CN1128193C - Strongly anti-fouling emulsoid paint composition for internal wall and its preparing process - Google Patents
Strongly anti-fouling emulsoid paint composition for internal wall and its preparing process Download PDFInfo
- Publication number
- CN1128193C CN1128193C CN 00136396 CN00136396A CN1128193C CN 1128193 C CN1128193 C CN 1128193C CN 00136396 CN00136396 CN 00136396 CN 00136396 A CN00136396 A CN 00136396A CN 1128193 C CN1128193 C CN 1128193C
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- powder
- glue
- white
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a high-performance antifouling latex toughened paint composition for internal walls. The present invention comprises the following components: 25 to 35 parts by weight of palm oil, 15 to 25 parts by weight of white emulsion, 30 to 45 parts by weight of 107 glue water, 2 to 8 parts by weight of talcum powder, 5 to 16 parts by weight of waterproof powder, 3 to 8 parts by weight of sierozem powder, 3 to 8 parts by weight of light calcium carbonate, 0.6 to 3 parts by weight of fluorescent whitening agent, 3 to 10 parts by weight of sodium benzoate, 8 to 15 parts by weight of sodium carbonate, 0.8 to 3 parts by weight of ethylene glycol, 0.6 to 5 parts by weight of tributyl phosphate and 0.5 to 2 parts by weight of deodorant. The paint has the advantages of high binding strength, acid resistance and alkali resistance, weather resistance and fire resistance, strong antifouling ability, good moisture resistance, good mildew resistance, convenient construction and long service life.
Description
Technical field:
The invention belongs to gluing decorative material, the strongly anti-fouling latex toughened paint composition that especially a kind of interior wall is used.
Background technology:
Existing commercially available toughened paint or enamel paint, moistureproof, anti-effect of going mouldy is undesirable, because the easy flavescence of going mouldy, and do not have anti-pollution function, influenced indoor attractive in appearance and environmental health greatly.
Summary of the invention:
The object of the present invention is to provide a kind of cohesive strength height, acid and alkali-resistance, heatproof, fire prevention, protection against the tide, mildew-resistant, special tool strongly anti-fouling function, the antifouling latex toughened paint of the strong side composition that the interior wall of easy construction is used.
Technical solution of the present invention is such, and the contriver is through the practice test more than 3 years, and finding a kind of is the composition of major ingredient with raw materials such as edible palm oils.It is strong that said composition has antifouling power, moistureproof, anti-going mouldy, and the cohesive strength height, sticking power 100% has reached the purpose of inventing.Composition of the present invention includes plam oil, white glue with vinyl, 107 glue, talcum powder, water-proofing powder, grey calcium powder, light calcium carbonate, white dyes, Sodium Benzoate, yellow soda ash, ethylene glycol, tributyl phosphate, reodorant.
The weight part of above-mentioned various raw materials is: plam oil 25～35, white glue with vinyl 15～25,107 glue 30～45, talcum powder 2～8, water-proofing powder 5～16, grey calcium powder 3～8, light calcium carbonate 3～8, white dyes 0.6～3, Sodium Benzoate 3～10, yellow soda ash 8～15, ethylene glycol 0.8～3, tributyl phosphate 0.6～5, reodorant 0.5～2.
The performance and the feature of above-mentioned various raw materials are as follows:
Plam oil: little yellow liquid, extremely lubricated, molecular dispersion is rapid, and suspending power is strong, can resist any pollution after entering composition.
White glue with vinyl: white is gluey, and caking ability is extremely strong, strong adhesion, and fast drying, film-forming properties is good.
107 glue: little yellow gluey, caking ability is strong, and strong adhesion forms the transparency and films soon.
Talcum powder: white powder, smooth interaction is extremely strong.
Water-proofing powder: white powder is moistureproof, mildew-resistant is extremely strong.
The ash calcium powder: white powder, soft, it is strong and fast to gain in strength.
Light calcium carbonate: white powder, soft delicate lightweight is as filling floating metope.
White dyes: micro-yellow powder, it is splendid to increase the whiteness performance.
Sodium Benzoate: white particle or crystallization shape powder, tool preservative activity.
Yellow soda ash: white powder, have good dispersiveness, can make dispersion keep satisfactory stability.
Ethylene glycol: colourless liquid, suspending power is strong, and is dispersed strong, makes the composition surface smooth as porcelain.
Tributyl phosphate: colourless liquid, have extremely strong dispersiveness, can eliminate all steam bubbles in the composition.
Reodorant: colourless liquid, deodorizing power is extremely strong, can eliminate peculiar smell in the composition.
Above-mentioned various raw material chemical industry shop is all on sale.
