CN111250693B - High-entropy alloy powder for additive remanufacturing and preparation method thereof - Google Patents
High-entropy alloy powder for additive remanufacturing and preparation method thereof Download PDFInfo
- Publication number
- CN111250693B CN111250693B CN202010063354.6A CN202010063354A CN111250693B CN 111250693 B CN111250693 B CN 111250693B CN 202010063354 A CN202010063354 A CN 202010063354A CN 111250693 B CN111250693 B CN 111250693B
- Authority
- CN
- China
- Prior art keywords
- entropy alloy
- alloy powder
- powder
- vacuum induction
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses high-entropy alloy powder for additive remanufacturing and a preparation method thereof, wherein the atomic expression of the high-entropy alloy powder is Al 0.4 CoCu 0.6 NiSi 0.2 The granularity interval is 50-150 mu m, and the preparation method comprises the following steps: sequentially putting the block materials of all metals into a vacuum induction smelting furnace according to the sequence of melting points from low to high in atomic percentage for vacuum induction smelting, and then adopting a gas atomization rapid solidification technology to prepare the alloy. According to the invention, a high-entropy alloy formula without Fe element and rare metal is obtained through a large number of experimental designs, and high-entropy alloy powder is prepared by combining a gas atomization rapid solidification technology, and the high-entropy alloy powder has relatively uniform structural components, higher sphericity, better fluidity, lower oxygen content, higher powder yield and better quality, has a simple fcc + trace bcc solid solution phase structure, has higher microhardness, and can be applied to the field of high-entropy alloy additive remanufacturing and forming.
Description
Technical Field
The invention belongs to the technical field of high-entropy alloy additive remanufacturing, and particularly relates to high-entropy alloy powder for additive remanufacturing and a preparation method thereof.
Background
The high-entropy alloy is a high-mixed-entropy alloy with various main elements, and has excellent comprehensive properties of high strength, high hardness, good plasticity, excellent wear resistance and corrosion resistance, better thermal stability, high oxidation resistance and the like.
At present, relatively more researches are still conducted on the application of the high-entropy alloy in the preparation of the coating, and in recent years, the research on the application of the high-entropy alloy in the additive remanufacturing is gradually increased.
However, the high-entropy alloy powder for additive remanufacturing is basically pure metal powder which is mechanically mixed, and due to the difference of physical properties such as melting points of different metal powders, part of powder in a formed structural member/layer is not melted or is partially melted, so that the defects of uneven structure, serious component segregation, low solid solubility and the like are caused, and further the comprehensive performance of the formed structural member/layer is affected.
In addition, most of the conventional high-entropy alloy powders contain Fe element and/or rare metal.
For the high-entropy alloy powder containing rare metals, the rare metals are expensive, so that the cost is high, and the high-entropy alloy powder is not suitable for industrial large-scale application, and most of the high-entropy alloy powder containing rare metals is poor in plasticity and is not suitable for additive remanufacturing (see literature 1).
For high-entropy alloy powder containing Fe, many researches are currently conducted mainly on AlCoCrFeNi or cocrfmnni series, and when the two series are used for additive remanufacturing, most of the mechanical strength is not ideal under the condition of ensuring plasticity (see documents 2 and 3).
However, there is a problem with the high-entropy alloy powder containing Fe element: in the material increasing remanufacturing process, due to solid solution diffusion among elements, elements in the high-entropy alloy can be dissolved into a base body, the elements in the base body can also be dissolved into the high-entropy alloy, the Fe base body is the most commonly used base body in the aspect of material increasing remanufacturing, if the designed high-entropy alloy contains the Fe element, the high-entropy alloy components at the combination interface can be changed, and phase change is even caused, so that the comprehensive performance of the high-entropy alloy is greatly influenced.
Document 1: yaojiang ZHao et al, "A hexagonal close-packed high-entry ally: the effect of error ", Materials & Design 2016, 96, pages 10-15.
