CN112144296A - Anti-wrinkle flame-retardant waterproof multifunctional fabric process - Google Patents
Anti-wrinkle flame-retardant waterproof multifunctional fabric process Download PDFInfo
- Publication number
- CN112144296A CN112144296A CN202011052277.0A CN202011052277A CN112144296A CN 112144296 A CN112144296 A CN 112144296A CN 202011052277 A CN202011052277 A CN 202011052277A CN 112144296 A CN112144296 A CN 112144296A
- Authority
- CN
- China
- Prior art keywords
- product
- flame
- agent
- tank
- shaping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a crease-resistant flame-retardant waterproof multifunctional fabric process which comprises the following steps of a, dyeing gray cloth to obtain a product A, B, shaping the product A, adding a flame retardant with the model of P-207Z during shaping to obtain a product B, washing the product C and the product B with water to obtain a product C, shaping the product d and the product C, adding a waterproof agent with the model of TF5501 during shaping, and obtaining a finished product. The preferred flame retardant and waterproof agent of the invention can lead the fabric to have flame retardant effect and waterproof effect under the matching of specific process steps and process parameters, and the crease resistance is remarkable, and the flame retardant property of the fabric reaches European standard EN 18011611; the waterproof grade can reach 100 cents in American standard; the folded fabric is folded for 3 hours under the pressure of 50 kilograms, the fold recovery angle of the fabric reaches 172 degrees, and the fold resistance is good. The invention has the advantages of flame retardant effect, waterproof effect, strong anti-wrinkle capability and wide application range.
Description
Technical Field
The invention belongs to the field of safety vest fabrics, and particularly relates to a process for preparing a crease-resistant, flame-retardant and waterproof multifunctional fabric for a safety vest.
Background
The safety vest has a reflective effect, and is also called a safety warning waistcoat or reflective clothes. The fabric of the existing safety vest is subjected to flame retardant treatment or waterproof treatment, so that the safety vest has good flame retardant property or good waterproof property, but the fabric cannot be subjected to flame retardant treatment and waterproof treatment at the same time, otherwise, the fabric cannot have good flame retardant property and good waterproof property, so that the limitation of the fabric in use is low, the prepared safety vest can only be used in fireproof occasions or waterproof occasions, and the application range is narrow, and the prepared safety vest is not suitable for occasions needing both fireproof and waterproof. For example, traffic polices are on duty, rain prevention is required, and the flame retardant effect is better for rescuing and reducing dangers such as spontaneous combustion of automobiles and the like; for example, fire police, the fire-resistant water gun is required to be flame-retardant, and has the best waterproof effect, so that the water sprayed by the high-pressure water gun is prevented from being wetted. Therefore, the fabric treated by the existing process has the defect of only flame retardant effect or only waterproof effect, and the application range is narrow.
Disclosure of Invention
The invention aims to provide a process for preparing a crease-resistant flame-retardant waterproof multifunctional fabric. The invention has the advantages of flame retardant effect, waterproof effect, strong anti-wrinkle capability and wide application range.
The technical scheme of the invention is as follows: a process for preparing the multifunctional anti-wrinkle flame-retarding water-proof fabric includes such steps as providing a fabric,
a. dyeing the gray cloth to obtain a product A,
b. setting product A, adding fire retardant (type P-207Z) to obtain product B, washing product C and product B with water to obtain product C,
d. and C, shaping, namely adding a waterproof agent with the model of TF5501 during shaping to obtain a finished product.
In the process of the multifunctional anti-wrinkle flame-retardant waterproof fabric, in the step a, the grey fabric is dyed in a high-temperature high-pressure dyeing machine, and the process comprises the following steps,
1, adding soaping agent of 1.5-2.5g/L and refining agent of 1.5-2.5g/L in sequence in a high-temperature high-pressure dyeing machine to obtain A1 product,
a2 and A1 products are heated to 75-85 ℃ at the speed of 2.5-3.5 ℃/min to obtain A2 products,
a3 and A2 products are kept warm for 12-18min to obtain A3 product,
adding stainine to a4 and A3 to obtain A4, adjusting the addition amount of stainine to make the pH of A4 to 4-5,
adding 2.5-3.5g/L leveling agent, type 2100, into product A5 and product A4 to obtain product A5,
adding disperse dye into products a6 and A5 to obtain product A6,
a7 and A6 products are heated to 100 ℃ and 110 ℃ at the speed of 1.5-2.5 ℃/min to obtain A7 products,
a8 and A7 products are kept warm for 4-6min to obtain A8 product,
a9 and A8 product are heated to 125-135 ℃ at 0.5-1.5 ℃/min to obtain A9 product,
a10 and A9 products are kept warm for 35-45min to obtain A10 product,
cooling product A11 and product A10 to obtain product A.
