CN111978445A - Low cis-polybutadiene rubber, preparation method and application thereof, aromatic vinyl resin and preparation method thereof - Google Patents

Low cis-polybutadiene rubber, preparation method and application thereof, aromatic vinyl resin and preparation method thereof Download PDF

Info

Publication number
CN111978445A
CN111978445A CN201910425474.3A CN201910425474A CN111978445A CN 111978445 A CN111978445 A CN 111978445A CN 201910425474 A CN201910425474 A CN 201910425474A CN 111978445 A CN111978445 A CN 111978445A
Authority
CN
China
Prior art keywords
molecular weight
low
weight component
polybutadiene rubber
cis
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910425474.3A
Other languages
Chinese (zh)
Other versions
CN111978445B (en
Inventor
李建成
徐林
王雪
赵姜维
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sinopec Beijing Research Institute of Chemical Industry
China Petroleum and Chemical Corp
Original Assignee
Sinopec Beijing Research Institute of Chemical Industry
China Petroleum and Chemical Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sinopec Beijing Research Institute of Chemical Industry, China Petroleum and Chemical Corp filed Critical Sinopec Beijing Research Institute of Chemical Industry
Priority to CN201910425474.3A priority Critical patent/CN111978445B/en
Publication of CN111978445A publication Critical patent/CN111978445A/en
Application granted granted Critical
Publication of CN111978445B publication Critical patent/CN111978445B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a low cis-polybutadiene rubber and a preparation method thereof, and an aromatic vinyl resin using the rubber as a toughening agent and a preparation method thereof. The preparation method of the low cis-polybutadiene rubber comprises the steps of polymerizing 1, 3-butadiene in an organic solvent in the presence of an organic lithium initiator and a structure regulator, contacting the obtained polymerization solution with a coupling agent to perform coupling reaction, wherein the coupling agent is a trifunctional coupling agent, and the molar weight of the coupling agent is nCThe molar amount of the organolithium initiator is nI，(2.1×nI)≥(nC×3)＞nI. The preparation method adopts a one-step coupling reactionTo obtain a low cis-polybutadiene rubber containing a high molecular weight component, a medium molecular weight component and a low molecular weight component, which is used as a toughening agent for an aromatic vinyl resin to impart improved impact resistance and good gloss to the aromatic vinyl resin.

Description

Low cis-polybutadiene rubber, preparation method and application thereof, aromatic vinyl resin and preparation method thereof
Technical Field
The invention relates to a low cis-polybutadiene rubber, a preparation method and application thereof, and also relates to an aromatic vinyl resin using the low cis-polybutadiene rubber as a toughening agent and a preparation method thereof.
Background
Conventional aromatic vinyl resins, for example: in the preparation of high impact polystyrene resin (HIPS resin), the rubber conventionally selected as the toughening agent may be low cis-polybutadiene rubber, high cis-polybutadiene rubber, butadiene-isoprene copolymer, solution-polymerized styrene-butadiene rubber, styrene-butadiene-styrene copolymer, and particularly, low cis-polybutadiene rubber and high cis-polybutadiene rubber are the most preferable. For low-temperature toughness resin, low cis-polybutadiene rubber is generally selected for toughening.
The molecular weight and the distribution of the toughened rubber have obvious influence on the impact resistance of the continuous body HIPS resin, and generally, the rubber molecular weight is too small, so that the toughening effect is poor; the rubber particle size is too concentrated, and the glossiness and the impact resistance of the resin are poor. In the selection of the toughening agent, rubbers with different particle sizes need to be matched, so that the rubbers with different particle sizes act synergistically to realize the balance of glossiness and impact resistance.
The matching of multistage particle sizes of the same rubber is difficult to realize, and the matching can be realized by compounding different types of rubbers, but the polymerization process is more complicated. The rubber with different particle diameters can also be compounded by using coupling agents with different functional groups, and the four-functional group coupling agent and the bifunctional group coupling agent are usually compounded; the metering accuracy and concentration of the coupling agent during compounding are difficult to ensure, and meanwhile, the reactivity of different coupling agents is inconsistent, so that the stability of the product is poor.
Therefore, there is still a need to develop a toughening agent suitable as an aromatic vinyl resin so that the aromatic vinyl resin achieves a balance of gloss and impact properties.
Disclosure of Invention
The invention aims to overcome the technical problem that the existing aromatic vinyl resin toughening agent is difficult to realize multistage particle size matching, and provides a low cis-polybutadiene rubber and a preparation method thereof.
According to a first aspect of the present invention, there is provided a low-cis polybutadiene rubber comprising a coupling center atom, a high molecular weight component having a number average molecular weight of 210,000-360,000, a medium molecular weight component having a number average molecular weight of 150,000-250,000, and a low molecular weight component having a number average molecular weight of 80,000-120,000, the content of the high molecular weight component being 4 to 55% by weight, the content of the medium molecular weight component being 25 to 50% by weight, and the content of the low molecular weight component being 5 to 70% by weight, based on the total amount of the low-cis polybutadiene rubber.
According to a second aspect of the present invention, there is provided a process for preparing a low cis-polybutadiene rubber, comprising the steps of:
(1) under the condition of anionic polymerization, in the presence of an organic lithium initiator and a structure regulator, polymerizing 1, 3-butadiene in an organic solvent to obtain a polymerization solution containing polybutadiene;
(2) contacting the polymerization solution with a coupling agent to carry out coupling reaction to obtain a coupling polymer solution, wherein the coupling agent is one or more than two of trifunctional coupling agents, and the molar weight n of the coupling agentCThe molar weight of the organic lithium initiator is nI，(2.1×nI)≥(nC×3)＞nI。
According to a third aspect of the present invention, there is provided a low-cis polybutadiene rubber prepared by the preparation process according to the second aspect of the present invention.
According to a fourth aspect of the present invention, there is provided the use of a low-cis polybutadiene rubber according to the first or third aspect of the present invention as an aromatic vinyl resin toughening agent.
According to a fifth aspect of the present invention, there is provided an aromatic vinyl resin comprising an aromatic vinyl base resin and a toughening agent, wherein the toughening agent is the low-cis polybutadiene rubber of the first or third aspect of the present invention.
According to a sixth aspect of the present invention, there is provided a method for producing an aromatic vinyl resin, the method comprising: polymerizing an aromatic vinyl monomer in the presence of a toughening agent, wherein the toughening agent is the low-cis polybutadiene rubber of the first or third aspect of the present invention.
The low cis-polybutadiene rubber according to the present invention contains a coupling center atom and also contains a high molecular weight component, a medium molecular weight component and a low molecular weight component, so that the particle size of the low cis-polybutadiene rubber is in a tertiary distribution, and when used as a toughening agent for aromatic vinyl resins, the three components act synergistically with each other, so that not only the aromatic vinyl resin has improved impact resistance but also the aromatic vinyl resin has good gloss.
According to the preparation method of the low cis-polybutadiene rubber, the low cis-polybutadiene rubber containing a high molecular weight component, a medium molecular weight component and a low molecular weight component simultaneously can be obtained through one-step coupling reaction by only adopting a trifunctional coupling agent and enabling the trifunctional coupling agent to be excessive relative to an organic lithium initiator without compounding the low cis-polybutadiene rubber with different molecular weights or adopting coupling agents with different functionalities.
Detailed Description
The endpoints of the ranges and any values disclosed herein are not limited to the precise range or value, and such ranges or values should be understood to encompass values close to those ranges or values. For ranges of values, between the endpoints of each of the ranges and the individual points, and between the individual points may be combined with each other to give one or more new ranges of values, and these ranges of values should be considered as specifically disclosed herein.
According to a first aspect of the present invention, there is provided a low cis-polybutadiene rubber comprising a coupling center atom, a high molecular weight component, a medium molecular weight component and a low molecular weight component, the high molecular weight component having a number average molecular weight (M)n) Is 210,000-360,000, preferably 230,000-350,000, more preferably 240,000-330,000, and further preferably 270,000-320,000; the number average molecular weight of the medium molecular weight component is 150,000-250,000, preferably 160,000-240,000, more preferably 170,000-230,000, and further preferably 180,000-220,000; the number average molecular weight of the low molecular weight component is 80,000-120,000, preferably 85,000-115,000, more preferably 90,000-110,000. According to the low cis-polybutadiene rubber of the present invention, the number average molecular weight size relationship among the high molecular weight component, the medium molecular weight component and the low molecular weight component is as follows: the number average molecular weight of the high molecular weight component > the number average molecular weight of the medium molecular weight component > the number average molecular weight of the low molecular weight component.
