CN111363426B - 一种环保的负氧离子浓缩液及制备方法 - Google Patents
一种环保的负氧离子浓缩液及制备方法 Download PDFInfo
- Publication number
- CN111363426B CN111363426B CN202010390492.5A CN202010390492A CN111363426B CN 111363426 B CN111363426 B CN 111363426B CN 202010390492 A CN202010390492 A CN 202010390492A CN 111363426 B CN111363426 B CN 111363426B
- Authority
- CN
- China
- Prior art keywords
- parts
- negative oxygen
- extract
- oxygen ion
- concentrated solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于建筑墙面装饰材料技术领域，具体涉及一种高效环保的负氧离子浓缩液及其制备方法。本发明一种高效环保的负氧离子浓缩液，其配方按重量份配比组分如下：去离子水45‑55份；电气石提取物20‑28份；稀土萃取液10‑15份；硅烷偶联剂8‑12份；纳米二氧化钛1‑2份；聚乙烯醇0.5‑1份。利用本发明最终得到的负氧离子浓缩液为无色透明的液体，粘度较低，在使用时采用去离子水稀释后可以直接采用喷枪或者蓝光纳米喷雾仪进行喷涂，施工方便，且耐水，耐擦拭，采用天然材料，不含甲醛、苯、二甲苯以及其他挥发性有害物质，更安全环保。
Description
技术领域
本发明属于建筑墙面装饰材料技术领域，具体涉及一种环保的负氧离子浓缩液及制备方法。
背景技术
空气负离子又称负氧离子，是带负电荷的氧离子，它就存在于空气中。平时人们生活在的室内环境中就含有负氧离子，只是含量低人们一般无法感知。而在海边、森林、瀑布、草原您会感到空气很清新，呼吸特别舒畅，是因为空气中负氧离子含量高的缘故。
世界卫生组织确认清新空气中负氧离子含量在1000-1500个/cm3，郊外、海边、森林、瀑布、草原负氧离子均达到3000个/cm3以上，一般家庭室内含量不足600个/cm3。负氧离子改善肺功能，在吸入负氧离子30分钟后，人的肺部能够吸收的氧气量增加20%，多排出15%的二氧化碳。负氧离子还可以改善心肌功能，改善睡眠；负氧离子能激活肌体多种酶，促进新陈代谢；负氧离子可改变肌体反应性，活跃网状内皮系统的功能，增强肌体免疫力；负氧离子还容易吸附细菌，使其发生结构改变和能量转移，以使细菌病变而死亡。
气象专家认为，像北京这样的大城市，属于大陆性气候，空气中负氧离子比海洋性气候地区少，加上空气污染比较严重，空气中负氧离子容易被烟雾、尘埃、病菌、汽车尾气等污染物吸附而消失，室内通风不良和污染，负氧离子就更加缺乏。为此，久居闹市区的居民应该经常到郊区田野、海滨、森林公园等，特别是到有瀑布流泉飞溅的风景区进行"空气浴"这样才能更有利于人体的身心健康。负氧离子可以在宇宙射线和紫外线辐射，静电力，光照，光合作用，照明激发等自然环境下自然生成，也可以在电晕放电、热金属电极或光电极的热电子发射、放射性同位素的辐射、紫外线照射等人为情况下人工合成。
目前市面上由于现有的负氧离子浓缩液粘度较高，无法直接采用喷涂的形式施工，而是采用溶胶凝胶技术，制备出纳米溶胶，喷涂在墙体表面，在墙面上凝胶化，形成纳米凝胶粒子，释放负氧离子，此种方法释放的负氧离子浓度较低，且施工成本高，施工繁琐。
发明内容
本发明为克服现有技术中存在的释放负氧离子浓度低且不能采用喷涂的形式直接施工的缺陷，提供一种高效环保且能直接采用喷涂的形式施工的负氧离子浓缩液及制备方法。
本发明解决其技术问题所采用的技术方案是：一种环保的负氧离子浓缩液，其配方按重量份配比组分如下：
去离子水45~55份；
电气石提取物20~28份；
稀土萃取液10~15份；
硅烷偶联剂8~12份；
纳米二氧化钛1~2份；
聚乙烯醇0.5~1份。
进一步地，所述电气石提取物为平均粒径500nm以下的电气石粉分馏萃取物。
