CN111600062A - Formation method for improving cycle life of silicon-carbon soft package lithium ion battery - Google Patents
Formation method for improving cycle life of silicon-carbon soft package lithium ion battery Download PDFInfo
- Publication number
- CN111600062A CN111600062A CN201910220449.1A CN201910220449A CN111600062A CN 111600062 A CN111600062 A CN 111600062A CN 201910220449 A CN201910220449 A CN 201910220449A CN 111600062 A CN111600062 A CN 111600062A
- Authority
- CN
- China
- Prior art keywords
- charging
- silicon
- battery cell
- lithium ion
- follows
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A formation method for improving the cycle life of a silicon-carbon soft package lithium ion battery comprises the steps of carrying out low-temperature standing treatment on a battery cell by adopting temperature control equipment; pressurizing the battery cell; charging the battery cell with gradient and small multiplying power, wherein the charging is carried out in the first stage to 6-15% of reversible capacity, and the charging current range is 0.02-0.05C; in the second stage, charging is carried out until the reversible capacity is 20-40%, and the charging current is 0.05-0.2 ℃; in the third stage, charging is carried out until the reversible capacity is 30-60%, and the charging current is 0.1-0.6 ℃; standing; aging; and (7) air exhaust and packaging. The invention solves the problems that the silicon-carbon material is easy to expand and the cycle performance of the silicon-carbon material is influenced in the prior art, and the process of the invention is adopted for the silicon-carbon soft package lithium ion battery, so that the compactness, the stability and the consistency of an SEI film are improved, the expansion of the silicon-carbon negative electrode material in the cycle process is inhibited to a certain extent, and the cycle performance of the battery is improved.
Description
Technical Field
The invention belongs to the technical field of manufacturing of soft package lithium ion batteries, and particularly relates to a formation method of a silicon-carbon soft package lithium ion battery, which is suitable for forming ring joints of the silicon-carbon soft package lithium ion battery and can obviously improve the cycle performance of the silicon-carbon soft package lithium ion battery.
Background
The development of new energy automobiles is a necessary way for the development of automobile industry in China under increasingly severe energy crisis and continuously increased environmental pollution pressure. The power battery is used as an energy storage and supply device and is a core component of the new energy automobile. The lithium ion battery becomes the first choice of the power battery due to the advantages of high energy density, long cycle life, environmental friendliness and the like.
At present, the improvement of the endurance mileage of the lithium ion battery is a focus of attention, so that the lithium ion battery with higher energy density needs to be developed. The conventional ternary cathode material is matched with a graphite cathode material, so that the material is mature, but the energy density is improved and the bottleneck is met, so that the development of the high-capacity silicon-carbon cathode is concerned. The silicon-carbon cathode material has the defects of large expansion coefficient and quick cycle attenuation in the later period. At present, the key research of technical personnel of various enterprises relates to coating modification of a silicon-carbon material, tubular or fibrous conductive agents such as silicon-carbon special glue and single-walled carbon nanotubes with excellent conductivity are used, and a special formation process is adopted to ensure more compact, uniform and stable SEI generation and the like so as to reduce the expansion degree of the silicon-carbon material as much as possible and improve the cycle performance of the silicon-carbon material.
Disclosure of Invention
The invention aims to provide a formation method for improving the cycle life of a silicon-carbon soft package lithium ion battery, which can improve the compactness and stability of an SEI (solid electrolyte interphase) film generated on the surface of a silicon-carbon negative electrode material.
The technical scheme of the invention comprises the following steps:
the method comprises the following steps: the battery cell is subjected to low-temperature standing treatment by adopting temperature control equipment, and the battery cell temperature in the formation process is as follows: the temperature is-15 to 15 ℃, and the standing time range is as follows: 12 h-24 h;
step two: pressurizing the battery cell, wherein the pressurizing pressure is as follows: 0.3-1 Mpa;
step three, charging the battery cell with gradient and small multiplying power:
in the first stage, the battery cell is charged with constant current: charging to 6-15% of reversible capacity, and the charging current range is 0.02-0.05C;
and in the second stage, the battery cell is subjected to constant current charging: charging to 20-40% of reversible capacity, and the charging current range is 0.05-0.2C;
and in the third stage, the battery cell is subjected to constant current charging: charging to 30-60% of reversible capacity, and charging current range is 0.1-0.6C;
step four, standing: the time is as follows: 24-48 h;
step five, aging: the aging temperature range is 25-45 ℃, and the aging time is 24-48 h;
sixthly, exhausting the battery cell under the vacuum degree of minus 60 to minus 95 kPa for the following time: 6-12 s, then packaging, wherein the packaging temperature is as follows: 160-190 ℃, and the packaging time is as follows: 4-8 s.
