CN111991137A

CN111991137A - Titanium nano sheet/graphene-based hot compress medicine pillow

Info

Publication number: CN111991137A
Application number: CN202010937478.2A
Authority: CN
Inventors: 吴立刚; 叶德林; 张以河; 马宇飞; 李明; 李正博
Original assignee: Beijing Kangene Technology Innovation Research Co ltd
Current assignee: Beijing Kangene Technology Innovation Research Co ltd
Priority date: 2020-09-08
Filing date: 2020-09-08
Publication date: 2020-11-27

Abstract

The invention provides a titanium nano sheet/graphene-based hot compress medicine pillow which comprises a pillow case and a pillow core, wherein the pillow case comprises a flexible contact layer and a titanium nano sheet/graphene-based heating film, the flexible contact layer is arranged on the outer side of the pillow case, the titanium nano sheet/graphene-based heating film is arranged on the inner side of the pillow case, and the flexible contact layer covers the titanium nano sheet/graphene-based heating film; the pillow core comprises a flexible containing bag and heat storage gel, and the heat storage gel is contained in the flexible containing bag. The titanium nano sheet/graphene-based hot compress medicine pillow can act on epidermis for antibiosis, promote release of active ingredients of medicines, and has the functions of promoting blood circulation, pore relaxation, improving epidermis absorption effect and the like by virtue of high-efficiency electrothermal conversion efficiency, high infrared normal emissivity, good flexibility and elasticity of the titanium nano sheet/graphene-based fiber film.

Description

Titanium nano sheet/graphene-based hot compress medicine pillow

Technical Field

The invention relates to the technical field of graphene heating devices, in particular to a flexible titanium nanosheet/graphene-based hot compress drug pillow.

Background

Graphene is a two-dimensional nanomaterial with a hexagonal honeycomb lattice structure formed by carbon atoms through sp2 hybrid orbitals and only one layer of carbon atoms thick. The unique structure of graphene gives it a number of excellent properties, such as a high theoretical specific surface area (2630 m)²The material is prepared by the following raw materials, such as the raw materials of the material are selected from the following raw materials, such as/g), ultrahigh electron mobility (200000 cm2/v.s), high thermal conductivity (5300W/m.K), high Young modulus (1.0TPa), high light transmittance (97.7%) and the like. By virtue of the advantages of the structure and the performance of the graphene, the graphene has a huge application prospect in the fields of energy storage and conversion devices, nano-electronic devices, multifunctional sensors, flexible wearable electronics, electromagnetic shielding, corrosion prevention and the like. In view of the flexibility and the conductive characteristic of graphene, the graphene slurry is added into the printing ink to prepare the conductive printing ink, and the graphene heating layer is further prepared by spraying and drying the printing ink to prepare the graphene heating body.

Along with the trend of people to good and healthy life, the traditional heating system is improved, more economic and clean alternative energy is searched, and the development of a novel green low-carbon heating system is reluctant. An electric heating technology based on graphene infrared emission performance (far infrared rays with the wavelength of 5-14 microns), namely graphene-based infrared heating ink and an infrared heating body technology thereof, provides an effective solution for solving the problems. Compared with the traditional heating methods such as coal burning, steam, hot air and resistance, the graphene heating method has the advantages of high heating speed, high electricity-heat conversion rate, automatic temperature control, zone control, stable heating, no abnormal sound in the heating process, high heat conduction efficiency, low operation cost (the power consumption of each square meter of the graphene electrothermal film can be reduced to 0.5 degree every day), relatively uniform heating, small floor area, low investment and production cost, long service life, high working efficiency and the like, and is more favorable for popularization and application. The energy-saving heating device replaces the traditional heating device, has particularly remarkable electricity-saving effect, can generally save electricity by about 30 percent, and even can reach 60 to 70 percent in individual occasions.

In the prior art, graphene is generally prepared into graphene slurry, ink or paint, and then prepared into a graphene heating coating and the like through a printing method. For example, patent application No. CN 201911401440.7, the patent name of which is graphene far infrared heating brick, discloses a graphene far infrared heating brick, a brick unit of the floor heating brick comprises a heating element and a heat dissipation member, wherein the heating element is made of graphene composite coating, and the heat dissipation member is made of graphene composite rack. The graphene heating coating is printed on the base material, and the graphene heating coating prepared by printing is easily broken after being repeatedly folded and stretched, so that the graphene heating coating is broken, and the heat production effect and the service life of the graphene heating coating are influenced. In addition, the defects that the graphene heating coating has poor adhesion effect with a flexible substrate and is easy to separate after being used for a long time are still the subject of the industry.

The graphene fiber membrane is prepared by adding graphene into a spinning solution and further using an electrostatic spinning technology, has the advantages of strong flexibility, good bending resistance effect, large surface area and the like, does not need to be attached to a substrate, and can be independently formed into a membrane or bonded on the flexible substrate through an adhesive for heat supply after the membrane is formed. The traditional Chinese medicine hot compress is a common medicine application mode, can effectively promote the release of active ingredients of the traditional Chinese medicine, strengthen the absorption of the organism and improve the curative effect of the traditional Chinese medicine, and has important auxiliary effects on the treatment of scapulohumeral periarthritis, cervical spondylosis, lumbar muscle strain, other arthralgia and the like. The current traditional Chinese medicine hot compress mode is as follows: wrapping the Chinese medicinal materials in hot towel or other hot compress bag, and applying the hot towel or hot compress bag to cervical vertebra, lumbar vertebra, shoulder, elbow joint, hip joint, knee joint, etc. However, this application method has the following disadvantages: (1) only a transient heating effect can be ensured, and the release of the active pharmaceutical ingredients is limited; (2) the hot compress device can only be attached to a flat surface skin, and the form of the hot compress device cannot be adjusted based on the human tissue structure or the movement deformation of the body for irregular and movable joint parts such as the neck, the waist, the knee joint, the hip joint and the like, and a dead angle exists in the process of attaching to the joint parts. Based on the high infrared normal emission amount, the high thermal efficiency, the high heat conduction efficiency, the thermal stability, the high flexibility and the elasticity of the flexible graphene fiber membrane, the traditional Chinese medicine hot compress medicine pillow is developed to solve the problems of slow absorption, small release amount of active ingredients, untight attaching and the like in the current traditional Chinese medicine hot compress field, and becomes a core point of the technical scheme of the invention.

Disclosure of Invention

In view of the above, the invention provides a flexible titanium nanosheet/graphene-based hot compress drug pillow, which aims to overcome the defects of slow absorption of active ingredients, small release amount of the active ingredients, non-tight fitting and the like of the conventional hot compress drug pillow.

In a first aspect, the invention provides a titanium nano sheet/graphene-based hot compress medicine pillow which comprises a pillow case and a pillow core, wherein the pillow case comprises a flexible contact layer and a titanium nano sheet/graphene-based heating film, the flexible contact layer is arranged on the outer side of the pillow case, the titanium nano sheet/graphene-based heating film is arranged on the inner side of the pillow case, and the flexible contact layer covers the titanium nano sheet/graphene-based heating film; the pillow core comprises a flexible accommodating bag and heat storage gel, and the heat storage gel is accommodated in the flexible accommodating bag;

the titanium nano sheet/graphene-based heating film comprises a first transparent insulating layer, an electrode, a second transparent insulating layer and a titanium nano sheet/graphene-based fiber film, wherein the first transparent insulating layer covers one surface of the titanium nano sheet/graphene-based fiber film, the second transparent insulating layer covers the other surface of the titanium nano sheet/graphene-based fiber film, one end of the electrode is electrically connected with the titanium nano sheet/graphene-based fiber film, and the other end of the electrode extends out of the first transparent insulating layer or the second transparent insulating layer;

the preparation method of the titanium nanosheet/graphene-based fiber membrane comprises the following steps:

