CN111718619A - Production process of water-based environment-friendly nubuck black paste - Google Patents
Production process of water-based environment-friendly nubuck black paste Download PDFInfo
- Publication number
- CN111718619A CN111718619A CN202010450807.0A CN202010450807A CN111718619A CN 111718619 A CN111718619 A CN 111718619A CN 202010450807 A CN202010450807 A CN 202010450807A CN 111718619 A CN111718619 A CN 111718619A
- Authority
- CN
- China
- Prior art keywords
- percent
- water
- friendly
- nubuck
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of black pulp, in particular to a production process of water-based environment-friendly nubuck black pulp, which comprises the following components in percentage by weight: high pigment carbon black: 35 to 40 percent; environment-friendly glycerol: 4 to 5 percent; aqueous polymer dispersant: 3 to 5 percent; water-based defoaming agent: 0.2 to 0.5 percent; ammonia water neutralizer: 1 to 2 percent; penetrant: 4 to 6 percent; mildew preventive: 0.1 to 0.3 percent; water: 50 to 55 percent. The water-based environment-friendly nubuck black slurry prepared by the invention has high blackness, high tinting strength, high compatibility and long service life, has more advantages than the cost of the original oil nubuck black, has good blackness and wide intermiscibility in water-based rear-stage color changing application, does not contain APEO and can be generally used in a water-based system.
Description
Technical Field
The invention relates to the technical field of black pulp, in particular to a production process of water-based environment-friendly nubuck black pulp.
Background
The original oily nubuck black slurry product for nubuck leather contains about 70% of DMF organic solvent, has low blackness, poor coloring power and poor compatibility, is not used in a water-based system, and the surface of the original oily nubuck black slurry product for nubuck leather can be corroded by microorganisms after long-time use, so that the service life is short.
Disclosure of Invention
The invention aims to provide a production process of aqueous environment-friendly nubuck black pulp, which aims to solve the problems that the original oily nubuck black pulp product for nubuck leather provided by the background technology contains about 70% of DMF organic solvent, has low blackness, poor tinting strength and compatibility, and is not commonly used in an aqueous system.
In order to achieve the purpose, the invention provides the following technical scheme:
a production process of water-based environment-friendly nubuck black pulp comprises the following components in percentage by weight:
high pigment carbon black: 35 to 40 percent of
Environment-friendly glycerol: 4 to 5 percent
Aqueous polymer dispersant: 3 to 5 percent of
Water-based defoaming agent: 0.2 to 0.5 percent
Ammonia water neutralizer: 1 to 2 percent
Penetrant: 4 to 6 percent
Mildew preventive: 0.1 to 0.3 percent
Water: 50 to 55 percent.
Preferably, the composition comprises the following components in percentage by weight:
high pigment carbon black: 35 percent of
Environment-friendly glycerol: 4.5 percent
Aqueous polymer dispersant: 3.5 percent
Water-based defoaming agent: 0.5 percent
Ammonia water neutralizer: 1.8 percent
Penetrant: 4.5 percent
Mildew preventive: 0.2 percent of
Water: 50 percent.
Preferably, the composition comprises the following components in percentage by weight: high pigment carbon black: 36 percent
Environment-friendly glycerol: 4 percent of
Aqueous polymer dispersant: 3 percent of
Water-based defoaming agent: 0.2 percent of
Ammonia water neutralizer: 1.6 percent
Penetrant: 4 percent of
Mildew preventive: 0.2 percent of
Water: 51 percent.
Preferably, the composition comprises the following components in percentage by weight: high pigment carbon black: 37 percent of
Environment-friendly glycerol: 4 percent of
Aqueous polymer dispersant: 3 percent of
Water-based defoaming agent: 0.2 percent of
Ammonia water neutralizer: 1.6 percent
Penetrant: 4 percent of
Mildew preventive: 0.2 percent of
Water: 50 percent.
Preferably, the aqueous polymer dispersant is a water-soluble dispersion resin.
Preferably, the water-soluble dispersion resin is one or more of acrylic resin, epoxy resin, polyurethane and polyether aldehyde ketone resin.
Preferably, the aqueous defoamer is a silicone defoamer.
Preferably, the penetrant is a dye penetrant.
Preferably, the mildew preventive is an OBPA mildew preventive.
