CN1111918C - Preparation method of nickel positive active material spherical alpha-nickel hydroxide - Google Patents
Preparation method of nickel positive active material spherical alpha-nickel hydroxide Download PDFInfo
- Publication number
- CN1111918C CN1111918C CN00123599A CN00123599A CN1111918C CN 1111918 C CN1111918 C CN 1111918C CN 00123599 A CN00123599 A CN 00123599A CN 00123599 A CN00123599 A CN 00123599A CN 1111918 C CN1111918 C CN 1111918C
- Authority
- CN
- China
- Prior art keywords
- nickel
- solution
- reaction
- mol
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a preparation method of nickel anode active material spherical alpha-nickel hydroxide, which comprises: a nickel salt water solution and a sodium hydroxide alkali solution with certain quantity and concentration and an auxiliary reaction reagent are pumped into a reaction kettle containing deionized water beforehand through a measuring delivery pump for reaction under the regulation of a constant temperature system, a solid content retention system and a pH regulation system; after the reaction finishes, crystal form transformation is completed through aging; the solid-liquid mixing system in the reaction kettle is treated by solid-liquid separation, washing and drying to obtain the alpha-Ni(OH)2 product. The nickel anode prepared by the present invention has high charge efficiency, large discharge depth and good performance of high-current charge and discharge.
Description
Technical field
The present invention relates to a kind of preparation method of nickel positive active material spherical alpha-nickel hydroxide, belong to Chemical Engineering and field of new.
Background technology
Nickel hydroxide (Ni (OH)
2) be various alkaline rechargeable batteries (as Ni/Cd, Ni/Zn, Ni/MH, Ni/H
2Deng) positive electrode active materials.Capacity and life-span to battery are played key effect.There is different crystal formations in nickel hydroxide with oxidation state going back ortho states, and present nickel electrode all adopts
Electricity is to circulation, and in the right electrochemical reaction process of this electricity, the variation of the oxidation state of nickle atom is about 1, thereby its electron transfer number has only 1, and its theoretical specific capacity only is 289mAh/g; In addition, when electrode when overcharging, β-NiOOH is converted into γ-NiOOH, changes α-Ni (OH) in discharge overcharges into
2, α-Ni (OH)
2Unstable in alkali lye, become β-Ni (OH) during placement again
2Because α-Ni (OH)
2And the crystalline density of γ-NiOOH is all less than β-Ni (OH)
2, thereby there is swelling in electrode in charge and discharge process.The expansion of electrode has caused redistributing of battery electrolyte inside, has increased the internal resistance and the polarization of electrode, causes the interior voltage rise height of battery and climbs the alkali phenomenon, has accelerated the inefficacy speed of battery.
But circulation can not have been satisfied modern electrical equipment well to performance demands such as rechargeable battery small size, light weight, high power capacity, long-life high current charge-discharges.
α-Ni (OH)
2Close with the crystalline density of γ-NiOOH, also there is the electrochemistry circulation between the two.Because the oxidation state of nickle atom can reach 3.67 among γ-NiOOH, thereby
Electricity is in the circulation, and the electron transfer number of each nickle atom can surpass 1 in theory, and its theoretical specific capacity will reach 480mAh/g, consider the influence of doping, and its electric specific capacity also will reach 380mAh/g.With α-Ni (OH)
2For the nickel positive pole of active material preparation, will avoid the expansion of electrode effectively, and greatly improve the specific discharge capacity of battery, satisfy modern electrical equipment well to the above-mentioned performance demands of rechargeable battery.
The 3 a large amount of valence metal ions that mix in the nickel hydroxide crystal can improve α-Ni (OH)
2Stability in alkali lye, thus guarantee to discharge and recharge
Between carry out.Prepare β-Ni (OH) at present
2Technology adopt the liquid phase reactor method more, contain in the nickel salt solution and sodium hydroxide solution adding system simultaneously of doped chemical (cobalt, zinc), having under the condition of stirring, generate nickel hydroxide.Yet, adopt this prepared α-Ni (OH)
2, when the amount of doped chemical is big, there is serious segregation phenomena, the doped chemical major part can not be evenly distributed in the nickel hydroxide lattice, but separates out separately in the system mother liquor.α-the Ni (OH) of preparation
2Form is amorphous or sheet, and washing, filtration, drying are all very difficult, causes the tap density of sample lower, and serviceability is relatively poor, be difficult for being filled in nickel foam or the nickel fiber, thereby the fill volume of reduction battery can not be brought into play effectively
The usefulness that electricity is right.
Summary of the invention
The objective of the invention is to propose a kind of preparation method of nickel positive active material spherical alpha-nickel hydroxide, that uses two or more has the mixed twine mixture of different complexing powers to nickel ion and dopant ion; Doping elements is with the form of metal ion or acid ion, and with nickel ion doping deposition, crystallization forms substitutional solid solution Ni under the trend that different pH changes
1-2xM
2x(OH)
2(CO
3)
xNH
2O (5%<x<15%).
