CN111468123A - Synthesis method of aniline compound - Google Patents
Synthesis method of aniline compound Download PDFInfo
- Publication number
- CN111468123A CN111468123A CN201910062904.XA CN201910062904A CN111468123A CN 111468123 A CN111468123 A CN 111468123A CN 201910062904 A CN201910062904 A CN 201910062904A CN 111468123 A CN111468123 A CN 111468123A
- Authority
- CN
- China
- Prior art keywords
- alkaline earth
- earth metal
- nitrobenzene
- carbon
- nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a synthesis method of aniline compounds, which comprises the following steps: the carbon-coated nickel nano composite material containing alkaline earth metal is used as a catalyst to catalyze nitrobenzene compounds to carry out hydrogenation reduction reaction in a hydrogen atmosphere; the nano composite material comprises a core-shell structure with a shell layer and an inner core, wherein the shell layer is a graphitized carbon layer containing alkaline earth metal and oxygen, and the inner core is nickel nano particles. The method adopts the carbon-coated nickel nanocomposite containing alkaline earth metal as the catalyst, the carbon material and the nickel nanoparticles act synergistically to produce a good catalytic effect, the alkaline earth metal of the shell layer further synergistically improves the catalytic performance of the material, and the catalyst is used for synthesizing the aniline compound by hydrogenation reduction of the nitrobenzene compound and has excellent activity, selectivity and safety.
Description
Technical Field
The invention belongs to the field of catalysis, and particularly relates to a synthesis method of an aniline compound.
Background
Aniline compounds are used as important organic synthesis intermediates, are widely applied to synthesis processes of chemicals such as medicines, pesticides, dyes, perfumes, daily chemicals and the like at present, occupy a very important position in the field of fine chemical engineering, and are widely applied to industries such as polyurethane, rubber auxiliaries, medicines, pesticides and explosives.
The synthesis process of aniline mainly comprises a nitrobenzene iron powder reduction method, a phenol ammonolysis method and a nitrobenzene catalytic hydrogenation method, and the production of aniline by nitrobenzene catalytic hydrogenation is the most widely applied process in the industry at present. The catalyst for catalyzing hydrogenation reaction of nitrobenzene is mainly noble metal catalysts such as platinum (Pt), palladium (Pd) and rhodium (Rh) and non-noble metal catalysts such as copper (Cu), nickel (Ni), lead (Zn) and molybdenum (Mo). However, in practical application, the noble metal catalyst has too high cost, and the loss of noble metal has great harm to the environment, so the application in industrial production is limited; non-noble metal supported catalysts also have a series of problems, such as easy agglomeration in the preparation process, easy elution in the catalytic hydrogenation process, poor stability, greater potential safety hazard and the like.
Therefore, it is desirable to provide a new aniline synthesis method to overcome the above problems.
It is noted that the information disclosed in the foregoing background section is only for enhancement of background understanding of the invention and therefore it may contain information that does not constitute prior art that is already known to a person of ordinary skill in the art.
Disclosure of Invention
The invention provides a synthesis method of aniline compounds, which adopts a carbon-coated nickel nanocomposite containing alkaline earth metal as a catalyst, wherein the nanocomposite is in a core-shell structure formed by coating nickel nanoparticles with a graphitized carbon layer containing alkaline earth metal and oxygen, a carbon material and the nickel nanoparticles act synergistically to produce a good catalytic effect, the alkaline earth metal of the shell layer further synergistically improves the catalytic performance of the material, and the catalyst is used for synthesizing aniline compounds by hydrogenation reduction of nitrobenzene compounds and has excellent activity, selectivity and safety.
In order to achieve the purpose, the invention adopts the following technical scheme:
the invention provides a synthesis method of aniline compounds, which comprises the following steps:
the carbon-coated nickel nano composite material containing alkaline earth metal is used as a catalyst to catalyze nitrobenzene compounds to carry out hydrogenation reduction reaction in a hydrogen atmosphere;
the nano composite material comprises a core-shell structure with a shell layer and an inner core, wherein the shell layer is a graphitized carbon layer containing alkaline earth metal and oxygen, and the inner core is nickel nano particles.
According to an embodiment of the present invention, wherein the nitrobenzene compound is substituted nitrobenzene, the substituent is selected from C1-20One or more of alkyl, cycloalkyl and aryl.
According to one embodiment of the present invention, the nitrobenzene compound is selected from one or more of nitrobenzene, 2, 6-dimethylnitrobenzene and p-isopropylnitrobenzene.
According to an embodiment of the present invention, the catalyst accounts for 1% to 50%, preferably 5% to 30% of the mass of the nitrobenzene compound.
According to one embodiment of the invention, the temperature of the hydrogenation reduction reaction is 60 ℃ to 120 ℃.
According to one embodiment of the present invention, the pressure of the hydrogen gas is 0.5 to 2 MPa.
According to one embodiment of the present invention, the reaction time is preferably 0.5h to 3 h.
According to one embodiment of the present invention, the catalyst and the nitrobenzene compound are mixed in a solvent and then subjected to a hydrogenation reduction reaction, wherein the solvent is selected from one or more of alcohols, ethers, alkanes and water.
According to one embodiment of the present invention, wherein the nanocomposite is a mesoporous material having at least one mesopore distribution peak. Optionally, the nanocomposite is a mesoporous material having two or more mesopore distribution peaks. Optionally, the nanocomposite material has a mesopore distribution peak in a pore size range of 2nm to 7nm and a pore size range of 8nm to 20nm, respectively. Optionally, wherein the mesopore material has a proportion of mesopore volume of more than 50%, preferably more than 80%, of the total pore volume.
