CN111663349A - Preparation method of corrosion-resistant steel wire rope - Google Patents
Preparation method of corrosion-resistant steel wire rope Download PDFInfo
- Publication number
- CN111663349A CN111663349A CN202010483005.XA CN202010483005A CN111663349A CN 111663349 A CN111663349 A CN 111663349A CN 202010483005 A CN202010483005 A CN 202010483005A CN 111663349 A CN111663349 A CN 111663349A
- Authority
- CN
- China
- Prior art keywords
- steel wire
- steel
- wire rope
- wire
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a corrosion-resistant steel wire rope, which mainly comprises the following steps: step A: cleaning the steel; and B: and C, soaking the steel in phosphate solution: carrying out cold wire drawing on the steel; step D: heating the steel after cold wire drawing, and carrying out lead bath quenching after heating; step E: drawing a steel wire; step G: galvanizing the surface of the steel wire, winding the steel wire on a spool for stranding, twisting the steel wire into strands, and processing on a rope-combining machine to obtain the steel wire rope. According to the preparation method of the corrosion-resistant steel wire rope, the steel wire rope can be rapidly produced by using the method, the process of the steel wire rope produced by the method is simple, more labor is not needed, the labor can be greatly saved, the production cost is reduced, and the steel wire rope produced by the method has strong corrosion resistance, high quality and long service life.
Description
Technical Field
The invention relates to a preparation method of a corrosion-resistant steel wire rope, and belongs to the technical field of steel wire rope production.
Background
The steel wire rope is a spiral steel wire bundle formed by twisting steel wires with mechanical property and geometric dimension meeting requirements together according to a certain rule, and consists of the steel wires, a rope core and lubricating grease. The steel wire rope is a spiral rope which is formed by twisting a plurality of layers of steel wires into strands, and then twisting a certain number of strands by taking a rope core as a center. In a material handling machine for lifting, pulling, tensioning and carrying. The steel wire rope has the advantages of high strength, light dead weight, stable work, difficulty in breaking the whole steel wire rope, and reliable work, and the rope core mainly plays a role in supporting the steel wire rope so as to achieve a stable cross section structure. The rope core includes a steel core and a fiber core, the fiber core includes a natural fiber core such as sisal, jute, cotton and the like, and a synthetic fiber core includes polyethylene and polypropylene filaments and the like. The natural fiber core can store more lubricating grease, plays a role in lubricating the steel wire rope, prolongs the service life of the steel wire rope, and is relatively complex in production process and relatively high in manual use, so that the production cost is relatively high.
Disclosure of Invention
The invention aims to provide a preparation method of a corrosion-resistant steel wire rope, and aims to solve the problems that the existing steel wire rope is complex in production process and high in production cost due to the fact that a large number of workers are used in the prior art.
In order to achieve the purpose, the invention provides the following technical scheme: a preparation method of a corrosion-resistant steel wire rope mainly comprises the following steps:
step A: cleaning the steel in a cleaning agent for 20-40min to remove rust and oxides on the surface of the steel;
and B: putting the steel into phosphate solution, and soaking for 20-50 min;
and C: cold-drawing the steel through a hole with a diameter smaller than that of the steel, wherein the hole of the cold-drawing die is directly larger than the formed steel wire by 2-3 mm;
step D: heating the steel after cold wire drawing, and carrying out lead bath quenching after heating;
step E: cleaning the wire drawing die box, connecting the quenched steel wires on a butt welding machine of a corresponding type, welding the two steel wires from two ends in the same direction in a positive mode, polishing the weld joint by using a grinding machine after welding to ensure the strength of the weld joint, and frequently stirring the wire drawing powder in the wire drawing die box in the wire drawing process to ensure that the wire drawing powder is uniformly attached to the surfaces of the steel wires and the lubrication is kept good;
step F: heating the drawn steel wire in a vacuum furnace, annealing and taking up the steel wire;
step G: galvanizing the surface of the steel wire, winding the steel wire on a spool for stranding, twisting the steel wire into strands, and processing on a rope-combining machine to obtain the steel wire rope.
Preferably, the cleaning agent is any one of sulfuric acid, copper sulfate or silver nitrate with the mass fraction of 25%.
Preferably, the temperature of the patenting in the step D is 500-700 ℃, the running speed of the steel wire is 20-30m/min, and the strength reaches 1350-145-MPa.
Preferably, the water temperature of the wire-drawing die box in the step E is not more than 50 ℃.
Preferably, in the step C, a steel material with a carbon content of 0.8-0.9% and a diameter of 8mm is selected for cold drawing, the diameter after cold drawing is 2.8mm, 3.2mm, 36mm and 4.0mm, and the steel material is obtained by drawing through the following steps:
8 to 7 to 6 to 5.5 to 5 to 4.5 to 4 to 3.5 to 3 to 2.8, the diameter unit is mm, and the wire drawing speed is 5 m/s;
8 to 6 to 5.5 to 5 to 4.5 to 4 to 3.2, the diameter unit is mm, and the wire drawing speed is 5 m/s;
8 to 6 to 5.5 to 5 to 4.5 to 4.0 to 3.6, the diameter unit is mm, and the wire drawing speed is 5 m/s;
8 to 6 to 5.5 to 5 to 4.5 to 4.0, the diameter unit is mm, and the drawing speed is 5 m/s.
