CN112662241A - Colored damp-proof wall ground reinforcing agent and preparation method thereof - Google Patents
Colored damp-proof wall ground reinforcing agent and preparation method thereof Download PDFInfo
- Publication number
- CN112662241A CN112662241A CN202011470922.0A CN202011470922A CN112662241A CN 112662241 A CN112662241 A CN 112662241A CN 202011470922 A CN202011470922 A CN 202011470922A CN 112662241 A CN112662241 A CN 112662241A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- agent
- proof wall
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a color damp-proof wall ground reinforcing agent and a preparation method thereof, belonging to the technical field of adhesion. The color damp-proof wall ground reinforcing agent comprises the following components: water, a bactericide, hydroxyethyl cellulose, colloidal attapulgite, a defoaming agent, a surfactant, a dispersing agent, a pH regulator, an anti-freezing agent, a functional emulsion, a film-forming auxiliary agent, calcium carbonate, a thickening agent and color paste. The color damp-proof wall ground reinforcing agent overcomes the problems of poor water resistance, poor adhesive force, low covering power, poor coloring effect and the like in the prior art, can be firmly attached to the surfaces of base materials such as concrete, cement, calcium silicate boards and the like to compact a base layer, and a frosted coating formed after drying can obviously improve the roughness, improve the adhesive force of putty and a new coating and greatly reduce the probability of hollowing and falling.
Description
Technical Field
The invention belongs to the technical field of adhesion, and particularly relates to a color damp-proof wall ground reinforcing agent and a preparation method thereof.
Background
The wall and ground reinforcing agent is mainly used for fixing sand and ash of a building base course, so that the firmness of base materials such as concrete, cement and ash walls is improved, the adhesive force of a coating and a wall body is enhanced, and the functions of preventing the coating of the inner wall and the outer wall from falling off and hollowing are achieved. The existing wall and ground reinforcing agent is mostly prepared by diluting VAE and white latex and then adding color paste, and has the defects of poor water resistance, poor adhesive force, low covering power, poor coloring effect and the like of a coating, and the coating becomes colloidal after meeting water, so that putty is easy to fade and penetrate, and the decoration appearance is influenced. The existing process is limited to fixing ash and sand, and large-area skinning is easy to occur when the base material is coated too thickly or meets low absorption rate.
Disclosure of Invention
Aiming at the problems in the prior art, the invention provides the color damp-proof wall ground reinforcing agent and the preparation method thereof, the color damp-proof wall ground reinforcing agent is a single-component product, has stable performance and convenient and quick construction, simultaneously has excellent adhesive force of concrete and cement base surfaces, can be firmly attached to the surfaces of base materials such as concrete, cement, calcium silicate boards and the like, can compact the base layer, and can obviously improve the roughness of a frosted coating formed after drying, improve the adhesive force of putty and a new coating, and greatly reduce the probability of hollowing and falling.
In order to achieve the purpose, the invention adopts the following technical scheme: the color damp-proof wall ground reinforcing agent comprises the following components in parts by mass: 400-500 parts of water, 2-5 parts of a bactericide, 2-5 parts of hydroxyethyl cellulose, 2-5 parts of colloidal attapulgite, 2-5 parts of a defoaming agent, 2-5 parts of a surfactant, 2-5 parts of a dispersing agent, 1-3 parts of a pH regulator, 5-10 parts of an antifreeze agent, 100-200 parts of a functional emulsion, 5-10 parts of a film forming additive, 100-200 parts of 400-mesh calcium carbonate, 100-200 parts of 1200-mesh calcium carbonate, 3-5 parts of a thickener and 5-8 parts of a color paste.
Further, the bactericide is Dow LX300, and the hydroxyethyl Cellulose is CelluloseTM893。
Further, the colloid attapulgite is
400, and the defoaming agent is Kalmiter 2290.
Further, the surfactant is ECOSURFTMBD-109, the dispersant being particularly good powderTM1620。
Further, the pH regulator is AMP-95, and the antifreeze agent is propylene glycol.
Further, the functional emulsion is BailemaoTMDC-420, wherein the film-forming additive is alcohol ester twelve.
Further, the thickener is malacisTMDR-50。
Further, the color paste is a world name water-based color paste.