On the other hand, the invention also provides a preparation method of the water-based environment-friendly nubuck and extra-black color paste, which comprises the following steps:
s1: taking high-pigment carbon black, environment-friendly glycerol, a water-based high-molecular dispersing agent, a water-based defoaming agent, an ammonia water neutralizer, a penetrating agent, a mildew preventive and water according to weight percentage;
s2: adding water, environment-friendly glycerol, a water-based polymer dispersant, a water-based defoaming agent and an ammonia water neutralizer into the stirrer in sequence, and then uniformly stirring, wherein the rotation speed of the stirrer is 500-;
s3: continuously stirring, adding penetrant, stirring for 20-30min, and finally adding high-pigment carbon black;
s4: after all the materials are added, adjusting the rotating speed of the stirrer to 1500-200r/min, and stirring for 30 min;
s5: adding the mixed slurry into a high-precision sand mill to grind twice, so that the fineness of the slurry is below 10 mu m, and the grinding temperature is 50-60 ℃;
s6: and after grinding is finished, adding the ground slurry into a stirrer for secondary stirring, and adding a mildew preventive to obtain the water-based environment-friendly nubuck super black paste.
Compared with the prior art, the invention has the beneficial effects that: the water-based environment-friendly nubuck black pulp prepared by the production process of the water-based environment-friendly nubuck black pulp has high blackness, high tinting strength, high compatibility and long service life, has more advantages in cost than the cost of the original oil nubuck black, has good blackness and wide intermiscibility in water-based rear-stage color changing application, does not contain APEO and can be generally used in a water-based system. The aqueous polymer dispersant added in the invention disperses the slurry through steric hindrance obstacle, is less influenced by temperature and pH, and can prevent the slurry from flocculating in the processes of preparation, storage, use and transportation. The high molecular dispersant makes the pigment in the special black paste distributed evenly, improves the tinting strength and the covering power of the black paste, and the luster and the leveling property after the film is formed. The viscosity of the system can be obviously reduced by the water-based high-molecular dispersing agent, and when the dosage of the dispersing agent is optimal, the viscosity of the system is minimum. The rheological property of a dispersion system can be improved, the construction is convenient, the energy is saved, and the added mildew preventive has strong inhibiting and killing effects on bacteria, fungi and algae, and effectively prevents the microorganisms from causing mildew.
Detailed Description
The invention provides the following technical scheme:
a production process of water-based environment-friendly nubuck black pulp comprises the following components in percentage by weight:
high pigment carbon black: 35 to 40 percent of
Environment-friendly glycerol: 4 to 5 percent
Aqueous polymer dispersant: 3 to 5 percent of
Water-based defoaming agent: 0.2 to 0.5 percent
Ammonia water neutralizer: 1 to 2 percent
Penetrant: 4 to 6 percent
Mildew preventive: 0.1 to 0.3 percent
Water: 50 to 55 percent.
Specifically, the aqueous polymeric dispersant in the invention is water-soluble dispersion resin, and the water-soluble dispersion resin is one or more of acrylic resin, epoxy resin, polyurethane and polyether aldehyde ketone resin.
Further, the water-based defoaming agent is an organic silicon defoaming agent, the penetrating agent is a penetrating agent for dyeing, and the mildew preventive is an OBPA mildew preventive.
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1
A production process of water-based environment-friendly nubuck black pulp comprises the following components in percentage by weight:
high pigment carbon black: 35 percent of
Environment-friendly glycerol: 4.5 percent
Aqueous polymer dispersant: 3.5 percent
Water-based defoaming agent: 0.5 percent
Ammonia water neutralizer: 1.8 percent
Penetrant: 4.5 percent
Mildew preventive: 0.2 percent of
Water: 50 percent.
The preparation method of the water-based environment-friendly nubuck black pulp comprises the following steps:
s1: taking high-pigment carbon black, environment-friendly glycerol, a water-based high-molecular dispersing agent, a water-based defoaming agent, an ammonia water neutralizer, a penetrating agent, a mildew preventive and water according to weight percentage;
s2: adding water, environment-friendly glycerol, a water-based polymer dispersant, a water-based defoaming agent and an ammonia water neutralizer into the stirrer in sequence, and then uniformly stirring, wherein the rotation speed of the stirrer is 500-;
s3: continuously stirring, adding penetrant, stirring for 20-30min, and finally adding high-pigment carbon black;
s4: after all the materials are added, adjusting the rotating speed of the stirrer to 1500-200r/min, and stirring for 30 min;
s5: adding the mixed slurry into a high-precision sand mill to grind twice, so that the fineness of the slurry is below 10 mu m, and the grinding temperature is 50-60 ℃;
s6: and after grinding is finished, adding the ground slurry into a stirrer for secondary stirring, and adding a mildew preventive to obtain the water-based environment-friendly nubuck super black paste.
Example 2
A production process of water-based environment-friendly nubuck black pulp comprises the following components in percentage by weight:
high pigment carbon black: 36 percent
Environment-friendly glycerol: 4 percent of
Aqueous polymer dispersant: 3 percent of
Water-based defoaming agent: 0.2 percent of
Ammonia water neutralizer: 1.6 percent
Penetrant: 4 percent of
Mildew preventive: 0.2 percent of
Water: 51 percent.
