CN112048038A - Environment-friendly rubber particle - Google Patents
Environment-friendly rubber particle Download PDFInfo
- Publication number
- CN112048038A CN112048038A CN201910487356.5A CN201910487356A CN112048038A CN 112048038 A CN112048038 A CN 112048038A CN 201910487356 A CN201910487356 A CN 201910487356A CN 112048038 A CN112048038 A CN 112048038A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- rubber particles
- friendly rubber
- rubber particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses environment-friendly rubber particles, which comprise 85-94 parts of fluororubber, 12-23 parts of hydrogen silicone oil, 8-19 parts of styrene, 10-22 parts of paraffin oil, 13-45 parts of carbon fiber and 5-19 parts of barium titanate. The rubber particles have the advantages of low cost, strong bending resistance, good fire resistance, long service life, large bearing capacity, small mass, environmental protection and the like.
Description
Technical Field
The invention belongs to the field of rubber particles, and particularly relates to an environment-friendly rubber particle.
Background
The rubber particles are produced by processing various waste rubbers, including waste rubber, tourist shoe soles, leftover materials, cable skins, rubber leftover materials, automobile cushion belts, automobile tires and other waste rubber raw materials.
The rubber particles are divided into black rubber particles and colored rubber particles; the colored rubber particles are divided into green rubber particles, red rubber particles, blue rubber particles, white rubber particles, brown rubber particles, yellow rubber particles and other colored rubber particles.
Disclosure of Invention
The purpose of the invention is as follows: the invention aims to provide environment-friendly rubber particles.
The technical scheme is as follows: the invention relates to an environment-friendly rubber particle, which comprises the following raw materials in parts by weight: 85-94 parts of fluororubber, 12-23 parts of hydrogen silicone oil, 8-19 parts of styrene, 10-22 parts of paraffin oil, 13-45 parts of carbon fiber and 5-19 parts of barium titanate.
Preferably, 88 to 90 parts of fluororubber. 15-20 parts of hydrogen silicone oil. 10-15 parts of styrene. 15-20 parts of paraffin oil. 18-35 parts of carbon fiber. 12-15 parts of barium titanate.
Has the beneficial effects that: compared with the prior art, the invention has the following remarkable advantages: the rubber particles have the advantages of low cost, strong bending resistance, good fire resistance, long service life, large bearing capacity, small mass, environmental protection and the like.
Detailed Description
The technical solution of the present invention will be further described in detail with reference to the following examples.
Example 1
The rubber particles of the present invention comprise: 88 parts of fluororubber, 15 parts of hydrogen silicone oil, 10 parts of styrene, 15 parts of paraffin oil, 18 parts of carbon fiber and 12 parts of barium titanate.
Example 2
The rubber particles of the present invention comprise: 90 parts of fluororubber, 20 parts of hydrogen silicone oil, 15 parts of styrene, 20 parts of paraffin oil, 35 parts of carbon fiber and 15 parts of barium titanate.
Example 3
The rubber particles of the present invention comprise: 85 parts of fluororubber, 12 parts of hydrogen silicone oil, 8 parts of styrene, 10 parts of paraffin oil, 13 parts of carbon fiber and 5 parts of barium titanate.
Example 4
The rubber particles of the present invention comprise: 94 parts of fluororubber, 23 parts of hydrogen silicone oil, 19 parts of styrene, 22 parts of paraffin oil, 45 parts of carbon fiber and 19 parts of barium titanate.
Claims (7)
1. The environment-friendly rubber particle is characterized by comprising the following raw materials in parts by weight: 85-94 parts of fluororubber, 12-23 parts of hydrogen silicone oil, 8-19 parts of styrene, 10-22 parts of paraffin oil, 13-45 parts of carbon fiber and 5-19 parts of barium titanate.
2. The environment-friendly rubber particle as defined in claim 1, wherein: 88-90 parts of fluororubber.
3. The environment-friendly rubber particle as defined in claim 1, wherein: 15-20 parts of hydrogen silicone oil.
4. The environment-friendly rubber particle as defined in claim 1, wherein: 10-15 parts of styrene.
5. The environment-friendly rubber particle as defined in claim 1, wherein: 15-20 parts of paraffin oil.
6. The environment-friendly rubber particle as defined in claim 1, wherein: 18-35 parts of carbon fiber.
7. The environment-friendly rubber particle as defined in claim 1, wherein: 12-15 parts of barium titanate.