The invention also provides a preparation method of the color damp-proof wall ground reinforcing agent, which comprises the following steps:
(1) weighing 400-500 parts by mass of water, 2-5 parts by mass of a bactericide, 2-5 parts by mass of hydroxyethyl cellulose, 2-5 parts by mass of colloidal attapulgite, 2-5 parts by mass of a defoaming agent, 2-5 parts by mass of a surfactant, 2-5 parts by mass of a dispersing agent, 1-3 parts by mass of a pH regulator, 5-10 parts by mass of an antifreeze agent, 100-200 parts by mass of a functional emulsion, 5-10 parts by mass of a film forming aid, 100-200 parts by mass of 400-mesh calcium carbonate, 100-200 parts by mass of 1200-mesh calcium carbonate, 3-5 parts by mass of a thickener and 5-8 parts by mass of a color paste;
(2) mixing 400-500 parts by mass of water, 2-5 parts by mass of hydroxyethyl cellulose and 2-5 parts by mass of colloidal attapulgite in sequence, and uniformly dispersing;
(3) then sequentially adding 2-5 parts by mass of a bactericide, 1-2 parts by mass of a defoaming agent, 2-5 parts by mass of a surfactant, 2-5 parts by mass of a dispersing agent, 1-3 parts by mass of a pH regulator and 5-10 parts by mass of an antifreeze agent, and after uniformly dispersing, adding 100-200 parts by mass of 400-mesh calcium carbonate and 100-200 parts by mass of 1200-mesh calcium carbonate, and uniformly dispersing;
(4) and then adding the rest defoaming agent, adding 100-200 parts by mass of functional emulsion, 5-10 parts by mass of film forming aid and 3-5 parts by mass of thickening agent after foam is eliminated, adding 5-8 parts by mass of color paste after uniform dispersion, and obtaining the color damp-proof wall ground reinforcing agent after uniform dispersion.
Compared with the prior art, the invention has the beneficial effects that:
(1) adopts hydroxyethyl cellulose and colloidal attapulgite as a thickening agent and a rheological additive in combination with malacisTMThe DR-50 low-shear high-viscosity thickening agent can construct high and stable low-shear viscosity, can effectively prevent the pigments and fillers from settling and layering, and improves the storage stability of the product; colloidal attapulgite and yalkenTMThe DR-50 low-shear high-viscosity thickening agent has good shear thixotropy, can quickly reduce viscosity under the action of medium and high shear force, enables the product to recover fluidity and leveling property, and improves the brushing and application performance.
(2) The calcium carbonate of 400 meshes is matched with the calcium carbonate of 1200 meshes for use, the calcium carbonate of 400 meshes with large particle size forms countless concave-convex structures on the surface of the coating, and the concave-convex structures and the putty powder improve the mechanical adhesion between the coatings in a riveting and embedding mode during the construction of the putty coating; the 1200-mesh small-particle-size calcium carbonate improves the covering property and color-developing property of the coating, and the product has bright color after being coated.
(3) Adopts the Dow calendarTMThe DC-420 rigid styrene-acrylic emulsion with small particle size and low odor has excellent permeability, can seal pores of a base layer, is alkali-resistant and water-resistant after a coating is dried, can reduce outward migration of moisture and alkaline substances, and has a good moisture-proof effect.
The technical scheme of the invention is elaborately designed, and the finally obtained color damp-proof wall ground reinforcing agent has the characteristics of water resistance, alkali resistance, weather resistance, durability, good covering effect, good coloring effect, environmental protection, no pollution, and simple and rapid construction.
Detailed Description
In order to make the purpose and technical solutions of the embodiments of the present invention clearer, the technical solutions of the present invention will be clearly described below with reference to the embodiments, and it is obvious that the described embodiments are some embodiments of the present invention, but not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
The invention provides a preparation method of a color damp-proof wall ground reinforcing agent, which specifically comprises the following steps:
(1) weighing 460 parts by mass of water and 2 parts by mass of CelluloseTM893 hydroxyethyl cellulose, 5 parts by mass
400 parts of colloidal attapulgite, 2 parts of Dow LX300, 2 parts of Karmet 2290 antifoaming agent and 2 parts of ECOSURFTMBD-109 surfactant, 2 parts by mass of TehaosanTM1620 parts of dispersing agent, 1 part by mass of AMP-95pH regulator, 10 parts by mass of propylene glycol, 150 parts by mass of 400-mesh calcium carbonate, 200 parts by mass of 1200-mesh calcium carbonate and 150 parts by mass of BailemoTMDC-420, 7.5 parts by mass of alcohol ester twelve and 4 parts by mass of malacisTMDR-50 and 6 parts of world name water-based color paste.