The preparation method of the water-based environment-friendly nubuck black pulp comprises the following steps:
s1: taking high-pigment carbon black, environment-friendly glycerol, a water-based high-molecular dispersing agent, a water-based defoaming agent, an ammonia water neutralizer, a penetrating agent, a mildew preventive and water according to weight percentage;
s2: adding water, environment-friendly glycerol, a water-based polymer dispersant, a water-based defoaming agent and an ammonia water neutralizer into the stirrer in sequence, and then uniformly stirring, wherein the rotation speed of the stirrer is 500-;
s3: continuously stirring, adding penetrant, stirring for 20-30min, and finally adding high-pigment carbon black;
s4: after all the materials are added, adjusting the rotating speed of the stirrer to 1500-200r/min, and stirring for 30 min;
s5: adding the mixed slurry into a high-precision sand mill to grind twice, so that the fineness of the slurry is below 10 mu m, and the grinding temperature is 50-60 ℃;
s6: and after grinding is finished, adding the ground slurry into a stirrer for secondary stirring, and adding a mildew preventive to obtain the water-based environment-friendly nubuck super black paste.
Example 3
A production process of water-based environment-friendly nubuck black pulp comprises the following components in percentage by weight:
high pigment carbon black: 37 percent of
Environment-friendly glycerol: 4 percent of
Aqueous polymer dispersant: 3 percent of
Water-based defoaming agent: 0.2 percent of
Ammonia water neutralizer: 1.6 percent
Penetrant: 4 percent of
Mildew preventive: 0.2 percent of
Water: 50 percent.
The preparation method of the water-based environment-friendly nubuck black pulp comprises the following steps:
s1: taking high-pigment carbon black, environment-friendly glycerol, a water-based high-molecular dispersing agent, a water-based defoaming agent, an ammonia water neutralizer, a penetrating agent, a mildew preventive and water according to weight percentage;
s2: adding water, environment-friendly glycerol, a water-based polymer dispersant, a water-based defoaming agent and an ammonia water neutralizer into the stirrer in sequence, and then uniformly stirring, wherein the rotation speed of the stirrer is 500-;
s3: continuously stirring, adding penetrant, stirring for 20-30min, and finally adding high-pigment carbon black;
s4: after all the materials are added, adjusting the rotating speed of the stirrer to 1500-200r/min, and stirring for 30 min;
s5: adding the mixed slurry into a high-precision sand mill to grind twice, so that the fineness of the slurry is below 10 mu m, and the grinding temperature is 50-60 ℃;
s6: and after grinding is finished, adding the ground slurry into a stirrer for secondary stirring, and adding a mildew preventive to obtain the water-based environment-friendly nubuck super black paste.
Comparative example
A production process of water-based environment-friendly nubuck black pulp comprises the following components in percentage by weight:
high pigment carbon black: 30 percent of
Environment-friendly glycerol: 4.5 percent
Aqueous polymer dispersant: 3.5 percent
Water-based defoaming agent: 0.5 percent
Ammonia water neutralizer: 1.8 percent
Penetrant: 4.5 percent
Mildew preventive: 0.2 percent of
Water: and 55 percent.
The preparation method of the water-based environment-friendly nubuck black pulp comprises the following steps:
s1: taking high-pigment carbon black, environment-friendly glycerol, a water-based high-molecular dispersing agent, a water-based defoaming agent, an ammonia water neutralizer, a penetrating agent, a mildew preventive and water according to weight percentage;
s2: adding water, environment-friendly glycerol, a water-based polymer dispersant, a water-based defoaming agent and an ammonia water neutralizer into the stirrer in sequence, and then uniformly stirring, wherein the rotation speed of the stirrer is 500-;
s3: continuously stirring, adding penetrant, stirring for 20-30min, and finally adding high-pigment carbon black;
s4: after all the materials are added, adjusting the rotating speed of the stirrer to 1500-200r/min, and stirring for 30 min;
s5: adding the mixed slurry into a high-precision sand mill to grind twice, so that the fineness of the slurry is below 10 mu m, and the grinding temperature is 50-60 ℃;
s6: and after grinding is finished, adding the ground slurry into a stirrer for secondary stirring, and adding a mildew preventive to obtain the water-based environment-friendly nubuck super black paste.
The blackness, tinting strength, compatibility and service life of the aqueous environment-friendly nubuck black paste prepared in the 3 groups of examples and the comparative example are detected, and the results are shown in the following table:
from the above table, the water-based environment-friendly nubuck black pulp prepared by the production process of the water-based environment-friendly nubuck black pulp has high blackness, high tinting strength, high compatibility and long service life, has more advantages than the cost of the original oil nubuck black pulp, has good blackness and wide compatibility in water-based rear-stage color changing application, does not contain APEO and can be generally used in a water-based system.
