CN112826807A - Soft capsule shell, soft capsule prepared from soft capsule shell and preparation method of soft capsule - Google Patents
Soft capsule shell, soft capsule prepared from soft capsule shell and preparation method of soft capsule Download PDFInfo
- Publication number
- CN112826807A CN112826807A CN202110129656.3A CN202110129656A CN112826807A CN 112826807 A CN112826807 A CN 112826807A CN 202110129656 A CN202110129656 A CN 202110129656A CN 112826807 A CN112826807 A CN 112826807A
- Authority
- CN
- China
- Prior art keywords
- soft capsule
- capsule shell
- gelatin
- soft
- glycerol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the field of soft capsule shell preparation, in particular to a soft capsule shell, a soft capsule prepared from the soft capsule shell and a preparation method of the soft capsule shell. The soft capsule shell provided by the invention comprises the following raw materials: the water quality control method comprises the following steps of (1) purifying water, glycerol, an additive and gelatin, wherein the mass ratio of the purifying water to the glycerol to the additive to the gelatin is 1: (0.4-0.6): (0.0001-0.021): 1; wherein the additive is inorganic salt and/or chitosan. The capsule shell of the soft capsule provided by the invention can effectively enhance the mechanical strength of the capsule shell, reduce the oxygen transmission rate of the capsule shell and slow down the oxidation of the content of the capsule.
Description
Technical Field
The invention relates to the field of soft capsule shell preparation, in particular to a soft capsule shell, a soft capsule prepared from the soft capsule shell and a preparation method of the soft capsule shell.
Background
With the development of pharmaceutical industry, soft capsules have been developed rapidly due to the characteristics of almost any medicine, no peculiar smell, easy swallowing, easy digestion and absorption, no side effect on the body, etc., and are widely used in the fields of food, medicine and health care products. The soft capsule consists of a capsule shell and a capsule shell content, has the characteristics of high bioavailability, sealing safety, accurate dosage, attractive appearance and the like, and is widely applied to the research of traditional Chinese medicines.
The capsule shell of the existing soft capsule mainly comprises gelatin, glycerol and water in a certain proportion, and the conventional formula is gelatin: glycerol: 1 part of water: (0.4-0.6): 1. however, the existing soft capsule taking gelatin as the main component of the capsule shell has poor oxygen isolation rate of the capsule shell, oxygen easily enters the capsule to oxidize the content of the capsule, thereby limiting the wide use of the soft capsule taking gelatin as the main component of the capsule shell, and meanwhile, the capsule shell taking gelatin as the main component has poor mechanical property; therefore, the development of a soft capsule shell with good oxygen insulation rate and mechanical property is urgently needed.
Disclosure of Invention
The invention aims to overcome the defects of poor oxygen insulation effect and poor mechanical property of a capsule shell taking gelatin as a main component in the prior art, and further provides a soft capsule shell, a soft capsule prepared from the soft capsule shell and a preparation method of the soft capsule shell.
In order to achieve the purpose, the invention adopts the following technical scheme:
a soft capsule shell comprises the following raw materials: the water quality control method comprises the following steps of (1) purifying water, glycerol, an additive and gelatin, wherein the mass ratio of the purifying water to the glycerol to the additive to the gelatin is 1: (0.4-0.6): (0.0001-0.021): 1; wherein the additive is inorganic salt and/or chitosan.
Preferably, the soft capsule shell comprises the following raw materials: the water quality control method comprises the following steps of (1) purifying water, glycerol, inorganic salt and gelatin, wherein the mass ratio of the purified water to the glycerol to the inorganic salt to the gelatin is 1: (0.4-0.6): (0.0001-0.0002): 1.
preferably, the soft capsule shell comprises the following raw materials: the water quality control agent comprises purified water, glycerol, chitosan and gelatin, wherein the mass ratio of the purified water to the glycerol to the chitosan to the gelatin is 1: (0.4-0.6): (0.01-0.02): 1.
preferably, the soft capsule shell comprises the following raw materials: the water quality control method comprises the following steps of (1) purifying water, glycerol, inorganic salt, chitosan and gelatin, wherein the mass ratio of the purified water to the glycerol to the inorganic salt to the chitosan to the gelatin is 1: (0.4-0.6): (0.0001-0.0002): (0.01-0.02): 1.
preferably, the inorganic salt is calcium chloride and/or sodium lauryl sulfate.
