CN112716868A - 一种多功能微晶软膜粉及其制备方法 - Google Patents
一种多功能微晶软膜粉及其制备方法 Download PDFInfo
- Publication number
- CN112716868A CN112716868A CN202110247941.5A CN202110247941A CN112716868A CN 112716868 A CN112716868 A CN 112716868A CN 202110247941 A CN202110247941 A CN 202110247941A CN 112716868 A CN112716868 A CN 112716868A
- Authority
- CN
- China
- Prior art keywords
- parts
- multifunctional
- microcrystalline
- soft film
- microcrystalline soft
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本申请涉及面膜领域，具体公开了一种多功能微晶软膜粉及其制备方法。多功能微晶软膜粉包括填充剂30‑50份；透明质酸钠0.05‑0.2份；硅藻土10‑30份；微晶纤维素0.5‑2份；蝶豆花提取物0.2‑1.5份；苹果籽提取物0.1‑1.0份；藻酸钠3‑10份；分散剂15‑30份。其制备方法为：将填充剂、透明质酸钠、硅藻土、微晶纤维素、蝶豆花提取物、藻酸钠加入分散剂中搅拌，搅拌速度80‑150r/min，每隔5‑15min反转一次，搅拌20‑40min，获得多功能微晶软膜粉。本申请多功能微晶软膜粉用于日常护理肌肤，其具有集补水、美白、抗敏、抗衰效果于一体的优点。
Description
技术领域
本申请涉及面膜领域，更具体地说，它涉及一种多功能微晶软膜粉及其制备方法。
背景技术
膜粉一般分软膜粉、硬膜粉和水洗膜粉。软膜粉是指能成膜后可以揭起的膜粉，使用时将软膜粉和水以一定的质量比混合均匀，之后均匀涂抹在面部，15分钟左右揭下即是软膜粉的使用方法。
软膜粉包括成膜剂、填充料、分散剂、补水剂以及其他功效性成分。目前软膜粉的基础功效是清洁、补水，随着人们对护肤产品的要求越来越高，对于面膜产品更是希望集多种功能于一身。因此，根据有效成分的不同，还可以具有美白、淡斑、祛痘等作用。但因为添加不同功能的成分可能会存在效果相互冲突的情况，为了确保软膜粉中成分自身的效果更好，一般加入的功能性成分的种类不能过多。
针对上述相关技术，发明人认为目前的软膜粉由于受限于多种功效成分同时添加时功效可能会相互冲突，因此，市面上具有效果好的多功能的软膜粉并不多，难以满足市场需求，还有改善的空间。
发明内容
为了使得软膜粉同时具有较好的清洁、补水、美白、抗衰以及抗敏的功效，本申请提供一种多功能微晶软膜粉及其制备方法。
第一方面，本申请提供一种多功能微晶软膜粉，采用如下的技术方案：
一种多功能微晶软膜粉，包括以下质量份数的组分：
填充剂30-50份；
透明质酸钠0.05-0.2份；
硅藻土10-30份；
微晶纤维素0.5-2份；
蝶豆花提取物0.2-1.5份；
苹果籽提取物0.1-1.0份；
藻酸钠3-10份；
分散剂15-30份。
优选的，所述多功能微晶软膜粉包括以下质量份数的组分：
填充剂38-42份；
透明质酸钠0.1-0.12份；