Document 2: zhiguang Zhu et al, "high micro structure and structure mechanics of a CoCrFeNiMn high entry alloy amplified magnetic influenced by selective laser marking", Scapta materials 2018, 154, pages 20-24.
Document 3: yevgeni Brif et al, "The use of high-entry alloys in additive manufacturing", Scampta materials 2015, 99 th, pages 93-96.
Disclosure of Invention
The invention aims to solve the problems and provides high-entropy alloy powder for additive remanufacturing, which is uniform in components, good in flowability, low in oxygen content and particularly free of Fe element and rare metal, and a preparation method thereof.
The technical scheme for realizing the purpose of the invention is as follows: a kind ofHigh-entropy alloy powder for additive remanufacturing, and atomic expression of high-entropy alloy powder is Al 0.4 CoCu 0.6 NiSi 0.2 。
The particle size interval of the high-entropy alloy powder for additive remanufacturing is 50-150 mu m.
The high-entropy alloy powder for additive remanufacturing is prepared by adopting an air atomization rapid solidification technology.
The preparation method of the high-entropy alloy powder for additive remanufacturing comprises the following steps:
firstly, preparing block materials of each metal, removing impurities and oxide films on the surfaces of the block materials of each metal by adopting a grinding machine, and then batching according to atomic percentage.
Secondly, sequentially putting all the metal block materials into a vacuum induction smelting furnace according to the sequence of melting points from low to high, and carrying out vacuum induction smelting under the protection of argon.
Thirdly, the metal liquid obtained by the vacuum induction melting in the step II is directly prepared into Al by adopting an air atomization rapid solidification technology 0.4 CoCu 0.6 NiSi 0.2 High entropy alloy powder.
The gas atomization rapid solidification technology in the third step adopts gas pressure of 2-5 MPa, air flow speed of 100-160 mm/s, liquid flow diameter of 5-10 mm and air flow jet angle of 30-60 degrees.
The invention has the following positive effects: according to the invention, a high-entropy alloy formula without Fe element and rare metal is obtained through a large number of experimental designs, and high-entropy alloy powder is prepared by combining a gas atomization rapid solidification technology, and the high-entropy alloy powder has relatively uniform structural components, higher sphericity, better fluidity, lower oxygen content, higher powder yield and better quality, has a simple fcc + trace bcc solid solution phase structure, has higher microhardness, and can be applied to the field of high-entropy alloy additive remanufacturing and forming.
Drawings
FIG. 1 shows Al obtained in example 1 0.4 CoCu 0.6 NiSi 0.2 SEM image of high entropy alloy powder; wherein, the picture a is a surface overall morphology SEM picture, the picture b is a surface morphology SEM picture of powder particles with larger particle size (A partially enlarged view).
FIG. 2 shows Al obtained in example 1 0.4 CoCu 0.6 NiSi 0.2 The relationship graph of the mass accumulation distribution of the high-entropy alloy powder and the particle size.
FIG. 3 shows Al obtained in example 1 0.4 CoCu 0.6 NiSi 0.2 XRD patterns of the high-entropy alloy powder in different particle size intervals.
FIG. 4 shows Al obtained in example 1 0.4 CoCu 0.6 NiSi 0.2 The microhardness of the high-entropy alloy powder in different particle size ranges.
Fig. 5 is a schematic diagram of the "staggered" forming path adopted in application example 1.
FIG. 6 shows Al obtained in application example 1 0.4 CoCu 0.6 NiSi 0.2 The high-entropy alloy forming structure has the geometric shape of a real object.
FIG. 7 shows Al obtained in application example 1 0.4 CoCu 0.6 NiSi 0.2 XRD pattern of high entropy alloy formed structure.
FIG. 8 shows Al obtained in application example 1 0.4 CoCu 0.6 NiSi 0.2 The stress-strain curve diagram of the room-temperature tensile engineering of the high-entropy alloy forming structure.