Making method of the present invention is; Various raw materials are weighed up by weight, 2～8 parts of talcum powder, 5～16 parts of water-proofing powder, 3～8 parts of grey calcium powders, 3～8 parts of light calcium carbonates, 0.6～3 part of white dyes, 3～10 parts of Sodium Benzoates, 8～15 parts of dry mixing of yellow soda ash are even, become the mixed powder of 37 μ m (400 order) later behind riddler with the dry grinder mill.Mix interior the stirring more than 40 minutes of mixed powder of (400 order) with 30～45 parts in 107 glue, then 25～35 parts of plam oils, 15～25 parts of white glue with vinyl, 0.8～3 part of ethylene glycol, 0.6～5 part of tributyl phosphate, 0.5～2 part of adding of reodorant are continued to stir 60～80 minutes one-tenth glue-like again, carry out packaging final prod then.
Composition of the present invention need not to increase any material when using, and as need color person, can add various pigment.
Compare with the state of the art, the advantage of interior wall strongly anti-fouling latex toughened paint of the present invention is the cohesive strength height, the effect of anti-bronsted lowry acids and bases bronsted lowry, and heatproof and fire prevention, and have very strong antifouling, moistureproof, mildew-resistant ability, easy construction, long service life.
Embodiment:
Enumerate embodiment below and application examples is explained the present invention.
Embodiment 1
Various raw materials are all buied from the industrial chemicals shop.White glue with vinyl wherein is the product that the Zhujiang River one river chemical industry company limited in Guangzhou produces, and water-proofing powder is the product that Xia Kou chemical plant, Fucheng, Hebei produces, and other raw material all is common products commonly used, so must not indicate producer.
Take by weighing talcum powder 50g, water-proofing powder 110g, grey calcium powder 50g, light calcium carbonate 50g, white dyes 20g, Sodium Benzoate 60g, yellow soda ash 120g by weight, being crushed to ball mill all is the sieve of 37 μ m (400 order) by the aperture, obtains the 460g mixed powder.To 107 glue that wherein add 138g (the 30 weight % that are equivalent to mixture), this mixture was stirred 50 minutes with agitator.And then to wherein adding plam oil 300g, white glue with vinyl 200g, ethylene glycol 20g, tributyl phosphate 30g and reodorant 10g, continue again to stir promptly to obtain interior wall strongly anti-fouling latex toughened paint 1158g of the present invention in 60 minutes, can directly provide use or canning sealing stand-by.
Application examples 1
Get the interior wall strongly anti-fouling latex toughened paint that makes among the embodiment 1 with the hairbrush brush on indoor cement sidewalls, spend a week after, can rub with hand and to have felt complete drying, and at the indoor smell that can't smell 107 glue fully.The greasy dirt of a small amount of smoke exhaust ventilator is applied on the surface of dry paint and pollutes to form, at this moment use the wiping gently of clean wet towel, greasy dirt is promptly removed fully, leaves no trace.Then after spending for three weeks, test is smeared prepared Chinese ink, ink, iron rust, oil smoke etc. respectively and is polluted to make on the dry paint surface, use the wet towel wiping for several times then, and various pollutions are all removed fully, do not stay any vestige.Pollution one water washing test through hundreds of times shows that coating of the present invention can stand pollution and the cleaning more than 500 times, and the metope after cleaning keeps primary colors basically.
Claims (3)
1, the strongly anti-fouling latex toughened paint composition that a kind of interior wall is used, include plam oil, white glue with vinyl, 107 glue, talcum powder, water-proofing powder, the ash calcium powder, light calcium carbonate, white dyes, Sodium Benzoate, yellow soda ash, ethylene glycol, tributyl phosphate, reodorant is characterized in that the weight part of various raw materials is: plam oil 25～35, white glue with vinyl 15～25,107 glue 30～45, talcum powder 2～8, water-proofing powder 5～16, ash calcium powder 3～8, light calcium carbonate 3～8, white dyes 0.6～3, Sodium Benzoate 3～10, yellow soda ash 8～15, ethylene glycol 0.8～3, tributyl phosphate 0.6～5, reodorant 0.5～2.
2, the strongly anti-fouling latex toughened paint composition of using according to the described interior wall of claim 1 is characterized in that the weight part of various raw materials is: plam oil 30, white glue with vinyl 20,107 glue 13.8, talcum powder 5, water-proofing powder 11, grey calcium powder 5, light calcium carbonate 5, white dyes 2, Sodium Benzoate 6, yellow soda ash 12, ethylene glycol 2, tributyl phosphate 3, reodorant 1.
3, the method for making of the strongly anti-fouling latex toughened paint composition that interior wall is used, it is characterized in that various raw materials are weighed up by weight, 2～8 parts of talcum powder, 5～16 parts of water-proofing powder, 3～8 parts of ash calcium powders, 3～8 parts of light calcium carbonates, 0.6～3 part of white dyes, 3～10 parts of Sodium Benzoates, 8～15 parts of dry mixing of yellow soda ash are even, behind riddler, become later the mixed powder of 37 μ m with the dry grinder mill, mixing with 30～45 parts in 107 glue in the mixed powder of 37 μ m stirs more than 40 minutes, then 25～35 parts of plam oils, 15～25 parts of white glue with vinyl, 0.8～3 part of ethylene glycol, 0.6～5 part of tributyl phosphate, 0.5～2 part of adding of reodorant continues to stir again packed in 60～80 minutes then.