CN111518458A - High-strength epoxy resin terrace material - Google Patents
High-strength epoxy resin terrace material Download PDFInfo
- Publication number
- CN111518458A CN111518458A CN202010510529.3A CN202010510529A CN111518458A CN 111518458 A CN111518458 A CN 111518458A CN 202010510529 A CN202010510529 A CN 202010510529A CN 111518458 A CN111518458 A CN 111518458A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- terrace material
- raw materials
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a high-strength epoxy resin terrace material which comprises the following raw materials in parts by weight: 35-45 parts of epoxy resin, 12-16 parts of styrene butadiene rubber, 14-20 parts of clay, 11-14 parts of dimethyl sebacate, 8-10 parts of ferric oxide, 2-4 parts of sodium gluconate, 2-4 parts of petroleum ether and 4-6 parts of carbon fiber. Compared with the prior art, the invention has the advantages that: high strength, pressure resistance, wear resistance, good stability, no influence of environmental conditions and strong applicability.
Description
Technical Field
The invention relates to the technical field of floor materials, in particular to a high-strength epoxy resin floor material.
Background
The terrace material has a wide application range, such as workshops, stadiums, meeting rooms, etc. Terrace materials have many functions such as water resistance, acid and alkali resistance, static electricity resistance and the like.
In order to adapt to more complex scenes, the wear-resistant and pressure-resistant performance of the terrace material needs to be improved, and the use strength of the terrace material is provided.
Disclosure of Invention
The invention aims to overcome the technical defects and provide a high-strength epoxy resin terrace material which has high strength, pressure resistance, wear resistance and good stability and is not influenced by environmental conditions.
In order to solve the technical problems, the technical scheme provided by the invention is as follows: the utility model provides a high strength epoxy terrace material, the raw materials include according to part by weight: 35-45 parts of epoxy resin, 12-16 parts of styrene butadiene rubber, 14-20 parts of clay, 11-14 parts of dimethyl sebacate, 8-10 parts of ferric oxide, 2-4 parts of sodium gluconate, 2-4 parts of petroleum ether and 4-6 parts of carbon fiber.
As an improvement, the raw materials comprise the following components in parts by weight: 40 parts of epoxy resin, 14 parts of butadiene styrene rubber, 17 parts of clay, 13 parts of dimethyl sebacate, 9 parts of ferric oxide, 3 parts of sodium gluconate, 3 parts of petroleum ether and 5 parts of carbon fiber.
And (3) putting the raw materials in parts by weight into a stirring kettle in sequence, and fully mixing and uniformly stirring to obtain the high-light epoxy resin terrace material.
Compared with the prior art, the invention has the advantages that:
the raw materials are simple in proportion and easy to produce and use in a standardized way;
the raw materials adopt carbon fibers, the carbon fibers have the characteristics of high temperature resistance, friction resistance, electric conduction, heat conduction, corrosion resistance and the like, are fibrous and soft in appearance, and can be processed into various fabrics;
the proper styrene butadiene rubber is added, so that the product has humidity elasticity and better use effect;
dimethyl sebacate is used as an intermediate for organic synthesis, so that the stable effect of the product can be ensured;
in addition, the added sodium gluconate can increase the plasticity and strength of the product, has a retarding effect and is convenient for construction and coating during specific use;
the terrace material prepared by the raw materials is wear-resistant and pressure-resistant, high in use strength and strong in adaptability, can be applied to various environments, can be integrally coated during use, is formed at one time, and is good in use effect.
Detailed Description
Example one
The utility model provides a high strength epoxy terrace material, the raw materials include according to part by weight: 40 parts of epoxy resin, 14 parts of butadiene styrene rubber, 17 parts of clay, 13 parts of dimethyl sebacate, 9 parts of ferric oxide, 3 parts of sodium gluconate, 3 parts of petroleum ether and 5 parts of carbon fiber.
And (3) putting the raw materials in parts by weight into a stirring kettle in sequence, and fully mixing and uniformly stirring to obtain the high-light epoxy resin terrace material.
Example two
The utility model provides a high strength epoxy terrace material which characterized in that, the raw materials include according to part by weight: 35 parts of epoxy resin, 12 parts of butadiene styrene rubber, 14 parts of clay, 11 parts of dimethyl sebacate, 8 parts of ferric oxide, 2 parts of sodium gluconate, 2 parts of petroleum ether and 4 parts of carbon fiber.
And (3) putting the raw materials in parts by weight into a stirring kettle in sequence, and fully mixing and uniformly stirring to obtain the high-light epoxy resin terrace material.
EXAMPLE III
The utility model provides a high strength epoxy terrace material, the raw materials include according to part by weight: 45 parts of epoxy resin, 16 parts of butadiene styrene rubber, 20 parts of clay, 14 parts of dimethyl sebacate, 10 parts of ferric oxide, 4 parts of sodium gluconate, 4 parts of petroleum ether and 6 parts of carbon fiber.
And (3) putting the raw materials in parts by weight into a stirring kettle in sequence, and fully mixing and uniformly stirring to obtain the high-light epoxy resin terrace material.
Claims (2)
1. The utility model provides a high strength epoxy terrace material which characterized in that, the raw materials include according to part by weight: 35-45 parts of epoxy resin, 12-16 parts of styrene butadiene rubber, 14-20 parts of clay, 11-14 parts of dimethyl sebacate, 8-10 parts of ferric oxide, 2-4 parts of sodium gluconate, 2-4 parts of petroleum ether and 4-6 parts of carbon fiber.
2. The high-strength epoxy resin terrace material according to claim 1, which is characterized by comprising the following raw materials in parts by weight: 40 parts of epoxy resin, 14 parts of butadiene styrene rubber, 17 parts of clay, 13 parts of dimethyl sebacate, 9 parts of ferric oxide, 3 parts of sodium gluconate, 3 parts of petroleum ether and 5 parts of carbon fiber.