preparing a pre-stripping dispersion liquid of titanium powder: providing titanium powder and adding the titanium powder into the pre-stripping dispersion liquid, performing primary water bath ultrasound on the pre-stripping dispersion liquid added with the titanium powder, wherein the temperature of the primary water bath ultrasound is 5-15 ℃, and centrifuging and collecting supernatant after the ultrasound is finished to prepare the pre-stripping dispersion liquid of the titanium powder;

preparing a mixture of titanium powder and graphene oxide: adding graphene oxide into a pre-stripping dispersion liquid of titanium powder, performing secondary water bath ultrasound, wherein the temperature of the secondary water bath ultrasound is 5-15 ℃, centrifuging after the ultrasound is finished, collecting a bottom layer mixture, dispersing the bottom layer mixture in water, washing and drying to obtain a mixture of the titanium powder and the graphene oxide;

preparing a titanium nanosheet/graphene oxide dispersion liquid: dispersing a mixture of titanium powder and graphene oxide in DMF to prepare a mixed solution, performing ultrasonic treatment on the mixed solution by using a pulse probe at the ultrasonic temperature of 5-15 ℃, and concentrating the mixed solution after the ultrasonic treatment is finished to prepare a titanium nano sheet/graphene oxide dispersion solution;

spinning: adding carbon black and PAN powder into the titanium nanosheet/graphene oxide dispersion liquid, uniformly stirring, and then carrying out three-stage water bath ultrasound, wherein the temperature of the three-stage water bath ultrasound is 5-15 ℃, and after the three-stage water bath ultrasound is finished, the three-stage water bath ultrasound is used as a spinning stock solution, and electrostatic spinning and collection are carried out by using a spinning needle with the inner diameter increased along the filament outlet direction, so as to prepare the titanium nanosheet/graphene oxide hybrid porous fibrous membrane;

and (3) post-treatment: washing the titanium nanosheet/graphene oxide hybrid porous fiber membrane, drying and reducing to obtain a titanium nanosheet/graphene-based fiber membrane;

the mass of the graphene oxide is 0.5-5 times of that of titanium powder in a pre-stripping dispersion liquid of the titanium powder, the mass fraction of PAN in the spinning stock solution is 8-12%, and the pre-stripping dispersion liquid is isopropanol, deionized water or a mixed solution of the isopropanol and the deionized water.

The titanium nano sheet/graphene-based hot compress medicine pillow comprises a pillow case and a pillow core, wherein the pillow case is provided with a titanium nano sheet/graphene-based heating film, and by means of the high heat efficiency, the high infrared normal emissivity, the antibacterial function and the good flexibility and elasticity of the titanium nano sheet/graphene-based heating film, the titanium nano sheet/graphene-based heating film can act on epidermis for antibiosis, promote the release of active ingredients of medicines, and the high infrared normal emissivity can also play roles in promoting blood circulation, pore relaxation, improving the absorption effect of the epidermis and the like. The heat storage gel is arranged in the pillow inner, and the heat storage gel with an indefinite form can be automatically adjusted based on the human tissue structure so as to realize the seamless fit with the human epidermis, such as tissue joints. In addition, the heat storage gel has larger specific heat capacity and a certain heat storage function, and a part of heat radiated in the heating process of the pillowcase can be absorbed by the built-in pillow core, so that the effect of slowly raising the temperature and the effect of maintaining the relative constant temperature of the hot compress medicine pillow are achieved; when the pillowcase stops heating, the heat in the pillow core also can be slowly released, and the functions of slowly cooling and maintaining the epidermis hot compress effect for a long time are achieved. When the titanium nano sheet/graphene-based hot compress medicine pillow is used, a user can firstly apply ointment or medicine paste on the surface of a body (or cover the ointment or medicine paste on the surface of the body and then cover the medicine paste with oily paper), and then lie on the titanium nano sheet/graphene-based hot compress medicine pillow, for example, the user can carry out hot compress on cervical vertebra, thoracic vertebra, lumbar vertebra, hip joint or navel, and can also lay the medicine pillow on (or press) a part to be hot compressed of the body, such as a shoulder, a wrist, an ankle or a knee joint, and by means of the automatic shape adjusting function of the pillow core and the high flexibility and high elasticity of the hot compress medicine pillow case, the titanium nano sheet/graphene-based hot compress medicine pillow can be completely attached to the part.

The titanium nano sheet/graphene-based heating film comprises a first transparent insulating layer, an electrode, a second transparent insulating layer and a titanium nano sheet/graphene-based fiber film, wherein the first transparent insulating layer and the second transparent insulating layer are attached to two surfaces of the titanium nano sheet/graphene-based fiber film, so that the titanium nano sheet/graphene-based fiber film is isolated in a closed insulating space, and electric leakage is prevented when the titanium nano sheet/graphene-based fiber film is electrified to generate heat. One end of the electrode is electrically connected with the titanium nano sheet/graphene-based fiber membrane, and the other end of the electrode extends out of the first transparent insulating layer or the second transparent insulating layer, so that the titanium nano sheet/graphene-based fiber membrane can be electrically conducted with an external power supply through the electrode. The first transparent insulating layer and the second transparent insulating layer can also ensure that the titanium nano sheet/graphene-based fiber film can radiate infrared rays outwards and further transfer heat to the surface skin or the pillow core efficiently.

The preparation method of the titanium nanosheet/graphene-based fibrous membrane comprises the steps of preparing a pre-stripping dispersion liquid of titanium powder, preparing a mixture of the titanium powder and graphene oxide, preparing the titanium nanosheet/graphene oxide dispersion liquid, spinning and post-treating. The step of preparing the pre-stripping dispersion liquid of the titanium powder can be used for stripping the titanium powder in advance, and the stripping efficiency of the titanium powder and the preparation efficiency of the titanium nanosheets are improved by collecting the primarily stripped titanium powder and using the primarily stripped titanium powder for the next stripping. The step of preparing the mixture of the titanium powder and the graphene oxide comprises the steps of carrying out water bath ultrasonic treatment on the preliminarily peeled titanium powder and the graphene oxide together, wherein the titanium powder is poor in dispersibility in a pre-peeling dispersion liquid, adding the graphene into the pre-peeling dispersion liquid of the titanium powder and carrying out water bath ultrasonic treatment together, and under the assistance of the graphene, the titanium powder is effectively peeled and can be well mixed with the graphene oxide. In the step of preparing the titanium nanosheet/graphene oxide dispersion liquid, the mixed liquid is subjected to ultrasonic treatment by adopting a pulse probe, so that the titanium nanosheet can be effectively prepared, and the titanium nanosheet and the graphene oxide dispersion liquid are further mixed, so that the titanium nanosheet or the graphene oxide are prevented from being stacked to cause overhigh local concentration and non-spinnability, and the conductivity and the dispersion uniformity among graphene sheet layers can be improved. The primary water bath ultrasound, the secondary water bath ultrasound and the pulse probe ultrasound are carried out at low temperature, so that the prepared titanium nanosheet can be effectively prevented from being degraded. In the spinning step, PAN powder and carbon black are added into a DMF solution, three-stage water bath ultrasound is performed after uniform stirring, the spinning solution is more uniform through the stirring and ultrasound processes, the uniformity of the physical size and the performance of the output yarn is ensured, the carbon black and the PAN powder can be fully dispersed in the titanium nano sheet/graphene oxide dispersion liquid, the uniform distribution and the uniform conductivity of the electric conductor of the spinning fiber are ensured, the electric conductor is fully doped on the PAN high molecular compound, and the titanium nano sheet/graphene oxide hybrid porous fiber with uniform conductivity is prepared. In the post-treatment step, the titanium nanosheet/graphene oxide hybrid porous fiber membrane is washed, dried and reduced, and the graphene oxide is reduced to reduced graphene oxide, so that the reduced titanium nanosheet/graphene-based fiber membrane is prepared, and has the advantages of stable chemical performance, heat resistance, strong electric conductivity, high infrared radiation rate and the like.

