CN112808272A - Nano composite substrate with SERS activity and degradation performance and preparation method thereof - Google Patents
Nano composite substrate with SERS activity and degradation performance and preparation method thereof Download PDFInfo
- Publication number
- CN112808272A CN112808272A CN202011536464.6A CN202011536464A CN112808272A CN 112808272 A CN112808272 A CN 112808272A CN 202011536464 A CN202011536464 A CN 202011536464A CN 112808272 A CN112808272 A CN 112808272A
- Authority
- CN
- China
- Prior art keywords
- mgo
- gold nanoparticles
- washing
- solution
- suspension
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A method of preparing a nanocomposite substrate having SERS activity and degradation properties, comprising: mixing MgCl2Dissolving ultrapure water to form a solution a; adding ammonia water and absolute ethyl alcohol into the solution a under the condition of continuous stirring to form solution b, filtering the solution b, washing and separating out Mg (OH)2And (4) precipitating. The precipitate is calcined at high temperature for a period of time to yield MgO. Subsequently dispersing it in H2O2Forming a suspension c, removing the solid from the suspensionIs separated out to obtain the product MgO2. Adding MgO2Ultrasonically mixing with polyetherimide to obtain suspension d, centrifuging and washing for several times, adding gold nanoparticles into the resuspended d, ultrasonically treating, washing, and resuspending to form gold nanoparticles and MgO2The complex of (a); soaking carbon nanotube sponge in the gold nanoparticles and MgO2In the composite of (1), a nanocomposite substrate is formed. The process of the invention is carried out with MgCl2Synthesis of MgO for precursors2And then the nano composite substrate with SERS activity and degradation performance is respectively assembled with the gold nanoparticles and the carbon nanotube sponge.
Description
Technical Field
The invention relates to degradation and SERS activity, in particular to a preparation method of a nano composite substrate with SERS activity and degradation performance.
Background
In a typical Fenton reaction, H2O2Are commonly used as oxidizing agents to degrade organic contaminants. However, liquid hydrogen peroxide is unstable and has high biotoxicity at high concentrations. Therefore, high-purity magnesium peroxide (MgO) is used2) Nanoparticles and their use in place of H2O2Degrading the organic dye. Gold nanoparticles are used as a noble metal, molecules are adsorbed on the surface of the noble metal, and a strong Surface Enhanced Raman Scattering (SERS) signal can be generated under the irradiation of laser, but the prepared nano material is difficult to recycle. In addition, the dispersed catalyst and reinforcing material are difficult to recover, and cause secondary pollution to the environment. The carbon-based material has larger specific surface area and pore structure, so that the carbon-based material can adsorb organic pollutants in a water body, and simultaneously, the material for carrying out catalytic reaction is loaded and recovered.
Disclosure of Invention
The invention aims to provide a preparation method of a nano composite material with SERS activity and degradation performance, which solves the problem of single function of the material and solves the problem of non-recoverable multifunctional nano material through assembling with carbon nanotube sponge.
In order to achieve the above purpose, the technical scheme of the invention is as follows:
a method for preparing a nanocomposite substrate with SERS activity and degradation properties, comprising the steps of:
s1: mixing MgCl2Dissolving in ultrapure water to form a solution a; adding ammonia water and absolute ethyl alcohol into the solution a under the condition of continuous stirring to form solution b, and filtering the solution b by suctionWashing to separate Mg (OH)2Precipitating;
s2: calcining the precipitate at a high temperature for a period of time to obtain MgO;
s3: subsequently dispersing it in H2O2To form a suspension c, and separating the solid from the suspension to obtain MgO as a product2;
S4: adding MgO2Ultrasonically mixing with polyetherimide to obtain suspension d, and centrifuging and washing for several times;
s5: adding gold nanoparticles into the resuspended d, ultrasonically treating for a period of time, centrifugally washing for several times, and forming gold nanoparticles and MgO after resuspension2The complex of (a);
s6: soaking carbon nanotube sponge in gold nanoparticles and MgO2In the composite of (1), a nanocomposite substrate is formed.
Preferably, in step S3, H is2O2The concentration of (2) is 30%.
Preferably, the step S4 includes: adding MgO2Ultrasonically mixing with polyetherimide to obtain suspension d, and centrifuging and washing for several times; the concentration of polyetherimide is 0.01%, ultrasonic treatment is carried out at normal temperature for 2h, and the centrifugal washing times with ultrapure water are 6 times.
Preferably, the step S5 includes: adding gold nanoparticles into the resuspended d, performing ultrasonic treatment at normal temperature for 2h, centrifuging and washing with ultrapure water for 4 times, and forming gold nanoparticles and MgO after resuspension2The complex of (1).
Preferably, the step S6 includes: acidifying carbon nano-sponge, and soaking the carbon nano-sponge in gold nanoparticles and MgO2In the composite of (1), a nanocomposite substrate is formed.
The invention also provides the nano composite substrate with SERS activity and degradation performance prepared by the method.
Compared with the prior art, the invention has the beneficial effects that:
the method of the present invention is MgO2And gold nano particles are self-assembled through static electricity. Using MgO2The degradation performance of the gold nanoparticles and the surface plasma resonance effect of the gold nanoparticles are combined to realize the multifunctional property of the material;
the method of the invention utilizes the strong adsorption performance of the carbon material to adsorb and enrich the organic pollutants, and then loads the composite material, thereby improving the problem that the dispersed catalyst is difficult to recover.