The invention also provides a preparation method of the soft capsule shell, which comprises the following steps:
1) mixing purified water, glycerol, additive and gelatin, and heating the mixture to obtain a glue solution;
2) pressing the glue solution into a glue piece, and performing injection molding on the glue piece to obtain the soft capsule shell.
Preferably, the heating temperature is 70-80 ℃, and the heat preservation time is 20-40min at 70-80 ℃.
Preferably, the step 1) further comprises the steps of degassing and sieving the obtained glue solution, and storing the sieved glue solution at 55-65 ℃ for later use.
Preferably, the obtained glue solution is vacuumized for three times under the vacuum degree of-0.08 MPa-0 MPa, each time for 10-15min for degassing, and the degassed glue solution is sieved by a 110-fold 130-mesh sieve.
The invention also provides a soft capsule which is composed of the capsule shell or the capsule shell prepared by the method and capsule contents.
The invention also provides a preparation method of the soft capsule, which comprises the following steps:
1) mixing purified water, glycerol, additive and gelatin, and heating the mixture to obtain a glue solution;
2) pressing the glue solution into a glue piece, injection-molding the glue piece, adding the capsule content, and sealing the opening to obtain a capsule;
3) and (4) shaping and drying the soft capsules, washing and drying again to obtain the soft capsules.
The present invention is not particularly limited in kind of capsule contents, and any capsule contents that can be conventionally used as soft capsules can be used as the capsule contents of the present invention.
Preferably, the setting and drying temperature in the step 3) is 18-20 ℃, and the setting and drying time is 1-2 h;
the solvent used in the washing step is edible alcohol;
the secondary drying temperature is 20-30 ℃, the relative humidity is 10-50%, and the drying time is 40-50 h.
The invention has the beneficial effects that:
1. the soft capsule shell comprises the following raw materials: the water quality control method comprises the following steps of (1) purifying water, glycerol, an additive and gelatin, wherein the mass ratio of the purifying water to the glycerol to the additive to the gelatin is 1: (0.4-0.6): (0.0001-0.021): 1; wherein the additive is inorganic salt and/or chitosan.
According to the invention, inorganic salt and/or chitosan with a specific proportion are added into ingredients taking gelatin as a main component, the inorganic salt can adjust the ion concentration and the storage modulus of the gelatin solution, increase the intermolecular electrostatic force, establish a salt bridge, strengthen the structural stability, and the chitosan can enhance the plasticity of the gelatin solution, crosslink amino acid residues in the gelatin and reduce the self-crosslinking degree of the gelatin.
2. The soft capsule shell provided by the invention comprises the following raw materials: the water quality control method comprises the following steps of (1) purifying water, glycerol, inorganic salt, chitosan and gelatin, wherein the mass ratio of the purified water to the glycerol to the inorganic salt to the chitosan to the gelatin is 1: (0.4-0.6): (0.0001-0.0002): (0.01-0.02): 1; the inorganic salt and the chitosan with the specific proportion are matched with other components, so that the tensile strength of the capsule shell can be further enhanced, and the oxygen transmission rate of the capsule shell can be reduced.
3. Further, the inorganic salt is calcium chloride and/or sodium dodecyl sulfate. The specific inorganic salt is matched with other components, so that the tensile strength of the capsule shell can be further enhanced, and the oxygen transmission rate of the capsule shell can be further reduced.