According to the preparation method of the titanium nanosheet/graphene-based fiber membrane, the graphene oxide is added in the preparation process of the titanium nanosheet, so that the titanium powder can be assisted to be stripped into the titanium nanosheet, and the titanium nanosheet and the graphene oxide can be uniformly mixed. The titanium nanosheet, the graphene oxide and the carbon black are further loaded on the fiber in the spinning process, so that the fiber has the advantages of high porosity, large specific surface area, strong infrared radiation, remarkable electric heating performance, high thermal conductivity, good flexibility, remarkable bending-resistant effect and the like, and the fiber also has the advantages of high mechanical strength, medium-high temperature resistance and the like due to the fact that a large amount of PAN (polyacrylonitrile) polymers are contained in the fiber.

Preferably, the bottom of the pillow case is further provided with a hard base, and the flexible contact layer is connected with the hard base or clamped in the hard base. Be connected through flexible contact layer and stereoplasm base, perhaps flexible contact layer joint in the stereoplasm base, play the effect of fixed titanium nanometer piece/graphite alkene base hot compress medicine pillow bottom from this, prevent that titanium nanometer piece/graphite alkene base hot compress medicine pillow from rolling in the use.

More preferably, the hard base is U-shaped, and the bottom of the flexible contact layer is connected with the hard base or the flexible contact layer is clamped in the hard base. The U-shaped hard base has a better fixing effect. Most preferably, a heat reflecting layer is further arranged on one surface, facing the flexible contact layer, of the hard base, and is used for reflecting infrared rays radiated outwards, so that the effects of saving heat and improving the heat utilization rate are achieved.

Preferably, the flexible contact layer is made of transparent insulating materials, the flexible containing bag is made of flexible resin or rubber, and the heat storage gel is never solidified heat conduction gel. Therefore, the flexible contact layer made of the transparent insulating material can ensure that infrared rays radiated by the titanium nano sheet/graphene-based heating film can effectively penetrate through the flexible contact layer and act on the surface, and can also be stretched along with the form change of the heat storage gel, so that seamless attachment and anti-creeping protection are realized. The flexible containing bag is matched with the never-solidified heat-conducting gel, so that sufficient deformation space is provided for the heat-conducting gel.

More preferably, the titanium nano sheet/graphene-based hot compress drug pillow further comprises a drug patch, wherein the drug patch comprises a medical adhesive tape and a medical cotton pad attached to the adhesive surface of the medical adhesive tape. When in use, the liquid medicine and the cream can be coated on the medical cotton pad, or the traditional Chinese medicine residues are soaked in water and then wrapped on the medical cotton pad, and then the medical adhesive tape is used for adhering the medical patch to the part to be hot-compressed.

Preferably, a transparent heat conduction layer is further arranged between the second transparent insulation layer and the titanium nanosheet/graphene-based fiber membrane, and the second transparent insulation layer is connected with the flexible contact layer. Through setting up transparent heat-conducting layer can high-efficient heat and the infrared radiation conduction that produces behind the circular telegram of titanium nanometer piece/graphite alkene base fibre membrane go out and further act on the hot compress position, promote the effect of infrared ray hot compress.

Preferably, a waterproof bonding layer is further arranged between the first transparent insulating layer and the second transparent insulating layer, and the waterproof bonding layer is bonded with the first transparent insulating layer and the second transparent insulating layer respectively to form a closed cavity;

the titanium nano sheet/graphene-based fiber membrane and the transparent heat conduction layer are arranged in the closed cavity, and the electrodes extend out of the closed cavity. The first transparent insulating layer and the second transparent insulating layer are respectively bonded with the waterproof bonding layer to form a closed cavity, and the titanium nanosheet/graphene-based fiber membrane and the transparent heat conducting layer are arranged in the closed cavity, so that a good insulating and waterproof effect is achieved.

Preferably, the electrode comprises a transverse arm and a vertical arm which are connected with each other, the transverse arm extends out of the transparent heat conduction layer to form the closed cavity, and the vertical arm extends out of the transparent heat conduction layer and is electrically connected with the titanium nanosheet/graphene-based fiber membrane. The electrodes are arranged in an L shape and comprise a transverse arm and a vertical arm which are mutually connected, the electric connection between the titanium nano sheet/graphene-based fiber membrane and an external power supply can be realized by means of the L-shaped electrodes, and the L-shaped loop can also form a closed waterproof cavity, so that the waterproof performance of the titanium nano sheet/graphene-based heating membrane is facilitated.

Preferably, in the step of preparing the pre-stripping dispersion liquid of the titanium powder, the mass-volume ratio of the titanium powder to the pre-stripping dispersion liquid is 10-500 mg/ml, the power of the primary water bath ultrasound is 250-500W, and the time of the primary water bath ultrasound is 24-72 h;

the rotating speed of the centrifugation is 1500-3500 RPM, and the time of the centrifugation is 5-30 min. The function of pre-stripping the titanium simple substance can be achieved through primary water bath ultrasound, the follow-up centrifugal process can separate the pre-stripped few-layer titanium simple substance from the un-stripped titanium powder, the small titanium simple substance generated by pre-stripping is transferred to the next stripping procedure, and the few-layer titanium nanosheet is efficiently prepared.

Preferably, in the step of preparing the mixture of titanium powder and graphene oxide, the power of the secondary water bath ultrasound is 250-500W, and the time of the secondary water bath ultrasound is 8-24 h;

the rotating speed of the centrifugation is 8000-15000 RPM, and the time of the centrifugation is 20-100 min. After adding the graphene oxide, mixing the graphene oxide with the preliminarily peeled titanium powder, further performing secondary water bath ultrasound, mixing the graphene oxide with the preliminarily peeled titanium powder, wherein the graphene oxide has the effect of assisting the peeling and dispersion of the titanium powder, and preventing the titanium nanosheets and the graphene oxide from being stacked mutually. And further collecting the titanium nanosheets and graphene oxide generated by stripping through centrifugation for subsequent steps.

Preferably, in the step of preparing the mixture of titanium powder and graphene oxide, the mixture of the bottom layer is dispersed in water for washing, then the solvent is concentrated and removed by using a rotary evaporation method, and the concentrated mixture is transferred to a temperature of 30-40 ℃ for vacuum drying for 2-8 hours to prepare the mixture of the titanium powder and the graphene oxide. Residual pre-stripping dispersion liquid on a mixture of titanium powder and graphene oxide can be effectively removed through the steps of removing a solvent through rotary evaporation, vacuum drying and the like, the subsequent steps of preparing the titanium nano sheet/graphene oxide dispersion liquid and spinning are facilitated, the spinnability of a spinning stock solution is improved, and meanwhile, the concentration of the titanium nano sheet/graphene oxide dispersion liquid is conveniently measured.

Preferably, in the step of preparing the titanium nanosheet/graphene oxide dispersion liquid, the mass-to-volume ratio of the mixture of the titanium powder and the graphene oxide to the DMF is 1-10 mg/ml, the ultrasonic time of the pulse probe is 2-12 h, the ultrasonic power of the pulse probe is 200-300W, and the ultrasonic frequency of the pulse probe is set as: ultrasound 5s, interval 5 s. Therefore, the mixture of titanium powder and graphene oxide can be promoted to be well dispersed in DMF through pulse probe ultrasound, and a dispersion liquid with well dispersed titanium nanosheets and graphene oxide is prepared to prepare a spinning solution for subsequent preparation.

Preferably, in the step of preparing the titanium nanosheet/graphene oxide dispersion liquid, after the ultrasonic treatment is finished, the mixed liquid is concentrated by a vacuum rotary evaporation method until the solid content is 10-50 mg/ml;

the vacuum degree of the vacuum rotary evaporation method is 0.05-0.08 MPa, and the temperature of the vacuum rotary evaporation method is 55-65 ℃. The titanium nano sheet/graphene oxide dispersion liquid is prepared through two steps, namely, the titanium nano sheet and the graphene oxide are firstly dispersed at low concentration and then concentrated to reach the high concentration required by spinning, so that the titanium nano sheet and the graphene oxide can be well dispersed in DMF, the conductive requirement of a fiber membrane can be met, the content of a conductive body in the titanium nano sheet/graphene-based fiber membrane can be effectively increased by concentrating the mixed liquid through a vacuum rotary evaporation method, and the conductivity of the fiber membrane is increased.