The final charge cut-off state of charge of the cell is 70% SOC.
Preferably, the temperature error is controlled to be +/-3 ℃ and the pressure error is controlled to be +/-0.01 MPa in the whole formation stage.
Compared with the prior art, the invention has the beneficial effects that:
1. according to the invention, the battery cell is subjected to low-temperature treatment in the steps, so that the SEI film is more compact and has stronger stability in the subsequent charging formation stage, and the expansion of the silicon-carbon negative electrode in the circulation process is further inhibited.
2. According to the invention, the pressurization treatment is carried out on the battery cell in the steps, so that the contact between the anode and the cathode and the diaphragm is more tight in the formation process, the migration path of lithium ions is effectively reduced, and meanwhile, the gas generated in the formation process can be discharged, and the abnormal conditions such as black spots and the like caused by the gas residue on the surface of the electrode plate are prevented.
3. According to the invention, the battery cell is charged with the gradient with small multiplying power in the third step, so that the compactness of the generated SEI film can be further ensured, meanwhile, the gas generated by side reaction can be relatively gentle, the gas can be discharged sufficiently, and the good contact between the anode and the cathode and the diaphragm and the uniformity and consistency of the SEI film can be ensured.
In conclusion, the invention provides a soft-package silicon-carbon lithium ion battery, which adopts a low-temperature, pressurized, gradient and small-rate charging formation process to improve the compactness, stability and consistency of an SEI film, so that the expansion of a silicon-carbon negative electrode material in a circulation process is inhibited to a certain extent, and the circulation performance of the battery is improved.
Drawings
FIG. 1 is a graph comparing the cycles at 25 deg.C, 1C/1C, 100% DOD for examples of the present invention and a prior art reference.
In the figure, curve 1 is the cycle curve of example 1 of the present invention, and the capacity retention rate decays to 80% after 690 cycles. Curve 2 is the cycle curve of the prior art reference example, with the capacity retention decaying to 80% at 297 cycles. Through comparison, the method for forming the silicon-carbon soft package lithium ion battery can obviously improve the cycle performance of the silicon-carbon soft package lithium ion battery.
Detailed Description
The invention will be further described with reference to specific examples in order to enhance the understanding and appreciation of the invention. It should be noted that the example is provided only for explaining the present invention, so as to facilitate the understanding of the preferred embodiments provided by the skilled person in the art, and not to limit the present invention, the present invention is not limited to the following embodiments, and some modifications and changes to the patent shall fall within the scope of the claims of the patent, i.e. equivalent changes made according to the claims of the present invention, and still fall within the scope covered by the present invention.
Example 1
A formation method for improving the cycle life of a silicon-carbon soft package lithium ion battery comprises the following steps:
the method comprises the following steps: setting the required temperature by adopting temperature control equipment, and carrying out low-temperature standing treatment on the battery cell for 12 h;
step two: pressurizing the battery cell in the formation process;
step three: charging the battery cell in a gradient small multiplying power manner;
the overall ambient temperature is: 15 ℃;
the pressurizing pressure of the battery cell is as follows: 0.4 MPa.
The method comprises the following steps of carrying out gradient small-magnification charging on the battery cell:
the first stage is as follows: constant current charging, wherein the charging is carried out until the reversible capacity is 10 percent, and the charging current is 0.02C;
and a second stage: constant current charging, wherein the charging is carried out until the reversible capacity is 30 percent, and the charging current is 0.08C;
and a third stage: and (4) constant-current charging, wherein the charging is carried out until the reversible capacity is 30%, and the charging current is 0.1C.