进一步地，所述稀土萃取液为粒径分布＜63μm的氧化铈、氧化钕、氧化铽及氧化镧中的一种或几种的混合。
进一步地，所述纳米二氧化钛的平均粒径在45-55纳米之间。
进一步地，所述聚乙烯醇为医用级聚乙烯醇。
进一步地，包括如下按重量份配比组分：去离子水55份，电气石提取物20份，稀土萃取液10份，硅烷偶联剂8份，纳米二氧化钛1.2份，医用级聚乙烯醇0.8份。
更进一步地，一种环保的负氧离子浓缩液的制备方法，包括以下步骤：
S1：按重量份配比称取原材料，检查并清洗仪器；
S2：向配方规定量的去离子水中加入配方规定量的纳米二氧化钛，在卧式或立式搅拌机中搅拌1-2h，之后加热到85℃，静置1h，形成稳定悬浊液；
S3：向S2悬浊液中加入配方规定量的电气石提取物和稀土萃取液，自然冷却至45℃；
S4：向S3混合液中加入配方规定量的硅烷偶联剂和医用级聚乙烯醇，在卧式或立式搅拌机中搅拌1-2h，然后出料获得所需的一种环保的负氧离子浓缩液。
本发明的一种环保的负氧离子浓缩液及制备方法的有益效果是：
1、本发明高效环保负氧离子浓缩液的负氧离子释放浓度高，且主要释放小微粒径负氧离子，利用本发明的负氧离子浓缩液制备方法，最终得到的负氧离子浓缩液为无色透明的液体，对于家装、汽车内部装饰及办公室装修都适用，用途较广泛。
2、本发明负氧离子浓缩液粘度较低，在使用时采用去离子水稀释后可以直接采用喷枪或者蓝光纳米喷雾仪进行喷涂，施工方便。
3、本发明的负氧离子浓缩液与壁面结合力好，可用于要求耐水或高粘结强度的场所，且耐擦拭。
4、本发明的负氧离子浓缩液采用天然材料，不含甲醛、苯、二甲苯以及其他挥发性有害物质，更安全环保。
附图说明
下面结合附图和具体实施方式对本发明作进一步详细的说明。
图1是本发明环保的负氧离子浓缩液的制备方法流程图。
具体实施方式
现在结合附图对本发明作进一步详细的说明。这些附图均为简化的示意图，仅以示意方式说明本发明的基本结构，因此其仅显示与本发明有关的构成。
如图1所示的本发明的一种环保的负氧离子浓缩液及制备方法的具体实施例如下：
实施例1
按制备100kg环保的负氧离子浓缩液计，按下列重量准备原料：去离子水50kg，电气石提取物25kg，稀土萃取液15kg，硅烷偶联剂8kg，纳米二氧化钛1kg，医用级聚乙烯醇1kg，其中在本发明实施例1中纳米二氧化钛是指平均粒径在100纳米以下的二氧化钛粉末，要求纳米二氧化钛平均粒径在45~55纳米之间。电气石提取物是将电气石粉碎至平均粒径500nm以下后，通过分馏萃取的方式获得的。
稀土萃取液是将氧化铈、氧化钕、氧化铽、氧化镧等稀土元素的一种或几种共混后，经过高温加热以分流萃取的方式获得，这里要求混合粉平均粒径分布＜63μm。
本发明实施例1的环保的负氧离子浓缩液制备方法，包括以下步骤：
S1：按重量份配比称取原材料，检查并清洗仪器；
S2：在无尘环境下向卧式或立式搅拌机中加入去离子水50kg，向加入的去离子水中加入纳米二氧化钛1kg，在卧式或立式搅拌机中搅拌1-2h，之后加热到85±1℃，静置1h，形成稳定悬浊液；
S3：向上述稳定悬浮液中加入电气石提取物25kg和稀土萃取液15kg，自然冷却至45±1℃；
S4：向S3形成的混合液中加入硅烷偶联剂8kg和医用级聚乙烯醇1kg，在卧式或立式搅拌机中搅拌1-2h，然后出料即可得一种环保的负氧离子浓缩液。其制备方法简单可以大规模生产。
实施例2
按制备100kg的一种环保的负氧离子浓缩液计，按下列重量准备原料：去离子水55kg，电气石提取物20kg，稀土萃取液10kg，硅烷偶联剂8kg，纳米二氧化钛1.2kg，医用级聚乙烯醇0.8kg，其本发明实施例2中纳米二氧化钛是指平均粒径在100纳米以下的二氧化钛粉末，要求纳米二氧化钛平均粒径在45-55纳米之间。电气石提取物是将电气石粉碎之平均粒径500nm以下后，通过分馏萃取的方式获得的。
稀土萃取液是将氧化铈、氧化钕、氧化铽、氧化镧等稀土元素的一种或几种共混后，经过高温加热以分流萃取的方式获得，这里要求混合粉平均粒径分布＜63μm。
本发明实施例2的环保的负氧离子浓缩液制备方法，包括以下步骤：
S1：按重量份配比称取原材料，检查并清洗仪器；
S2：在无尘环境下向卧式或立式搅拌机中加入去离子水55kg，向加入的去离子水中加入纳米二氧化钛1.2kg，在卧式或立式搅拌机中搅拌1-2h，之后加热到85±1℃，静置1h，形成稳定悬浊液；