According to an embodiment of the present invention, wherein the alkaline earth metal content is 0.1 at% to 3 at%, preferably 0.2 at% to 3 at%, in atomic percent; the carbon content is 80 at% to 95 at%, preferably 84 at% to 92 at%; the nickel content is 0.1 at% to 10 at%, preferably 1 at% to 8 at%; the oxygen content is 1 at% to 20 at%, preferably 5 at% to 12 at%.
According to the invention, the sum of the contents of the individual components in the nanocomposite material is 100 at%.
According to one embodiment of the present invention, the graphitized carbon layer has a thickness of 0.3nm to 6.0nm, preferably 0.3nm to 3 nm.
According to an embodiment of the present invention, the particle size of the core-shell structure is 1nm to 200nm, preferably 3nm to 100nm, more preferably 4nm to 50 nm.
According to an embodiment of the invention, wherein the alkaline earth metal is selected from one or more of beryllium (Be), magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba) and radium (Ra).
The invention has the beneficial effects that:
the method for synthesizing the aniline compound provided by the invention uses the carbon-coated nickel nano composite material containing alkaline earth metal as the catalyst to carry out hydrogenation reduction on the nitrobenzene compound, and the catalyst material is very stable, does not spontaneously combust, is resistant to oxidation and acid corrosion, has low danger and is suitable for storage and transportation, thereby ensuring the safety of the aniline compound synthesis process.
The carbon-coated nickel nanocomposite containing alkaline earth metal shows good repeatability, high activity and high selectivity in the reaction of catalytically reducing nitrobenzene compounds into aniline compounds, and the nickel coated in the graphitized carbon layer has a penetration effect, so that the electronic state of the alkaline earth metal loaded on the surface of the graphitized carbon layer is influenced, and a synergistic effect is exerted, so that the nanocomposite has good catalytic performance; in addition, the nano composite material has stronger magnetism, and can be conveniently used for separating a catalyst by utilizing the magnetism or used for processes such as a magnetic stabilization bed and the like.
Drawings
FIG. 1 is a photograph showing the magnetic properties of the alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 1;
FIG. 2 is a TEM image of an alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 1;
FIG. 3 is an XRD pattern of an alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 1;
FIGS. 4a and 4b respectively show N of the alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 12Adsorption-desorption isotherms and BJH pore size distribution curves;
FIG. 5 is a TEM image of an alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 2;
FIG. 6 is an XRD pattern of an alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 2;
FIG. 7 is a BJH pore size distribution curve of an alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 2;
FIG. 8 is a TEM image of an alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 3;
FIG. 9 is an XRD pattern of an alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 3;
fig. 10 is a BJH pore size distribution curve of the alkaline earth metal-containing carbon-coated nickel nanocomposite prepared in preparation example 3.
Detailed Description
The present invention is described in further detail below by way of specific embodiments in conjunction with the attached drawings, it being understood that the specific embodiments described herein are merely illustrative and explanatory of the invention and do not limit the invention in any way.
In the present invention, anything or matters not mentioned is directly applicable to those known in the art without any change except those explicitly described. Moreover, any embodiment described herein may be freely combined with one or more other embodiments described herein, and the technical solutions or ideas thus formed are considered part of the original disclosure or original description of the present invention, and should not be considered as new matters not disclosed or contemplated herein, unless a person skilled in the art would consider such combination to be clearly unreasonable.
All features disclosed in this invention may be combined in any combination and such combinations are understood to be disclosed or described herein unless a person skilled in the art would consider such combinations to be clearly unreasonable. The numerical points disclosed in the present specification include not only the numerical points specifically disclosed in the examples but also the endpoints of each numerical range in the specification, and ranges in which any combination of the numerical points is disclosed or recited should be considered as ranges of the present invention.
Any terms not directly defined herein should be understood to have meanings associated with them as commonly understood in the art of the present invention. The following terms as used throughout this specification should be understood to have the following meanings unless otherwise indicated.
Term(s) for
The term "alkyl" is defined herein as a straight or branched chain alkyl group such as methyl, ethyl, propyl, isopropyl, butyl, t-butyl, pentyl, hexyl and the like.
The term "cycloalkyl" is defined herein as an alkyl group connected by single bonds and constituting a ring, such as cyclohexyl.
The term "aryl" is defined herein as a functional group or substituent derived from a simple aromatic ring, such as benzyl.
The term "nitrobenzene-based compound" refers to a compound produced by substituting at least one hydrogen atom on a benzene ring with a nitro group, and the "nitrobenzene-based compound" includes nitrobenzene and substituted nitrobenzene containing only nitro substituents, and the "substituted nitrobenzene" refers to a compound containing one or more other substituents on the benzene ring in addition to the nitro substitution site.
The term "graphitized carbon layer" means a carbon structure in which a layered structure is clearly observed under a high-resolution transmission electron microscope, not an amorphous structure, and the interlayer distance is about 0.34 nm. The composite material formed after the graphitized carbon layer is coated with the nickel nano particles is spherical or quasi-spherical.
The term "mesoporous" is defined as a pore having a pore diameter in the range of 2 to 50 nm. Pores with a pore size of less than 2nm are defined as micropores and pores with a pore size of more than 50nm are defined as macropores.
The term "mesoporous material" is defined as a porous material comprising a mesoporous channel structure.
The terms "alkaline earth metal" and "oxygen" in the "graphitized carbon layer containing alkaline earth metal and oxygen" refer to alkaline earth metal elements and oxygen elements, wherein the "alkaline earth metal content" of the nanocomposite refers to the content of the alkaline earth metal elements, and the "oxygen content" refers to the content of the oxygen elements, and specifically refers to the content of the alkaline earth metal elements and the oxygen elements in various forms in the graphitized carbon layer formed in the preparation process of the carbon-coated nanocomposite, wherein the "alkaline earth metal content" is the total content of all forms of the alkaline earth metal elements, and the "oxygen content" is the total content of all forms of the oxygen elements. The "alkaline earth metal content" and "oxygen content" were determined by XPS method.