According to the low cis-polybutadiene rubber of the present invention, the molecular weight distribution index (M) of the high molecular weight componentw/Mn) May be 1 to 1.1, preferably 1.02 to 1.08; the molecular weight distribution index of the medium molecular weight component may be 1 to 1.1, preferably 1.02 to 1.08; the low molecular weight component may have a molecular weight distribution index of 1 to 1.1, preferably 1.02 to 1.08.
The low-cis polybutadiene rubber according to the present invention contains the high-molecular-weight component in an amount of 4 to 55% by weight, preferably 12 to 55% by weight, more preferably 15 to 50% by weight, and still more preferably 18 to 45% by weight, based on the total amount of the low-cis polybutadiene rubber; the content of the medium molecular weight component is 25 to 50 wt%, preferably 30 to 50 wt%, more preferably 35 to 48 wt%, and further preferably 40 to 45 wt%; the content of the low-molecular weight component is 5 to 70% by weight, preferably 7 to 60% by weight, more preferably 10 to 50% by weight, and further preferably 15 to 42% by weight.
The number average molecular weight of the low cis-polybutadiene rubber according to the present invention may be 130,000-230,000, preferably 150,000-210,000. The low cis-polybutadiene rubber according to the present invention may have a molecular weight distribution index of 1.3 to 2.3, preferably 1.5 to 2.1. In the present invention, the number average molecular weight and the molecular weight distribution index of the low cis-polybutadiene rubber mean the overall number average molecular weight and the overall molecular weight distribution index of the low cis-polybutadiene rubber.
In the invention, the number average molecular weight and the molecular weight distribution index are measured by gel permeation chromatography, and the mass percentage content of the high molecular weight component, the medium molecular weight component and the low molecular weight component is measured by gel permeation chromatography. The gel permeation chromatography analysis adopts an HLC-8320 type gel permeation chromatograph of Tosoh corporation in Japan, chromatographic columns are TSKgel SuperMultiporeHZ-N and TSKgel SuperMultiporeHZ standard columns, a solvent is chromatographic pure Tetrahydrofuran (THF), narrow-distribution polystyrene is used as a standard sample, a polymer sample is prepared into a tetrahydrofuran solution with the mass concentration of 1mg/mL, the sample introduction amount is 10.00 mu L, the flow rate is 0.35mL/min, and the test temperature is 40.0 ℃. The calculation method of the mass percentage of the high molecular weight component, the medium molecular weight component and the low molecular weight component comprises the following steps:
mass percent (%) of the high molecular weight component (%) - (peak area corresponding to the peak of the high molecular weight component/(peak area corresponding to the high molecular weight component + peak area corresponding to the medium molecular weight component + peak area corresponding to the low molecular weight component) in the GPC curve;
mass percent (%) of the medium molecular weight component (%) - (peak area corresponding to the peak of the medium molecular weight component/(peak area corresponding to the high molecular weight component + peak area corresponding to the medium molecular weight component + peak area corresponding to the low molecular weight component) in the GPC curve;
Mass percentage (%) of the low molecular weight component, peak area of the peak corresponding to the low molecular weight component/(peak area corresponding to the high molecular weight component + peak area corresponding to the medium molecular weight component + peak area corresponding to the low molecular weight component) in the GPC curve;
in the present invention, the peak area of the peak of each component is a percentage of the normalized peak area obtained by GPC measurement.
According to the low-cis polybutadiene rubber of the present invention, the viscosity of the low-cis polybutadiene rubber in a 5 wt% styrene solution at 25 ℃ may be 90cP or more, preferably 100-200cP, more preferably 110-180cP, and still more preferably 115-170 cP.
The low-cis polybutadiene rubber according to the present invention has a reduced viscosity of a 5 wt% styrene solution at 25 ℃ and thus has better processability, as compared to compounding a linear low-cis polybutadiene rubber having a component corresponding to the high molecular weight, a linear low-cis polybutadiene rubber having a component corresponding to the medium molecular weight, and a linear low-cis polybutadiene rubber having a component corresponding to the low molecular weight. The low-cis polybutadiene rubber according to the present invention has a viscosity of X cps in a 5 wt% styrene solution at 25 ℃ and a viscosity of Y cps in a 5 wt% styrene solution at 25 ℃ as a low-molecular weight component, and the ratio of X/Y may be 1 to 1.5, for example: 1. 1.1, 1.2, 1.3, 1.4 or 1.5, preferably 1.1 to 1.4. The ratio of the viscosity of a compound obtained by compounding a linear low-cis polybutadiene rubber having a component corresponding to the high molecular weight, a linear low-cis polybutadiene rubber having a component corresponding to the medium molecular weight, and a linear low-cis polybutadiene rubber having a component corresponding to the low molecular weight to Y in a 5 wt% styrene solution at 25 ℃ is usually 3 or more.
In the present invention, the viscosity of the rubber in a 5 wt% styrene solution at 25 ℃ is measured in accordance with the Q/SHYS.3155.SXJC06-2016 standard.
According to the low-cis polybutadiene rubber of the present invention, the Mooney viscosity at 100 ℃ of the low-cis polybutadiene rubber may be 40 to 70, preferably 45 to 65, more preferably 48 to 60.
In the present invention, Mooney viscosity is measured by a Mooney viscometer model SMV-201SK-160 manufactured by Shimadzu corporation of Japan according to a method specified in the Chinese national standard GB/T1232-92, in a test mode: ML (1+4), test temperature 100 ℃.
The vinyl content of the low-cis polybutadiene rubber according to the present invention may be 8 to 20% by weight, preferably 10 to 16% by weight.
According to the low-cis polybutadiene rubber of the present invention, the content of the cis 1, 4-structural unit of the low-cis polybutadiene rubber may be 30 to 40% by weight.
In the present invention, the vinyl group content means a structural unit in which butadiene is polymerized in a 1, 2-form, and in the present invention, the cis-1, 4-structural unit means a structural unit in which butadiene is polymerized in a 1, 4-form and the configuration is cis-form. In the invention, the content of vinyl and the content of cis-1, 4-structural units are measured by a nuclear magnetic resonance spectroscopy, the solvent adopted in the test is deuterated chloroform, and tetramethylsilicon is used as an internal standard.
According to the low cis-polybutadiene rubber of the present invention, the low cis-polybutadiene rubber contains a coupling center atom. According to the low cis-polybutadiene rubber of the present invention, the coupling center atom may be provided by a coupling agent. According to the low-cis polybutadiene rubber of the present invention, the high molecular weight component and the medium molecular weight component contain a coupling center atom, and the low molecular weight component is substantially free of a coupled polymer and is a linear polymer. That is, according to the low-cis polybutadiene rubber of the present invention, the high molecular weight component and the medium molecular weight component are coupled polymers, which are components formed by reacting a coupling agent with the living terminal groups of the corresponding linear polymer to link at least two linear polymer chains together through the coupling center atom of the coupling agent.
The low-cis polybutadiene rubber according to the present invention may have a mass content of the coupling center atom of 88 to 245ppm, based on the total amount of the low-cis polybutadiene rubber, for example: 88. 89, 90, 91, 92, 93, 94, 95, 96, 97, 98, 99, 100, 101, 102, 103, 104, 105, 106, 107, 108, 109, 110, 111, 112, 113, 114, 115, 116, 117, 118, 119, 120, 121, 122, 123, 124, 125, 126, 127, 128, 129, 130, 131, 132, 133, 134, 135, 136, 137, 138, 139, 140, 141, 142, 143, 144, 145, 146, 147, 148, 149, 150, 151, 152, 153, 154, 155, 156, 157, 158, 159, 160, 161, 162, 163, 164, 165, 166, 167, 168, 169, 170, 171, 172, 173, 174, 175, 176, 177, 178, 179, 180, 181, 182, 183, 211, 185, 187, 188, 189, 190, 191, 193, 194, 195, 196, 198, 195, 200, 202, 209, 215, 202, 204, 209, 212, 214, 216, 204, 213, 204, 213, 217. 218, 219, 220, 221, 222, 223, 224, 225, 226, 227, 228, 229, 230, 231, 232, 233, 234, 235, 236, 237, 238, 239, 240, 241, 242, 243, 244 or 245ppm, preferably 110-220ppm, more preferably 120-210 ppm.
