CN113046908A - 一种含有石墨烯以及锗离子布料 - Google Patents
一种含有石墨烯以及锗离子布料 Download PDFInfo
- Publication number
- CN113046908A CN113046908A CN202110303320.4A CN202110303320A CN113046908A CN 113046908 A CN113046908 A CN 113046908A CN 202110303320 A CN202110303320 A CN 202110303320A CN 113046908 A CN113046908 A CN 113046908A
- Authority
- CN
- China
- Prior art keywords
- germanium
- graphene
- yarns
- yarn
- terylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及功能性面料加工技术领域，具体公开了一种含有石墨烯以及锗离子布料，锗离子纱线以及石墨烯纱线，其所述的材料重量百分比如下：锗离子纱线56％、石墨烯纱线44％，所述锗离子纱线包括，1％锗离子以及99％涤纶；所述石墨烯纱线包括，0.1％石墨烯以及99.9％涤纶，所述锗离子纱线通过所述锗离子与涤纶进行原位聚合得到，将石墨烯纱线以及锗离子纱线进行编织成布料，石墨烯纱线以及锗离子纱线混合形成特殊材质具有远红外作用，对人体具有一定的保健作用。
Description
技术领域
本发明涉及功能性面料加工技术领域，具体公开了一种含有石墨烯以及锗离子布料。
背景技术
锗的药用保健功效：强化自然治愈力、改善全身体质、防止老化、预防癌症、消除肿瘤、肝病、气喘、血压调整、排除体内的毒素、自律神经失调症等等慢性病症；因为锗离子的特性，只有贴合在病变处的锗离子使用品才能起到预警作用，目前市面上有很多含有锗元素的手链及床垫等保健用品，只能限制在佩戴的范围内才能起到预警作用，不能及时的预警全身范围内病变的部位，并且疏导病变时产生的生物电。
石墨烯具有以下作用：
石墨烯拥有的大苯环结构在5-15微米的波长范围内有着强烈的红外吸收，是理想的远红外吸收材料，同样也是理想的远红外辐射材料。石墨烯功能纤维能够吸收外界的光、热能并将其转化为对人体及其有益的远红外射线反射回皮肤。4-16微米的远红外线被称为“生命射线”，其能量能够与人体细胞组织发生共振，加速血液循环及新陈代谢。可有效缓解疲劳、抗氧化、净化体内毒素以提高人体
精力充沛，减少脂肪团形成。
石墨烯上的碳原子组成的共轭结构恰好能够与紫外线的能量匹配，从而能够有效的吸收屏蔽紫外线。同时石墨烯特有的二维结构，也使得其在光线屏蔽方面特别有效，仅用极少量的添加量就可获得很好的紫外屏蔽效果。波长范围290-400 纳米的紫外线照射会让皮肤产生大量自由基，导致细胞膜的过氧化反应，使黑色素细胞产生更多的黑色素。石墨烯功能纤维能够屏蔽紫外线，保护皮肤不被晒伤，降低皮肤癌发病风险。
作为一种压电材料，石墨烯能够释放出丰富的负离子。市场上一些负离子纤维产品采用“独居石”这种具有放射性的材料，会对人体产生巨大的危害，而石墨烯功能性纤维则安全环保。负离子被称为“空气的维生素”，具有两大功能：净化空气——去除粉尘，分解有害气体；疗养保健——改善大脑功能，增加机体免疫力，促进新陈代谢，调节神经机能，消除疲劳，可使心率减慢，高血压患者的血压趋于正常，还可以使呼吸道表面的纤毛运动加强，腺体分泌增强，改善肺的通气功能，降低呼吸道对创伤的易感性。
石墨烯独特的纳米级边缘，大比表面积以及表面官能团能够切割、包裹细菌，催化细菌的氧化应激，从而达到抑制细菌生长的抗菌效果。虽然其抗菌机理学界仍在积极研究，但是其作为一种抗菌剂，既不会产生耐药性，也不像重金属离子一样对环境、人体造成威胁，已经展现出极其诱人的前景。石墨能催化寄生在人体皮肤表面的螨虫发生氧化应激，从而有效抑制螨虫繁殖生长。同时石墨烯功能纤维不含任何抗抗螨化学制剂，安全环保，对人体无刺激，人螨普遍寄生于人体毛囊和皮质腺内，科研人员长期研究发现，螨虫感染度高者可致病，而螨少虽未致病，也同样影响美容效果，螨虫寄生可引起的痤疮、粉刺、小红疙瘩、瘙痒等各种肌肤问题，石墨烯功能性纤维具有抑制螨虫生长功能，减轻螨虫带来的皮肤问题，该特性特别适用于家纺类等不能经常洗地的产品，现有布料未能将锗离子以及石墨烯的功能性相结合。
发明内容
本发明针对上述现有技术的不足设计而提供一种含有石墨烯以及锗离子布料，包括以下步骤：
本发明为解决上述问题所采用的技术方案如下：
一种含有石墨烯以及锗离子布料，其组成成分包括：锗离子纱线以及石墨烯纱线，其所述的材料重量百分比如下：
锗离子纱线:56％；
石墨烯纱线：44％；