The term "mesopore distribution peak" refers to a mesopore distribution peak on a pore distribution curve calculated from a desorption curve according to the Barrett-Joyner-Halenda (BJH) method.
The term "TOF" is defined herein as the amount of a reactant converted per unit time by a single active metal atom, and TOF measures the rate at which a catalyst catalyzes a reaction and indicates the intrinsic activity of the catalyst.
Reagents, instruments and tests
Unless otherwise specified, all reagents used in the invention are analytically pure, and all reagents are commercially available.
The XRD diffractometer adopted by the invention is an XRD-6000X-ray powder diffractometer (Shimadzu Japan), and the XRD test conditions are Cu target, K α ray (the wavelength lambda is 0.154nm), tube voltage is 40kV, tube current is 200mA, and scanning speed is 10 degrees (2 theta)/min.
The high-resolution transmission electron microscope (HRTEM) adopted by the invention is JEM-2100(HRTEM) (Nippon electronics Co., Ltd.), and the test conditions of the high-resolution transmission electron microscope are as follows: the acceleration voltage was 200 kV.
The X-ray photoelectron spectrum analyzer (XPS) is an ESCA L ab220i-X L type electron spectrum analyzer which is produced by VG scientific company and is provided with Avantage V5.926 software, the X-ray photoelectron spectrum analyzer has the analysis and test conditions that an excitation source is monochromized A1K α X-rays, the power is 330W, and the basic vacuum is 3 × 10 during analysis and test-9mbar. In addition, the electron binding energy was corrected with the C1s peak (284.6eV), and the late peak processing software was XPSPEAK.
BET test method: in the invention, the pore structure property of a sample is measured by a Quantachrome AS-6B type analyzer, the specific surface area and the pore volume of the catalyst are obtained by a Brunauer-Emmett-Taller (BET) method, and the pore distribution curve is obtained by calculating a desorption curve according to a Barrett-Joyner-Halenda (BJH) method.
In the invention, after the average particle diameter of the metal nanoparticles is divided into peaks by an XRD (X-ray diffraction) pattern, the average particle diameter is calculated according to the Sherle formula: d ═ k γ/(B cos θ) was calculated. Wherein k is Scherrer constant, k is 0.89; b is half-height width; theta is the diffraction angle, unit radian; gamma is the x-ray wavelength, 0.154054 nm.
The invention provides a synthesis method of aniline compounds, which comprises the following steps:
the method comprises the following steps of (1) catalyzing nitrobenzene compounds to perform hydrogenation reduction reaction in a hydrogen atmosphere by using a carbon-coated nickel nanocomposite containing alkaline earth metal as a catalyst, wherein the chemical reaction formula is shown as follows, wherein R represents one or more substituent groups on a benzene ring; the nitrobenzene compounds also comprise nitrobenzene which does not contain a substituent R:
the nano composite material comprises a core-shell structure with a shell layer and an inner core, wherein the shell layer is a graphitized carbon layer containing alkaline earth metal and oxygen, and the inner core is nickel nano particles.
In some embodiments, the nitrobenzene compound further comprises a substituent on the benzene ring, and the substituent is selected from C1-20One or more of alkyl, cycloalkyl, and aryl. Such as p-isopropylnitrobenzene, the above substitution may be mono-or poly-substituted, such as 2, 6-dimethylnitrobenzene.
In some embodiments, the catalyst accounts for 1% to 50%, preferably 5% to 30% of the mass of the nitrobenzene compound.
In some embodiments, the temperature of the hydrogenation reduction reaction is generally in the range of 60 ℃ to 120 ℃.
In some embodiments, the pressure of the hydrogen is generally from 0.5MPa to 2 MPa.
In some embodiments, the hydrogenation reduction reaction is performed after the catalyst and the nitrobenzene compound are mixed in a solvent, wherein the solvent is selected from one or more of alcohols, ethers, alkanes and water, such as ethanol, tetrahydrofuran, cyclohexane, and the like.
According to one embodiment of the present invention, the nanocomposite of the present invention is a composite material composed of a "graphitized carbon layer containing an alkaline earth metal and oxygen", a "nickel nanoparticle that is tightly coated with (not in contact with) the graphitized carbon layer", and a "nickel nanoparticle that can be in contact with and confined to the outside". The carbon material has catalytic activity, and the nickel coated in the graphitized carbon layer has penetration effect, so that the electronic state of alkaline earth metal loaded on the surface of the graphitized carbon layer is influenced, and the nano composite material plays a synergistic role, so that the nano composite material has better catalytic performance.
In some embodiments, wherein the nanocomposite is a mesoporous material having at least one mesopore distribution peak. That is, the nano composite material has at least one mesoporous distribution peak on a pore distribution curve obtained by calculating a desorption curve according to a Barrett-Joyner-Halenda (BJH) method. As known to those skilled in the art, mesoporous materials generally have large specific surface areas and relatively regular channel structures, so that the mesoporous materials can play better roles in separation, adsorption and catalytic reactions of macromolecules and can be used as microreactors for limited-domain catalysis. The nano composite material has rich mesoporous structure, so that the nano composite material has higher mass transfer efficiency and more excellent catalytic performance.
In some embodiments, the batch-produced composite has two distribution peaks in the mesoporous range; if a plurality of batches of the composite material are mixed, more distribution peaks can be obtained in the mesoporous range. When the nano composite material has the multilevel mesoporous structure with different aperture ranges, the nano composite material can show more unique performance, and the applicable application range of the multilevel mesoporous structure is wider.
According to the nanocomposite material of the present invention, in some embodiments, the mesoporous structure has one mesoporous distribution peak in mesoporous ranges of 2nm to 5nm and 6nm to 15nm, respectively.
According to the nanocomposite material of the present invention, in some embodiments, the mesoporous structure has one mesoporous distribution peak in mesoporous ranges of 2nm to 7nm and 8nm to 20nm, respectively.