Detailed Description
The following examples are provided to further understand the present invention, not to limit the scope of the present invention, but to provide the best mode, not to limit the content and the protection scope of the present invention, and any product similar or similar to the present invention, which is obtained by combining the present invention with other prior art features, falls within the protection scope of the present invention.
The examples do not show the specific experimental steps or conditions, and can be performed according to the conventional experimental steps described in the literature in the field. The reagents or instruments used are not indicated by manufacturers, and are all conventional reagent products which can be obtained commercially.
Example 1
The embodiment provides a soft capsule, which comprises a capsule shell, wherein the capsule shell comprises the following raw materials: 100g of purified water, 40g of glycerol, 2g of chitosan and 100g of gelatin;
the preparation method of the soft capsule comprises the following steps:
1) sequentially putting purified water, glycerol, chitosan and gelatin into a gelatin melting tank, stirring, mixing, heating the mixture to 70 ℃, and preserving heat at 70 ℃ for 30min to completely melt the gelatin to obtain a gelatin solution;
2) vacuumizing the obtained glue solution for three times under the vacuum degree of-0.08 MPa, degassing for 10min each time, removing bubbles in the glue solution, sieving the degassed glue solution with a 120-mesh sieve, and storing the sieved glue solution at 60 ℃ for later use;
3) pressing the glue solution obtained in the step 2) into a glue film with the thickness of 0.8mm by a glue spreading wheel, performing injection molding on the glue film to obtain a soft capsule shell, sealing the lower end of the soft capsule shell, rapidly adding propolis solution (capsule content), and rapidly sealing the opening of the soft capsule shell to form a closed soft capsule;
4) shaping the capsule by a rolling cage type drying machine matched with a soft capsule machine, wherein the shaping and drying temperature is 20 ℃, the shaping and drying time is 1h, and the shaped and dried capsule is uniformly placed in a drying disc and temporarily stored in a pre-drying room;
5) washing the shaped and dried soft capsules with 95% edible alcohol by mass fraction, and drying the soft capsules after the washing is finished, wherein the drying temperature is 30 ℃, the relative humidity is 30%, and the drying time is 40h, so as to obtain the soft capsules.
Example 2
The embodiment provides a soft capsule, which comprises a capsule shell, wherein the capsule shell comprises the following raw materials: 100g of purified water, 40g of glycerol, 0.02g of calcium chloride and 100g of gelatin;
the preparation method of the soft capsule comprises the following steps:
1) sequentially adding purified water, glycerol, calcium chloride and gelatin into a gelatin melting tank, stirring, mixing, heating the mixture to 70 ℃, and keeping the temperature at 70 ℃ for 30min to completely melt the gelatin to obtain a gelatin solution;
2) vacuumizing the obtained glue solution for three times under the vacuum degree of-0.08 MPa, degassing for 10min each time, removing bubbles in the glue solution, sieving the degassed glue solution with a 120-mesh sieve, and storing the sieved glue solution at 60 ℃ for later use;
3) pressing the glue solution obtained in the step 2) into a glue film with the thickness of 0.8mm by a glue spreading wheel, performing injection molding on the glue film to obtain a soft capsule shell, sealing the lower end of the soft capsule shell, rapidly adding propolis solution (capsule content), and rapidly sealing the opening of the soft capsule shell to form a closed soft capsule;
4) shaping the capsule by a rolling cage type drying machine matched with a soft capsule machine, wherein the shaping and drying temperature is 20 ℃, the shaping and drying time is 1h, and the shaped and dried capsule is uniformly placed in a drying disc and temporarily stored in a pre-drying room;
5) washing the shaped and dried soft capsules with 95% edible alcohol by mass fraction, and drying the soft capsules after the washing is finished, wherein the drying temperature is 30 ℃, the relative humidity is 30%, and the drying time is 40h, so as to obtain the soft capsules.