In the process of the anti-wrinkle flame-retardant waterproof multifunctional fabric, in the step a1, 2g/L of soaping agent and 2g/L of refining agent,
in the step a2, the A1 product is heated to 80 ℃ at the speed of 3 ℃/min,
in the step A3, the A2 product is kept warm for 15min,
in the step a5, adding 3g/L of leveling agent into the A4 product,
in the step a7, the A6 product is heated to 105 ℃ at the speed of 2 ℃/min,
in the step a8, the A7 product is kept warm for 5min,
in the step a9, the product A8 is heated to 130 ℃ at 1 ℃/min,
in the step a10, the A9 product is kept warm for 40 min.
In the process of the anti-wrinkle flame-retardant waterproof multifunctional fabric, in the step b, the product A is shaped by a shaping machine, the shaping temperature is 150-170 ℃, the speed is 45-55m/min, and the shaping solution contains a flame retardant with the concentration of 5-7%.
In the process of the anti-wrinkle flame-retardant waterproof multifunctional fabric, in the step b, the setting temperature is 160 ℃, the vehicle speed is 50m/min, and the flame retardant concentration is 6%.
In the process of the anti-wrinkle flame-retardant waterproof multifunctional fabric, in the step c, the fabric B is washed in a full-automatic rope washing machine, the full-automatic rope washing machine is provided with four grooves, the temperature of a solution in the first groove is 65-75 ℃, the solution in the first groove contains a deoiling agent and a chelating dispersant, the deoiling agent is TF-109r1, the concentration is 2.5-3.5g/L, the chelating dispersant is DM-8108, and the concentration is 1.5-2.5 g/L; the temperature of the solution in the second tank is 75-85 ℃, the solution in the second tank contains degreaser and chelating dispersant, the degreaser is TF-109r1, the concentration is 1.5-2.5g/L, the chelating dispersant is DM-8108, the concentration is 0.5-1.5 g/L; the third tank contains hot water with the temperature of 85-95 ℃; the fourth tank contains warm water at 55-65 deg.C.
In the process of the anti-wrinkle flame-retardant waterproof multifunctional fabric, in the step c, the temperature of the solution in the first tank is 70 ℃, the deoiling agent in the first tank is 3g/L, and the chelating dispersant in the first tank is 2 g/L; the temperature of the solution in the second tank is 80 ℃, the deoiling agent in the second tank is 2g/L, and the chelating dispersant in the second tank is 1 g/L; hot water in a third groove is 90 ℃; the warm water in the fourth tank is 60 ℃.
In the process of the anti-wrinkle flame-retardant waterproof multifunctional fabric, in the step d, the fabric C is shaped in a shaping machine at the shaping temperature of 195-210 ℃ and the vehicle speed of 60-70m/mim, the shaping solution contains a stiffening agent and a waterproof agent, the stiffening agent is 6320 (resin) and has the concentration of 2-3 percent, and the waterproof agent is TF-5501 and has the concentration of 1-2 percent.
In the process of the anti-wrinkle flame-retardant waterproof multifunctional fabric, in the step d, the setting temperature is 200-.
Compared with the prior art, the preferred flame retardant and waterproof agent can ensure that the fabric has both flame retardant effect and waterproof effect and obvious crease resistance under the matching of specific process steps and process parameters. Through inspection, the flame retardant property of the fabric reaches European standard EN 18011611; the waterproof grade can reach 100 cents in American standard; the folded fabric is folded for 3 hours under the pressure of 2 kilograms per square centimeter, the recovery angle of the drape fold of the fabric reaches 172 degrees within 1 minute, and the wrinkle resistance is good. The invention has both flame retardance and waterproofness, so the invention can be applied to both fireproof occasions and waterproof occasions, and has wider application range. The invention has the advantages of flame retardant effect, waterproof effect, strong anti-wrinkle capability and wide application range.
Detailed Description
The present invention is further illustrated by the following examples, which are not to be construed as limiting the invention.