Detailed Description
(example 1)
The preparation method of the high-entropy alloy powder for additive remanufacturing of the embodiment comprises the following steps:
firstly, removing impurities and oxide films on the original surface of metal by using Al, Co, Cu, Ni and Si block materials (the purity is more than or equal to 99.9 percent) by using a grinding machine, and then removing impurities and oxide films on the original surface of metal according to the atomic percent of Al 0.4 CoCu 0.6 NiSi 0.2 Ingredients, the total weight is 20 kg.
Secondly, sequentially putting the metal block materials in the step I into a vacuum induction smelting furnace according to the sequence of melting points from low to high, and vacuumizing until the vacuum degree is less than 2.5 multiplied by 10 -3 MPa, then argon is filled to the pressure of 5 multiplied by 10 -2 And Pa, under the condition of argon protection, heating and melting the alloy through an induction coil to start melting, wherein the melting time is 30min, and electromagnetic stirring is introduced in the melting process to ensure the uniformity of alloy components.
Thirdly, nitrogen is introduced through a tightly coupled annular seam type nozzle of atomizing equipment until the pressure is 4MPa, the air flow speed is 130mm/s, the liquid flow diameter is 8mm, the air flow injection angle is controlled to be 45 degrees, and the metal liquid obtained by vacuum induction melting in the second step is directly prepared into Al by adopting an air atomization rapid solidification technology 0.4 CoCu 0.6 NiSi 0.2 High entropy alloy powder.
(test example 1)
Observation of Al obtained in example 1 0.4 CoCu 0.6 NiSi 0.2 SEM images of the high entropy alloy powder, and the results are shown in FIG. 1.
Wherein, the a picture is a surface overall morphology SEM picture, and the b picture is a surface morphology SEM picture (partial enlarged view) of powder particles with larger particle sizes.
As can be seen from diagram a in fig. 1: the high-entropy alloy powder prepared by the invention has uniform particles, is basically spherical and has good sphericity, which shows that the high-entropy alloy powder has good fluidity.
As can be seen from the b diagram in fig. 1: the satellite balls exist on the surfaces of the powder particles with larger particle sizes, mainly due to different cooling speeds of the powder, the cooling speed of the powder with small particle sizes is higher, the cooling speed of the powder with large particle sizes is relatively lower, when the smaller liquid drops are solidified, the large liquid drops can be still in a liquid state or a semi-solid state, and the small particles in the solidified state can be embedded on the surfaces of the large particles when colliding with the large particles which are not solidified.
(test example 2)
Al obtained in example 1 0.4 CoCu 0.6 NiSi 0.2 The high-entropy alloy powder is sieved into three granularity intervals of-50 microns (namely less than 50 microns), 50-150 microns and +150 microns (namely more than 150 microns).
The graph of mass cumulative distribution versus particle size is shown in FIG. 2.
As can be seen from fig. 2: the high-entropy alloy powder prepared by the method has a wide particle size distribution range, the mass fraction of most of the high-entropy alloy powder is not more than 150 mu m (the mass fraction is about 90%), the mass fraction of the high-entropy alloy powder of 50-150 mu m (namely used for additive remanufacturing) is about 70%, and the powder yield is high.
(test example 3)
Al obtained in example 1 was tested 0.4 CoCu 0.6 NiSi 0.2 XRD patterns of three different particle size intervals of the high-entropy alloy powder show that the result is shown in figure 3.
As can be seen in fig. 3: the phase structure of three different particle size intervals is fcc + trace bcc, and the bcc phase content increases with decreasing particle size.
(test example 4)
Al obtained in example 1 was tested 0.4 CoCu 0.6 NiSi 0.2 The microhardness of the high-entropy alloy powder in three different particle size intervals is shown in figure 4.
As can be seen from fig. 4, the microhardness decreases significantly with increasing particle size.