Preferably, in the spinning step, the mass-to-volume ratio of the carbon black to the titanium nanosheet/graphene oxide dispersion is 50-100 mg/ml;

the time of the three-stage water bath ultrasound is 4-12 hours, the power of the three-stage water bath ultrasound is 250-500W, and the collection is to collect the titanium nano sheet/graphene oxide hybrid porous fiber by adopting a collecting plate. The addition of the carbon black can further improve the conductivity of the titanium nanosheet/graphene-based fibrous membrane, regulate and control the ratio of the carbon black to the titanium nanosheet/graphene oxide dispersion liquid, improve the conductivity of the titanium nanosheet/graphene-based fibrous membrane, avoid the influence of excessive use of the carbon black on the spinnability of a spinning solution, and reduce the flexibility of the titanium nanosheet/graphene-based fibrous membrane. The titanium nanosheets, the graphene oxide and the carbon black are further stripped and dispersed through three-stage water bath ultrasound to prepare a conductive body with a smaller size, so that the conductive body can be uniformly doped into the titanium nanosheets/graphene hybrid porous fibers, and the titanium nanosheets/graphene-based fiber membrane with good flexibility, high conductivity, excellent heat resistance and strong mechanical property is prepared.

Preferably, in the spinning step, the inner diameter of the thin end of the spinning needle head is 0.3mm, the inner diameter of the thick end of the spinning needle head is 0.36mm, the electrostatic spinning voltage is 20-50 KV, and the receiving distance is 10-30 cm. Therefore, through electrostatic spinning by using the spinning needle with the inner diameter increased along the filament outlet direction, the fluid velocity of the spinning stock solution forms sudden drop and generates outward component velocity along the radial direction, so that the titanium nano sheets and the graphene oxide are distributed along the radial direction, and the titanium nano sheets/graphene oxide hybrid porous fiber formed after solidification has a large number of pore-shaped structures distributed along the radial direction, so that the titanium nano sheets/graphene oxide hybrid porous fiber has good radial flexibility and axial elasticity, and the titanium nano sheets/graphene oxide hybrid porous fiber membrane has good flexibility and elasticity in all directions.

Preferably, in the post-treatment step, the titanium nano sheet/graphene oxide hybrid porous fiber membrane is washed by deionized water for 1-3 times, and the titanium nano sheet/graphene oxide hybrid porous fiber membrane is transferred to a vacuum drying oven at 60-85 ℃ for drying for 4-12 hours;

soaking the dried titanium nano sheet/graphene oxide hybrid porous fiber membrane in HI and NaBH₄And hydrazine hydrate and ascorbic acid are reduced to prepare the titanium nano sheet/graphene-based fiber membrane. Residual DMF in the titanium nano sheet/graphene-based fiber membrane is removed through the washing and drying processes, the PAN/titanium nano sheet/graphene oxide hybrid porous fiber membrane is prepared, and the washed and dried PAN/titanium nano sheet/graphene oxide hybrid porous fiber membrane is higher in porosity and larger in specific surface area and flexibility. Finally, the graphene oxide is reduced into reduced graphene oxide through a reduction process, the reduced titanium nano sheet/graphene-based fiber membrane has better environmental stability and heat resistance, and the titanium nano sheet/graphite is effectively prolongedThe service life of the alkenyl fiber membrane.

The titanium nano sheet/graphene-based fiber membrane has the advantages of high porosity, good flexibility, large specific surface area, high conductivity, high electrothermal conversion efficiency, high infrared emissivity, high heat conduction efficiency and the like, and also has obvious sterilization and bacteriostasis effects. When the titanium nano sheet/graphene-based fiber membrane is applied to floor heating, physical therapy or clothes, the titanium nano sheet/graphene-based fiber membrane also has the infrared physical therapy effect. The basic fiber material of the titanium nano sheet/graphene-based fiber membrane is Polyacrylonitrile (PAN), so that the titanium nano sheet/graphene-based fiber membrane has the advantages of high mechanical property, medium-high temperature resistance, difficult aging and the like. When the titanium nano sheet/graphene-based fiber film is applied to a heating device, the titanium nano sheet/graphene-based fiber film has the advantages of uniform heat generation, stable heating performance, high infrared emission performance, medium-high temperature resistance and the like, and has low attenuation rate in long-term use.

Advantages of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or may be learned by practice of embodiments of the invention.

Drawings

In order to more clearly illustrate the contents of the present invention, a detailed description thereof will be given below with reference to the accompanying drawings and specific embodiments.

Fig. 1 is a schematic structural view of a titanium nanosheet/graphene-based drug pillow for hot compress according to one embodiment of the present invention;

fig. 2 is a schematic structural view of a pillow case and a pillow core in the titanium nanosheet/graphene-based thermal compress drug pillow shown in fig. 1;

fig. 3 is a schematic structural diagram of the titanium nanosheet/graphene-based heating film provided by the invention.

Detailed Description

While the following is a description of the preferred embodiments of the present invention, it will be understood by those skilled in the art that various changes and modifications may be made without departing from the spirit and scope of the invention.

As shown in fig. 1-2, a titanium nanosheet/graphene-based drug pillow for hot compress 1 according to one embodiment of the present invention. The titanium nano sheet/graphene-based hot compress drug pillow 1 comprises a pillow case 11 and a pillow core 12, wherein the pillow case 11 is used for accommodating the pillow core 12. In a specific embodiment, a zipper can be further disposed on the pillow case 11, so that the pillow core 12 can be accommodated in the pillow case 11 or taken out of the pillow case 11 through opening and closing of the zipper, the pillow case 11 can be conveniently cleaned, and the pillow core can be replaced according to different requirements.

The pillowcase 11 includes flexible contact layer and titanium nano sheet/graphene based heating film 2, and wherein the flexible contact layer is located the pillowcase outside and is used for contacting the epidermis, and titanium nano sheet/graphene based heating film 2 is located pillowcase 11 inboard and is used for the heat production, and the flexible contact layer covers titanium nano sheet/graphene based heating film 2. In a specific embodiment, the flexible contact layer may be made of a transparent insulating material, such as flexible transparent silicone or PE. In other embodiments, the flexible contact layer may also be a porous woven layer, which also has the function of conducting infrared rays. The pillow core 12 includes a flexible containing bag and heat storage gel, the flexible containing bag is preferably a closed cavity made of flexible resin or rubber, and the flexible containing bag can be deformed correspondingly based on the deformation of the heat storage gel. The heat storage gel is contained in the flexible containing bag, and is preferably a never-cured heat conducting gel, in the embodiment, the heat storage gel is preferably a never-cured heat conducting gel produced by Shenzhen Jinlingda electronics Limited, and in other embodiments, other types of heat conducting gels can be used.

Further, the bottom of the pillow case 11 is provided with a hard base 13, and in this embodiment, the flexible contact layer is connected to the hard base 13 for fixing the bottom of the flexible contact layer. In other embodiments, the flexible contact layer can also be clamped in the hard base 13, with the same effect.

Further, the titanium nanosheet/graphene-based hot compress medical pillow 1 may further include a patch including a medical adhesive tape and a medical cotton pad attached to an adhesive surface of the medical adhesive tape. When in use, the medicine spray can be directly sprayed on the medical cotton pad or the medicine is coated on the medical cotton pad, and then the medical cotton pad is covered on the part to be hot compressed and is fixed by the medical adhesive tape. And then covering the titanium nano sheet/graphene-based hot compress medicine pillow 1 on the medicine patch, and electrifying for hot compress. In other embodiments, the medical cotton pad can be replaced by a sponge medicine bag, the ground traditional Chinese medicinal materials are filled in the sponge medicine bag and soaked in water, and the water absorption and ventilation effects of the sponge medicine bag can effectively promote the release of the active ingredients of the medicine through a steam carrier and act on the epidermis.