S3：向S2的稳定悬浊液中加入电气石提取物20kg和稀土萃取液10kg，自然冷却至45±1℃；
S4：向S3形成的混合液中加入硅烷偶联剂8kg和医用级聚乙烯醇0.8kg，在卧式或立式搅拌机中搅拌1-2h，然后出料即可得一种环保的负氧离子浓缩液。
实施例3
按制备100kg的一种环保的负氧离子浓缩液计，按下列重量准
备原料：去离子水45kg，电气石提取物25kg，稀土萃取液15g，硅烷偶联剂12kg，纳米二氧化钛2kg，医用级聚乙烯醇1kg，其本发明实施例3中纳米二氧化钛是指平均粒径在100纳米以下的二氧化钛粉末，要求纳米二氧化钛平均粒径在45-55纳米之间。电气石提取物是将电气石粉碎之平均粒径500nm以下后，通过分馏萃取的方式获得的。
稀土萃取液是将氧化铈、氧化钕、氧化铽、氧化镧等稀土元素的一种或几种共混后，经过高温加热以分流萃取的方式获得，这里要求混合粉平均粒径分布＜63μm。
本发明实施例3的环保的负氧离子浓缩液制备方法，包括以下步骤：
S1：按重量份配比称取原材料，检查并清洗仪器；
S2：在无尘环境下向卧式或立式搅拌机中加入去离子水45kg，向加入的去离子水中加入纳米二氧化钛2kg，在卧式或立式搅拌机中搅拌1-2h，之后加热到85±1℃，静置1h，形成稳定悬浊液；
S3：向上述稳定悬浊液中加入电气石提取物25kg和稀土萃取液15kg，自然冷却至45±1℃；
S4：向S3形成的混合液中加入硅烷偶联剂12kg和医用级聚乙烯醇1kg，在卧式或立式搅拌机中搅拌1-2h，然后出料即可得一种环保的负氧离子浓缩液。
对上述实施例1、实施例2及实施例3进行每平米墙面及顶面喷涂45毫升喷涂后，在室温23.5℃，空气湿度30%状态下进行检测，释放出的负氧离子浓度数据如下表所示：
| 项目 | 负氧离子浓度 |
| 实施例1 | 7835个/cm<sup>3</sup> |
| 实施例2 | 8320个/cm<sup>3</sup> |
| 实施例3 | 8446个/cm<sup>3</sup> |
本发明实施例1、实施例2及实施例3中最终的负氧离子浓缩液为无色透明的液体，可以应用在家装、汽车内部装饰及办公室装修等场所中，且发明的负氧离子浓缩液采用天然材料，不含甲醛、笨、二甲苯等挥发性有害物质，安全环保。本发明的高效环保的负氧离子浓缩液如上表所示的数据可以看出负氧离子的释放浓度较高，且主要释放微小粒径的负氧离子，有利于人体的身心健康，负氧离子浓缩液的粘度低，可以采用去离子水稀释后直接采用喷枪或者蓝光纳米喷雾仪进行喷涂，施工方便，与壁面结合力较好，耐水，耐擦拭。
应当理解，以上所描述的具体实施例仅用于解释本发明，并不用于限定本发明。由本发明的精神所引伸出的显而易见的变化或变动仍处于本发明的保护范围之中。
Claims (3)
1.一种环保的负氧离子浓缩液，其特征在于，其配方按重量份配比组分如下：
去离子水45~55份；
电气石提取物20~28份；
稀土萃取液10~15份；
硅烷偶联剂8~12份；
纳米二氧化钛1~2份；
聚乙烯醇0.5~1份；
所述电气石提取物为平均粒径500nm以下的电气石粉分馏萃取物；
所述稀土萃取液为粒径分布＜63μm的氧化铈、氧化钕、氧化铽及氧化镧中的一种或几种的混合；
所述纳米二氧化钛的平均粒径在45-55纳米之间；
上述负氧离子浓缩液的制备方法包括以下步骤：
S1：按重量份配比称取原材料，检查并清洗仪器；
S2：向配方规定量的去离子水中加入配方规定量的纳米二氧化钛，在卧式或立式搅拌机中搅拌1-2h，之后加热到85±1℃，静置1h，形成稳定悬浊液；
S3：向上述稳定悬浊液中加入配方规定量的电气石提取物和稀土萃取液，自然冷却至45±1℃；
S4：向S3中形成的混合液中加入配方规定量的硅烷偶联剂和医用级聚乙烯醇，在卧式或立式搅拌机中搅拌1-2h后出料得到环保的负氧离子浓缩液。
2.根据权利要求1所述的一种环保的负氧离子浓缩液，其特征在于：所述聚乙烯醇为医用级聚乙烯醇。
3.根据权利要求1所述的一种环保的负氧离子浓缩液，其特征在于，包括如下按重量份配比组分：
去离子水55份；
电气石提取物20份；
稀土萃取液10份；
硅烷偶联剂8份；
纳米二氧化钛1.2份；
医用级聚乙烯醇0.8份。