In some embodiments, the proportion of mesopore volume in the composite material to the total pore volume is greater than 50%, preferably greater than 80%, according to the nanocomposite material of the present invention. In some embodiments, the proportion of mesopore volume to the total pore volume is greater than 90%, and even 100%.
According to the nanocomposite material of the present invention, in some embodiments, the mesoporous volume thereof may be 0.05cm3/g~1.25cm3Per g, also may be 0.10cm3/g~0.30cm3/g。
The nanocomposites according to the invention, in some embodiments, have specific surface areas generally greater than 140m2/g, may be greater than 200m2/g。
The nanocomposites according to the invention, which are not pyrophoric in air, can be stored in air.
According to the nanocomposite of the invention, in some embodiments, the carbon layer of the composite is doped with an oxygen element and not with a nitrogen element.
According to the nanocomposite material of the invention, in some embodiments, the carbon layer of the composite material is doped with only oxygen, and is not doped with other elements than hydrogen and oxygen.
In some embodiments, wherein the alkaline earth metal content is 0.1 at% to 3 at%, preferably 0.2 at% to 3 at%, as measured by XPS; the carbon content is 80 at% to 95 at%, preferably 84 at% to 92 at%; the nickel content is 0.1 at% to 10 at%, preferably 1 at% to 8 at%; the oxygen content is 1 at% to 20 at%, preferably 5 at% to 12 at%.
According to the invention, the sum of the contents of the individual components in the nanocomposite material is 100 at%.
According to the nanocomposite material of the present invention, the graphitized carbon layer is doped with oxygen. The oxygen content can be adjusted by additionally introducing an oxygen-containing compound, such as a polyol, during the manufacturing process. The catalytic performance of the graphitized carbon layer can be adjusted by adjusting the oxygen content in the nano composite material, so that the graphitized carbon layer is suitable for catalyzing different reactions. In some embodiments, the oxygen content in the nanocomposite is less than 15.0%, preferably 5% to 12%, by mass.
According to one embodiment of the present invention, the graphitized carbon layer has a thickness of 0.3nm to 6.0nm, preferably 0.3nm to 3 nm.
According to an embodiment of the present invention, the particle size of the core-shell structure is 1nm to 200nm, preferably 3nm to 100nm, more preferably 4nm to 50 nm.
In some embodiments, wherein the alkaline earth metal is selected from one or more of beryllium (Be), magnesium (Mg), calcium (Ca), strontium (Sr), barium (Ba), and radium (Ra).
The invention also provides a preparation method of the nano composite material, which comprises the following steps:
putting nickel salt and polybasic organic carboxylic acid into a solvent to be mixed to form a homogeneous solution;
removing the solvent in the homogeneous solution to obtain a precursor;
carrying out primary pyrolysis on the precursor in an inert atmosphere or a reducing atmosphere;
contacting the product after the primary pyrolysis with a solution containing the alkaline earth metal, and then carrying out drying treatment; and the contact mode comprises the step of immersing the product after the primary pyrolysis in the alkaline earth metal solution, or the step of placing the product after the primary pyrolysis in the alkaline earth metal solution for stirring. The time for dipping or stirring is not suitable to be too long or too short, preferably between 10min and 300min, the temperature is preferably between 0 ℃ and 100 ℃, and the contact reaction is preferably carried out under the condition of stirring. According to the invention, the product after primary pyrolysis can be filtered or not after being contacted with the solution containing alkaline earth metal, and then the obtained product is dried;
and putting the dried product in an inert atmosphere for secondary pyrolysis to obtain the carbon-coated nickel nanocomposite containing the alkaline earth metal.
Specifically, the precursor is a water-soluble mixture, which means that nickel salt and polybasic organic carboxylic acid are dissolved into a homogeneous solution in a solvent such as water and/or ethanol, and then the solvent is directly removed to obtain the nickel-containing precursor. The solvent may be removed by evaporation, and the temperature and process of evaporation of the solvent may be by any available art, for example, spray drying at 80 ℃ to 120 ℃ or drying in an oven.
In some embodiments, wherein the nickel salt is selected from one or more of an organic acid salt, a carbonate salt, and a basic carbonate salt of nickel, the organic acid salt of nickel is preferably an organic carboxylate salt of nickel that is free of heteroatoms, more preferably an acetate salt of the nickel that is free of heteroatoms, wherein the heteroatoms refer to metal atoms other than the nickel.
In some embodiments, wherein the poly-organic carboxylic acid is selected from one or more of citric acid, maleic acid, trimesic acid, terephthalic acid, malic acid, ethylenediaminetetraacetic acid (EDTA), and dipicolinic acid. Wherein the mass ratio of the nickel salt to the polybasic organic carboxylic acid is 1: 0.1-10, preferably 1: 0.5-5, and more preferably 1: 0.8-3.
In some embodiments, the method further comprises mixing the nickel salt, the polybasic organic carboxylic acid and other organic compounds except the nickel salt and the polybasic organic carboxylic acid in a solvent such as water, ethanol and the like to form a homogeneous solution, and then removing the solvent to obtain the water-soluble mixture containing nickel. Such other organic compounds include, but are not limited to, organic polyols. In some embodiments, the mass ratio of the nickel salt, the polybasic organic carboxylic acid and the other organic compound is 1: 0.5-10: 0-10, preferably 1: 1-3: 0-3.
In some embodiments, wherein the primary pyrolysis comprises: heating the precursor to a constant temperature section in an inert atmosphere or a reducing atmosphere, and keeping the constant temperature in the constant temperature section;
wherein the heating rate is 0.5-30 ℃/min, preferably 1-10 ℃/min; the temperature of the constant temperature section is 400-800 ℃, and preferably 500-800 ℃; the constant temperature time is 20min to 600min, preferably 30min to 300 min; the inert atmosphere is nitrogen or argon, and the reducing atmosphere is a mixed gas of an inert gas and hydrogen, for example, a small amount of hydrogen is doped in the inert atmosphere.