Preferably, the diameter of the steel wire drawn in the step E is 2.8mm, 2.4mm, 2.0mm and 1.8 mm; the method is characterized by comprising the following steps of:
4.0 to 3.5 to 3.0 to 2.8, the diameter unit is mm, and the wire drawing speed is 1 m/s;
3.6 to 3.2 to 2.8 to 2.4, the diameter unit is mm, and the wire drawing speed is 1 m/s;
3.2 to 2.8 to 2.4 to 2.0, the diameter unit is mm, and the wire drawing speed is 1 m/s;
2.8 to 2.4 to 2.0 to 1.8, the diameter unit is mm, and the wire drawing speed is 1 m/s.
Preferably, a steel wire rope oiling groove is arranged between the traction wheel and the take-up device of the rope combining machine in the step G, and the steel wire rope is oiled. After being oiled, the steel wire rope is uniformly wound on a spool of the take-up mechanism through the wire arranging mechanism. After twisting, the rope end of the steel wire rope is tightly tied by a soft steel wire and fixed on the wheel disc of the I-shaped wheel.
Compared with the prior art, the invention has the following beneficial effects:
according to the preparation method of the corrosion-resistant steel wire rope, the steel wire rope can be rapidly produced by using the method, the process of the steel wire rope produced by the method is simple, more labor is not needed, the labor can be greatly saved, the production cost is reduced, and the steel wire rope produced by the method has strong corrosion resistance, high quality and long service life.
Detailed Description
In order to make the technical solutions of the present invention more clear and definite for those skilled in the art, the present invention is further described in detail with reference to the following examples, but the embodiments of the present invention are not limited thereto.
The preparation method of the corrosion-resistant steel wire rope provided by the embodiment mainly comprises the following steps:
step A: cleaning the steel in a cleaning agent for 20-40min to remove rust and oxides on the surface of the steel;
and B: putting the steel into phosphate solution, and soaking for 20-50 min;
and C: cold-drawing the steel through a hole with a diameter smaller than that of the steel, wherein the hole of the cold-drawing die is directly larger than the formed steel wire by 2-3 mm;
step D: heating the steel after cold wire drawing, and carrying out lead bath quenching after heating;
step E: cleaning the wire drawing die box, connecting the quenched steel wires on a butt welding machine of a corresponding type, welding the two steel wires from two ends in the same direction in a positive mode, polishing the weld joint by using a grinding machine after welding to ensure the strength of the weld joint, and frequently stirring the wire drawing powder in the wire drawing die box in the wire drawing process to ensure that the wire drawing powder is uniformly attached to the surfaces of the steel wires and the lubrication is kept good;
step F: heating the drawn steel wire in a vacuum furnace, annealing and taking up the steel wire;
step G: galvanizing the surface of the steel wire, winding the steel wire on a spool for stranding, twisting the steel wire into strands, and processing on a rope-combining machine to obtain the steel wire rope.
The cleaning agent is any one of sulfuric acid, copper sulfate or silver nitrate with the mass fraction of 25%.
In the step D, the temperature of the patenting is 500-700 ℃, the running speed of the steel wire is 20-30m/min, and the strength reaches 1350-145-MPa.
And E, the water temperature of the wire-drawing die box does not exceed 50 ℃.
In the step C, steel with the carbon content of 0.8-0.9% and the diameter of 8mm is selected for cold drawing, the diameters after cold drawing are respectively 2.8mm, 3.2mm, 36mm and 4.0mm, and the steel is respectively drawn by the following procedures:
8 to 7 to 6 to 5.5 to 5 to 4.5 to 4 to 3.5 to 3 to 2.8, the diameter unit is mm, and the wire drawing speed is 5 m/s;
8 to 6 to 5.5 to 5 to 4.5 to 4 to 3.2, the diameter unit is mm, and the wire drawing speed is 5 m/s;
8 to 6 to 5.5 to 5 to 4.5 to 4.0 to 3.6, the diameter unit is mm, and the wire drawing speed is 5 m/s;
8 to 6 to 5.5 to 5 to 4.5 to 4.0, the diameter unit is mm, and the drawing speed is 5 m/s.
The diameter of the steel wire after drawing in the step E is 2.8mm, 2.4mm, 2.0mm and 1.8 mm; the method is characterized by comprising the following steps of:
4.0 to 3.5 to 3.0 to 2.8, the diameter unit is mm, and the wire drawing speed is 1 m/s;
3.6 to 3.2 to 2.8 to 2.4, the diameter unit is mm, and the wire drawing speed is 1 m/s;
3.2 to 2.8 to 2.4 to 2.0, the diameter unit is mm, and the wire drawing speed is 1 m/s;
2.8 to 2.4 to 2.0 to 1.8, the diameter unit is mm, and the wire drawing speed is 1 m/s.
