CN113186635A - Preparation method of rabbit hair-like real silk fabric - Google Patents
Preparation method of rabbit hair-like real silk fabric Download PDFInfo
- Publication number
- CN113186635A CN113186635A CN202110494422.9A CN202110494422A CN113186635A CN 113186635 A CN113186635 A CN 113186635A CN 202110494422 A CN202110494422 A CN 202110494422A CN 113186635 A CN113186635 A CN 113186635A
- Authority
- CN
- China
- Prior art keywords
- silk
- soaking
- preparation
- steps
- rabbit hair
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a rabbit hair-like real silk fabric, which is characterized by comprising the following steps of: the method comprises the following steps: selecting proper quantity and quality of silkworm cocoons, putting the silkworm cocoons into clear water, adding a degreasing agent into the water, and stirring for 0.2-0.4h, so that the silkworm cocoons are separated into flaky silk; step two: soaking the processed sheet silk in a cleaning solution at a ratio of 1:40, turning over the sheet silk every 2-4 hours during the soaking process, and separating sericin on the surface of the sheet silk from silk; step three: washing the soaked silk with clear water, and soaking the silk in hot water for 2-3h to obtain defatted silk; step four: dehydrating the degreased silk, and then soaking the degreased silk in a softener for 0.5-1h to obtain soft silk after soaking; the preparation method of the rabbit hair-imitated real silk fabric saves cost, and is low in manufacturing cost, good in comfort level and high in safety.
Description
Technical Field
The invention relates to the technical field of fabric preparation, in particular to a preparation method of a rabbit hair-like real silk fabric.
Background
With the overall improvement of living standard and the enhancement of environmental protection consciousness, consumers put forward the requirements of individuation, diversification, functionalization, comfort, safety and no public nuisance to textiles. The garment fabric is a common textile, so that people pay more attention to the garment fabric, and higher requirements are provided for comfort, health and safety of the garment fabric. Animal wool fabrics, such as wool, mohair or alpaca and other wool fabrics, have the characteristics of soft hand feeling, super warmth retention, fashion and the like, and are popular with consumers. However, because animal hair is expensive, only expensive clothes can be made. In addition, animal protection, animal killing, and the use of animal fur for making clothes, accessories, shoes, etc. are currently being called for in both the international and domestic markets, resulting in an extremely high demand for alternatives to animal fur in the market. The rabbit wool fiber is a common animal hair fiber, is one of natural fibers, has the characteristics of fluffiness, whiteness, lightness, smoothness and good heat preservation, is a precious animal fiber, and is known as 'green soft gold', but because of the material cost of the rabbit wool fiber and the consideration of the green environmental protection, the rabbit wool fiber is gradually occupied in a larger space in the market and gradually replaces the rabbit wool fiber to a certain extent, and the market has higher requirements on the simulation and the functionality of a rabbit wool fiber product, so that the rabbit wool-like silk fabric preparation method is provided.
Disclosure of Invention
The invention aims to overcome the defects in the prior art, provides the preparation method of the rabbit hair-like silk fabric, saves cost, has low manufacturing cost, good comfort level and high safety, and can effectively solve the problems in the background art.
In order to achieve the purpose, the invention provides the following technical scheme: a preparation method of a rabbit hair-like silk fabric comprises the following steps:
the method comprises the following steps: selecting proper quantity and quality of silkworm cocoons, putting the silkworm cocoons into clear water, adding a degreasing agent into the water, and stirring for 0.2-0.4h, so that the silkworm cocoons are separated into flaky silk;
step two: soaking the processed sheet silk in a cleaning solution at a ratio of 1:40, turning over the sheet silk every 2-4 hours during the soaking process, and separating sericin on the surface of the sheet silk from silk;
step three: washing the soaked silk with clear water, and soaking the silk in hot water for 2-3h to obtain defatted silk;
step four: dehydrating the degreased silk, and then soaking the degreased silk in a softener for 0.5-1h to obtain soft silk after soaking;
step five: dehydrating the soft silk, and then putting the dehydrated soft silk in a cool place for airing, thereby obtaining the prepared silk;
step six: silk is used as bottom silk, acrylic fiber and nylon are mixed into surface silk, the surface silk is woven into gray cloth, and the gray cloth is cut into proper size by using a tool;
step seven: putting the cut gray cloth into a conveying furnace for conveying and heating, wherein the heating temperature is kept between 200 ℃ and 220 ℃, so that the gray cloth is dried;
step eight: putting the dried gray cloth into a reaction cylinder, adding an antistatic agent and a fluffing agent into the reaction cylinder, and soaking for 0.2-0.4h at the temperature of 40-50 ℃;
step nine: and (3) hot-blowing the treated gray cloth by using an air heater, and straightening the surface of the gray cloth after drying to obtain the finished fabric.