Further, the titanium nanosheet/graphene-based heating film 2 includes a first transparent insulating layer 21, an electrode 22, a second transparent insulating layer 23, and a titanium nanosheet/graphene-based fiber film 24. The first transparent insulating layer 21 covers the upper surface of the titanium nanosheet/graphene-based fiber membrane 24, and the second transparent insulating layer 23 covers the lower surface of the titanium nanosheet/graphene-based fiber membrane 24, so that the titanium nanosheet/graphene-based fiber membrane 24 is isolated in a closed insulating space, and electric leakage is prevented when the titanium nanosheet/graphene-based fiber membrane 24 generates heat when electricity is conducted. One end of the electrode 22 is electrically connected to the titanium nanosheet/graphene-based fiber membrane 24, and specifically, the electrode 22 may penetrate through the titanium nanosheet/graphene-based fiber membrane 24, or the electrode 22 may be pressed by the titanium nanosheet/graphene-based fiber membrane 24. The other end of the electrode 22 extends out of the first transparent insulating layer 21 (or extends out of the second transparent insulating layer 23, and also has the function of electrically connecting the titanium nanosheet/graphene-based fiber membrane 24 and the function of waterproofing), that is, the electrode 22 extends to the outside from the inside of the insulating space between the first transparent insulating layer 21 and the second transparent insulating layer 23, so that the titanium nanosheet/graphene-based fiber membrane 24 is electrically conducted with an external power supply. In particular, the connection to an external power source may be through a waterproof plug/socket.

Further, the material of the first transparent insulating layer 21 and the second transparent insulating layer 23 may be PET or PI.

Further, a transparent heat conduction layer 25 is further arranged between the second transparent insulation layer 23 and the titanium nanosheet/graphene-based fiber film 24. The transparent heat conduction layer 25 may be a transparent heat conduction glue or a flexible water bag (for example, water contained in a transparent film), one of which allows light to pass through without affecting the infrared physiotherapy effect of the titanium nanosheet/graphene-based fiber membrane 24; the transparent heat conducting layers 25 of the two layers have larger specific heat capacity generally and can play a certain heat storage role. When the pillowcase is assembled, the second transparent insulating layer 23 of the titanium nano sheet/graphene-based heating film 2 is connected with the inner side of the flexible contact layer, so that the pillowcase has certain heat storage and thermal stability effects, and rapid temperature rise and fall changes caused by the fact that the titanium nano sheet/graphene-based fiber film 24 is directly connected with the flexible contact layer are prevented.

Further, a waterproof adhesive layer 26 is further disposed between the first transparent insulating layer 21 and the second transparent insulating layer 23, and the waterproof adhesive layer 26 is respectively adhered to the first transparent insulating layer 21 and the second transparent insulating layer 23 to form a closed cavity. The titanium nano sheet/graphene-based fiber membrane 24 and the transparent heat conduction layer 25 are arranged in the closed cavity, and the electrode 22 extends from the inside of the closed cavity to the outside of the closed cavity.

Further, the electrode 22 includes a transverse arm and a vertical arm which are connected perpendicularly to each other, the transverse arm extends out of the closed cavity from the transparent heat conduction layer, and the vertical arm extends out of the transparent heat conduction layer 25 longitudinally and is electrically connected with the titanium nano-sheet/graphene-based fiber membrane 24. In other embodiments, the electrode 22 may have other structures, and only the titanium nanosheet/graphene-based fiber membrane 24 is ensured to be electrically conducted to the outside through the electrode 22.

The following describes in detail the preparation method of the titanium nanosheet/graphene-based fibrous membrane and the prepared titanium nanosheet/graphene-based fibrous membrane by using specific examples, including examples and comparative examples (hereinafter referred to as "comparative examples"), which are set with reference to parameter ranges of example 4 for discussing the influence of each parameter on the performance of the titanium nanosheet/graphene-based fibrous membrane.

A preparation method of a titanium nanosheet/graphene-based fiber membrane comprises the following steps:

preparing a pre-stripping dispersion liquid of titanium powder: titanium powder was provided and added to the pre-peeling dispersion, the type of pre-peeling dispersion (the pre-peeling dispersion in examples 7 and 8 was a mixed pre-peeling dispersion with a mass ratio of deionized water to isopropyl alcohol of 1: 1) and the concentration of titanium powder in the pre-peeling dispersion are shown in table 1. The pre-stripped dispersion added with titanium powder is subjected to primary water bath ultrasound, wherein the temperature (the primary water bath ultrasound is referred to as "one-pass" for short, the temperature here is a temperature value set by a water bath kettle, and the actual water bath temperature has a certain fluctuation), power and ultrasound time of the primary water bath ultrasound are shown in table 1. And after the ultrasonic treatment is finished, centrifuging the pre-stripping dispersion liquid added with the titanium powder, and collecting supernatant to prepare the pre-stripping dispersion liquid of the titanium powder, wherein the centrifugal rotating speed and the centrifugal time are shown in the table 1.

TABLE 1 parameters of the Pre-strip Dispersion step for preparing titanium powder

Preparing a mixture of titanium powder and graphene oxide: to the previously prepared pre-exfoliated dispersion of titanium powder, graphene oxide was added, where the ratio of the mass of graphene oxide to the mass of titanium powder in the supernatant (where titanium powder in the supernatant refers to titanium powder dispersed in the supernatant, and the mass of titanium powder in the supernatant can be obtained by subtracting the mass of titanium powder centrifugally precipitated in the pre-exfoliation step from the mass of total titanium powder supplied) is seen in table 2. After the addition of graphene oxide, the pre-exfoliated dispersion liquid of graphene oxide and titanium powder was transferred to a water bath kettle for secondary water bath ultrasound, wherein the temperature (referred to as "secondary ultrasound" for short) of the secondary water bath ultrasound, the power and the ultrasound time are shown in table 2. And after the secondary water bath ultrasound treatment is finished, centrifuging the pre-stripping dispersion liquid of the titanium powder added with the graphene oxide, and collecting a bottom layer mixture, wherein the centrifugal rotating speed and the centrifugal time are shown in table 2. And dispersing the bottom layer mixture in water, oscillating and washing the bottom layer mixture, transferring the washed mixture into a vacuum rotary evaporator for rotary evaporation to remove the pre-stripping dispersion liquid, transferring the rotary-evaporated mixture into a vacuum drying oven for drying, wherein the temperature and the drying time of the drying oven are shown in table 2.

TABLE 2 parameters of the procedure for preparing the mixture of titanium powder and graphene oxide

Preparing a titanium nanosheet/graphene oxide dispersion liquid: a mixture of titanium powder and graphene oxide was dispersed in DMF (N, N-dimethylformamide) to prepare a mixed solution, wherein the concentration of the mixture of titanium powder and graphene oxide (referred to as "mixture concentration") is shown in table 3. Performing ultrasound on a DMF solution of a mixture of titanium powder and graphene oxide by using a pulse probe, wherein the frequency of the pulse probe ultrasound is set as follows: ultrasound 5s, interval 5s, wherein the temperature of the pulse probe ultrasound (abbreviated as "pulse ultrasound"), the power of the pulse probe ultrasound, and the time of the pulse probe ultrasound are shown in table 3. After the pulse probe finishes the ultrasonic treatment, the mixed solution is concentrated by a vacuum rotary evaporation method, and the specific temperature and the vacuum degree of the vacuum rotary evaporation method (referred to as rotary evaporation for short) are shown in table 3. The concentration of the solid content of the concentrated mixture (here, the solid content can be measured by high-speed centrifugation, drying, etc.) is shown in table 3. And concentrating to obtain the titanium nano sheet/graphene oxide dispersion liquid.