The final charge cut-off state of charge of the cell is 70% SOC.
The state of the whole formation stage of the battery cell is as follows: the temperature error is +/-3 ℃, and the pressure error is +/-0.01 MPa.
Step four, standing: the time is 24 h;
step five, aging: the aging temperature range is 25 ℃, and the aging time is 48 h.
Step six, performing air extraction on the battery cell under the vacuum degree of-85 kPa, wherein the air extraction time is as follows: 8 s, then packaging, wherein the packaging temperature is as follows: the packaging time is 6 s at 180 ℃.
Example 2
A formation method for improving the cycle life of a silicon-carbon soft package lithium ion battery comprises the following steps:
the method comprises the following steps: setting the required temperature by adopting temperature control equipment, and carrying out low-temperature standing treatment on the battery cell for 20 h;
step two: pressurizing the battery cell in the formation process;
step three: charging the battery cell in a gradient small multiplying power manner;
the overall ambient temperature is: 0 ℃ is used.
The pressurizing pressure of the battery cell is as follows: 0.6 MPa.
The method comprises the following steps of carrying out gradient small-magnification charging on the battery cell:
the first stage is as follows: constant current charging, wherein the charging is carried out until the reversible capacity is 15 percent, and the charging current is 0.03C;
and a second stage: constant current charging, wherein the charging is carried out until the reversible capacity is 20 percent, and the charging current is 0.05C;
and a third stage: and (4) constant-current charging, wherein the charging is carried out until the reversible capacity is 40%, and the charging current is 0.1C.
The final charge cut-off state of charge of the cell is 80% SOC.
The state of the whole formation stage of the battery cell is as follows: the temperature error is +/-3 ℃, and the pressure error is +/-0.01 MPa.
Step four, standing: the time is 30 h;
step five, aging: the aging temperature range is 40 ℃, and the aging time is 35 h.
Step six, air suction is carried out on the battery cell under the vacuum degree of-90 kPa, and the air suction time is as follows: 6 s, then packaging, wherein the packaging temperature is as follows: the packaging time was 5 s at 185 ℃.
Reference example
The conventional formation process is taken as a reference example:
the cell is not pressurized at room temperature, the cell is subjected to constant-current charging at the multiplying power of 0.05C during formation until the charging capacity reaches 15% of the reversible capacity of the cell, then the cell is subjected to constant-current charging at the multiplying power of 0.1C, and finally, the charging cut-off state of charge is 60% SOC.
Claims (3)
1. A formation method for improving the cycle life of a silicon-carbon soft package lithium ion battery is characterized by comprising the following steps:
the method comprises the following steps: the battery cell is subjected to low-temperature standing treatment by adopting temperature control equipment, and the battery cell temperature in the formation process is as follows: the temperature is-15 to 15 ℃, and the standing time range is as follows: 12 h-24 h;
step two: pressurizing the battery cell, wherein the pressurizing pressure is as follows: 0.3-1 Mpa;
step three, charging the battery cell with gradient and small multiplying power:
in the first stage, the battery cell is charged in a constant current manner until the reversible capacity is 6-15%, and the charging current range is 0.02-0.05 ℃;
and a second stage: charging the battery cell at a constant current until the reversible capacity is 20-40%, and the charging current is 0.05-0.2 ℃;
and a third stage: charging the battery cell at a constant current until the reversible capacity is 30-60%, and the charging current is 0.1-0.6 ℃;
step four, standing: the time is as follows: 24-48 h;
step five, aging: the aging temperature is 25-45 ℃ and the aging time is 24-48 h.
2. The formation method for improving the cycle life of the silicon-carbon soft package lithium ion battery according to claim 1, is characterized in that: the final charge cut-off state of charge of the cell is 70% SOC.
3. The formation method for improving the cycle life of the silicon-carbon soft package lithium ion battery according to claim 1, is characterized in that: and sixthly, exhausting the battery cell under the vacuum degree of-60 to-95 kPa for the following time: 6-12 s, then packaging, wherein the packaging temperature is as follows: 160-190 ℃, and the packaging time is as follows: 4-8 s.