In some embodimentsThe alkaline earth metal solution is a solution containing a salt and/or a base of an alkaline earth metal, for example, magnesium chloride (MgCl)2) Solution, magnesium nitrate (Mg (NO)3)2) Solution, calcium chloride (CaCl)2) Solution, calcium nitrate (Ca (NO)3)2) Solution, barium chloride (BaCl)2) Solutions, and the like. The mass ratio of the alkaline earth metal salt and/or alkali to the product after primary pyrolysis is 1: 1-100, preferably 1: 1.5 to 50, preferably 1: 1.5 to 20. When the amount of the alkaline earth metal-containing salt or base is too large, the catalytic performance of the finally formed nanocomposite is affected, and the activity is lowered.
In some embodiments, wherein the secondary pyrolysis comprises: under the inert atmosphere, heating the dried product to a constant temperature section, and keeping the constant temperature in the constant temperature section;
wherein the heating rate is 0.5-10 ℃/min, preferably 2.5-10 ℃/min; the temperature of the constant temperature section is 80-800 ℃, and preferably 300-600 ℃; the constant temperature time is 20 min-600 min; the inert atmosphere is nitrogen or argon.
The carbon-coated nickel nanocomposite is prepared by the method, a method of pyrolyzing a metal-organic framework compound (MOF) serving as a precursor is not adopted, the method needs to prepare a crystalline solid Material (MOF) with a periodic structure in a solvent at high temperature and high pressure, the condition for preparing MOFs is strict, the needed ligand is expensive, and the mass production is difficult; in addition, the composite material prepared by the method has imprecise cladding on the metal particles, and is remarkably different from the nano composite material in structure. The alkaline earth metal contained in the shell layer of the core-shell structure in the nano composite material can generate a synergistic effect with the core nickel nano particles, so that the catalytic performance is more excellent. The method for preparing the nano composite material is convenient for adjusting the oxygen content in the graphitized carbon layer in the preparation process, thereby conveniently adjusting the electronic characteristics of the nano composite material so as to be suitable for catalyzing different reactions.
The present invention is described in further detail below by way of specific embodiments in conjunction with the attached drawings, it being understood that the specific embodiments described herein are merely illustrative and explanatory of the invention and do not limit the invention in any way.
Preparation example 1
(1) Weighing 10g of nickel acetate and 10g of citric acid, adding the nickel acetate and the citric acid into a beaker containing 30m L of deionized water, stirring the mixture at 70 ℃ to obtain a homogeneous solution, and continuously heating and evaporating the homogeneous solution to dryness to obtain a solid precursor.
(2) And (2) placing the solid precursor obtained in the step (1) in a porcelain boat, then placing the porcelain boat in a constant temperature area of a tube furnace, introducing nitrogen with the flow rate of 100m L/min, heating to 650 ℃ at the speed of 5 ℃/min, keeping the temperature for 2h, stopping heating, and cooling to room temperature in the nitrogen atmosphere to obtain the carbon-coated nickel material.
(3) 2g of the material obtained in step (2) were weighed, 4ml of an aqueous solution containing 0.1528g of magnesium nitrate was added, and the mixture was immersed at room temperature for 24 hours, followed by drying at 120 ℃.
(4) And (3) placing the dried material obtained in the step (3) in a porcelain boat, then placing the porcelain boat in a constant temperature area of a tube furnace, introducing nitrogen with the flow rate of 50m L/min, heating to 350 ℃ at the speed of 2.5 ℃/min, keeping the temperature for 3h, stopping heating, and cooling to room temperature in the nitrogen atmosphere to obtain the magnesium-containing carbon-coated nickel nanocomposite.
Characterization of the materials:
the atomic percentage of the elements contained in the nanocomposite material measured by X-ray photoelectron spectroscopy (XPS) is as follows: the carbon content was 84.25 at%, the nickel content was 5.63 at%, the oxygen content was 9.21 at%, and the magnesium content was 0.91 at%.
As shown in fig. 1, the nanocomposite was placed in water as a suspension, a magnet was placed on the outside of the container, and after a period of time the nanocomposite was attracted to one side of the magnet, which was seen to be magnetic. TEM images of the nanocomposite. As shown in fig. 2, it can be seen that the outer layer of the nickel nanoparticle is wrapped with a graphitized carbon layer to form a complete core-shell structure. The X-ray diffraction pattern of this nanocomposite is shown in FIG. 3, and the XRD pattern of this material shows diffraction peaks (2. theta. angle 25.9 ℃) of graphite carbon and diffraction peaks (2. theta. angles 44.5 °, 51.7 ° and 76.4 ℃) of face-centered cubic (fcc) Ni. The average particle size of the carbon-coated nickel nanoparticles was calculated to be 12.3nm by the scherrer equation.
The BET test showed that the nanocomposite had a specific surface area of 152m2Per g, pore volume 0.32cm3Per g, wherein>The mesoporous volume of 2nm is 0.32cm3(ii) in terms of/g, representing 100% of the total pore volume. FIG. 4a is N of the nanocomposite2An adsorption-desorption isotherm is shown in fig. 4b, which is a BJH pore size distribution curve of the nanocomposite, and it can be seen that the composite has two mesopore distribution peaks at 3.8nm and 13.2 nm.
Preparation example 2
(1) 10g of nickel acetate and 20g of citric acid were weighed into a beaker containing 50m L of deionized water, stirred at 80 ℃ to obtain a homogeneous solution, and continuously heated and evaporated to dryness to obtain a solid precursor.