TABLE 3 parameters of the procedure for preparing titanium nanoplate/graphene oxide dispersions

Spinning: adding carbon black and PAN powder into the prepared titanium nanosheet/graphene oxide dispersion liquid, specifically, referring to table 4, the mass-to-volume ratio of the carbon black to the titanium nanosheet/graphene oxide dispersion liquid (the ratio of the mass of the carbon black to the volume of the titanium nanosheet/graphene oxide dispersion liquid, referred to as "carbon black concentration") and the mass fraction of PAN after the PAN powder is added (the mass fraction of PAN in the whole system). Stirring the titanium nanosheet/graphene oxide dispersion liquid until the carbon black and the PAN powder are uniformly dispersed, and then performing three-stage water bath ultrasound (referred to as "three-stage ultrasound"), wherein specific stirring speed, stirring time, temperature of the three-stage water bath ultrasound, power of the three-stage water bath ultrasound and time of the three-stage water bath ultrasound are shown in table 4. After the ultrasound is finished, the spinning solution is directly used for electrostatic spinning, a spinning needle with the inner diameter increased along the yarn outlet direction is used, the inner diameter of the thin end of the spinning needle is 0.3mm, the inner diameter of the thick end of the spinning needle is 0.36mm, the receiving distance is 20cm, and the voltage of the specific electrostatic spinning is shown in table 4.

TABLE 4 parameters of the spinning step

And (3) post-treatment: and (3) washing the titanium nanosheet/graphene oxide hybrid porous fiber membrane by using deionized water, drying in vacuum, and repeating the washing and drying processes once. Soaking the washed titanium nanosheet/graphene oxide hybrid porous fiber membrane in a reducing agent for reduction, wherein the specific type of the reducing agent can be HI or NaBH₄Any of hydrazine hydrate and ascorbic acid, the kind of reducing agent in specific examples, reduction time are shown in table 5. And repeating the washing and drying processes for 1-2 times after reduction to obtain the titanium nanosheet/graphene-based fibrous membrane.

TABLE 5 parameters of the post-treatment step

Comparative example 1

Comparative example 1 the setup was made with reference to example 4, comparative example 1 differing from example 4 only in that: the steps of preparing titanium nano sheets, and carrying out secondary water bath ultrasound, pulse probe ultrasound, spinning and post-treatment on the titanium nano sheets and the graphene oxide together are omitted.

A preparation method of a graphene-based fiber membrane comprises the following steps:

preparing a mixture of graphene oxide: adding graphene oxide to the isopropanol pre-stripping dispersion liquid, wherein the ratio of the mass of the graphene oxide to the volume of the isopropanol is 100 mg/ml. After the addition of graphene oxide, the pre-exfoliated dispersion of graphene oxide was transferred to a water bath kettle for secondary water bath ultrasound, wherein the temperature (secondary water bath ultrasound is simply referred to as "secondary ultrasound", and the temperature here is also a temperature value set for the water bath kettle), power, and ultrasound time of the secondary water bath ultrasound were the same as those of example 4. And after the secondary water bath ultrasound is finished, centrifuging the pre-stripping dispersion liquid added with the graphene oxide, and collecting a bottom layer mixture, wherein the centrifugal speed and the centrifugal time are the same as those in the embodiment 4. And dispersing the bottom layer mixture in water, oscillating and washing the bottom layer mixture, transferring the washed mixture into a vacuum rotary evaporator for rotary evaporation to remove the pre-stripping dispersion, transferring the rotary evaporated mixture into a vacuum drying oven for drying, wherein the temperature and the drying time of the drying oven are the same as those of the example 4.

Preparing a graphene oxide dispersion liquid: similarly to example 4, the mixture of graphene oxide prepared above was dispersed in DMF to prepare a mixed solution, and then subjected to pulse probe ultrasound and concentration in this order to prepare a graphene oxide dispersion.

Spinning: in the same manner as in example 4, carbon black and PAN powder were added to the graphene oxide dispersion liquid prepared above, specifically, the mass-to-volume ratio of carbon black to graphene oxide dispersion liquid was 80mg/ml, and the mass fraction of PAN was 9%, and the processes of stirring, three-stage water bath ultrasound, spinning, and the like were sequentially performed to prepare a graphene-based fiber membrane.

And (3) post-treatment: refer to example 4.

Comparative example 2

preparing a pre-stripping dispersion liquid of titanium powder: refer to example 4.

Preparing a mixture of titanium powder and graphene oxide: to the previously prepared pre-exfoliated dispersion of titanium powder, graphene oxide was added, wherein the ratio of the mass of graphene oxide to the mass of titanium powder in the supernatant was referred to example 4. The pre-exfoliated dispersion of titanium powder with added graphene oxide was centrifuged, and the bottom layer mixture was collected, where the centrifugation speed, the centrifugation time, and the like were as in example 4. The bottom layer mixture was dispersed in water, the bottom layer mixture was washed by shaking, the washed mixture was transferred to a vacuum rotary evaporator to remove the pre-peeling dispersion by rotary evaporation, and the rotary evaporated mixture was transferred to a vacuum drying oven to be dried, the temperature and drying time of the oven were as in example 4.

Preparing a titanium nanosheet/graphene oxide dispersion liquid: refer to example 4.

Spinning: refer to example 4.

And (3) post-treatment: refer to example 4.

Comparative example 3

Preparing a mixture of titanium powder and graphene oxide: refer to example 4.

Preparing a titanium nanosheet/graphene oxide dispersion liquid: a mixture of titanium powder and graphene oxide was dispersed in DMF to prepare a mixed solution, wherein the concentration of the mixture of titanium powder and graphene oxide was as in example 4. The mixed solution was concentrated by a vacuum rotary evaporation method, and specifically, the temperature, the degree of vacuum, and the like of the vacuum rotary evaporation method (simply referred to as "rotary evaporation") were as in example 4. The solid content concentration of the concentrated mixture was as in example 4. And concentrating to obtain the titanium nano sheet/graphene oxide dispersion liquid.

Spinning: refer to example 4.

And (3) post-treatment: refer to example 4.

Effects of the embodiment

(1) Antibacterial testing

Taking the titanium nanosheet/graphene-based fiber membrane or the graphene-based fiber membrane prepared in the examples 1 to 8 and the comparative examples 1 to 3, cutting the fiber membrane with the length and the width of 20cm and the thickness of about 0.5mm by a blade, and inserting electrodes at two ends of the fiber membrane for electrifying and generating heat and carrying out an antibacterial test. The test method is as follows: the culture solution (rejuvenated) of model strains (escherichia coli, candida albicans, salmonella typhimurium, staphylococcus aureus) was spotted by means of an inoculating needle onto petri dishes (containing conventional solid medium for bacterial culture), each petri dish was inoculated with a single strain 10 times and each strain 200 times (divided into 20 dishes). After inoculation, all the culture dishes are divided into two groups and respectively placed in two culture chambers for simulating living environment. One of them is the laboratory group culture room, is provided with a plurality of aforementioned fibrous membranes in the laboratory group culture room and circular telegram heat production, and the culture dish is 5 ~ 30cm apart from the fibrous membrane, and the laboratory group culture room is by fibrous membrane heat production energy supply, and the temperature control in the culture room is about 37 ℃, and another culture room is the control group culture room, and the temperature that sets up the control group culture room equally is 37 ℃, is supplied heat by the air conditioner, and statistics laboratory group bacterial colony growth condition after 12h all cultivateed in laboratory group culture room and control group culture room. The average colony size (diameter of colony) of each bacterial colony in the control group is calculated, the average colony size is used as a reference value, the colony with the diameter less than or equal to half of the reference value in the experimental group is marked as bacteriostasis, the colony which does not grow at the point of sample application is marked as sterilization, and the colony with the diameter more than or equal to half of the reference value is marked as normal growth. The results of the statistical percentages are shown in Table 6.

