CN111875904A - Rapid decorative plate capable of releasing negative ions and manufacturing method thereof - Google Patents
Rapid decorative plate capable of releasing negative ions and manufacturing method thereof Download PDFInfo
- Publication number
- CN111875904A CN111875904A CN202010796625.9A CN202010796625A CN111875904A CN 111875904 A CN111875904 A CN 111875904A CN 202010796625 A CN202010796625 A CN 202010796625A CN 111875904 A CN111875904 A CN 111875904A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- weight
- environment
- decorative plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rapid decorative plate capable of releasing negative ions and a manufacturing method thereof, belonging to the technical field of decorative plate manufacturing, wherein the decorative plate body comprises 100 parts by weight of PVC resin powder, 100 parts by weight of stone powder, 150 parts by weight of bamboo wood powder, 50-75 parts by weight of bamboo wood powder, 30-50 parts by weight of diatomite, 3-4.5 parts by weight of an environment-friendly stabilizer, 5 parts by weight of an environment-friendly flame retardant, 1-2 parts by weight of an environment-friendly foaming agent, 1-2 parts by weight of negative ion powder, 5-8 parts by weight of a foaming regulator, 0.3-1.5 parts by weight of PE wax, 0.3-1.5 parts by weight of stearic acid and 1; compared with the prior art, the decorative plate has the advantages that the manufacturing process is simple, the decorative plate is firm in structure and not easy to crack, has good compression resistance and wear resistance, can resist bacteria, can release negative oxygen ions to purify air, remove formaldehyde, is beneficial to blood oxygen delivery and beneficial to human health, and has better effect when the negative ion powder is directly used as a raw material to manufacture the decorative plate.
Description
Technical Field
The invention relates to the technical field of decorative plate manufacturing, in particular to a quick decorative plate capable of releasing negative ions and a manufacturing method thereof.
Background
The wall decorative plate has wide application in industry and life, is formed by high-temperature hot melt plasticizing extrusion of bamboo powder and the like at present, and has the advantages of light weight and convenient installation.
The negative ions have a plurality of purposes, and have a plurality of advantages, such as purifying air, killing germs, improving sleep and the like.
In summary, the applicant provides a bamboo-wood quick decorative plate capable of releasing negative ions, which combines the bamboo-wood quick decorative plate and the bamboo-wood quick decorative plate into a whole.
Disclosure of Invention
Aiming at the problem that the decorative plate in the prior art does not have the negative ion release function, the quick decorative plate capable of releasing the negative ions and the manufacturing method thereof are provided.
In order to achieve the technical purpose, the technical scheme adopted by the invention is as follows:
the quick decorative plate capable of releasing negative ions comprises, by weight, 100 parts of PVC resin powder, 100 parts of stone powder and 150 parts of bamboo wood powder, 50-75 parts of bamboo wood powder, 30-50 parts of diatomite, 3-4.5 parts of an environment-friendly stabilizer, 5 parts of an environment-friendly flame retardant, 1-2 parts of an environment-friendly foaming agent, 1-2 parts of negative ion powder, 5-8 parts of a foaming regulator, 0.3-1.5 parts of PE wax, 0.3-1.5 parts of stearic acid and 1-3 parts of a bactericide.
The decorative plate body is further limited to comprise 100 parts of PVC resin powder, 125 parts of stone powder, 60 parts of bamboo wood powder, 40 parts of diatomite, 3.5 parts of environment-friendly stabilizer, 5 parts of environment-friendly flame retardant, 1.5 parts of environment-friendly foaming agent, 1.5 parts of anion powder, 7 parts of foaming regulator, 0.9 part of PE wax, 0.9 part of stearic acid and 1.5 parts of bactericide by weight.
Further limiting, the anion powder is tourmaline powder;
a method for manufacturing a quick decorative plate capable of releasing negative ions comprises the following manufacturing steps:
4.1 mixing PVC resin powder, stone powder, bamboo wood powder, diatomite, an environment-friendly stabilizer, an environment-friendly flame retardant, an environment-friendly foaming agent, anion powder, a foaming regulator, PE wax, stearic acid and a bactericide, and stirring the mixture in a stirring machine with 800-1400 revolutions/second at the temperature of 100-130 ℃ for 20-30 minutes;
4.2 directly extruding the mixture obtained in the step at the temperature of 150 ℃ and 200 ℃ through an extrusion die;
4.3 cooling the finished product extruded by the extruder, and then cutting the finished product by a cutting machine.
Compared with the prior art, the decorative plate has the beneficial effects that the manufacturing process is simple, the decorative plate is firm in structure and not easy to crack, has good compression resistance and wear resistance, can resist bacteria, can release negative oxygen ions to purify air, removes formaldehyde, is beneficial to blood oxygen delivery and beneficial to human health, and has better effect when the negative ion powder is directly used as a raw material to manufacture the decorative plate.
Detailed Description
In order that those skilled in the art can better understand the present invention, the following embodiments are provided to further illustrate the present invention.
