CN111443421A - 一种低损耗环芯少模光纤 - Google Patents

一种低损耗环芯少模光纤 Download PDF

Info

Publication number
CN111443421A
CN111443421A CN202010441958.XA CN202010441958A CN111443421A CN 111443421 A CN111443421 A CN 111443421A CN 202010441958 A CN202010441958 A CN 202010441958A CN 111443421 A CN111443421 A CN 111443421A
Authority
CN
China
Prior art keywords
optical fiber
refractive index
fiber
mode
core
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010441958.XA
Other languages
English (en)
Inventor
郑宏军
黎昕
刘阳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liaocheng University
Original Assignee
Liaocheng University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liaocheng University filed Critical Liaocheng University
Priority to CN202010441958.XA priority Critical patent/CN111443421A/zh
Publication of CN111443421A publication Critical patent/CN111443421A/zh
Pending legal-status Critical Current

Abstract

本发明提出了一种低损耗环芯少模光纤；采用纯二氧化硅材料作为环形纤芯，有效降低光纤损耗；采用大折射率差，有效降低光纤串扰；实现了低损耗、低串扰环芯两模式运作。

Description

一种低损耗环芯少模光纤
技术领域
本发明涉及一种低损耗环芯少模光纤，可应用于光纤光学、光纤通信、光纤无线接入、光学信息处理和新一代信息技术等领域。
背景技术
近年来，各种通信业务流量指数增长，单模光纤通信受到了前所未有的挑战。光纤通信业界围绕空分复用（包括芯式复用和模分复用及其结合）这一物理维度对通信网络传输容量实现了突破；空分复用中的多芯光纤和少模光纤及其相关器件和应用研究成为前沿研究热点[Guifang Li, Neng Bai, and Ningbo Zhao and Cen Xia, Space-divisionmultiplexing: the next frontier in optical communication. Advances in Optics& Photonics, 2014, 6(4): 5041-5046；Guifang Li, Magnus Karlsson, Xiang Liu,and Yves Quiquempois, Focus issue introduction: space-division multiplexing,Opt. Express 2014, 22, 32526-32527; He Wen, Hongjun Zheng et al. Few-modefibre-optic microwave photonic links [J]. Light: Science and Applications2017, 6, 8; 郑宏军，黎昕，白成林，啁啾脉冲在光纤中的传输，北京：科学出版社，2018，1-184；董秋焕，刘阳，郑宏军黎昕，白成林，胡卫生，模分复用系统中少模复用（解复用）技术研究[J].聊城大学学报(自然科学版)，2020，33(2): 50-67；王潇，郑宏军*（通讯作者），黎昕，刘阳，于如愿，白成林，胡卫生，模分复用系统中的少模光纤研究新进展，聊城大学学报（自然科学版）, 2019.4，32(2): 69-79]；一种环芯少模光纤也得到了大家的关注；环芯少模光纤仅支持单径向模式，具有较大的模式间折射率差 [Yongmin Jung, Qiongyue Kang,Hongyan Zhou, Rui Zhang, Su Chen, Honghai Wang, Yucheng Yang, Xianqing Jin,Frank P. Payne, Shaif-ul Alam, and David J. Richardson, "Low-Loss 25.3 kmFew-Mode Ring-Core Fiber for Mode-Division Multiplexed Transmission," J.Lightwave Technol. 35, 1363-1368 (2017)]；纯二氧化硅纤芯可以有效地减少光纤衰减和熔接损耗，目前大都应用于单模光纤(T. Hasegawa et al. 2016. Advances in ultra-low loss silica fibers[J]. Frontiers in Optics,paper FTu2B.2; S. Ten. 2016.Ultra Low-loss Optical Fiber Technology[J]. Optical Fiber CommunicationConference, paper Th4E.5; Yoshiaki Tamura. 2018. Ultra-low loss silica corefiber for long haul transmission [J]. Optical Fiber Communication Conference,paper M4B.1)。少模光纤不同模式下的有效折射率差（ERID）大于0.5x10-3可以避免模式耦合(Pierre Sillard et al. Few-Mode Fibers for Space-Division MultiplexedTransmissions[J], European Conference & Exhibition on Optical Communication,2013. 03 (A1): 1-3; Roland Ryf. Switching and Multiplexing Technologies forMode-Division Multiplexed Networks, Optical Fiber Communication Conference＆Exposition, 2017, Tu2c)。综上，若将纯二氧化硅纤芯、环芯折射率分布少模光纤的概念有机融合，有望解决目前少模光纤的研究挑战，有重要的学术价值和应用价值，研究意义重大、应用前景广阔。
