CN1129264A - Improved process for making filament-blended profiled-section combined filament yarn of polyester - Google Patents
Improved process for making filament-blended profiled-section combined filament yarn of polyester Download PDFInfo
- Publication number
- CN1129264A CN1129264A CN 95116944 CN95116944A CN1129264A CN 1129264 A CN1129264 A CN 1129264A CN 95116944 CN95116944 CN 95116944 CN 95116944 A CN95116944 A CN 95116944A CN 1129264 A CN1129264 A CN 1129264A
- Authority
- CN
- China
- Prior art keywords
- stretching
- degree
- yarn
- monofilament
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention utilizes the different spinneret orifices with vairous sections which are positioned in same spinneret plate and directly stretches spinning equipment to produce the invented polyester heterotiter and heterosection combined filament yarn whose winding speed is greater than 3000 m/min., Said invention starts with the increasement of spinning temp., elongation of heated time, appropriate control of stretch and winding tension and selection of spin finishes with high friction coefficient to solve the problems of that the grey yarn of the combined filament yarn has the broken yarn and staining. After having been dyed and finished the grey yarn made up by using said invention can make the face have high bulkiness gradation feeling and dry-unsmooth cool and refreshing feeling.
Description
The present invention is the spinning manufacture method of filament-blended profiled-section combined filament yarn, in detail, and for the relevant spinning nozzle that has different multiple sections in the same spinnerets that utilizes is made the Polyester Filament that volume speed is higher than 3000m/min with step direct fabrics extension.
Always, the manufacturing step of filament-blended profiled-section combined filament yarn is all the spinning cake of making different fiber numbers or different section in spinning, doubling extension when stretching sth. made by twisting (discloses 61-28036 as Japan is special again, 61-179333 and 62-268834 etc.) or use the spinnerets of each tool different section fiber number spinning nozzle, its processing procedure as shown in Figure 3 in stretching sth. made by twisting extension (disclosing clear 62-268834 as Japan is special) again to make spinning cake prior to spinning, melt and dissolved polyester body with different discharge-amounts in spinneret (1) heating after the spinnerets of single section (1 ') or with certain discharge-amount in spinneret (1) heating after spinnerets (1 ') the back ejection of the spinning nozzle of six kinds of sections of tool be a tow (2) takes turns (5) and draw to friction pulley (6) and batch spinning cake (7A into different fiber numbers or the different section of iso-fineness with 1400m/min through oil nozzle (4) organizine that oils again again after the cooling air cooling, 7B, 7C, 7D) deposit after again through manually transferring on the spinning cake frame of elongator, cake silk rear haulage is through heated wheel (8), heating plate (9) and extending after wheel (10) heating extends typing batches and is precursor (11).Its processing procedure is complicated and have low speed not extend thread resting period short (resting period of a specified duration excessively will be caused the variation of spinning cake rerum natura) spinning cake transfer labour expense height, and metachromia easily changes, and shortcoming such as yield poorly.
Purpose of the present invention is to provide one to utilize the direct fabrics extension device to produce filament-blended profiled-section combined filament yarn to simplify manufacturing step and to avoid the resting period to influence the manufacturing processing procedure of combined yarn quality.
The inventor develops the procedure for producing that direct fabrics extend filament-blended profiled-section combined filament yarn, and the result through the test of concentrating on studies is produced works out finally with higher spinning temperature (being higher than 290 ℃), long extension heated time 1.0 * 10
-3-2.0 * 10
-3Divide and coiling tension less than (0.25*Den) gram, the finish of the coefficient of kinetic friction (F/M μ d) 〉=more than 0.330.Can obtain between good metachromia and monfil maximum degree of stretching poor 〉=40% former spinning cake.Describe technology contents of the present invention in detail in following:
Filament-blended profiled-section combined filament yarn of the present invention, its spinnerets is combined by three kinds of above spinning nozzles of section, the section configuration of the spinning nozzle of spinnerets that the present invention adopts as shown in Figure 1, as Fig. 2, direct bearing of the present invention uses the spinnerets (2) with different section spinning nozzle more than three kinds, melt and dissolved condensate heats after spinnerets (2) ejection is cooled off through the cooling air of cooling air device (4) for tow (3) again in the spinneret (1) of 290-310 ℃ of temperature, boundling is gone into after oil nozzle (5) oils greater than the finish more than 0.330 with the coefficient of kinetic friction (F/M μ d), tow draws into heated wheel (6) with the heating of 70-120 ℃ temperature, heat time heating time 1.0-2.0 * 10
-3Divide, again after extension HEAT SETTING wheel (7) is with 1.30-1.70 times extension ratio extension, tow draws behind contact wheel (8) again, to feed rate greater than 1.0%, coiling tension is less than the tension force of (0.25*Den) gram, batch with the coiling speed that is higher than 3000 meters/minute and to be former spinning cake (9), extend processing procedure through above direct fabrics and can obtain to supply the filament-blended profiled-section combined filament yarn that fine thing uses, must not process and avoid not extending silk through above-mentioned transfer extension of stretching the sth. made by twisting process again and deposit the influence of factor, more can improve output because of the raising of rolling up speed to quality.