硅藻土18-22份；
微晶纤维素1-1.2份；
蝶豆花提取物0.6-0.8份；
苹果籽提取物0.4-0.6份；
藻酸钠5.4-6.4份；
分散剂20-25份。
通过采用上述技术方案，发明人发现将功效组分蝶豆花提取物和藻酸钠同时加入微晶软膜粉中时，使用后补水效果反而小于藻酸钠自身的补水效果，美白、抗衰效果反而小于蝶豆花提取物自身的效果，可见，蝶豆花提取物和藻酸钠在补水、美白、抗衰方面存在相互抑制的问题；另外，发明人意外地发现，加入苹果籽提取物除了可以起到提高抗敏作用之外，与蝶豆花提取物以及藻酸钠以特定比例配合，还可以缓解蝶豆花提取物和藻酸钠在补水、美白、抗衰方面存在相互抑制的情况，从而使得获得的微晶软膜粉具有较好的补水、美白、抗敏、抗衰的功效。
通过加入硅藻土和透明质酸钠，硅藻土具有较好的吸附性，当微晶软膜粉涂抹在面部时，通过硅藻土吸附毛孔中的油脂、灰尘以及面部表面的脏物，吸附完成后，通过透明质酸钠快速补充面部的水分，使得刚被清洁的角质层充满水，使得毛孔周围的细胞变得膨胀，使得毛孔就会变得不明显，从而使得微晶软膜具有较好的洗净清洁、补水的效果。
通过加入微晶纤维素，微晶纤维素与微晶软膜粉中的组分配合，使得微晶软膜粉在遇水搅拌成糊后具有较好的稳定性，同时微晶纤维素与硅藻土配合，通过二者的多孔性使得微晶粉的吸附效果较好，进而使得清洁效果好，使得微晶软膜粉中的有效成分更充分被吸收，从而提高了微晶软膜粉的补水、美白、抗敏以及抗衰的功效。
优选的，所述多功能微晶软膜粉还包括以下质量份数的组分：
硫酸钙4-10份；
焦磷酸四钠0.5-1.5份。
通过采用上述技术方案，由于使用微晶软膜粉时会先加水搅拌成均匀的糊状，硫酸钙吸水后会放热，使得微晶软膜在面部具有一定的温度，使得面部的毛孔微微张开，使得微晶软膜的吸附性更好，使得面部清洁得更干净，使得微晶软膜粉的功效组分更易被皮肤吸收而得到更好的补水、美白、抗衰、抗敏的效果，但因为硫酸钙形成的膜是脆性的，不易整体从面部剥落而造成使用的不便，因此通过与硅藻土、藻酸钠、焦磷酸四钠以特定比例配合，使得微晶软膜粉成膜后可以整体剥落，而且与现有的软膜相比，每次使用10g左右就可以与使用现有软膜30g左右的效果大致相同，使得面部的成膜厚度较小，进而使得面部与外界空气保持较为通畅的呼吸作用，使得面部的毛孔、汗腺排口、皮脂腺排口的通畅程度，进而使得微晶软膜粉的功效更好。
由于硫酸钙、硅藻土、藻酸钠、焦磷酸四钠以特定比例配合，使得微晶软膜粉涂于面部形成一层薄膜，防止水分蒸发，使角质层膨胀，保湿性加强，毛孔、汗腺扩张、皮肤表面湿度升高，改善局部微循环，使面膜内功效组分易于透入皮肤；面膜干燥时收缩，对皮肤保持张力，使其绷紧而消除细小皱纹；在剥离或洗去面膜时，可使皮肤的分泌物、皮屑、污垢等随面膜一起被除去，达到满意的洁肤效果，从而使得微晶软膜粉具有较好的补水、美白、抗衰以及抗敏的多功能效果。
优选的，所述硅藻土的平均粒径为20-50μm。
通过采用上述技术方案，由于人的面部毛孔的直径大约为20-55μm，采用平均粒径为20-50μm的硅藻土，使得微晶纤维粉在面部成膜后，硅藻土得以填充在毛孔中深层吸附清洁皮肤，进而使得清洁效果更好，使得微晶软膜粉中的功效组分更好被皮肤吸收，从而提高了多功能微晶软膜粉的补水、美白、抗衰以及抗敏的功效。
优选的，所述藻酸钠的分子量为8万-15万。
