CN111172812A - Transparent wood pulp book wrapping paper and preparation method thereof - Google Patents
Transparent wood pulp book wrapping paper and preparation method thereof Download PDFInfo
- Publication number
- CN111172812A CN111172812A CN202010083409.XA CN202010083409A CN111172812A CN 111172812 A CN111172812 A CN 111172812A CN 202010083409 A CN202010083409 A CN 202010083409A CN 111172812 A CN111172812 A CN 111172812A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood pulp
- wrapping paper
- book
- book wrapping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses transparent wood pulp book wrapping paper and a preparation method thereof, wherein the transparent wood pulp book wrapping paper comprises the following components in parts by mass: the invention is used for replacing plastic book cover to wrap book, and has the characteristics of transparency, self-adhesion, water resistance and fouling resistance, and has the characteristic of degradability, thus being an environment-friendly and pollution-free product.
Description
Technical Field
The invention relates to the technical field of papermaking, in particular to transparent wood pulp book wrapping paper and a preparation method thereof.
Background
In daily life, books are often packaged by the book cover so as to be protected from water and dirt, the common book cover is made of plastic materials, and the plastic is a pollutant which is difficult to degrade and causes environmental pollution when being thrown everywhere after being used.
Disclosure of Invention
Aiming at the defects of the prior art, the invention provides the transparent wood pulp book wrapping paper, and solves the problem that the plastic book wrapping cover pollutes the environment.
In order to achieve the purpose, the invention is realized by the following technical scheme: the transparent wood pulp book wrapping paper comprises the following components in parts by weight: 40-65 parts of wood pulp, 20-40 parts of acrylic adhesive, 10-20 parts of butadiene styrene rubber, 3-10 parts of wet strength agent and 2-5 parts of water repellent agent.
Preferably, the wood pulp is 50-55 parts, the acrylic adhesive is 25-35 parts, the styrene-butadiene adhesive is 13-17 parts, the wet strength agent is 5-8 parts, and the water repellent agent is 3-4 parts.
Preferably, the wood pulp is 52.5 parts, the acrylic adhesive is 30 parts, the styrene-butadiene adhesive is 15 parts, the wet strength agent is 6.5 parts, and the water repellent agent is 3.5 parts.
Preferably, the wood pulp is softwood pulp.
Based on the transparent wood pulp book wrapping paper, the invention also provides a preparation method of the transparent wood pulp book wrapping paper, which comprises the following steps:
(1) preparing materials: preparing materials according to the mass parts of the components;
(2) and pulping: placing softwood pulp into a hydrapulper for fully pulping;
(3) pulping: putting the slurry obtained in the step 2 into a beating machine for beating to enable the beating degree to reach 15-20 ℃;
(4) and homogenizing: adding a wet strength agent into the slurry obtained in the step 3, and fully homogenizing by adopting a homogenizing device;
(5) and papermaking: papermaking the slurry after homogenate by an inclined wire paper machine;
(6) and dipping: dipping paper with butyl benzene glue and drying by a drying cylinder;
(7) and coating: coating a release agent on the front surface of the paper, and coating acrylic glue on the back surface of the paper;
(8) and preparing book wrapping paper: and drying the paper again, reeling, and cutting to obtain the book wrapping paper for manufacturing the book wrapping cover.
Preferably, the beating degree in the step 3 is 17-18 degrees.
Preferably, the drying temperature in the step 6 is 100-110 ℃.
Preferably, the drying temperature in the step 8 is 100-110 ℃.
The transparent wood pulp book wrapping paper has the following beneficial effects: the book wrapping paper is transparent, does not shield book covers, has the advantages of self-adhesion, water resistance and fouling resistance, is convenient to package, and is an environment-friendly pollution-free product due to the fact that main materials are wood pulp and have the characteristics of being non-toxic and degradable.
Detailed Description
The following will specifically describe the formulation of the components and the specific preparation method of the present invention with reference to the specific examples.
Example 1
The transparent wood pulp book wrapping paper comprises the following components in parts by weight: 40 parts of wood pulp, 20 parts of acrylic rubber, 10 parts of butadiene styrene rubber, 3 parts of wet strength agent and 2 parts of water repellent agent.
Specifically, the wood pulp is softwood pulp.
The preparation method of the transparent wood pulp book wrapping paper comprises the following specific steps:
(1) preparing materials: preparing materials according to the mass parts of the components;
(2) and pulping: placing softwood pulp into a hydrapulper for fully pulping;
(3) pulping: putting the slurry obtained in the step 2 into a beating machine for beating to enable the beating degree to reach 15 ℃;
(4) and homogenizing: adding a wet strength agent into the slurry obtained in the step 3, and fully homogenizing by adopting a homogenizing device;
(5) and papermaking: papermaking the slurry after homogenate by an inclined wire paper machine;
(6) and dipping: dipping paper with butyl benzene glue, and drying by using a drying cylinder at the drying temperature of 100 ℃;
(7) and coating: coating a release agent on the front surface of the paper, and coating acrylic glue on the back surface of the paper;
(8) and preparing book wrapping paper: and drying the paper again, reeling, and cutting to obtain the book wrapping paper for manufacturing the book wrapping cover, wherein the drying temperature is 100 ℃.