The preparation method of the nickel positive active material spherical alpha-nickel hydroxide that the present invention proposes may further comprise the steps:
1, material liquid preparation: preparation contains the nickel sulfate solution A of complexing agent and additive, wherein the concentration of nickelous sulfate is 0.5~3 mol, complexing agent is any material in trisodium citrate, sodium glutamate and the disodium ethylene diamine tetraacetate, its concentration is 0.01~0.5 mol, additive is zinc sulfate or cobaltous sulfate, and concentration is 0.001~0.5 mol; Preparation contains the sodium hydrate aqueous solution B of ammonia, and wherein concentration sodium hydroxide is 5~8 mol, and the concentration of ammonia is 0.1~0.5 mol; The salt of doped chemical M is dissolved in solution A or the solution B, doped chemical is existed with the form of metal ion or acid ion, above-mentioned doped chemical M is any among Al, Co, Fe, Mn or the In, and the mol ratio of dopant ion and nickel ion is: 0.1~0.3;
2, reaction: add a certain amount of deionized water in special reactor in advance, the temperature in the control reactor is 30~80 ℃; Under stirring condition, solution A and solution B be continuously pumped into respectively according to certain flow-rate ratio carry out chemical reaction in the reactor, the nickel hydroxide of generation is discharged reactor continuously.In course of reaction, the pH value of control reaction system is 8~13, and the reaction time is 2~6 hours.
3, ageing: that will discharge contains α-Ni (OH)
2Mother liquor transfer in the aging tank, at room temperature be exposed in the air, continue to stir 1 hour.
4, product and mother liquor carry out Separation of Solid and Liquid through solid-liquid separator, wherein solid spherical α-Ni (OH)
2Particle enters washer and washs with deionized water, enter then drier 60 ℃ dry 2 hours down, dry back obtains spherical alpha-Ni (OH)
2Product.After mother liquor is discharged by solid-liquid separator, discharging after the liquid waste processing device is handled.
Selectable complexing agent comprises: ammoniacal liquor or ammonium salt (ammonium sulfate, ammonium nitrate or ammonium chloride), citric acid or citrate, amino acid or amino-acid salt (single amino acid or kilnitamin all can), tartaric acid or tartrate, ethylenediamine, EDTA.As mentioned above, the complexing agent that mix to use, wherein a kind of is ammoniacal liquor or ammonium salt, in addition, selects for use at least aly from above-mentioned optionally other complexing agent, mixes use with ammoniacal liquor or ammonium salt then.The 3 valency metallic elements that mix can be from selecting one or more the column element down, and these elements comprise: Al, Co, Fe, Mn, In and Ga.Doped chemical shared ratio in crystal is about 10~30%.
The crystallization control and the two-way engagement technology of the use mixed twine mixture that the present invention proposes are compared the α-Ni that makes (OH) as the technology of complexing agent with using single ammoniacal liquor or ammonium salt
2Mode of appearance is sphere or class sphere, and the electron transfer number of each nickle atom in charge and discharge process can reach 1.4~1.5, and electro-chemical activity is higher, and serviceability is better.
The preparation spherical alpha-Ni (OH) that the present invention set up
2Technology have the following advantages: technological process is simple, and technological parameter control realizes easily.The anodal expansion of the nickel that adopts this kind active material to make is little, the specific capacity height, and the high rate charge-discharge performance is good, has bigger practical value.
Embodiment
Introduce embodiments of the invention below:
Embodiment one, takes by weighing 78 gram ZnSO
47H
2O, 370 gram doped chemical salt, CoSO
47H
2O, 1970 gram NiSO
46H
2O, 20 gram sodium glutamates are dissolved in the deionized water, are mixed with 3000 ml water solution A; Take by weighing 600 gram NaOH, measure 115 milliliters of the ammoniacal liquor of 13 mol, be mixed with 3000 ml water solution B; In effective volume is 7 liters reactor, add 6 liters of deionized waters.Having under the condition of stirring, reacting according to above-mentioned technology the 2nd step, wherein the flow of water solution A is 700 milliliters/hour, and the flow of aqueous solution B is~650 milliliters/hour.The pH value of controlling reaction system by the flow of adjusting aqueous solution B is 12.0 ± 0.05.Reaction temperature is 50 ± 0.5 ℃.The mother liquor of discharging at room temperature is exposed in the air, continues to stir 1 hour.After stopping to stir, mother liquor carries out Separation of Solid and Liquid through solid-liquid separator, and wherein solid spherical alpha-nickel hydroxide particle enters washer and washs, and enters 60 ℃ of dryings of drier 2 hours then, obtains the spherical alpha-nickel hydroxide sample.The tap density that records this sample is 1.52g/cm
3Take by weighing 0.5 this sample of gram, 25 milligrams of nickel powders, 20 milligram 60% poly-tetrafluoro emulsion and suitable quantity of water are that collector is made positive pole with the nickel foam, are negative pole with the hydrogen bearing alloy, 25 ℃ record the specific discharge capacity of this sample when 0.2C discharges and recharges is 335mAh/g.