Example 3
The embodiment provides a soft capsule, which comprises a capsule shell, wherein the capsule shell comprises the following raw materials: 100g of purified water, 40g of glycerol, 0.02g of calcium chloride, 1.98g of chitosan and 100g of gelatin;
the preparation method of the soft capsule comprises the following steps:
1) sequentially adding purified water, glycerol, calcium chloride, chitosan and gelatin into a gelatin melting tank, stirring, mixing, heating the mixture to 70 ℃, and preserving heat at 70 ℃ for 30min to completely melt the gelatin to obtain a gelatin solution;
2) vacuumizing the obtained glue solution for three times under the vacuum degree of-0.08 MPa, degassing for 10min each time, removing bubbles in the glue solution, sieving the degassed glue solution with a 120-mesh sieve, and storing the sieved glue solution at 60 ℃ for later use;
3) pressing the glue solution obtained in the step 2) into a glue film with the thickness of 0.8mm by a glue spreading wheel, performing injection molding on the glue film to obtain a soft capsule shell, sealing the lower end of the soft capsule shell, rapidly adding propolis solution (capsule content), and rapidly sealing the opening of the soft capsule shell to form a closed soft capsule;
4) shaping the capsule by a rolling cage type drying machine matched with a soft capsule machine, wherein the shaping and drying temperature is 20 ℃, the shaping and drying time is 1h, and the shaped and dried capsule is uniformly placed in a drying disc and temporarily stored in a pre-drying room;
5) washing the shaped and dried soft capsules with 95% edible alcohol by mass fraction, and drying the soft capsules after the washing is finished, wherein the drying temperature is 30 ℃, the relative humidity is 30%, and the drying time is 40h, so as to obtain the soft capsules.
Example 4
The embodiment provides a soft capsule, which comprises a capsule shell, wherein the capsule shell comprises the following raw materials: 100g of purified water, 40g of glycerol, 2g of calcium chloride and 100g of gelatin;
the preparation method of the soft capsule comprises the following steps:
1) sequentially adding purified water, glycerol, calcium chloride and gelatin into a gelatin melting tank, stirring, mixing, heating the mixture to 70 ℃, and keeping the temperature at 70 ℃ for 30min to completely melt the gelatin to obtain a gelatin solution;
2) vacuumizing the obtained glue solution for three times under the vacuum degree of-0.08 MPa, degassing for 10min each time, removing bubbles in the glue solution, sieving the degassed glue solution with a 120-mesh sieve, and storing the sieved glue solution at 60 ℃ for later use;
3) pressing the glue solution obtained in the step 2) into a glue film with the thickness of 0.8mm by a glue spreading wheel, performing injection molding on the glue film to obtain a soft capsule shell, sealing the lower end of the soft capsule shell, rapidly adding propolis solution (capsule content), and rapidly sealing the opening of the soft capsule shell to form a closed soft capsule;
4) shaping the capsule by a rolling cage type drying machine matched with a soft capsule machine, wherein the shaping and drying temperature is 20 ℃, the shaping and drying time is 1h, and the shaped and dried capsule is uniformly placed in a drying disc and temporarily stored in a pre-drying room;
5) washing the shaped and dried soft capsules with 95% edible alcohol by mass fraction, and drying the soft capsules after the washing is finished, wherein the drying temperature is 30 ℃, the relative humidity is 30%, and the drying time is 40h, so as to obtain the soft capsules.