Preferably, in the step one, the degreasing agent is an alkaline degreasing agent, and the ratio of the degreasing agent to the clean water is 1:10-1: 13.
Preferably, in the second step, the soaking time of the sheet silk is 25-30 h.
Preferably, in step three, the temperature of the hot water is maintained between 95 ℃ and 100 ℃.
Preferably, in the fourth step, the softener is ester-based quaternary ammonium salt, and the ratio of the degreased silk to the softener is 1:30-1: 35.
Preferably, in the sixth step, the ratio of the nylon to the acrylic fibers is 1:5-1:6, and the tool is preferably a cutting machine.
Preferably, in step eight, the antistatic agent and the bulking agent are added in a ratio of 1: 1.
Compared with the prior art, the invention has the beneficial effects that: the preparation method of the rabbit hair-imitated real silk fabric has the following advantages:
1. the silk is subjected to various treatments, so that harmful substances and impurities on the surface of the silk are removed, the subsequently made silk fabric is safer and cleaner, and the service life of the silk fabric is prolonged;
2. the rabbit hair imitation woven by mixing nylon and acrylic fibers in a certain proportion can effectively reduce the kill of animals, and meanwhile, the manufacturing cost is low, and the purpose of saving the cost is achieved;
3. the gray cloth is treated by using various solutions, so that the comfort and flexibility of the real silk fabric are ensured, and the practicability of the real silk fabric is effectively improved.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The first embodiment is as follows: a preparation method of a rabbit hair-like silk fabric comprises the following steps:
the method comprises the following steps: selecting proper quantity and quality of silkworm cocoons, putting the silkworm cocoons into clean water, adding a degreasing agent into the water, and stirring for 0.2h, wherein the degreasing agent is an alkaline degreasing agent, and the ratio of the degreasing agent to the clean water is 1:10, so that the silkworm cocoons are degummed into flaky silk;
step two: soaking the processed sheet silk in a cleaning solution for 25h, wherein the ratio of the sheet silk to the cleaning solution is 1:40, and the sheet silk is turned over every 2h in the soaking process to separate sericin on the surface of the sheet silk from silk;
step three: washing the soaked silk with clear water, soaking the silk in hot water for 2-3h, and keeping the temperature of the hot water at 95 ℃ to obtain degreased silk;
step four: dehydrating the degreased silk, and then soaking the degreased silk in a softener for 0.5h, wherein the softener is ester-based quaternary ammonium salt, the ratio of the degreased silk to the softener is 1:30, and obtaining the softened silk after soaking;
step five: dehydrating the soft silk, and then putting the dehydrated soft silk in a cool place for airing, thereby obtaining the prepared silk;
step six: the silk is used as the bottom silk, the acrylic fiber and the nylon are mixed into the face silk, the ratio of the nylon to the acrylic fiber is 1:5, the base fabric is woven, the base fabric is cut into a proper size by using a tool, and the tool preferably adopts a cutting machine;
step seven: putting the cut gray cloth into a conveying furnace for conveying and heating, and keeping the heating temperature at 200 ℃ so as to dry the gray cloth;
step eight: putting the dried gray cloth into a reaction cylinder, adding an antistatic agent and a fluffing agent into the reaction cylinder, wherein the ratio of the added antistatic agent to the fluffing agent is 1:1, and soaking for 0.2h at 40 ℃;
step nine: and (3) hot-blowing the treated gray cloth by using an air heater, and straightening the surface of the gray cloth after drying to obtain the finished fabric.