According to the low cis-polybutadiene rubber of the present invention, the coupling center atom is derived from a coupling agent, which is preferably one or two or more of trifunctional coupling agents. Preferably, the coupling agent is one or more than two of the coupling agents shown in the formula I,
Figure BDA0002067355340000081
in the formula I, R1Is C1-C6Alkyl of (2) including C1-C6Straight chain alkyl of (2) and C3-C6Specific examples thereof may include, but are not limited to: methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, n-pentyl, isopentyl, tert-pentyl, neopentyl and n-hexyl.
In the formula I, R2、R3And R4For the dissociation of the groups, i.e. in the coupling reaction,as a group which reacts with the living end groups of the living polymer chain. In the formula I, R2、R3And R4Preferably a halogen group, more preferably chlorine.
In formula I, Z is a coupling center atom, preferably a silicon atom or a tin atom, more preferably a silicon atom.
Specific examples of the coupling agent according to the low-cis polybutadiene rubber of the present invention may include, but are not limited to: one or more than two of methyl trichlorosilane, ethyl trichlorosilane and methyl tribromosilane. Preferably, the coupling agent is methyltrichlorosilane and/or ethyltrichlorosilane.
According to the low-cis polybutadiene rubber of the present invention, the high molecular weight component and the medium molecular weight component contain a coupling center atom. According to the low cis-polybutadiene rubber of the present invention, in addition to the coupling agent residue contained in the molecular chain of the high molecular weight component and the medium molecular weight component, at least part of the molecular chain of the low molecular weight component also contains the coupling agent residue (i.e., at least part of the low molecular weight component contains a coupling center atom), except that the coupling agent residue in the molecular chain of the low molecular weight component is connected to only one polymer chain.
The low cis-polybutadiene rubber according to the present invention, wherein the low cis-polybutadiene rubber has a coupling center atom in a molar percentage of NZThe molar percentage of the high molecular weight component is NHThe mol percentage of the medium molecular weight component is NMThe low molecular weight component is NLThe number of coupling arms of the high molecular weight component is AHThe number of coupling arms of the medium molecular weight component is AM，3(NH+NM+NL)≥(NZ×3)≥(NH×AH+NM×AM+NL). Preferably, (N)Z×3)/(NH×AH+NM×AM+NL) In the range of 1 to 2.8, for example: 1. 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2, 2.1, 2.2, 2.3, 2.4, 2.5, 2.6, 2.7 or 2.8. More preferably, (N)Z×3)/(NH×AH+NM×AM+NL) The ratio of (A) to (B) is 1.1-2.5. Further preferably, (N) Z×3)/(NH×AH+NM×AM+NL) The ratio of (A) to (B) is 1.3-2.2. Still further preferably, (N)Z×3)/(NH×AH+NM×AM+NL) The ratio of (A) to (B) is 1.4-1.8.
In the present invention, the mass percentage of the coupling center atom is measured by a plasma method (ICP method), and the molar percentage of the coupling center atom is converted from this. In the invention, the mole percentage content and the coupling arm number of the high molecular weight component, the medium molecular weight component and the low molecular weight component are measured by adopting a GPC method, and the specific method comprises the following steps:
the number of coupling arms of the high molecular weight component is equal to the number average molecular weight of the high molecular weight component/the number average molecular weight of the low molecular weight component;
the number of coupling arms of the medium molecular weight component is equal to the number average molecular weight of the medium molecular weight component/the number average molecular weight of the low molecular weight component;
a molar percentage of the high molecular weight component ═ (peak area corresponding to the high molecular weight component/number average molecular weight of the high molecular weight component) ÷ (peak area corresponding to the high molecular weight component/number average molecular weight of the high molecular weight component + peak area corresponding to the medium molecular weight component/number average molecular weight of the medium molecular weight component + peak area corresponding to the low molecular weight component/number average molecular weight of the low molecular weight component);
a mole percent of the medium molecular weight component ═ g (peak area corresponding to the medium molecular weight component/number average molecular weight of the medium molecular weight component) ÷ (peak area corresponding to the high molecular weight component/number average molecular weight of the high molecular weight component + peak area corresponding to the medium molecular weight component/number average molecular weight of the medium molecular weight component + peak area corresponding to the low molecular weight component/number average molecular weight of the low molecular weight component);
The mole percent of the low molecular weight component (peak area corresponding to the low molecular weight component/number average molecular weight of the low molecular weight component) ÷ (peak area corresponding to the high molecular weight component/number average molecular weight of the high molecular weight component + peak area corresponding to the medium molecular weight component/number average molecular weight of the medium molecular weight component + peak area corresponding to the low molecular weight component/number average molecular weight of the low molecular weight component).
The low-cis polybutadiene rubber according to the present invention may further contain at least one auxiliary agent to impart new properties to the low-cis polybutadiene rubber and/or to improve the properties of the low-cis polybutadiene rubber. The adjuvant may include an antioxidant. The type of the antioxidant is not particularly limited in the present invention and may be conventionally selected, and for example, the antioxidant may be a phenolic and/or amine antioxidant. Specifically, the antioxidant may be one or more of 4, 6-bis (octylthiomethyl) o-cresol (trade name: antioxidant 1520), N-octadecyl beta- (3, 5-di-tert-butyl-4-hydroxyphenyl) propionate (trade name: antioxidant 1076), N- (1, 3-dimethylbutyl) -N '-phenyl-p-phenylenediamine (trade name: antioxidant 4020), N-cumyl-N' -phenyl-p-phenylenediamine (trade name: antioxidant 4010NA), and N-phenyl-2-naphthylamine (trade name: antioxidant D), and preferably, the antioxidant 1520 and the antioxidant 1076 are used. When the antioxidant 1520 and the antioxidant 1076 are used in combination, the weight ratio of the antioxidant 1520 to the antioxidant 1076 may be 1: 1-3. The antioxidant may be used in an amount conventionally used in the art. In one embodiment, the weight ratio of the antioxidant to the low cis polybutadiene rubber may be 0.1 to 0.4: 100.
According to a second aspect of the present invention, there is provided a process for preparing a low cis-polybutadiene rubber, comprising the steps of:
(1) under the condition of anionic polymerization, in the presence of an organic lithium initiator and a structure regulator, polymerizing 1, 3-butadiene in an organic solvent to obtain a polymerization solution containing polybutadiene;
(2) contacting the polymerization solution with a coupling agent to carry out coupling reaction to obtain a coupling polymer solution, wherein the coupling agent is one or more than two of trifunctional coupling agents, and the molar weight n of the coupling agentCThe molar weight of the organic lithium initiator is nI，(2.1×nI)≥(nC×3)＞nI。
In the step (1), the organolithium initiator may be any organolithium compound capable of initiating butadiene polymerization, which is commonly used in the field of anionic polymerization, and is preferably a compound represented by the formula II,
R5li (formula II)
In the formula II, R5Is C1-C6Alkyl of (C)3-C12Cycloalkyl of, C7-C14Aralkyl or C6-C12Aryl group of (1).
Said C is1-C6Alkyl of (2) includes C1-C6Straight chain alkyl of (2) and C3-C6Specific examples thereof may include, but are not limited to: methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, n-pentyl, isopentyl, tert-pentyl, neopentyl and n-hexyl.
Said C is3-C12Specific examples of the cycloalkyl group of (a) may include, but are not limited to: cyclopropyl, cyclopentyl, cyclohexyl, 4-methylcyclohexyl, 4-ethylcyclohexyl, 4-n-propylcyclohexyl and 4-n-butylcyclohexyl.
Said C is7-C14Specific examples of the aralkyl group of (a) may include, but are not limited to: phenylmethyl, phenylethyl, phenyl-n-propyl, phenyl-n-butyl, phenyl-t-butyl, phenyl-isopropyl, phenyl-n-pentyl and phenyl-n-butyl.
Said C is6-C12Specific examples of the aryl group of (a) may include, but are not limited to: phenyl, naphthyl, 4-methylphenyl and 4-ethylphenyl.
Specific examples of the organolithium initiator may include, but are not limited to: one or more of ethyllithium, n-propyllithium, isopropyllithium, n-butyllithium, sec-butyllithium, tert-butyllithium, n-pentyllithium, n-hexyllithium, cyclohexyllithium, phenyllithium, 2-naphthyllithium, 4-butylphenyl lithium, 4-methylphenyllithium and 4-butylcyclohexyllithium. Preferably, the organolithium initiator is n-butyllithium and/or sec-butyllithium. More preferably, the organolithium initiator is n-butyllithium.