Example 1:
a rapid decorative plate capable of releasing negative ions comprises 100 parts of PVC resin powder, 125 parts of stone powder, 60 parts of bamboo wood powder, 40 parts of diatomite, 3.5 parts of an environment-friendly stabilizer, 5 parts of an environment-friendly flame retardant, 1.5 parts of an environment-friendly foaming agent, 1.5 parts of negative ion powder, 7 parts of a foaming regulator, 0.9 part of PE wax, 0.9 part of stearic acid and 1.5 parts of a bactericide by weight; the anion powder is tourmaline powder;
the manufacturing steps of this embodiment are as follows:
4.1 mixing PVC resin powder, stone powder, bamboo wood powder, diatomite, an environment-friendly stabilizer, an environment-friendly flame retardant, an environment-friendly foaming agent, anion powder, a foaming regulator, PE wax, stearic acid and a bactericide, and stirring the mixture in a stirring machine with 800-1400 revolutions/second at the temperature of 100-130 ℃ for 20-30 minutes; preferably, the stirring temperature is 120 ℃, and the stirring speed is 1000 revolutions per second for 25 minutes;
4.2 directly extruding the mixture obtained in the step at the temperature of 150 ℃ and 200 ℃ through an extrusion die; preferably, the extrusion temperature is 180 ℃;
4.3 cooling the finished product extruded by the extruder, and then cutting the finished product by a cutting machine.
Example 2:
a rapid decorative plate capable of releasing negative ions comprises 100 parts of PVC resin powder, 110 parts of stone powder, 70 parts of bamboo wood powder, 50 parts of diatomite, 4 parts of an environment-friendly stabilizer, 5 parts of an environment-friendly flame retardant, 2 parts of an environment-friendly foaming agent, 2 parts of negative ion powder, 6 parts of a foaming regulator, 0.8 part of PE wax, 0.8 part of stearic acid and 1 part of a bactericide in a preferred weight ratio; the anion powder is tourmaline powder;
the manufacturing steps of this embodiment are as follows:
4.1 mixing PVC resin powder, stone powder, bamboo wood powder, diatomite, an environment-friendly stabilizer, an environment-friendly flame retardant, an environment-friendly foaming agent, anion powder, a foaming regulator, PE wax, stearic acid and a bactericide, and stirring the mixture in a stirring machine with 800-1400 revolutions/second at the temperature of 100-130 ℃ for 20-30 minutes; preferably, the stirring temperature is 130 ℃, and the stirring speed is 1200 r/s for 30 minutes;
4.2 directly extruding the mixture obtained in the step at the temperature of 150 ℃ and 200 ℃ through an extrusion die; the preferred extrusion temperature is 200 ℃;
4.3 cooling the finished product extruded by the extruder, and then cutting the finished product by a cutting machine.
Compared with the prior art, the decorative plate has the beneficial effects that the manufacturing process is simple, the decorative plate is firm in structure and not easy to crack, has good compression resistance and wear resistance, can resist bacteria, can release negative oxygen ions to purify air, removes formaldehyde, is beneficial to blood oxygen delivery and beneficial to human health, and has better effect when the negative ion powder is directly used as a raw material to manufacture the decorative plate.
The fast decorative plate capable of releasing negative ions and the manufacturing method thereof provided by the invention are described in detail above. The description of the specific embodiments is only intended to facilitate an understanding of the method of the invention and its core ideas. It should be noted that, for those skilled in the art, it is possible to make various improvements and modifications to the present invention without departing from the principle of the present invention, and those improvements and modifications also fall within the scope of the claims of the present invention.
Claims (4)
1. The utility model provides a swift decorative board of anion can release which characterized in that: the decorative plate body comprises, by weight, 100 parts of PVC resin powder, 100 parts of stone powder and 150 parts of bamboo wood powder, 50-75 parts of bamboo wood powder, 30-50 parts of diatomite, 3-4.5 parts of an environment-friendly stabilizer, 5 parts of an environment-friendly flame retardant, 1-2 parts of an environment-friendly foaming agent, 1-2 parts of anion powder, 5-8 parts of a foaming regulator, 0.3-1.5 parts of PE wax, 0.3-1.5 parts of stearic acid and 1-3 parts of a bactericide.
2. The quick decorative plate capable of releasing negative ions according to claim 1, wherein: the decorative plate body comprises, by weight, 100 parts of PVC resin powder, 125 parts of mountain flour, 60 parts of bamboo wood powder, 40 parts of diatomite, 3.5 parts of an environment-friendly stabilizer, 5 parts of an environment-friendly flame retardant, 1.5 parts of an environment-friendly foaming agent, 1.5 parts of anion powder, 7 parts of a foaming regulator, 0.9 part of PE wax, 0.9 part of stearic acid and 5 parts of a bactericide.
3. The rapid decoration plate capable of releasing negative ions as claimed in claim 2, wherein: the anion powder is tourmaline powder.
4. A method for manufacturing a quick decorative plate capable of releasing negative ions is characterized in that: the manufacturing steps are as follows:
4.1 mixing PVC resin powder, stone powder, bamboo wood powder, diatomite, an environment-friendly stabilizer, an environment-friendly flame retardant, an environment-friendly foaming agent, anion powder, a foaming regulator, PE wax, stearic acid and a bactericide, and stirring in a stirring machine with 800-1400 rpm for 20-30 minutes at the temperature of 100-130 ℃;
4.2 directly extruding the mixture obtained in the step at the temperature of 150 ℃ and 200 ℃ through an extrusion die;
4.3 cooling the finished product extruded by the extruder, and then cutting the finished product by a cutting machine.