通过采用上述技术方案，由于藻酸钠分子量采用8-15万，使得成膜后的面膜不易因分子量太大而粘结在一起，也不易因分子量小而成膜困难，使得微晶软膜粉的的成膜更薄更通透，从而进一步提高了微晶软膜粉的补水、美白、抗衰以及抗敏的功效。
优选的，所述分散剂是麦芽糊精与硅石以1.3-1.5的质量比复配而成。
通过采用上述技术方案，由于分散剂是麦芽糊精与硅石以1.3-1.5的质量比复配而成，使得微晶面膜粉具有较好溶解性、填充性、稳定性且不易吸潮，能够稳定保护有效活性物质不被氧化、不阻塞毛孔，进而使得微晶软膜粉中的功效组分更好被皮肤吸收，从而进一步提高了多功能微晶软膜粉的补水、美白、抗衰以及抗敏的功效。
优选的，所述透明质酸钠是分子量为50万-80万的中分子透明质酸钠和分子量为0.5-0.8万的小分子透明质酸钠以质量比为1:1-1:4混合而成。
通过采用上述技术方案，由于小分子的透明质酸钠在皮肤表层形成透气膜可渗透到皮肤的真皮层，在皮肤内部发挥作用，锁住水分，促进皮肤代谢，使皮肤湿润光滑、细腻柔嫩、富有弹性，但它防止水分蒸发的能力很差，因此通过与中分子透明质酸钠配合锁住水分，最后微晶软膜粉在面部成膜阻挡水分的流失，从而使得微晶软膜粉的补水效果大大提升，也使得抗衰效果得以提升。
第二方面，本申请提供一种多功能微晶软膜粉的制备方法，采用如下的技术方案：
一种微晶软膜粉的制备方法，将填充剂、透明质酸钠、硅藻土、微晶纤维素、蝶豆花提取物、藻酸钠加入分散剂中搅拌，搅拌速度80-150r/min，每隔5-15min反转一次，搅拌20-40min，获得多功能微晶软膜。
优选的，与所述填充剂一起加入的还有硫酸钙和焦磷酸四钠。
通过采用上述技术方案，采用间隔时间反转搅拌，使得粉末状的组分被搅拌得更均匀，使得微晶软膜粉在面部分布均匀，从而使得微晶软膜粉的功效更好地发挥。
综上所述，本申请具有以下有益效果：
1、本申请由于同时加入苹果籽提取物、蝶豆花提取物以及藻酸钠，三者以特定比例配合，不但使微晶软膜具有较好的抗敏效果，而且缓解了蝶豆花提取物和藻酸钠在补水、美白、抗衰方面存在相互抑制的情况，从而使得获得的微晶软膜具有较好的补水、美白、抗敏、抗衰的功效。
2、本申请中优选采用同时加入硫酸钙、硅藻土、藻酸钠和焦磷酸，四钠四者以特定比例配合，使面膜内功效组分易于透入皮肤，使其绷紧而消除细小皱纹，也具有较好的清洁效果，从而使得微晶软膜粉具有的补水、美白、抗衰以及抗敏性进一步提高。
3、本申请中优先采用小分子的透明质酸钠和中分子透明质酸钠以特定比例配合，渗透真皮层补水，在面部锁水，与微晶软膜粉在面部成膜阻挡水分的流失，从而使得微晶软膜粉的补水效果大大提升。
具体实施方式
以下结合实施例对本申请作进一步详细说明。
实施例的原料来源见表1。
表1
实施例
实施例1-4
实施例1-4公开一种多功能微晶软膜粉，由以下组分制备而成。
填充剂、透明质酸钠、硅藻土、微晶纤维素、蝶豆花提取物、苹果籽提取物、藻酸钠、分散剂。
填充剂为葡萄糖，分散剂为硅石，藻酸钠的分子量为20万-30万，透明质酸钠的分子量为100-120万，硅藻土的平均粒径70μm，具体投入量见表2，单位：Kg。
表2
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | |
| 葡萄糖 | 30 | 38 | 42 | 50 |
| 透明质酸钠 | 0.05 | 0.1 | 0.12 | 0.2 |
| 硅藻土 | 10 | 18 | 22 | 30 |
