CN112897965A - 利用碱激发材料快速修复裂缝的方法 - Google Patents
利用碱激发材料快速修复裂缝的方法 Download PDFInfo
- Publication number
- CN112897965A CN112897965A CN202110127234.2A CN202110127234A CN112897965A CN 112897965 A CN112897965 A CN 112897965A CN 202110127234 A CN202110127234 A CN 202110127234A CN 112897965 A CN112897965 A CN 112897965A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- alkali
- activated
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种利用碱激发材料快速修复裂缝的方法，该方法包括以下步骤：将生石灰、氯化钙、高炉矿渣、钠基膨润土、碳酸镁、柠檬酸、二氧化铌、氢氧化钠、硫化钠、二氧化硅混合后，加入乙基纤维素和壳聚糖，混合得到碱激发灌浆料；将沥青加热至150‑165℃，加入石膏粉，然后加入碎石、石英砂，铺筑；加入所述的碱激发灌浆料，至孔隙率为98％‑100％，再进行养护。经过本发明的方法修复裂缝，能够快速凝结，并且终凝时间减少，从而快速修复裂缝。
Description
技术领域
本发明属于固化领域，尤其涉及一种利用碱激发材料快速修复裂缝的方法。
背景技术
碱激发胶凝材料，亦称“化学激发胶凝材料”。利用碱激发剂(苛性碱、含碱硅酸盐、铝酸盐)的催化原理制得的水硬性胶凝材料。包括碱矿渣水泥、地聚合物或土聚水泥等。主要由具一定急冷热历史的含铝硅酸盐煅烧天然矿物或工业废渣(如偏高岭土、矿渣、粉煤灰、硅灰、钢渣等)和碱激发剂组成。凝结硬化快、强度高和耐高温。用于土木建筑、固核固废、高强、密封和高温环境等工程。
申请号为CN201610572671.4的中国专利申请公开了一种改性低膨胀工业废渣基碱激发材料的制备方法，属于碱激发材料制备技术领域。本发明硅钙渣球磨过筛后，与电石渣等混合抽滤，滤饼洗涤干燥后，加入砂岩等混合煅烧。得改性熟料水泥备用，再取高炉矿渣等球磨，与制得碱激发剂混合后，加入备用的改性熟料水泥等混合模压，养护脱模后再常温下养护，只得材料，抗压强度强。
发明内容
本发明为了解决现有技术的不足，提供了一种利用碱激发材料快速修复裂缝的方法，凝结速度快，应用范围广。
为了解决上述技术问题，本发明采用以下技术方案：
利用碱激发材料快速修复裂缝的方法，包括以下步骤：将生石灰、氯化钙、高炉矿渣、钠基膨润土、碳酸镁、柠檬酸、二氧化铌、氢氧化钠、硫化钠、二氧化硅混合后，加入乙基纤维素和壳聚糖，混合得到碱激发灌浆料；将沥青加热至150-165℃，加入石膏粉，然后加入碎石、石英砂，铺筑；加入所述的碱激发灌浆料，至孔隙率为98％-100％，再进行养护。
作为优选，石英砂为粒径1-2mm的石英砂和粒径为2-2.5mm的石英砂，二者的重量比例为1：5-1：4。
作为优选，按重量份计，所述的生石灰40-60份、氯化钙30-40份、高炉矿渣100-200份、钠基膨润土20-30份、碳酸镁20-30份、柠檬酸10-20份、二氧化铌10-20份、氢氧化钠20-60份、硫化钠10-30份、二氧化硅20-40份、乙基纤维素30-60份和壳聚糖30-40份。
作为优选，按重量份计，所述的生石灰50份、氯化钙35份、高炉矿渣150份、钠基膨润土25份、碳酸镁25份、柠檬酸15份、二氧化铌15份、氢氧化钠40份、硫化钠20份、二氧化硅30份、乙基纤维素40份和壳聚糖35份。