In the step (1), the molecular weight of polybutadiene can be adjusted by adjusting the ratio of the organolithium initiator to 1, 3-butadiene. According to the preparation method of the present invention, in a preferred embodiment, the molar ratio of 1, 3-butadiene to the organolithium initiator is 1400-: 1. in this preferred embodiment, the molar ratio of 1, 3-butadiene to the organolithium initiator is more preferably 1500-: 1, more preferably 1600-: 1. according to this preferred embodiment, the finally prepared polybutadiene rubber is suitable as a toughening agent for aromatic vinyl resins.
In the step (1), the structure regulator is used for regulating the vinyl content in the polybutadiene formed by polymerization, and may be one or more than two of an ether-type structure regulator and an amine-type structure regulator.
The ether type structure regulator can be one or more than two of aliphatic monoether, aliphatic polyether, aromatic ether and cyclic ether.
The aliphatic monoether can be one or more than two of aliphatic symmetrical monoethers and aliphatic asymmetrical monoethers. Specific examples of the aliphatic monoethers may include, but are not limited to: one or more of methyl ether, ethyl ether, propyl ether and methyl ethyl ether.
The aliphatic polyether can be one or more of aliphatic symmetrical polyether and aliphatic asymmetrical polyether. Specific examples of the aliphatic polyether may include, but are not limited to: one or more of ethylene glycol dialkyl ether, diethylene glycol dialkyl ether and diethylene glycol dialkyl ether. The alkyl group may be C1-C4Alkyl, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl or tert-butyl.
The aromatic ether may be anisole and/or diphenyl ether.
The cyclic ether may be one or more of tetrahydrofuran, tetrahydrofurfuryl alkyl ether and 1, 4-dioxan. Specific examples of the cyclic ether may include, but are not limited to: one or more than two of tetrahydrofuran, tetrahydrofurfuryl methyl ether, tetrahydrofurfuryl ethyl ether, tetrahydrofurfuryl propyl ether, tetrahydrofurfuryl isopropyl ether, tetrahydrofurfuryl butyl ether and 1, 4-dioxycyclohexane.
The amine structure regulator can be one or more than two of N, N, N ', N' -tetramethyl ethylenediamine, N, N-dimethyl tetrahydrofurfuryl amine, triethylamine and tripropylamine.
In a preferred embodiment, the structure regulator in step (1) is one or more of tetrahydrofuran, tetrahydrofurfuryl alkyl ether, ethylene glycol dialkyl ether, diethylene glycol dialkyl ether and amine-type structure regulator, and the alkyl group may be C1-C4Alkyl, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl or tert-butyl. In the preferred embodiment, the structure modifier is preferably one or more of tetrahydrofuran, tetrahydrofurfuryl methyl ether, tetrahydrofurfuryl ethyl ether, tetrahydrofurfuryl propyl ether, tetrahydrofurfuryl butyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, and N, N-dimethyltetrahydrofurfuryl amine; more preferably one or more of tetrahydrofurfuryl methyl ether, tetrahydrofurfuryl ethyl ether and tetrahydrofurfuryl propyl ether.
In step (1), the amount of the structure-regulating agent may be conventionally selected. In step (1), the molar ratio of the structure-regulating agent to the organolithium initiator may be 0.01 to 1: 1, preferably 0.02 to 0.8: 1, more preferably 0.05 to 0.7: 1.
In the step (1), the polymerization is carried out in an organic solvent, which may be any of various organic substances capable of mediating the polymerization reaction under solution polymerization conditions, preferably a nonpolar solvent, for example, a hydrocarbon solvent. The hydrocarbon solvent may be one or more selected from cyclohexane, n-hexane, n-pentane, n-heptane, isooctane, benzene and raffinate oil. The raffinate oil is the distillate oil left after the aromatic hydrocarbon is extracted from the catalytic reforming product rich in the aromatic hydrocarbon in the petroleum refining process. The solvent may be used in an amount conventional in the art. In general, in step (1), the solvent may be used in an amount such that the concentration of 1, 3-butadiene is 1 to 25% by weight, preferably 10 to 20% by weight.
In step (1), the polymerization may be carried out under conventional anionic polymerization conditions. The polymerization in the step (1) is carried out so that the conversion of 1, 3-butadiene is 99% by weight or more. Generally, in step (1), the polymerization may be carried out at a temperature of 0 to 100 ℃, preferably 40 to 95 ℃, more preferably 60 to 90 ℃. In step (1), the duration of the polymerization may be 20 to 80 minutes, preferably 30 to 60 minutes. In the step (1), the polymerization may be carried out at a pressure of 0.1 to 1MPa, preferably 0.2 to 0.5MPa, the pressure being a gauge pressure.
According to the preparation method of the invention, in the step (2), the coupling agent is used in excess, and the molar quantity of the organic lithium initiator is nI，(2.1×nI)≥(nC×3)＞nI. According to the preparation method, excessive coupling agents are adopted, the polybutadiene rubber with different molecular weights can be obtained through one-step coupling reaction, and more than two coupling agents are avoided or the polybutadiene rubber with different molecular weights is not compounded. Preferably, nC/nIThe ratio of (A) to (B) is 0.38-0.7: controlling the amount of the coupling agent and the organolithium initiator to be the ratio can further improve the performance of the finally prepared polybutadiene rubber as a toughening agent of the aromatic vinyl resin, so that the aromatic vinyl resin obtains better performance balance between the impact resistance and the optical performance. More preferably, nC/nIThe ratio of (A) to (B) is 0.42-0.65: 1. further preferably, nC/nIThe ratio of (A) to (B) is 0.45-0.6: 1.
in the step (2), the coupling agent is one or more than two of trifunctional coupling agents.
Preferably, the coupling agent is one or more than two of the coupling agents shown in the formula I,
Figure BDA0002067355340000131
in the formula I, R1Is C1-C6Alkyl of (2) including C1-C6Straight chain alkyl of (2) and C3-C6Specific examples thereof may include, but are not limited to: methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, n-pentyl, isopentyl, tert-pentyl, neopentyl and n-hexyl.
In the formula I, R2、R3And R4Are dissociating groups, i.e. groups which react as reactive groups with the reactive end groups of the living polymer chains in the coupling reaction. In the formula I, R2、R3And R4Preferably a halogen group, more preferably chlorine.
In formula I, Z is a coupling center atom, preferably a silicon atom or a tin atom, more preferably a silicon atom.
Specific examples of the coupling agent may include, but are not limited to: one or more than two of methyl trichlorosilane, ethyl trichlorosilane and methyl tribromosilane. Preferably, the coupling agent is methyltrichlorosilane and/or ethyltrichlorosilane.
According to the preparation method of the present invention, in the step (2), the coupling reaction may be carried out at a temperature of 50 to 100 ℃, preferably 60 to 80 ℃. The duration of the coupling reaction may be 20-40 minutes. The coupling reaction may be carried out at a pressure of from 0.1 to 1MPa, preferably from 0.2 to 0.5MPa, the pressure being gauge pressure.
The preparation method according to the present invention preferably further comprises a step (3) of contacting the coupled polymer solution with a terminating agent to carry out a terminating reaction to obtain a terminated reaction solution.
The terminator may be any of various substances capable of terminating a living chain, which are commonly used in the field of anionic polymerization. The terminating agent may be C 1-C4Preferably one or more of isopropyl alcohol, stearic acid, citric acid and carbon dioxide, more preferably carbon dioxide. The carbon dioxide is adopted for termination reaction, the carbon dioxide can form carbonate with metal ions (Li, Mg, Al, Fe and Zn) in a polymerization system to be separated from the polymer, the color development reaction of the metal ions is avoided, and the product has lower chroma. The carbon dioxide can be in the form of a gasThe formula (for example, carbon dioxide gas having a gauge pressure of 0.2 to 1MPa, preferably 0.3 to 0.6 MPa) is introduced into the reaction system, or may be introduced into the reaction system in the form of an aqueous dry ice solution (for example, the concentration may be 0.1 to 5% by weight).