TABLE 6 antimicrobial test results

From the results in table 6, it is clear that the titanium nanosheet/graphene-based fiber membranes prepared in examples 1-8 all showed more than 98% of bactericidal rate against escherichia coli, candida albicans and salmonella typhimurium and more than 89% of bactericidal rate against staphylococcus aureus after being electrified. After the titanium nanosheets and the graphene are mutually doped, the titanium nanosheets and the graphene can be promoted to be directly contacted and doped, the titanium nanosheets or the graphene are prevented from being stacked or partially gathered, the spinnability of a single two-dimensional material spinning solution can be improved, the titanium nanosheets and the graphene are mixed with dispersed carbon black powder, the mutually doped titanium nanosheets and the graphene are directly adsorbed on the carbon black powder, a stable conductive network structure of titanium nanosheets-graphene-carbon black particles can be formed, meanwhile, the titanium nanosheets or graphene layers are prevented from being stacked mutually or easily broken (partially broken) under the action of external force, the number of conductive network paths is increased, the resistance is reduced, the structure of a conductive network is perfected, and the conductive performance and the long-term stability of the titanium nanosheets/graphene-based fiber film are improved. After the titanium nanosheet/graphene-based fiber membrane is electrified, the surface area can be increased by virtue of a large number of void structures existing on the surface of the fiber membrane, so that the doped titanium nanosheet-graphene-carbon black particles are favorable for releasing a large number of infrared rays, and the sterilization effect is achieved. In addition, by means of carrier transmission between the titanium nanosheets and the graphene sheet layers, a small amount of active oxygen free radicals can be generated at the heterojunction between the titanium nanosheets and the graphene sheet layers, and the effects of assisting sterilization and cleaning surfaces are achieved.

In contrast, the graphene-based fiber membrane prepared in comparative example 1 has a sterilization rate of 76% for escherichia coli, candida albicans, and salmonella typhimurium and 52% for staphylococcus aureus after being electrified. The reason may be related to that the graphene-based fiber film prepared in comparative example 1 has a relatively low infrared emissivity, and the graphene-based fiber film prepared in comparative example 1 only contains electric conductors such as graphene and carbon black, and lacks the auxiliary effect of titanium nanosheets, so that the graphene-based fiber film has a relatively low infrared emissivity and cannot generate active radicals. The sterilization rate of the titanium nanosheet/graphene-based fiber membrane prepared in the comparative example 2 on escherichia coli, candida albicans and salmonella typhimurium after being electrified reaches 96%, and the sterilization rate on staphylococcus aureus only reaches 68%. Based on the fact that sufficient water bath ultrasound is not performed in comparative example 2, graphene oxide is directly added into the pre-stripping dispersion liquid of titanium powder, the titanium nanosheet can not be stripped with the assistance of graphene, and an effective titanium nanosheet/graphene mutual doping structure can not be formed, so that the prepared titanium nanosheet/graphene-based fiber film active conductor has the defects of nonuniform dispersion, low infrared emissivity, low yield of active free radicals, low antibacterial efficiency and the like. The sterilization rate of the titanium nanosheet/graphene-based fiber membrane prepared in the comparative example 3 on escherichia coli, candida albicans and salmonella typhimurium after being electrified reaches 91%, and the sterilization rate on staphylococcus aureus only reaches 60%. As with comparative example 2, based on that pulse probe ultrasound is not performed in comparative example 3, titanium nanosheets cannot be peeled off with the aid of graphene, and an effective titanium nanosheet/graphene mutual doping structure cannot be formed, resulting in defects of uneven dispersion, low infrared emissivity, low yield of active free radicals, low antibacterial efficiency and the like of the prepared titanium nanosheet/graphene-based fiber film active conductor.

(2) Infrared wavelength and normal emissivity testing

The titanium nano sheet/graphene-based fiber film or the graphene-based fiber film prepared in the examples 1 to 8 and the comparative examples 1 to 3 is used for testing infrared wavelength and normal emissivity according to the standard CAS 115-. The calculation data show that the titanium nanosheet/graphene-based fiber membranes prepared in the examples 1-8 can release far infrared rays of 3-20 micrometers, the far infrared ray ratio of the far infrared rays in the 4-16 micrometer wave band exceeds 87%, the normal emissivity exceeds 90%, and the increase of the microcirculation blood flow of animal experiments exceeds 67%. The electrothermal conversion rate is up to more than 99%, and the visible heating film can be widely applied to the fields of floor heating, physical therapy, clothes and the like. In contrast, the far infrared ray content of the titanium nanosheet/graphene-based fibrous membrane or the graphene-based fibrous membrane prepared in comparative examples 1-3 in the wavelength range of 4-16 microns is lower than 73% (61% for the graphene-based fibrous membrane in example 1), the normal emissivity is lower than 80% (65% for the graphene-based fibrous membrane in example 1), and the increase in the animal experimental microcirculation blood flow is lower than 65% (52% for the graphene-based fibrous membrane in example 1). The reason for this is probably related to the stable circuit network structure formed by the titanium nano-sheet/graphene-based fiber film, i.e. the titanium nano-sheet and the graphene are doped with each other, so that the uniform distribution of the electric conductor is increased, the resistance value of the fiber film is reduced, the uniformity of the spinning fiber is improved, and the like.

(3) Stability and leakage safety testing

The titanium nanosheet/graphene-based fiber film or the graphene-based fiber film prepared in the examples 1 to 8 and the comparative examples 1 to 3 is cut into a fiber film with the length, the width and the thickness of 20cm and about 0.5mm by a blade, electrodes are inserted into two ends of the fiber film, a mains supply is connected to the two ends of the fiber film, the titanium nanosheet/graphene-based fiber film or the graphene-based fiber film generates heat, and the uniformity of heating temperature is assessed by an infrared imaging instrument. The heating temperature difference of any two positions of each fiber membrane is less than or equal to 5 ℃ and more than 2.5 ℃, the fiber membrane is marked as qualified, the fiber membrane is less than or equal to 2.5 ℃, the fiber membrane is marked as excellent, the fiber membrane is marked as unqualified when the temperature is more than 5 ℃, and the statistical result is shown in table 7.

And continuously electrifying the titanium nanosheet/graphene-based fiber membrane or the graphene-based fiber membrane for heat generation uniformity test to generate heat for heat generation stability test. The statistical method, the heat production is carried out for 90000 hours by continuous electrification, and compared with the beginning of the heat production, the disqualification is marked when the heat production power is reduced by more than 2.5 percent after the 90000 hours of the heat production; the heat production power is reduced by less than or equal to 2.5 percent and is greater than 1 percent, and the product is marked as qualified; the decrease of heat generation power less than or equal to 1% is marked as excellent, and the statistical results are shown in Table 7.

The two surfaces of the titanium nano sheet/graphene-based fiber membrane or the graphene-based fiber membrane are compounded by hot pressing through an insulating polymer membrane (such as PET or PI), and after 90000 hours of electricity and heat generation, the electricity and the heat generation are continued to be carried out for a leakage safety test. The specific test method was measured with reference to GB/T12113 (idt IEC 60990). The leakage current is less than or equal to 0.05mA and greater than 0.02mA and is marked as qualified; the leakage current is less than 0.02mA and is marked as excellent; the leakage current is greater than 0.05mA and is marked as unqualified. The measurement results are shown in Table 7.

TABLE 7 stability and leakage safety test results

As can be seen from the results in table 7, most of the titanium nanosheet/graphene-based fibrous membranes prepared in examples 1 to 8 showed excellent test results in the temperature uniformity test, the heat generation stability test and the leakage safety test, and only example 1 showed a qualified test result, which indicates that the titanium nanosheet/graphene-based fibrous membranes prepared in examples 1 to 8 of the present invention have excellent heat generation uniformity, heat generation stability and leakage safety. The fiber film prepared in the comparative example 1 is unqualified in temperature uniformity test and heat generation stability test, and the fiber film prepared in the comparative example 3 is unqualified in temperature uniformity test and heat generation stability test, and may be related to uneven dispersion of the electric conductor, unstable electric conductor and easy aging under the condition of electrifying.