作为优选，按重量份计，所述的生石灰40份、氯化钙30份、高炉矿渣100份、钠基膨润土20份、碳酸镁20份、柠檬酸10份、二氧化铌10份、氢氧化钠20份、硫化钠10份、二氧化硅20份、乙基纤维素30份和壳聚糖30份。
作为优选，按重量份计，所述的生石灰60份、氯化钙40份、高炉矿渣200份、钠基膨润土30份、碳酸镁30份、柠檬酸20份、二氧化铌20份、氢氧化钠60份、硫化钠30份、二氧化硅40份、乙基纤维素60份和壳聚糖40份。
作为优选，按重量份计，所述的生石灰47份、氯化钙38份、高炉矿渣180份、钠基膨润土28份、碳酸镁28份、柠檬酸13份、二氧化铌13份、氢氧化钠27份、硫化钠17份、二氧化硅27份、乙基纤维素37份和壳聚糖37份。
作为优选，铺筑厚度为3-4mm，铺筑的孔隙率为30％-32％。
本发明具有以下有益效果：氢氧化钠和硫化钠的加入能够激发生石灰，形成一种新型凝胶材料，乙基纤维素和壳聚糖的加入则进一步提高本发明的凝结效果；经过本发明的方法修复裂缝，能够快速凝结，并且终凝时间减少，从而快速修复裂缝。
具体实施方式
下面结合具体实施例对本发明作进一步详细介绍。
实施例1
利用碱激发材料快速修复裂缝的方法，包括以下步骤：将生石灰、氯化钙、高炉矿渣、钠基膨润土、碳酸镁、柠檬酸、二氧化铌、氢氧化钠、硫化钠、二氧化硅混合后，加入乙基纤维素和壳聚糖，混合得到碱激发灌浆料；将沥青加热至150-165℃，加入石膏粉，然后加入碎石、石英砂，铺筑，铺筑厚度为3mm，铺筑的孔隙率为30％-32％；加入所述的碱激发灌浆料，至孔隙率为98％-100％，再进行养护。
石英砂为粒径1-2mm的石英砂和粒径为2-2.5mm的石英砂，二者的重量比例为1：3：4。
按重量份计，所述的生石灰50份、氯化钙35份、高炉矿渣150份、钠基膨润土25份、碳酸镁25份、柠檬酸15份、二氧化铌15份、氢氧化钠40份、硫化钠20份、二氧化硅30份、乙基纤维素40份和壳聚糖35份。
实施例2
利用碱激发材料快速修复裂缝的方法，包括以下步骤：将生石灰、氯化钙、高炉矿渣、钠基膨润土、碳酸镁、柠檬酸、二氧化铌、氢氧化钠、硫化钠、二氧化硅混合后，加入乙基纤维素和壳聚糖，混合得到碱激发灌浆料；将沥青加热至150-165℃，加入石膏粉，然后加入碎石、石英砂，铺筑，铺筑厚度为4mm，铺筑的孔隙率为30％-32％；加入所述的碱激发灌浆料，至孔隙率为98％-100％，再进行养护。
石英砂为粒径1-2mm的石英砂和粒径为2-2.5mm的石英砂，二者的重量比例为1：1：4。
按重量份计，所述的生石灰40份、氯化钙30份、高炉矿渣100份、钠基膨润土20份、碳酸镁20份、柠檬酸10份、二氧化铌10份、氢氧化钠20份、硫化钠10份、二氧化硅20份、乙基纤维素30份和壳聚糖30份。
实施例3
利用碱激发材料快速修复裂缝的方法，包括以下步骤：将生石灰、氯化钙、高炉矿渣、钠基膨润土、碳酸镁、柠檬酸、二氧化铌、氢氧化钠、硫化钠、二氧化硅混合后，加入乙基纤维素和壳聚糖，混合得到碱激发灌浆料；将沥青加热至150-165℃，加入石膏粉，然后加入碎石、石英砂，铺筑，铺筑厚度为3mm，铺筑的孔隙率为30％-32％；加入所述的碱激发灌浆料，至孔隙率为98％-100％，再进行养护。
石英砂为粒径1-2mm的石英砂和粒径为2-2.5mm的石英砂，二者的重量比例为1：5：4。
按重量份计，所述的生石灰60份、氯化钙40份、高炉矿渣200份、钠基膨润土30份、碳酸镁30份、柠檬酸20份、二氧化铌20份、氢氧化钠60份、硫化钠30份、二氧化硅40份、乙基纤维素60份和壳聚糖40份。