The preparation method according to the present invention may further include step (4): adding at least one auxiliary agent to the termination reaction liquid obtained in step (3) to impart new properties to the finally produced low-cis polybutadiene rubber and/or to improve the properties of the finally produced low-cis polybutadiene rubber.
In particular, the adjuvant may include an antioxidant. The type of the antioxidant is not particularly limited in the present invention and may be conventionally selected, and for example, the antioxidant may be a phenolic and/or amine antioxidant. Specifically, the antioxidant may be one or more of 4, 6-bis (octylthiomethyl) o-cresol (trade name: antioxidant 1520), N-octadecyl beta- (3, 5-di-tert-butyl-4-hydroxyphenyl) propionate (trade name: antioxidant 1076), N- (1, 3-dimethylbutyl) -N '-phenyl-p-phenylenediamine (trade name: antioxidant 4020), N-cumyl-N' -phenyl-p-phenylenediamine (trade name: antioxidant 4010NA), and N-phenyl-2-naphthylamine (trade name: antioxidant D), and is preferably one or more of antioxidant 1520 and antioxidant 1076. When the antioxidant 1520 and the antioxidant 1076 are used in combination, the weight ratio of the antioxidant 1520 to the antioxidant 1076 may be 1: 1-3. The antioxidant may be used in an amount conventionally used in the art. In one embodiment, the weight ratio of the antioxidant to 1, 3-butadiene may be from 0.1 to 0.4: 100.
According to the preparation method of the present invention, the obtained mixture can be purified and separated by a conventional method, thereby obtaining the low cis-polybutadiene rubber. Specifically, the resulting mixture may be subjected to centrifugal separation, filtration, decantation or hot water coagulation to obtain a low cis-polybutadiene rubber; the resulting mixture may also be stripped to remove the solvent therefrom to provide a low cis polybutadiene rubber.
The polymerization method of the present invention may be carried out by a batch polymerization method or a continuous polymerization method, and is not particularly limited.
According to a third aspect of the present invention, there is provided a low-cis polybutadiene rubber prepared by the preparation process according to the second aspect of the present invention.
The low cis-polybutadiene rubber prepared by the method of the second aspect of the invention can obtain the high molecular weight component, the medium molecular weight component and the low molecular weight component by controlling the dosage of the coupling agent to be excessive and without compounding.
Specifically, the low-cis polybutadiene rubber according to the third aspect of the present invention contains a high molecular weight component, a medium molecular weight component and a low molecular weight component, and the number average molecular weight of the high molecular weight component may be 210,000-360,000, preferably 230,000-350,000, more preferably 240,000-330,000, and further preferably 270,000-320,000; the number average molecular weight of the medium molecular weight component may be 150,000-250,000, preferably 160,000-240,000, more preferably 170,000-230,000, and further preferably 180,000-220,000; the number average molecular weight of the low molecular weight component may be 80,000-120,000, preferably 85,000-115,000, more preferably 90,000-110,000. According to the low-cis polybutadiene rubber of the third aspect of the present invention, the number average molecular weight size relationship among the high molecular weight component, the medium molecular weight component and the low molecular weight component is as follows: the number average molecular weight of the high molecular weight component > the number average molecular weight of the medium molecular weight component > the number average molecular weight of the low molecular weight component.
The low-cis polybutadiene rubber according to the third aspect of the present invention, wherein the high-molecular-weight component has a molecular weight distribution index (M)w/Mn) May be 1 to 1.1, preferably 1.02 to 1.08; the molecular weight distribution index of the medium molecular weight component may be 1 to 1.1, preferably 1.02 to 1.08; the low molecular weight component may have a molecular weight distribution index of 1 to 1.1, preferably 1.02 to 1.08.
The low-cis polybutadiene rubber according to the third aspect of the present invention, the content of the high-molecular weight component may be 4 to 55% by weight, preferably 12 to 55% by weight, more preferably 15 to 50% by weight, still more preferably 18 to 45% by weight, based on the total amount of the low-cis polybutadiene rubber; the content of the medium molecular weight component may be 25 to 50% by weight, preferably 30 to 50% by weight, more preferably 35 to 48% by weight, and further preferably 40 to 45% by weight; the content of the low-molecular weight component may be 5 to 70% by weight, preferably 7 to 60% by weight, more preferably 10 to 50% by weight, and further preferably 15 to 42% by weight.
The low cis-polybutadiene rubber according to the third aspect of the present invention may have a number average molecular weight of 130,000-230,000, preferably 150,000-210,000. The low cis-polybutadiene rubber according to the third aspect of the present invention may have a molecular weight distribution index of 1.3 to 2.3, preferably 1.5 to 2.1.
According to a fourth aspect of the present invention, there is provided the use of a low-cis polybutadiene rubber according to the first or third aspect of the present invention as an aromatic vinyl resin toughening agent.
The low-cis polybutadiene rubber according to the present invention may be added to the aromatic vinyl resin as a toughening agent using a conventional method, for example: the low cis-polybutadiene rubber may be added during polymerization to form the aromatic vinyl resin, or may be added as a toughening agent to the aromatic vinyl resin.
According to a fifth aspect of the present invention, there is provided an aromatic vinyl resin comprising an aromatic vinyl base resin and a toughening agent, wherein the toughening agent is the low-cis polybutadiene rubber of the first or third aspect of the present invention.
The aromatic vinyl base matrix resin may be a polymer formed by homopolymerizing or copolymerizing an aromatic vinyl monomer, which means a monomer having both an aromatic group (e.g., phenyl group) and a vinyl group in a molecular structure. Specific examples of the aromatic vinyl monomer may include, but are not limited to: one or the combination of more than two of styrene, o-methylstyrene, m-methylstyrene, p-methylstyrene, o-ethylstyrene, m-ethylstyrene, p-ethylstyrene and vinylnaphthalene. Preferably, the aromatic vinyl monomer is styrene.
One preferred example of the aromatic vinyl resin is high impact polystyrene.
The amount of low cis polybutadiene rubber used as a toughening agent may be conventionally selected. Specifically, the low cis-polybutadiene rubber may be used in an amount of 5 to 15 parts by weight, relative to 100 parts by weight of the high impact polystyrene.
According to a sixth aspect of the present invention, there is provided a method for producing an aromatic vinyl resin, the method comprising: polymerizing an aromatic vinyl monomer in the presence of a toughening agent, wherein the toughening agent is the low-cis polybutadiene rubber of the first or third aspect of the present invention.
According to the method for preparing the aromatic vinyl resin of the present invention, specific examples of the aromatic vinyl monomer may include, but are not limited to: one or the combination of more than two of styrene, o-methylstyrene, m-methylstyrene, p-methylstyrene, o-ethylstyrene, m-ethylstyrene, p-ethylstyrene and vinylnaphthalene. Preferably, the aromatic vinyl monomer is styrene.
According to the method for preparing an aromatic vinyl resin of the present invention, the polymerization reaction may be carried out by a radical polymerization method. The type of the radical initiator used in the radical polymerization is not particularly limited, and may be selected conventionally, and may be one or two or more kinds of thermal decomposition type radical initiators, for example. Preferably, the radical initiator is one or more than two of a peroxide type initiator and an azobisnitrile type initiator. Specific examples of the radical initiator may include, but are not limited to: one or more of diacyl peroxide, peroxy-2-ethylhexyl tert-butyl carbonate, peroxydicarbonate, peroxycarboxylate, alkyl peroxide and azobisnitrile compounds (such as azobisisobutyronitrile and azobisisoheptonitrile). Preferably, the free radical initiator is one or more than two of dibenzoyl peroxide, di-o-methylbenzoyl peroxide, tert-butyl peroxybenzoate and tert-butyl peroxy-2-ethylhexylcarbonate.
The amount of the radical initiator to be used may be conventionally selected so as to be able to obtain an aromatic vinyl resin having a desired molecular weight. Methods for determining the amount of initiator to be used based on the molecular weight of the polymer to be expected are well known to those skilled in the art and will not be described in detail herein.