(2) And (2) placing the solid obtained in the step (1) in a porcelain boat, then placing the porcelain boat in a constant temperature area of a tube furnace, introducing nitrogen with the flow rate of 150m L/min, heating to 600 ℃ at the speed of 5 ℃/min, keeping the temperature for 2h, stopping heating, and cooling to room temperature in the nitrogen atmosphere to obtain the carbon-coated nickel material.
(3) Weighing 2g of the carbon-coated nickel material obtained in the step (2), adding 4m of L aqueous solution containing 0.8589g of magnesium nitrate, soaking at room temperature for 24h, and drying the product at 120 ℃.
(4) And (3) placing the dried material obtained in the step (3) in a porcelain boat, then placing the porcelain boat in a constant temperature area of a tube furnace, introducing nitrogen with the flow rate of 70m L/min, heating to 500 ℃ at the speed of 10 ℃/min, keeping the temperature for 2h, stopping heating, and cooling to room temperature in the nitrogen atmosphere to obtain the magnesium-containing carbon-coated nickel nanocomposite.
Characterization of the materials:
the atomic percentage of the elements contained in the nanocomposite material measured by X-ray photoelectron spectroscopy (XPS) is as follows: the carbon content was 84.47 at%, the nickel content was 1.68 at%, the oxygen content was 12.30 at%, and the magnesium content was 1.55 at%.
From the TEM image (fig. 5) of this material it can be seen that: the outer layer of the nickel nano-particles is wrapped with a graphitized carbon layer to form a complete core-shell structure. Fig. 6 shows an X-ray diffraction pattern of the nanocomposite material in which XRD patterns showed the presence of diffraction peaks corresponding to carbon (2 θ angle of 25.6 °) and fcc Ni (2 θ angles of 44.4 °, 51.8 ° and 76.3 °), and the average particle diameter of the carbon-coated nickel nanoparticles was calculated to be 7.8nm by scherrer's equation.
The BET test shows that the specific surface area of the material is 143m2Per g, pore volume 0.33cm3Per g, wherein>Pore volume of 0.33cm at 2nm3(ii) in terms of/g, representing 100% of the total pore volume. Fig. 7 is a BJH pore size distribution curve of the nanocomposite, and it can be seen that the composite has two mesopore distribution peaks at 3.73nm and 11.68 nm.
Preparation example 3
(1) Weighing 10g of nickel acetate and 10g of terephthalic acid, adding the nickel acetate and the terephthalic acid into 30m L deionized water, stirring at 70 ℃ to obtain a homogeneous solution, and continuously heating and evaporating to dryness to obtain a solid precursor.
(2) And (3) placing the solid precursor in a porcelain boat, then placing the porcelain boat in a constant temperature area of a tube furnace, introducing nitrogen at the flow rate of 100m L/min, heating to 650 ℃ at the speed of 5 ℃/min, keeping the temperature for 2h, stopping heating, and cooling to room temperature in a nitrogen atmosphere to obtain the material containing the carbon-coated nickel.
(3) Weighing 2g of the carbon-coated nickel material obtained in the step (2), adding 4m of L aqueous solution containing 0.32g of magnesium nitrate, soaking at room temperature for 24h, and drying the product at 120 ℃.
(4) And (3) placing the dried material obtained in the step (3) in a porcelain boat, then placing the porcelain boat in a constant temperature area of a tube furnace, introducing nitrogen with the flow rate of 100m L/min, heating to 400 ℃ at the speed of 5 ℃/min, keeping the temperature for 1h, stopping heating, and cooling to room temperature in the nitrogen atmosphere to obtain the magnesium-containing carbon-coated nickel nanocomposite.
Characterization of the materials:
the atomic percentage of the elements contained in the nanocomposite material measured by X-ray photoelectron spectroscopy (XPS) is as follows: the carbon content is 88.78 at%; the nickel content was 4.56 at%, the oxygen content was 6.13 at%, and the magnesium content was 0.53 at%.
FIG. 8 TEM image of the nanocomposite, it can be seen that: the carbon-coated nickel-based composite material comprises a core-shell structure of carbon-coated nickel, a graphitized carbon layer is used as a shell, and nano metal nickel is used as a core. Fig. 9 is an XRD pattern of the nanocomposite, which shows the presence of diffraction peaks corresponding to carbon (2 theta angle of 25.9 °) and fcc Ni (2 theta angles of 44.5 °, 51.7 ° and 76.4 °). The average particle size of the carbon-coated nickel nanoparticles was calculated to be 8.1nm by the scherrer equation.
The BET test shows that the specific surface area of the material is 172m2Per g, pore volume 0.286cm3Per g, wherein>Pore volume of 0.279cm at 2nm3In terms of/g, 97.6% of the total pore volume. Fig. 10 is a BJH pore size distribution curve of the nanocomposite, and it can be seen that there are two mesopore distribution peaks at 4.04nm and 19.19nm in the nanocomposite.
Comparative preparation example
(1) Weighing 10g of nickel acetate and 10g of citric acid, adding the nickel acetate and the citric acid into a beaker containing 30m L of deionized water, stirring the mixture at 70 ℃ to obtain a homogeneous solution, and continuously heating and evaporating the homogeneous solution to dryness to obtain a solid precursor.
(2) And (2) placing the solid obtained in the step (1) in a porcelain boat, then placing the porcelain boat in a constant temperature area of a tube furnace, introducing nitrogen with the flow rate of 100m L/min, heating to 650 ℃ at the speed of 5 ℃/min, keeping the temperature for 2h, stopping heating, and cooling to room temperature in the nitrogen atmosphere to obtain the carbon-coated nickel nanocomposite.
Characterization of the materials:
the atomic percentage of the elements contained in the nanocomposite material measured by X-ray photoelectron spectroscopy (XPS) is as follows: the carbon content was 88.26 at%, the nickel content was 5.4 at%, and the oxygen content was 6.36 at%.