所述锗离子纱线包括，1％锗离子以及99％涤纶；
所述石墨烯纱线包括，0.1％石墨烯以及99.9％涤纶；
所述锗离子纱线通过所述锗离子与涤纶进行原位聚合得到。
进一步的，所述锗离子纱线原位聚合包括以下步骤：
S1:将锗离子溶液及稀盐酸置于容器中，将涤纶放入含有APS溶液内;
S2:将S1中制得的APS涤纶置于密闭容器中，并将容器抽真空；
S3:将涤纶处于锗离子溶液中，涤纶表面的氧化剂APS与锗离子单体反应，进行原位聚合。
进一步的，所述锗离子纱线以及所述石墨烯纱线进行编织成布料。
进一步的，所述布料采用纬编双纱编织工艺，采用面纱石墨烯纱线编织，底纱锗离子涤纶编织成布料。
进一步的，所述的锗离子溶液内为纳米锗粉，粒径为20-30纳米。
综上所述，本发明有益效果：本发明提供了一种含有石墨烯以及锗离子布料，锗离子纱线以及石墨烯纱线，其所述的材料重量百分比如下：锗离子纱线56％、石墨烯纱线44％，所述锗离子纱线包括，1％锗离子以及99％涤纶；所述石墨烯纱线包括，0.1％石墨烯以及99.9％涤纶，所述锗离子纱线通过所述锗离子与涤纶进行原位聚合得到，将石墨烯纱线以及锗离子纱线进行编织成布料，石墨烯纱线以及锗离子纱线混合形成特殊材质具有远红外作用，对人体具有一定的保健作用。
具体实施方式
下面具体阐明本发明的实施方式，不构成对本发明专利保护范围的限制。
一种含有石墨烯以及锗离子布料，其组成成分包括：锗离子纱线以及石墨烯纱线，其所述的材料重量百分比如下：
锗离子纱线:56％；
石墨烯纱线：44％；
所述锗离子纱线包括，1％锗离子以及99％涤纶；
所述石墨烯纱线包括，0.1％石墨烯以及99.9％涤纶；
所述锗离子纱线通过所述锗离子与涤纶进行原位聚合得到。
作为本实施例一种优选的实施方式，所述锗离子纱线原位聚合包括以下步骤：
S1:将锗离子溶液及稀盐酸置于容器中，将涤纶放入含有APS溶液内;
S2:将S1中制得的APS涤纶置于密闭容器中，并将容器抽真空；
S3:将涤纶处于锗离子溶液中，涤纶表面的氧化剂APS与锗离子单体反应，进行原位聚合。
此外，所述锗离子纱线以及所述石墨烯纱线进行编织成布料。
作为本实施例另一种优选的实施方式，所述布料采用横竖交叉编织法编织，采用横向多根锗纱线，竖向多根石墨烯纱线编织，每股横向锗纱线间隔0.2-3CM，每股竖向石墨烯纱线间隔0.05- 1CM，横向及竖向的锗纱线间隔距离对等或不对等，编织成布料。
进一步的，所述布料采用纬编双纱编织工艺，采用面纱石墨烯纱线编织，底纱锗离子涤纶编织成布料。
具体的，所述的锗离子溶液内为纳米锗粉，粒径为20-30纳米。
本发明提供了一种含有石墨烯以及锗离子布料，锗离子纱线以及石墨烯纱线，其所述的材料重量百分比如下：锗离子纱线56％、石墨烯纱线44％，所述锗离子纱线包括，1％锗离子以及99％涤纶；所述石墨烯纱线包括，0.1％石墨烯以及99.9％涤纶，所述锗离子纱线通过所述锗离子与涤纶进行原位聚合得到，将石墨烯纱线以及锗离子纱线进行编织成布料，石墨烯纱线以及锗离子纱线混合形成特殊材质具有远红外作用，对人体具有一定的保健作用。
上述实施例为本发明较佳的实施方式，但本发明的实施方式并不受上述实施例的限制，其他的任何未违背本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包括在本发明的保护范围。
Claims (5)
1.一种含有石墨烯以及锗离子布料，其特征在于，其组成成分包括：锗离子纱线以及石墨烯纱线，其所述的材料重量百分比如下：
锗离子纱线:56％；
石墨烯纱线：44％；
所述锗离子纱线包括，1％锗离子以及99％涤纶；
所述石墨烯纱线包括，0.1％石墨烯以及99.9％涤纶；
所述锗离子纱线通过所述锗离子与涤纶进行原位聚合得到。
2.根据权利要求1所述的一种含有石墨烯以及锗离子布料，其特征在于：所述锗离子纱线原位聚合包括以下步骤：
S1:将锗离子溶液及稀盐酸置于容器中，将涤纶放入含有APS溶液内;
S2:将S1中制得的APS涤纶置于密闭容器中，并将容器抽真空；
S3:将涤纶处于锗离子溶液中，涤纶表面的氧化剂APS与锗离子单体反应，进行原位聚合。
3.根据权利要求1所述的一种含有石墨烯以及锗离子布料，其特征在于:所述锗离子纱线以及所述石墨烯纱线进行编织成布料，所述布料采用纬编双纱编织工艺，采用面纱石墨烯纱线编织，底纱锗离子涤纶编织成布料。
4. 根据权利要求3所述的一种含有石墨烯以及锗离子布料，其特征在于：所述布料采用横竖交叉编织法编织，采用横向多根锗纱线，竖向多根石墨烯纱线编织，每股横向锗纱线间隔0.2-3CM，每股竖向石墨烯纱线间隔0.05- 1CM，横向及竖向的锗纱线间隔距离对等或不对等，编织成布料。
5.根据权利要求1所述的一种含有石墨烯以及锗离子布料，其特征在于：所述的锗离子溶液内为纳米锗粉，粒径为20-30纳米。