According to the method for preparing an aromatic vinyl resin of the present invention, the polymerization reaction can be carried out under conventional conditions. Generally, the conditions of the polymerization reaction include: the temperature can be 100 ℃ and 170 ℃ and the time can be 4-12 hours (e.g., 7-9 hours). Preferably, the polymerization reaction can be carried out in stages at different temperatures. For example: the polymerization reaction may include a first polymerization reaction, a second polymerization reaction, a third polymerization reaction, and a fourth polymerization reaction, the first polymerization reaction may be performed at a temperature of 115-125 ℃, and the duration of the first polymerization reaction may be 3-4 hours; the second polymerization reaction may be performed at a temperature of 130-140 ℃, and the duration of the second polymerization reaction may be 1-3 hours; the third polymerization reaction may be carried out at a temperature of 150-160 ℃, and the duration of the third polymerization reaction may be 0.5-1.5 hours; the fourth polymerization reaction may be carried out at a temperature of 165-175 deg.C, and the duration of the fourth polymerization reaction may be 0.5-1.5 hours.
The high impact polystyrene has excellent impact resistance, and the cantilever beam impact strength of the high impact polystyrene can be 13kJ/m2Above (e.g., 13-20 kJ/m)2) And is usually 15kJ/m2Above (e.g., 15-20 kJ/m)2) Preferably 17kJ/m2The above; the 60 ° surface gloss may be 55 or more, usually 62 or more, preferably 65 or more, for example: 68-75.
The present invention will be described in detail with reference to examples, but the scope of the present invention is not limited thereto.
In the following examples and comparative examples, the monomer conversion was determined gravimetrically as the weight percent of polymer weight after solvent removal as a function of monomer charge.
In the following examples and comparative examples, the content of 1, 2-polymerized structural units in the low-cis polybutadiene rubber was determined as a vinyl content by using an AVANCEDRX400MHz type nuclear magnetic resonance apparatus manufactured by BRUKER, wherein the frequency was 400MHz, the solvent was deuterated chloroform, and the internal standard was tetramethylsilane. The gel permeation chromatography analysis was performed on a gel permeation chromatograph model HLC-8320 from the company eastern cao, japan, wherein the test conditions included: the chromatographic column is TSKgel SuperMultiporeHZ-N, the standard column is TSKgel SuperMultiporeHZ, the solvent is chromatographically pure THF, the calibration standard sample is polystyrene, the sample mass concentration is 1mg/mL, the sample amount is 10.00 mu L, the flow rate is 0.35mL/min, and the test temperature is 40 ℃. Plasma analysis (ICP) was carried out on an ICPMS-2030, model number available from Shimadzu, Japan, and was determined according to the GB/T18174-2000 standard.
In the following examples and comparative examples, the viscosity of a 5 wt% styrene solution of rubber at a temperature of 25 ℃ was measured at a constant temperature of 25 ℃ using a capillary viscometer.
In the following examples and comparative examples, the Mooney viscosity was measured using a Mooney viscometer without a rotor, model SMV-201SK-160, manufactured by Shimadzu corporation of Japan, in which the preheating time was 1min, the rotation time was 4min, and the measuring temperature was 100 ℃.
In the following examples and comparative examples, the color was determined according to the Q/SH 3165251-: the color system is CIELAB, the optical geometry is 45/0, the light source is a C light source, the observation angle is 2 degrees, and the diameter of the observation hole is 30 mm.
In the following examples and comparative examples, mechanical properties were measured using an INSTRON 5567 Universal Material testing machine, UK, in which notched Izod impact Strength was measured according to GB/T1843-1996 (kJ/m)2). In the following examples and comparative examples, 60 ℃ gloss was measured according to ASTM D526(60 ℃).
In the following examples and comparative examples, the pressure refers to gauge pressure.
In the following examples and comparative examples, antioxidant 1520 was purchased from national pharmaceutical Agents; antioxidant 1076 was purchased from Inokay reagent, tetrahydrofurfurylethyl ether from carbofuran reagent, methyltrichlorosilane, ethyltrichlorosilane and dimethyldichlorosilane from carbofuran reagent (analytically pure, diluted to a concentration of 0.1mol/L), and n-butyllithium and sec-butyllithium from carbofuran reagent, each diluted with hexane to a concentration of 0.4 mol/L.
Examples 1-9 serve to illustrate the invention.
Example 1
(1) Under the protection of nitrogen, adding an organic solvent, 1, 3-butadiene and a structure regulator into a polymerization reaction kettle, raising the temperature in the polymerization reaction kettle to the polymerization reaction temperature, then adding an organic lithium initiator, and carrying out anionic solution polymerization reaction at the temperature (the temperature, the pressure and the time of the polymerization reaction are shown in table 1) to obtain a polymerization reaction mixed solution.
(2) An excess amount of trifunctional coupling agent (specific type and amount are shown in Table 2) was added to the polymerization mixture, and a coupling reaction was carried out under the conditions shown in Table 2 (coupling reaction temperature, pressure and time are shown in Table 2), to obtain a coupling reaction mixture.
(3) After the coupling reaction was completed, a terminator (specific type and amount shown in table 2) was added to the coupling reaction mixture to terminate the coupling reaction. To the mixture obtained by the termination reaction, an antioxidant (the kind and amount thereof are shown in Table 2) was added and mixed to obtain a polymerization solution of low cis-polybutadiene rubber. The resulting polymerization solution was subjected to steam coagulation desolventization treatment and dried to obtain low cis-polybutadiene rubber having the structural and property parameters as listed in tables 3 and 4.
Examples 2 to 9
Low-cis polybutadiene rubbers were prepared in the same manner as in example 1, except that the conditions shown in tables 1 and 2 were respectively employed to obtain low-cis polybutadiene rubbers, and the structural and property parameters of the obtained low-cis polybutadiene rubbers are shown in tables 3 and 4.
Comparative example 1
A low-cis polybutadiene rubber was prepared by the same procedure as in example 1, except that in the step (2), the amount of the coupling agent was as shown in Table 2, and the structural and property parameters of the resulting low-cis polybutadiene rubber were as shown in tables 3 and 4.
Comparative example 2
A low-cis polybutadiene rubber was prepared by the same procedure as in example 1, except that in the step (2), the amount of the coupling agent was as shown in Table 2, and the structural and property parameters of the resulting low-cis polybutadiene rubber were as shown in tables 3 and 4.
Comparative example 3
A low-cis polybutadiene rubber was prepared by the same procedure as in example 1, except that, in the step (2), methyltrichlorosilane as a coupling agent was replaced with an equimolar amount of dimethyldichlorosilane. The structural and property parameters of the resulting low cis polybutadiene rubber are set forth in tables 3 and 4.
Comparative example 4
A low-cis polybutadiene rubber was prepared in the same manner as in example 1, except that the amount of n-butyllithium used as the initiator in step (1) was 8mmol, and the amount of methyltrichlorosilane used in step (2) was 3.6 mmol. The structural and property parameters of the resulting low cis polybutadiene rubber are set forth in tables 3 and 4.
Comparative example 5
Low-cis polybutadiene linear polymers having number average molecular weights of 9.3 ten thousand, 18.8 ten thousand and 27.2 ten thousand were prepared in the same manner as in steps (1) and (3) of example 1, respectively (see Table 1 and Table 3 for specific reaction conditions), and the three linear polymers were mixed at a mass ratio of 9.3 ten thousand/18.8 ten thousand/27.2 ten thousand to 2.43/2.56/1 to obtain low-cis polybutadiene rubber linear copolymers having the structure and property parameters shown in tables 3 and 4.
TABLE 1
Figure BDA0002067355340000221
TABLE 2
Figure BDA0002067355340000231
TABLE 3
Figure BDA0002067355340000241
1: the sum of the areas of a peak corresponding to a high molecular weight component (i.e., a first peak), a peak corresponding to a medium molecular weight component (i.e., a second peak), and a peak corresponding to a low molecular weight component (i.e., a third peak) in a GPC curve is taken as a reference.
TABLE 4
Figure BDA0002067355340000242
1: X/Y, X being the viscosity of the low cis-polybutadiene rubber prepared in this example or comparative example in a 5 wt% styrene solution at 25 ℃, Y being the viscosity of the low molecular weight component of the low cis-polybutadiene rubber prepared in this example or comparative example in a 5 wt% styrene solution at 25 ℃.
2: the measurement was carried out by a plasma method.