| 微晶纤维素 | 0.5 | 1 | 1.2 | 2 |
| 蝶豆花提取物 | 0.2 | 0.6 | 0.8 | 1.5 |
| 苹果籽提取物 | 0.1 | 0.4 | 0.6 | 1 |
| 藻酸钠 | 3 | 5.4 | 6.4 | 10 |
| 硅石 | 15 | 20 | 25 | 30 |
实施例1-3的多功能微晶软膜粉的制备方法为：将葡萄糖、透明质酸钠、硅藻土、微晶纤维素、蝶豆花提取物、藻酸钠和硅石一起加入搅拌锅中搅拌，搅拌速度80r/min，每隔5min反转一次，搅拌20min，获得多功能微晶软膜。
实施例4的多功能微晶软膜粉的制备方法为：将葡萄糖、透明质酸钠、硅藻土、微晶纤维素、蝶豆花提取物、藻酸钠和硅石一起加入搅拌锅中搅拌，搅拌速度150r/min，每隔15min反转一次，搅拌40min，获得多功能微晶软膜。
实施例5
与实施例2的区别仅在于：搅拌锅里还加入有4Kg硫酸钙和0.5Kg焦磷酸四钠。
实施例6
与实施例2的区别仅在于：搅拌锅里还加入有10Kg硫酸钙和1.5Kg焦磷酸四钠。
实施例7
与实施例2的区别仅在于：硅藻土的平均粒径为20μm。
实施例8
与实施例2的区别仅在于：硅藻土的平均粒径为50μm。
实施例9
与实施例2的区别仅在于：藻酸钠的分子量为8万-15万。
实施例10
与实施例2的区别仅在于：分散剂是麦芽糊精与硅石以1:1.3的质量比复配而成。
实施例11
与实施例2的区别仅在于：分散剂是麦芽糊精与硅石以1:1.5的质量比复配而成。
实施例12
与实施例2的区别仅在于：透明质酸钠是分子量为50万-80万的中分子透明质酸钠和分子量为0.5-0.8万的小分子透明质酸钠以质量比为1:1混合而成。
实施例13
与实施例2的区别仅在于：透明质酸钠是分子量为50万-80万的中分子透明质酸钠和分子量为0.5-0.8万的小分子透明质酸钠以质量比为1:4混合而成。
实施例14
与实施例2的区别仅在于：
搅拌锅里还加入有4Kg硫酸钙和0.5Kg焦磷酸四钠。
硅藻土的平均粒径为20μm。
藻酸钠的分子量为8万-15万。
分散剂是麦芽糊精与硅石以1.3的质量比复配而成。
透明质酸钠是分子量为50万-80万的中分子透明质酸钠和分子量为0.5-0.8万的小分子透明质酸钠以质量比为1:4混合而成。
对比例
对比例1
与实施例2的区别在于，采用等量葡萄糖代替蝶豆花提取物、苹果籽提取物和藻酸钠。
对比例2
与实施例2的区别在于，采用等量葡萄糖代替苹果籽提取物和藻酸钠。
对比例3
与实施例2的区别在于，采用等量葡萄糖代替蝶豆花提取物和苹果籽提取物。
对比例4
与实施例2的区别在于，采用等量葡萄糖代替蝶豆花提取物和藻酸钠。
对比例5
与实施例2的区别在于，采用等量葡萄糖代替苹果籽提取物。
对比例6
与实施例2的区别在于，采用等量葡萄糖代替藻酸钠。
对比例7
与实施例2的区别在于，采用等量葡萄糖代替蝶豆花提取物。
性能检测试验
试验1
补水效果检测
测试仪器：德国CK公司的MPA10(Multi Probe Adapter)系统，探头为CorneometerCM825水分测试探头。
准备样品：取实施例1-14和对比例1-7制备的多功能微晶软膜粉30g±2g的微晶软膜粉，加入电导率为5US的水120mL搅拌成透明凝胶状，共21组样品，每组样品又分成三等份备用。