(2) 460 parts by mass of water and 2 parts by mass of Cellulose are mixed in sequenceTM893 hydroxyethyl cellulose, 5 parts by mass
Putting 400 colloidal attapulgite into a container to be uniformly dispersed;
(3) then, 2 parts by mass of Dow LX300, 1 part by mass of Camite 2290 antifoaming agent and 2 parts by mass of ECOSURF are added in this orderTMBD-109 surfactant, 2 parts by mass of TehaosanTM1620, 1 part by mass of AMP-95pH regulator and 10 parts by mass of propylene glycol, and after uniform dispersion, 150 parts by mass of 400-mesh calcium carbonate and 200 parts by mass of 1200-mesh calcium carbonate are added and uniformly dispersed.
(4) Then adding the rest of the Camite 2290 antifoaming agent, and adding 150 parts by mass of Bailemo after most of foams are eliminatedTMDC-420, adding 7.5 parts by mass of alcohol ester twelve and 4 parts by mass of malacis AsiaTMDR-50, adding 6 after dispersing evenlyAnd (3) uniformly dispersing the world aqueous color paste by mass to obtain the color damp-proof wall ground reinforcing agent.
The color damp-proof wall ground reinforcing agent prepared by the method is used on the surface of a cement test board for detecting the performance of the cement test board, and the test result is shown in table 1.
Example 2
The invention provides a preparation method of a color damp-proof wall ground reinforcing agent, which specifically comprises the following steps:
(1) weighing 500 parts by mass of water and 4 parts by mass of CelluloseTM893 hydroxyethyl cellulose, 2 parts by mass
400 parts of colloid attapulgite, 2 parts of bactericide, 2 parts of Cammite 2290 antifoaming agent and 2 parts of ECOSURFTMBD-109 surfactant, 3 parts by mass of TehaosanTM1620 parts of dispersing agent, 1 part by mass of AMP-95pH regulator, 8 parts by mass of propylene glycol, 200 parts by mass of 400-mesh calcium carbonate, 170 parts by mass of 1200-mesh calcium carbonate and 100 parts by mass of BailemoTMDC-420, 5 parts of alcohol ester twelve, 3 parts of malacis by massTMDR-50 and 5 parts of famous water-based color paste.
(2) 500 parts by mass of water and 4 parts by mass of Cellulose are mixed in sequenceTM893 hydroxyethyl cellulose, 2 parts by mass
Putting 400 colloidal attapulgite into a container to be uniformly dispersed;
(3) then sequentially adding 2 parts by mass of bactericide, 1 part by mass of Camite 2290 antifoaming agent and 2 parts by mass of ECOSURFTMBD-109 surfactant, 3 parts by mass of TehaosanTM1620, 1 part by mass of AMP-95pH regulator and 8 parts by mass of propylene glycol, and after uniform dispersion, 200 parts by mass of 400-mesh calcium carbonate and 170 parts by mass of 1200-mesh calcium carbonate are added and uniformly dispersed.
(4) Then adding the rest of the Camite 2290 antifoaming agent, and adding 100 parts by mass of Lianmo after most of the foam is eliminatedTMDC-420, 5 parts of alcohol ester twelve and 3 parts of malacisTMDR-50, uniformly dispersedThen 5 parts by mass of world water-based color paste is added, and the color damp-proof wall ground reinforcing agent is obtained after uniform dispersion.
The color damp-proof wall ground reinforcing agent prepared by the method is used on the surface of a cement test board for detecting the performance of the cement test board, and the test result is shown in table 1.