The main composition key element of the combination of monofilaments of combined yarn of the present invention, for the monofilament above macrofibril of 3 red Buddhist nuns and thin fibril below the 1.5 red Buddhist nuns are lumped together and section configuration tool projecting point, thick fibre and thin fine spinning nozzle section can have 6 kinds, so silk can get the fine thing of the fluffy sense of dry refreshing soft tool after fibre is made, so its monofilament that can obtain different fiber numbers and degree of stretching, tie up in six kinds of spinning nozzle basal areas and vary in size, in the same spinnerets, the sectional area of single hole more then discharge-amount is bigger, bigger in the spinning nozzle initial velocity, under certain coiling speed, (Draft Ratio) is less for the spinning draw ratio, and filament number is bigger, and degree of stretching is higher, otherwise then the fiber number of monofilament is less, and degree of stretching is lower; For improveing above-mentioned shortcoming, finish the present invention through studying intensively.
Monofilament degree of the stretching maximum difference of the combined yarn of applicant's invention is more than 40%, and the degree of stretching of adjacent monofilament difference is below 10%, usually then below 5%.Owing to like this monofilament degree of stretching difference makes that after the fine cloth dyeing and finishing, cloth cover has bulkiness, if the too small then fluffy poor effect of degree of stretching maximum difference between monofilament; It is unfavorable that adjacent monofilament degree of stretching difference is too greatly then produced, easily fracture of wire.
The present invention has multiple different section spinning nozzle on a spinnerets for utilizing, if spinning temperature is crossed and is lower than 290 ℃ and will causes and polymericly flow not goodly, distributes uneven and causes to spue and have some setbacks, and easily fracture of wire can't be produced.
The too low frictional force deficiency that then causes between tow and heated wheel of the coefficient of kinetic friction of finish, and then make the tow slip swing, cause the disrumpent feelings silk that twines of bundle, the dyeability inequality of silk.
The heated wheel heating-up temperature is too high, heat time heating time is oversize, can cause tow too soft and on heated wheel, swing, and cause the phenomenon that tow is disrumpent feelings and metachromia is uneven, and the heated wheel temperature is too low, and heat time heating time is too short, then causes the molecule in prepattern district fully not loose, when extending, will have and extend bottle head (NECK) generation and cause fracture of wire, if use lower extension ratio then to cause the phenomenon of extending the not enough dyeability inequality of orientation.
The Tension Control that over feed rate(OFR) after extending batches causes greater than (0.25*DEN) Ke Shiyi for the very big coiling tension of influence of spinning cake moulding and throws silk and moulding and lift up the angle and alleviate difficult.
For solving the above problems, wait and tax one's ingenuity through the applicant, study intensively, according to aforementioned of the present invention create conditions to produce can obtain productivity, the filament-blended profiled-section combined filament yarn that easy zbility is good.
Embodiment:
The shape of use shown in Fig. 1 and table 1 and the spinning nozzle of size (spinning nozzle<A〉two kinds of each 12 holes of size, spinning nozzle<B〉two kinds of each 8 holes of size, spinning nozzle<C〉two kinds of each 4 holes of size) add up to the spinnerets in 48 holes and use the direct fabrics extension device, setting the spinneret temperature is that 290 ℃ of-310 ℃ of discharge-amounts are that 35-50 Grams Per Minute heated wheel temperature are 80-110 ℃, extending wheel speed is 4000-4900m/min, coiling speed is 3920-4800m/min, and the filament number of each section and degree of stretching measurement result are as shown in table 2.