测试方法：随机选择健康志愿者63名，年龄在30-50周岁，随机分成21组，每组3名，在恒温环境(20±1℃)，相对湿度50±5％，休息1小时后。按10g±0.5用量将样品均匀涂抹在受试者的面部，20分钟后揭下，用水分测试探头分别测试脸部肌肤的水合状态，共测三次。
测试结果：以水合度表示，详见表3。
试验2
抗敏效果检测
测试仪器：面部图像分析仪VISIA，美国Canfield。
准备样品：取实施例1-14和对比例1-7制备的多功能微晶软膜粉20g±2g的微晶软膜粉，加入电导率为5US的水80mL搅拌成透明凝胶状，共21组样品，每组样品又分成2等份备用。
测试方法：选取敏感性肌肤的受试42名，受试者分为21组，每组为2名受试者，按10g±0.5用量将样品均匀涂抹在受试者的面部，20分钟后揭下，使用8周，每周使用3次。采用面部图像分析仪VISIA拍摄受试者在使用测试样品前和测试样品0周、8周后面部图像并分析得到脸部红色区的分值，红色区的分值表示超过同年龄段、同类型皮肤、同性别的120人的比例，分值越高，说明红斑量超越人数越多，结果用使用0周的分值减去使用8周后的分值的红色区分值差来表示，详见表3。
试验3-4
美白、抗衰效果检测
测试仪器：
美白测试—德国CK公司的MPA10系统，探头为Skin-Glossymeter GL200皮肤光泽度测试探头。
抗衰测试—面部图像分析仪VISIA，美国Canfield。
测试方法：在试验1的受试人员以及涂抹方法的基础上，持续使用8周，每周使用3次，之后分别使用MPA10系统和VISIA仪器测试，美白效果用前后L值的差值表示，L差值越大，说明美白效果越好，抗衰效果用使用前后的wrinkles score的差值表示，wrinklesscore的差值越大，说明抗衰效果越好，检测数据详见表4。
表3
表4
根据表3-4中对比例5与对比例2、对比例3的数据对比可得，对比例5的水合度增加量、L值增加量、wrinkles score差值均小于对比例2、对比例3，说明同时加入蝶豆花提取物和藻酸钠时，蝶豆花提取物抑制了藻酸钠的补水效果，藻酸钠抑制了蝶豆花的美白、抗衰的效果，实施例2与对比例5的数据对比可得，实施例1-4的水合度增加量、L值增加量、wrinkles score差值均远大于对比例5，说明同时加入蝶豆花提取物、藻酸钠和苹果籽提取物并以特定比例配合，苹果籽提取物缓解了蝶豆花提取物和藻酸钠之间的抑制作用，使得微晶软膜粉同时具有较好的补水、美白、抗衰效果，通过实施例1-4与对比例4的数据对比可得，实施例1-4的红色区超越分值略高于对比例4，说明加入苹果籽提取物后使得微晶软膜粉具有较好的抗敏效果，从而使得微晶软膜粉同时具有较好的补水、美白、抗衰、抗敏的效果，成为名副其实的多功能微晶软膜粉。
根据表3-4中实施例1-4的数据相比，实施例2-3的水合度增加量、L值增加量、wrinkles score差值、红色区超越分值均大于实施例1、4，说明当蝶豆花提取物、藻酸钠和苹果籽提取物以实施例2、3的比例配合时，微晶软膜粉的各个功效才得以更好。
根据表3-4中实施例5-6与实施例2的数据相比，实施例5-6的水合度增加量、L值增加量、wrinkles score差值、红色区超越分值均大于实施例2，说明当硫酸钙、硅藻土、藻酸钠、焦磷酸四钠以特定比例配合，使得微晶软膜粉的成膜后可以整体剥落，也使得面部的成膜厚度较小，进而使得面部与外界空气保持较为通畅的呼吸作用，进而使得微晶软膜粉的功效更好。