(test example 5)
Al obtained in example 1 was tested by ON-3000 oxynitrides 0.4 CoCu 0.6 NiSi 0.2 The oxygen content of the high-entropy alloy powder is 165ppm, the oxygen content of the powder is low, and the use requirement is met.
(application example 1)
The application example is to prepare a high-entropy alloy forming structure from the high-entropy alloy powder prepared in the embodiment 1, and the specific method comprises the following steps:
s1: and (4) preparing a substrate.
Cutting No. 45 steel wire into rectangular block samples with the size of 150 × 100 × 30mm, sequentially grinding off oxide skin on the surfaces of the samples by 200#, 400# and 800# sandpaper, repeatedly cleaning the surfaces by acetone and alcohol respectively, finally drying and packaging to obtain a base for later use.
S2: and (4) preparing powder.
Al prepared in example 1 and having a particle size range of 50 to 150 μm 0.4 CoCu 0.6 NiSi 0.2 And (3) placing the high-entropy alloy powder in a drying oven, drying for 2h at the temperature of 120 ℃, and removing moisture to increase the fluidity of the powder.
S3: and preparing the high-entropy alloy forming structure by adopting a laser cladding forming technology.
The forming path adopted by the laser cladding of S3 is a "staggered" forming path (see fig. 5), that is, a layer is deposited along the X direction (or Y direction), then two layers are deposited on the layer [ Z direction ] along the Y direction (or X direction), then two layers are deposited on the two layers along the X direction (or Y direction), and so on, and finally a layer is deposited along the X direction (or Y direction).
The main technological parameters adopted in the forming process are as follows: the diameter of a light spot is 4.5mm, the powder feeding rate is 25g/min, the laser power is 2600W, and the scanning speed is 12 mm/s.
In order to reduce the influence of oxidation in the forming process, argon continuously flowing (the flow rate is 15L/min) is adopted as a protective gas in the laser cladding process.
To reduce residual stress, the substrate is first prescanning three times before laser cladding forming deposition begins, and the substrate is preheated to reduce the temperature gradient between the forming structure and the substrate.
The high-entropy alloy forming structure object manufactured in the application example 1 is shown in fig. 6, and can be seen from fig. 6: the forming structure has good surface macroscopic appearance and average geometric dimension: the length x height is about 80 x 14 mm.
The XRD phase analysis result of the high-entropy alloy formed structure obtained in application example 1 is shown in FIG. 7, and it can be seen from FIG. 7 that: the phase composition of the formed structure is mainly fcc plastic phase, and contains trace bcc strengthening phase.
The high-entropy alloy forming structure prepared by the application example 1 is subjected to room temperature quasi-static compression, and the room temperature tensile engineering stress-strain curve is shown in fig. 8, which can be seen from fig. 8: the forming structure has the advantages that the tensile strength can reach 1195.6MPa, the yield strength can reach 662.0MPa, the elongation can reach 14.5 percent without heat treatment, the forming structure has high strength and excellent plasticity, and the strong plasticity balance is realized.
Claims (2)
1. A preparation method of high-entropy alloy powder for additive remanufacturing comprises the following steps:
firstly, preparing block materials of each metal, removing impurities and oxide films on the surfaces of the block materials of each metal by adopting a grinding machine, and then batching according to atomic percentage;
sequentially putting all the metal block materials into a vacuum induction smelting furnace according to the sequence of melting points from low to high, and carrying out vacuum induction smelting under the protection of argon;
thirdly, the metal liquid obtained by the vacuum induction melting in the step II is directly prepared into Al by adopting an air atomization rapid solidification technology 0.4 CoCu 0.6 NiSi 0.2 High entropy alloy powder.
2. A method of preparing high entropy alloy powder for additive remanufacturing according to claim 1, wherein: the gas atomization rapid solidification technology in the third step adopts gas pressure of 2-5 MPa, air flow speed of 100-160 mm/s, liquid flow diameter of 5-10 mm and air flow jet angle of 30-60 degrees.