CN111471414A - Special glue for single-component lens and preparation method thereof - Google Patents
Special glue for single-component lens and preparation method thereof Download PDFInfo
- Publication number
- CN111471414A CN111471414A CN202010546016.8A CN202010546016A CN111471414A CN 111471414 A CN111471414 A CN 111471414A CN 202010546016 A CN202010546016 A CN 202010546016A CN 111471414 A CN111471414 A CN 111471414A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- special
- component
- viscosity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a single-component special lens adhesive which is prepared from the following raw materials in parts by weight: 80000c.s viscosity 107 glue 66.5-71.8 parts, simethicone 16.5-20.8 parts, fumed silica 6.8-7.8 parts, ketoxime type cross-linking agent 4.6-5.4 parts, coupling agent 1.22-1.26 parts and catalyst 0.073-0.082 parts, relate to the technical field of organosilicon sealant, the special glue for one-component lenses of the invention is prepared by 80000c.s viscosity 107 glue, simethicone, fumed silica, ketoxime type cross-linking agent, coupling agent and catalyst through high-speed stirring and dispersing, the bonding effect to the lenses is good and the durability is good, no pollution and corrosion phenomenon appear, after the batch production of the product, the product can completely replace imported like products.
Description
Technical Field
The invention relates to the technical field of organosilicon sealants, in particular to a single-component special lens sealant and a preparation method thereof.
Background
The organic silicon sealant is widely used for bonding and sealing joints of glass, doors, windows and walls due to good elasticity, bonding property and aging resistance, wherein special requirements are required in the aspect of traditional lens bonding, corrosion and pollution to lenses cannot occur, the sealant mainly depends on import, for example, the neutral transparent sealant of the special lens rubber Wake is expensive, and therefore, the development of the single-component special lens sealant is necessary.
However, the applicant of the present invention finds that the prior art has at least the following technical problems:
the imported glue has the defects of high cost and insufficient supply of goods.
Disclosure of Invention
The embodiment of the invention provides a single-component special adhesive for lenses and a preparation method thereof, which solve the technical problems that the cost of the imported adhesive is high and the supply of goods is insufficient due to the adoption of the imported adhesive in the prior art, achieve good bonding effect and good durability on the lenses, and have no pollution and corrosion phenomena, and can completely replace the technical effect of imported similar products after the products are produced in batches.
In view of the above problems, the present invention provides a single-component lens dedicated adhesive and a preparation method thereof.
In a first aspect, the invention provides a single-component special lens adhesive which is prepared from the following raw materials in parts by weight: 80000c.s viscosity 107 glue 66.5-71.8 parts, simethicone 16.5-20.8 parts, fumed silica 6.8-7.8 parts, ketoxime type cross-linking agent 4.6-5.4 parts, coupling agent 1.22-1.26 parts and catalyst 0.073-0.082 part.
Preferably, the 80000c.s viscosity 107 glue is polysiloxane of 80000c.s viscosity; the dimethyl silicone oil is methyl terminated polysiloxane with 350c.s viscosity; the fumed silica is fumed silica.
Preferably, the ketoxime type cross-linking agent is methyl tributyrinoxime silane and vinyl tributyrinoxime silane.
Preferably, the ratio of methyl tributyrinoxime silane to vinyl tributyrinoxime silane is 3: 1.
Preferably, the coupling agent is r-aminopropyltriethoxysilane and N- (β -aminoethyl) -r-aminopropyltrimethoxysilane, and the catalyst is dibutyltin dilaurate.
Preferably, the ratio of r-aminopropyltriethoxysilane to N- (β -aminoethyl) -r-aminopropyltrimethoxysilane is 5: 1.
Preferably, the special rubber further comprises 1.8-2.2 parts of carbon black according to parts by weight.
Preferably, the special glue further comprises 4.5-5.5 parts of titanium dioxide according to parts by weight.
Preferably, the special glue further comprises 0.9-1.1 parts of silver powder according to parts by weight.
In a second aspect, the invention provides a preparation method of a single-component lens special-purpose adhesive, which comprises the following specific steps:
proportioning, namely proportionally adding 80000c.s viscosity 107 glue and simethicone into a cylinder of a high-speed dispersion machine;
pushing the prepared cylinder into a high-speed dispersion machine, starting up stirring, starting vacuum to a negative pressure value of-0.08 mpa, pumping a quantitative ketoxime type cross-linking agent into the cylinder by using the vacuum, keeping stirring in the period, and connecting a cooling system outside the cylinder;
after the stirring is uniform, the vacuum is relieved, quantitative fumed silica is added into a powder feeding port, the stirring speed is increased, and the stirring state is kept;
and after uniformly stirring, starting vacuum with the negative pressure value of-0.08 mpa, pumping a certain amount of the coupling agent and the catalyst into a cylinder by utilizing the vacuum, keeping stirring during the pumping, and removing bubbles in the vacuum to obtain the single-component special lens adhesive.