The aqueous polymer dispersant added in the invention disperses the slurry through steric hindrance obstacle, is less influenced by temperature and pH, and can prevent the slurry from flocculating in the processes of preparation, storage, use and transportation. The high molecular dispersant makes the pigment in the special black paste distributed evenly, improves the tinting strength and the covering power of the black paste, and the luster and the leveling property after the film is formed. The viscosity of the system can be obviously reduced by the water-based high-molecular dispersing agent, and when the dosage of the dispersing agent is optimal, the viscosity of the system is minimum. The rheological property of a dispersion system can be improved, the construction is convenient, the energy is saved, and the added mildew preventive has strong inhibiting and killing effects on bacteria, fungi and algae, and effectively prevents the microorganisms from causing mildew.
The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, and the preferred embodiments of the present invention are described in the above embodiments and the description, and are not intended to limit the present invention. The scope of the invention is defined by the appended claims and equivalents thereof.
Claims (10)
1. A production process of water-based environment-friendly nubuck black pulp is characterized by comprising the following steps: comprises the following components in percentage by weight:
high pigment carbon black: 35 to 40 percent of
Environment-friendly glycerol: 4 to 5 percent
Aqueous polymer dispersant: 3 to 5 percent of
Water-based defoaming agent: 0.2 to 0.5 percent
Ammonia water neutralizer: 1 to 2 percent
Penetrant: 4 to 6 percent
Mildew preventive: 0.1 to 0.3 percent
Water: 50 to 55 percent.
2. The production process of the aqueous environment-friendly nubuck black pulp as claimed in claim 1, wherein: comprises the following components in percentage by weight:
high pigment carbon black: 35 percent of
Environment-friendly glycerol: 4.5 percent
Aqueous polymer dispersant: 3.5 percent
Water-based defoaming agent: 0.5 percent
Ammonia water neutralizer: 1.8 percent
Penetrant: 4.5 percent
Mildew preventive: 0.2 percent of
Water: 50 percent.
3. The production process of the aqueous environment-friendly nubuck black pulp as claimed in claim 1, wherein: comprises the following components in percentage by weight:
high pigment carbon black: 36 percent
Environment-friendly glycerol: 4 percent of
Aqueous polymer dispersant: 3 percent of
Water-based defoaming agent: 0.2 percent of
Ammonia water neutralizer: 1.6 percent
Penetrant: 4 percent of
Mildew preventive: 0.2 percent of
Water: 51 percent.
4. The production process of the aqueous environment-friendly nubuck black pulp as claimed in claim 1, wherein: comprises the following components in percentage by weight:
high pigment carbon black: 37 percent of
Environment-friendly glycerol: 4 percent of
Aqueous polymer dispersant: 3 percent of
Water-based defoaming agent: 0.2 percent of
Ammonia water neutralizer: 1.6 percent
Penetrant: 4 percent of
Mildew preventive: 0.2 percent of
Water: 50 percent.
5. The process for producing the aqueous environment-friendly nubuck black pulp according to any one of claims 1 to 4, wherein: the water-based polymer dispersant is water-soluble dispersion resin.
6. The production process of the aqueous environment-friendly nubuck black pulp as claimed in claim 5, wherein: the water-soluble dispersion resin is one or more of acrylic resin, epoxy resin, polyurethane and polyether-aldehyde-ketone resin.
7. The process for producing the aqueous environment-friendly nubuck black pulp according to any one of claims 1 to 4, wherein: the water-based defoaming agent is an organic silicon defoaming agent.
8. The process for producing the aqueous environment-friendly nubuck black pulp according to any one of claims 1 to 4, wherein: the penetrant is a penetrant for dyeing.
9. The process for producing the aqueous environment-friendly nubuck black pulp according to any one of claims 1 to 4, wherein: the mildew preventive is OBPA mildew preventive.
10. The process for producing the aqueous environment-friendly nubuck black pulp according to any one of claims 1 to 4, wherein: the preparation method comprises the following steps:
s1: taking high-pigment carbon black, environment-friendly glycerol, a water-based high-molecular dispersing agent, a water-based defoaming agent, an ammonia water neutralizer, a penetrating agent, a mildew preventive and water according to weight percentage;
s2: adding water, environment-friendly glycerol, a water-based polymer dispersant, a water-based defoaming agent and an ammonia water neutralizer into the stirrer in sequence, and then uniformly stirring, wherein the rotation speed of the stirrer is 500-;
s3: continuously stirring, adding penetrant, stirring for 20-30min, and finally adding high-pigment carbon black;
s4: after all the materials are added, adjusting the rotating speed of the stirrer to 1500-200r/min, and stirring for 30 min;
s5: adding the mixed slurry into a high-precision sand mill to grind twice, so that the fineness of the slurry is below 10 mu m, and the grinding temperature is 50-60 ℃;
s6: and after grinding is finished, adding the ground slurry into a stirrer for secondary stirring, and adding a mildew preventive to obtain the water-based environment-friendly nubuck super black paste.