Example two: a preparation method of a rabbit hair-like silk fabric comprises the following steps:
the method comprises the following steps: selecting proper quantity and quality of silkworm cocoons, putting the silkworm cocoons into clean water, adding a degreasing agent into the water, and stirring for 0.3h, wherein the degreasing agent is an alkaline degreasing agent, and the ratio of the degreasing agent to the clean water is 1:11, so that the silkworm cocoons are degummed into flaky silk;
step two: soaking the processed sheet silk in a cleaning solution for 28 hours, wherein the ratio of the sheet silk to the cleaning solution is 1:40, and turning over the sheet silk every 3 hours in the soaking process to separate sericin on the surface of the sheet silk from silk;
step three: washing the soaked silk with clear water, soaking the silk in hot water for 2.5h, and keeping the temperature of the hot water at 98 ℃ to obtain degreased silk;
step four: dehydrating the degreased silk, and then soaking the degreased silk in a softener for 0.8h, wherein the softener is ester-based quaternary ammonium salt, the ratio of the degreased silk to the softener is 1:32, and obtaining the softened silk after soaking;
step five: dehydrating the soft silk, and then putting the dehydrated soft silk in a cool place for airing, thereby obtaining the prepared silk;
step six: the silk is used as the bottom silk, the acrylic fiber and the nylon are mixed into the face silk, the ratio of the nylon to the acrylic fiber is 1:5.5, the base fabric is woven, the base fabric is cut into a proper size by using a tool, and the tool preferably adopts a cutting machine;
step seven: putting the cut gray cloth into a conveying furnace for conveying and heating, and keeping the heating temperature at 210 ℃ so as to dry the gray cloth;
step eight: putting the dried gray cloth into a reaction cylinder, adding an antistatic agent and a fluffing agent into the reaction cylinder, wherein the ratio of the added antistatic agent to the fluffing agent is 1:1, and soaking for 0.3h at the temperature of 45 ℃;
step nine: and (3) hot-blowing the treated gray cloth by using an air heater, and straightening the surface of the gray cloth after drying to obtain the finished fabric.
Example three: a preparation method of a rabbit hair-like silk fabric comprises the following steps:
the method comprises the following steps: selecting proper quantity and quality of silkworm cocoons, putting the silkworm cocoons into clean water, adding a degreasing agent into the water, and stirring for 0.4h, wherein the degreasing agent is an alkaline degreasing agent, and the ratio of the degreasing agent to the clean water is 1:13, so that the silkworm cocoons are degummed into flaky silk;
step two: soaking the processed sheet silk in a cleaning solution for 30 hours, wherein the ratio of the sheet silk to the cleaning solution is 1:40, and the sheet silk is turned over every 4 hours in the soaking process to separate sericin on the surface of the sheet silk from silk;
step three: washing the soaked silk with clear water, soaking the silk in hot water for 3h, and keeping the temperature of the hot water at 100 ℃ to obtain degreased silk;
step four: dehydrating the degreased silk, and then soaking the degreased silk in a softener for 1h, wherein the softener is ester-based quaternary ammonium salt, the ratio of the degreased silk to the softener is 1:35, and obtaining the softened silk after soaking;
step five: dehydrating the soft silk, and then putting the dehydrated soft silk in a cool place for airing, thereby obtaining the prepared silk;
step six: the silk is used as the bottom silk, the acrylic fiber and the nylon are mixed into the face silk, the ratio of the nylon to the acrylic fiber is 1:6, the base fabric is woven, the base fabric is cut into a proper size by using a tool, and the tool preferably adopts a cutting machine;
step seven: putting the cut gray cloth into a conveying furnace for conveying and heating, and keeping the heating temperature at 220 ℃ so as to dry the gray cloth;
step eight: putting the dried gray cloth into a reaction cylinder, adding an antistatic agent and a fluffing agent into the reaction cylinder, wherein the ratio of the added antistatic agent to the fluffing agent is 1:1, and soaking for 0.4h at 50 ℃;
step nine: and (3) hot-blowing the treated gray cloth by using an air heater, and straightening the surface of the gray cloth after drying to obtain the finished fabric.