Example 3
The invention provides a preparation method of a color damp-proof wall ground reinforcing agent, which specifically comprises the following steps:
(1) weighing 400 parts by mass of water and 5 parts by mass of CelluloseTM893 hydroxyethyl cellulose, 2 parts by mass
400 parts of colloid attapulgite, 5 parts of bactericide, 5 parts of Cammite 2290 antifoaming agent and 5 parts of ECOSURFTMBD-109 surfactant and 5 parts by mass of TehaosanTM1620 parts of dispersing agent, 3 parts of AMP-95pH regulator, 5 parts of propylene glycol, 100 parts of 400-mesh calcium carbonate, 100 parts of 1200-mesh calcium carbonate and 200 parts of calamine molTMDC-420, 10 parts by mass of alcohol ester twelve and 5 parts by mass of malacisTMDR-50 and 8 parts of famous water-based color paste.
(2) 400 parts by mass of water and 5 parts by mass of Cellulose are sequentially addedTM893 hydroxyethyl cellulose, 2 parts by mass
Putting 400 colloidal attapulgite into a container to be uniformly dispersed;
(3) then, 5 parts by mass of bactericide, 2 parts by mass of Camite 2290 antifoaming agent and 5 parts by mass of ECOSURF are sequentially addedTMBD-109 surfactant and 5 parts by mass of TehaosanTM1620, 3 parts of AMP-95pH regulator and 5 parts of propylene glycol, and after the components are uniformly dispersed, 100 parts of 400-mesh calcium carbonate and 100 parts of 1200-mesh calcium carbonate are added and uniformly dispersed.
(4) Then adding the rest of the Karmet 2290 antifoaming agent, and adding 200 parts by mass of Bailemo after most of foams are eliminatedTMDC-420, adding 10 parts by mass of alcohol ester twelve and 5 parts by mass of malacisTMAnd DR-50, adding 8 parts by mass of world water-based color paste after uniform dispersion, and obtaining the color damp-proof wall ground reinforcing agent after uniform dispersion.
The color damp-proof wall ground reinforcing agent prepared by the method is used on the surface of a cement test board for detecting the performance of the cement test board, and the test result is shown in table 1.
Comparative example
After the commercially available common wall surface reinforcing agent is uniformly stirred according to the use specification, the surface of a cement test board is used for detecting the performance of the cement test board, and the test result is shown in table 1.
TABLE 1 concrete interface treating agent Properties of examples 1 to 3 and comparative example
And (4) analyzing results: the color damp-proof wall and floor treating agent prepared by the method of the embodiment 1 to 3 has the characteristics of water resistance, alkali resistance, weather resistance, durability, good covering effect, good coloring effect, environmental protection, no pollution and simple and quick construction, and is characterized in that 400-mesh calcium carbonate hydroxyethyl cellulose and colloid attapulgite are adopted as a thickening agent and a rheological aid and matched with malacisTMThe DR-50 low-shear high-viscosity thickening agent can construct high and stable low-shear viscosity, can effectively prevent the pigments and fillers from settling and layering, and improves the storage stability of the product; colloidal attapulgite and yalkenTMThe DR-50 low-shear high-viscosity thickening agent has good shear thixotropy, can quickly reduce viscosity under the action of medium and high shear force, enables the product to recover fluidity and leveling property, and can obviously improve the brushing and application performance; the calcium carbonate of 400 meshes is matched with the calcium carbonate of 1200 meshes for use, the calcium carbonate of 400 meshes with large particle size forms countless concave-convex structures on the surface of the coating, and the concave-convex structures and the putty powder improve the mechanical adhesion between the coatings in a riveting and embedding mode during the construction of the putty coating; coverage and color development of 1200-mesh small-particle-size calcium carbonate lifting coatingThe product has bright color after being coated; adopts the Dow calendarTMThe DC-420 rigid styrene-acrylic emulsion with small particle size and low odor has excellent permeability, can seal pores of a base layer, is alkali-resistant and water-resistant after a coating is dried, can reduce outward migration of moisture and alkaline substances, and has a good moisture-proof effect. The wall surface reinforcing agent in the comparative example has poor performances such as water resistance, adhesive force, covering power, coloring effect and the like because polyvinyl acetate or VAE emulsion has large molecular particle size and soft chain segment, and the polyvinyl alcohol is used as a protective colloid, so that the film forming hardness is insufficient, the adhesive force is low, the water resistance and alkali resistance are basically absent, and the putty is easy to fade when a coating is changed into a colloid state when meeting water. Therefore, the colorful damp-proof wall ground reinforcing agent has the characteristics of water resistance, alkali resistance, weather resistance, durability, good covering effect, good coloring effect, environmental protection, no pollution, and simple and rapid construction.