One or more technical solutions in the embodiments of the present application have at least one or more of the following technical effects:
according to the single-component special lens adhesive and the preparation method thereof, provided by the embodiment of the invention, the single-component special lens adhesive is prepared by 80000c.s viscosity 107 adhesive, dimethyl silicone oil, fumed silica, ketoxime type cross-linking agent, coupling agent and catalyst through high-speed stirring and dispersing, has a good bonding effect and good durability on lenses, and does not cause pollution and corrosion. After the product is produced in batches, the product can completely replace imported similar products.
The foregoing description is only an overview of the technical solutions of the present invention, and the embodiments of the present invention are described below in order to make the technical means of the present invention more clearly understood and to make the above and other objects, features, and advantages of the present invention more clearly understandable.
Drawings
FIG. 1 is a graph of tensile stress strain of a product obtained in example 1 of the present invention;
FIG. 2 is a graph of tensile stress strain of the product obtained in example 2 of the present invention;
FIG. 3 is a chromatogram of methyl tris (butanone oxime) silane as a ketoxime type crosslinking agent in example 3 of the present invention;
FIG. 4 is a chromatogram of vinyltributketoximosilane as a ketoxime type crosslinking agent in example 3 of the present invention.
Detailed Description
The embodiment of the invention provides a single-component special glue for lenses and a preparation method thereof, which are used for solving the technical problems that the cost of the imported glue is high and the supply of goods is insufficient due to the adoption of the imported glue in the prior art.
The technical scheme provided by the invention has the following general idea:
the invention provides a single-component special lens adhesive which is prepared from the following raw materials in parts by weight: 80000c.s viscosity 107 glue 66.5-71.8 parts, simethicone 16.5-20.8 parts, fumed silica 6.8-7.8 parts, ketoxime type cross-linking agent 4.6-5.4 parts, coupling agent 1.22-1.26 parts and catalyst 0.073-0.082 part. The invention achieves the technical effects of good bonding effect and good durability to the lens, no pollution and corrosion phenomena, and the product can completely replace imported similar products after batch production.
The technical solutions of the present invention are described in detail below with reference to the drawings and specific embodiments, and it should be understood that the specific features in the embodiments and examples of the present invention are described in detail in the technical solutions of the present application, and are not limited to the technical solutions of the present application, and the technical features in the embodiments and examples of the present application may be combined with each other without conflict.
Example 1
The composition is prepared from the following raw materials in parts by weight:
20000c.s107 glue-70.8 parts
350c.s Dimethylsilicone oil- -16.8 parts
7.8 portions of inlet L M-150 fumed silica
Ketoxime type crosslinking agent- -5 parts
Coupling agent- -1.25 parts
Catalyst- -0.08 part
The 20000c.s107 glue is polysiloxane with 20000c.s viscosity; the dimethyl silicone oil is methyl terminated polysiloxane with 350c.s viscosity; the fumed silica is fumed silica.
The ketoxime type cross-linking agent is methyl tributyl ketoxime silane and vinyl tributyrinoxime silane.
And the ratio of the methyl tributyrinoxime silane to the vinyl tributyrinoxime silane is 3: 1.
The coupling agent is r-aminopropyltriethoxysilane and N- (β -aminoethyl) -r-aminopropyltrimethoxysilane, and the catalyst is dibutyltin dilaurate.
And said r-aminopropyltriethoxysilane and N- (β -aminoethyl) -r-aminopropyltrimethoxysilane
The ratio of silane was 5: 1.
The preparation method comprises the following specific steps:
proportioning, namely, proportioning 20000c.s viscosity 107 glue and simethicone into a cylinder of a high-speed dispersion machine according to the above feeding amount and proportion;
pushing the prepared cylinder into a high-speed dispersion machine, starting up stirring, starting vacuum to a negative pressure value of-0.08 mpa, pumping a quantitative ketoxime type cross-linking agent into the cylinder by using the vacuum, keeping stirring in the period, and connecting a cooling system outside the cylinder;
after the stirring is uniform, the vacuum is relieved, quantitative fumed silica is added into a powder feeding port, the stirring speed is increased, and the stirring state is kept;
and after uniformly stirring, starting vacuum with the negative pressure value of-0.08 mpa, pumping a certain amount of the coupling agent and the catalyst into a cylinder by utilizing the vacuum, keeping stirring during the pumping, and removing bubbles in the vacuum to obtain the single-component special lens adhesive.