3：AHNumber average molecular weight of the high molecular weight component/number average molecular weight of the low molecular weight component;
AMnumber average molecular weight of the medium molecular weight component/number average molecular weight of the low molecular weight component;
NH(peak area corresponding to high molecular weight component/number average molecular weight of high molecular weight component) ÷ (peak area corresponding to high molecular weight component/number average molecular weight of high molecular weight component + peak area corresponding to medium molecular weight component/number average molecular weight of medium molecular weight component + peak area corresponding to low molecular weight component/number average molecular weight of low molecular weight component);
NM(peak area corresponding to medium molecular weight component/number average molecular weight of medium molecular weight component) ÷ (peak area corresponding to high molecular weight component/number average molecular weight of high molecular weight component + peak area corresponding to medium molecular weight component/number average molecular weight of medium molecular weight component + peak area corresponding to low molecular weight component/number average molecular weight of low molecular weight component);
NL(peak area corresponding to low molecular weight component/number average molecular weight of low molecular weight component) ÷ (peak area corresponding to high molecular weight component/number average molecular weight of high molecular weight component + peak area corresponding to medium molecular weight component/number average molecular weight of medium molecular weight component + peak area corresponding to low molecular weight component/number average molecular weight of low molecular weight component).
As can be seen from Table 4, the low-cis polybutadiene rubber according to the present invention has a content of 3 times the number of coupling center atoms in comparison with (N) H×AH+NM×AM+NL) The ratio of (A) to (B) is greater than 1, which shows that most molecular chains contain coupling center atoms in the low cis-polybutadiene rubber, namely, not only the molecular chains of the high molecular weight component and the medium molecular weight component formed by coupling contain coupling center atoms, but also the molecular chains of the low molecular weight component basically contain coupling center atoms. Comparing example 1 with comparative example 5, it can be seen that the low cis polybutadiene rubber according to the present invention has a reduced viscosity and thus, better processability, compared with the mixture obtained by mixing three linear polymers. It can also be seen from Table 4 that the low cis-polybutadiene rubber according to the present invention has a low color and is suitable for use as a toughening agent for aromatic vinyl resins.
Experimental examples 1 to 9
Experimental examples 1-9 HIPS resin was prepared by a conventional bulk method using the low cis-polybutadiene rubbers prepared in examples 1-9 as a toughening agent, respectively, the toughening agent accounting for 8% of styrene monomer to obtain high impact polystyrene, and the specific polymerization method was:
mixing a toughening agent, styrene and a free radical initiator, carrying out polymerization with stirring, carrying out vacuum flash evaporation on a reaction product after the polymerization reaction is finished, removing unreacted monomers and a solvent to obtain the high impact polystyrene, wherein the polymerization reaction conditions are listed in Table 5, and the performance parameters of the prepared high impact polystyrene are listed in Table 6.
Experimental comparative examples 1 to 5
High impact polystyrene was prepared in the same manner as in experimental example 1, except that the low cis-polybutadiene prepared in comparative examples 1 to 5 was used as the toughening agent, respectively. The polymerization conditions are listed in Table 5 and the properties of the high impact polystyrene prepared are listed in Table 6.
Experimental comparative examples 6 to 7
High impact polystyrene was prepared in the same manner as in experimental example 1, except that Japanese Asahi chemical-formed products 720A and 730A (solvent-removed) were used as the toughening agent, respectively. The polymerization conditions are listed in Table 5 and the properties of the high impact polystyrene prepared are listed in Table 6.
Reference Experimental example 1
High impact polystyrene was prepared in the same manner as in experimental example 1, except that a toughening agent was not used. The performance parameters of the polymers prepared are listed in table 6.
TABLE 5
Figure BDA0002067355340000261
TABLE 6
Numbering Notched Izod impact Strength (kJ/m)2) Surface gloss (60 degree)
Experimental example 1 17.2 73
Experimental example 2 17.6 69
Experimental example 3 18.3 72
Experimental example 4 17.9 71
Experimental example 5 17.2 69
Experimental example 6 15.4 68
Experimental example 7 15.8 63
Experimental example 8 15.2 62
Experimental example 9 13.8 59
Experimental comparative example 1 12.6 62
Experimental comparative example 2 6.9 65
Experimental comparative example 3 11.5 62
Experimental comparative example 4 8.7 74
Experimental comparative example 5 14.9 42
Experimental comparative example 6 7.9 79
Experimental comparative example 7 10.8 74
Experimental reference example 1 1.2 94
It can be seen from the results in Table 6 that the high impact polystyrene prepared using the low cis polybutadiene rubber of the present invention as a toughening agent has good impact resistance while maintaining good gloss.
The preferred embodiments of the present invention have been described above in detail, but the present invention is not limited thereto. Within the scope of the technical idea of the invention, many simple modifications can be made to the technical solution of the invention, including combinations of various technical features in any other suitable way, and these simple modifications and combinations should also be regarded as the disclosure of the invention, and all fall within the scope of the invention.

Claims (25)

1. A low cis-polybutadiene rubber comprising a coupling center atom, a high molecular weight component, a medium molecular weight component and a low molecular weight component, the number average molecular weight of the high molecular weight component being 210,000-360,000, the number average molecular weight of the medium molecular weight component being 150,000-250,000, the number average molecular weight of the low molecular weight component being 80,000-120,000, the content of the high molecular weight component being 4-55 wt%, the content of the medium molecular weight component being 25-50 wt%, the content of the low molecular weight component being 5-70 wt% based on the total amount of the low cis-polybutadiene rubber.
2. The low-cis polybutadiene rubber as claimed in claim 1, wherein the number average molecular weight of the high molecular weight component is 230,000-350,000, preferably 240,000-330,000, more preferably 270,000-320,000; the number average molecular weight of the medium molecular weight component is 160,000-240,000, preferably 170,000-230,000, more preferably 180,000-220,000; the number average molecular weight of the low molecular weight component is 85,000-115,000, preferably 90,000-110,000;
preferably, the molecular weight distribution index of the high molecular weight component is 1 to 1.1, the molecular weight distribution index of the medium molecular weight component is 1 to 1.1, and the molecular weight distribution index of the low molecular weight component is 1 to 1.1.
3. The low-cis polybutadiene rubber according to claim 1 or 2, wherein the content of said high-molecular-weight component is 12 to 55% by weight, preferably 15 to 50% by weight, more preferably 18 to 45% by weight, based on the total amount of the low-cis polybutadiene rubber; the content of the medium molecular weight component is 30 to 50 wt%, preferably 35 to 48 wt%, and more preferably 40 to 45 wt%; the content of the low molecular weight component is 7 to 60% by weight, preferably 10 to 50% by weight, more preferably 15 to 42% by weight.
4. The low-cis polybutadiene rubber according to any one of claims 1-3, wherein the number average molecular weight of the low-cis polybutadiene rubber is 130,000-230,000, preferably 150,000-210,000;
preferably, the low cis-polybutadiene rubber has a molecular weight distribution index of 1.3 to 2.3.
5. The low cis-polybutadiene rubber according to any one of claims 1-4, wherein the viscosity of the low cis-polybutadiene rubber in a 5 wt% styrene solution at 25 ℃ is 90cP or more, preferably 100-200cP, more preferably 110-180cP, still more preferably 115-170 cP;
preferably, the low cis-polybutadiene rubber has a viscosity of X centipoise in a 5 wt% styrene solution at 25 ℃, the low molecular weight component of the low cis-polybutadiene rubber has a viscosity of Y centipoise in a 5 wt% styrene solution at 25 ℃, and the ratio of X/Y is 1 to 1.5, preferably 1.1 to 1.4.
6. The low-cis polybutadiene rubber according to any one of claims 1 to 5, wherein the Mooney viscosity at 100 ℃ of the low-cis polybutadiene rubber is 40 to 70, preferably 45 to 65, more preferably 48 to 60.
7. The low-cis polybutadiene rubber according to any one of claims 1-6, wherein the vinyl content of the low-cis polybutadiene rubber is 8-20 wt%, preferably 10-16 wt%.
8. The low-cis polybutadiene rubber according to any one of claims 1 to 7, wherein the content of cis 1, 4-structural units in the low-cis polybutadiene rubber is 30 to 40% by weight.
9. The low-cis polybutadiene rubber of any one of claims 1-8, wherein said high molecular weight component and said medium molecular weight component contain coupling center atoms, at least a portion of said low molecular weight component contains coupling center atoms, and said low molecular weight component is a linear polymer;
preferably, the coupling center atom is a silicon atom and/or a tin atom;
more preferably, the mass content of the coupling center atom is 88 to 245ppm, preferably 110-220ppm, more preferably 120-210ppm, based on the total amount of the low-cis polybutadiene rubber.