It should be noted that the above examples are only for illustrating the technical solutions of the present invention and not for limiting the technical solutions, and it should be understood by those skilled in the art that the present invention is not limited by the above embodiments, and the present invention may have various changes and modifications without departing from the spirit and scope of the invention, and these changes and modifications fall into the scope of the claimed invention.
Claims (9)
1. The color damp-proof wall ground reinforcing agent is characterized by comprising the following components in parts by mass: 400-500 parts of water, 2-5 parts of a bactericide, 2-5 parts of hydroxyethyl cellulose, 2-5 parts of colloidal attapulgite, 2-5 parts of a defoaming agent, 2-5 parts of a surfactant, 2-5 parts of a dispersing agent, 1-3 parts of a pH regulator, 5-10 parts of an antifreeze agent, 100-200 parts of a functional emulsion, 5-10 parts of a film forming additive, 100-200 parts of 400-mesh calcium carbonate, 100-200 parts of 1200-mesh calcium carbonate, 3-5 parts of a thickener and 5-8 parts of a color paste.
2. The color damp-proof wall and floor reinforcing agent according to claim 1, wherein the bactericide is Dow LX300, and the hydroxyethyl Cellulose is CelluloseTM893。
3. The colored moisture barrier wall and floor reinforcement of claim 1, wherein the colloidal attapulgite is attapulgite
400, and the defoaming agent is Kalmiter 2290.
4. The colored moisture barrier wall and floor reinforcement of claim 1, wherein the surfactant is ecosmufTMBD-109, the dispersant being particularly good powderTM1620。
5. The color damp-proof wall and ground reinforcing agent as claimed in claim 1, wherein the pH regulator is AMP-95 and the antifreeze agent is propylene glycol.
6. The colored moisture barrier wall and floor reinforcement of claim 1, wherein the functional emulsion is BailemonTMDC-420, wherein the film-forming additive is alcohol ester twelve.
7. The colored moisture-proof wall and ground reinforcing agent as claimed in claim 1, wherein the thickening agent is malacisTMDR-50。
8. The color damp-proof wall and floor reinforcing agent as defined in claim 1, wherein the color paste is a world-name aqueous color paste.
9. A method for preparing the colored damp-proof wall and ground reinforcing agent according to any one of claims 1 to 8, which comprises the following steps:
(1) weighing 400-500 parts by mass of water, 2-5 parts by mass of a bactericide, 2-5 parts by mass of hydroxyethyl cellulose, 2-5 parts by mass of colloidal attapulgite, 2-5 parts by mass of a defoaming agent, 2-5 parts by mass of a surfactant, 2-5 parts by mass of a dispersing agent, 1-3 parts by mass of a pH regulator, 5-10 parts by mass of an antifreeze agent, 100-200 parts by mass of a functional emulsion, 5-10 parts by mass of a film forming aid, 100-200 parts by mass of 400-mesh calcium carbonate, 100-200 parts by mass of 1200-mesh calcium carbonate, 3-5 parts by mass of a thickener and 5-8 parts by mass of a color paste;
(2) mixing 400-500 parts by mass of water, 2-5 parts by mass of hydroxyethyl cellulose and 2-5 parts by mass of colloidal attapulgite in sequence, and uniformly dispersing;
(3) then sequentially adding 2-5 parts by mass of a bactericide, 1-2 parts by mass of a defoaming agent, 2-5 parts by mass of a surfactant, 2-5 parts by mass of a dispersing agent, 1-3 parts by mass of a pH regulator and 5-10 parts by mass of an antifreeze agent, and after uniformly dispersing, adding 100-200 parts by mass of 400-mesh calcium carbonate and 100-200 parts by mass of 1200-mesh calcium carbonate, and uniformly dispersing;
(4) and then adding the rest defoaming agent, adding 100-200 parts by mass of functional emulsion, 5-10 parts by mass of film forming aid and 3-5 parts by mass of thickening agent after foam is eliminated, adding 5-8 parts by mass of color paste after uniform dispersion, and obtaining the color damp-proof wall ground reinforcing agent after uniform dispersion.