根据表3-4中实施例7-8与实施例2的数据相比，实施例7-8的水合度增加量、L值增加量、wrinkles score差值、红色区超越分值均大于实施例2，说明采用平均粒径为20-50μm的硅藻土使得面部清洁更彻底，使得微晶软膜粉中的功效组分更好被皮肤吸收，从而提高了多功能微晶软膜粉的补水、美白、抗衰、抗敏的功效。
根据表3-4中实施例9与实施例2的数据相比，实施例9的水合度增加量、L值增加量、wrinkles score差值、红色区超越分值均大于实施例2，说明采用分子量为8万-15万的藻酸钠，使得微晶软膜粉的的成膜更薄更通透，从而进一步提高了微晶软膜粉的功效。
根据表3-4中实施例10-11与实施例2的数据相比，实施例10-11的水合度增加量、L值增加量、wrinkles score差值、红色区超越分值均大于实施例2，说明麦芽糊精与硅石以特定比例配合形成的分散剂，能够稳定保护有效活性物质不被氧化、不阻塞毛孔，进而使得微晶软膜粉中的功效组分更好被皮肤吸收，从而进一步提高了多功能微晶软膜粉的功效。
根据表3-4中实施例12-13与实施例2的数据相比，实施例12-13的水合度增加量、wrinkles score差值均大于实施例2，说明采用小分子的透明质酸钠和中分子透明质酸钠以特定比例配合，使得微晶软膜粉的补水效果大大提升，也使得抗衰效果得以提升。
本具体实施例仅仅是对本申请的解释，其并不是对本申请的限制，本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改，但只要在本申请的权利要求范围内都受到专利法的保护。
Claims (9)
1.一种多功能微晶软膜粉，其特征在于，包括以下质量份数的组分：
填充剂30-50份；
透明质酸钠0.05-0.2份；
硅藻土10-30份；
微晶纤维素0.5-2份；
蝶豆花提取物0.2-1.5份；
苹果籽提取物0.1-1.0份；
藻酸钠3-10份；
分散剂15-30份。
2.根据权利要求1所述的多功能微晶软膜粉，其特征在于：包括以下质量份数的组分：
填充剂38-42份；
透明质酸钠0.1-0.12份；
硅藻土18-22份；
微晶纤维素1-1.2份；
蝶豆花提取物0.6-0.8份；
苹果籽提取物0.4-0.6份；
藻酸钠5.4-6.4份；
分散剂20-25份。
3.根据权利要求1或2所述的多功能微晶软膜粉，其特征在于：所述多功能微晶软膜粉还包括以下质量份数的组分：
硫酸钙4-10份；
焦磷酸四钠0.5-1.5份。
4.根据权利要求1或2所述的多功能微晶软膜粉，其特征在于：所述硅藻土的平均粒径为20-50μm。
5.根据权利要求1或2所述的多功能微晶软膜粉，其特征在于：所述藻酸钠的分子量为8万-15万。
6.根据权利要求1或2所述的多功能微晶软膜粉，其特征在于：所述分散剂是麦芽糊精与硅石以1：1.3-1.5的质量比复配而成。
7.根据权利要求1或2所述的多功能微晶软膜粉，其特征在于：所述透明质酸钠是分子量为50万-80万的中分子透明质酸钠和分子量为0.5-0.8万的小分子透明质酸钠以质量比为1：1-4混合而成。
8.一种如权利要求1或2任一所述多功能微晶软膜粉的制备方法，其特征在于： 将填充剂、透明质酸钠、硅藻土、微晶纤维素、蝶豆花提取物、藻酸钠加入分散剂中搅拌，搅拌速度80-150r/min，每隔5-15min反转一次，搅拌20-40min，获得多功能微晶软膜粉。
9.根据权利要求8所述的多功能微晶软膜粉的制备方法，其特征在于：与所述填充剂一起加入的还有硫酸钙和焦磷酸四钠。