10. The low-cis polybutadiene rubber of claim 9, wherein the coupling central atom is derived from a coupling agent which is one or more of trifunctional coupling agents;
more preferably, the coupling agent is one or more than two of the coupling agents shown in the formula I,
Figure FDA0002067355330000031
in the formula I, R1Is C1-C6Alkyl of R2、R3And R4Is a dissociative group, preferably a halogen group, more preferably chlorine, and Z is a coupling center atom, preferably a silicon atom or a tin atom, more preferably a silicon atom;
Further preferably, the coupling agent is methyltrichlorosilane and/or ethyltrichlorosilane.
11. The low-cis polybutadiene rubber of claim 10, wherein the low-cis polybutadiene rubber has a molar percentage of coupling center atoms of NZThe molar percentage of the high molecular weight component is NHThe mol percentage of the medium molecular weight component is NMThe low molecular weight component is NLThe number of coupling arms of the high molecular weight component is AHThe number of coupling arms of the medium molecular weight component is AM，3(NH+NM+NL)≥(NZ×3)≥(NH×AH+NM×AM+NL)；
Preferably, (N)Z×3)/(NH×AH+NM×AM+NL) The ratio of (A) to (B) is 1-2.8;
more preferably, (N)Z×3)/(NH×AH+NM×AM+NL) The ratio of (A) to (B) is 1.1-2.5;
further preferably, (N)Z×3)/(NH×AH+NM×AM+NL) The ratio of (A) to (B) is 1.3-2.2;
still further preferably, (N)Z×3)/(NH×AH+NM×AM+NL) The ratio of (A) to (B) is 1.4-1.8.
12. A process for preparing a low-cis polybutadiene rubber, comprising the steps of:
(1) under the condition of anionic polymerization, in the presence of an organic lithium initiator and a structure regulator, polymerizing 1, 3-butadiene in an organic solvent to obtain a polymerization solution containing polybutadiene;
(2) contacting the polymerization solution with a coupling agent to carry out coupling reaction to obtain a coupling polymer solution, wherein the coupling agent is one or more than two of trifunctional coupling agents, and the molar weight of the coupling agent is n CThe molar weight of the organic lithium initiator is nI，(2.1×nI)≥(nC×3)＞nI。
13. The production method according to claim 12, wherein, in the step (2), n isC/nIThe ratio of (A) to (B) is 0.38-0.7: 1, preferably 0.42 to 0.65: 1, more preferably 0.45 to 0.6: 1.
14. the production method according to claim 12 or 13, wherein, in the step (2), the coupling reaction is carried out at a temperature of 50 to 100 ℃, the duration of the coupling reaction is 20 to 40 minutes, the coupling reaction is carried out at a pressure of 0.1 to 1MPa, and the pressure is a gauge pressure.
15. The production method according to any one of claims 12 to 14, wherein the coupling agent is one or more than two of the coupling agents represented by formula I,
Figure FDA0002067355330000041
in the formula I, R1Is C1-C6Alkyl of R2、R3And R4Is a dissociative group, preferably a halogen group, more preferably chlorine, and Z is a coupling center atom, preferably a silicon atom or a tin atom, more preferably a silicon atom;
further preferably, the coupling agent is methyltrichlorosilane and/or ethyltrichlorosilane.
16. The production method according to any one of claims 12 to 15, wherein the organolithium initiator is a compound represented by formula II,
R5li (formula II)
In the formula II, R5Is C1-C6Alkyl of (C) 3-C12Cycloalkyl of, C7-C14Aralkyl or C6-C12Aryl of (a);
preferably, the organolithium initiator is one or more of ethyllithium, n-propyllithium, isopropyllithium, n-butyllithium, sec-butyllithium, tert-butyllithium, n-pentyllithium, n-hexyllithium, cyclohexyllithium, phenyllithium, 2-naphthyllithium, 4-butylphenyl lithium, 4-methylphenyl lithium and 4-butylcyclohexyllithium;
preferably, in the step (1), the molar ratio of the 1, 3-butadiene to the organic lithium initiator is 1400-: 1, preferably 1500-: 1.
17. the production method according to any one of claims 12 to 16, wherein the structure-regulating agent is one or more of an ether-type structure-regulating agent and an amine-type structure-regulating agent;
preferably, the structure regulator is tetrahydrofuran, tetrahydrofurfuryl alkyl ether, ethylene glycol dialkyl ether, diethylene glycol dioxaneOne or more of alkyl ether, diethylene glycol dialkyl ether and amine type structure regulator, wherein the alkyl is preferably C1-C4An alkyl group;
more preferably, the structure regulator is one or more of tetrahydrofuran, tetrahydrofurfuryl methyl ether, tetrahydrofurfuryl ethyl ether, tetrahydrofurfuryl propyl ether, tetrahydrofurfuryl butyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether and N, N-dimethyltetrahydrofurfuryl amine;
Further preferably, the structure regulator is one or more than two of tetrahydrofurfuryl methyl ether, tetrahydrofurfuryl ethyl ether and tetrahydrofurfuryl propyl ether;
preferably, in step (1), the molar ratio of the structure modifier to the organolithium initiator is from 0.01 to 1: 1.
18. the production method according to any one of claims 12 to 17, wherein, in the step (1), the polymerization is carried out at a temperature of 0 to 100 ℃, preferably 40 to 95 ℃, the duration of the polymerization is 20 to 80 minutes, preferably 30 to 60 minutes, the polymerization is carried out at a pressure of 0.1 to 1MPa, preferably 0.2 to 0.5MPa, and the pressure is a gauge pressure.
19. The production method according to any one of claims 12 to 18, further comprising a step (3) of contacting the coupled polymer solution with a terminating agent to carry out a termination reaction;
preferably, the terminating agent is C1-C4Preferably, the alcohol, organic acid and carbon dioxide are one or more selected from isopropanol, stearic acid, citric acid and carbon dioxide.
20. A low-cis polybutadiene rubber prepared by the preparation process of claim 19.
21. The low-cis polybutadiene rubber as claimed in claim 20, wherein the low-cis polybutadiene rubber contains a high molecular weight component, a medium molecular weight component and a low molecular weight component, the number average molecular weight of the high molecular weight component being 210,000-360,000, preferably 230,000-350,000, more preferably 240,000-330,000, and further preferably 270,000-320,000; the number average molecular weight of the medium molecular weight component is 150,000-250,000, preferably 160,000-240,000, more preferably 170,000-230,000, and further preferably 180,000-220,000; the number average molecular weight of the low molecular weight component is 80,000-120,000, preferably 85,000-115,000, more preferably 90,000-110,000;
Preferably, the molecular weight distribution index of the high molecular weight component is 1 to 1.1, the molecular weight distribution index of the medium molecular weight component is 1 to 1.1, and the molecular weight distribution index of the low molecular weight component is 1 to 1.1;
preferably, the content of the high molecular weight component is 4 to 55% by weight, preferably 12 to 55% by weight, more preferably 15 to 50% by weight, still more preferably 18 to 45% by weight, based on the total amount of the low-cis polybutadiene rubber; the content of the medium molecular weight component is 25 to 50 wt%, preferably 30 to 50 wt%, more preferably 35 to 48 wt%, and further preferably 40 to 45 wt%; the content of the low-molecular weight component is 5 to 70% by weight, preferably 7 to 60% by weight, more preferably 10 to 50% by weight, and further preferably 15 to 42% by weight.
22. The low-cis polybutadiene rubber according to claim 20 or 21, wherein the number average molecular weight of the low-cis polybutadiene rubber is 130,000-230,000, preferably 150,000-210,000;
preferably, the low cis-polybutadiene rubber has a molecular weight distribution index of 1.3 to 2.3, preferably 1.5 to 2.1.
23. Use of the low cis polybutadiene rubber of any one of claims 1-11 and 20-22 as an aromatic vinyl resin toughening agent.
24. An aromatic vinyl resin comprising an aromatic vinyl base resin and a toughening agent, wherein the toughening agent is the low-cis polybutadiene rubber of any one of claims 1 to 11 and 20 to 22.
25. A method for preparing an aromatic vinyl resin, comprising: polymerizing an aromatic vinyl monomer in the presence of a toughening agent, wherein the toughening agent is the low cis-polybutadiene rubber of any one of claims 1-11 and 20-22.
CN201910425474.3A 2019-05-21 2019-05-21 Low cis-polybutadiene rubber, preparation method and application thereof, and aromatic vinyl resin and preparation method Active CN111978445B (en)