Drawings
FIG. 1(a) MgO2X-ray powder diffractogram (XRD); (b) MgO (magnesium oxide)2X-ray powder diffractogram (XRD) of @ Au;
FIG. 2(a) MgO2Scanning Electron Micrographs (SEM); (b) MgO (magnesium oxide)2Scanning Electron Microscopy (SEM) of @ Au; (c) MgO (magnesium oxide)2The ultraviolet picture of @ Au degradation of organic pollutants; (d) MgO (magnesium oxide)2@ Au assay 10-4A SERS spectrum of the M organic contaminant;
FIG. 3(a) MgO Supported sponge2Scanning Electron Microscopy (SEM) of @ Au; (b) sponge-loaded MgO2And SERS spectra before and after the @ Au composite material degrades organic pollutants.
The specific implementation mode is as follows:
the technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Examples
1、MgO2The synthesis method of @ Au comprises the following steps:
mixing MgCl2Dissolving ultrapure water to form a solution a; adding ammonia water and absolute ethyl alcohol into the solution a under the condition of continuous stirring to form solution b, filtering the solution b, washing and separating out Mg (OH)2And (4) precipitating. The precipitate is calcined at high temperature for a period of time to yield MgO. Subsequently dispersing it in H2O2To form a suspension c, and separating the solid from the suspension to obtain MgO as a product2. Adding MgO2With polyetherimidesUltrasonic mixing to obtain suspension d, centrifugal washing for several times, adding gold nanoparticles into the resuspended suspension d, ultrasonic treating for a period of time, centrifugal washing for several times, and resuspending to form gold nanoparticles and MgO2The complex of (1). FIG. 1 shows MgO obtained by the above experimental conditions2And MgO2XRD of @ Au. The XRD pattern (1a) shows that the obtained product is MgO with better crystallinity2FIG. 1b shows MgO2The complex with the gold nanoparticles is successfully self-assembled through electrostatic interaction. FIG. 2(a) shows MgO2The Scanning Electron Microscope (SEM) of (b) is MgO2Scanning Electron Microscopy (SEM) of @ Au, in which it can be seen from FIGS. 2(a) and 2(b) that magnesium peroxide has a bulk structure in which nanoparticles having a small particle size are stacked; MgO with very small particle size is adhered to the surface of gold nano-particles with the particle size of about 70nm2. FIG. 2(c) shows MgO2The @ Au ultraviolet graph degrades organic pollutants, and the result shows that the compound can effectively degrade the organic pollutants. FIG. 2(d) shows MgO2@ Au assay 10-4And the SERS spectrogram of the M organic pollutants can be analyzed to obtain that the compound has SERS activity.
2. MgO loaded carbon nanotube sponge2@Au:
Soaking carbon nanotube sponge in the gold nanoparticles and MgO2Forming a nanocomposite substrate. FIG. 3(a) MgO Supported sponge2Scanning Electron Microscopy (SEM) of @ Au; (b) sponge-loaded MgO2And SERS spectra before and after the @ Au composite material degrades organic pollutants. SEM image shows MgO2The @ Au nanocomposite was successfully attached to the sponge. Fig. 3(b) illustrates that the material is supported on a sponge, which does not affect the performance of the material, and the sponge can perform a good collection function for the dispersed catalyst.
Claims (6)
1. A method for preparing a nanocomposite substrate with SERS activity and degradation performance, comprising the following steps:
s1: mixing MgCl2Dissolving in ultrapure water to form a solution a; adding ammonia water and absolute ethyl alcohol into the solution a under the condition of continuous stirring to form solution b, filtering, washing and separating the solution bOut of Mg (OH)2Precipitating;
s2: calcining the precipitate at a high temperature for a period of time to obtain MgO;
s3: subsequently dispersing it in H2O2To form a suspension c, and separating the solid from the suspension to obtain MgO as a product2;
S4: adding MgO2Ultrasonically mixing with polyetherimide to obtain suspension d, and centrifuging and washing for several times;
s5: adding gold nanoparticles into the resuspended d, ultrasonically treating for a period of time, centrifugally washing for several times, and forming gold nanoparticles and MgO after resuspension2The complex of (a);
s6: soaking carbon nanotube sponge in gold nanoparticles and MgO2In the composite of (1), a nanocomposite substrate is formed.
2. The method according to claim 1, wherein in step S3, H2O2The concentration of (2) is 30%.
3. The method for preparing a composite material according to claim 1, wherein the step S4 includes: adding MgO2Ultrasonically mixing with polyetherimide to obtain suspension d, and centrifuging and washing for several times; the concentration of polyetherimide is 0.01%, ultrasonic treatment is carried out at normal temperature for 2h, and the centrifugal washing times with ultrapure water are 6 times.
4. The method for preparing a composite material according to claim 1, wherein the step S5 includes: adding gold nanoparticles into the resuspended d, performing ultrasonic treatment at normal temperature for 2h, centrifuging and washing with ultrapure water for 4 times, and forming gold nanoparticles and MgO after resuspension2The complex of (1).
5. The method for preparing a composite material according to claim 1, wherein the step S6 includes: acidifying carbon nano-sponge, and soaking the carbon nano-sponge in gold nanoparticles and MgO2In the composite of (1), a nanocomposite substrate is formed.
6. A nanocomposite substrate having SERS activity and degradation properties produced by the method of any preceding claim.