(4) Sheet resistance test

Taking the titanium nanosheet/graphene-based fiber film or the graphene-based fiber film prepared in the examples 1 to 8 and the comparative examples 1 to 3, cutting the fiber film with the length, the width and the thickness of 20cm and about 0.5mm by a blade, inserting electrodes at two ends of the fiber film, connecting commercial power to the two ends of the fiber film to supply heat to the titanium nanosheet/graphene-based fiber film or the graphene-based fiber film, and carrying out a sheet resistance test. The test method is as follows: and continuously electrifying the titanium nanosheet/graphene-based fibrous membrane or the graphene-based fibrous membrane to generate heat, and testing the sheet resistance value of the graphene fibrous membrane once every other week (W). The test results are shown in Table 8.

TABLE 8 sheet resistance test results

As can be seen from the results in table 8, the sheet resistance of the titanium nanosheet/graphene-based fiber membranes prepared in examples 1-8 is small (no more than 365 Ω/□), the variation of the sheet resistance is not obvious around when heat is generated by continuous energization, and the sheet resistance and the stability thereof are both suitable for being applied to electric heating equipment and can be widely applied to the fields of floor heating, physiotherapy, clothing and the like. In contrast, the titanium nanosheet/graphene-based fibrous membrane or graphene-based fibrous membrane prepared in comparative examples 1-3 has a large initial sheet resistance (the sheet resistance value after stabilization is still large and may be related to instability and easy aging of the fibrous membrane component under the condition of electrification and heat generation), a large change in sheet resistance value, a significant decrease in heat generation power, and is not suitable for being applied to electric heating equipment. The reason for this is probably that the dispersion of the electric conductor such as titanium nanosheets and graphene is not uniform.

(5) Heat resistance and tensile Property test

The titanium nanosheet/graphene-based fiber membrane or the graphene-based fiber membrane prepared in the examples 1 to 8 and the comparative examples 1 to 3 is cut into a fiber membrane with the length, the width and the thickness of 20cm and about 0.5mm by a blade, and a thermal deformation temperature test is carried out according to GB/T1634-material 2004, wherein the heating rate is 120 ℃/h. The test results are shown in Table 9.

The prepared titanium nano sheet/graphene-based fiber membrane or graphene-based fiber membrane is taken to be subjected to tensile resistance test on a universal tester (the test standard is GB/T1040-.

TABLE 9 Heat resistance test results

From the results in table 9, it can be seen that the thermal deformation temperatures of the titanium nanosheet/graphene-based fibrous membrane or the graphene-based fibrous membrane prepared in examples 1 to 8 and comparative examples 1 to 3 both exceed 108 ℃, and the fibrous membrane can meet the heat generation requirements of low-temperature and medium-high-temperature heat-generating equipment. The heat distortion temperature is related to the PAN content in the titanium nanosheet/graphene-based fibrous membrane or the graphene-based fibrous membrane. Within a certain range, the thermal deformation temperature of the titanium nanosheet/graphene-based fibrous membrane or the graphene-based fibrous membrane is increased along with the increase of the PAN content, and the thermal deformation temperature is also increased due to the good dispersion of the titanium nanosheet and the graphene; however, too high a PAN content results in a dope that is too viscous and affects spinnability and fiber porosity.

From the results in table 9, it is known that the tensile strength of the titanium nanosheet/graphene-based fiber film or the graphene-based fiber film prepared in examples 1 to 8 and comparative examples 1 to 3 exceeds 25MPa, and the requirements of flexibility, wear resistance and tensile resistance of common heat-generating equipment can be met. The tensile strength of the fiber membrane is related to the content of PAN (polyacrylonitrile), within a certain range, the tensile strength of the titanium nanosheet/graphene-based fiber membrane or the graphene-based fiber membrane is improved along with the improvement of the content of PAN, and the good dispersion of the titanium nanosheet and graphene is also beneficial to improving the tensile strength.

The above-mentioned embodiments only express several embodiments of the present invention, and the description thereof is more specific and detailed, but not construed as limiting the scope of the present invention. It should be noted that, for a person skilled in the art, several variations and modifications can be made without departing from the inventive concept, which falls within the scope of the present invention. Therefore, the protection scope of the present patent shall be subject to the appended claims.

Claims

1. The titanium nano sheet/graphene-based hot compress medicine pillow is characterized by comprising a pillow case and a pillow core, wherein the pillow case comprises a flexible contact layer and a titanium nano sheet/graphene-based heating film, the flexible contact layer is arranged on the outer side of the pillow case, the titanium nano sheet/graphene-based heating film is arranged on the inner side of the pillow case, and the flexible contact layer covers the titanium nano sheet/graphene-based heating film; the pillow core comprises a flexible accommodating bag and heat storage gel, and the heat storage gel is accommodated in the flexible accommodating bag;

2. The titanium nanosheet/graphene-based drug pillow for hot compress of claim 1, wherein a hard base is further disposed at the bottom of the pillowcase, and the flexible contact layer is connected with or clamped in the hard base.

3. The titanium nanoplate/graphene-based drug pillow for hot compress of claim 1, wherein the flexible contact layer is made of a transparent insulating material, the flexible containing bag is made of a flexible resin or rubber, and the heat storage gel is a never-cured heat conducting gel.

4. The titanium nanoplate/graphene-based drug pillow for hot compress of claim 1, wherein a transparent heat conducting layer is further disposed between the second transparent insulating layer and the titanium nanoplate/graphene-based fiber membrane, and the second transparent insulating layer is connected to the flexible contact layer.

5. The titanium nanoplate/graphene-based drug pillow for hot compress of claim 4, wherein a waterproof adhesive layer is further disposed between the first transparent insulating layer and the second transparent insulating layer, and the waterproof adhesive layer is respectively adhered to the first transparent insulating layer and the second transparent insulating layer to form a closed cavity;

the titanium nano sheet/graphene-based fiber membrane and the transparent heat conduction layer are arranged in the closed cavity, and the electrodes extend out of the closed cavity.

6. The titanium nanoplatelet/graphene-based drug pillow for thermal compress of claim 5 wherein the electrodes comprise interconnected transverse arms extending from the transparent thermally conductive layer out of the closed cavity and vertical arms extending from the transparent thermally conductive layer and electrically connected to the titanium nanoplatelet/graphene-based fiber membrane.

7. The titanium nano sheet/graphene-based heating film according to claim 1, wherein in the step of preparing the titanium nano sheet/graphene oxide dispersion liquid, the mass-to-volume ratio of the mixture of the titanium powder and the graphene oxide to DMF is 1-10 mg/ml, the time of the pulse probe ultrasound is 2-12 h, the power of the pulse probe ultrasound is 200-300W, and the frequency of the pulse probe ultrasound is set as: ultrasound 5s, interval 5 s.

8. The titanium nano sheet/graphene-based heating film as claimed in claim 1, wherein in the step of preparing the titanium nano sheet/graphene oxide dispersion liquid, after the ultrasonic treatment is finished, the mixed liquid is concentrated by a vacuum rotary evaporation method until the concentration of the solid content is 10-50 mg/ml;

the vacuum degree of the vacuum rotary evaporation method is 0.05-0.08 MPa, and the temperature of the vacuum rotary evaporation method is 55-65 ℃.

9. The titanium nanoplate/graphene-based heating film according to claim 1, wherein in the spinning step, the mass-to-volume ratio of the carbon black to the titanium nanoplate/graphene oxide dispersion is 50 to 100 mg/ml;

the time of the three-stage water bath ultrasound is 4-12 hours, the power of the three-stage water bath ultrasound is 250-500W, and the collection is to collect the titanium nano sheet/graphene oxide hybrid porous fiber by adopting a collecting plate.

10. The titanium nano sheet/graphene-based heating film as claimed in claim 1, wherein in the post-treatment step, the titanium nano sheet/graphene oxide hybrid porous fiber film is washed with deionized water for 1-3 times, and the titanium nano sheet/graphene oxide hybrid porous fiber film is transferred to a vacuum drying oven at 60-85 ℃ for drying for 4-12 h;

and (3) soaking the dried titanium nanosheet/graphene oxide hybrid porous fiber membrane in any one of HI, NaBH4, hydrazine hydrate and ascorbic acid for reduction to obtain the titanium nanosheet/graphene-based fiber membrane.