Example 5
The embodiment provides a soft capsule, which comprises a capsule shell, wherein the capsule shell comprises the following raw materials: 100g of purified water, 50g of glycerol, 0.01g of sodium dodecyl sulfate, 1g of chitosan and 100g of gelatin;
the preparation method of the soft capsule comprises the following steps:
1) sequentially adding purified water, glycerol, sodium dodecyl sulfate, chitosan and gelatin into a gelatin melting tank, stirring, mixing, heating the mixture to 80 ℃, and preserving heat at 80 ℃ for 20min to completely melt the gelatin to obtain a gelatin solution;
2) vacuumizing the obtained glue solution for three times under the vacuum degree of-0.08 MPa, degassing for 15min each time, removing bubbles in the glue solution, sieving the degassed glue solution with a 120-mesh sieve, and storing the sieved glue solution at 55 ℃ for later use;
3) pressing the glue solution obtained in the step 2) into a glue film with the thickness of 0.8mm by a glue spreading wheel, performing injection molding on the glue film to obtain a soft capsule shell, sealing the lower end of the soft capsule shell, rapidly adding propolis solution (capsule content), and rapidly sealing the opening of the soft capsule shell to form a closed soft capsule;
4) shaping the soft capsules by a rolling cage type drying machine matched with a soft capsule machine, wherein the shaping and drying temperature is 18 ℃, the shaping and drying time is 2 hours, and the shaped and dried soft capsules are uniformly placed in a drying disc and temporarily stored in a pre-drying room;
5) washing the shaped and dried soft capsules with 95% edible alcohol by mass fraction, and drying the soft capsules after the washing is finished, wherein the drying temperature is 20 ℃, the relative humidity is 20%, and the drying time is 50h, so as to obtain the soft capsules.
Example 6
The embodiment provides a soft capsule, which comprises a capsule shell, wherein the capsule shell comprises the following raw materials: 100g of purified water, 40g of glycerol, 0.02g of sodium dodecyl sulfate, 2g of chitosan and 100g of gelatin;
the preparation method of the soft capsule comprises the following steps:
1) sequentially adding purified water, glycerol, sodium dodecyl sulfate, chitosan and gelatin into a gelatin melting tank, stirring, mixing, heating the mixture to 80 ℃, and preserving heat at 80 ℃ for 20min to completely melt the gelatin to obtain a gelatin solution;
2) vacuumizing the obtained glue solution for three times under the vacuum degree of-0.08 MPa, degassing for 10min each time, removing bubbles in the glue solution, sieving the degassed glue solution with a 120-mesh sieve, and storing the sieved glue solution at 65 ℃ for later use;
3) pressing the glue solution obtained in the step 2) into a glue film with the thickness of 0.8mm by a glue spreading wheel, performing injection molding on the glue film to obtain a soft capsule shell, sealing the lower end of the soft capsule shell, rapidly adding propolis solution (capsule content), and rapidly sealing the opening of the soft capsule shell to form a closed soft capsule;
4) shaping the soft capsules by a rolling cage type drying machine matched with a soft capsule machine, wherein the shaping and drying temperature is 18 ℃, the shaping and drying time is 2 hours, and the shaped and dried soft capsules are uniformly placed in a drying disc and temporarily stored in a pre-drying room;
5) washing the shaped and dried soft capsules with 95% edible alcohol by mass fraction, and drying the soft capsules after the washing is finished, wherein the drying temperature is 30 ℃, the relative humidity is 25%, and the drying time is 50h, so as to obtain the soft capsules.
Comparative example 1
The present comparative example provides a soft capsule comprising a capsule shell comprising the following raw materials: 100g of purified water, 40g of glycerol and 100g of gelatin;
the preparation method of the soft capsule comprises the following steps:
1) sequentially putting purified water, glycerol and gelatin into a gelatin melting tank, stirring, mixing, heating the mixture to 70 ℃, and preserving heat at 70 ℃ for 30min to completely melt the gelatin to obtain a gelatin solution;
2) vacuumizing the obtained glue solution for three times under the vacuum degree of-0.08 MPa, degassing for 10min each time, removing bubbles in the glue solution, sieving the degassed glue solution with a 120-mesh sieve, and storing the sieved glue solution at 60 ℃ for later use;
3) pressing the glue solution obtained in the step 2) into a glue film with the thickness of 0.8mm by a glue spreading wheel, performing injection molding on the glue film to obtain a soft capsule shell, sealing the lower end of the soft capsule shell, rapidly adding propolis solution (capsule content), and rapidly sealing the opening of the soft capsule shell to form a closed soft capsule;
4) shaping the capsule by a rolling cage type drying machine matched with a soft capsule machine, wherein the shaping and drying temperature is 20 ℃, the shaping and drying time is 1h, and the shaped and dried capsule is uniformly placed in a drying disc and temporarily stored in a pre-drying room;
5) washing the shaped and dried soft capsules with 95% edible alcohol by mass fraction, and drying the soft capsules after the washing is finished, wherein the drying temperature is 30 ℃, the relative humidity is 30%, and the drying time is 40h, so as to obtain the soft capsules.