Example 1. A process for preparing the multifunctional anti-wrinkle flame-retarding water-proof fabric includes such steps as providing a fabric,
a1, dyeing the grey cloth (terylen plain cloth) in the existing high-temperature high-pressure dyeing machine, adding 2g/L soaping agent and 2g/L refining agent in sequence in the high-temperature high-pressure dyeing machine to obtain A1 product,
heating product A2 and A1 to 80 deg.C at 3 deg.C/min to obtain product A2,
a3 and A2 products are kept warm for 15min to obtain A3 products,
adding stainine to a4 and A3 to obtain A4, adjusting the addition amount of stainine to make the pH of A4 to 4.5,
adding 3g/L leveling agent, leveling agent type 2100, into a5 and A4 to obtain A5,
adding disperse dye into products a6 and A5 to obtain product A6,
heating product A7 and A6 to 105 deg.C at 2 deg.C/min to obtain product A7,
a8 and A7 products are kept warm for 5min to obtain A8 products,
a9 and A8 products are heated to 130 ℃ at 1 ℃/min to obtain A9 products,
preserving heat of a10 and A9 products for 40min to obtain A10 products,
cooling product A11 and product A10 to obtain product A.
b. And (3) shaping the product A by using the conventional shaping machine at the shaping temperature of 160 ℃ at the vehicle speed of 50m/min, wherein the shaping solution contains 6% of flame retardant, the type of the flame retardant is P-207Z, and the product B is obtained.
c. Washing the product B in an existing full-automatic rope washing machine, wherein the full-automatic rope washing machine is provided with four grooves, and seen from the washing direction, the temperature of the solution in the first groove is 70 ℃, the solution in the first groove contains a deoiling agent and a chelating dispersant, the deoiling agent is TF-109r1, the concentration is 3g/L, the chelating dispersant is DM-8108, and the concentration is 2 g/L; the temperature of the solution in the second tank is 80 ℃, the solution in the second tank contains a degreaser and a chelating dispersant, wherein the degreaser is TF-109r1, the concentration of the degreaser is 2g/L, and the chelating dispersant is DM-8108, the concentration of the chelating dispersant is 1 g/L; the third tank has hot water at 90 deg.C; the fourth tank contains 60 deg.C warm water to obtain product C.
d. The product C is shaped in the existing shaping machine, the shaping temperature is 200-.
The flame retardant properties of the finished product of example 1 meet european standard EN 18011611; the waterproof grade can reach 100 cents in American standard; the folded fabric is folded for 3 hours under the pressure of 2 kilograms per square centimeter, and the recovery angle of the drape fold of the fabric reaches 172 degrees within 1 minute.
Example 2. A process for preparing the multifunctional anti-wrinkle flame-retarding water-proof fabric includes such steps as providing a fabric,
a1, dyeing the grey cloth in the existing high-temperature high-pressure dyeing machine, adding 1.5g/L soaping agent and 2.5g/L refining agent in sequence in the high-temperature high-pressure dyeing machine to obtain A1 product,
heating product A2 and A1 to 85 deg.C at 2.5 deg.C/min to obtain product A2,
keeping the temperature of A3 and A2 products for 12min to obtain A3 product,
adding stainine to a4 and A3 to obtain A4, adjusting the addition amount of stainine to make the pH of A4 to 4,
adding 3.5g/L leveling agent, leveling agent type 2100, into a5 and A4 to obtain A5,
adding disperse dye into products a6 and A5 to obtain product A6,
heating product A7 and product A6 to 100 deg.C at 2.5 deg.C/min to obtain product A7,
a8 and A7 products are kept warm for 4min to obtain A8 products,
a9 and A8 products are heated to 130 ℃ at 1.5 ℃/min to obtain A9 products,
a10 and A9 products are kept warm for 35min to obtain A10 products,
cooling product A11 and product A10 to obtain product A.
b. And (3) shaping the product A by using the conventional shaping machine at the shaping temperature of 150 ℃ at the vehicle speed of 55m/min, wherein the shaping solution contains a flame retardant with the concentration of 5 percent, and the type of the flame retardant is P-207Z, so that the product B is obtained.