The sample glue was prepared according to the formulation of example 1 and the proprietary glue obtained by the procedure. The main performance tests were carried out on samples of 20000c.s107 glue according to the execution standard of silicone structural glue GB16776-2005, the failure form of the sample is cohesive failure, glass is used as bonding material, and the samples are made into 3 specifications, i.e. I-shaped pieces with the thickness of 12mm, the width of 50mm and the length of 12mm, and the test results are reported in the following table 1 and the attached figure 1:
table 1 tensile bond property test report
From the above Table 1 and with reference to FIG. 1, it can be seen that
The technical indexes are as follows: the tensile strength of the glue was 0.74Mpa and the elongation was 185.11%.
Example 2
The composition is prepared from the following raw materials in parts by weight:
80000c.s107 glue- -68.8 parts
350c.s Dimethylsilicone oil- -18.8 parts
Domestic H L-150 fumed silica-7.8 parts
Ketoxime type crosslinking agent- -5 parts
Coupling agent- -1.25 parts
Catalyst- -0.08 part
The 80000c.s107 gum is polysiloxane with 80000c.s viscosity; the dimethyl silicone oil is methyl terminated polysiloxane with 350c.s viscosity; the fumed silica is fumed silica.
The ketoxime type cross-linking agent is methyl tributyl ketoxime silane and vinyl tributyrinoxime silane.
And the ratio of the methyl tributyrinoxime silane to the vinyl tributyrinoxime silane is 3: 1.
The coupling agent is r-aminopropyltriethoxysilane and N- (β -aminoethyl) -r-aminopropyltrimethoxysilane, and the catalyst is dibutyltin dilaurate.
And said r-aminopropyltriethoxysilane and N- (β -aminoethyl) -r-aminopropyltrimethoxysilane
The ratio of silane was 5: 1.
The preparation method comprises the following specific steps:
proportioning, namely, adding 80000c.s viscosity 107 glue and simethicone into a cylinder of a high-speed dispersion machine according to the feeding amount and the proportion;
pushing the prepared cylinder into a high-speed dispersion machine, starting up stirring, starting vacuum to a negative pressure value of-0.08 mpa, pumping a quantitative ketoxime type cross-linking agent into the cylinder by using the vacuum, keeping stirring in the period, and connecting a cooling system outside the cylinder;
after the stirring is uniform, the vacuum is relieved, quantitative fumed silica is added into a powder feeding port, the stirring speed is increased, and the stirring state is kept;
and after uniformly stirring, starting vacuum with the negative pressure value of-0.08 mpa, pumping a certain amount of the coupling agent and the catalyst into a cylinder by utilizing the vacuum, keeping stirring during the pumping, and removing bubbles in the vacuum to obtain the single-component special lens adhesive.
The sample glue was prepared according to the formulation of example 2 and the proprietary glue obtained by the procedure. The main performance tests were carried out on samples of 80000c.s107 glue according to the execution standard of silicone structural glue GB16776-2005, with the sample failure mode being cohesive failure and glass being the bonding material, and made into 3 specifications of i-shaped pieces with a thickness of 12mm, a width of 50mm and a length of 12mm, and the test results are reported in table 2 below and in fig. 2 below:
table 2 tensile bond property test report
From the above table 2 and with reference to fig. 2, it can be derived
The technical indexes are as follows: the tensile strength of the glue was 0.87Mpa and the elongation was 202.81%.
Example 3
In the test process, the main material cross-linking agents of methyl tributyl ketoxime silane and vinyl tributyl ketoxime silane which affect the curing and the performance of the silicone adhesive are subjected to chromatographic analysis, and the results are as follows:
determination of content of methyl-tributyroximosilane
Vinyl tributyrinoxime silane content determination
The chromatographic analysis results can be obtained by combining the data with the attached figures 3 and 4
The content of the effective component of the (mono) methyl tributyl ketoxime silane is 95.6081%;
the content of the effective component of the (di) vinyl tributyroximo silane is 96.4073 percent.
