聚物的混合物。”替换实施例5中的“3.5wt%的高附着力的树脂体系，以高附着力的树脂体系重量为100%计，高附着力的树脂体系是20wt%的1,2-聚丁二烯均聚物、30wt%的松香改性酚醛树脂和50wt%的和长链烷基丙烯酸酯共聚物的混合物。”，其余操作同实施例5，制备得到本对比例的用于提高导电浆料附着力的有机载。
实验例
取实施例1-5和对比例1-12制备得到的用于提高导电浆料附着力的有机载制备铝浆（本实验例以铝浆为例，但不仅限于铝浆），其中铝浆的配方为：9wt%的有机载体、2wt%的玻璃粉和89wt%的铝粉，测试性能，具有结果见表1-4。
将用实施例1的有机载体制备得到的铝浆采用轮廓仪观察其轮廓图，见图1，从图1可以看出采用本发明有机载体制备的铝浆印刷栅线线性良好，将对比例1制备的有机载体制备得到的铝浆采用轮廓仪观察其轮廓图，见图2，从图2可以铝浆印刷栅线线性不好。
1 不同分散剂体系对浆料储存稳定性影响
表1 不同分散剂体系对铝浆储存稳定性的影响
从上表可知：采用实施例1-5制备得到的铝浆的触变指数较高，均优于对比例1-5，且储存稳定性也较对比例1-5高，本发明的因此采用本发明的分散剂体系制备得到的铝浆的稳定性较。
2 树脂对浆料的影响
2.1 玻璃化温度≥130℃的树脂对高温烘干掉粉的影响
表2玻璃化温度≥130℃的树脂对高温烘干掉粉的影响
从上表可知，采用实施例1-5制备得到的铝浆在250℃、320℃、380℃温度下各烘干5min的不出现掉粉情况，而对比例6中不添加玻璃化温度≥130℃的树脂，在250℃烘干5min就出现烘干掉粉情况，对比例7中未添加弹性体树脂，在320℃温度下烘干5min出现多次指擦易掉粉，对比例6-7均出现残留严重的问题。
2.2 相容性树脂对印刷形貌影响
表3 相容性树脂对印刷形貌影响
从上表可知，采用实施例1-5制备得到的铝浆轴面饱和平滑，线宽均比对比例8-10窄，线高均比实施例8-10高，因此可以添加相容性树脂的机载体可以有效提高铝浆的高宽比，对比例8中未添加的相容性树脂，会出现铝浆发黑，轴面起皮，部分区域毛刺的现象，实施例9添加的相容性树脂过少出现铝浆发黑，轴面起皮，极少区域毛刺的现象，实施例10添加的相容性树脂过多也出现铝浆发黑，轴面起皮，极少区域毛刺的现象。
2.3 弹性体树脂对栅线高宽比的影响
表4 弹性体树脂对栅线高宽比的影响
从上表可知，采用实施例1-5制备得到的铝浆轴面饱和平滑，线宽均比对比例11-12窄，线高均比实施例11-12高，因此可以发现添加弹性体树脂有机载体可以有效提高铝浆的高宽比，对比例11中未添加的弹性体树脂，出现部分区域毛刺的现象，实施例11添加的弹性体树脂过少出现，极少区域毛刺的现象。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (10)
1.一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：以所述用于提高导电浆料附着力的有机载体重量为100％计，包括1.5-8.5wt％的高附着力的树脂体系、1-5wt％的分散剂体系、84.5-90wt％的有机溶剂、1-4wt％的触变剂和1-4wt％的增稠剂；
以所述高附着力的树脂体系重量为100％计，所述高附着力的树脂体系是0-30wt％的弹性体树脂、15-30wt％的玻璃化温度≥130℃的树脂和40-60wt％的相容性树脂的混合物；
以所述分散剂体系重量为100％计，所述分散剂体系是10-40wt％的脂肪酸类添加剂、10-30wt％的润湿剂和30-60wt％的润滑剂的混合物。
2.根据权利要求1所述的一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：所述弹性体树脂为1,2-聚丁二烯均聚物、端羟基聚丁二烯、马来酸酐化聚丁二烯树脂和苯乙烯-丁二烯共聚物中的至少一种。
3.根据权利要求1所述的一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：所述玻璃化温度≥130℃的树脂为双马来酰亚胺树脂、酚醛树脂、松香改性酚醛树脂和苯并噁嗪树脂中的至少一种。
4.根据权利要求1所述的一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：所述相容性树脂为丙烯酸树脂、丙烯酸-马来酸酐共聚物、苯乙烯-马来酸酐共聚物和长链烷基丙烯酸酯共聚物中的至少一种。
5.根据权利要求1所述的一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：所述脂肪酸类添加剂为饱和脂肪酸及其衍生改性物和不饱和脂肪酸及其衍生改性物中的至少一种。
6.根据权利要求1所述的一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：所述润湿剂为饱和脂肪醇接枝物及其磷酸酯化衍生物和不饱和脂肪醇的接枝物及其磷酸酯化衍生物中的至少一种。
7.根据权利要求1所述的一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：所述润滑剂为二聚酸、二聚酸胺化衍生物、三聚酸、三聚酸胺化衍生物中的至少一种。
8.根据权利要求1所述的一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：所述有机溶剂为二乙二醇丁醚、松油醇、丁基卡比醇、邻苯二甲酸二丁酯和二乙二醇丁醚醋酸酯以任意比例互溶得到。
9.根据权利要求1所述的一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：所述触变剂为改性聚酰胺蜡、聚烯烃蜡、改性氢化蓖麻油和氢化蓖麻油中的至少一种。
10.根据权利要求1所述的一种用于提高太阳能电池用导电浆料附着力的有机载体，其特征在于：所述增稠剂为乙基纤维素和聚酰胺纤维中的至少一种。