Embodiment two, add trisodium citrate 70 grams when obtain solution A, do not add sodium glutamate and cobaltous sulfate; In solution B, add Al
2(SO
4)
33H
2O 238 grams, other forms feed liquid with embodiment one, finishes preparation process according to the operating condition among the embodiment one.The tap density that records the gained sample is 1.51g/cm
3, identical with anode formula among the embodiment one, the specific discharge capacity when recording this sample 0.2C and discharging and recharging is 329mAh/g.
Embodiment three, add MnSO when obtain solution A
4H
2O 102 grams, disodium ethylene diamine tetraacetate (EDTA) 5 grams, no longer add other complexing agents: no longer add other metal salt solutions in the solution B, other is formed with embodiment one, finishes preparation process according to the operating condition among the embodiment one.The tap density that records the gained sample is 1.65g/cm
3, identical with anode formula among the embodiment one, the specific discharge capacity when recording this sample 0.2C and discharging and recharging is 322mAh/g.
Embodiment four, add FeSO when obtain solution A
4H
2O 140 grams no longer add other metal salt solutions, and other is formed with embodiment one, finishes preparation process according to the operating condition among the embodiment one.The tap density that records the gained sample is 1.47g/cm
3, identical with anode formula among the embodiment one, the specific discharge capacity when recording this sample 0.2C and discharging and recharging is 306mAh/g.
Embodiment five, add InSO when obtain solution A
4180 grams no longer add other metal salt solutions, and other is formed with embodiment one, finishes preparation process according to the operating condition among the embodiment one.The tap density that records the gained sample is 1.49g/cm
3, identical with anode formula among the embodiment one, the specific discharge capacity when recording this sample 0.2C and discharging and recharging is 312mAh/g.
Comparative example one: blending process and parameter are with embodiment two, but Al
2(SO
4)
33H
2O is formulated in the solution A.Other forms feed liquid with embodiment two.Having under the condition of stirring, solution A and solution B are added in the reactor simultaneously, the flow of solution A is 700 milliliters/hour, and the pH value of controlling reaction system by the flow of adjusting solution B is 8.5 ± 0.05.Other parameter is with embodiment one.Obtain sample through reaction, ageing with after separating drying.The tap density that records this sample is 1.2g/cm
3Anode formula is with embodiment one, and recording the specific discharge capacity of this sample when the 0.2C rate charge-discharge is 293mAh/g.
Comparative example two: blending process and parameter be with embodiment one, but do not contain other complexing agents in the solution A; Other is formed with embodiment one.Having under the condition of stirring, solution A and solution B are added in the reactor simultaneously, the flow of water solution A is 700 milliliters/hour, and the pH value of controlling reaction system by the flow of adjusting solution B is 12.0 ± 0.05.Other parameter is with embodiment one.Obtain product through reaction, ageing with after separating drying.The tap density that records this sample is 1.1g/cm
3Anode formula is with embodiment one, and recording the specific discharge capacity of this sample when the 0.2C rate charge-discharge is 296mAh/g.
Claims (1)
1, a kind of preparation method of nickel positive active material spherical alpha-nickel hydroxide is characterized in that, this method may further comprise the steps:
(1) material liquid preparation: preparation contains the nickel sulfate solution A of complexing agent and additive, wherein the concentration of nickelous sulfate is 0.5~3 mol, complexing agent is any material in trisodium citrate, sodium glutamate and the disodium ethylene diamine tetraacetate, its concentration is 0.01~0.5 mol, additive is zinc sulfate or cobaltous sulfate, and concentration is 0.001~0.5 mol; Preparation contains the sodium hydrate aqueous solution B of ammonia, and wherein concentration sodium hydroxide is 5~8 mol, and the concentration of ammonia is 0.1~0.5 mol; The salt of doped chemical M is dissolved in solution A or the solution B, doped chemical is existed with the form of metal ion or acid ion, above-mentioned doped chemical M is any among Al, Co, Fe, Mn or the In, and the mol ratio of dopant ion and nickel ion is: 0.1~0.3;
(2) reaction: add deionized water in reactor in advance, the temperature in the control reactor is 30~80 ℃; Under stirring condition, is that the ratio of A: B=1: 0.6-0.9 is continuously pumped into respectively and carries out chemical reaction in the reactor with solution A and solution B according to flow-rate ratio, the nickel hydroxide that generates is discharged reactor continuously, in course of reaction, the pH value of control reaction system is 8~13, and the reaction time is 2~6 hours;
(3) ageing: that will discharge contains α-Ni (OH)
2Mother liquor transfer in the aging tank, at room temperature be exposed in the air, continue to stir 1 hour;
(4) product and mother liquor carry out Separation of Solid and Liquid through solid-liquid separator, wherein solid spherical α-Ni (OH)
2Particle enters washer and washs with deionized water, enters drier then and descends dry 2 hours at 60 ℃, promptly obtains spherical alpha-Ni (OH) after the drying
2Product.