c. Washing the product B in an existing full-automatic rope washing machine, wherein the full-automatic rope washing machine is provided with four grooves, and seen from the washing direction, the temperature of the solution in the first groove is 75 ℃, the solution in the first groove contains a deoiling agent and a chelating dispersant, the deoiling agent is TF-109r1, the concentration is 2.5g/L, and the chelating dispersant is DM-8108, the concentration is 2.5 g/L; the temperature of the solution in the second tank is 75 ℃, the solution in the second tank contains a degreaser and a chelating dispersant, wherein the degreaser is TF-109r1, the concentration of the degreaser is 2.5g/L, and the chelating dispersant is DM-8108, the concentration of the chelating dispersant is 0.5 g/L; the third tank has hot water at 95 deg.C; the fourth tank contains warm water of 55 deg.C to obtain product C.
d. The product C is shaped in the existing shaping machine, the shaping temperature is 195 ℃, the vehicle speed is 70m/mim, the shaping solution contains a stiffening agent and a waterproofing agent, the stiffening agent type number 6320 (resin) and the concentration are 2 percent, and the waterproofing agent type TF-5501 and the concentration are 1 percent, thus obtaining the finished product.
Example 3. A process for preparing the multifunctional anti-wrinkle flame-retarding water-proof fabric includes such steps as providing a fabric,
a1, dyeing the grey cloth in the existing high-temperature high-pressure dyeing machine, adding 2.5g/L soaping agent and 1.5g/L refining agent in sequence in the high-temperature high-pressure dyeing machine to obtain A1 product,
heating product A2 and product A1 to 75 deg.C at 3.5 deg.C/min to obtain product A2,
a3 and A2 products are kept warm for 18min to obtain A3 products,
adding stainine to a4 and A3 to obtain A4, adjusting the addition amount of stainine to make the pH of A4 to 5,
adding 2.5g/L leveling agent, leveling agent type 2100, into a5 and A4 to obtain A5,
adding disperse dye into products a6 and A5 to obtain product A6,
heating product A7 and A6 to 110 deg.C at 1.5 deg.C/min to obtain product A7,
a8 and A7 products are kept warm for 6min to obtain A8 products,
a9 and A8 products are heated to 130 ℃ at 0.5 ℃/min to obtain A9 products,
keeping the temperature of a10 and A9 products for 45min to obtain A10 product,
cooling product A11 and product A10 to obtain product A.
b. And (3) shaping the product A by using the conventional shaping machine at the shaping temperature of 170 ℃ at the vehicle speed of 45m/min, wherein the shaping solution contains a flame retardant with the concentration of 7 percent, and the type of the flame retardant is P-207Z, so that the product B is obtained.
c. Washing the product B in an existing full-automatic rope washing machine, wherein the full-automatic rope washing machine is provided with four grooves, and seen from the washing direction, the temperature of the solution in the first groove is 65 ℃, the solution in the first groove contains a deoiling agent and a chelating dispersant, the deoiling agent is TF-109r1, the concentration is 3.5g/L, and the chelating dispersant is DM-8108, and the concentration is 1.5 g/L; the temperature of the solution in the second tank is 85 ℃, the solution in the second tank contains a degreaser and a chelating dispersant, wherein the degreaser is TF-109r1, the concentration is 1.5g/L, and the chelating dispersant is DM-8108, the concentration is 1.5 g/L; the third tank has hot water at 85 ℃; the fourth tank contains 65 deg.C warm water to obtain product C.
d. And C, shaping the product in the existing shaping machine, wherein the shaping temperature is 210 ℃, the vehicle speed is 70m/mim, the shaping solution contains a stiffening agent and a waterproofing agent, the stiffening agent is 6320 (resin) in concentration, the waterproofing agent is TF-5501 in concentration and 2 in concentration, and a finished product is obtained.
The invention has the advantages of flame retardant effect, waterproof effect, strong anti-wrinkle capability and wide application range.
Claims (9)
1. A process for preparing a crease-resistant flame-retardant waterproof multifunctional fabric is characterized by comprising the following steps of: comprises the following steps of (a) carrying out,
a. dyeing the gray cloth to obtain a product A,
b. setting the product A, adding a flame retardant with the model of P-207Z to obtain a product B,
c. washing the product B with water to obtain product C,
d. and C, shaping, namely adding a waterproof agent with the model of TF5501 during shaping to obtain a finished product.