The nanocomposite material had diffraction peaks (2 θ angles of 44.5 °, 51.7 °, and 76.4 °) corresponding to those of graphitic carbon (2 θ angle of 26 °) and Ni of face-centered cubic structure (fcc). The average particle size of the carbon-coated nickel nanoparticles was calculated to be 4.7nm by the scherrer equation. The BET test shows that the specific surface area of the composite material is 146m2Per g, pore volume 0.37cm3Per g, wherein>The mesoporous volume of 2nm is 0.365cm3In terms of/g, 98.6% of the total pore volume.
Example 1
The composite material obtained in the preparation example 1 is used as a catalyst for a reaction of hydrogenation of nitrobenzene compounds to prepare target aniline compounds, and the specific experimental steps are as follows:
adding 0.1g of nano composite material, 1.97g of nitrobenzene and 100m of L ethanol into a reaction kettle, introducing H2After 3 times of replacement, the reaction kettle is charged with H2And (3) controlling the pressure in the reaction kettle to be 2MPa, stirring and heating, heating to the preset reaction temperature of 60 ℃, stopping heating after reacting for 3 hours, cooling to room temperature, discharging pressure, and opening the reaction kettle to take the product aniline for chromatographic analysis. The reactant conversion and the target product selectivity were calculated by the following formulas:
conversion-amount of reacted reaction mass/amount of added reaction × 100%
The selectivity is × 100% based on the mass of the target product/mass of the reaction product
After analysis, the nitrobenzene conversion rate is 100% and the aniline selectivity is 99.2%.
When the reaction proceeded for 300s, a sample was taken and subjected to chromatography to calculate the conversion of the reactant, and TOF of the catalyst was 12.1 × 10, obtained by the formula TOF (amount of reacted reactant species)/(amount of catalytically active metal species 300s)-3s-1。
Example 2
The nano composite material prepared in preparation example 1 is used as a catalyst for nitrobenzene compound hydrogenation reduction reaction, and the specific experimental steps are as follows:
adding 0.1g of nano composite material, 0.49g of nitrobenzene and 30m of L ethanol into a reaction kettle, and introducing H2After replacing the reaction kettle for 3 times, introducing H again2The pressure in the reaction kettle is made to be 0.5MPa, the temperature is raised by stirring, the temperature is raised to the preset reaction temperature of 120 ℃, the heating is stopped after the reaction is continued for 0.5 hour, the temperature is reduced to the room temperature, the pressure is discharged, the reaction kettle is opened, the product aniline is taken out for chromatographic analysis, and the conversion rate of reactants, the product selectivity and the TOF are respectively calculated by the formula shown in the example 1, so that the conversion rate of nitrobenzene is 100 percent, the selectivity of the aniline is 99.4 percent, and the TOF is 9.95 × 10-3s-1。
Example 3
The nano composite material prepared in preparation example 1 is used as a catalyst for nitrobenzene compound hydrogenation reduction reaction, and the specific experimental steps are as follows:
adding 0.1g of nano composite material, 0.33g of nitrobenzene and 30m of L ethanol into a reaction kettle, and introducing H2After replacing the reaction kettle for 3 times, introducing H again2Making the pressure in the reaction kettle be 1MPa, stirring and heating, heating to 60 deg.C, continuously making reaction for 2 hr, stopping heating, cooling to room temperature, discharging pressure, opening reaction kettle and taking out aniline product to make chromatographic analysis so as to obtain nitrobenzene conversion rate of 100%, aniline selectivity of 99.8% and TOF of 10.9 × 10-3s-1。
Example 4
The nano composite material prepared in preparation example 1 is used as a catalyst for nitrobenzene compound hydrogenation reduction reaction, and the specific experimental steps are as follows:
0.2g of the nanocomposite, 0.66g of nitrobenzene and 50m of L g of cyclohexane were added to a reaction vessel, and H was fed in2After replacing the reaction kettle for 3 times, introducing H again2Making the pressure in the reaction kettle be 1MPa, stirring and heating, heating to preset reaction temperature of 100 deg.C, continuously making reaction for 1 hr, stopping heating, cooling to room temperature, discharging pressure, opening reaction kettle and taking out product aniline and making chromatographic analysis so as to obtain the invented product with reactant conversion rate of 100%, aniline selectivity of 99.6% and TOF of 13.8 × 10-3s-1。
Example 5
The nano composite material prepared in preparation example 1 is used as a catalyst for nitrobenzene compound hydrogenation reduction reaction, and the specific experimental steps are as follows:
adding 0.1g of nano composite material, 0.35g of p-isopropyl nitrobenzene and 30m of L ethanol into a reaction kettle, and introducing H2After replacing the reaction kettle for 3 times, introducing H again2The pressure in the reaction kettle is 1MPa, the temperature is raised by stirring, the temperature is raised to the preset reaction temperature of 80 ℃, and the reaction is continued for 2 hoursStopping heating, cooling to room temperature, discharging pressure, opening the reaction kettle, taking out the product of p-isopropylaniline, and carrying out chromatographic analysis, wherein the conversion rate of reactants, the product selectivity and the TOF are respectively calculated by the formula shown in example 1, and the conversion rate of p-isopropylnitrobenzene is 100%, the selectivity of p-isopropylaniline is 98.9%, and the TOF is 9.31 × 10-3s-1。
Example 6
The nano composite material prepared in preparation example 1 is used as a catalyst for nitrobenzene compound hydrogenation reduction reaction, and the specific experimental steps are as follows:
adding 0.1g of nano composite material, 0.35g of 2, 6-dimethyl nitrobenzene and 30m of L ethanol into a reaction kettle, and introducing H2After replacing the reaction kettle for 3 times, introducing H again2The pressure in the reaction kettle is enabled to be 1MPa, the temperature is raised by stirring, the temperature is raised to the preset reaction temperature of 80 ℃, the heating is stopped after the reaction is continued for 2 hours, the temperature is reduced to the room temperature, the pressure is discharged, the reaction kettle is opened, the product 2, 6-dimethylaniline is taken out for chromatographic analysis, the conversion rate of the reactant, the selectivity of the product and the TOF are respectively calculated by the formula shown in the example 1, and the conversion rate of the 2, 6-dimethylnitrobenzene is 100 percent, the selectivity of the 2, 6-dimethylaniline is 99.0 percent, and the TOF is 10.5 × 10-3s-1。
Example 7
The nano composite material prepared in preparation example 2 is used as a catalyst for nitrobenzene compound hydrogenation reduction reaction, and the specific experimental steps are as follows:
adding 0.2g of nano composite material, 0.66g of nitrobenzene and 50m of L ethanol into a reaction kettle, and introducing H2After replacing the reaction kettle for 3 times, introducing H again2Making the pressure in the reaction kettle be 1MPa, stirring and heating, heating to 60 deg.C, continuously making reaction for 2 hr, stopping heating, cooling to room temperature, discharging pressure, opening reaction kettle and taking out aniline product to make chromatographic analysis so as to obtain the invented product with 100% conversion rate of nitrobenzene, 99.8% selectivity of aniline and 10.4 × 10 TOF-3s-1。
Example 8
The nano composite material prepared in preparation example 3 is used as a catalyst for nitrobenzene compound hydrogenation reduction reaction, and the specific experimental steps are as follows:
adding 0.2g of nano composite material, 0.66g of nitrobenzene and 50m of L ethanol into a reaction kettle, and introducing H2After replacing the reaction kettle for 3 times, introducing H again2Making the pressure in the reaction kettle be 1MPa, stirring and heating, heating to 60 deg.C, continuously making reaction for 2 hr, stopping heating, cooling to room temperature, discharging pressure, opening reaction kettle and taking out aniline product to make chromatographic analysis so as to obtain nitrobenzene conversion rate of 100%, aniline selectivity of 99.3% and TOF of 10.2 × 10-3s-1。
Comparative example
The nano composite material prepared by the comparative preparation example is used as a catalyst for the hydrogenation reduction reaction of nitrobenzene compounds, and the specific experimental steps are as follows:
adding 0.1g of nano composite material, 1.97g of nitrobenzene and 100m of L ethanol into a reaction kettle, and introducing H2After replacing the reaction kettle for 3 times, introducing H again2Making the pressure in the reaction kettle be 2MPa, stirring and heating, heating to 60 deg.C, continuously making reaction for 3 hr, stopping heating, cooling to room temperature, discharging pressure, opening reaction kettle and taking out aniline product to make chromatographic analysis so as to obtain the invented product with 100% conversion rate of nitrobenzene, 98.8% selectivity of aniline and 5.32 × 10 TOF-3s-1。
It can be seen from the above examples and comparative examples that the nanocomposite of the present invention has a good catalytic effect when used as a catalyst for catalyzing a catalytic hydrogenation reaction of nitrobenzene compounds, and compared with a catalyst containing no alkaline earth metal, the nanocomposite containing carbon coated nickel containing alkaline earth metal not only enables the catalytic reaction to have a high conversion rate and product selectivity, but also has a higher catalytic reaction rate and a better catalytic performance.
It should be noted by those skilled in the art that the described embodiments of the present invention are merely exemplary and that various other substitutions, alterations, and modifications may be made within the scope of the present invention. Accordingly, the present invention is not limited to the above-described embodiments, but is only limited by the claims.
Claims (12)
1. A synthetic method of aniline compounds comprises the following steps:
the carbon-coated nickel nano composite material containing alkaline earth metal is used as a catalyst to catalyze nitrobenzene compounds to carry out hydrogenation reduction reaction in a hydrogen atmosphere;
the nano composite material comprises a core-shell structure with a shell layer and an inner core, wherein the shell layer is a graphitized carbon layer containing alkaline earth metal and oxygen, and the inner core is nickel nano particles.
2. The method of claim 1, wherein the nitrobenzene compound is a substituted nitrobenzene, the substituent selected from C1-20One or more of alkyl, cycloalkyl and aryl.
3. The method according to claim 1, wherein the nitrobenzene compounds are selected from one or more of nitrobenzene, 2, 6-dimethylnitrobenzene and p-isopropylnitrobenzene.
4. The synthesis method according to claim 1, wherein the catalyst accounts for 1-50% of the mass of the nitrobenzene compounds, preferably 5-30%.
5. The synthesis method according to claim 1, wherein the temperature of the hydrogenation reduction reaction is 60-120 ℃.
6. The synthesis process according to claim 1, wherein the pressure of hydrogen is 0.5 to 2 MPa.
7. The synthesis method according to claim 1, wherein the catalyst is mixed with nitrobenzene compounds in a solvent and then subjected to hydrogenation reduction reaction, wherein the solvent is selected from one or more of alcohols, ethers, alkanes and water.
8. The synthesis method according to any one of claims 1 to 7, wherein the nanocomposite is a mesoporous material having at least one mesopore distribution peak.
9. The method of synthesizing as defined in claim 8 wherein the nanocomposite is a mesoporous material having two or more mesopore distribution peaks.
10. The method of synthesis according to claim 8, wherein the mesoporous material has a proportion of mesopore volume of more than 50%, preferably more than 80%, of the total pore volume.
11. The method of claim 1, wherein the alkaline earth metal comprises 0.1 at% to 3 at%, carbon comprises 80 at% to 95 at%, nickel comprises 0.1 at% to 10 at%, and oxygen comprises 1 at% to 20 at%, in terms of atomic percentage.
12. The method of synthesis according to any one of claims 1 to 11, the alkaline earth metal being selected from one or more of beryllium, magnesium, calcium, strontium, barium and radium.