Table 1
The spinneret orifice size | ????A1 | ????A2 | ????B1 | ????B2 | ????C1 | ????C2 |
????a(mm) | ????0.08 | ????0.08 | ????0.08 | ????0.08 | ????0.08 | ????0.08 |
????b(mm) | ????0.20 | ????0.30 | ????0.60 | ????0.80 | ????0.40 | ????0.50 |
????c(mm) | ????0.40 | ????0.440 | ????0.30 | ????0.30 | ????0.90 | ????1.00 |
????d(mm) | ????0.08 | ????0.08 | ????0.10 | ????0.10 | ||
H (hole) | ????12 | ????12 | ????8 | ????8 | ????4 | ????4 |
Table 2
Combined yarn constitutes the rerum natura of monofilament | The weight % of heavy denier silk | Fine denier filament's weight % | Emax- Emin (%) | The maximum of E1+1-E1 (%) | |||
The monofilament group | The bar number | Filament number (den) | Monofilament degree of stretching distribution (%) | ||||
?A2 | ?12 | ????1.0 | ?38.2-58.7 | ????13 | ?31,7 | 57.3 | ????4.8 |
?A1 | ?12 | ????1.2 | ?58.8-67.7 | ||||
?B2 | ?8 | ????1.7 | ?69.4-73.0 | ||||
?B1 | ?8 | ????2.0 | ?76.3-81.0 | ||||
?C2 | ?4 | ????2.4 | ?81.4-87.1 | ||||
?C1 | ?4 | ????3.2 | ?89.6-95.5 |
Emax: the degree of stretching (%) of maximum degree of stretching monofilament in the combined yarn
Emin: the degree of stretching (%) of minimum degree of stretching monofilament in the combined yarn
E 1: be the degree of stretching (%) of arbitrary monofilament in the combined yarn
E1+1: in the combined yarn with the degree of stretching (%) of the nearest monofilament of E degree of stretching
According to the fine filament-blended profiled-section combined filament yarn that extends of Direct Spinning that the present invention produces, can directly supply fine thing and use, spinning cake must not stretched through transfer and use for fine thing after sth. made by twisting is processed as precursor again.
Combined yarn of the present invention, the above percentage by weight of the red Buddhist nun 3 red Buddhist nuns of monofilament is more than 10%, the degree of stretching of adjacent monofilament difference is below 10%, usually then below 5%.Because the difference of degree of stretching between monofilament, the projecting point that makes silk have fluffy sense to add the monofilament section configuration after fine cloth dyeing and finishing makes cloth cover have dry and astringent refrigerant sense.
Fig. 1 is the section of spinning nozzle of the present invention.
Fig. 2 is that direct fabrics of the present invention extend processing procedure.
Fig. 3 is that two sections processing procedures are extended in known spinning.
Fig. 4 is the cloth cover photo after the fine cloth dyeing and finishing of combined yarn of the present invention.
Claims (2)
1. the improved process for making of a filament-blended profiled-section combined filament yarn of polyester, it is characterized in that the processing procedure that direct fabrics extend, employed spinnerets is combined by three kinds of above spinning nozzles of section in shown in Figure 1, its create conditions into the melt and dissolved condensate of polyester after the heating of the spinneret (1) of 290 ℃-310 ℃ of temperature, be tow (3) through spinnerets (2) ejection, go into oil nozzle (5) through the cooling air cooling boundling of cooling air device (4) again, after oiling greater than the finish more than 0.330 with the coefficient of kinetic friction (F/M μ d), tow draws after heated wheel (6) extends with 1.30-1.70 times extension ratio, tow draws through contact with the tension force of coiling tension less than (0.25*Den) gram again, batches with the coiling speed that is higher than 3000 meters/minute to be the different section polyester of polyester iso-fineness combined yarn goods.
2. filament-blended profiled-section combined filament yarn of polyester as claimed in claim 1, the above percentage by weight of the red Buddhist nun 3 red Buddhist nuns of its combined yarn monofilament is more than 10%, the following percentage by weight of the red Buddhist nun 1.5 red Buddhist nuns of monofilament is more than 25%, and degree of stretching has following partaker between monofilament:
Emax-Emin≥40%
E1+1-E1≤10%
Emax is the degree of stretching (%) of maximum degree of stretching monofilament in the combined yarn
Emin is the degree of stretching (%) of minimum degree of stretching monofilament in the combined yarn
E1 is in the combined yarn, the degree of stretching of arbitrary monofilament (%)
E1+1 for the nearest list of E degree of stretching after degree of stretching (%).