And G, arranging a steel wire rope oil coating groove between the traction wheel and the take-up device of the rope combining machine, and coating oil on the steel wire rope. After being oiled, the steel wire rope is uniformly wound on a spool of the take-up mechanism through the wire arranging mechanism. After twisting, the rope end of the steel wire rope is tightly tied by a soft steel wire and fixed on the wheel disc of the I-shaped wheel.
The above description is only for the purpose of illustrating the present invention and is not intended to limit the scope of the present invention, and any person skilled in the art can substitute or change the technical solution of the present invention and its conception within the scope of the present invention.
Claims (7)
1. The preparation method of the corrosion-resistant steel wire rope is characterized by mainly comprising the following steps of:
step A: cleaning the steel in a cleaning agent for 20-40min to remove rust and oxides on the surface of the steel;
and B: putting the steel into phosphate solution, and soaking for 20-50 min;
and C: cold-drawing the steel through a hole with a diameter smaller than that of the steel, wherein the hole of the cold-drawing die is directly larger than the formed steel wire by 2-3 mm;
step D: heating the steel after cold wire drawing, and carrying out lead bath quenching after heating;
step E: cleaning the wire drawing die box, connecting the quenched steel wires on a butt welding machine of a corresponding type, welding the two steel wires from two ends in the same direction in a positive mode, polishing the weld joint by using a grinding machine after welding to ensure the strength of the weld joint, and frequently stirring the wire drawing powder in the wire drawing die box in the wire drawing process to ensure that the wire drawing powder is uniformly attached to the surfaces of the steel wires and the lubrication is kept good;
step F: heating the drawn steel wire in a vacuum furnace, annealing and taking up the steel wire;
step G: galvanizing the surface of the steel wire, winding the steel wire on a spool for stranding, twisting the steel wire into strands, and processing on a rope-combining machine to obtain the steel wire rope.
2. The method for producing a corrosion-resistant steel wire rope according to claim 1, characterized in that: the cleaning agent is any one of sulfuric acid, copper sulfate or silver nitrate with the mass fraction of 25%.
3. The method for producing a corrosion-resistant steel wire rope according to claim 1, characterized in that: the temperature of the patenting in the step D is 500-700 ℃, the running speed of the steel wire is 20-30m/min, and the strength reaches 1350-145-MPa.
4. The method for producing a corrosion-resistant steel wire rope according to any one of claims 1, characterized in that: and E, the water temperature of the wire-drawing die box does not exceed 50 ℃.
5. The method for producing a corrosion-resistant steel wire rope according to any one of claims 1, characterized in that: in the step C, steel with the carbon content of 0.8-0.9% and the diameter of 8mm is selected for cold drawing, the diameters after cold drawing are respectively 2.8mm, 3.2mm, 36mm and 4.0mm, and the steel is respectively drawn by the following procedures:
8 to 7 to 6 to 5.5 to 5 to 4.5 to 4 to 3.5 to 3 to 2.8, the diameter unit is mm, and the wire drawing speed is 5 m/s;
8 to 6 to 5.5 to 5 to 4.5 to 4 to 3.2, the diameter unit is mm, and the wire drawing speed is 5 m/s;
8 to 6 to 5.5 to 5 to 4.5 to 4.0 to 3.6, the diameter unit is mm, and the wire drawing speed is 5 m/s;
8 to 6 to 5.5 to 5 to 4.5 to 4.0, the diameter unit is mm, and the drawing speed is 5 m/s.
6. The method for producing a corrosion-resistant steel wire rope according to any one of claims 1, characterized in that: the diameters of the steel wires drawn in the step E are 2.8mm, 2.4mm, 2.0mm and 1.8 mm; the method is characterized by comprising the following steps of:
4.0 to 3.5 to 3.0 to 2.8, the diameter unit is mm, and the wire drawing speed is 1 m/s;
3.6 to 3.2 to 2.8 to 2.4, the diameter unit is mm, and the wire drawing speed is 1 m/s;
3.2 to 2.8 to 2.4 to 2.0, the diameter unit is mm, and the wire drawing speed is 1 m/s;
2.8 to 2.4 to 2.0 to 1.8, the diameter unit is mm, and the wire drawing speed is 1 m/s.
7. The method for producing a corrosion-resistant steel wire rope according to any one of claims 1, characterized in that: and G, arranging a steel wire rope oil coating groove between the traction wheel of the rope combining machine and the take-up device, and coating oil on the steel wire rope. After being oiled, the steel wire rope is uniformly wound on a spool of the take-up mechanism through the wire arranging mechanism. After twisting, the rope end of the steel wire rope is tightly tied by a soft steel wire and fixed on the wheel disc of the I-shaped wheel.