实施例4
利用碱激发材料快速修复裂缝的方法，包括以下步骤：将生石灰、氯化钙、高炉矿渣、钠基膨润土、碳酸镁、柠檬酸、二氧化铌、氢氧化钠、硫化钠、二氧化硅混合后，加入乙基纤维素和壳聚糖，混合得到碱激发灌浆料；将沥青加热至150-165℃，加入石膏粉，然后加入碎石、石英砂，铺筑，铺筑厚度为4mm，铺筑的孔隙率为30％-32％；加入所述的碱激发灌浆料，至孔隙率为98％-100％，再进行养护。
石英砂为粒径1-2mm的石英砂和粒径为2-2.5mm的石英砂，二者的重量比例为1：4：4。
按重量份计，所述的生石灰47份、氯化钙38份、高炉矿渣180份、钠基膨润土28份、碳酸镁28份、柠檬酸13份、二氧化铌13份、氢氧化钠27份、硫化钠17份、二氧化硅27份、乙基纤维素37份和壳聚糖37份。
对照例1
与实施例1的区别在于：不加乙基纤维素和壳聚糖。
性能测试：
以上所述，仅为本发明较佳的具体实施方案，本发明的保护范围不限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，可显而易见地得到的技术方案的简单变化或等效替换均落入本发明的保护范围内。
Claims (8)
1.利用碱激发材料快速修复裂缝的方法，其特征在于，包括以下步骤：将生石灰、氯化钙、高炉矿渣、钠基膨润土、碳酸镁、柠檬酸、二氧化铌、氢氧化钠、硫化钠、二氧化硅混合后，加入乙基纤维素和壳聚糖，混合得到碱激发灌浆料；将沥青加热至150-165℃，加入石膏粉，然后加入碎石、石英砂，铺筑；加入所述的碱激发灌浆料，至孔隙率为98％-100％，再进行养护。
2.根据权利要求1所述的利用碱激发材料快速修复裂缝的方法，其特征在于，按重量份计，所述的生石灰40-60份、氯化钙30-40份、高炉矿渣100-200份、钠基膨润土20-30份、碳酸镁20-30份、柠檬酸10-20份、二氧化铌10-20份、氢氧化钠20-60份、硫化钠10-30份、二氧化硅20-40份、乙基纤维素30-60份和壳聚糖30-40份。
3.根据权利要求3所述的利用碱激发材料快速修复裂缝的方法，其特征在于，按重量份计，所述的生石灰50份、氯化钙35份、高炉矿渣150份、钠基膨润土25份、碳酸镁25份、柠檬酸15份、二氧化铌15份、氢氧化钠40份、硫化钠20份、二氧化硅30份、乙基纤维素40份和壳聚糖35份。
4.根据权利要求3所述的利用碱激发材料快速修复裂缝的方法，其特征在于，按重量份计，所述的生石灰40份、氯化钙30份、高炉矿渣100份、钠基膨润土20份、碳酸镁20份、柠檬酸10份、二氧化铌10份、氢氧化钠20份、硫化钠10份、二氧化硅20份、乙基纤维素30份和壳聚糖30份。
5.根据权利要求3所述的利用碱激发材料快速修复裂缝的方法，其特征在于，按重量份计，所述的生石灰60份、氯化钙40份、高炉矿渣200份、钠基膨润土30份、碳酸镁30份、柠檬酸20份、二氧化铌20份、氢氧化钠60份、硫化钠30份、二氧化硅40份、乙基纤维素60份和壳聚糖40份。
6.根据权利要求3所述的利用碱激发材料快速修复裂缝的方法，其特征在于，按重量份计，所述的生石灰47份、氯化钙38份、高炉矿渣180份、钠基膨润土28份、碳酸镁28份、柠檬酸13份、二氧化铌13份、氢氧化钠27份、硫化钠17份、二氧化硅27份、乙基纤维素37份和壳聚糖37份。
7.根据权利要求1所述的利用碱激发材料快速修复裂缝的方法，其特征在于，石英砂为粒径1-2mm的石英砂和粒径为2-2.5mm的石英砂，二者的重量比例为1：5-1：4。
8.根据权利要求1所述的利用碱激发材料快速修复裂缝的方法，其特征在于，铺筑厚度为3-4mm，铺筑的孔隙率为30％-32％。