Example 2
The transparent wood pulp book wrapping paper comprises the following components in parts by weight: 65 parts of wood pulp, 40 parts of acrylic adhesive, 20 parts of butadiene styrene adhesive, 10 parts of wet strength agent and 5 parts of water repellent agent.
Specifically, the wood pulp is softwood pulp.
The preparation method of the transparent wood pulp book wrapping paper comprises the following specific steps:
(1) preparing materials: preparing materials according to the mass parts of the components;
(2) and pulping: placing softwood pulp into a hydrapulper for fully pulping;
(3) pulping: putting the slurry obtained in the step 2 into a beating machine for beating to enable the beating degree to reach 20 ℃;
(4) and homogenizing: adding a wet strength agent into the slurry obtained in the step 3, and fully homogenizing by adopting a homogenizing device;
(5) and papermaking: papermaking the slurry after homogenate by an inclined wire paper machine;
(6) and dipping: dipping paper with butyl benzene glue, and drying by using a drying cylinder at the drying temperature of 110 ℃;
(7) and coating: coating a release agent on the front surface of the paper, and coating acrylic glue on the back surface of the paper;
(8) and preparing book wrapping paper: and drying the paper again, reeling, and cutting to obtain the book wrapping paper for manufacturing the book wrapping cover, wherein the drying temperature is 110 ℃.
Example 3
52.5 parts of wood pulp, 30 parts of acrylic rubber, 15 parts of butadiene styrene rubber, 6.5 parts of wet strength agent and 3.5 parts of water repellent agent.
Specifically, the wood pulp is softwood pulp.
The preparation method of the transparent wood pulp book wrapping paper comprises the following specific steps:
(1) preparing materials: preparing materials according to the mass parts of the components;
(2) and pulping: placing softwood pulp into a hydrapulper for fully pulping;
(3) pulping: putting the slurry obtained in the step 2 into a beating machine for beating to enable the beating degree to reach 17 ℃;
(4) and homogenizing: adding a wet strength agent into the slurry obtained in the step 3, and fully homogenizing by adopting a homogenizing device;
(5) and papermaking: papermaking the slurry after homogenate by an inclined wire paper machine;
(6) and dipping: dipping paper with butyl benzene glue, and drying by using a drying cylinder at 105 ℃;
(7) and coating: coating a release agent on the front surface of the paper, and coating acrylic glue on the back surface of the paper;
(8) and preparing book wrapping paper: and drying the paper again, reeling, and cutting to obtain the book wrapping paper for manufacturing the book wrapping cover, wherein the drying temperature is 105 ℃.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (8)
1. Transparent wood pulp book wrapping paper, its characterized in that: the composition comprises the following components in parts by mass: 40-65 parts of wood pulp, 20-40 parts of acrylic adhesive, 10-20 parts of butadiene styrene rubber, 3-10 parts of wet strength agent and 2-5 parts of water repellent agent.
2. The transparent wood pulp book wrapping paper according to claim 1, wherein the wood pulp is 50-55 parts, the acrylic glue is 25-35 parts, the styrene butadiene glue is 13-17 parts, the wet strength agent is 5-8 parts, and the water repellent agent is 3-4 parts.
3. The transparent wood pulp book wrapping paper according to claim 2, wherein the wood pulp is 52.5 parts, the acrylic glue is 30 parts, the styrene butadiene glue is 15 parts, the wet strength agent is 6.5 parts, and the water repellent agent is 3.5 parts.
4. The transparent wood pulp book cover according to claim 3, characterized in that the wood pulp is softwood pulp.
5. The method for preparing the transparent wood pulp book wrapping paper of any one of claims 1 to 4, characterized by comprising the following steps:
(1) preparing materials: preparing materials according to the mass parts of the components;
(2) and pulping: placing softwood pulp into a hydrapulper for fully pulping;
(3) pulping: putting the slurry obtained in the step 2 into a beating machine for beating to enable the beating degree to reach 15-20 ℃;
(4) and homogenizing: adding a wet strength agent into the slurry obtained in the step 3, and fully homogenizing by adopting a homogenizing device;
(5) and papermaking: papermaking the slurry after homogenate by an inclined wire paper machine;
(6) and dipping: dipping paper with butyl benzene glue and drying by a drying cylinder;
(7) and coating: coating a release agent on the front surface of the paper, and coating acrylic glue on the back surface of the paper;
(8) and preparing book wrapping paper: and drying the paper again, reeling, and cutting to obtain the book wrapping paper for manufacturing the book wrapping cover.
6. The method for preparing the transparent wood pulp book wrapping paper according to claim 5, wherein the beating degree in the step 3 is 17-18 degrees.
7. The method for preparing the transparent wood pulp book wrapping paper according to claim 5, wherein the drying temperature in the step 6 is 100-110 ℃.
8. The method for preparing the transparent wood pulp book wrapping paper according to claim 5, wherein the drying temperature in the step 8 is 100-110 ℃.