In the schemes of the embodiments 1 and 2, the materials are selected and compared, mainly based on the performance index of the product, the reason for formulating the embodiment 1 is that the viscosity of 20000c.s107 rubber is relatively low, and the dispersing process has certain advantages (good mixing effect with fumed silica and insignificant heat generation during stirring), but the experimental results show that the performance on strength and maximum elongation is weaker than that of the embodiment 2, the effect of the product of the embodiment 2 can completely meet the technical index, the requirements of batch production can be met to solve the technical problems of high cost and insufficient supply of goods, and the reason for formulating the embodiment 2 is that 80000c.s107 rubber and dimethyl silicone oil are reasonably mixed, so that the mixing effect of the materials is optimized, and the overall performance of the rubber can be optimized. The results of the comprehensive tests show that example 2 meets the requirements in terms of operation and performance of the production process.
The invention has the beneficial effects that:
1. by using a silicone adhesive material (80000c.s, the viscosity of which is 107 glue, dimethyl silicone oil, fumed silica, a ketoxime type cross-linking agent, a coupling agent and a catalyst), the production operation process is simple, and the cost is much lower than that of an imported material;
2. the production period is short, and finished products can be obtained only by 80 minutes for each batch of 780 kg;
3. the index is controllable, and different color requirements can be produced according to the requirements of customers:
(1) bright black, adding carbon black, and accounting for weight parts, 1.8-2.2 parts;
(2) bright white, adding titanium dioxide, and accounting for weight parts, 4.5-5.5 parts;
(3) bright gray, adding silver powder, and accounting for weight parts, 0.9-1.1 parts.
4. The continuous production method is suitable for batch production.
It will be apparent to those skilled in the art that various changes and modifications may be made in the present invention without departing from the spirit and scope of the invention. Thus, if such modifications and variations of the present invention fall within the scope of the claims of the present invention and their equivalents, the present invention is also intended to include such modifications and variations.
Claims (10)
1. The utility model provides a special glue of single component lens which characterized in that: the composition is prepared from the following raw materials in parts by weight: 80000c.s viscosity 107 glue 66.5-71.8 parts, simethicone 16.5-20.8 parts, fumed silica 6.8-7.8 parts, ketoxime type cross-linking agent 4.6-5.4 parts, coupling agent 1.22-1.26 parts and catalyst 0.073-0.082 part.
2. The single-component glue special for lenses according to claim 1, characterized in that: the 80000c.s viscosity 107 glue is polysiloxane with 80000c.s viscosity; the dimethyl silicone oil is methyl terminated polysiloxane with 350c.s viscosity; the fumed silica is fumed silica.
3. The single-component glue special for lenses according to claim 1, characterized in that: the ketoxime type cross-linking agent is methyl tributyl ketoxime silane and vinyl tributyrinoxime silane.
4. The single-component glue special for lenses according to claim 3, characterized in that: the ratio of the methyl tributyrinoxime silane to the vinyl tributyrinoxime silane is 3: 1.
5. The special single-component adhesive for lenses as claimed in claim 1, wherein the coupling agent is r-aminopropyltriethoxysilane and N- (β -aminoethyl) -r-aminopropyltrimethoxysilane, and the catalyst is dibutyltin dilaurate.
6. The special single-component glue for lenses as claimed in claim 5, wherein the ratio of r-aminopropyltriethoxysilane to N- (β -aminoethyl) -r-aminopropyltrimethoxysilane is 5: 1.
7. The single-component glue special for lenses according to claim 1, characterized in that: the special rubber also comprises 1.8 to 2.2 parts of carbon black according to the parts by weight.
8. The single-component glue special for lenses according to claim 1, characterized in that: the special adhesive also comprises 4.5-5.5 parts of titanium dioxide according to parts by weight.
9. The single-component glue special for lenses according to claim 1, characterized in that: the special glue also comprises 0.9-1.1 parts of silver powder according to parts by weight.
10. A preparation method of a single-component special lens glue is characterized by comprising the following steps: the method comprises the following specific steps:
proportioning, namely proportionally adding 80000c.s viscosity 107 glue and simethicone into a cylinder of a high-speed dispersion machine;
pushing the prepared cylinder into a high-speed dispersion machine, starting up stirring, starting vacuum to a negative pressure value of-0.08 mpa, pumping a quantitative ketoxime type cross-linking agent into the cylinder by using the vacuum, keeping stirring in the period, and connecting a cooling system outside the cylinder;
after the stirring is uniform, the vacuum is relieved, quantitative fumed silica is added into a powder feeding port, the stirring speed is increased, and the stirring state is kept;
and after uniformly stirring, starting vacuum with the negative pressure value of-0.08 mpa, pumping a certain amount of the coupling agent and the catalyst into a cylinder by utilizing the vacuum, keeping stirring during the pumping, and removing bubbles in the vacuum to obtain the single-component special lens adhesive.