Test example 1
In order to verify the mechanical properties and oxygen transmission rate of the capsule shell structure of the soft capsule of the present invention, the 0.8mm thick films obtained in the above examples 1-6 and step 3) of the comparative example were tested after drying, wherein the oxygen transmission rate was tested according to the GB/T19789-2005 standard; mechanical properties were tested according to GB/T1040.3-2006. The test results are shown in table 1.
TABLE 1 results of mechanical Properties and oxygen Transmission Rate test of Capsule shells films
It should be understood that the above examples are only for clarity of illustration and are not intended to limit the embodiments. Other variations and modifications will be apparent to persons skilled in the art in light of the above description. And are neither required nor exhaustive of all embodiments. And obvious variations or modifications therefrom are within the scope of the invention.
Claims (10)
1. The soft capsule shell is characterized by comprising the following raw materials: the water quality control method comprises the following steps of (1) purifying water, glycerol, an additive and gelatin, wherein the mass ratio of the purifying water to the glycerol to the additive to the gelatin is 1: (0.4-0.6): (0.0001-0.021): 1; wherein the additive is inorganic salt and/or chitosan.
2. The soft capsule shell according to claim 1, comprising the following raw materials: the water quality control method comprises the following steps of (1) purifying water, glycerol, inorganic salt, chitosan and gelatin, wherein the mass ratio of the purified water to the glycerol to the inorganic salt to the chitosan to the gelatin is 1: (0.4-0.6): (0.0001-0.0002): (0.01-0.02): 1.
3. the soft capsule shell according to claim 1 or 2, wherein the inorganic salt is calcium chloride and/or sodium dodecyl sulfate.
4. A process for the preparation of the soft capsule shell according to any one of claims 1 to 3, comprising the steps of:
1) mixing purified water, glycerol, additive and gelatin, and heating the mixture to obtain a glue solution;
2) pressing the glue solution into a glue piece, and performing injection molding on the glue piece to obtain the soft capsule shell.
5. The method for preparing a soft capsule shell according to claim 4, wherein the heating temperature is 70-80 ℃ and the holding time at 70-80 ℃ is 20-40 min.
6. The process for preparing a soft capsule shell according to claim 5, wherein the step 1) further comprises degassing and sieving the obtained gum solution.
7. The method for preparing the soft capsule shell according to claim 6, wherein the step 1) further comprises the step of storing the sieved gelatin solution at 55-65 ℃ for later use.
8. A soft capsule, characterized in that it consists of a capsule shell according to any one of claims 1 to 3 or a capsule shell prepared by a process according to any one of claims 4 to 7 and the capsule contents.
9. A process for the preparation of the soft capsules according to claim 8, comprising the steps of:
1) mixing purified water, glycerol, additive and gelatin, and heating the mixture to obtain a glue solution;
2) pressing the glue solution into a glue piece, injection-molding the glue piece, adding the capsule content, and sealing the opening to obtain a capsule;
3) and (4) shaping and drying the soft capsules, washing and drying again to obtain the soft capsules.
10. The method for preparing the soft capsule according to claim 9, wherein the setting and drying temperature in the step 3) is 18 ℃ to 20 ℃, and the setting and drying time is 1 to 2 hours;
the solvent used in the washing step is edible alcohol;
the secondary drying temperature is 20-30 ℃, the relative humidity is 10-50%, and the drying time is 40-50 h.