发明内容
在国家自然科学基金 (编号61671227和61431009）、山东省自然科学基金（ZR2011FM015）、“泰山学者”建设工程专项经费支持下，本发明提出了一种低损耗环芯少模光纤；该光纤融合了纯二氧化硅纤芯、环芯折射率分布少模光纤的优点，为光纤光学、光纤通信、光纤无线接入、光学信息处理和新一代信息技术等领域的深入研究提供了重要支持。
本发明解决其技术问题所采用的技术方案是：
本发明提出了一种低损耗环芯少模光纤；该光纤半径r<1.5μm时纤芯采用掺氟二氧化硅材料，折射率为1.4350；1.5μm≤r≤5μm时纤芯采用纯二氧化硅材料，折射率为1.4440；r>5μm时光纤包层采用掺氟二氧化硅材料，折射率为1.4350；最外包层半径r为62.5μm；在1500nm-1600nm波长范围内模式间折射率差均大于；在1550nm处有效折射率差为；模式与包层折射率差随入射波长的增大而减小；在1500nm-1600nm波长范围内折射率差均大于；在1550nm处折射率差为；采用纯二氧化硅材料作为环形纤芯，有效降低光纤损耗；采用大折射率差，有效降低光纤串扰；实现了低损耗、低串扰环芯两模式运作，从而进一步提高光纤传输性能；该光纤呈现出支持单径向模式的性能和模间的有效折射率差大的特点；光纤中模场特性可以通过改变纤芯、包层折射率分布、尺寸来改变。
本发明的有益效果如下：
1.该光纤采用纯二氧化硅材料作为环形纤芯，有效降低光纤损耗；
2.采用模式间大折射率差，有效降低光纤串扰；
3.该光纤中模场特性可以通过改变纤芯、包层的折射率分布、尺寸来改变。
4.该光纤融合了纯二氧化硅纤芯、环芯少模光纤的优点，从而进一步提高光纤传输性能，为光纤光学、光纤通信、光纤无线接入和光学信息处理、新一代信息技术等领域的深入研究提供了重要支持。
附图说明
图1是少模光纤的环芯折射率分布图。
图2是少模光纤横截面的折射率等高线分布图。
图3是光纤中模式间有效折射率差、模式的有效折射率与包层折射率差随入射波长变化情况; 标有小圆圈的曲线表示光纤中模式间有效折射率差n(LP01)-n(LP11)的变化情况；标有星号的曲线表示模式的有效折射率与包层折射率差n(LP11)-n(Cladding)随入射波长变化情况。
具体实施方式
下面结合实施例和附图详细说明本发明的技术方案，但保护范围不限于此。
实施例1 图1是少模光纤的环芯折射率分布图；图1可以看出，r<1.5μm时纤芯采用掺氟二氧化硅材料，折射率为1.4350；1.5μm≤r≤5μm时纤芯采用纯二氧化硅材料，折射率为1.4440；r>5μm时光纤包层采用掺氟二氧化硅材料，折射率为1.4350；采用纯二氧化硅材料作为环形纤芯，有效降低光纤损耗。
图2是少模光纤横截面的折射率等高线分布图。图2可得，环芯处折射率为1.4440，周边包层折射率为1.4350；环芯处折射率大于周边折射率；最外包层半径为62.5μm。
图3所示是光纤中模式间有效折射率差、模式的有效折射率与包层折射率差随入射波长变化情况; 标有小圆圈的曲线表示光纤中模式间有效折射率差n(LP01)-n(LP11)的变化情况；标有星号的曲线表示模式的有效折射率与包层折射率差n(LP11)-n(Cladding)随入射波长变化情况。图中可得，光纤中模式间有效折射率差随波长增加而增大，为了降低模式间的串扰、降低各模式能量向包层的耗散，该光纤的折射率差很大；在1500nm-1600nm波长范围内模式间折射率差均大于；在1550nm处有效折射率差为，比文献[Yongmin Jung,Qiongyue Kang, Hongyan Zhou, Rui Zhang, Su Chen, Honghai Wang, Yucheng Yang,Xianqing Jin, Frank P. Payne, Shaif-ul Alam, and David J. Richardson, "Low-Loss 25.3 km Few-Mode Ring-Core Fiber for Mode-Division MultiplexedTransmission," J. Lightwave Technol. 35, 1363-1368 (2017)]中的折射率差大很多。模式与包层折射率差随入射波长的增大而减小；在1500nm-1600nm波长范围内折射率差均大于；在1550nm处折射率差为。根据实验结果[Xianqing Jin, Ariel Gomez, Kai Shi,Benn C. Thomsen, Feng Feng, George S. D. Gordon, Timothy D. Wilkinson,Yongmin Jung, Qiongyue Kang, Pranabesh Barua, Jayanta Sahu, Shaif-ul Alam,David J. Richardson, Dominic C. O'Brien, and Frank P. Payne, "Mode CouplingEffects in Ring-Core Fibers for Space-Division Multiplexing Systems," J.Lightwave Technol. 34, 3365-3372 (2016)]，模式间的串扰与有效折射率差(ERID)有关。ERID越大，模式串扰越小。因此，我们提出的环芯少模光纤可以有效地降低模式间的串扰。
总之，所提出的光纤实现了低损耗、低串扰环芯两模式运作。应当指出的是，具体实施方式只是本发明比较有代表性的例子，显然本发明的技术方案不限于上述实施例，还可以有很多变形。本领域的普通技术人员，以本发明所明确公开的或根据文件的书面描述毫无异议地得到的，均应认为是本专利所要保护的范围。

Claims (1)

1.一种低损耗环芯少模光纤，其特征在于：所述光纤半径r<1.5μm时纤芯采用掺氟二氧化硅材料，折射率为1.4350；1.5μm≤r≤5μm时纤芯采用纯二氧化硅材料，折射率为1.4440；r>5μm时光纤包层采用掺氟二氧化硅材料，折射率为1.4350；最外包层半径r为62.5μm；在1500nm-1600nm波长范围内模式间折射率差均大于；在1550nm处有效折射率差为；模式与包层折射率差随入射波长的增大而减小；在1500nm-1600nm波长范围内折射率差均大于；在1550nm处折射率差为。
CN202010441958.XA 2020-05-22 2020-05-22 一种低损耗环芯少模光纤 Pending CN111443421A (zh)