2. The anti-wrinkle flame-retardant waterproof multifunctional fabric process according to claim 1, characterized in that: in the step a, the grey cloth is dyed in a high-temperature high-pressure dyeing machine, and the method comprises the following steps,
1, adding soaping agent of 1.5-2.5g/L and refining agent of 1.5-2.5g/L in sequence in a high-temperature high-pressure dyeing machine to obtain A1 product,
a2 and A1 products are heated to 75-85 ℃ at the speed of 2.5-3.5 ℃/min to obtain A2 products,
a3 and A2 products are kept warm for 12-18min to obtain A3 product,
adding stainine to a4 and A3 to obtain A4, adjusting the addition amount of stainine to make the pH of A4 to 4-5,
adding 2.5-3.5g/L leveling agent, type 2100, into product A5 and product A4 to obtain product A5,
adding disperse dye into products a6 and A5 to obtain product A6,
a7 and A6 products are heated to 100 ℃ and 110 ℃ at the speed of 1.5-2.5 ℃/min to obtain A7 products,
a8 and A7 products are kept warm for 4-6min to obtain A8 product,
a9 and A8 product are heated to 125-135 ℃ at 0.5-1.5 ℃/min to obtain A9 product,
a10 and A9 products are kept warm for 35-45min to obtain A10 product,
cooling product A11 and product A10 to obtain product A.
3. The anti-wrinkle flame-retardant waterproof multifunctional fabric process according to claim 2, characterized in that: in the step a1, the soaping agent is 2g/L of refining agent 2g/L,
in the step a2, the A1 product is heated to 80 ℃ at the speed of 3 ℃/min,
in the step A3, the A2 product is kept warm for 15min,
in the step a5, adding 3g/L of leveling agent into the A4 product,
in the step a7, the A6 product is heated to 105 ℃ at the speed of 2 ℃/min,
in the step a8, the A7 product is kept warm for 5min,
in the step a9, the product A8 is heated to 130 ℃ at 1 ℃/min,
in the step a10, the A9 product is kept warm for 40 min.
4. The anti-wrinkle flame-retardant waterproof multifunctional fabric process according to claim 1, characterized in that: in the step b, the product A is shaped by a shaping machine, the shaping temperature is 150-.
5. The anti-wrinkle flame-retardant waterproof multifunctional fabric process according to claim 4, characterized in that: in the step b, the setting temperature is 160 ℃, the vehicle speed is 50m/min, and the flame retardant concentration is 6%.
6. The anti-wrinkle flame-retardant waterproof multifunctional fabric process according to claim 1, characterized in that: in the step c, the product B is washed in a full-automatic rope washing machine, the full-automatic rope washing machine is provided with four grooves, the temperature of the solution in the first groove is 65-75 ℃, the solution in the first groove contains a deoiling agent and a chelating dispersant, the deoiling agent is TF-109r1, the concentration is 2.5-3.5g/L, and the chelating dispersant is DM-8108, and the concentration is 1.5-2.5g/L when viewed from the washing direction; the temperature of the solution in the second tank is 75-85 ℃, the solution in the second tank contains degreaser and chelating dispersant, the degreaser is TF-109r1, the concentration is 1.5-2.5g/L, the chelating dispersant is DM-8108, the concentration is 0.5-1.5 g/L; the third tank contains hot water with the temperature of 85-95 ℃; the fourth tank contains warm water at 55-65 deg.C.
7. The anti-wrinkle flame-retardant waterproof multifunctional fabric process according to claim 6, characterized in that: in the step c, the temperature of the solution in the first tank is 70 ℃, the deoiling agent in the first tank is 3g/L, and the chelating dispersant in the first tank is 2 g/L; the temperature of the solution in the second tank is 80 ℃, the deoiling agent in the second tank is 2g/L, and the chelating dispersant in the second tank is 1 g/L; hot water in a third groove is 90 ℃; the warm water in the fourth tank is 60 ℃.
8. The anti-wrinkle flame-retardant waterproof multifunctional fabric process according to claim 1, characterized in that: in the step d, the product C is shaped in a shaping machine at the shaping temperature of 195- & ltSUB & gt plus 210 ℃ and the vehicle speed of 60-70m/mim, and the shaping solution contains a stiffening agent and a waterproofing agent, wherein the stiffening agent is 6320 (resin) and has the concentration of 2-3 percent, and the waterproofing agent is TF-5501 and has the concentration of 1-2 percent.
9. The anti-wrinkle flame-retardant waterproof multifunctional fabric process according to claim 8, characterized in that: in the step d, the setting temperature is 200-.