At first carry out multiple processing to silk to get rid of the harmful substance and the impurity on silk surface, thereby make the silk surface fabric of follow-up making safer and clean, also improve the life of silk surface fabric simultaneously, adopt the mixed imitative rabbit hair of weaving formation of nylon and acrylic fibres of certain proportion can effectively reduce the kill of animal simultaneously, the while cost is cheap, also play the purpose of saving the cost, use multiple solution to handle the gray cloth at last, both guaranteed the comfort level and the compliance of silk surface fabric, the practicality of silk surface fabric has also effectively been improved simultaneously.
The above description is only an embodiment of the present invention, and not intended to limit the scope of the present invention, and all modifications of equivalent structures and equivalent processes, which are made by the present specification, or directly or indirectly applied to other related technical fields, are included in the scope of the present invention.
Claims (7)
1. A preparation method of a rabbit hair-like real silk fabric is characterized by comprising the following steps:
the method comprises the following steps: selecting proper quantity and quality of silkworm cocoons, putting the silkworm cocoons into clear water, adding a degreasing agent into the water, and stirring for 0.2-0.4h, so that the silkworm cocoons are separated into flaky silk;
step two: soaking the processed sheet silk in a cleaning solution at a ratio of 1:40, turning over the sheet silk every 2-4 hours during the soaking process, and separating sericin on the surface of the sheet silk from silk;
step three: washing the soaked silk with clear water, and soaking the silk in hot water for 2-3h to obtain defatted silk;
step four: dehydrating the degreased silk, and then soaking the degreased silk in a softener for 0.5-1h to obtain soft silk after soaking;
step five: dehydrating the soft silk, and then putting the dehydrated soft silk in a cool place for airing, thereby obtaining the prepared silk;
step six: silk is used as bottom silk, acrylic fiber and nylon are mixed into surface silk, the surface silk is woven into gray cloth, and the gray cloth is cut into proper size by using a tool;
step seven: putting the cut gray cloth into a conveying furnace for conveying and heating, wherein the heating temperature is kept between 200 ℃ and 220 ℃, so that the gray cloth is dried;
step eight: putting the dried gray cloth into a reaction cylinder, adding an antistatic agent and a fluffing agent into the reaction cylinder, and soaking for 0.2-0.4h at the temperature of 40-50 ℃;
step nine: and (3) hot-blowing the treated gray cloth by using an air heater, and straightening the surface of the gray cloth after drying to obtain the finished fabric.
2. The preparation method of the rabbit hair-like silk fabric according to claim 1, which is characterized by comprising the following steps: in the first step, the degreasing agent is an alkaline degreasing agent, and the ratio of the degreasing agent to clean water is 1:10-1: 13.
3. The preparation method of the rabbit hair-like silk fabric according to claim 1, which is characterized by comprising the following steps: in the second step, the soaking time of the flaky silks is 25-30 h.
4. The preparation method of the rabbit hair-like silk fabric according to claim 1, which is characterized by comprising the following steps: in step three, the temperature of the hot water is kept between 95 ℃ and 100 ℃.
5. The preparation method of the rabbit hair-like silk fabric according to claim 1, which is characterized by comprising the following steps: in the fourth step, the softener is ester quaternary ammonium salt, and the ratio of the degreased silk to the softener is 1:30-1: 35.
6. The preparation method of the rabbit hair-like silk fabric according to claim 1, which is characterized by comprising the following steps: in the sixth step, the ratio of nylon and acrylic fiber is 1:5-1:6, and the tool is preferably a cutting machine.
7. The preparation method of the rabbit hair-like silk fabric according to claim 1, which is characterized by comprising the following steps: in step eight, the ratio of the antistatic agent to the bulking agent added is 1: 1.